NORSOK STANDARD
STRUCTURAL STEEL FABRICATION
M-101Rev.4. Dec. 2000
This NORSOK standard is developed by NTS with broad industry participation. Please note thatwhilst every effort has been made to ensure the accuracy of this standard, neither OLF nor TBL or
any of their members will assume liability for any use thereof. NTS is responsible for theadministration and publication of this standard.
Norwegian Technology CenterOscarsgt. 20, Postbox 7072 Majorstua
N-0306 Oslo, NORWAY
Telephone: + 47 22 59 01 00 Fax: + 47 22 59 01 29Email: norsok@nts.no Website: http://www.nts.no/norsok
Copyrights reserved
Structural steel fabrication M-101Rev. 4, Dec. 2000
NORSOK standard Page 1 of 36
CONTENTS
FOREWORD 3INTRODUCTION 3
1 SCOPE 4
2 NORMATIVE REFERENCES 4
3 DEFINITIONS AND ABBREVIATIONS 53.1 Definitions 53.2 Abbreviations 5
4 SELECTION OF STEELS 64.1 Design classes 64.2 Selection of steel quality level 6
5 QUALIFICATION OF WELDING PROCEDURES AND WELDERS 65.1 Welding procedure specification (WPS) 65.2 Qualification of welding procedures 65.3 Welding procedure approval record (WPAR) - Range of approval 75.4 Examination of the test weld 85.5 Welder and welding operators qualifications 11
6 FABRICATION AND WELDING REQUIREMENTS 116.1 General 116.2 Forming 116.3 Assembly 126.4 Preparation for coatings 136.5 Preparation and fit-up of weld bevels 136.6 Welding processes 136.7 Welding consumables 146.8 Preheat and interpass temperature 146.9 Production welding 156.10 Post weld heat treatment (PWHT) 166.11 Grinding 166.12 Peening 16
7 PRODUCTION TESTS 17
8 FABRICATION TOLERANCES 17
9 NON-DESTRUCTIVE TESTING (NDT) 179.1 General 179.2 Qualification of inspectors and NDT-operators 189.3 Extent of visual examination and NDT 199.4 Visual examination and finish of welds 219.5 Radiographic testing 219.6 Ultrasonic testing 219.7 Magnetic particle and Penetrant testing 229.8 Acceptance criteria 22
10 REPAIR 28
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 2 of 36
10.1 Definitions 2810.2 Correction of welds containing defects 2810.3 Repair by welding 2810.4 Repair welding procedure 2910.5 Correction of distortion 29
ANNEX A 1 - TYPICAL GRINDING DETAILS FOR HIGH FATIGUE UTILISATION(INFORMATIVE) 30
ANNEX A 2 - TYPICAL PEENING DETAILS FOR HIGH FATIGUE UTILISATION(INFORMATIVE) 31
ANNEX B - CORRELATION BETWEEN STEEL QUALITY LEVEL, MDS NUMBER ANDSTEEL GRADE/DESIGNATIONS (NORMATIVE) 33
ANNEX C - QUALIFICATION OF WELDING CONSUMABLES BY DATA SHEETS(NORMATIVE) 34
ANNEX D - WELDING CONSUMABLE DOCUMENTED BY BATCH TESTING(NORMATIVE) 36ANNEX E FABRICATION TOLERANCES (NORMATIVE) 37
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 3 of 36
FOREWORD
NORSOK (The competitive standing of the Norwegian offshore sector) is the industry initiative toadd value, reduce cost and lead time and eliminate unnecessary activities in offshore fielddevelopments and operations.
The NORSOK standards are developed by the Norwegian petroleum industry as a part of theNORSOK initiative and supported by OLF (The Norwegian Oil Industry Association) and TBL(Federation of Norwegian Manufacturing Industries). NORSOK standards are administered andissued by NTS (Norwegian Technology Center).
The purpose of NORSOK standards is to contribute to meet the NORSOK goals, e.g. to developstandards that ensure adequate safety, value adding and cost effectiveness and thus are used inexisting and future petroleum industry developments.
The NORSOK standards make extensive references to international standards. Where relevant, thecontents of a NORSOK standard will be used to provide input to the international standardisationprocess. Subject to implementation into international standards, the NORSOK standard will bewithdrawn.
Annex A is informative. Annexes B, C, D and E are normative.
INTRODUCTION
Revision 4 of this standard has been necessary due to regulations in new design standard N 004 andnew designation of steel grades. In addition a steel grade with SMYS 690 is introduced withadditional requirements to fabrication.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 4 of 36
1 SCOPE
This standard covers the requirements for fabrication and inspection of offshore steel structures withSMYS < 500 MPa and with a minimum design temperature down to -14°C. For special applicationsteels with SMYS up to 690 MPa may be used.
Note: For highly fatigue utilized structures, more severe requirements may apply, and these will beshown on the design drawings.
2 NORMATIVE REFERENCES
The following standards include provisions which, through reference in this text, constituteprovisions of this NORSOK standard. Latest issue of the references shall be used unless otherwiseagreed. Other recognized standards may be used provided it can be shown that they meet or exceedthe requirements of the standards referenced below.
API 2B Specification for fabricated structural steel pipe.API RP 2X Ultrasonic examination of offshore structural fabrications.ASME, Section V Non-destructive testing.
BS 7448, Part 1 Fracture mechanics toughness tests.BS 7910 Guide on methods for assessing the acceptability of flaws in fusion
welded structures.
DNV RP D404 Unstable fracture.
EN 287-1 Approval testing of welders - Fusion welding.EN 288-series Specification and qualification of welding procedures for metallic
materials.EN 444 NDT - General principles for radiographic examination of metallic
materials by X-rays and gamma rays.EN 462-series NDT - Image quality of radiographs.EN 473 Qualification and certification of NDT personnel - General principles.EN 719 Welding coordination - Tasks and responsibilities.EN 729-series Quality requirements for welding - Fusion welding of metallic materials.EN 875 Welding - Welded joints in metallic materials - Specimen location and
notch orientation for impact tests.EN 970 Welding - Visual examination of fusion welded joints.EN 1011-series Welding - Recommendation for welding of metallic materials, relevant
parts.EN 1289 Non destructive examination of welds - Penetrant testing of welds -
Acceptance levels.EN 1290 NDT of welds - Magnetic particle examination of welds - .
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 5 of 36
EN 1291 NDT of welds - Magnetic particle examination of welds - Acceptancelevels.
EN 1418 Welding personnel - Approval testing for fully mechanised and automaticwelding.
EN 1435 Non destructive examination of welds - Radiographic examination ofwelded joints.
EN 1597-1 Welding consumables - Test methods - Part 1: Test piece for all weldmetal test specimens in steel, nickel and nickel alloys.
EN 1714 Non destructive examination of welds - Ultrasonic examination ofwelded joints.
EN 10204 Metallic products - Types of inspection documents.prEN 10225 Weldable structural steels for fixed offshore structures.EN 26847 Covered electrodes for manual metal arc welding.
Deposition of a weld pad for chemical analysis.
ISO 3690 Welding - Determination of hydrogen indeposited weld metal arisingfrom the use of covered electrodes for welding mild and low alloy steels.
ISO 5817 (=EN 25817) Arc welded joints in steel - Guidance on quality levels for imperfections.
NORSOK M-001 Material selectionNORSOK M-120 Material data sheets for structural steelNORSOK N-001 Structural designNORSOK N-004 Design of steel structuresNS 477 Welding. Rules for approval of welding inspectors.
3 DEFINITIONS AND ABBREVIATIONS
3.1 DefinitionsNormative references Shall mean normative in the application of NORSOK standards.Informative references Shall mean informative in the application of NORSOK standards.Shall Shall is an absolute requirement which shall be followed strictly in order
to conform with the standard.Should Should is a recommendation. Alternative solutions having the same
functionality and quality are acceptable.May May indicates a course of action that is permissible within the limits of
the standard (a permission).Can Can is conditional and indicates a possibility open to the user of the
standard.
3.2 AbbreviationsAWS American Welding SocietyBS British StandardCE Carbon Equivalent equationCTOD Crack Tip Opening DisplacementDAC Distance Amplitude CurveDC Design ClassDIN Deutsche Institut für Normung
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 6 of 36
DNV Det Norske VeritasEN (pr EN) European Standard (proposal for EN)FCAW Flux Cored Arc WeldingFSH Full Screen HeightHAZ Heat Affected ZoneHDM Hydrogen content, deposit metalIIW International Institute of WeldingISO International Organization for StandardizationNDT Non Destructive TestingMDS Material Data SheetMSF Module Support FramePcm Carbon equivalent (Parameter for crack, modified)PWHT Post Weld Heat TreatmentSAW Submerged Arc WeldingSMYS Specified Minimum Yield StrengthSQL Steel Quality LevelWPS Welding Procedure SpecificationWPAR Welding Procedure Approval Record
4 SELECTION OF STEELS
4.1 Design classesThe design classes will be decided by the designer and shall form the basis for selection of steelquality level (SQL). Reference is made to NORSOK standard N-004.
4.2 Selection of steel quality levelThe steel quality level will be decided by the designer in compliance with N-004.
Annex B gives the correlation between the steel quality levels I, II, III and IV, and designations onequivalent steels given in NORSOK standard M-120, Material data sheets.
Selection of a better steel quality level in fabrication than the minimum required by the designershall not lead to more stringent requirements in fabrication.
5 QUALIFICATION OF WELDING PROCEDURES AND WELDERS
5.1 Welding procedure specification (WPS)WPS shall be established in accordance with EN 288 part 2.
5.2 Qualification of welding proceduresWelding procedures used for structures requiring steel quality level I and II for all strength levelsand steel quality level III for SMYS ≥ 355 MPa shall be qualified in accordance with EN 288 part 3and the additional requirements in this standard.
The qualification is primarily valid for the workshop performing the welding tests, and otherworkshops under the same technical and quality management. It may also be transferred to and usedby a subcontractor, provided the principles of EN 729 part 2 are implemented and documented.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 7 of 36
5.3 Welding procedure approval record (WPAR) - Range of approval
5.3.1 For welding of steels with SMYS ≤≤≤≤500 MPaThe WPAR is valid within the limitations specified in EN 288 part 3, with the followingclarifications and modifications:
a) Control of heat input according to EN 288 part 3, section 8.4.7, shall apply. If an approvaltesting have been performed at both a high and a low heat input level (with all specifiedmechanical testing), then all intermediate heat inputs are also qualified.
b) When the steel to be welded has a Pcm ≥ 0.21, or a carbon content C ≥ 0.13%, then an increaseof more than 0.02 Pcm units or 0.03 carbon equivalent units (IIW formula) over the value on theapproval test shall require a new qualification test.
c) A change from wrought (rolled, forged) steel to cast steel or converse.d) A change in delivery condition (normalised, thermomechanically controlled processed or
quenched and tempered).e) A change in microalloying element or manufacturing technique for steel with SMYS ≥ 400
MPa.f) A change in groove angle more than +20 deg./-10 deg.g) A qualification of fillet welds carried out on plate thickness equal to or greater than 30 mm,
applies for all plate and throat thicknesses. Single layer fillet welds qualifies multi-layer, but notthe converse.
h) CTOD testing shall be included in the qualification of welding procedures for weldments with aplate thickness above 50 mm for all strength levels for steel quality level I and II and for SMYS>400 MPa for steel quality level III. CTOD testing shall be included in the qualification ofwelding procedures for weldments with a plate thickness below and equal 50 mm if requestedby the designer for the specified steel quality level.
Testing shall be executed from as welded and PWHT weld assemblies as applicable, covering thefollowing combined conditions:
• Full penetration buttweld with K-, or half V -groove as deemed most representative for theactual fabrication. V and X groove are acceptable for weld metal test..
• A welding procedure representing the maximum heat input to be used in fabrication.• Maximum joint thickness (within 10%).
Assemblies shall be made and tested for the actual combination of steel manufacturer, weldingprocess and welding consumable (brand) used, except welding consumables used for root passesonly, provided these are removed completely by gouging and grinding.
Note: The changes specified in d) and e) need not require re-qualification if HAZ properties for thematerial to be welded have been documented from the steel manufacturer for relevant thicknessesand heat input ranges. If sufficient documentation from the steel manufacturer is not available, achange of material shall require re-qualification of a reduced number of procedures. The number ofprocedures to be re-qualified shall be sufficient to verify that the HAZ properties of the newmaterial is comparable with that used for the previous qualifications.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 8 of 36
5.3.2 For welding of steels with SMYS >>>>500MPaIn addition to the requirements given in 5.3.1 the following additional requirements apply forwelding of steels with SMYS >500 MPa
a) A change in steel manufacturer.b) CTOD testing as described in 5.3.1 h) shall be executed for thicknesses above 30 mmc) Stress relieving if required/specified by designerd) When the steel to be welded has a Pcm ≥ 0,21 or a carbon content ≥ 0,13, then an increase of
more than 0,03 Pcm or 0,04 carbon equivalent units (IIW formula) over the value of theapproval test shall require a new qualification test.
5.4 Examination of the test weld
5.4.1 GeneralThe type and number of tests shall be in accordance with table 5.1. Testing shall be performed inaccordance with EN 288 and the additional requirements given below.
The test weld shall be 100% examined for both surface and volumetric defects with the relevantNDT-methods. The soundness of the weld shall comply with clause 9.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 9 of 36
Table 5.1 Type and number of tests
Mechanical testingJointconfiguration
Jointthickness(mm)
Tensiletest
Bendtests 1)
CharpyV-notch
tests
Hardnessand
macro 5)
CTOD
Buttwelds(Tubulars andplates)
t<50t≥50
22
22
4 sets6 sets
11
Ref. 5.3.1hand 5.4.4
T-joints(plates) 4)
t<50t≥50
3)
3)
4 sets 2)
6 sets22
Tubular joints4)
t<50t≥50
3)
3)
4 sets 2)
6 sets22
Fillet welds All 2
Notes:1. Bend tests shall consist of 1 face and 1 root bend specimen for t < 20 mm and 2 side
bend specimens for t ≥ 20 mm2. If the dimensions of the joint does not allow Charpy V-notch testing, the Charpy V-
notch properties shall be documented on a butt weld joint made with the sameconsumable and same base material, and welding parameters and thickness within therange qualified for the joint.
3. It shall be documented on a butt weld test that the welding consumable used will havesufficient tensile strength.
4. T-joints on plates qualify for tubular joints, and vice versa.5. For welds on submerged structures with cathodic protection, the hardness limits in
NORSOK M-001 (i.e. max 350 HV10) shall apply in addition to the requirements ofEN 288. For SMYS 690 MPa max 400 HV10 shall apply.
5.4.2 Charpy V-notch testingSampling of Charpy V-notch impact tests shall be carried out in accordance with EN 875, with thenotch in the positions listed below. (All specimens shall be machined with the notch through thethickness, 2 mm below the surface of the material.) (Designation in parenthesis refers to EN 875).
• Notch in centre of weld (VWT 0/2)• Notch in fusion line (VHT 0/2)• Notch in HAZ, 2 mm from fusion line (VHT 2/2)• Notch in HAZ, 5 mm from fusion line (VHT 5/2)
For welds with a joint thickness of 50 mm or more, two additional sets of Charpy V-notch testsshall be taken from the root area, with the notch in the following positions:• Notch in centre of weld (VWT 0/b)• Notch in fusion line (VHT 0/b)
The test temperature and energy requirements shall comply with table 5.2.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 10 of 36
Table 5.2 Charpy impact test temperatures and energy requirements for weldingprocedure qualifications.
Material Steel quality levelthickness I II IIImm SMYS
≤400400<SMYS≤500
SMYS>500
SMYS≤400
400<SMYS≤500
SMYS>500
355≤SMYS≤500
SMYS>500
t ≤ 12 0°C -20°C -20°C 0°C -0°C -20°C -0°C 0°C12 < t ≤ 25 -20°C -40°C -40°C 0°C -20°C -40°C 0°C -20°C25 < t ≤ 50 -40°C -40°C -40°C -20°C -40°C -40°C -20°C -40°Ct > 50 -40°C -40°C -40°C -40°C -40°C -40°C -40°C -40°CEnergyRequirement 1)
36J 42J 60J 27J 42J 60J 27J 42J
Note:1. The minimum average value is given in the table. No individual value shall be less than 70% of
the minimum average value. Reduction factors of energy requirements for subsize specimensshall be: 7,5 mm - 5/6 and 5 mm - 2/3.
5.4.3 Transverse tensile testingTesting shall be carried out in accordance with EN 288. The fracture shall be located outside theweld metal (i.e. max. 20% of the fracture surface shall consist of weld metal/HAZ).
5.4.4 CTOD testingThe CTOD- technique with the Bx2B through-thickness notched type specimen according to BS7448 Part 1 should be used. Three valid test specimens shall be obtained for each test position.
CTOD-testing of welds shall be carried out with the fatigue notch tip positioned in the coarsegrained region of the heat affected zone and in the weld metal. For HAZ, determination of the actuallocation of the fatigue crack tip shall be performed after testing. Ref. is made to prEN 10225.
Note: Test assemblies may be given hydrogen diffusion treatment prior to testing, and specimensmay be precompressed.
If not specified otherwise, the test temperature for design temperature down to -14 °C shall be:-10 °C for splash zone or above.0 °C for submerged parts.
Other test temperature may be prescribed by the designer.Three (3) valid test specimens shall be obtained for each notch location.The requirement for minimum CTOD value shall be prescribed by the designer. If not specified, therequirement for minimum CTOD value shall be as for the steel purchase order.
CTOD-testing of HAZ can be omitted if relevant CTOD properties in HAZ have been documentedpreviously in accordance with requirements in this standard, provided the requirements for theessential variables are met.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 11 of 36
CTOD-testing of weld metal can be omitted if relevant CTOD properties in WM have beendocumented previously in accordance with requirements in this standard, provided the requirementsfor the essential variables are met.
The required fracture toughness level shall be decided in design for joints when steel quality level Iand II are required. Testing is normally not requested for structures with plate thickness below 40mm for SMYS≤500 MPa or for structures with plate thicknes below 25 mm for SMYS>500 MPa.
5.5 Welder and welding operators qualificationsThe welders, welding operators and tack welders shall be qualified in accordance with EN 287, EN1418 or equivalent. For tack welders, an internal test may be used.
For welding of single sided acute angled tubular joints with α < 70º, welders shall be qualified witha realistic joint, representing the minimum angle α to be used in production.
For welding of joints where steel quality level IV is selected, a certificate for welding of plates inposition PE is sufficient for welding all product forms.
6 FABRICATION AND WELDING REQUIREMENTS
6.1 GeneralAll welding work shall be according to recommendations given in relevant part of EN 1011. Themanufacturer shall have a quality system, which fulfil the relevant part of EN 729 and the applicablelevel of EN 719.
The fabricator shall apply a weld numbering system for identification on all shop drawings and asreference in all documentation.
6.2 FormingCold forming of steel (i.e. forming below 250°C) shall be carried out within the deformation rangerecommended by the steel manufacturer. For steel quality level I and II, the deformation limitwithout documentation of mechanical properties is 5%.
If the deformation is more than the above given limits, either heat treatment shall be performed, orstrain ageing tests shall be carried out according to the following procedure:
• The material shall be permanently strained locally to the actual deformation.• The material shall be artificially aged at 250°C for 1 hour.• One set of 3 impact test specimens shall be tested from the base material in the strained plus
artificially aged condition. The notch shall be located within the plastically strained portion of thematerial, in the part of the cross section which have received the highest strain.
• The impact testing temperature shall be as specified for the actual steel grade in question.• The Charpy-V impact value shall comply with the minimum requirements for the steel grade and
shall not be more than 25% lower than the impact value for the material before deformation andstrain ageing.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 12 of 36
If forming is performed at temperature above 250°C, it shall be documented that the base materialproperties, weldability, weldmetal and HAZ properties satisfy the actual MDS and this standard.
The percentage strain due to forming is defined as follows:
100% x diameter thicknessmid Forming
thicknessWallstrainPercent =
6.3 Assembly
6.3.1 GeneralIn tubular joints, circumferential and longitudinal weld joints should not be placed in the shadedareas shown in fig. 6.1, unless otherwise shown on design drawings.
W 1
W 1
W 1
W 1
W 2W
3
D
W 2
W 2
W 2
Longitudinal welds Circumferential welds
W1 = 75 mm or min. 2 times chord thicknessW2 = 150 mm or min. D/4W3 = 600 mm or min. D
Fig. 6.1 Prohibited location of welds in tubular joints. Longitudinal respectively circumferentialwelds shall not be located in shaded area.
6.3.2 SplicesSplices shall not be located in areas, noted as restricted on design drawings.
6.3.3 TaperingTapering shall be in accordance with the requirements given in relevant standards or drawings. If noother requirements are specified, a tapering of 1:4 should be used.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 13 of 36
6.3.4 Bolting connectionBolting material shall comply with requirements in NORSOK standard M-001, Material selection.Holes shall be made by machine drilling.
6.3.5 Seal/blind-compartments.Crevices and areas which become inaccessible after fabrication or assembly shall be sealed off fromthe outside atmosphere. Seal welds shall have a throat thickness of at least 3 mm. Where steel itemsshall be hot dip galvanised, hollow sections shall be ventilated.
6.3.6 Temporary cut-outsTemporary cut-outs shall not be located in restricted areas as shown on design drawings. Temporarycut outs shall have a corner radius not less than 100 mm. Temporary cut-outs shall be closed byrefitting the same or an equivalent plate and employing the same welding, inspection anddocumentation procedures and requirements that govern the structural part in question.
6.3.7 Straightening of structural membersMembers distorted by welding shall be straightened according to a detailed work instruction. Thebase material properties shall satisfy the specified requirements after straightening.
Maximum temperature for straightening shall not exceed the temperature limit recommended by thesteel manufacturer, but it shall in no case be higher than 600°C.
6.3.8 Doubler platesAll temporary attachments which shall be flame cut or welded under water shall be attached to thestructure by using doubler plates.
All attachments in the splash zone shall be attached to the structure by using doubler plates.
6.4 Preparation for coatingsEdges of plates and structural shapes which are intended to be coated shall be rounded toapproximately 2 mm radius, unless otherwise indicated on design drawings.
6.5 Preparation and fit-up of weld bevelsPermanent backing strips are not accepted, unless shown in design drawings.
Buttering shall be carried out in accordance with a relevant WPAR. Buttering in excess of 20 mmshall be avoided.
6.6 Welding processesThe welding processes listed in EN 288-3 are acceptable.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 14 of 36
6.7 Welding consumablesThe manufacturers shall ensure that welding consumables applied for joints where steel quality levelI, II and III are required, meet the requirements for mechanical properties as specified for thewelding procedure qualification, in both as welded and (where applicable) PWHT condition.
This may be achieved through (alternatively):
• Batch testing including chemical analysis and mechanical properties, see annex D.• An established and reliable system of batch certification against accepted supplier data sheets,
see annex C.• For steels with SMYS ≥ 500 MPa Annex D is mandatory
Except for solid wires such consumables shall be classified by the supplier as extra low hydrogen,i.e. HDM ≤ 5ml/100g weld metal. For self shielded flux cored wire HDM ≤ 8ml/100g may beaccepted, provided preheating temperature and post weld holding temperature and time is assessedto avoid hydrogen cracking. Hydrogen testing shall be according to ISO 3690 or equivalent.
For all steels with SMYS ≥ 500 MPa special precautions shall be taken to verify that selectedconsumables comply with hydrogen requirements. Stricter requirements than given above may berelevant. Prequalification with mock-up structures shall apply if there is a risk for high restraint inwelding or erection.
Consumables for joints in steel quality level III (with SMYS <355MPa) and IV and for joiningstainless to carbon steel shall be selected with due consideration of base material properties,thickness and weldability, to ensure sufficient weld strength, toughness and homogenity.Suchconsumables shall be delivered with EN 10204 type 2.2 certificate, as a minimum.
All welding consumables shall be individually marked.
When certification according to Annex C is used, welding consumables (except welding fluxes)shall be supplied with an inspection certificate (type 3.1B) in accordance with EN 10204, includinga statement of compliance with the Welding Consumable Data Sheet and the chemical compositionof the weld deposit (elements of the data sheet). Welding fluxes shall be supplied with a test report(EN 10204 type 2.2), declaring conformity with the approved product type.
6.8 Preheat and interpass temperaturePreheating above 50ºC should be achieved by electric heating elements. Cutting torches are notallowed for preheating.
The minimum interpass temperature shall not drop below the minimum required preheattemperature. If not otherwise stated in the WPS, and qualified by the WPAR, the maximuminterpass temperature shall not exceed 250°C measured at the edge of the groove. For C- and C/Mn-steels, a maximum interpass temperature of 250ºC may be used, even if a lower temperature wasrecorded on the WPAR.
The preheat temperatures used during repair welding should be minimum 50°C higher than thepreheat used for the original weld.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 15 of 36
Note: Production welding of high strength steels with SMYS>500 MPa is normally more sensitiveto hydrogen cracking than experienced during welding for qualification. Special precautions,including preheating temperature, minimum holding temperature and extended post weld holdingtemperature for 24 hours or more, shall be taken into consideration.
6.9 Production welding
6.9.1 GeneralWelding shall be carried out in accordance with the WPS and applicable drawings.
Butt welds in joints where steel quality level I and II for all strength levels, or steel quality level IIIfor SMYS > 400 MPa are required shall, whenever possible, be welded from both sides.
If any welding is conducted after PWHT, the PWHT shall be repeated.
For joints in inspection category A, the ”straight” edges of K- and 1/2V-butt weld grooves shall havea groove angle of at least 10O, unless it is documented that possible defects can be detected by theUT technique used . (For K-grooves, the 10O should be machined from the root to each platesurface.)
Any occurrence of cracking during production welding shall be investigated. Welding should besuspended until the cause of cracks and defects has been identified and measures taken to preventtheir reoccurrence. Cracks or other persistent weld defects may lead to revision and requalificationof the WPS.
6.9.2 AttachmentsTemporary attachments as lifting lugs, lugs for scaffolding and assembly, supports for cables,equipment, ladders or other fabrication and erection aids should be removed. If indicated on designdrawings that removal (full or partial) is not required, the temporary attachments may be left as is,or removed only partially.
All welding of attachments shall comply with the requirements for the structure to which they areattached. Temporary attachments shall be cut minimum 3 mm from the base metal and ground. Theground area shall be visually examined and magnetic particle/penetrant tested (as relevant) inaccordance with the inspection category in question.
6.9.3 Stainless steel componentsPermanent or temporary structural elements, attachments or penetration sleeves in stainless steelmaterials may be selected for various purposes.
Requirements for welding and testing of stainless outfitting structures shall follow similarclassification principles as for other structural steel elements. All welding and testing of welds tocarbon steel structures shall as a minimum comply with the requirements for the structure to whichthey are attached.
Unless other requirements apply higher alloyed consumables than given for the relevant stainlesscomponent shall be selected for tacking and final welding.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 16 of 36
6.10 Post weld heat treatment (PWHT)PWHT shall be required for structural welds in steel quality level I or II, or quality level III withRe>400MPa, when the nominal thickness (as defined in EN 288-3, section 8.3.2.1) exceeds 50 mm,unless adequate fracture toughness can be documented in the as welded conditions. For restrainedjoints of complicated design, PWHT may be required for smaller thicknesses, independent of steelquality level.
PWHT shall be carried out in accordance with a procedure which shall include:
• Heating rate.• Cooling rate.• Soaking temperature and time.• Heating facilities.• Insulation.• Control devices.• Recording equipment.• Configuration of structure to be PWHT or details if local PWHT shall be carried out.• Number and location of thermocouples to be used during PWHT.
The holding time and temperature shall be as recommended by the steel manufacturer
The temperature difference between different parts of the structure during soaking time shall notexceed 30°C within the heated area. Double sided heating shall be used as far as possible.
The temperatures shall be continuously and automatically recorded on a chart.
6.11 GrindingWhen grinding is specified on design drawings or is instructed as a corrective action, the grindingshall be performed according to a detailed procedure. Grinding tools, direction, surface roughnessand final profile shall be specified. Reference samples for typical joints and sections may beprepared and used for acceptance of treated welds. Typical examples for requirements for grindingof joints are given in Annex A.
6.12 PeeningWeld improvement by peening shall be performed in accordance with detailed procedures.Normally pregrinding of a groove will be required to assure correct location of peening area. Toolsfor grinding and peening, surface roughness and profile of grinding as well as peening shall bespecified. Tools for check and measurements shall be described and shall be available duringoperations. Documentation of correct performance shall include macrophotography. Typicalexamples of requirements for peening of joints are given in Annex A.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 17 of 36
7 PRODUCTION TESTSProduction tests shall be selected on weldments in critical regions to verify that the specifiedrequirements have been meet. Minimum one test coupon is required from each applied weldingprocess.
Test coupons shall be welded in a manner which realistically simulates the actual productionwelding, normally as extension of the production weld, and meet the requirements for weldingprocedure approval tests.
CTOD testing is not required for production testing.
If a production test fails, the reason for the failure shall be determined and remedial actionimplemented.
8 FABRICATION TOLERANCESFabrication tolerances shall be in accordance with Annex E, unless otherwise specified on drawings.
9 NON-DESTRUCTIVE TESTING (NDT)
9.1 GeneralThe inspection category shall be decided by the designer in accordance with NORSOK N-004, andshall be specified on the design drawings.
Final inspection and NDT of structural steel welds shall not be carried out before 48 hours aftercompletion except where PWHT is required. The time delay may be reduced to 24 hours for steelgrades with SMYS of 355MPa or lower, and for steel grades with SMYS of 420MPa or lower forplate thicknesses below 40 mm, provided delayed cracking have not been observed for the materialsand/or welding consumables in question.
When PWHT is performed, the final NDT shall be carried out when all heat treatment have beencompleted.
Prior to fabrication start-up, contractor shall implement a system for recording of weld defect rates.The defect rates shall be recorded on a weekly basis from each production area (geographically splitin production areas at the same yard) and shall be reported together with the accumulated defectrate. The defect rate statistics shall be used as a tool in weld quality control. Causes for defects shallimmediately be investigated and corrective actions shall be taken to prevent further occurrence.Cracks detected with any NDT method shall require documented investigation/action by theresponsible welding engineer.
At a weekly high defect rate or at repeated occurrence of planar defects, two trigger levels apply forextended NDT for welds in inspection category B, C and D. Two steps of actions apply withintrigger level 2.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 18 of 36
Trigger level 1If a defect rate for any method exceed 10 % for a single week the extent shall be increased to 100 %for all welds in question irrelevant of the required inspection category for the welds.
Trigger level 2If a defect rate for any method of 5 - 10 % for a single week is observed the following two steps ofextended NDT shall apply:Step 1.A defect rate for any NDT method exceeding 5 % (1% for MT) for a single week require doublingof the extent of NDT according to the inspection category. Spot extent shall be increased to 20 %.Step 2.If the defect rate for the weld length where the extended NDT is taken in accordance with Step 1above exceed 5 %, the extent shall be increased to 100 % for all welds in question irrelevant of therequired inspection category for the welds.
The increased NDT extent shall cover welds of the same inspection categories, welded in the sameperiod of time when the high defect rate was produced, to assure that the weld quality is maintainedalso with the lower extent of NDT. Unless the causes for defects found leads to immediate anddocumented preventive actions, the higher level of extent of NDT shall be maintained until theweekly defect rate is well below 5 %.
Generally, if the defect rate approaches 10 % during any stage in production welding, furtherwelding should be held until investigations are completed and corrective actions implemented.
A low defect rate may be used as basis for a reduction in the extent of NDT for inspectioncategories B, C and D, provided that a correct defect rate identification is prepared for each weldmethod, each NDT method and each production area. See Note 2 in Table 9.1.
1) welds)of parts testedof(Length 100%)length x (Defect :as defined is ratedefect The
Note 1: “Tested part of welds” means the part that is tested with the same NDT method.
NDT after repair shall not be included when calculating the defect rate.
9.2 Qualification of inspectors and NDT-operatorsPersonnel responsible for welding inspection - welding inspectors - shall be qualified in accordancewith NS 477 or equivalent scheme.
Personnel performing visual inspections of welded joints shall be qualified in accordance withrelevant part of EN 473/NORDTEST.
Personnel responsible for all NDT activities shall be qualified according to EN 473/NORDTESTLevel 3 or equivalent.
The NDT operators shall be qualified according to EN 473/NORDTEST Level 2 or equivalent.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 19 of 36
Operators simply producing radiographs and not performing evaluation, do not require level 2, butshall have sufficient training.
In undertaking testing of castings or forgings the NDT operator should also document experiencewith forged and cast products.
9.3 Extent of visual examination and NDTThe required minimum extent of examination/testing is given in table 9.1. Design drawings mayshow areas of welds where testing is mandatory.
Testing performed shall be representative for the weld quality. Partial NDT shall normally be planedfor on all shop drawings.
Ultrasonic testing to reveal the presence of possible weld metal transverse cracking shall beincluded for butt welds with thickness more than 25 mm. The testing shall be performed onminimum 5% of welds in inspection category A and B for SAW (12) and FCAW (131 and 136)
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 20 of 36
Table 9.1 Minimum extent (in %) of non-destructive testing for structural welds.
Inspectioncategory
Type ofconnection
Visualexamination
Extent of testing
RT UT MTA Buttw.
T-conn.Fillet/partial
100100100
10--
100100
-
100100100
B1) Buttw.T-conn.Fillet/partial
100100100
Spot--
50 2)
50 2)
-
100 2)
100 2)
100 2)
C1) Buttw.T-conn.Fillet/partial
100100100
---
20 2)
20 2)
-
20 2)
20 2)
20 2)
D1) All conn. 100 - - spotE All conn. 100 - - -
Legend -RT = Radiographic testingUT = Ultrasonic testingMT = Magnetic particle testingSpot means 2 - 5%.
Note:1. The extent of NDT shall be increased for Inspection categories B, C and D if repeated
occurrence of planar defects are revealed or if the weekly defect rate for any NDTmethod, including all types of defects, are as given for the limits below.
Trigger level 1 - Defect rate exceeding 10 %:The extent shall be increased to 100 % irrelevant of inspection category.
Trigger level 2 - Defect rate of 10 % and below calls for stepwise increase in extent:Step 1 - Defect rate exceeding 5 % ( MT exceeding 1%): The original extent shall bedoubled. Spot extent shall be increased to 20 %.Step 2 - Defect rate for the extended testing under Step 1 exceed 5 %: The extent shallbe increased to 100 % of the weld lengths in question for all inspection categories.
The required level of increased extent shall be maintained until a defectrate below 5 % is re-established and documented.
2. The extent may be reduced to 50% of the specified extent, based on experience and documentedrecords with similar joints, provided the defect rate (see clause 10.1 and 11.1) for UT/RT is<2.0% and for MT is <0.2% during the last 100m of weld. The last 100m shall be continuouslyupdated every week. If the defect rate exceeds the limits given above, the normal extent of NDTshall apply again.A possible reduction in the extent of NDT shall be considered separately for each weldingmethod and each production area.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 21 of 36
When partial testing is defined for welds in an area, the testing shall be spread such that the mostessential members and nodes are included in the inspection, and such that areas of welds mostsusceptible to weld defects are covered.
The specified percentage to be tested in table 9.1 refers to the total length of welds in eachinspection category.
All WPS's used and welds representing all welding personnel involved in the fabrication shall besubject to NDT.
During the initial fabrication the extent of UT and MT of inspection category B and C welds shallbe intensified, normally to twice the level given in table 9.1. This extent shall be maintained for aweld and test length sufficient to conclude that the weld repair percentage is at a reasonable level.
The increased initial testing may be accounted for in the overall extent provided the initial testingconfirms consistent good workmanship.
In addition to what is listed in table 9.1, the following shall apply for inspection category A and B:
a) One film at each end for longitudinal welds of tubulars (including tubulars for nodes and stubs).b) Where radiographic testing is required, intersection welds, and those locations where presence
of defects is deemed to be most harmful, shall be tested.c) Ultrasonic and radiographic testing shall not overlap, except when 100% UT is specified.
However, ambiguous imperfections revealed by UT shall in addition be tested by RT.d) Ultrasonic testing is normally not applicable for thicknesses less than 10 mm. For such
thicknesses, UT may be replaced with RT. In general, RT should be considered if UT is notpossible. Radiographic testing is normally not applicable for thicknesses above 40 mm.
e) MT shall be performed on both external and internal surface as accessible or as required by thedesigner.
9.4 Visual examination and finish of weldsThe visual examination shall be carried out in accordance with EN 970.
9.5 Radiographic testingRadiographic testing shall be carried out in accordance with EN 1435, Class A.
Suspect planar indications discovered by RT shall be type determined, located and sized by UT.
Penetrameters of wire type (according to EN 462-1 or equivalent) shall be utilised. Sensitivity levelshall be in accordance with EN 462 part 3, Class A. However, if gamma ray sources are used, thesensitivity shall be 2% or better.
9.6 Ultrasonic testingUltrasonic testing of welds in plate and tubular butt welds and double side welded tubular jointsshall be performed in accordance with EN 1714, examination level C.
Reference blocks shall be made with thickness and side-drilled holes in accordance with table 9.2.DAC reference curves shall be established.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 22 of 36
The effective test range of a DAC curve shall be determined by the point at which the curve hasfallen to 25% FSH, when it will be necessary to raise the curve using reflectors at increased depth.The reference block shall be from a steel type that is representative for the steel to be inspected.
Where ultrasonic testing is to be performed on steel produced by controlled rolling orthermomechanical treatment, reference blocks shall be produced both perpendicular to, and parallelto, the direction of rolling. The rolling direction shall be clearly identified.
The actual refracted angle for each probe measured from the reference block or as measured on theactual object being examined, shall be used when plotting indications.
A transfer correction between the reference block and the test surface shall be performed.
Ultrasonic examination procedures shall be sufficiently detailed to ensure 100% of the weld bodyand heat affected zones are examined for longitudinal defects.All indications exceeding 20% DAC shall be investigated to the extent that they can be evaluated interms of the acceptance criteria.
All indications exceeding acceptance criteria shall be reported, unless more stringent requirementsare given in table 9.5.
The examination record shall include the position, the echo height, length, depth and type ofindication.
9.7 Magnetic particle and Penetrant testingMagnetic particle testing shall be carried out in accordance with prEN 1290. Magnetic yokes usingalternating current shall be used. Prods are acceptable where the geometry of the welded jointprevents the use of yokes. Permanent magnets are not acceptable.For non-magnetic materials penetrant testing in accordance with EN 1289 should be used.
9.8 Acceptance criteria
9.8.1 GeneralAll welds shall comply with the requirements given below, in 9.8.2 - 9.8.5.
9.8.2 Visual examinationAll welds shall show evidence of good workmanship. The quality shall comply with therequirements of table 9.3.
9.8.3 RadiographsThe soundness of the welded joint shall comply with the requirements of table 9.4.
9.8.4 Ultrasonic testing acceptance criteriaThe acceptance criteria for welds shall comply with table 9.5 unless more stringent requirements arespecified by the designer.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 23 of 36
9.8.5 Magnetic particle testingLinear indications (i.e. indications with a length/width ratio above 3 and length above 1.5 mm ) arenot acceptable. Any linear indications shall be ground and re-examined. Rounded indications shallbe evaluated in accordance with the requirements of table 9.3.The same acceptance criteria applies for penetrant testing.
9.8.6 All methodsAll defects shall be repaired according to clause 10.
Defects may be accepted by the relevant parties when repair work is considered detrimental to thetotal integrity of the weld. Such acceptance shall be based on a fitness for purpose evaluation inaccordance with BS 7910 , DNV RP D404 or other recognised methods.
Table 9.2 Calibration reference block requirements
Thickness ofmaterial to be
examined (mm)
Thickness of block Diameter of hole Distance of holefrom one surface
10 < t < 50 40 or t Ø 3 mm +/-0.2 mm50 < t < 100 75 or t t/2 and t/4.100 < t < 150 125 or t Ø 6 mm +/-0.2 mm Additional holes are150 < t < 200 175 or t allowed and200 < t < 250 225 or t recommended
t > 250 275 or t
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 24 of 36
Table 9.3 Structural steel welds. Visual and MT-acceptance criteria for structural steelwelds
Welding Acceptance criteriaType of defect Insp. cat. A, B Inspection category C, D, ECracks Not acceptable Not acceptableIncompletepenetration or lackof fusion
Not acceptable Single - side weld:Length < t/2, max 10 mmDefects shall be regarded as a continuousdefect if the distance between them is < t.
Undercut Max depth 0.5 mmContinuousundercut is notpermitted
Maximum depth 0.75 mmContinuous undercut is not permitted
Surface porosityExposed slag
Not acceptable Not acceptable. However, the followingdefects may be acceptable if it does notconflict with surface treatment requirements:Accumulated pore diameters in any area of 10x 150 mm is not to exceed 15 mm. Max. sizeof a single pore is t/4 or 4 mm, whichever isthe smaller.
Concave root Max. concavity 0.5 mm if the transition is smoothly formed.Excessive pen. 1) Max. 3 mmRoughness of weld(fig. 1)
“U” shall be less than 2.5 mm. Weld surface shall be smooth,without sharp transitions. The bottom of roughness in butt weldsshall not be below the base material surface.
Misalignment ofbutt welds (fig. 2)
Max. misalignment (M), 0.15 x t or max. 4 mm,whichever is the smaller.
Reinforcement ofbutt welds (fig. 3) 1)
“t” less or equal to 10 Max reinforcement “C” 2 mm“t” greater than 10, up to 25 Max reinforcement “C” 3 mm“t” greater than 25, up to 50 Max reinforcement “C” 4 mm“t” greater than 50 Max reinforcement “C” 5 mm
Reinforcement offillet/partial pen.welds (fig.4) 1)
“a” less or equal to 10 Max reinforcement “C” 2 mm“a” greater than 10, up to 15 Max reinforcement “C” 3 mm“a” greater than 15, up to 25 Max reinforcement “C” 4 mm“a” greater than 25 Max reinforcement “C” 5 mm
Symmetry of filletwelds (fig. 5)
“a” less or equal to 6 Max difference, b - h: 3 mm“a” greater than 6, up to 13 Max difference, b - h: 5 mm“a” greater than 13 Max difference, b - h: 8 mm
Grinding arc strikesetc. Removal oftemporaryattachments 2)
Grinding of base material shall not exceed 7% of the wall thicknessor max. 3 mm. Repair welding and inspection shall be performed ifremoval of the base metal exceeds the specified requirements.
Sharp edges Minimum 2 mm radius (Ref. 6.4)
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 25 of 36
Notes:1) Localised reinforcements exceeding the above requirements are acceptable.2) Temporary attachments shall be cut min. 3 mm from the base metal and ground smooth.
The ground area shall be visually inspected and MT shall be performed in accordancewith the inspection category in question.
3) When required (ref. 6.11), grinding of the surface shall be specified. Typical examples ofgrinding requirements are given in annex A.
U
U
Fig. 1 Roughness of weld
c
t
M
t
Fig. 2 Misalignment of butt weld Fig.3 Reinforcement of butt weld
c
ac
a a
b
h
Fig. 4a Fig. 4b Fig. 5Reinforcement of fillet weld Reinforcement of partial pen. weld Symmetry of fillet weld
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 26 of 36
Table 9.4 Structural steel welds, RT acceptance criteria
Type of defect Inspection categoryA, B C, D, E
Internal porosity (Note 1)
Isolated:Pore diameter max t/4, but max.6
mmmax t/3, but max. 6 mm
Cluster:Pore diameter max. 3 mm max. 4 mm
Scattered:Accumulated pore diameters in any10x150 mm area of weld
max. 20 mm max. 25 mm
Slag inclusions, or piping porosity (Note 2)Width t/4, max .6 mm t/3, max. 6 mmLength (Note 3) 2t, max 50 mm 4t, max. 100 mmIncomplete penetration, lack of fusionLength (Note 2) t, max. 25 mm 2t, max 50 mmCracks Not acceptable Not acceptable
Notes:1) If more than one pore is located inside a circle of diameter 3 times the pore diameter, the
pores are to be considered as a cluster.2) Defects in a line where the distance between the defect is shorter than the longest defect
shall be regarded as one continuous defect.3) No length limitation for width ≤2 mm for t ≥20 mm and for width ≤1 mm for t <20 mm.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 27 of 36
Table 9.5 Structural steel welds. UT acceptance criteria.
Description Inspection categoryA + B
Inspection categoryC, D, E
Notes
General If the type of defect can not be ascertained with certainty thedefect shall be repaired when the length exceeds 10 mm and theecho height exceeds the reference curve.
1234
Cracks Unambiguous cracks are unacceptable regardless of size oramplitude.
Lack offusion orincompletepenetration
Internal defects :I: The echo height exceeds the reference curve:Max length t, Max length 2t,max 25 mm max 50 mmII: The echo height is between 50 and 100% of the reference
curve:Max length 2t, Max length 4t,max 50 mm max 100 mmSurface defects are not acceptable except:For root defects in single sided welds , the max length for whichthe echo height exceeds the reference curve shall be:Max length t, Max length 2t,max 25 mm max 50 mm
12345
Slaginclusions
When echo height exceeds the reference curve:Max length 2t, Max length 4t,max 50 mm max 100 mm
12
Porosity Repair is required if porosity may mask for other defects. 1
Notes:1. Type of defect shall be decided by:
I: Supplementary non-destructive testing.II: The ultrasonic operator's assessment of the defect, using his knowledge of thewelding process, signal geometry, defect position etc.
2. If elongated defects are situated on line and the distance between them is less than thelength of the longest indication, the defects shall be evaluated as one continuous defect.
3. Defect length shall be determined by the 6dB drop method from the end of the defect(for defects larger than the beam) or by the maximum amplitude technique (for defectssmaller than the beam).
4. With UT performed from only one side of the weld with only one surface accessible, theacceptable echo heights are reduced from 100% to 50% and from 50% to 20%,respectively.
5. With “internal defects” it is meant defects which are located more than 6 mm from thenearest surface. A defect is classified as a “surface defect” if any part of the defect islocated less than 6 mm or t/4, whichever is smaller, from the nearest surface.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 28 of 36
10 REPAIR
10.1 DefinitionsWeld discontinuities: Irregularities in the body of the weld or on the weld surface classified as eitherweld imperfection or as weld defect.
Weld imperfection: Discontinuities that are within the acceptance criteria defined in clause 9 andare considered to have no practical limitations on the intended use of the product. Weldimperfections may be left without remedial work. Cosmetic grinding may be performed at thediscretion of the fabricator.
Weld defect: Discontinuity with a size and/or density that exceeds the acceptance criteria defined inclause 9.
10.2 Correction of welds containing defectsAll repairs shall be carried out in accordance with established procedures.
Welds containing cracks shall not be repaired, until the reason for the cracking has been determined.If necessary, the defective part of the weld shall be cut out for further examination. Crater cracksmay be repaired by grinding followed by NDT and subsequent repair welding according to anaccepted repair welding procedure.
Other defects shall be corrected by grinding, repair welding or re-welding.
When weld defects are removed by grinding only, the final weld surface and the transition to thebase material shall be smooth. Removal of defects shall be verified by local visual inspection, aidedby applicable NDT methods. If applicable, the remaining thickness in the ground area shall bemeasured. Repair welding is required if the remaining thickness is less than that specified.
10.3 Repair by welding
10.3.1 Repair and re-repair weldingBefore repair welding, the defect shall be completely removed.
The excavated area shall have smooth transitions to the metal surface and allow good access forboth NDT after excavation and subsequent repair welding. After excavation, complete removal ofthe defect shall be confirmed by MT or PT. PWHT shall be performed after repair if specified forthe original weld.
The excavated groove shall be minimum 50 mm long, measured at defect depth even if the defectitself is smaller. Defects spaced less than 100 mm shall be repaired as one continuous defect.
After repair welding the complete weld (i.e. the repaired area plus at least 100 mm on each side)shall be subjected at least to the same NDT as specified for the original weld.
Repair welding may only be carried out twice in the same area.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 29 of 36
10.3.2 Re-weldingRe-welding shall be performed in accordance with the procedures and WPS utilised for the originalweld, and includes complete removal of the original weld and HAZ.
10.4 Repair welding procedureRepair and re-re-repair welding may be performed using the same WPS as for the original weld, or aseparately qualified procedure.
For repairs using a different process, and/or consumable, a separate WPS shall be qualified ifrequired by 5.2. Mechanical testing may be limited to HAZ Charpy V-notch testing in the originalweld, provided the process/consumable is backed up by other WPAR’s.
10.5 Correction of distortionImproperly fitted parts should be cut apart and re-welded in accordance with the applicable qualifiedWPS.
Parts distorted by welding, beyond the tolerances, should be straightened in accordance with therequirement in clause 6.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 30 of 36
ANNEX A 1 - TYPICAL GRINDING DETAILS FOR HIGH FATIGUEUTILISATION (INFORMATIVE)
TYP. TUBULAR JOINT GRINDING DETAIL
TYPICAL GRINDING DETAILSFOR HIGH FATIGUE UTILISATION
T4= 2mm or 0,05 x T3 max.(wichever is less)
Removesharp edges
OUTSIDE
BRACE WALL
T4
T3
T2 = 2mm or 0,05 x T1 max.(wichever is less)
T1
Removesharp edges
Weld rad.
Rotary burr grinder
chord wall
Remove overlap flushwith plate surface
Blend out to remove edge on undercut
Maximum depth below platesurface for blend is not to exceed1,5mm
Grinding direct ion
TYP. BUTT WELD JOINT GRINDING DETAIL
Notes to figures:1. For removal of undercuts the toe of the weld should be blended in a smooth transition and
extended below the plate surface in order to remove the toe defects.2. Grinding should extend below plate surface to a minimum of 0.5 mm below the bottom of any
visible undercut and ensuring that no exposed defects remain, using a rotary burr grinder.Grinding marks should run at right angels to weld axis and under no circumstances parallel to it.
3. Minimum radii of weld profiles after blending should not be less than 10 mm.4. Upon completion of blending of toe the whole of the ground surface shall be inspected with
100% visual examination and 100% MT.5. Ground surface shall be free of any cracks or cracklike indications, and there shall be no
evidence of undercut or overlap.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 31 of 36
ANNEX A 2 - TYPICAL PEENING DETAILS FOR HIGH FATIGUEUTILISATION (INFORMATIVE)
A.2.1 General
Peening of local area as weld toe or weld trasition is an acceptable method to improve fatigue life ofstructures. Peening is applied together with grinding where grinding serves the purposes to removestress risers such as surface defects and to define a steering grove for the tool in the area to bepeened. Both grinding and peening require skills and preparations not normally available infabrication yards. Due to the dependancy of correct performance specific precautions shall be takenwhen peening is planned for.
A.2.2 Requirements for application
When peening is planned for the following preparations are required :
• Nomination of responsible engineer for preparations, performance and documentation• A complete responsibility and personnel matrix• Statement on expected or required improvements• Detailed work instructions• Documentation on operators experience, skill or training• Selection of peening methods to be applied• Detailed mark up drawings showing all areas of application• Detailed stepwise procedure for the work, including:! grinding details as tools, radius, depth and direction! tools to be used for peening! method, intensity and extent of peening! quality control measures! documentation of performance and results• Verification of performance such as experiments, tests or other relevant information• As built record index for the final DFI resume
As preparation for peening the surface shall be dressed in a way that makes lack of coveragedetectable, preferably by stone grinding. Applicable tool for grinding is normally a rotary burr orstone of 6 to 8 mm diameter when a single tool hammer is used and 10 to 12 mm when a needlehammer is used. The depth of the groove is approximately 0.5 mm below the original surface.All surface defects shall be removed by grinding prior to peening.
Applicable tool for peening is normally pneumatic hammers. A needle hammer is normally usedwhen a wider area shall be covered. For local toe peening a single tool hammer is recommended.Correct tool is essential to maintain correct peening in compliance with requirements.Special tools with adjusted curvature shall be prepared in accordance with weld geometry.
Needle peening shall be applied with a coverage of minimum 200 %. Single hammer peening shallresult in a fully covered hammered groove where the surface is smooth with uniform indentation.All traces from previous grinding shall be completely removed.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 32 of 36
Devices for quality control and documentation shall be thoroughly selected. Groove depthmeasuring tools and macro photo is normally applied. Reference specimens shall be prepared forcomparison between ground and final peened surfaces.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 33 of 36
ANNEX B - CORRELATION BETWEEN STEEL QUALITY LEVEL, MDSNUMBER AND STEEL GRADE/DESIGNATIONS (NORMATIVE)
Steelqualitylevel
NORSOKMDS No.Note 1
Rev.No.
Referencestandard
Product type Steel grade Former Steelgrade
Y20 3 Plates S355G10+N/G10+M S355N4z/M4zY21 3 Rolled sections S355G12+N/G12+M S355N3z/M3zY22 3 Seamless tubulars S355G15+Q/G15+N S355Q3z/N3zY30 3 Plates S420G2+Q/G2+M S420Q3z/M3zY31 3 Rolled sections S420G4+M S420M3zY32 3 prEN 10225 Seamless tubulars S420G6+Q(mod) S420Q3 (z mod)
I Y40 3 Plates S460G2+Q/G2+M S460Q3zM3zY41 3 Rolled sections S460G4+M S460M3zY42 3 Seamless tubulars S460G6+Q(mod) S460Q3(z-mod)Y50 3 Plates S500G2+Q/G2+M S500Q3z/M3zY51 3 Rolled sections S500G4+M S500M3zY52 3 Seamless tubulars S500G6+Q(mod) S500Q3(z-mod)Y70 Plates S690+QY25 3 Plates S355G9+N/G9+M S355N4/M4Y26 3 Rolled sections S355G11+N/G11+M S355N3/M3Y27 3 Seamless tubulars S355G14+Q/G14+N S355Q3/N3Y28 Welded tubulars S355G13+NY35 3 Plates S420G1+Q/G1+M S420Q3/M3Y36 3 Rolled sections S420G3+M S420M3Y37 3 Seamless tubulars S420G6+Q S420Q3Y45 3 Plates S460G1+Q/G1+M S460Q3/M3
II Y46 3 prEN 10225 Rolled sections S460G3+M S460M3Y47 3 Seamless tubulars S460G6+Q S460Q3Y55 3 Plates S500G1+Q/G1+M S500Q3/M3Y56 3 Rolled sections S500G3+M S500M3Y57 3 Seamless tubulars S500G6+Q S500Q3Y70 Plates S690+QY05 EN 10113 Plates and sections S355NL/MLY06 prEN 10225 Tubulars S355G1+N
III Y07 EN 10210 Hot finished tubulars S355NHY08 EN 10219 Cold formed tubulars S355MLHY15 En 10113 Plates and sections S420NL/MLY16 EN 10219 Cold formed tubulars S420MLH
S235JRG2EN 10025 Plates and sections S275JR
S355J0S235JRH
IV Y01 3 EN 10210 Hot finished tubulars S275J0HS355J0HS235JRH
EN 10219 Cold formed tubulars S275J0HS355J2H
Note 1 NORSOK Material data sheets are published in NORSOK standard M-120.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 34 of 36
ANNEX C - QUALIFICATION OF WELDING CONSUMABLES BY DATASHEETS (NORMATIVE)
C.1 SCOPEThe purpose of certification is to verify that each batch of consumables has a chemical compositionwithin limits as specified by the supplier in conformance with a recognised classification standard.By controlled and certified chemistry the supplier also confirms that mechanical properties of theweld metal fulfil the minimum requirements specified for the product.
For this specification a batch (or lot) is defined as the volume of product identified by the supplierunder one unique batch/lot number, manufactured in one continuous run from batch controlled rawmaterials.
Each individual consumable (brand name and dimension) shall be certified per batch, except forsolid wire (GTAW, GMAW, SAW), originating from the same heat, where one diameter mayrepresent all.
C.2 DATA SHEETEach welding consumable or combination of consumables shall have a unique data sheet, issued asa controlled document within the suppliers quality system. The purchaser shall base his selection,ordering and receiving of consumables upon reviewed and accepted data sheets.
The data sheet shall give guaranteed limits and/or minimum values for composition and mechanicalproperties, determined under defined reference conditions.
If the consumable shall be used for welds in PWHT condition, then the properties shall also bedocumented in PWHT condition in addition to the as-welded condition.
Specifically this shall include, as applicable:
• Chemical analysis limits for solid wires and metal powders. For information also typical weldmetal analysis, using a relevant shielding gas or flux.
• Chemical analysis limits of weld metal from coated electrodes and cored wires, deposited
according to EN 26847. For information also specified limits for S, P and N in the core wire orstrip.
The analysis shall include limits for all elements specified in the relevant classification standardand/or intentionally added and for residual elements known to influence weld metal quality.
Minimum:C, Si, Mn, S, P, Cu, Ni, Cr, Mo, V, Nb.
For SAW fluxes the analysis shall be given as ranges for all main ingredient and flux basicity.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 35 of 36
• Mechanical properties (range or/and guaranteed minimum) of the weld, deposited and testedaccording to prEN 1597 part 1 and including tensile strength, yield strength elongation, notchtoughness Charpy-V at -40ºC. For information also typical properties of a relevant butt weldshould be added.
• Diffusible hydrogen content HDM max., including any information on drying, restricted welding
parameters etc. required to ensure this value in practice. • When relevant for the product, basic information about CTOD properties, to be supported by
separate test reports as required and agreed.
Data sheets shall also contain product classification according to recognised standards, relevantapprovals and information on packing, storage etc. as required for correct application and use of theproduct.
C.3 CERTIFICATEEvery batch of consumables shall be supplied with an inspection certificate 3.1.B, containing as aminimum the specific tested chemical composition of the wire or weld metal, as applicable. Thechemical elements shall conform to those of the data sheets, with a statement “below specifiedmaximum” acceptable for residual elements.
The supplier may optionally add information about mechanical properties, based on specific or non-specific type of control. (Ref. EN 10204). Other tests may also be agreed between supplier andpurchaser.
Certificates shall be actively used by the purchaser to control received consumables against theaccepted data sheet. Full conformance of chemical composition shall be required to release eachbatch for fabrication welding.
Structural steel fabrication M-101 Rev. 4, Dec. 2000
NORSOK standard Page 36 of 36
ANNEX D - WELDING CONSUMABLE DOCUMENTED BY BATCHTESTING (NORMATIVE)
D.1 SCOPEThe purpose of the batch testing is to verify that the consumables remains nominally equivalent tothat used for welding procedure qualification, with respect to chemistry and mechanical properties.
For this specification a batch (or lot) is defined as the volume of product identified by the supplierunder one unique batch/lot number, manufactured in one continuous run from batch controlled rawmaterials.
Each individual product (brand name and dimensions) shall be tested once per batch, except forsolid wire originating from the same heat, where one diameter may represent all. SAW fluxes do notrequire individual testing, while SAW wires shall be tested in combination with a selected, nominalbatch of flux.
Chemical Analysis
For solid wires and metal powders the analysis shall represent the product itself.
For coated electrodes and cored wires the analysis shall represent the weld metal, depositedaccording to EN 26847.
The analysis shall include:• All elements specified in the relevant classification standard and /or intentionally added.• The main impurities S, P and N.
D.2 MECHANICAL PROPERTIESUnless otherwise specified the properties shall represent all weld metal, deposited and testedaccording to prEN 1597 part1.
Properties tested shall include:• Tensile strength, yield strength and elongation.• Impact strength Charpy-V, at temperatures -40ºC, or as specified by purchaser.
The need for other types of tests shall be evaluated for the application in question, such as:• Mechanical properties based on a defined butt weld rather than all weld metal test.• Mechanical properties in the PWHT condition.• CTOD testing.• Testing of hydrogen level.
D.3 DOCUMENTATIONBatch tests shall be documented by an inspection certificate 3.1B to EN 10204, with reference to arecognised product classification standard and containing all specified test results.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 37 of 65
ANNEX E - FABRICATION TOLERANCES (NORMATIVE)
CONTENTS
E.1 SCOPE AND OBJECTIVES 38
E.2 CODES, STANDARDS AND SPECIFICATIONS 38
E.3 DEFINITIONS 38
E.4 GENERAL REQUIREMENTS 39E.4.1 Implementation policy of requirements 39E.4.2 Procedures and documents 40E.4.3 Qualification of inspectors 40E.4.4 Instrument reliability 40E.4.5 Reference temperature 40E.4.6 Control methods 41E.4.7 Interface criteria’s 43E.4.8 Alignment Requirement 43
E.5 FABRICATION TOLERANCES FOR STRUCTURAL COMPONENTS 44E.5.1 I / H- Girders 44E.5.2 Box Girders 45E.5.3 Tubulars 46E.5.4 Panels 49E.5.5 Girder Nodes 50E.5.6 Box Nodes 52E.5.7 Tubular Nodes 53E.5.8 Cast and Forged Elements 55E.5.9 Curved and cylindrical shell 56E.5.10 Conical transitions 56
E.6 ASSEMBLY TOLERANCES 57E.6.1 Topsides and modules 57E.6.2 Jacket and other tubular frame structures 58E.6.3 Floating production units 63E.6.4 Subsea structures 64
E.7 FABRICATION TOLERANCES FOR SPECIAL ITEMS 65E.7.1 Crane Pedestal 65E.7.2 Skid Beams 65E.7.3 Outfitting Structure 65E.7.4 Installation Aids 65E.7.5 Grillages 65E.7.6 Cranes 65
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 38 of 65
E.1 SCOPE AND OBJECTIVES
This annex defines the maximum allowable dimensional tolerances for offshore steel items andstructures.
The Designer may, however, specify stricter tolerances and additional tolerances. These will, in casetake presedence over this annex.
Note: It should be observed that the requirement to fabrication tolerances in this annex may be morestrict than the manufacturing tolerances for steel products according to M-120.
The intention of this annex is to give dimensional tolerances which will ascertain that:• The calculated strength and fatigue resistance is present in the structures• Items and structures can be assembled without dimensional rework• All parts of the structures are suitable for their intended use• The structures are thrustworthy relative to measurements given on the structural drawings• The relevant components tolerances are achieved and maintained after the components final
incorporation in the completed structure(s)
E.2 CODES, STANDARDS AND SPECIFICATIONS
Reference standards for this annex are:
ISO-8062 Castings - System of dimensional tolerances and machiningENV 1090-1 1995 for Cranes. Execution of steel structures - Part 1: General
E.3 DEFINITIONS
Terminology used in conjunction with this annex:
AFC drawing:Engineering drawings formally approved for construction.
Centreline:A real or imaginary line that is equidistant from the surface or sides of the (measured) object.
Deflection:Load imposed curves, bends, angles or irregularities from an unloaded structure. Note: Opposed tostraightness deviation.
Flatness:Flatness is here defined as vertical offset at any point from a plane parallel with the surveyed object.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 39 of 65
Grid System:The grid system is defined as the design reference system for all parts, components and elements ofa completed structure.The grid system defines the 3D position of any item within a completed structure.The grid system is normally denoted in one of the following manners:• x, y and z coordinates,• North, east and height coordinates• Longitudinal, transversal and elevation coordinates.The grid system defines the design origo (location and elevation datum) for a structure.
Position Deviation:The specified point's actual position relative to it's nominal position.(Measured value minus nominal value equals deviation).
Reference Lines:Reference lines are marked lines on construction parts and assemblies. The reference lines shall beparallel to, and in determined distances from grid lines.
Straightness Deviation:Curves, bends, angles or irregularities from a straight generator.
Note: Straightness deviation is regarded to be fabrication imposed irregularities and not caused byelastic deformation.
Survey Reference SystemA reference system constituting of fixed and coordinate determined points, from where surveys canbe performed, and where the location and elevation of the fixed points are identifiable relative to thegrid system.
Work Point:A marked or imaginary point on a member or structure from which dimensions shall be related.
E.4 GENERAL REQUIREMENTS
E.4.1 Implementation policy of requirementsThe tolerances given in this annex shall be applied for completed structures.
For single elements to be parts of complex structures, specification of detailed and more stringenttolerances for each fabrication and erection sequence may be necessary in order to meet therequirements of this annex in the completed structure. Such tolerances shall be presented in theplan/scope of work for fabrication.
Specification of detailed and more stringent tolerances for intermediate and final interfaces may alsobe necessary in order to meet the requirements of this annex in the completed structure.
The allowable tolerances given for individual members shall not cumulate to give unacceptabledeviation for the finished section or complete structure.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 40 of 65
If tolerances given for individual sections and components are conflicting, those tolerancesrepresenting the stricter values shall be governing.
If no appropriate tolerance is stated in this document, the tolerance requirements shall be agreed.
All tolerance requirements are based on nominal values on unloaded structure.
E.4.2 Procedures and documentsThe following procedures and documents shall be prepared:
Plan for fabrication and erection including methods, techniques and dimensional control to assurethat all structures can be fabricated and assembled to dimensions within the specified tolerances.The plan shall assure that all allowable tolerances for individual elements are not cumulative to theextent of exceeding the allowable tolerance for the complete structure.
Dimensional inspection procedures relevant for the structures and any additional specificationsneeded to those included in this document, subject drawings or other regulations/guidelines for thestructural fabrication.
The following documents shall be prepared prior to start of fabrication:• Plan for dimensional assurance/inspection• Dimensional inspection procedures
During fabrication and erection deviations outside the specified tolerances shall be identified andinformed of in advance of the formal handling of deviations.The detailed deviation reports shall be available at all stages in fabrication, and shall be submittedon request.
Final documentation shall be prepared in correspondence with the requirements for as builtdocumentation and fabrication record.
E.4.3 Qualification of inspectorsPersonnel responsible for dimensional control activities shall have a minimum background of atleast 5 years relevant experience in industrial surveying.
Personnel monitoring dimensions and tolerances shall have relevant training in use andunderstanding of instruments, and subsequent calculations, enabling them to perform all necessarycontrols of own work performance.
E.4.4 Instrument reliabilityAll instruments used shall be in accurate permanent adjustment, have current valid controlcertificates and be subject to a programme of periodic checking.
E.4.5 Reference temperatureReference temperature for survey activities should be +20 deg. C.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 41 of 65
The field work temperature shall as a minimum be noted on all dimensional reports, when this isnecessary for future use of the report and the component surveyed. For components to be assembled,built under significantly different temperature conditions, dimensions shall be computed to thereference temperature and this shall be annotated on any subsequently produced document or report.
E.4.6 Control methods
E.4.6.1 Reference SystemPrior to fabrication a survey reference system related to the grid system, shall be established. Thesurvey reference system shall use the same numerical values, and the same orientation directions ofthe system axis as the grid system.
The system's north axis shall be positive toward platform north (or bow, if ship).The system's east axis shall be positive toward east (or starboard, if ship).The system's elevation shall be positive upward.The numerical value should be the same for all disciplines and packages.For special structures such as jackets being built laying down, the reference system must be adjustedto this fabrication situation, but the final as built survey shall be related to the platform grid system.
The survey reference system should be established within the following tolerances:
Sections/complete structures: ±3 mm
Stricter survey reference system tolerances shall be used on components where the requirements ofthe final product are more stringent than the above tolerance. For components where the tolerance ofthe product are less than ±2 mm, the proposed survey methods shall be described.
At all stages during fabrication and erection, the Contractor shall ensure that the survey referencesystem and the fabricated item shall be in correct position relative to each other.
Permanent survey stations shall be properly constructed and be protected from disturbance.The permanent survey stations shall be rechecked periodically, or whenever additional permanentsurvey stations are established. All additional or rechecked surveys shall be properly documented.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 42 of 65
Fig. E.4.6-1 Principal reference system
Figure E.4.6.1, indicates sample of applicable and practical reference systems.The layout of the reference system may be specially designed to suit the task at hand and themethods chosen for controls.
E.4.6.2 Marking criteria’sDuring layout and assembly of each structural item all work points and centrelines, which arerelevant for the remaining steps of the construction, shall be marked and identified.
Location of hidden stiffeners, bulkheads etc. shall be marked on the outside of the structure toensure a correct assembly, if relevant for the remaining steps of the construction.
All primary datum work points on the structure shall be set out using accepted engineeringsurveying techniques consistent with the tolerances required by this annex. All girders, boxes, nodesand other structures shall be properly and clearly marked relative to the grid system at all interfaces,if relevant for the remaining steps of the construction.
E.4.6.3 AccuracySurveys shall be performed using survey techniques and technology which enables the achievementof a survey accuracy better than the specified tolerances.The methods and equipment used must enable verification of the survey accuracy.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 43 of 65
All activities related to measurement and inspection of dimensions and tolerances shall take intoaccount the effects of self weight while the structure is under fabrication.
E.4.7 Interface criteria’sAll non-adjustable interfaces and interfaces deemed critical prior to erection shall be surveyed anddocumented. A comparison of the interface results prior to erection shall be performed andnecessary actions in order to meet the global requirements shall be carried out.
E.4.8 Alignment RequirementRequirements to alignments with regard to eccentricity of butt joints and cruciform joints are asfollows:
a) Butt-jointsReference is made to table 9.3.
b) Cruciform JointsEccentricity of non-continuous plating in cruciform joints shall not exceed the followingrequirements, (ref. figure 4.8-1)
e ≤ t1/2 (mm), maximum 5 mm, for t2 ≤ 20 mme ≤ t1/2 (mm), maximum 8 mm, for t2 > 20 mmt1 = smaller thickness in mm of non-continuous platet2 = thickness in mm of continuous platet3 = larger thickness in mm of non-continuous plate
e = 2m + t3 - t12
m = misalignmente = eccentricity
Fig. E.4.8-1 Cruciform joints
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 44 of 65
E.5 FABRICATION TOLERANCES FOR STRUCTURAL COMPONENTS
E.5.1 I / H- Girders
Type of deviation Figure Nota-tion
Ref.Length
Allow % ofref. length
Max.Deviation mm
Lateral or verticaldeflection
5.1-1A f L ±0.15 ±10
Length 5.1-1A L L ±0.25 ±3
Height 5.1-1B H H ±0.3 ±3Width 5.1-1B B B ±3Inclination of web 5.1-1B V H ±0.8 ±10
Eccentricity of webon flange
5.1-1B V1 H ±1.0 ±3
Buckling of web 5.1-1B V3 H ±0.75 ±10
Curvature/rotationflange
5.1-1B V2 B/2 ±2.5 ±3
Twisting of section 5.1-1C d5 L ±0.10 ±10
Fig. E.5.1-1 I-/H-Girders tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 45 of 65
E.5.2 Box Girders
Type of deviation Figure Notation Ref. Length Allow % ofref. Length
Max Dev.mm
Position deviation atend/interface section
5.2-1A d1 Ref. CentreLines
- ±3
Length 5.1-1A L L ±0.25 ±3Height 5.1-1B H H ±0.3 ±3Width 5.1-1B B B ±3Out of straightness 5.2-1B d2 L ±0.15 ±10
Buckling of plates 5.2-1C d3 H, W ±0.5 ±10
Pos. deviation of loadbearing stiffenersinclusive inclination
5.2-1D d4 Ref. CentreLines
- ±5
Twisting 5.2-1E d5 H ±0,5 ±6
Fig. E.5.2-1 Box Girders tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 46 of 65
E.5.3 TubularsThe allowable tolerance given for individual tubular segments shall not be cumulative for thefinished tubular.
a) Circumference:
The external circumference shall not depart from the nominal external circumference by more thanthe following (Ref. Figure 5.3-1):
• Measured at joints or within ±610 mm from the joint (Zone A in Figure 5.3-1):of the nominal wall thickness or ±10 mm whichever is the smallest.
• The tolerances in (i) may be increased by 50% for the remaining length of the tubular (Zone B inFigure 5.3-1).
b) Out-of Roundness (Ovality):
Ovality is defined as the difference between the measured maximum and minimum internal (orexternal) diameters and shall not be more than 1% of the nominal OD (ODn) or 8 mm, whichever isthe least. (Ref. Figure 5.3-2)
c) Out of circularity:
Circularity is defined as the difference between the actual and the average radius, both beeingdetermined from the optimum centre of the tubular. Maximum difference is not to be more than0.25% of ODn.
d) Straightness:
The maximum allowable deviation from straightness in any 3 m increment of length shall be 3 mm.The straightness deviation over tube length (L), shall not exceed 0.001 x L, with maximum 10 mmdeviation for lengths up to 12 m. Above 12 m length max. allowable deviation is 12 mm. Out ofstraightness shall be checked on two longitudinal planes separated by 90°.
e) Length:
Unless otherwise noted, the tubular shall be delivered within following tolerances:
• Unbevelled ends: La ≥ Ln +25 mm• Bevelled ends: La = Ln ± 5 mm
f) Tube ends:
The tube ends shall be perpendicular to the longitudinal axis within the following tolerances:
• Unbevelled ends: 5 mm• Bevelled ends: 3 mm
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 47 of 65
g) Local out-of roundness:
The local out-of roundness shall not deviate from the theoretical curvature by more than e=0.002 xODn (ref. fig. 5.3-3). The local out-of roundness shall be measured inside or outside over 20° of thecircumference.
h) Local Out-Of Straightness:
Local straightness is defined as the deviation of the shell plate from a straight generator of length(L) parallel to the true centre line of the tubular. This tolerance shall not exceed 20% of the wallthickness. Local straightness shall be checked on the inside or outside of tubulars with a nominalexternal diameter greater than 2000 mm or with a nominal external diameter to nominal wallthickness ratio greater than 65. These checks shall be carried out at 45° intervals of arc with L= 3 m.
Above tubular tolerances apply to welded and not seamless tubulars.
Fig. E.5.3-1 Tubulars - Circumfential tolerance
Fig. E.5.3-2 Tubulars - Ovality tolerance
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 48 of 65
Fig. E.5.3-3 Tubulars - Local out-of roundness references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 49 of 65
E.5.4 Panels
Type of deviation Figure Notation Ref. Allow. % Max. dev. mmPANEL SHEET:Out of plane straightness,sagging/hogging, betweengirders
5.4-1 p1 W ±0.15 ±15
Local buckles betweenstiffeners 5.4-1 p2 W1 ±0,5 ±5GIRDERS/ STIFFENERS:
Out of straightnessin X and Y direction 5.4-1 g1 W 0.15% ±10Position deviation 5.4-1 g2 Grid
system ±10Inclination 5.4-1 g3 Hg ±0.8 ±10Out of straightness of webnormal to web(web buckles) 5.4-1 g4 Hg , W1 ±0.75 ±10
Fig. E.5.4-1 Deck panels tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 50 of 65
E.5.5 Girder Nodes
Type of deviation Figure Notation Ref. length Allow % ofref. length
Max. deviationmm
Position deviation ofinterfaces
5.5-1B,5.5-1C
d1 Ref. CentreLine
- ±5
Lateral and verticalstraightness of node
5.5-1A f L ±0.15 ±5
Lateral and verticalstraightness of stiffeners
5.5-1A f1 L,H ±0.1 ±5
Height of node 5.5-1B s - - ±5
Pos. deviation stiffenersinclusive inclination
5.5-1B,5.5-1C
d2 Ref. CentreLine
- ±5
Position deviationcolumn interfaces
5.5-1C d3 Ref.CentreLine
- ±5
Baseplate flatness/rotation rel.to Z axis
5.5-1A,5.5-1B
b1 Ref. CentreLine
- ±2
Pos.deviation baseplaterelative to Z axis
5.5-1B d4 Ref.CentreLine
- ±3
Fig. E.5.5-1 Girder nodes tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 51 of 65
Fig. E.5.5-1 Girder nodes tolerances
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 52 of 65
E.5.6 Box Nodes
Type of deviation Figure Notation Ref. Length Allow ofref. length
Max. deviationmm
Position deviation of main boxinterface
5.6-1A d1 Ref. CentreLine
- ±3
Out of straightness 5.6-1B d2 L ± 0,10% ±10
Buckling of plates 5.6-1C d3 H, W ±0,5% ±10
Radial and tangential stub enddeviation
5.6-1C,5.6-1E
d4 Ref. CentreLine
- ±5
Pos. deviation of load bearingstiffeners incl. inclination
5.6-1D d5 Ref. Centreline
- ±5
Offset of centrelines at centreof node
5.6-1E,5.6-1F
d6 Ref. CentreLine
- ±5
Fig. E.5.6.1 Box nodes tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 53 of 65
E.5.7 Tubular Nodes
Type of deviation Figure Notation Ref. length Allow ofref. length
Max.deviationmm
Overlength of stub 5.7-1A l2 L2 +25-0
Overlength of node can barrel 5.7-1A l1 L1 +10-0
Stub ends perpendicularity 5.7-1A p - ±3
Radial and tangential stub end/node cans position
5.7-2 V ∆α Gridsystem
0.2° of arc ±6
Position of intersection pointnode can / stub
5.7-2 E Gridsystem
±6
Internal stiffeners-Position-Inclination of web-Flange width-Bow of web-Rotation of flange-Eccentricity of flange on web-Height of stiffeners
5.7-1A5.7-1B5.7-1B5.7-1C5.7-1B
5.7-1B5.7-1B
PMBN
Lx
hb
1,0%1,5%
1,0%
±5±5±3±6±6
±6+10/-3
Local straightness ofstubs/barrel
5.7-1A Wallthickness
25% 8
Straightness of barrel 5.7-1A L 1/1200 10
The centre line of stub shall be within 0.2° from the stub angle specified on the design drawings.Maximum position deviation measured at the intersection of stub end / node can shall be ±6 mm.For stubs longer than 1 stub diameter, the position deviation between can and stub may be taken atthe 1 diameter location.
Tolerance for:
• Circumference• Out-of Roundness (Ovality)• Local out-of roundness• Out-of circularity
are defined in Section E.5.3
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 54 of 65
Fig. A
Fig. B (tolerance references)
Fig. C (tolerance references - internal stiffeners)
Fig. E.5.7-1 Tubular nodes
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 55 of 65
Fig. E.5.7-2 Node stub location
E.5.8 Cast and Forged ElementsAll relevant tolerances regarding these elements’ geometry i.e. hole positions, flatness, web and ribpositions shall be specified on the design drawings.
The nominal axes, work points, rib centrelines etc. shall be properly marked on each elementinterface(s) to adjacent main steel.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 56 of 65
During installation of cast and forged items, special care shall be taken that the parent plate edgesare located within prepared face of casting / forging.
See also ISO-8062 standard for tolerances.
E.5.9 Curved and cylindrical shellFor elements including curved shells (such as semi submersible’s pontoons) special dimensionalprocedures shall be implemented for measurement and computing.
Sylindrical shells.The maximum deviation from the nominal radius, measured at ringstiffeners or at bulkheads shallnot exceed the value:
δ = | ra - r| <= 0,005 rra = actual distance from the cylinder axis to the shell wallr = nominal radius of the shell
Components defined as Cylindrical Shell to be specified on design drawings.
E.5.10 Conical transitionsAt both ends of a cone, the maximum deviation from the nominal radius shall not exceed the value:δ=| ra - r| <= 0,005 r
where ra= Actual distance from the cylinder axis to the cone wall r = Nominal radius at cone end
Requirements for internal stiffeners shall be in accordance with table 5.7.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 57 of 65
E.6 ASSEMBLY TOLERANCES
E.6.1 Topsides and modules
Type of deviation Figure Notation Ref. Allowable% of ref.length
Max.deviationmm
Position of any point of mainsteel
6.1-1 X1,Y1 Grid system ±10
Position of support node 2) 6.1-1 X2, Y2,Z2
Grid system ±6
Position of lifting node 6.1-1 X2, Y2,Z2
Grid system ±10
Elevation of decks and mezz.decks sag./hog.
6.1-1 H1, H2,H3
Grid system ±10
Footings deviation fromelevation reference 1)
6.1-1 H Grid system ±5
For truss frames without any defined support points the elevation reference should be based on amean of all levelled points on main steel.
NOTES:1) Maximum allowable deviation shall also apply to mating surface level at stab-in onto
jacket legs.2) Includes Main Support Frame (MSF) stab-in nodes and module footing nodes.
Fig. E.6.1-1 Topside and module tolerance references
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 58 of 65
E.6.2 Jacket and other tubular frame structures
E.6.2.1 Assembly tolerances
Type of deviation Figure Notation Ref. Max. dev. mmPosition deviationof centre of nodes 6.2.1-A
∆x, ∆y Grid system ±12
Rotation of node 6.2.1-A S ±6Distance deviationbetween two nodes
6.2.1-A ±20
Diagonal distancebetween coloumnin each hor. plane
12
Position of legring stiffeners anddiaphragms ±6Inclination ofringstiffeners 6Straightness oflegs / chords 6.2.1-B/C ∆f L X±10Straightness ofbraces 6.2.1-C ∆f L X±L/1000Position ofintersecting braces Grid system ±15
NOTE: Local tolerances for sliding and pivoting ends shall be specified on the structural drawings.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 59 of 65
Fig. E.6.2-1 Jacket and tubular frame structures - assembly tolerances
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 60 of 65
E.6.2.2 Final Tolerances for Jacket, Interface Jacket/MSF
Type of deviation Figure Notation Reference Max. dev.mm
Horizontal positiondeviation of centre ofstab-in cans
6.2.2 Vx, VyV =√ (Vx²+Vy²)
Grid system1)
±6±8
Jacket:Distance between centreof column to centre ofany column at stab-incans
6.2.2 F L ±12
Jacket:Mating surface level atstab-in
Grid system2)
±3
MSF:Distance between centreof column to centre ofany column at stab-incans
6.2.2 F L ±6
Ovality of stab-in can As in sectionE.5.3b
Horizontal positiondeviation of caissons,risers, J-tube
Grid system ±6
NOTES:
1) The position of the stab-in cans shall, if the situation allowes, be related to the top-side stab-in cones with the tolerances stated above.
2) The jacket legs shall by preference be cut within above tolerances after grout is cured.
If survey of the deck footings show out-of acceptable elevation/flatness tolerances, ref. SectionE.6.1, the measured deviations shall be considered incorporated when cutting the legs in order tominimise loads due to differential settlements in footings.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 61 of 65
Fig. E.6.2-2 Final tolerance jacket interface jacket/MSF
E.6.2.3 Guides, Sleeves, Piles and clamps
The position deviation of the centre of pile guides/sleeves shall be ±25 mm related to thecoordinate system.Local alignment of sleeves 20 mm.Radius of spacer plates ±5 mm.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 62 of 65
E.6.2.4 Piles
Type of deviation Figure Notation Ref. Max. dev. mm.
Length ±100
Diameter betweenspacerplates
6.2.4 d1 As specified ondrawing
Diameter in drivinghead
6.2.4 d2 As specified ondrawing
End perpendicularityin driving head
6.2.4 P As specified ondrawing
Pile markings ±50For general tolerances, see E.5.3 Tubulars.
Fig. E.6.2-4 Piles tolerance references
E.6.2.5 Conductor Guides
The position deviation of the centre of the conductor guides shall be ±10 mm related to thecoordinate system for top el. and ±15 mm for the other elevations related to the same coordinatesystem.
The maximum deviation of any conductor guide from the optimised centreline through all conductorguides, shall not vary more than ±15 mm.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 63 of 65
E.6.2.6 AppurtenancesCaissons, J-tubes and risers.
Type of deviation Figure Notation Ref. Max.dev. mm
Length - - - ±25
E.6.3 Floating production units
E.6.3.1 Semi submersibles and tension leg platformsOverall hull / substructure tolerances:
Type of deviation Figure Ref. Max. dev. mmGlobal position of column top /bottom
6.3.1-16.3.1-2
Globalgrid system ±15
Distance between top / bottomof two columns
6.3.1-16.3.1-2
±30
Local position of column top /bottom 6.3.1-3
Localgrid system ±5
Fig. E.6.3.1-1 Semi submerisibles / tension leg platforms. Global tolerance
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 64 of 65
Fig. E.6.3.1-2 Semi submerisibles / tension leg platforms. Global tolerance
Fig. E.6.3.1-3 Semi submerisibles / tension leg platforms. Local tolerance
E.6.3.2 ShipShips should be fabricated using a grid system with origo in the aft perpendicular, and in accordancewith section E.3 of this annex. Based on the grid system a reference system according to sectionE.4.6.1 should be permanently marked onboard the ship.
E.6.4 Subsea structuresSubsea structures should be fabricated according to tolerances given on drawings.
Structural steel fabrication M-101Rev. 4, Nov. 2000
NORSOK standard Page 65 of 65
E.7 FABRICATION TOLERANCES FOR SPECIAL ITEMS
E.7.1 Crane PedestalCrane pedestal tolerances shall be specified in a separate document to be prepared by the designer,taking into account the structural aspects as well as the mechanical functional tolerances andequipment interface tolerances.
E.7.2 Skid BeamsSkid beam tolerances shall be specified in a separate document to be prepared by the designer,taking into account the structural aspects as well as the mechanical functional tolerances andequipment interface tolerances.
E.7.3 Outfitting Structure
• This section covers all primary and secondary outfitting structures.• The difference in elevation of deck plates and/or grating at joints shall not exceed 2 mm.• Plates and gratings shall be without visible warping.• Landing and stairway locations shall not deviate more than 25 mm from the dimensions shown
on the AFC drawings.• Fabrication of handrails shall be performed to such a degree of accuracy that when erected, the
toprail shall be continuous, straight, have smooth transitions and be level to the eye.• Members in the vertical plane shall not be out of plumb by more than 6 mm on each 3000 mm
section and not more than 26 mm over the total height of the structure.• Wherever tolerances are not shown on the drawings, or specified elsewhere, fabrication work
shall be accurate to within 10 mm of all nominal dimensions.• Matching holes for bolted connections shall not exceed 2 mm difference in location.
E.7.4 Installation AidsInstallation aid structures such as primary and secondary guides and bumpers shall be fabricated andinstalled in accordance with acceptable tolerances for relevant elements/structures defined in thisdocument.
Specific tolerance requirements are shown on respective drawings, and shall be mandatory.
E.7.5 GrillagesLoad out grillage, barge grillage and seafastening shall be fabricated and installed in accordancewith acceptable tolerances for relevant structures/elements defined in this document.(Ref. section E.4.8)
Specific tolerance requirements shall be shown on respective drawings and shall be mandatory.
E.7.6 CranesReference standard: ENV 1090-1 applies.