Effect of salt bath nitriding on microstructure, corrosion resistance, and mechanical
properties of a hot work tool steel
Hangtao Fua, Jin Zhanga,*, Jinfeng Huangb, Yong Liana and Cheng Zhangb
a Institute for Advanced Materials and Technology, University of Science and Technology
Beijing, China
b State Key Lab. for Advanced Metals and Materials, University of Science and Technology
Beijing, China
* Corresponding author at: Institute for Advanced Materials and Technology, University of
Science and Technology Beijing, 100083 Beijing, China
E-mail address: zhangjin@ustb.edu.cn
Tel: +861082377393
Abstract:
In this study a kind of hot work tool steel was modified by salt bath nitriding for 4 h at 540°C
and 560°C respectively and post-oxidation was carried out. Surface and cross-sectional
hardness test results revealed that surface hardness increased apparently after the treatment
because of the formation of compound layer and diffusion zone. Microstructure and phase
analysis showed that more homogeneous compound layer, and more Fe3O4-phase could be
generated after treated at 560°C than at 540°C. As a result, the corrosion potential was
elevated and the self-corrosion current density reduced more obviously. As well, thickness
and porosity of the compound layer also increased with the nitriding temperature elevating.
Due to the solution of nitrogen atom, XRD diffraction peaks broadened and the position of
peaks shifted to lower angle in different degrees at different depths showing the same
mailto:zhangjin@ustb.edu.cn
tendency as hardness curves. Salt bath nitriding deteriorated impact property from 32.3J to
5.2J seriously.
Keywords:
Salt bath nitriding; Hot work tool steel; Microstructure; Diffraction analysis; Corrosion
resistance; Impact property
1. Introduction
Nitriding is one of the most widely used surface treatment modifications which has
established a popular surface engineering method for improving hardness, fatigue strength,
wear and corrosion resistance of various tools [1-4]. Salt bath nitriding gets its popular in
many industrial components [5-7]. In salt bath nitriding, the samples are immersed in cyanate
salt bath, nitrogen atoms diffuse into the substrate through grain boundaries, sub-boundaries
and dislocations driven by chemical potential [8]. Properties are improved due to the
formation compound layer (or so called white layer) and the alloy nitride particles in diffusion
zone. CrN and iron nitrides (Fe2-3N and Fe4N) in the compound layer has outstanding
property of hardness [9, 10], and Fe3O4 formed during nitriding shows favorable properties of
corrosion and wear resistance [6].
The hot work tool steel used in this article is a newly developed low carbon steel
25Cr3Mo2NiSiWVNb. Low content of carbon provides excellent toughness. Chromium and
Nickel could enhance the resistance to heat and combustion. Molybdenum carbide generates
dispersion strengthen effect to enhance temper resistance. Appropriate content of niobium
could refine grains to elevate the toughness and to provide more diffusion paths for nitriding
http://dict.youdao.com/search?q=corrosion&keyfrom=E2Ctranslationhttp://dict.youdao.com/w/resistance/
treatment [11]. Bonding force with nitrogen for elements such as Mo, Cr, W, V, Nb is higher
than that with iron, and the nitrides of these elements shows better wear and combustion
resistance [12]. It is worth of studying the phase and other property changes after salt bath
nitriding on this kind of hot wok tool steel for its further use.
2. Experimental
The material used in this work is a low carbon steel 25Cr3Mo2NiSiWVNb with the
chemical composition shown in Table 1. Before salt bath nitriding, the material was quenched
at 980°C and tempered at 650°C. Samples for tests were machined into dimension of 10 mm
× 10 mm × 55 mm with standard Charpy U-notch for impact test and φ20 mm × 5 mm for
other tests. All surfaces of the samples were grinded by silicon carbide paper until 2000#.
Samples were dipped in the molten salt bath in titanium crucible for 4 h at 540°C and 560°C
respectively for nitriding (CNO- concentration of 35%-37%), and immersed in the oxidizing
salt bath at 400°C for 10 min to eliminate the trace amount of cyanogen. After oxidation, the
samples were cooled down slowly in air to room temperature.
Table 1 Chemical composition of work tool steel 25Cr3Mo2NiSiWVNb (wt.%).
C Cr Mo W Ni Nb V Fe
0.2~0.3 2.7~3.5 1.5~2.4 1.1~1.6 1.0~1.5 0.2~0.3 0.1~0.3 Bal.
Cross-sections of nitrided layers etched by nital (4%HNO3+96%ethanol vol.%) were
observed by ZEISS Imager M2m optical microscope and FEI Quanta 250 Environmental
Scanning Electron Microscope (20kV). Phase structures of surface layer were analyzed by the
type Rigaku X-ray diffractometer (Cu Kα radiation, λ=0.15406 nm, working voltage 40kV,
working current 150mA, step size 0.02°). HXD-1000 Vicker Micro-hardness Tester was used
http://dict.youdao.com/w/concentration/
to measure the surface and cross-sectional hardness. Three indentations were made with 300 g
load for 15 s and the average was calculated to determine each hardness value. The
electrochemical characterization was carried out by potentiodynamic polarization test using a
Versa STAT electrochemical workstation. A standard three electrode cell was used which was
comprised by the sample as the working electrode, a saturated calomel electrode as the
reference electrode and a platinum electrode as the counter electrode. The electrolyte used
was 3.5wt.% NaCl solution. Siemens-TD400C pendulum impact testing machine was used for
the impact test and impact fractures were subjected to the same SEM device mentioned above
to reveal the fracture mechanism.
3. Results and discussion
3.1 Microstructure Analysis
Fig. 1 shows the cross-sectional microstructure of samples treated for 4 h at 540°C and
560°C respectively in different magnification. Nitrided layer consists of compound layer and
diffusion zone as shown in Fig. 1 (a) and (d). For sample treated at 540°C, thickness of
compound layer is about 4 µm with signs of non-uniform thickness as is shown in rectangles
in Fig. 1 (a) and (b). A 7-9 µm thick and continuous compound layer accompanied by a 3-5
µm porous layer in Fig. 1 (f) can be got after treated at 560°C. Under the compound layer, it is
diffusion zone which is about 150-180 µm in thickness. There are some alloy nitrides
developed during the treatment in this zone due to the precipitation of nitrides along with
grain boundaries [12, 13], as shown in circles in Fig. 1 (b) (c) (e) and (f).
Fig. 1 Cross-sectional microstructures of 25Cr3Mo2NiSiWVNb nitriding at different
temperatures: (a), (b), (c) at 540°C and (d), (e), (f) at 560°C.
During salt bath nitriding, the inward diffusion of nitrogen and its subsequent actions
with iron and other alloying elements result in the formation of compound layer consisting of
the corresponding nitrides [14]. Thickness of the compound layer and type of nitrides formed
are largely a function of temperature and the nitrogen chemical potential at surface [15-17]. It
can be seen there is an obvious increase in the depths of compound layer when temperature
was elevated from 540°C to 560°C. This layer is composed mainly of ε-phase (Fe2-3N) [18].
The ε-phase shows perfect corrosion resistance and remains bright under the optical
microscope with etch of mild acid. Elevated temperature of the salt bath resulted in high
concentration of nitrogen on the outside of compound layer. The metastable ε-phase
decomposed and nitrogen atoms were released gradually from the compound layer. As
temperature elevating, nitrogen enrichment on the surface of compound layer enhances the
potential for atoms to escape and exacerbate the porosity. So the degree of porosity is more
apparently at 560°C.These factors led to the porous morphology [6, 19], as shown in Fig. 1 (f).
During the treatment, nitrogen atoms mainly diffuse through grain boundaries and
http://dict.youdao.com/search?q=concentration&keyfrom=E2Ctranslation
sub-boundaries [20, 21]. Relatively faster diffusion speed along the grain boundaries
promotes nitrogen enrichment and nitrides precipitation once the solid solubility limit is
exceeded at this sites. Within the diffusion zone, nitrogen atoms combined with the metal
atoms into nitrides which distribute along with original tempered grain boundaries and
sub-boundaries.
3.2 Diffraction Analysis
Fig. 2 gives the phase composition of the surface layer of samples treated at 540°C and
560°C. It can be observed that this layer consisted mainly of ε-phase (Fe2-3N), together with
some Fe3O4 and CrN in agreement to other researchers [6, 14]. Sample treated at 560°C got
more magnetite Fe3O4 after the treatment than that treated at 540°C which would result in
better corrosion resistance.
Fig. 2 X-ray diffraction pattern of samples treated at 540°C and 560°C.
Fig. 3 shows the X-ray diffraction patterns at different depths below the surface of sample
treated at 560°C. Diffraction peaks broadened and their positions shifted after the treatment.
This can be contributed to an increase in the atomic level lattice strain induced during
treatment [10].Optical microscope shows there are a small number of nitride precipitations
along the boundaries in Fig.1, which is too little to show in the diffraction patterns. Compared
with the untreated sample, all the diffraction peak positions in depths of 30 µm, 60 µm and 90
µm below the surface shifted to lower angle in different degrees. The number of solute
nitrogen atoms decreased as the depth increased. So the position shift decreased successively.
This phenomenon coincides with Bragg equation:
2dsinθ=λ
where d is the lattice plane distance, θ is the diffraction angle, λ is the Cu target’s wavelength.
As wavelength is a constant, the lattice plane distance increases with the diffraction angle (i.e.
θ or 2θ) decreases due to the solute atoms. Number of nitrogen atoms in subsurface is more
than that in deep zone, so position shift according to the depth near the subsurface is more
apparent as shown in Fig. 3. Fig. 4 shows the position shift of the main diffraction peaks (α-Fe
(110)) at different depths for samples treated at 540°C and 560°C compared with untreated. It
can be seen that the two curves intersected at about 70 µm below the surface.
Fig. 3 X-ray diffraction patterns of different depths below the surface of sample treated at
560°C compared with the untreated.
Fig. 4 Position shift of the main diffraction peaks (α-Fe (110)) at different depths below the
surface for samples treated at 540°C and at 560°C.
3.3 Micro-hardness
The changes of micro-hardness were shown in Fig. 5 and Fig. 6. Fig. 5 reveals that both
the treated samples were apparently harder than the untreated one. Surface hardness of
untreated is about 355 HV, which increased to 952 HV and 765 HV after the treatment at
540°C and 560°C respectively. As the formation of porous layer in the treatment of 560°C,
the surface hardness is lower than that treated at lower temperature. After polishing away the
porous layer, the hardness increases to 955 HV. Fig. 6 shows the hardness-depth profile. The
result shows exactly the same tendency as the position shift of the main diffraction peaks
shown in Fig. 4. This phenomenon proves the direct relationships among hardness increase,
peak position shift and lattice distortion caused by the solute nitrogen atoms. It was observed
that the curves can be divided into three parts. Within the depth of 70 µm, sample treated at
540°C shows higher hardness than that treated at 560°C. Beyond this depth, the reducing
trend of the hardness curve along thickness for sample treated at 560°C is smaller than that
treated at 540°C. In the depth of about 240 µm, both the curves increasingly coincide and
then become the same as substrate. Case depth is defined as the distance from the surface
where hardness value is 50 units more than the substrate. It can be seen the case depths are
about 150 µm and 180 µm respectively.
Fig. 5 Surface hardness of samples untreated and treated at 540°C and 560°C.
Fig. 6 Variation of cross-sectional hardness of samples treated for 4 h at 540°C and 560°C.
After the treatment, surface hardness increased significantly because of two factors. One
is the formation of high hardness compound layer, second is the heavy lattice distortion
caused by the diffusion of nitrogen atoms. Continuous decrease of hardness from surface to
the substrate reveals the presences of a diffusion zone, where precipitates of nitrides and other
metallic alloys nitrides are formed at the grain boundaries as well as that in the grains.
Nitrides in grains are too small to be observed by OM or low magnification SEM, which
distort the lattice and pin dislocations and thereby increase the hardness [22]. Formation of
compound layer prevents the contact between salt bath medium and the substrate. And the
precipitates formed along boundaries cut down the major diffusion paths. So the number of
active nitrogen atoms diffused from the medium decreases which could not provide enough
support for further diffusion. Then atoms concentrated in the subsurface (10~70 µm of depth
below the surface) became the main source for further diffusion. Nitrogen atoms disintegrated
from the salt bath medium could not penetrate the compound layer to support the further
diffusion. Diffusion rate for nitrogen atoms increased while the temperature was elevated
from 540°C to 560°C, so more active atoms transformed from the subsurface to deeper
substrate. This illustrates the intersection at the depth of about 70 µm in Fig. 6. More active
nitrogen atoms diffused from the subsurface to deeper substrate at 560°C than at 540°C,
which brings about two results. Firstly, the subsurface lost more nitrogen atoms so the lattice
distortion at 560°C is slighter than at 540°C (within 70 µm), which directly influences the
hardness in this section. Secondly, the deeper zone (beyond 70 µm) could get more active
atoms from the subsurface at 560°C, so hardness curves show the opposite result in this
region. Hardness directly reflects the solid solubility of nitrogen atoms and the degree of
lattice distortion in diffusion zone.
3.4 Corrosion Resistance
Results of potentiodynamic corrosion tests of samples are shown in Fig. 7. Current
density no longer increased with potential when they reach to some extent for treated samples.
This means the passivation tendency occurred in anodic polarization. While the anodic
activation still existed for the untreated sample. The corrosion potential (Ecorr) and corrosion
current density (icorr) are shown in Table 2. The corrosion potential increased about 200 mV at
560°C and the current density decreased about 1/100 compared with the untreated sample.
Thus, corrosion resistance was improved apparently by treated at 560 °C. However, sample
treated at 540°C did not show much improvement in corrosion resistance.
Fig. 7 Potentiodynamic polarization curves of samples untreated and treated at 540°C and
560°C.
Table 2 Ecorr and icorr of samples untreated and treated at 540°C and 560°C.
Ecorr/mV icorr/(A·cm-2)
Untreated -441 3.95×10-6
Treated at 540°C -401 2.21×10-6
Treated at 560°C -252 3.88×10-8
Corrosion resistance improvement is attributed to the formation of magnetite Fe3O4 and
compound layer on the surface. Fe3O4 has good chemical stability and ε-phase could prevent
the substrate from the attack of corrosive medium because of the nobility of nitrides [23, 24].
Although porosity and precipitation of CrN would increase pathways for corrosion[14, 25],
sample treated at 560°C shows an excellent corrosion resistance because the formation of
dense and continuous compound layer is more effective than others and more Fe3O4 was
produced during the treatment. The compound layer of the sample treated at 540°C is
non-uniform as shown in Fig. 1, so the corrosive medium could attack the diffusion zone
directly.
3.5 Impact Property
Energy absorbed by the Charpy U-notch samples in the impact test is shown in Table 3. It
can be seen that the energy absorbed is rapidly reduced for samples treated at both
temperatures compared with the untreated one. The impact fracture morphology of the
untreated and treated at 560°C are shown in Fig. 8. Sample treated at 540°C shows similar
morphology as that treated at 560°C. It can be observed that for the untreated sample, there is
an obvious shear lip on the start of the fracture. The fracture shows morphology of ups and
downs in some degree. But for the one after treatment, the fracture is almost completely flat.
The substrate of both samples shows quasi-cleavage fracture. The most obvious contrast
involves the initiation of the fractures. The obvious ductile fracture with a large number of
small dimples appeared in untreated sample, while the entire cleavage fractures in treated
sample because of the hardened nitriding layer.
Table 3 Impact property of samples untreated and treated at 540°C and 560°C.
Property Untreated Treated at 540°C Treated at 560°C
Energy absorbed/J 32.3±1.2 5.2±0.5 5.2±0.3
The process of fracture occurs in four steps with loading: dislocations movement induces
plastic deformation, crack nucleation, crack growth and fracture. For the untreated sample, a
large number of dislocations migrates which induces obvious plastic deformation to show
shear lip at the onset of the fracture. For the treated sample, dislocations are pinned toughly
by the solute nitrogen atoms, so hardly any plastic deformation can be found and a completely
cleavage fracture was observed [8].
Fig. 8 Impact fracture morphologies of 25Cr3Mo2NiSiWVNb (a) untreated and (b) treated at
560°C.
4. Conclusion
A thin Fe3O4-phase film, compound layer (consist of ε-phase and CrN) and diffusion
zone formed on the surface of 25Cr3Mo2NiSiWVNb after the salt bath nitriding and
post-oxidation, which increased the surface hardness to above 950HV from 355 HV. In the
diffusion zone, solution nitrogen atoms caused diffraction peaks broadened and their positions
shifted to lower angle in different degrees at different depths, which showed the same
tendency as hardness profile curves. Strengthened surface deteriorated impact property
seriously after the salt bath nitriding.
Thickness and porosity of compound layer expanded with the nitriding temperature
increasing from 540°C to 560°C. Sample treated at 560°C got more homogeneous compound
layer and more Fe3O4-phase, and it showed the best corrosion resistance among the untreated
and treated samples.
Acknowledgment
We grateful acknowledge the Chengdu Surface Metal Technology Co. Ltd. for their
facility support of this research work.
References:
1 L. B. Winck, J. L. A. Ferreira, J. A. Araujo, M. D. Manfrinato, C. R. M. da Sliva, Surface
nitriding influence on the fatigue life behavior of ASTM A743 steel type CA6NM, Surf.
Coat. Technol. 232 (2013) 844-850.
2 R. B. Huang, J. Wang, S. Zhong, M. X. Li, J. Xiong, H. Y. Fan, Surface modification of
2205 duplex stainless steel by low temperature salt bath nitrocarburizing at 430°C, Appl.
Surf. Sci. 271 (2013) 93-97.
3 M. L. Fares, M. Z. Touhami, M. Belaid, H. Bruyas, Surface characteristics analysis of
nitrocarburized (Tenifer) and carbonitrided industrial steel AISI 02 types, Surf. Interface
Anal. 41 (2009) 179-186.
4 H. Nagamatsu, R. Ichiki, Y. Yasumatsu, T. Inoue, M. Yoshida, S. Akamine, S. Kanazawa,
Steel nitriding by atmospheric-pressure plasma jet using N2-H2 mixture gas, Surf. Coat.
Technol. 225 (2013) 26-33.
5 G. J. Li, Q. Peng, C. Li, Y. Wang, J. Gao, S. Y. Chen, J. Wang, B. L. Shen, Microstructure
analysis of 304L austenitic stainless steel by QPQ complex salt bath treatment, Mater.
Charact. 59 (2008) 1359-1363.
6 W. Cai, F. N. Meng, X. Y. Gao, J. Hu, Effect of QPQ nitriding time on wear and corrosion
behavior of 45 carbon steel, Appl. Surf. Sci. 261 (2012) 411-414.
7 G. J. Li, J. Wang, Q. Peng, C. Li, Y. Wang, B. L. Shen, Influence of salt bath
nitrocarburizing and post-oxidation process on surface microstructure evolution of
17-4PH stainless steel. J. Mater. Process. Technol. 207 (2008) 187-192.
8 J. Vatavuk, L. C. F. Canale, G. E. Totten, S. G. Cardoso, The effect of nitriding on the
toughness and bending resistance of tool steels, Int. J. Microstruct. Mater. Prop. 3 (2008)
563-575.
9 J. Alphonsa, B. A. Padsala, B. J. Chauhan, G. Jhala, P. A. Rayjada, N. Chauhan, S. N.
Soman, P. M. Raole, Plasma nitriding on welded joints of AISI 304 stainless steel, Surf.
Coat. Technol. 228 (2013) S306-S311.
10 T. Balusamy, T. S. N. Sankara Narayanana, K. Ravichandran, I. S. Parkc, M. H. Lee,
Plasma nitriding of AISI 304 stainless steel: Role of surface mechanical attrition
treatment, Mater. Charact. 85 (2013) 38-47.
11 F.B. Pickering, Physical metallurgy and the design of steels, London, Applied Science
Publishers Ltd, 1978.
12 F. Lantelme, H. Groult, H. Mosqueda, P. L. Magdinier, H. Chavanne, V. Monteux, P.
Maurin-Perrier, Molten Salts Chemistry, Elsevier Inc., 2013.
13 Y. Birol, Response to thermal cycling of plasma nitrided hot work tool steel at elevated
temperatures, Surf. Coat. Technol. 205 (2010) 597-602.
14 R. L. O. Basso, R. J. Candal, C. A. Figueroa, D. Wisnivesky, F. Alvarez, Influence of
microstructure on the corrosion behavior of nitrocarburized AISI H13 tool steel obtained
by pulsed DC plasma, Surf. Coat. Technol. 203 (2009) 1293-1297.
15 H. Y. Li, D. F. Luo, C. F. Yeung, K. H. Lau, Microstructural studies of QPQ complex salt
bath heat-treated steels, J. Mater. Process. Technol. 69 (1997) 45-49.
16 F. Borgioli, A. Fossati, E. Galvanetto, T. Bacci, Glow-discharge nitriding of AISI 316L
austenitic stainless steel: influence of treatment temperature, Surf. Coat. Technol. 200
(2005) 2470-2480.
17 Z. S. Zhou, M. Y. Dai, Z. Y. Shen, J. Hua, Effect of D.C. electric field on salt bath
nitriding for 35 steel and kinetics analysis, J. Alloys Compd. 623 (2015) 261-265.
http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068http://www.sciencedirect.com/science/article/pii/B9780123985385000068
18 L. Wang, X. L. Xu, XTEM and XPS studies of plasma nitrocarburising layers on 0.45% C
steel, Surf. Coat. Technol. 126 (2000) 288-293.
19 W. Schröter; A. Spengler, Beitrag zum Erkenntnisstand der Porenentstehung bei der
Schichtbildung durch Stickstoff in Eisenwerkstoffen, Tagungsband der
ATTT/AWT-Tagung, Aachen, 2002, S 35-49.
20 S. M. Hassani-Gangaraj, A. Moridi, M. Guagliano, A. Ghidini, Nitriding duration
reduction without sacrificing mechanical characteristics and fatigue behavior: The
beneficial effect of surface nano-crystallization by prior severe shot peening, Mater. Des.
55 (2014) 492-498.
21 W. P. Tong, N. R. Tao, Z. B. Wang, J. Lu, K. Lu, Nitriding iron at lower temperature, Sci.
299 (2003) 686-688.
22 J. O Brien M, D. Goodman, Plasma (Ion) Nitriding, ASM Handbook, vol. 4, American
Society for Metals, Metals Park, OH, 1991
23 A. Basu, J. D. Majumdar, J. Alphonsa, S. Mukherjee, I. Manna, Corrosion resistance
improvement of high carbon low alloy steel by plasma nitriding, Mater. Lett. 62 (2008)
3117-3120.
24 K. Köster, P. Kaestner, G. Bräuer, H. Hoche, T. Troßmann, M. Oechsner, Material
condition tailored to plasma nitriding process for ensuring corrosion and wear resistance
of austenitic stainless steel, Surf. Coat. Technol. 228 (2013) S615-S618.
25 R. L. O. Basso, H. O. Pastore, V. Schmidt, I. J. R. Baumvol, S. A. C. Abarca, F. S. de
Souza, A. Spinelli, C. A. Figueroa , C. Giacomelli, Microstructure and corrosion
behaviour of pulsed plasma-nitrided AISI H13 tool steel, Corros. Sci. 52 (2010)
3133-3139.