Heat Treatment: Lecture Q&P, M3 concept

Post on 16-Apr-2017

707 views 1 download

transcript

1

1. Schaeffler diagram2. M3 Concept 3. Quenching & Partitioning Heat Treatments

Lecture Series- C

2

• The Schaeffler diagram is an important tool for predicting the constitution

of austenitic Cr-Ni steel welds with carbon contents up to 0.12%. However,

it does not allow determination of the composition and volume

• of the carbide phase.

• This Schaeffler diagram is especially suited to weld metals in order to

predict the structure.

 Schaeffler diagram

Schaeffler and Delong diagrams are used to predict structure on the basis of alloying elements. (Stainless Steel Weld) Plots the compositional limits at room temperature of austenite, ferrite and martensite, in terms of nickel and chromium equivalents The Cr and Ni equivalent can be empirically determined as:

Cr equivalent = (Cr) + 2(Si) + 1.5(Mo) + 5(V) + 5.5(Al) + 1.75(Nb) + 1.5(Ti) + 0.75(W)

Ni equivalent = (Ni) + (Co) + 0.5(Mn) + 0.3(Cu) + 25(N) + 30(C)

4

Chrome and nickel are among the most important alloying elements here. All ferrite formers have a chromium equivalent and all austenite formers a nickel equivalent.

 Schaeffler diagram

 Modified Schaeffler diagram

Delong modified the schaeffler diagram Ferrite No.(FN) is also plotted on schaeffler diagramWidely use in predicting phase-structure in weld metal Also include calculation of volume and composition of carbide phase

 Modified Schaeffler diagram FN can be roughly determine by:

FN = 3.34 Creq – 2.46 Nieq – 28.6

--> FN between 3-7 (max.) is preferredSolidification mode of S.S. during casting or welding can be predicted roughly as under:

Creq/Nieq < 1.5 (Austenitic)

Creq/Nieq > 2.0 (Ferritic)

In b/w 1.5 and 2.0 is the mixed structure

8

 Schaeffler-Delong diagram

FN = Ferrite No.

Low %ferrite leads to solidification cracking in weld metal, but low %ferrite render/reduce Stainless steel more corrosion resistant

 Schaeffler-Delong diagram

M3 Concept

12

• The performance of steel products is closely related to the constitutes and morphology of microstructures.

• The characterization and effective control of microstructure are now from micron scale to nano scale steadily (to be in nano order).

• The properties have been raised from the order of 106 to 109 unit (to be in Giga order).

Future Perspective of Steels

Future Perspective

TensileStrength

FatigueStrength

Fatiguecycles

Creep strength

Improved from MPa to GPa order

Improved from MPa to GPa order

Improved from Mega cyles to Gega

Cycles

Improved from Mega secs to

Giga secs

Third Generation Steels

Toughness ≥ 200 J

Ductility ‘A’ ≥ 20 %

Y.S. ≥ 800-1000 MPa

Target Values

Mass production on existing mills !

M3 Concept

Fig. – The performance of steels are associated with the microstructure, characterized by Multi-phase, Meta-stability and Multi-scale

M3 Concept

Multi-phase

Meta-stability

Multi-scale

Mixture ofBainite,

Martensite,Retained austenite

Stability of austeniteStrain-induced

Martensite (SIM)

UFG, Ultra Fine GrainNano-laths martensite

Nano-Bainite

M3 ConceptSchematic of Research Targets and Future Directions

Third generation AHSS with improvednductility and reduced cost. Third generation martensitic steels for improved creep strength.

18

Quenching & Partitioning Heat Treatments

Quenching & PartitioningA Novel method, proposed by G. Speer, for the development of multiphase

steels with considerable retention of austenite in the microstructure.

The Q&P process consists of a first quench (quenching step) to a

temperature below the Ms but above the Mf to form a mixture of martensite

and austenite.

Subsequent isothermal treatment (partitioning step) at the same

temperature (one-step treatment) or at a higher temperature (two step

treatment), in order to transfer the C from the supersaturated αM into the γ.

Final structure = Decarburized (carbon depleted) martensite + C enriched

austenite + Fresh martensite.

Quenching & Partitioning

Fig. – Schematic representation of One and Two step Q&P process

Quenching & PartitioningIn addition to carbon partitioning into austenite,other processes that could occur during the ‘‘partitioning’’ step are:

Tempering of Martensite Carbon trapping at dislocations and interfaces in the martensite Formation of carbides (both transition carbides and/or cementite) Decomposition of the austenite to bainite or other transformation

productsCompetition occurs b/w theses processes.*Bainite has been recognized as a potential constituent particularly at increased quench temperatures where the amount of martensite is limited and bainite transformation kinetics are more rapid than at a lower temperature.

Quenching & Partitioning

Fresh martensite is formed after quenching from partitioning temperature to

room temperature, b/c of unstable austenite.

This microstructure can lead to an interesting combination of mechanical

properties.

Good formability, as a result of the TRIP effect from the retained austenite,

and a strength higher than that of conventional TRIP steels due to martensite.

Q&P – Design Requirements

(a) Absence of ferrite and/or pearlite formation during the quenching step.

(b) Retardation or inhibition of bainite formation, in order to minimize possible overlapping of carbon partitioning and formation of bainite.

(c) Retardation or minimization of the precipitation of carbides, which consumes carbon that is then no longer available for carbon enrichment of the austenite.

(d) A sufficiently high carbon content for thermal stabilization of a considerable fraction of retained austenite at room temperature.

Q&P Steel - MicrostructuresFig. - Light optical micrograph of Q&P microstructure in AISI 9260 steel quenched to 190°C and partitioned at 400°C. Nital etch; retained austenite appears white.

Fig. – SEM micrograph showing blocky austenite within the martensite matrix formed during Q&P heat treatment.

Q&P Steel - Microstructures

Fig. - Field emission scanning electron micrographs of medium carbon low alloy steel samples quenched at 180 ◦C, partitioned at 300 ◦C for (a) 30 s (b) 120 s and (c) 900 s respectively.

Q&P Steels - Properties

Fig. - Comparison of impact toughness at room temperature between Q&P and Q&T at various partitioning (or tempering) temperatures.

Q&P Steels - Properties

Fig. - Comparison of the engineering stress-strain curves and strain hardening of Q&P and Q&T