SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
C 1/2Mo Steel, e.g. ASTM A-182 F1 & ASTMA-204 B.
Material Specification(typical)
FILLER METAL
593-718 CTemperature Range
1 hr/25mm WT, 1 hr minimum.Time Range
222 C/hr/25mm WTHeating Rate
278 C/hr/25mm WTCooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P3-3WPS No. 0WPS Revision No.
10 C For WT less than 12.7mm79 C For WT equal to or greater than 12.7mm
Preheat Temp.
Interpass Temp.
BM Thickness Range:
3 P-No.BASE METAL
TON/A Group3P-No. N/AGroup
4.8-203mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-D2ER80S-D2E7018-A1E7018-A1
2.42.43.23.2
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
10 deg -/+ 2.5
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
12-1712-1720-2520-25
100-155100-15590-16090-160
3.8-8.93.8-8.93.8-125-10.2
Spec. No. (SFA) A5.28 A5.5
AWS No. (Class.) ER80S-D2 E7018-A1
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 12.2mm 203mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
Not in stockSAMS S/N 20-483-089
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P3-3
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design is for BM thickness greater than 22mm.Other
*Mandatory above 427 COther
Recommended GTAW wire is METRODE MnMoOther
NoneOther
1 of 2Page
315 C Maximum.
Jun 5, 2000
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4, 5, 6, 7, 8, 9 & 10 represent Fill2.3. Fill1 or Fill2 application may be waived. However, this will be generally controlled by the BM thicknessand the user's decision.4. The bead sequence shown in the drawing is recommended but not mandatory.5. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111222
RootFill1Fill2CapFill1Fill2Cap
GTAWGTAWSMAWSMAWGTAWSMAWSMAW
ER80S-D2ER80S-D2E7018-A1E7018-A1ER80S-D2E7018-A1E7018-A1
2.42.43.23.22.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
ER80S-D2ER80S-D2E7018-A1E7018-A1
2.42.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
2.42.43.23.2
ER80S-D2ER80S-D2E7018-A1E7018-A1
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
22.5 deg -0/+ 2.5
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is optional depending upon thepenetration & quality of the root pass back side.
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
A=
B=
C=
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
Other Dimensions/Comments:
A=
B=
C=
D=
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Other Dimensions/Comments:See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
SPECIFIC INSTRUCTIONS & DETAILS
12-1712-1720-2520-2512-1720-2520-25
VOLT.
100-155100-15590-16090-160
100-15590-16090-160
AMP.
DCSPDCSPDCRPDCRPDCSPDCRPDCRP
3.8-8.93.8-8.93.8-125-10.23.8-8.93.8-125-10.2
DCSPDCSPDCRPDCRP
POL.
12-1712-1720-2520-25
VOLT.
100-155100-15590-16090-160
AMP.
2.5-7.53.8-8.93.8-125-10.2
TRAVEL SPEED(cm/min)
DCSPDCRPDCRPDCRP
12-1712-1720-2520-25
100-155100-15590-16090-160
2.5-7.53.8-8.93.8-125-10.2
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Alternative recommended joint design for BM thickness greater than 22mm.
Recommended joint design for BM thickness equal to or less than 22mm.
Other
Other
Other Recommended joint design for branch connection.
P3-3WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P3-3 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
C 1/2Mo Steel, e.g. ASTM A-182 F1 & ASTMA-204 B.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P3-1WPS No. 0WPS Revision No.
10 C For WT less than 12.7mm79 C For WT equal to or greater than 12.7mm
Preheat Temp.
Interpass Temp.
BM Thickness Range:
3 P-No.BASE METAL
TON/A Group3P-No. N/AGroup
1.6-19mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-D2ER80S-D2ER80S-D2
2.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAW
111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
12-1513-1713-16
105-130115-155115-155
3.8-5.73.8-8.93.8-8.9
Spec. No. (SFA) A5.28
AWS No. (Class.) ER80S-D2
Size of Filler Metals 2.4mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
Not in stockSAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P3-1
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
Recommended GTAW wire is METRODE MnMoOther
NoneOther
1 of 2Page
315 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111
RootFillCap
GTAWGTAWGTAW
ER80S-D2ER80S-D2ER80S-D2
2.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
12-1513-1713-16
VOLT.
105-130115-155115-155
AMP.
DCSPDCSPDCSP
3.8-5.73.8-8.93.8-8.9
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P3-1WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P3-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
N/ATungsten Electrode Size and Type N/AOrifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
NoneShielding Gas (Type)
N/AFlow Rate
POST WELD HEAT TREATMENT
C 1/2Mo Steel, e.g. ASTM A-182 F1 & ASTMA-204 B.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P3-2WPS No. 0WPS Revision No.
10 C For WT less than 12.7mm79 C For WT equal to or greater than 12.7mm
Preheat Temp.
Interpass Temp.
BM Thickness Range:
3 P-No.BASE METAL
TON/A Group3P-No. N/AGroup
1.6-19mmGroove
UnlimitedFillet
50.8mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
E7018-A1E7018-A1E7018-A1E7018-A1E7018-A1
3.23.23.23.23.2
A =
B =
C =
D =
SMAWSMAWSMAWSMAWSMAW
11122
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFillCapFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCRPDCRPDCRPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
19-2419-2419-2419-2419-24
90-16090-16090-16090-16090-160
12.7-17.86.4-11.47.6-12.76.4-11.47.6-12.7
Spec. No. (SFA) A5.5
AWS No. (Class.) E7018-A1
Size of Filler Metals 3.2mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-483-089SAMS S/N
PQR Revision No. 0
Root Pass V-Down or V-Up
Arc Air and/or GrindingMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P3-2
Refer to table IV.1 for complete listing of materials.Other
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
11122
RootFillCapFillCap
SMAWSMAWSMAWSMAWSMAW
E7018-A1E7018-A1E7018-A1E7018-A1E7018-A1
3.23.23.23.23.2
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
None
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
19-2419-2419-2419-2419-24
VOLT.
90-16090-16090-16090-16090-160
AMP.
DCRPDCRPDCRPDCRPDCRP
12.7-17.86.4-11.47.6-12.76.4-11.47.6-12.7
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P3-2WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P3-2 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
1-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 11 Cl.1 & ASTM A-335 P11.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P4-1WPS No. 0WPS Revision No.
149 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
4 P-No.BASE METAL
TO1 Group4P-No. 1Group
1.6-19mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B2ER80S-B2ER80S-B2
2.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAW
111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank X Structural
SIDE
RootFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
13-1614-1814-18
100-130115-155115-155
3.8-6.43.8-6.43.8-6.4
Spec. No. (SFA) A5.28
AWS No. (Class.) ER80S-B2
Size of Filler Metals 2.4mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-504-615SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P4-1
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Apr 9, 2001
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111
RootFillCap
GTAWGTAWGTAW
ER80S-B2ER80S-B2ER80S-B2
2.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
13-1614-1814-18
VOLT.
100-130115-155115-155
AMP.
DCSPDCSPDCSP
3.8-6.43.8-6.43.8-6.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P4-1WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P4-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
N/ATungsten Electrode Size and Type N/AOrifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
NoneShielding Gas (Type)
N/AFlow Rate
POST WELD HEAT TREATMENT
1-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 11 Cl.1 & ASTM A-335 P11.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P4-2WPS No. 0WPS Revision No.
149 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
4 P-No.BASE METAL
TO1 Group4P-No. 1Group
1.6-19mmGroove
UnlimitedFillet
50.8mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
E8018-B2E8018-B2E8018-B2E8018-B2E8018-B2
3.23.23.23.23.2
A =
B =
C =
D =
SMAWSMAWSMAWSMAWSMAW
11122
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank X Structural
SIDE
RootFillCapFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCRPDCRPDCRPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
19-2419-2419-2419-2419-24
90-16090-16090-16090-16090-160
12.7-17.87.6-14
5.7-11.47.6-14
5.7-11.4
Spec. No. (SFA) A5.5
AWS No. (Class.) E8018-B2
Size of Filler Metals 3.2mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-484-253SAMS S/N
PQR Revision No. 0
Root Pass V-Down or V-Up
Arc Air and/or GrindingMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P4-2
Refer to table IV.1 for complete listing of materials.Other
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Apr 9, 2001
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
11122
RootFillCapFillCap
SMAWSMAWSMAWSMAWSMAW
E8018-B2E8018-B2E8018-B2E8018-B2E8018-B2
3.23.23.23.23.2
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
None
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
19-2419-2419-2419-2419-24
VOLT.
90-16090-16090-16090-16090-160
AMP.
DCRPDCRPDCRPDCRPDCRP
12.7-17.87.6-14
5.7-11.47.6-14
5.7-11.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P4-2WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P4-2 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
1-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 11 Cl.1 & ASTM A-335 P11.
Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WTHeating Rate
278 C/hr/25mm WTCooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P4-3WPS No. 0WPS Revision No.
149 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
4 P-No.BASE METAL
TO1 Group4P-No. 1Group
4.8-203mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B2ER80S-B2E8018-B2E8018-B2
2.42.43.23.2
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
10 deg -/+ 2.5
Application: Piping X Pipeline Pressure Vessel X Tank X Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
13-1913-1920-2620-25
95-16095-16090-16090-160
4.4-74.4-7
3.8-10.85-10.2
Spec. No. (SFA) A5.28 A5.5
AWS No. (Class.) ER80S-B2 E8018-B2
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 10.2mm 203mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-615SAMS S/N 20-484-523
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P4-3
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design is for BM thickness greater than 22mm.Other
*Mandatory above 427 COther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4, 5, 6, 7, 8, 9 & 10 represent Fill2.3. Fill1 or Fill2 application may be waived. However, this will be generally controlled by the BM thicknessand the user's decision.4. The bead sequence shown in the drawing is recommended but not mandatory.5. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111222
RootFill1Fill2CapFill1Fill2Cap
GTAWGTAWSMAWSMAWGTAWSMAWSMAW
ER80S-B2ER80S-B2E8018-B2E8018-B2ER80S-B2E8018-B2E8018-B2
2.42.43.23.22.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
ER80S-B2ER80S-B2E8018-B2E8018-B2
2.42.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
2.42.43.23.2
ER80S-B2ER80S-B2E8018-B2E8018-B2
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
22.5 deg -0/+ 2.5
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is optional depending upon thepenetration & quality of the root pass back side.
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
A=
B=
C=
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
Other Dimensions/Comments:
A=
B=
C=
D=
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Other Dimensions/Comments:See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
SPECIFIC INSTRUCTIONS & DETAILS
13-1913-1920-2620-2513-1920-2620-25
VOLT.
100-165100-16590-16090-160
100-15590-16090-160
AMP.
DCSPDCSPDCRPDCRPDCSPDCRPDCRP
4.4-74.4-7
3.8-10.85-10.24.4-7
3.8-10.85-10.2
DCSPDCSPDCRPDCRP
POL.
13-1913-1920-2620-25
VOLT.
100-165100-16590-16090-160
AMP.
4.4-74.4-7
3.8-10.85-10.2
TRAVEL SPEED(cm/min)
DCSPDCRPDCRPDCRP
13-1913-1920-2620-25
100-165100-16590-16090-160
2.5-7.53.8-8.9
3.8-10.85-10.2
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Alternative recommended joint design for BM thickness greater than 22mm.
Recommended joint design for BM thickness equal to or less than 22mm.
Other
Other
Other Recommended joint design for branch connection.
P4-3WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P4-3 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
2-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 P22 &ASTM A-335 P22.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5A-1WPS No. 0WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5A P-No.BASE METAL
TON/A Group5AP-No. N/AGroup
1.6-19mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER90S-B3ER90S-B3ER90S-B3
2.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAW
111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
13-1614-1814-18
100-130115-155115-155
3.8-6.43.8-6.43.8-6.4
Spec. No. (SFA) A5.28
AWS No. (Class.) ER90S-B3
Size of Filler Metals 2.4mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-504-625SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5A-1
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Sep 2, 2000
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111
RootFillCap
GTAWGTAWGTAW
ER90S-B3ER90S-B3ER90S-B3
2.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
13-1614-1814-18
VOLT.
100-130115-155115-155
AMP.
DCSPDCSPDCSP
3.8-6.43.8-6.43.8-6.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5A-1WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P5A-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
N/ATungsten Electrode Size and Type N/AOrifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
NoneShielding Gas (Type)
N/AFlow Rate
POST WELD HEAT TREATMENT
2-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 P22 &ASTM A-335 P22.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5A-2WPS No. 0WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5A P-No.BASE METAL
TON/A Group5AP-No. N/AGroup
1.6-19mmGroove
UnlimitedFillet
50.8mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
E9018-B3E9018-B3E9018-B3E9018-B3E9018-B3
3.23.23.23.23.2
A =
B =
C =
D =
SMAWSMAWSMAWSMAWSMAW
11122
None
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFillCapFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCRPDCRPDCRPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
19-2419-2419-2419-2419-24
90-16090-16090-16090-16090-160
12.7-17.86.4-11.47.6-12.76.4-11.47.6-12.7
Spec. No. (SFA) A5.5
AWS No. (Class.) E9018-B3
Size of Filler Metals 3.2mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-484-594SAMS S/N
PQR Revision No. 0
Root Pass V-Down or V-Up
Arc Air and/or GrindingMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5A-2
Refer to table IV.1 for complete listing of materials.Other
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
11122
RootFillCapFillCap
SMAWSMAWSMAWSMAWSMAW
E9018-B3E9018-B3E9018-B3E9018-B3E9018-B3
3.23.23.23.23.2
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
None
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
19-2419-2419-2419-2419-24
VOLT.
90-16090-16090-16090-16090-160
AMP.
DCRPDCRPDCRPDCRPDCRP
12.7-17.86.4-11.47.6-12.76.4-11.47.6-12.7
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5A-2WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P5A-2 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
2-1/4Cr 1/2Mo Steel, e.g. ASTM A-387 P22 &ASTM A-335 P22.
Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WTHeating Rate
278 C/hr/25mm WTCooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5A-3WPS No. 0WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5A P-No.BASE METAL
TON/A Group5AP-No. N/AGroup
4.8-203mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER90S-B3ER90S-B3E9018-B3E9018-B3
2.42.43.23.2
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
10 deg -/+ 2.5
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
13-1913-1920-2620-25
95-16095-16090-16090-160
4.4-74.4-7
3.8-10.85-10.2
Spec. No. (SFA) A5.28 A5.5
AWS No. (Class.) ER90S-B3 E9018-B3
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 10.2mm 203mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-625SAMS S/N 20-484-594
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5A-3
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design is for BM thickness greater than 22mm.Other
*Mandatory above 427 COther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Sep 2, 2000
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4, 5, 6, 7, 8, 9 & 10 represent Fill2.3. Fill1 or Fill2 application may be waived. However, this will be generally controlled by the BM thicknessand the user's decision.4. The bead sequence shown in the drawing is recommended but not mandatory.5. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111222
RootFill1Fill2CapFill1Fill2Cap
GTAWGTAWSMAWSMAWGTAWSMAWSMAW
ER90S-B3ER90S-B3E9018-B3E9018-B3ER90S-B3E9018-B3E9018-B3
2.42.43.23.22.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
ER90S-B3ER90S-B3E9018-B3E9018-B3
2.42.43.23.2
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
2.42.43.23.2
ER90S-B3ER90S-B3E9018-B3E9018-B3
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
22.5 deg -0/+ 2.5
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is optional depending upon thepenetration & quality of the root pass back side.
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
A=
B=
C=
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
Other Dimensions/Comments:
A=
B=
C=
D=
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Other Dimensions/Comments:See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
SPECIFIC INSTRUCTIONS & DETAILS
13-1913-1920-2620-2513-1920-2620-25
VOLT.
100-165100-16590-16090-160
100-15590-16090-160
AMP.
DCSPDCSPDCRPDCRPDCSPDCRPDCRP
4.4-74.4-7
3.8-10.85-10.24.4-7
3.8-10.85-10.2
DCSPDCSPDCRPDCRP
POL.
13-1913-1920-2620-25
VOLT.
100-165100-16590-16090-160
AMP.
4.4-74.4-7
3.8-10.85-10.2
TRAVEL SPEED(cm/min)
DCSPDCRPDCRPDCRP
13-1913-1920-2620-25
100-165100-16590-16090-160
2.5-7.53.8-8.9
3.8-10.85-10.2
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Alternative recommended joint design for BM thickness greater than 22mm.
Recommended joint design for BM thickness equal to or less than 22mm.
Other
Other
Other Recommended joint design for branch connection.
P5A-3WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P5A-3 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
5Cr 1/2Mo Steel, e.g. ASTM A-213 T5 &ASTM A-335 P5.
Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WT*Heating Rate
278 C/hr/25mm WT*Cooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5B-1WPS No. 1WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5B P-No.BASE METAL
TON/A Group5BP-No. N/AGroup
4.8-22.0mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B6ER80S-B6ER80S-B6ER80S-B6
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAWGTAW
1111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
13-1712-1913-1815-19
110-150100-185130-185135-175
3.8-6.44.4-74.4-74.4-7
Spec. No. (SFA) A5.28
AWS No. (Class.) ER80S-B6
Size of Filler Metals 2.4mm
Max. Deposit Thickness 4.8-22.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-504-641SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5B-1
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
*Mandatory above 427 COther
This GTAW wire was formerly classified ER502Other
NoneOther
1 of 2Page
315 C Maximum.
Sep 2, 2000
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4, 5, 6, 7 & 8 represent Fill2.3. Fill1 or Fill2 application may be waived. However, this will be generally controlled by the BM thicknessand the user's decision.4. The bead sequence shown in the drawing is recommended but not mandatory.5. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootFill1Fill2Cap
GTAWGTAWGTAWGTAW
ER80S-B6ER80S-B6ER80S-B6ER80S-B6
2.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
13-1712-1913-1815-19
VOLT.
110-150100-185130-185135-175
AMP.
DCSPDCSPDCSPDCSP
3.8-6.44.4-74.4-74.4-7
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5B-1WPS No. 1WPS Revision No. PQR Revision No. 0PQR No. P5B-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
5Cr 1/2Mo Steel, e.g. ASTM A-213 T5 &ASTM A-335 P5.
Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WT*Heating Rate
278 C/hr/25mm WT*Cooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5B-2WPS No. 1WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5B P-No.BASE METAL
TON/A Group5BP-No. N/AGroup
4.8-22.0mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B6ER80S-B6E8015-B6E8015-B6
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
13-1712-1625-3325-31
110-140110-140
55-9055-90
3.8-6.44.4-74.4-74.4-7
Spec. No. (SFA) A5.9 A5.5
AWS No. (Class.) ER80S-B6 E8015-B6
Size of Filler Metals 2.4mm 2.4mm
Max. Deposit Thickness 3.4mm 16.6mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-641SAMS S/N 20-484-684
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5B-2
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
*Mandatory above 427 COther
GTAW wire & SMAW electrode were formerly classified ER502 & E502-15Other
NoneOther
1 of 2Page
315 C Maximum.
Mar 24, 2001
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4 & 5 represent Fill2.3. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
ER80S-B6ER80S-B6E8015-B6E8015-B6
2.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
13-1712-1625-3325-31
VOLT.
110-140110-140
55-9055-90
AMP.
DCSPDCSPDCRPDCRP
3.8-6.44.4-74.4-74.4-7
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5B-2WPS No. 1WPS Revision No. PQR Revision No. 0PQR No. P5B-2 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
9Cr 1Mo Steel, e.g. ASTM A-213 T9 & ASTMA-335 P9.
Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WT*Heating Rate
278 C/hr/25mm WT*Cooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5B-3WPS No. 1WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5B P-No.BASE METAL
TON/A Group5BP-No. N/AGroup
4.8-22.0mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B8ER80S-B8ER80S-B8ER80S-B8
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAWGTAW
1111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
13-1710-1714-1815-19
105-145110-155115-165130-175
3.8-6.43.8-7.63.8-7.63.8-6.4
Spec. No. (SFA) A5.28
AWS No. (Class.) ER80S-B8
Size of Filler Metals 2.4mm
Max. Deposit Thickness 22.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
Not in Stock.SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5B-3
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
*Mandatory above 427 COther
This GTAW wire was formerly classified ER505 ( it is METRODE 9CRMO TIG)Other
NoneOther
1 of 2Page
315 C Maximum.
Sep 2, 2000
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4, 5, 6, 7 & 8 represent Fill2.3. Fill1 or Fill2 application may be waived. However, this will be generally controlled by the BM thicknessand the user's decision.4. The bead sequence shown in the drawing is recommended but not mandatory.5. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootFill1Fill2Cap
GTAWGTAWGTAWGTAW
ER80S-B8ER80S-B8ER80S-B8ER80S-B8
2.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
13-1710-1714-1815-19
VOLT.
105-145110-155115-165130-175
AMP.
DCSPDCSPDCSPDCSP
3.8-6.43.8-7.63.8-7.63.8-6.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5B-3WPS No. 1WPS Revision No. PQR Revision No. 0PQR No. P5B-3 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
100% ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
9Cr 1Mo Steel, e.g. ASTM A-213 T9 & ASTM A-335 P9.Material Specification(typical)
FILLER METAL
704-746 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WT*Heating Rate
278 C/hr/25mm WT*Cooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P5B-4WPS No. 1WPS Revision No.
177 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
5B P-No.BASE METAL
TON/A Group5BP-No. N/AGroup
4.8-22.0mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
4-7 l/minGas Backing Flow Rate
100% ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER80S-B8ER80S-B8
E8015-B8E8015-B8
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFill1Fill2Cap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
11-1411-1523-3023-29
90-120100-13060-10075-105
7.6-12.23.8-6.45-12.73.8-8.9
Spec. No. (SFA) A5.28 A5.5
AWS No. (Class.) ER80S-B8 E8015-B8
Size of Filler Metals 2.4mm 2.4mm
Max. Deposit Thickness 4.8mm 17.2mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
Not in Stock.SAMS S/N Not in Stock.
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P5B-4
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt weld.Other
*Mandatory above 427 COther
GTAW wire is METRODE 9CRMO TIG, SMAW electrode is METRODE CHROMET9Other
NoneOther
1 of 2Page
315 C Maximum.
Mar 24, 2001
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. Fill passes 2 & 3 represent Fill1.2. Fill passes 4 & 5 represent Fill2.3. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootFill1Fill2Cap
GTAWGTAWSMAWSMAW
ER80S-B8ER80S-B8
E8015-B8E8015-B8
2.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
11-1411-1523-3023-29
VOLT.
90-120100-13060-10075-105
AMP.
DCSPDCSPDCRPDCRP
7.6-12.23.8-6.45-12.73.8-8.9
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P5B-4WPS No. 1WPS Revision No. PQR Revision No. 0PQR No. P5B-4 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
N/ATungsten Electrode Size and Type N/AOrifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
NoneShielding Gas (Type)
N/AFlow Rate
POST WELD HEAT TREATMENT
Martensitic Stainless Steel, e.g. ASTM A-240type 410 & ASTM A-182 F6NM.
Material Specification(typical)
FILLER METAL
732-788 CTemperature Range
1 hr/25mm WT, 2 hr minimum.Time Range
222 C/hr/25mm WT*Heating Rate
278 C/hr/25mm WT*Cooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P6-1WPS No. 0WPS Revision No.
149 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
6 P-No.BASE METAL
TON/A Group6P-No. N/AGroup
4.8-50.8mmGroove
UnlimitedFillet
50.8mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
E410E410E410E410E410
3.23.23.23.23.2
A =
B =
C =
D =
SMAWSMAWSMAWSMAWSMAW
11122
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
22.5 deg -0/+ 2.5
Application: Piping X Pipeline Pressure Vessel X Tank Structural
SIDE
RootFillCapFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness 0 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCRPDCRPDCRPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
23-2921-2719-2521-2719-25
115-150105-14595-135
105-14595-135
8.9-143.6-10.23.6-8.9
3.6-10.23.6-8.9
Spec. No. (SFA) A5.4
AWS No. (Class.) E410
Size of Filler Metals 3.2mm
Max. Deposit Thickness 50.8mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-487-010SAMS S/N
PQR Revision No. 0
Root Pass V-Down or V-Up
Arc Air and/or GrindingMethod of Backgouging N/AContact Tube to Work Distance
PQR No. P6-1
Refer to table IV.1 for complete listing of materials.Other
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
NoneOther
Recommended joint design for BM thickness greater than 22mm.Other
*Mandatory above 427 COther
NoneOther
NoneOther
1 of 2Page
315 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The bead sequence shown in the drawing is recommended but not mandatory.2. The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1112
RootFillCap
Back Weld
SMAWSMAWSMAWSMAW
E410E410E410E410
3.23.23.23.2
1112
RootFillCap
Back Weld
SMAWSMAWSMAWSMAW
E410E410E410E410
3.23.23.23.2
1112
RootFillCap
Back Weld
SMAWSMAWSMAWSMAW
3.23.23.23.2
E410E410E410E410
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
None
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
10 deg -/+ 2.5
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
A=
B=
C=
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
Other Dimensions/Comments:
A=
B=
C=
D=
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Other Dimensions/Comments:1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
SPECIFIC INSTRUCTIONS & DETAILS
23-2921-2719-2521-27
VOLT.
115-150105-14595-135
105-145
AMP.
DCRPDCRPDCRPDCRP
8.9-143.6-10.23.6-8.9
3.6-10.2
DCRPDCRPDCRPDCRP
POL.
23-2921-2719-2521-27
VOLT.
115-150105-14595-135
105-145
AMP.
8.9-143.6-10.23.6-8.9
3.6-10.2
TRAVEL SPEED(cm/min)
DCRPDCRPDCRPDCRP
23-2921-2719-2521-27
115-150105-14595-135
105-145
8.9-143.6-10.23.6-8.9
3.6-10.2
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Alternative recommended joint design for BM thickness greater than 22mm.
Recommended joint design for BM thickness equal to or less than 22mm.
Other
Other
Other Recommended joint design for branch connection.
P6-1WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P6-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-312TP304L & ASTM A-240 Type 316.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-1AWPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO1 Group8P-No. 1Group
3.0-12.0mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
2-7 l/minGas Backing Flow Rate
ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER316LER316LER316L
2.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAW
111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -176 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
12-1511-1411-14
90-11580-10080-100
6.4-8.95-10.25-7.6
Spec. No. (SFA) A5.9
AWS No. (Class.) ER316L
Size of Filler Metals 2.4mm
Max. Deposit Thickness 12.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-504-795SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-1
NoneOther
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
NoneOther
Recommended joint design for butt joint.Other
NoneOther
See SPECIFIC INSTRUCTIONS & DETAILS section for filler metal selection.Other
NoneOther
1 of 2Page
177 C Maximum.
Sep 15, 2003
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The number of beads may vary, depending upon bead thickness.2. Additional filler metal listing: Base Metal Filler Metal S/N 304 308L or 316L 20-504-797 & 20-504-795 304L 308L or 316L 20-504-797 & 20-504-795 316 316L 20-504-795 316L 316L 20-504-795 321 347 20-504-803 347 347 20-504-803
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111
RootFillCap
GTAWGTAWGTAW
ER316LER316LER316L
2.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
12-1511-1411-14
VOLT.
90-11580-10080-100
AMP.
DCSPDCSPDCSP
6.4-8.95-10.25-7.6
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P8-1AWPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-1 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-312TP304L & ASTM A-240 Type 316.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-2AWPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO1 Group8P-No. 1Group
3.0-12.0mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
2-7 l/minGas Backing Flow Rate
ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER316LER316LE316LE316L
2.42.43.23.2
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootHotFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -178 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
12-1511-1420-2421-26
85-10565-8565-8570-90
7.6-10.25.7-8.3
10.2-15.211.4-16.4
Spec. No. (SFA) A5.9 A5.4
AWS No. (Class.) ER316L E316L
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 6.2mm 5.8mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-795SAMS S/N 20-484-698
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-2
NoneOther
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
NoneOther
Recommended joint design for butt joint.Other
NoneOther
See SPECIFIC INSTRUCTIONS & DETAILS section for filler metal selection.Other
NoneOther
1 of 2Page
177 C Maximum.
Sep 15, 2003
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The number of beads may vary, depending upon bead thickness.2. Additional filler metal listing: Base Metal Filler Metal GTAW S/N SMAW S/N 304 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 304L 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 316 316L 20-504-795 20-484-698 316L 316L 20-504-795 20-484-698 321 347 20-504-803 20-485-155 347 347 20-504-803 20-485-155
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootHotFillCap
GTAWGTAWSMAWSMAW
ER316LER316LE316LE316L
2.42.43.23.2
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
12-1511-1420-2421-26
VOLT.
85-10565-8565-8570-90
AMP.
DCSPDCSPDCRPDCRP
7.6-10.25.7-8.3
10.2-15.211.4-16.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P8-2AWPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-2 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-312TP304L & ASTM A-240 Type 316.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-3AWPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO1 Group8P-No. 1Group
9.5-19.0mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
2-7 l/minGas Backing Flow Rate
ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER316LER316LE316LE316L
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootHotFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -195 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
10-1411-1520-2320-23
85-11590-12060-7060-70
8.3-11.45-7.6
4.4-9.54.4-7
Spec. No. (SFA) A5.9 A5.4
AWS No. (Class.) ER316L E316L
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 6.2mm 12.8mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-795SAMS S/N 20-484-698
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-3
NoneOther
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
NoneOther
Recommended joint design for butt joint.Other
NoneOther
See SPECIFIC INSTRUCTIONS & DETAILS section for filler metal selection.Other
NoneOther
1 of 2Page
177 C Maximum.
Sep 15, 2003
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The number of beads may vary, depending upon bead thickness.2. Additional filler metal listing: Base Metal Filler Metal GTAW S/N SMAW S/N 304 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 304L 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 316 316L 20-504-795 20-484-698 316L 316L 20-504-795 20-484-698 321 347 20-504-803 20-485-155 347 347 20-504-803 20-485-155
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
1111
RootHotFillCap
GTAWGTAWSMAWSMAW
ER316LER316LE316LE316L
2.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
10-1411-1520-2320-23
VOLT.
85-11590-12060-7060-70
AMP.
DCSPDCSPDCRPDCRP
8.3-11.45-7.6
4.4-9.54.4-9.5
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P8-3AWPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-3 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
ArgonShielding Gas (Type)
7-12 l/minFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-312TP304L & ASTM A-240 Type 316.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-4AWPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO1 Group8P-No. 1Group
15.9-50.8mmGroove
UnlimitedFillet
25.4mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
2-7 l/minGas Backing Flow Rate
ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER316LER316LE316LE316L
2.42.42.42.4
A =
B =
C =
D =
GTAWGTAWSMAWSMAW
1111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
10 deg -/+ 2.5
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootHotFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -195 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
11-1511-1519-2619-26
95-11595-11560-7560-75
5.7-8.35.7-8.3
6.4-11.46.4-11.4
Spec. No. (SFA) A5.9 A5.4
AWS No. (Class.) ER316L E316L
Size of Filler Metals 2.4mm 3.2mm
Max. Deposit Thickness 9.4mm 41.4mm
SAW Electrode-Flux (Class.) N/A N/A
N/AFlux Trade Name N/A
20-504-795SAMS S/N 20-484-698
SMAW
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-4
NoneOther
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
NoneOther
Recommended joint design is for BM thickness greater than 22mm.Other
NoneOther
See SPECIFIC INSTRUCTIONS & DETAILS section for filler metal selection.Other
NoneOther
1 of 2Page
177 C Maximum.
Sep 15, 2003
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The bead sequence shown in the drawing is recommended but not mandatory.2. The number of beads may vary, depending upon bead thickness.3. Additional filler metal listing: Base Metal Filler Metal GTAW S/N SMAW S/N 304 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 304L 308L or 316L 20-504-797, 20-504-795 20-485-234, 20-484-698 316 316L 20-504-795 20-484-698 316L 316L 20-504-795 20-484-698 321 347 20-504-803 20-485-155 347 347 20-504-803 20-485-155
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111122
RootHotFillCapFillCap
GTAWGTAWSMAWSMAWSMAWSMAW
ER316LER316LE316LE316LE316LE316L
2.42.42.42.42.42.4
1111
RootHotFillCap
GTAWGTAWSMAWSMAW
ER316LER316LE316LE316L
2.42.42.42.4
1111
RootHotFillCap
GTAWGTAWSMAWSMAW
2.42.42.42.4
ER316LER316LE316LE316L
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
22.5 deg -0/+ 2.5
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.3. Backgouging is optional depending upon thepenetration & quality of the root pass back side.
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
A=
B=
C=
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
Other Dimensions/Comments:
A=
B=
C=
D=
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Other Dimensions/Comments:1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Amperage, voltage, and travel speed limits aremandatory due to heat input restrictions.
SPECIFIC INSTRUCTIONS & DETAILS
11-1511-1519-2619-2619-2619-26
VOLT.
95-11595-11560-7560-7560-7560-75
AMP.
DCSPDCSPDCRPDCRPDCRPDCRP
5.7-8.35.7-8.3
6.4-11.46.4-11.46.4-11.46.4-11.4
DCSPDCSPDCRPDCRP
POL.
11-1511-1519-2619-26
VOLT.
95-11595-11560-7560-75
AMP.
5.7-8.35.7-8.3
6.4-11.46.4-11.4
TRAVEL SPEED(cm/min)
DCSPDCSPDCRPDCRP
11-1511-1519-2619-26
95-11595-11560-7560-75
5.7-8.35.7-8.3
6.4-11.46.4-11.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Alternative recommended joint design for BM thickness greater than 22mm.
Recommended joint design for BM thickness equal to or less than 22mm.
Other
Other
Other Recommended joint design for branch connection.
P8-4AWPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-4 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
ArgonShielding Gas (Type)
5-12 l/minFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-240Type 310 & 310S and ASTM A-312 TP310S.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-5WPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO2 Group8P-No. 2Group
1.6-11.2mmGroove
UnlimitedFillet
UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
5-7 l/minGas Backing Flow Rate
ArgonGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
ER310ER310ER310
2.42.42.4
A =
B =
C =
D =
GTAWGTAWGTAW
111
3.2mm -0/+0.8
1.6mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -29 CMinimum DesignTemperature
YesNo
PWHT GTAWWelding Process
VOLT. AMP.
DCSPDCSPDCSP
POL.TRAVEL SPEED
(cm/min)
8-128-138-12
55-10570-10555-105
N/AN/AN/A
Spec. No. (SFA) A5.9
AWS No. (Class.) ER310
Size of Filler Metals 2.4mm
Max. Deposit Thickness 11.2mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-504-827SAMS S/N
PQR Revision No. 0
None
N/AMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-5
Refer to table IV.1 for complete listing of materials.Other
Other
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
NoneOther
Recommended joint design for butt joint.Other
NoneOther
NoneOther
Gas purging should be maintained throughout welding.Other
1 of 2Page
177 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
1. The number of beads may vary, depending upon bead thickness.2. Shielding gas flow should be maintained after arc is extinguished.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
111
RootFillCap
GTAWGTAWGTAW
ER310ER310ER310
2.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
3.2mm -0/+0.8
A=
1.6mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
See SPECIFIC INSTRUCTIONS & DETAILS section at thebottom of page 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
8-128-138-12
VOLT.
55-10570-10555-105
AMP.
DCSPDCSPDCSP
N/AN/AN/A
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P8-5WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-5 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
N/ATungsten Electrode Size and Type N/AOrifice or Gas Cup Size
Department Revision Date
NoneApproval restrictions
PREHEAT
NoneShielding Gas (Type)
N/AFlow Rate
POST WELD HEAT TREATMENT
Austenitic Stainless Steel, e.g. ASTM A-240Type 310 & 310S and ASTM A-312 TP310S.
Material Specification(typical)
FILLER METAL
NoneTemperature Range
N/ATime Range
N/AHeating Rate
N/ACooling Rate
Stringer and WeaveString or Weave Bead
Brushing & GrindingInitial & Interpass Cleaning (Brushing, Grinding, etc.)
MultipleMultiple or Single Passes
GAS
POSITION
V-UPWelding Progression
TECHNIQUE & ELECTRICAL CHARACTERISTICS
P8-6WPS No. 0WPS Revision No.
10 CPreheat Temp.
Interpass Temp.
BM Thickness Range:
8 P-No.BASE METAL
TO2 Group8P-No. 2Group
1.6-19mmGroove
UnlimitedFillet
50.8mm-UnlimitedGroove
UnlimitedFillet
Pipe Diameter Range:
N/AGas Backing Flow Rate
NoneGas Backing (Type)AllGroove AllFillet
JOINT SKETCH
E310-15E310-15E310-15E310-15E310-15
2.42.42.42.42.4
A =
B =
C =
D =
SMAWSMAWSMAWSMAWSMAW
11122
None
0.8mm -/+ 0.8
37.5 deg -/+ 2.5
N/A
Application: Piping X Pipeline X Pressure Vessel X Tank Structural
SIDE
RootFillCapFillCap
PASS PROCESS FILLER METAL SIZE (mm)
Other Dimensions/Comments:
SourNon-Sour
Service YesNo
Impact Toughness -29 CMinimum DesignTemperature
YesNo
PWHT SMAWWelding Process
VOLT. AMP.
DCRPDCRPDCRPDCRPDCRP
POL.TRAVEL SPEED
(cm/min)
23-2923-2923-2923-2923-29
70-10055-8555-8555-8555-85
7.6-12.75-10.2
6.4-11.45-10.2
6.4-11.4
Spec. No. (SFA) A5.4
AWS No. (Class.) E310-15
Size of Filler Metals 2.4mm
Max. Deposit Thickness 19.0mm
SAW Electrode-Flux (Class.) N/A
N/AFlux Trade Name
20-482-660SAMS S/N
PQR Revision No. 0
Root Pass V-Down or V-Up
Arc Air and/or GrindingMethod of Backgouging N/AContact Tube to Work Distance
Consulting Services Department
PQR No. P8-6
Refer to table IV.1 for complete listing of materials.Other
Other
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
NoneOther
Recommended joint design for butt weld.Other
NoneOther
NoneOther
NoneOther
1 of 2Page
177 C Maximum.
Nov 24, 1998
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
The number of beads may vary, depending upon bead thickness.
SIDE PASS PROCESS FILLER METAL SIZE(mm)
Other Dimensions/Comments:
11122
RootFillCapFillCap
SMAWSMAWSMAWSMAWSMAW
E310-15E310-15E310-15E310-15E310-15
2.42.42.42.42.4
SIDE PASS PROCESS FILLER METAL SIZE(mm)
SIDE PASS PROCESS FILLER METAL SIZE(mm)
None
A=
0.8mm -/+ 0.8
B=
37.5 deg -/+ 2.5
C=
N/A
D=
1. See SPECIFIC INSTRUCTIONS & DETAILS section atthe bottom of page 2.2. Backgouging is mandatory before welding side 2.
A=
B=
C=
D=
Other Dimensions/Comments:
A=
B=
C=
D=
Other Dimensions/Comments:
SPECIFIC INSTRUCTIONS & DETAILS
23-2923-2923-2923-2923-29
VOLT.
70-10055-8555-8555-8555-85
AMP.
DCRPDCRPDCRPDCRPDCRP
7.6-12.75-10.2
6.4-11.45-10.2
6.4-11.4
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL. VOLT. AMP.TRAVEL SPEED
(cm/min)
POL.TRAVEL SPEED
(cm/min)
Recommended joint design for branch connection.Other
Other
Other
P8-6WPS No. 0WPS Revision No. PQR Revision No. 0PQR No. P8-6 2 of 2Page
SAUDI ARAMCO
WELDING PROCEDURE SPECIFICATIONS
2%Th, 2.4mmTungsten Electrode Size and Type 4, 6, 8Orifice or Gas Cup Size
Department Revision Date
NoneA