Supporting Information
Direct synthesis of 3D hollow porous graphene balls from coal tar pitch for high performance supercapacitors
Xiaojun He a,, Hebao Zhang a, Hao Zhang a, Xiaojing Li a, Nan Xiao b, and Jieshan
Qiu b,*
a School of Chemistry and Chemical Engineering, Anhui Key Lab of Coal Clean
Conversion and Utilization, Anhui University of Technology, No. 59 Hudong Road,
Maanshan 243002, China
b Carbon Research Lab, Liaoning Key Lab for Energy Materials and Chemical
Engineering, State Key Lab of Fine Chemicals, Dalian University of Technology,
Dalian 116024, China
*Corresponding authors. Tel: +86-555-2312355. Fax: +86-555-2311822. E-mail:
agdxjhe@126.com (X.J. He); Tel: +86-411-84986024. Fax: +86-411-84986015. E-
mail: jqiu@dlut.edu.cn (J. S. Qiu).
Electronic Supplementary Material (ESI) for Journal of Materials Chemistry A.This journal is © The Royal Society of Chemistry 2014
Fig. S1. A graphene-like stone ball under the foot of a monster in front of the Lama
Temple in Beijing of China, which was designed and built as an art decoration in 1694
in Qing dynasty. The stone ball seems to be made of a blown graphene sheet with
only carbon six-member rings.
Fig. S2. (a) TEM image of HPGBNP−6; (b) TEM image of HPGBNP−4; (c) FESEM
image of PC1Ar; (d) TEM image of HPGB2Ar; (e) TEM image of HPGBAr.
Fig. S2a and b show the TEM images of HPGBs (HPGBNP−6 and HPGBNP−4) that
were synthesized directly from coal tar pitch by a simple nano-MgO template strategy
coupled with KOH activation at pressure of −0.05 to −0.10 MPa. Fig. S2c shows that
only conventional porous carbon (PC1Ar) was synthesized in the absence of nano-
MgO template. Fig. S2d shows the TEM image of HPGB (HPGB2Ar) with some
wrinkles that was made from coal tar pitch by only using nano-MgO as template. Fig.
S2e shows the TEM image of HPGBAr.
0 200 400 600 800 1000 1200 1400
HPGBNP-4
HPGBNP-6
HPGBN2
HPGBArIn
tensit
y (a
.u.)
Binding energy (eV)
C1s
O1s
Fig. S3. XPS spectra of HPGBs, showing that no observable N-species (≈396 eV, N1s)
are present in HPGBAr, HPGBN2, HPGBNP−6 and HPGBNP−4. This means that the
working gas atmosphere is not involved in the chemical reactions related to HPGBs
under the experimental conditions.