C 245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 1
EE C245 – ME C218Introduction to MEMS Design
Fall 2007
Prof. Clark T.-C. Nguyen
Dept. of Electrical Engineering & Computer SciencesUniversity of California at Berkeley
Berkeley, CA 94720
Lecture 8: Surface Micromachining
C 245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 2
Lecture Outline
• Reading: Senturia Chpt. 3, Jaeger Chpt. 11, Handout: “Surface Micromachining for MicroelectromechanicalSystems”
• Lecture Topics:Finish diffusionPolysilicon surface micromachiningStictionResidual stressTopography issuesNickel metal surface micromachining3D “pop-up” MEMSFoundry MEMS: the “MUMPS” processThe Sandia SUMMIT process
2
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 3
Metallurgical Junction Depth, xj
xj = point at which diffused impurity profile intersects the background concentration, NB
Log[N(x)]
NO
NB
x = distance f/ surfacexj
e.g., p-type Gaussian
e.g., n-type
Log[N(x)-NB]
NO-NB
NB
x = distance f/ surfacexj
Net impurity conc.
n-type region
p-type region
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 4
Expressions for xj
• Assuming a Gaussian dopant profile: (the most common case)
• For a complementary error function profile:
( ) Bj
oj NDt
xNtxN =
⎥⎥⎦
⎤
⎢⎢⎣
⎡⎟⎟⎠
⎞⎜⎜⎝
⎛−=
2
2exp, ⎟⎟
⎠
⎞⎜⎜⎝
⎛=
B
oj N
NDtx ln2
( ) Bj
oj NDt
xNtxN =⎟⎟
⎠
⎞⎜⎜⎝
⎛=
2erfc, ⎟⎟
⎠
⎞⎜⎜⎝
⎛= −
o
Bj N
NDtx 1erfc2
→
→
3
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 5
Sheet Resistance
• Sheet resistance provides a simple way to determine the resistance of a given conductive trace by merely counting the number of effective squares
• Definition:
•What if the trace is non-uniform? (e.g., a corner, contains a contact, etc.)
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 6
# Squares From Non-Uniform Traces
4
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 7
Sheet Resistance of a Diffused Junction
• For diffused layers:
• This expression neglects depletion of carriers near the junction, xj → thus, this gives a slightly lower value of resistance than actual
• Above expression was evaluated by Irvin and is plotted in “Irvin’s curves” on next few slides
Illuminates the dependence of Rs on xj, No (the surface concentration), and NB (the substrate background conc.)
( ) ( )11 −−
⎥⎦⎤
⎢⎣⎡=⎥⎦
⎤⎢⎣⎡== ∫∫
jj x
o
x
oj
s dxxNqdxxx
R μσρ
Sheet resistance
Effective resistivity
Majority carrier mobility
Net impurity concentration
[extrinsic material]
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 8
Irvin’s Curves (for n-type diffusion)
Example.Given:NB = 3x1016 cm-3
No = 1.1x1018 cm-3
(n-type Gaussian)xj = 2.77 μmCan determine these given known predep. and drive conditions
Determine the Rs.
p-type
5
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 9
Irvin’s Curves (for p-type diffusion)
Example.Given:NB = 3x1016 cm-3
No = 1.1x1018 cm-3
(p-type Gaussian)xj = 2.77 μmCan determine these given known predep. and drive conditions
Determine the Rs.
n-type
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 10
Surface Micromachining
6
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 11
Silicon Substrate
Polysilicon Surface-Micromachining
• Uses IC fabrication instrumentation exclusively
• Variations: sacrificial layer thickness, fine- vs. large-grained polysilicon, in situvs. POCL3-dopingSilicon Substrate
Free-Standing
PolysiliconBeam
HydrofluoricAcid
ReleaseEtchant
Wafer
300 kHz Folded-Beam Micromechanical Resonator
NitrideInterconnectPolysilicon
SacrificialOxide Structural
PolysilconIsolationOxide
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 12
Polysilicon
7
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 13
Why Polysilicon?
• Compatible with IC fabrication processesProcess parameters for gate polysilicon well knownOnly slight alterations needed to control stress for MEMS applications
• Stronger than stainless steel: fracture strength of polySi ~ 2-3 GPa, steel ~ 0.2GPa-1GPa
• Young’s Modulus ~ 140-190 GPa• Extremely flexible: maximum strain before fracture ~ 0.5%• Does not fatigue readily
• Several variations of polysilicon used for MEMSLPCVD polysilicon deposited undoped, then doped via ion implantation, PSG source, POCl3, or B-source dopingIn situ-doped LPCVD polysiliconAttempts made to use PECVD silicon, but quality not very good (yet) → etches too fast in HF, so release is difficult
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 14
Polysilicon Surface-Micromachining Process Flow
8
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 15
Layout and Masking Layers
• At Left: Layout for a folded-beam capacitive comb-driven micromechanical resonator
•Masking Layers:
1st Polysilicon
2nd Polysilicon
Anchor Opening
A A′ Capacitive comb-drive for linear actuation
Folded-beam support structure for stress relief
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 16
Surface-Micromachining Process Flow• Deposit isolation LTO (or PSG):
Target = 2μm1 hr. 40 min. LPCVD @450oC
• Densify the LTO (or PSG)Anneal @950oC for 30 min.
• Deposit nitride:Target = 100nm22 min. LPCVD @800oC
• Deposit interconnect polySi:Target = 300nmIn-situ Phosphorous-doped1 hr. 30 min. LPCVD @650oC
• Lithography to define poly1 interconnects
• RIE polysilicon interconnects:CCl4/He/O2 @300W,280mTorr
• Remove photoresist in PRS2000
Silicon Substrate
NitrideInterconnectPolysilicon
IsolationOxide
Silicon Substrate
Silicon Substrate
Photoresist
Cross-sections through A-A′
9
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 17
Surface-Micromachining Process Flow
• Deposit sacrificial PSG:Target = 2μm1 hr. 40 min. LPCVD @450oC
• Densify the PSGAnneal @950oC for 30 min.
• Lithography to define anchors
• Etch anchorsRIE using CHF3/CF4/He @350W,2.8TorrRemove PR in PRS2000Quick wet dip in 10:1 HF to remove native oxide
• Deposit structural polySiTarget = 2μmIn-situ Phosphorous-doped11 hrs. LPCVD @650oC
Silicon Substrate
SacrificialOxide
Silicon Substrate
Photoresist
Silicon Substrate
Structural Polysilcon
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 18
Surface-Micromachining Process Flow• Deposit oxide hard mask (PSG)
Target = 500nm25 min. LPCVD @450oC
• Stress Anneal1 hr. @ 1050oCOr RTA for 1 min. @ 1100oC in 50 sccm N2
• Lithography to define poly2 structure (e.g., shuttle, springs, drive & sense electrodes)
Hard bake the PR longer to make it stronger
• Etch oxide mask firstRIE using CHF3/CF4/He @350W,2.8Torr
• Etch structural polysiliconRIE using CCl4/He/O2@300W,280mTorrUse 1 min. etch/1 min. rest increments to prevent excessive temperatureSilicon Substrate
Silicon Substrate
Silicon Substrate
Oxide Hard Mask
10
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 19
Surface-Micromachining Process Flow
• Remove PR (more difficult)Ash in O2 plasmaSoak in PRS2000
• Release the structuresWet etch in HF for a calculated time that insures complete undercutting If 5:1 BHF, then ~ 30 min.If 48.8 wt. % HF, ~ 1 min.
• Keep structures submerged in DI water after the etch
• Transfer structures to methanol
• Supercritical CO2 dry release
Silicon Substrate
Silicon Substrate
Free-StandingPolysilicon Beam
HydrofluoricAcid
ReleaseEtchant
Wafer
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 20
Polysilicon Surface-Micromachined Examples
• Below: All surface-micromachined in polysilicon using variants of the described process flow
Free-Free Beam Resonator
ThreeThree--Resonator Micromechanical FilterResonator Micromechanical Filter
FoldedFolded--Beam CombBeam Comb--Driven ResonatorDriven Resonator
11
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 21
Structural/Sacrifical Material Combinations
H2O2, hot H2OPoly-GePoly-SiGe
TMAH, XeF2SiAl
XeF2Poly-SiSiO2
O2 plasmaPhotoresistAl
HF, BHFSiO2, PSG, LTOPoly-Si
EtchantSacrificial MaterialStructural Material
•Must consider other layers, too, as release etchantsgenerally have a finite E.R. on any material
• Ex: concentrated HF (48.8 wt. %)Polysilicon E.R. ~ 0Silicon nitride E.R. ~ 1-14 nm/minWet thermal SiO2 ~ 1.8-2.3 μm/minAnnealed PSG ~ 3.6 μm/minAluminum (Si rich) ~ 4 nm/min (much faster in other Al)
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 22
Wet Etch Rates (f/ K. Williams)
12
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 23
Film Etch Chemistries
• For some popular films:
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 24
Issues in Surface Micromachining
• Stiction: sticking of released devices to the substrate or to other on-chip structures
Difficult to tell if a structure is stuck to substrate by just looking through a microscope
• Residual Stress in Thin FilmsCauses bending or warping of microstructuresLimits the sizes (and sometimes geometries) of structures
• TopographyStringers can limit the number of structural levels
Substrate
BeamStiction
Stringer
13
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 25
Microstructure Stiction
EE C245: Introduction to MEMS Design Lecture 8 C. Nguyen 9/20/07 26
Microstructure Stiction
• Stiction: the unintended sticking of MEMS surfaces
• Release stiction:Occurs during drying after a wet release etchCapillary forces of droplets pull surfaces into contactVery strong sticking forces, e.g., like two microscope slides w/ a droplet between
• In-use stiction: when device surfaces adhere during use due to:
Capillary condensationElectrostatic forcesHydrogen bondingVan der Waals forces
Stiff Beam
Rinse Liquid
Wide Beam
Anchor
Substrate
Substrate
BeamStiction