6 Description of Charge Transport in Disordered Organic Materials
S.D. Baranovski and O. Rubel
Faculty of Physics and Material Sciences Center, Philipps Universität Marburg, Germany
6.1 Introduction 222 6.2 CharacteristicExperimentalObservationsandthe
ModelforChargeCarrierTransportinRandomOrganicSemiconductors 224
6.3 EnergyRelaxationofChargeCarriersinaGaussianDOS.TransitionfromDispersivetoNondispersiveTransport 228
6.4 TheoreticalTreatmentofChargeCarrierTransportinRandomOrganicSemiconductors 230
6.4.1 Averagingofhoppingrates 230 6.4.2 Percolationapproach 233 6.4.3 TransportenergyforaGaussianDOS 233 6.4.4 Calculationsoftrel andm 235 6.4.5 Saturationeffects 241 6.5 TheoreticalTreatmentofChargeCarrierTransport
inOne-dimensionalDisorderedOrganicSystems 243 6.5.1 Generalanalyticalformulas 245 6.5.2 Driftmobilityintherandom-barriermodel 246 6.5.3 DriftmobilityintheGaussiandisordermodel 248 6.5.4 Mesoscopiceffectsforthedriftmobility 251 6.5.5 Driftmobilityintherandom-energymodelwith
correlateddisorder(CDM) 253 6.5.6 Hoppingin1Dsystems:beyondthe
nearest-neighborapproximation 254 6.6 OntheRelationBetweenCarrierMobilityand
DiffusivityinDisorderedOrganicSystems 255 6.7 OntheDescriptionofCoulombEffectsCausedby
DopinginDisorderedOrganicSemiconductors 258 6.8 ConcludingRemarks 262 References 263
Charge Transport in Disordered Solids with Applications in Electronics EditedbyS.Baranovski.©2006JohnWiley&Sons,Ltd
c06.indd 221 5/6/2006 06:08:02 PM
222 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
6.1 INTRODUCTION
In this chapterwe focuson the theoretical description of charge transport in disorderedorganicmaterials.This topic is enormouslybroad since thevarietyof organicmaterialswithdifferentconductingpropertiesisveryrich.Insomeorganicsubstancessuperconduc-tivity has been found with transition temperatures as high as 10K [1]. Some polymericconductorsbasedonpolyacetyleneevidencethevaluesoftheelectricalconductivitieswhicharecomparabletothoseofthebestconductingmetals.Forexample,iniodine-dopedpoly-acetylenepreparedbytheNaarmannmethodavalueoftheconductivityabove105Wcm-1wasobtained[2].Manyorganicmaterialssuchaspolyethylenewithconductivitiesbelow10-8Wcm-1canbeconsideredasgoodinsulators.Itisnotpossible,ofcourse,tocoverthepropertiesofallthesematerialsinonechapter.In[3]somedeviceapplicationsoforganicmaterialsaredescribed.Untilnowelectrophotographicimagerecordinghasbeenthemaintechnique thatexploited theelectricalconductingpropertiesoforganicsolidsonabroadindustrialscale[4].Themaineffortsofresearchersarefocusedpresentlyonthedevelop-ment of organic materials for applications in light-emitting diodes (LEDs) as well as inphotovoltaics.Materialsusedforthesepurposesaremostlyrandomorganic,notablycon-jugated,or/andmolecularlydopedpolymerswithsemiconductingproperties[4,5].There-forewerestrictourdescriptioninthischaptertoconsideringelectricalconductioninsuchorganicsemiconductingmaterials.
Severalhandbookshavebeenpublishedrecently,whicharedevotedtothedescriptionofphysicalpropertiesanddeviceapplicationsoforganicmaterials.Forexample,numerousdetailsofthechemistry,physicsandengineeringofsemiconductingpolymerscanbefoundinrecentbooks[5,6].TotheinterestedreaderwecanalsorecommendthecomprehensivemonographofPopeandSwenberg[7]wherevariouselectronicprocessesinorganiccrystalsandpolymersarebeautifullydescribed.WewilldiscussbelowthechargecarriertransportproblemsraisedinChapterXIVofthatmonograph.
Discussingcharge transportpropertiesoforganicmaterials,oneshouldclearlydistin-guishbetween thepropertiesoforderedsystemssuchasmolecularcrystalsononehandand thoseofessentiallydisorderedsystems likemoleculardopedpolymerson theother.Transport models used to describe electrical conduction in these two distinct classes ofmaterialsareessentiallydifferent.
Inordertodescribegoodconductingpropertiesofsuchorganicmaterialsasmolecularcrystals,oneusuallyemploysratherstandardmethodsofsolid-statephysicsdevelopedforchargetransportincrystallineinorganicsolids.Forapplicationstoorganicmaterialsoneslightlymodifies the standard theoryby taking into account the strongelectron–phononinteraction leading topolaroneffectsandnonlinearexcitationssuchassolitons [1,7].Acompletelydifferentsetofideasisexploitedinordertodescribechargecarriertransportinessentiallydisorderedorganicmaterials,suchasmolecularlydopedpolymers[8],low-molecular-weightglasses[9,10]andconjugatedpolymers[11]. In thesematerialschargetransportisassumedtobeduetothevariable-rangehopping(VRH)ofelectronsorholesviastatesrandomlydistributedinspaceandenergylocalizedstates[1,5,7,8,12,13].Itisthistransportmodethatisdescribedinthischapter.ThequestionmayariseastowhyoneneedsdescribethistransportmodeoncemoreiftheVRHinapplicationtodisorderedorganicsemiconductorshasalreadybeendescribedinnumerousreviewarticles[1,8,12,13]andalsoinrecentbookchapters(forinstance,ChapterXIVin[7]andthechapterofH.Bässler in [4]).Wedo itbecausewefind the treatmentof theVRH inapplication to
c06.indd 222 5/6/2006 06:08:02 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 223
Y2
organicdisorderedmaterialsgivenintheaboveliteraturetobeincomplete.Someexamplesoftheincompletenessaregivenbelow.
(i) IthasalreadybecomeatraditiontoclaimthattheGaussianshapeoftheenergydis-tribution of localized states (DOS) assumed for random organic systems preventsanalytical solutionof thehopping transportproblem[7,8,12,13].Weshow, to thecontrary,thatsuchasolutioncanbeeasilyobtainedwithinthestandardsetofideasfortheVRHintroducedin[14].
(ii) IthasalreadybecomeatraditiontoclaimthatthebesttheoreticalapproachtodescribetheVRHinrandomorganicsystemsisbasedonMonteCarlocomputersimulations[1,4,5,7,8,12,13].Weshowbelowthatalthoughcomputersimulationsoftenprovidevaluable informationon transportproperties, the simulation results shouldbe takenwith caution. For instance, some dependences of transport coefficients on materialparametershavebeenconsideredasuniversalsimplybecauseothermaterialparame-terswerenotchangedinthecourseofthesimulations.Furthermorefinitesizeeffectsincomputersimulationshavenotalwaysbeentreatedappropriately.
(iii) Inmostreviewarticlesandbookchapterspublishedsofartheeffectofcarriermobilitydecreasingwithincreasingelectricfieldwasspecifiedasoneofthemostchallengingfortheoreticalexplanation[4,5,7,8,12,13].Wewillshowbelow,forexactlysolvablemodels[15,16]thatthiseffectmightbeanartifactthathasbeencausedbymisinter-pretationofexperimentalresults.
(iv) ThereisnoconsensusbetweenresearchersontheverybasicquestiononwhethertheconventionalEinsteinrelationbetweenthechargecarriermobilityanddiffusivity isvalidforhoppingtransportindisorderedsystems.Weclarifythisproblembelow.
(v) RecentlymanycontradictorypapershavebeenpublishedonthetheoreticaltreatmentofhopingtransportinarandomsystemwithGaussianDOS.Inalldisorderedorganicandinorganicmaterialsaverystrongnonlineardependenceofthecarriermobilitym ontheconcentrationoflocalizedstatesN isobservedexperimentallyinthehoppingregime.Thisstrongdependenceiscausedbytheverystrongexponentialdependenceofthetransitionratesonthedistancesbetweenlocalizedstates.Whileforinorganicmaterialsthedependencem (N)hasbeenwelldescribedtheoreticallywithintheVRHapproach,andhasalreadybecomeasubjectoftextbooks[17],theverysamedepend-encem (N)stilllookspuzzlingformanytheoreticiansworkingwithorganicmaterials.Sometimes it isclaimedthat thedependencem (N) in thehoppingregimeshouldbelinear[18–21],inmarkedcontradictiontoexperimentaldata.Sometimesadependenceoftheformln(m)∝ -g (Na3)-1/3hasbeensuggested[22,23],wherea isthelocaliza-tionlengthandg isanumericalcoefficient.Thespreadofvaluesforg intheliteratureisenormous.Forexample,in[22]g wasestimatedas1.056<g <1.076whilein[23]itwasclaimedtobeintherange1.54<g <1.59,dependingontemperature.Thisdif-ferenceing leadstothedifferenceinm valuesatlowconcentrations(Na3)1/3<0.02ofmore than10ordersofmagnitude!.Since there isnocross-citationbetween[22]and[23],publishedinthesameyear,itisdifficulttoguesswhichofthesecontradic-toryresultstheauthorsconsiderascorrect.Weshowbelowthatneitheroftheseresultsseemcorrect.Furthermore,whileinsomerecentpublicationsitiscorrectlyclaimedthataveragingofhoppingratesleadstotheomissionoftheconcentrationdependence
c06.indd 223 5/6/2006 06:08:02 PM
224 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
ofthecarriermobilitym (N)[23]inotherpublicationsbythesameauthorsitisclaimedthataveragingofhoppingratesiscapableofdescribingtheconcentrationdependenceofthemobility[24,25].Remarkably,whattheauthorscallaveragingofhopingratesin[24,25]isnotwhattheycallaveragingofhoppingratesin[18–21,23].Evenmoreremarkable is the statement of a recent publication [26] that the results of [18–21],claimingthelineardependencem (N),arecorrect.Thereareotherrecentpapersthatleadtothisconclusion[27,28].Thebeliefoftheresearchersworkingwithdisorderedorganicsemiconductorsintheaveragingofhoppingratesissostrongthatsometimestheagreementbetweenexperimentalresultsandthecorrectformulaswithexponentialdependence m (N) are called occasional, because the latter dependence cannot beobtainedbyaveragingofhoppingrates[29].
This unsatisfactory situation with theoretical description of hopping conductivity inorganic disordered solids shows that many researchers working with hopping transportin organic semiconductors are not familiar with the basic fundamental ideas, wellapproved and known in the parallel field of hopping transport in inorganic disorderedsystems.Our aim in this chapter is to provide thedescriptionof these elementary ideasinapplicationtorandomorganicsystems.Forexample,usingtheroutineVRHapproach[30,31]wecalculate thedependencem (N) inorganicdisorderedsolids. Itappears tobein agreement with experimental data. Only in the limit of very dilute systems is thedependenceln(m)∝ -g (Na3)-1/3valid,butwithg 1.73,inagreementwiththeclassicalpercolation result [17] and at variance with the results of [18–21, 23–25, 27, 28].
Inthenextsectionwebrieflydescribethemodelforchargecarriertransportindisor-deredorganicsemiconductorsformulatedandjustifiedinpreviousreviews[1,5,7,8,12,13]. In subsequent sections we describe theoretical methods which provide transparentsolutionsofvarioustransportproblemsintheframeworkofthismodel.
6.2 CHARACTERISTIC EXPERIMENTAL OBSERVATIONS AND THE MODEL FOR CHARGE CARRIER TRANSPORT IN RANDOM ORGANIC SEMICONDUCTORS
Althoughthevarietyofdisorderedorganicsolidsisveryrich,thedetailsofchargetrans-port in most of such materials are common. The canonical examples of disorderedorganic materials with the hopping transport mechanism are the binary systems thatconsistofdopedpolymericmatrixes.Examplesincludepolyvinylcarbazole(PVK)orbis-polycarbonate (Lexan)dopedwitheither strongelectronacceptors suchas, for example,trinitrofluorenoneactingasanelectrontransportingagent,orstrongelectrondonorssuchas, forexample,derivativesof triphenylamineor triphenylmethaneforhole transport.Toavoidthenecessityofspecifyingeachtimewhetherchargetransportiscarriedbyelectronsorholes,inthegeneraldiscussionbelowweusethenotation‘chargecarrier’.Theresultsarevalidforeachtypeofcarriers—electronsorholes.Chargecarriersinrandomorganicmaterialsarebelievedtobehighlylocalized.Localizationcentersaremoleculesormolecu-larsubunits,henceforthcalledsites.
Inordertounderstandthechargetransportmechanisminrandomorganicsolids,letusbrieflyrecallsomeexperimentalobservationsthataredecisiveforformulatingthetransport
c06.indd 224 5/6/2006 06:08:03 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 225
Y2
model.Amongthesearethedependencesofthecarrierdriftmobility,diffusivityandcon-ductivityontemperatureT,onthestrengthofappliedelectricfieldF,andonsuchimportantmaterialparametersasthespatialconcentrationoflocalizedstatesN.
(i) Dependence of transport coefficients on the concentration of localized states.Alreadyintheearlystagesofthestudyofmolecularlydopedpolymersitwasestablishedthatthe dependence of the carrier kinetic coefficients on the concentration of localizedstatesisverystrongandthatitisessentiallynonlinear[32].InFigure6.1thedepend-ence of the logarithm of the carrier drift mobility, ln(m), on R = N-1/3 obtained intime-of-flight experiments is shown. This extremely nonlinear dependence at lowconcentrationscanbefittedbytheexpression
µα
∝ -
-
exp2 1 3N
(6.1)
Figure 6.1 Electronandholemobilitydataplottedasafunctionoftheaverageseparationbetweenuncomplexedmoleculestreatedaslocalizedstates(reproducedwithpermissionfrom[32].Copyright1972,AmericanInstituteofPhysics)
c06.indd 225 5/6/2006 06:08:03 PM
226 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
whichGill[32]suggestedinthisform,assumingthata isthelocalizationlengthofchargecarriersinthelocalizedstates.Asshownin[14],suchdependenceoftransportcoefficientsontheconcentrationoflocalizedstatesN ischaracteristicforincoherenthopping transportmechanism inwhich thechargecarrierhopsbetween thenearestavailable localizedstates. Indeed,sucha transportmode isexpectedfor thecaseoflowconcentrationsN,atwhichthemainlimitingfactorforcarriertransitionsbetweenlocalizedstatesisprovidedbytheexponentialdistancedependenceofhoppingprob-abilities (see [14]). At high concentrations, the deviations from the dependencedescribedbyEquation(6.1)wereobservedexperimentally[33],asexpectedforhoppingtransport in theVRHmode thatsucceeds thenearest-neighbor transportmodewithrisingN.Thisresultshouldbeconsideredasthekeyobservationleadingtotheconclu-sionthattransportmechanismindisorderedorganicsolidsistheincoherenthoppingofchargecarriersbetweenspatiallylocalizedstates.
(ii) Dependence of transport coefficients on temperature.Thetemperaturedependenceofthe drift mobility obtained in time-of-flight experiments in random organic solidsusuallytakestheform
µ ∝ -
expT
T0
2
(6.2)
whereT0isaparameter[1,4,5,7,8,12,13].However,inseveralstudiesanArrheniusdependencehasalsobeenreported
µ ∝ -
exp
DkT
(6.3)
whereD is theactivationenergy.Usually the latterdependence inorganicmaterialsisobservedbymeasurementsof theelectricalconductivity infield-effect transistors(see, for instance, [34]). We will show below that both temperature dependencesdescribedbyEquations(6.2)and(6.3)arepredictedtheoreticallyintheframeofthesametransportmodel,dependingonthetotalconcentrationofchargecarriersinthesystem.At lowcarrierdensities thedependencedescribedbyEquation (6.2) ispre-dicted, while at high carrier densities the dependence described by Equation (6.3)shouldbevalid.
(iii) Dependence of transport coefficients on the strength of the applied electric field.Numerous experimental studies have shown that at high electric fields the chargecarrier transportcoefficients increasewith thefieldstrengthF, beingapproximatelyproportionaltoexp[(F/F0)1/2]inabroadrangeoffieldstrengths,withsomeparameterF0[5,7,8,12,13].Morecuriously,ithasbeenreportedthatathightemperaturesthecarrierdriftmobilitymeasuredintime-of-flightexperimentsincreaseswithdecreasingfieldatratherlowfieldstrengthes[5,7,8,12,13].
Whenformulatingtheappropriate transportmechanismforchargecarriers inrandomorganic materials such as molecular glasses and molecular doped polymers, one shouldkeepinmindtheseexperimentalobservations.
c06.indd 226 5/6/2006 06:08:03 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 227
Y2
The corresponding model established to treat the charge carrier transport in randomorganicsolidsisasfollows[1,5,7,8,12,13].ItisassumedthatchargecarriersmoveviaincoherenthoppingtransitionsbetweenlocalizedstatesrandomlydistributedinspacewithsomeconcentrationN.Allstatesarepresumedtobelocalized.Theenergiesofchargecar-riersonthesestatesareassumedtohaveaGaussiandistributionsothatthedensityofstates(DOS)takestheform
gNε
σ πεσ
( ) = -
2 2
2
2exp (6.4)
wheres is the energy scale of the distribution and the energye is measured relative tothe center of the DOS. The origin of the energetic disorder is the fluctuation in thelatticepolarizationenergiesandthedistributionofsegmentlengthinthep-ors-bondedmain-chainpolymer[8].TheGaussianshapeoftheDOSwasassumedonthebasisoftheGaussianprofileoftheexcitonicabsorptionbandandbyrecognitionthatthepolarizationenergyisdeterminedbyalargenumberofinternalcoordinates,eachvaryingrandomlybysmallamounts[8].LaterwewillseethattheGaussianshapeoftheDOSaccountsfortheobservedtemperaturedependenceofthekineticcoefficientssuchascarrierdriftmobility,diffusivity,andconductivity.Theenergyscales oftheDOSinmostrandomorganicmate-rials is of the order of ~0.1eV [8]. In the initial model, no correlations between spatialpositionsoflocalizedstatesandtheirenergieswereincluded[8].Forthesakeofsimplicitywewillassumebelowthatthisassumptionvalidunlessthecontraryisspecified.
A tunneling transition rate of a charge carrier from a localized state i to a lower inenergy localized state j dependson the spatial separationrij between the sites i and j asn (rij)=n0exp(-2rij/a),wherea isthelocalizationlengthwhichweassumeequalforsitesi and j.This lengthdetermines the exponential decayof the carrierwavefunction in thelocalizedstates.Thedecaylengthonsinglesiteshasbeenevaluatedinnumerousstudiesoftheconcentration-dependentdriftmobility.Forexample,fortrinitrofluorenoneinPVKtheestimatesa 1.1× 10-8cmanda 1.8× 10-8cmwereobtainedforholesandelec-trons,respectively[32].FordispersionsofN-isopropylcarbazoleinpolycarbonatetheesti-matea 0.62× 10-8cmforholeshasbeenobtained [35].Thepreexponential factorn0depends on the electron interaction mechanism that causes the transition. Usually it isassumed that carrier transitions contributing to charge transport in disordered materialsarecausedbyinteractionswithphonons.Oftenthecoefficientn0issimplyassumedtobeof theorderof thephonon frequency~1013s-1, althoughamore rigorousconsideration isinfactnecessarytodeterminen0.Suchaconsiderationshouldtakeintoaccountthepar-ticular structure of the electron localized states and also the details of the interactionmechanism[36,37].
Whenachargecarrierperformsatransitionupwardinenergyfromalocalizedstatei toahigherinenergylocalizedstatej,thetransitionratealsodependsontheenergydiffer-encebetweenthestates.Thisdifferenceshouldbecompensated,forexample,byabsorptionof a phonon with the corresponding energy [38]. Generally, the transition rate from theoccupiedsitei toanemptysitej canbeexpressedas
v r vr
kTij i j
ij j i j i, , exp expε εα
ε ε ε ε( ) = -
-
- + -
0
2
2 (6.5)
c06.indd 227 5/6/2006 06:08:04 PM
228 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Ifthesystemisinthermalequilibrium,theoccupationprobabilitiesofsiteswithdifferentenergiesaredeterminedbytheFermistatistics.ThiseffectcanbetakenintoaccountbymodifyingEquation(6.5)andaddingtermswhichaccountfortherelativeenergypositionsofsitesi andj withrespecttotheFermienergyeF.Takingintoaccounttheseoccupationprobabilitiesoneshouldwritethetransitionratebetweensitesi andj intheform[38]
v vr
kTij
ij j F j F j i= -
-
- + - + -
0
2
2exp exp
αε ε ε ε ε ε
(6.6)
With thehelpof theseformulas theproblemof the theoreticaldescriptionofhoppingconductioncanbeeasilyformulated.Onehastocalculatetheconductivitywhichispro-videdbytransitioneventswiththeratesdescribedbyEquations(6.5)or(6.6)inthemani-foldoflocalizedstateswiththeDOSdescribedbyEquation(6.4).
Unfortunately,ithasbecomeacommonbeliefthattheGaussianformoftheDOSpre-ventsclosed-formanalyticalsolutionsofthehoppingtransportproblemsinrandomorganicsystemsandthereforethebestwaytostudytheseproblemsisacomputersimulation[7,8,12,13].Wewilldoourbestinthisreporttoprovetheopposite.However,beforedoingsowe would like to present several important results obtained previously by computersimulations.
6.3 ENERGY RELAXATION OF CHARGE CARRIERS IN A GAUSSIAN DOS. TRANSITION FROM DISPERSIVE TO NONDISPERSIVE TRANSPORT
One of the most remarkable results known for energy relaxation of charge carriers in aGaussianDOSistheexistenceoftheso-calledequilibrationenergy⟨e∞⟩ [7,8,12,13].ThissituationisincontrasttothecaseoftheexponentialDOS,whereintheemptysystematlow temperatures thechargecarrier always relaxesdownward inenergy, asdiscussed in[14].TheenergyrelaxationintheexponentialDOSleadstothedispersivecharacterofthechargetransport,inwhichkineticcoefficientsaretimedependentandthecarriermobilityslowsdown in thecourseof theenergy relaxation,asdescribed in [14]. In theGaussianDOS thechargecarrieronaverage relaxes fromhigh-energystatesdownward inenergyonlyuntilitarrivesattheequilibrationenergy⟨e∞⟩, evenintheemptysystemwithoutanyinteractionsbetween the relaxingcarriers [7,8, 12,13]. In computer simulations [8,12,13],noninteractingcarrierswereinitiallydistributeduniformlyinenergyandtheirfurtherrelaxationviahoppingprocesseswiththeratesdescribedbyEquation(6.5)wastraced.ThetemporalevolutionofapacketofnoninteractingcarriersrelaxingwithinaGaussianDOSisschematicallyshowninFigure6.2.InitiallytheenergydistributionofcarrierscoincideswiththatoftheDOS.Inthecourseoftimethecarrierenergydistributionmovesdownwarduntilitsmaximum⟨e (t)⟩ arrivesattheenergy⟨e∞⟩=limt→∞⟨e (t)⟩=-s2/kT [8,12,13].Thisresultcanbeeasilyobtainedanalytically[39].Inthermalequilibrium
εε ε ε ε
ε ε ε εσ
∞-∞∞
-∞∞
=( ) -( )( ) -( )
= -∫∫
d
d
g kT
g kT kT
exp
exp
2
(6.7)
c06.indd 228 5/6/2006 06:08:04 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 229
Y2
Thetimerequiredtoreachthisequilibriumdistribution(calledtherelaxationtime)trel isofkey importance for the analysisof experimental results [40]. Indeedat time scalesshorterthantrel,chargecarriersinitiallyrandomlydistributedoverlocalizedstatesperformadownwardenergyrelaxationduringwhichtransportcoefficients,suchasthecarrierdriftmobility, essentially depend on time, and charge transport is dispersive, as described in[14]. At time scales longer thantrel, the energy distribution of charge carriers stabilizesaround the equilibration energy ⟨e∞⟩, even in a very dilute system with noninteractingcarriers.Insucharegime,transportcoefficientsaretimeindependent.Inotherwords,att trel dispersivetransportissucceededbythenondispersive(Gaussian)transportbehavior.Thisisoneofthemostimportantresultsforchargecarriertransportindisorderedorganicmedia[8].Whileatshorttimesdispersivecurrenttransientswereobservedinsuchmateri-als,atlongtimestransportcharacteristicsarenondispersive,timeindependentandhencetheycanbewellcharacterizedanddescribedincontrasttoanalogousquantitiesininorganicdisorderedmaterialswithexponentialDOS.Inthelattermaterials,asshownin[8],trans-port coefficients in dilute systems are always dispersive (time dependent). Hence, theydependonsuchexperimentalconditionsasthelengthofasampleandthestrengthoftheelectricfield.ThereforethetransportcoefficientsindisorderedmaterialswithexponentialDOScanhardlybecharacterized.On thecontrary, inorganicdisorderedmaterialswithGaussian DOS, transport coefficients do not depend on the experimental conditions att >trel andhencetheycanbewellcharacterized.Ithasbeenestablishedbycomputersimu-lationsthattrel stronglydependsontemperature[8,40],
τ σrel exp∝
B
kT
2
(6.8)
wherenumericalcoefficientB isclosetounity:B 1.1.Ithasalsobeenfoundbycomputersimulationsthatthecarrierdriftmobilitym atlongtimescorrespondingtothenondispersivetransportregimehasthefollowingpeculiartemperaturedependence[7,8,12,13,40]
Figure 6.2 Temporal evolution of the distribution of carrier energies in a Gaussian DOS(s /kT=2.0).⟨e∞⟩ denotesthetheoreticalequilibriumenergydeterminedbyEquation(6.7)(repro-ducedwithpermissionfrom[8].Copyright1993,Wiley-VCH)
c06.indd 229 5/6/2006 06:08:05 PM
230 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
µ σ∝ -
exp
C
kT
2
(6.9)
ForcoefficientC thevalueC=2/3hasbecomeaconventionalone[7,8,12,13,40].Infact,computer simulations [41]give for thiscoefficient thevalueC 0.69,while rathersophisticatedanalyticalcalculations[39,42]predictaclosevalueC 0.64.Equation(6.9)withC=2/3isbelievedtobeuniversal,anditiswidelyusedtodeterminetheenergyscales oftheDOSfromtheexperimentalmeasurementsoftheln(m)versusT -2[43,44].
However,itlooksratherstrangethatthecoefficientsC andB inEquations(6.8)and(6.9)areconsideredastheuniversalones.Infact, it is themainfeatureoftheVRHtransportmodethatthespatialandenergyparametersareinterconnectedinthefinalexpressionsfortransportcoefficients[17].Equations(6.5)and(6.6)showthatboththeenergydifferencebetween localized states and the spatial distance between them determine the hoppingprobability.Hoppingtransportinasystemwithspatiallyandenergeticallydistributedlocal-izedstatesisessentiallyaVRHprocessasdescribedin[14].Insuchaprocess,thetransportpathusedbychargecarriersisdeterminedbybothenergyandspatialvariablesintransitionprobabilities. It means that the temperature dependence of transport coefficients shouldinclude the spatialparameterNa3,while thedependenceof transport coefficientson theconcentrationN of localizedstatesshoulddependon the temperaturenormalizedby theenergyscaleoftheDOS,kT/s.Incomputersimulations[41],aparticularvalueofthespatialparameterwastaken:Na3=0.001andthemagnitudeC 0.69wasobtainedforthispar-ticularvalueofNa3.ThequestionthenarisesonwhetherthisvalueofC isstableagainstvariationsofNa3.
Thereisanotherimportantquestion,alreadyraisedinthescientificliterature[40],thatisrelatedtotheapparentdifferenceinthetemperaturedependencesoftrel andm expressedbythedifferencebetweencoefficientsC andB inEquations(6.8)and(6.9).Therelaxationtimetrel atwhichatransitionfromdispersivetonondispersivetransportshouldtakeplacedependsontheratios /kT morestronglythanonthecarrierdriftmobilitym.Thishasanimportantconsequencethatatime-of-flightsignalproducedbyapacketofchargecarriersdrifting across a sample of some given length must become dispersive above a certaindegreeofdisorder,i.e.,belowacertaintemperatureatotherwiseconstantsystemparame-ters,becauseeventuallytrel willexceedthecarriertransienttime[40].Thetimeevolutionofthetime-of-flightsignalisshowninFigure6.3asafunctionoftheratios /kT.Theearlyanalyticaltheories[39,42]alreadyindicatedthedifferencebetweencoefficientsC andB,althoughtheypredictedC >B incontrasttothesimulationresults.Thereforeabetterana-lytical theory for description of the VRH transport in a system of random sites with aGaussiandistributionisdefinitelydesirable.
6.4 THEORETICAL TREATMENT OF CHARGE CARRIER TRANSPORT IN RANDOM ORGANIC SEMICONDUCTORS
6.4.1 Averaging of hopping rates
Theattempts todevelopamore transparentandusable theory than that in [39,42]wereperformedbyArkhipovandBässler [18–21].The resultobtained for thedependencesof
c06.indd 230 5/6/2006 06:08:05 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 231
Y2
the carrier mobility on temperature, T, and on the concentration of localized states, N,reads[18–21]
µ π ασ
σ= -
1 20
5 2
2
1
4
ev N
kTexp (6.10)
Asimilarexpression isprovidedby themodelofRoichmanandco-workers [27,28].This result gives for the temperature dependence a numerical coefficient 1/4 in front of(s /kT)2intheexponent,whichistwiceassmallastheone(1/2)predictedbycomputersimulations[8,40,41]andbypreviousanalytical theories[39,42].Moreimportant, thisexpressionpredictsalineardependenceofthecarriermobilitym onN incontradictiontoexperimentalresults[32].
Thereasonforthesecontradictionsisrathertransparent.Equation(6.10)isobtainedbythe configurational averaging of hopping rates [18–21]. Although this method has beenalready analyzed in textbooks (see, for instance, [17]) andqualified as inappropriate for
Figure 6.3 Time-of-flight signal, parametric in s /kT (sample length 8000 lattice planes,F =6×105Vcm-1)(reproducedwithpermissionfrom[8].Copyright1993,Wiley-VCH)
c06.indd 231 5/6/2006 06:08:06 PM
232 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
treatmentofhoppingtransportindisorderedmaterials,itisrepeatedlyusedbynumerousresearchers.Thisoccursnotonlyinthestudiesofchargetransport,butalsointhestudiesofthehoppingcarrierenergyrelaxation.Forexample,itisoftenclaimedintheliteraturethatexponentialdependenceofthelocaltransitionratesonthedistancesbetweenlocalizedstatesis‘averagedout’inthefinalresultsfortherelaxationrateleadingtothelineardepend-enceoftherelaxationrateontheconcentrationofstatesN (see,forinstance[45]).However,ithadbeenalreadyemphasizedbyAmbegaokaret al.in1971[46]ataveryearlystageofthestudyofhoppingtransportthatanessentialingredientofasuccessfultheoryforhoppingtransportindisorderedmaterialsisthatittakesintoaccountthathoppingisnotdeterminedbytherateof‘average’hops,butratherby therateof thosehops thatare‘mostdifficultbutstillrelevant’:hoppingconductionisinfactapercolationproblem.Unfortunately,thebeliefoftheresearchersworkingwithdisorderedorganicsemiconductorsintheaveragingofhoppingratesissostrongthatsometimestheagreementbetweenexperimentalresultsontheexponentialdependencem (N)withEquation(6.1)arecalledoccasional,becausethelatterequationcannotbeobtainedbyaveragingofhoppingrates[29].Wethereforefinditnecessarytoclarifyoncemoretheinvalidityof theensembleaveragingofhoppingratesforthedescriptionofhoppingtransportindisorderedmaterials,althoughthisinvalidityhasbeenalreadyexplainedintextbooks(see,forinstance,[17]).
Intheapproachbasedontheaveragingofhoppingrates,oneassumesthatcarriermobil-ityisproportionaltotheaveragehoppingrate⟨n⟩ multipliedbythesquaredtypicaldisplace-mentr2ofachargecarrierinsinglehoppingevents:m ∝ r2⟨n⟩.Theshortcomingofsuchatreatmentismostlytransparentinthecaseofhightemperatures,kT >s,atwhichchargetransport takesplacevianearest-neighborhopping.Thelatter is trueunder theconditionNa3<<1necessaryforelectronstatestobelocalized,asassumedinthemodel[7,8,12,13,40].AthighT, theenergy-dependent terms in transitionprobabilitiesdonotplayanessentialroleandthehoppingratesaredeterminedmostlybyspatialseparationsbetweenlocalizedstates:n (r) n0exp(-2r/a).Multiplyingthistransitionprobabilitybytheprob-abilitydensitytofindthenearestneighboratagivendistancer,providedthetotalconcen-trationofsitesisN:j(r)dr=4pr2N exp(-4pr3N/3)dr andintegratingoverdistances,oneobtainsfortheaveragehoppingrate:
v r vr
r N r N v N= -
-
∞
∫ d 00
2 30
324
4
3exp exp
απ π π α (6.11)
Itiseasytounderstandthisresult.Duetotheverystrongdecreaseofthefunctionn (r)=n0 exp(-2r/a) with increasing r at the scale r a and due to the weak dependenceof the functionj(r)= 4pr2N exp(-4pr3N/3)onr atr a , theaveragehopping rate inEquation(6.11)isdeterminedbytransitionswithr a ,sincethemaincontributiontotheintegralcomesfromsuchdistancesr a.Assumingm ∝ r2⟨n⟩ withr a and⟨n⟩ describedbyEquation(6.11)oneobtains[18–21,27,28]m ∝ n0Na5,asexpressedinEquation(6.10).Thisresultishoweverinvalidforadilutesystemoflocalizedstates,forwhichtheconditionNa3<< 1shouldbefulfilledtojustifythelocalization.Theaveragehoppingrateisdeter-mined by transitions over the distances r a with the raten n0. The probability offindingsuchaclosepairofsiteswithr a atthetotalconcentrationN ofsitesispropor-tionaltoNa3.Thisisthereasonwhytheresultfortheaveragehoppingrate⟨n⟩ islinearlyproportional to N. However, the charge carrier cannot move over considerable distancesusingonly transitionswith the lengthr a ina systemwith lowconcentrationof sites
c06.indd 232 5/6/2006 06:08:06 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 233
Y2
Na3 << 1. Therefore, the averaging of hopping rates cannot describe the charge carrierkineticcoefficientsinarandomorganicmaterialsandothertheoreticalmethodsshouldbeused.
6.4.2 Percolation approach
Oneofthemostpowerfultheoreticaltoolstodescribechargecarriertransportindisorderedsystems isprovidedby thepercolation theoryasdescribed innumeroushandbooks (see,for instance, [17]).Webrieflydescribed thismethod inChapter2[14].According to thepercolationtheory,onehas toconnectsiteswithfastest transitionrates inorder tofulfilltheconditionthattheaveragenumberZ ofbondspersiteonthetransportpathisequaltotheso-calledpercolationthreshold[17,47,48]:
Z B≡ = ±C 2 7 0 1. . (6.12)
Thismethodhasbeenverysuccessfullyappliedtothetheoreticaldescriptionofhoppingtransport indopedcrystalline semiconductors [17]andalso indisorderedmaterialswithexponential DOS [49]. The treatment of charge transport in disordered systems with aGaussianDOSintheframeworkofthepercolationtheorycanbefoundin[50,51].However,thistheoryisnoteasyforcalculations.ThereforeitisdesirabletohaveamoretransparenttheoreticaldescriptionoftransportphenomenaindisorderedsystemswithaGaussianDOS.Inthenextsectionwepresentsuchanapproachbasedonthewell-approvedconceptofthetransportenergy,thatwassuccessfullyappliedearliertodescribetransportphenomenaininorganicdisorderedsystemswithexponentialDOS.
6.4.3 Transport energy for a Gaussian DOS
Theroutineandsofarwidelyacceptedinterpretationofthetemperaturedependenceofthecarrier mobility described by Equation (6.9) claims that activation of carriers from theenergylevel⟨e∞⟩ determinedbyEquation(6.7)tosometransportlevelisresponsibleforthedriftmobilitym [4,8,12,13,40].Furthermore,ithasbeenclaimed[52]thatEquation(6.9)alongwith(6.7)wouldascertainthetransportleveltobeat⟨e∞⟩ +(Cs)2/kT ≈ -5s2/(9kT).However, in such interpretation one treats the hopping transport as a pure activation ofchargecarriersfromthelevel⟨e∞⟩ overtheactivationbarrierwiththehight(Cs)2/kT neces-sarytoobtainEquation(6.9).Thetransportmechanism,inwhichtransitionprobabilitiesarelimitedsolelybytheenergyactivation,mightbevalidinorderedcrystallinesemicon-ductors.Transportinrandomdisorderedmaterialsis,however,ahoppingprocesslimitednotonlybytheenergyactivation,butalsobythenecessityforchargecarrierstotunnelinspacebetweenthelocalizedstates.Itistheinterplaybetweenspatialandenergy-dependentterms in the transitionprobabilities thatdetermines thehopping transportprocess in theVRHregime.Remarkablyitissometimesclaimed[52]thatindisorderedsystemswithaGaussian DOS there is no transport energy in the VRH sense. We disagree with suchstatements and show below that the transport energy for the Gaussian DOS can becalculated in full analogy with the corresponding derivation for the exponential DOSdescribedin[14],whereitwasshown,following[53–57]thataparticularenergylevelet,
c06.indd 233 5/6/2006 06:08:07 PM
234 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
called by Monroe [53] the transport energy (TE), determines all hopping transportphenomena.
Theconceptof transportenergycanbeeasilyextended todescribehopping transportphenomenainadisorderedsystemwiththeGaussianDOS[58].SincethederivationoftheTEfortheGaussianDOSisabsolutelyanalogoustothatfortheexponentialDOSdescribedin[14],wepresentherethisconceptinacompactedform.TheintroductionoftheTEmakessense only at low temperatures, kT <s, in the VRH regime, since otherwise the trivialnearest-neighborapproximationisvalid(see[14]).Qualitatively, theenergyrelaxationofcarriersinaGaussianDOSisschematicallyshowninFigure6.4.Atlowtemperatures,kT <s,carriersplacedinthehigh-energypartoftheGaussianDOSperformdownwardenergytransitionsuntiltheyreachaparticularenergylevelet calledthetransportenergy.Atet thecharacteroftherelaxationchanges.Afterahoptoastatebelowet,thecarrierhopsupwardinenergytoastateinthevicinityofet.Thishoppingprocessnearandbelowet resemblesamultiple-trappingprocesswhereet playstheroleofthemobilityedge.Inordertocalculateet,oneshouldfindthemaximumofthehoppingtransitionprobabilitywithrespecttotheenergyofthefinalstateex foracarrierplacedinitiallyatasitewithdeepenergyei:
d
d
v i x
x
↑ ( ) =ε εε
, .0 (6.13)
Itiseasytoshow[58]thatthefinalenergyet determinedbyEquation(6.13)doesnotdependontheinitialenergyei andhenceitisuniversalforgivenparameterss /kT andNa3.TheTEinarandomsystemwiththeGaussianDOSisdeterminedas
ε σ α σt = ( )X N kT3, (6.14)
whereX(Na3; kT/s)isthesolutionoftheequation[58]
Figure 6.4 SchematicpictureofcarrierenergyrelaxationintheGaussianDOSviathetransportenergy et (reproduced with permission from [31]. Copyright 2000 by the American PhysicalSociety)
c06.indd 234 5/6/2006 06:08:07 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 235
Y2
exp expX
t t N kTX2
22
4 31 2 3 1 3
29 2
-( )
= ( ) -∞
-
∫ d π α σ (6.15)
Ithasbeenshown[58]thatatlowtemperatures,kT <s,themaximumdeterminedbyEquation(6.13)issharpandthereforetheintroductionoftheTEforaGaussianDOSmakessense.AnequationfortheTEinaGaussianDOSliterallycoincidingwithEquation(6.15)waslaterpublishedbyArkhipovet al.[59],whoalsoclaimedthattheconceptoftransportenergyisapplicabletopracticallyallrealisticDOSdistributions.Wecannotagreewiththelatterstatement.Ithasbeenshownin[58]that,forexample,inasystemwiththeDOSinthe form g ε ε ε( ) ∝ -( )exp 0 themaximumdeterminedbyEquation (6.13) is sobroadandthepositionofet issodeepinthetailoftheDOSthatintroductionoftheTEmakesnosense.TheDOSdescribedbythelatterformulaisknowntobevalidforsuchabroadclassofdisorderedsystemsasthemixedcrystalswithcompositionaldisorder[60].Henceit should be considered as a realistic one. Furthermore, sometimes the TE approach isapplied toasystemwithaconstant,energy-independentDOS[61].Wedonot think thatsuchaprocedureismeaningful.IftheenergydependenceoftheDOSisweak,thetransportpathintheequilibriumconditionscorrespondstothevicinityoftheFermilevel.Concomi-tantly, the temperaturedependenceof theconductivityobeys theclassicalMott formula:s (T)∝ (T0/T)1/4,asdescribedin[14].Inthenexttwosubsectionswedescribehowonecanuse theconceptof transportenergy inorder toexplainexperimentallyobserveddepend-ences of the transport coefficients on temperature and on the concentration of localizedstates,N,inasystemwithGaussianDOS.
6.4.4 Calculations of trel and m
Afterhavingunderstood the relaxationkinetics, it is easy to calculatetrel andm.Letusstartwithtemperaturedependencesofthesequantities.Weconsiderthecase⟨e∞⟩ <et <0,whichcorresponds toany reasonablechoiceofmaterialsparametersNa3 andkT/s [58].Aftergenerationofcarriers inanonequilibriumsituation, thecarrierenergydistributionmovesdownwardinenergywithitsmaximum⟨e (t)⟩ logarithmicallydependentontimet [8,40,41].Statesabove⟨e (t)⟩ achievethermalequilibriumwithet attime t,whilestatesbelow⟨e (t)⟩ havenochanceattimet toexchangecarrierswithstatesinthevicinityofet,andhencetheoccupationofthesedeepenergystatesdoesnotcorrespondtotheequilibriumoccupation. The system of noninteracting carriers comes into thermal equilibrium whenthetime-dependentenergy⟨e (t)⟩ achievestheequilibriumlevel⟨e∞⟩ determinedbyEquation(6.7).Thecorrespondingtimeistherelaxationtimetrel [8,40,41].Atthistime,dispersiveconductionisreplacedbytheGaussiantransport[8,40,41].Aslongastherelaxationofcarriersoccursviathermalactivationtothelevelet,therelaxationtimetrel isdeterminedbytheactivatedtransitionsfromtheequilibriumlevel⟨e∞⟩ tothetransportenergyet [31].HenceaccordingtoEquation(6.5),trel isdeterminedbytheexpression[31]
τ εα
ε εrel
t t= ( ) + -
- ∞vr
kT0
1 2exp (6.16)
where
c06.indd 235 5/6/2006 06:08:08 PM
236 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
r gε π ε εε
( ) = ( )
-∞
-
∫4
3
1 3
d (6.17)
From Equations (6.14–6.17) it is apparent that the activation energy of the relaxationtimeinEquation(6.16)dependsonbothparameterss /kT andNa3,andtherefore,generallyspeaking,thisquantitycannotberepresentedbyEquation(6.8)and,ifatall,thecoefficientB shoulddependonthemagnitudeoftheparameterNa3.
Letuscalculatetheexponentinthetemperaturedependenceoftrel inEquation(6.16),ln(treln0),andplotitasafunctionof(s /kT)2forvariousvaluesofNa3.SolvingEquation(6.15) numerically and using Equations (6.7), (6.14–6.17), one obtains results given inFigure6.5.ForNa3=0.001,thedependencedescribedbyEquation(6.8)withB 1.0isingoodagreementwithcomputersimulationsthatgiveB 1.1[8,40].HencetheresultoftheanalyticcalculationsconfirmsEquation(6.8).However,Equation(6.8)canbecon-sideredonlyasanapproximationbecause itoriginates fromratherdifferent temperature
Figure 6.5 TemperaturedependencesoftherelaxationtimefordifferentvaluesofNa3.SolidlinesrepresentthebestfitsintheformofEquation(6.8)fordependencesobtainedbynumericalsolutionofEquations(6.15)and(6.16).ThevaluesoftheparameterB obtainedfromsuchafitarespecifiedin the text (reproduced with permission from [31]. Copyright 2000 by the American PhysicalSociety)
c06.indd 236 5/6/2006 06:08:08 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 237
Y2
dependencesofdifferenttermsintheexponentofEquation(6.16).Thispossibilityofeffec-tivedescriptionviaEquation(6.8)isprovidedbythestrongtemperaturedependenceof⟨e∞⟩ givenbyEquation (6.7)while the temperaturedependencesof thequantitieset andr(et)areweakerandtheyalmostcanceleachotherinEquation(6.16).However,atanothervalueof theparameterNa3=0.02, the relaxation timetrel isdescribedbyEquation(6.8)withanothervalueofthecoefficientB 0.9.ThisclearlyshowsthatthetemperaturedependenceinEquation(6.8)cannotbeuniversalwithrespecttotheconcentrationoflocalizedstatesN andthedecayparameterofthecarrierwavefunctiona.
Nowweturntothecalculationofthecarrierdriftmobilitym.Weassumethatthetran-sienttimettr,necessaryforacarriertotravelthroughasampleislongerthantrel,andhencethechargetransporttakesplaceintheequilibriumconditions.Asdescribedabove,everysecondjumpbringsthecarrierupwardinenergytothevicinityofet, beingsucceededbya jump to the spatially nearest site with deeper energy determined solely by the DOS.Therefore, inorder tocalculate thedriftmobility,m , it iscorrect toaveragethe timesofhopping transitions over energy states below et, since only these states are essential forcharge transport in thermal equilibrium [30, 31]. Hops downward in energy from thelevelet occurexponentiallyfasterthanupwardhopstowardset.Therefore,onecanneglectthe former in the calculation of the average time hti. The carrier drift mobility can beevaluatedas
µ ε
e
kT
r
t
2t( )
(6.18)
wherer(et)isdeterminedbyEquations(6.17),(6.14),(6.15)and(6.4).Theaveragehoppingtimehastheform[30]
t g v gr B
kT
t
= ( )
( ) ( )
+-
-∞
--
-∞∫ d d t c1 3
tε ε ε ε εα
ε εε 1
01 2
expεεt
∫ (6.19)
whereBc 2.7 is thepercolationparameter takenfromEquation(6.12).ThisnumericalcoefficientisintroducedintoEquation(6.19)inordertowarranttheexistenceofaninfinitepercolationpathoverthestateswithenergiesbelowet.UsingEquations(6.4),(6.14),(6.15),(6.18) and (6.19), oneobtains for the exponential terms in the expression for the carrierdriftmobilitytherelation
ln expµ ε π απer v
kT BN t t
X20
1
3 224
3t
c
dt( )
= - -( )
-
-∞∫
- -
-1 3
21
2
X
kT kTtσ σ
(6.20)
ItisEquation(6.20)thatdeterminesthedependenceofthecarrierdriftmobilityontheparametersNa3ands /kT.
InFigure6.6thedependenceofthedriftmobilityontemperatureatNa3=0.01isshownfor several values ofs. Equation (6.20) confirms the validity of Equation (6.9), thoughwiththecoefficientC slightlydependentonthevalueoftheparameterNa3.Incomputer
c06.indd 237 5/6/2006 06:08:09 PM
238 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
simulationsthevalueNa3=0.001waschosenandC 0.69wasobtained[41].Equation(6.20)predictsaveryclosevalueC 0.68forNa3=0.001.However,atNa3=0.02weobtainfromEquation(6.20)adifferentvalueC 0.62,whichshowsthatthiscoefficientinEquation(6.9)indeeddependsonthevalueofparameterNa3asexpectedfortheVRHtransportprocess.VerysimilardataforC wereobtainedinseveralotherpapers[61–63].
It is clear from thispicturehowsensitive is themobility to thevalueof temperature.Comparisonofthesedependenceswithexperimentalmeasurementsoftheln(m)versusT -2(someare shown inFigure6.7)provides informationon the energy scales of theDOS(see,forexample,[8,44]).WewouldliketoemphasizehereoncemorethatthechoiceofthenumericalcoefficientC inEquation(6.9)isimportantfortheestimationofs fromthecomparisonwithexperimentaldata.Thisparameter isnotuniversal,beingdependentonthevalueofNa3.
InFigure6.8,thedependenceofthedriftmobilityonNa3isshownforkT/s=0.3.AlsoexperimentaldataofGill[33]areshowninthefigure.Itiswellillustratedthattheslopeof the mobility exponent as a function of (Na3)-1/3 given by the theory described aboveagreeswiththeexperimentaldata.Comparisonbetweenthetheory[30]andexperimentalresults[32,33,35,64]providesanestimateforthedecayparametera ofthecarrierwave-functioninlocalizedstates.Thevaluesbetweena 0.1nmanda 0.3nmareobtained
Figure 6.6 Temperaturedependenceofzero-fieldmobilityinorganicsemiconductorsobtainedviaEquation (6.20) for different disorder energy scales,s (reproduced with permission from [109].Copyright2006bySpringer)
c06.indd 238 5/6/2006 06:08:09 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 239
Y2
dependingonthechosenpolymerandthedopingspecies.Atverylowconcentrationofthelocalizedstates,N, theprobabilityofcarrier tunneling in spacedominates the transitionrate inEquation (6.5). In this regimeof thenearest-neighborhopping, theconcentrationdependenceofthedriftmobilityisdescribedbytheexpression[17]
µ γα
∝ -
-
expN 1 3
(6.21)
whereg=1.73± 0.03[17]asexplainedin[14].Equation(6.21)isillustratedbythedashedlineinFigure6.8.
Inseveralrecentpublications,thedependencedescribedbyEquation(6.21)forrandomorganicsolidswasclaimed,butwithdifferentnumericalcoefficientsg [22–25].Wesupposethatthesedeviationsintheobtainedvaluesofthecoefficientg fromthewell-knowntext-bookresultg=1.73± 0.03arecausedby theunjustifiedassumption thatcarriersalwayshop to theneighboringsitewith theoptimalexponent in the transitionratedescribedby
Figure 6.7 Experimentaldatafortemperaturedependenceofzero-fieldmobilityinorganicsemi-conductors:(1)di-p-tolylphenylaminecontaining(DEASP)-traps[110];(2)(BD)-dopedpolycabonate[43];(3)(NTDI)-dopedpoly(styrene)[111];(4)(BD)-dopedTTA/polycarbonate[112](reproducedwithpermissionfrom[109].Copyright2006bySpringer)
c06.indd 239 5/6/2006 06:08:10 PM
240 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Equation(6.5)[22–25].Suchanassumptionisoftenmadeintheoreticalstudiesofhoppingtransport in organic materials (see, for instance [65]). Expression (6.12) shows howeverthat,whencalculatingtheDC hoppingtransport,oneshouldtakeintoaccountonaveragenot a single neighbor, but at least Bc 2.7 neighbors per site. This average numberBc 2.7isresponsibleforthecorrectvalueofthecoefficientg=1.73± 0.03inEquation(6.21)asdescribedin[14]followingthetextbooks[17].
Wewouldalso like tocommenthereon thecontradictorystatements in the literatureabout the invalidity/validityof theaveragingprocedureforhoppingrates todescribe thehoppingconductivityinrandomsystems.InSection6.4.1,itisshownthatthisprocedureininvalid(seealso[17]).Thishasbeenconfirmedinseveralrecentpublications(see,forinstance,[23]).However, inotherpublicationstheaveragingprocedureforhoppingrateswasclaimedcapableofdescribing thehoppingconductivity [22,24,25,66]. It isworthnotingthattheprocedure,whichtheauthorscalltheaveragingofhoppingratesin[22,24,25,66]isnottheprocedure,whichtheycalltheaveragingofhoppingrates[23]andwhichwasusedin[18–21]anddescribedinSection6.4.1.In[22,24,25,66],theaveragehoppingrateisdefinedviathefollowingchainofarguments.Ononehand,thegeneralexpressionfortheDC conductivityinthefollowingformisused[67]
Figure 6.8 ConcentrationdependenceofthedriftmobilityevaluatedfromEquation(6.20)(solidline)andthedependenceobservedexperimentally[33](squares)forTNF/PEandTNF/PVK.ThedashedlinereferencestheresultofEquation(6.21)withg =1.73forthenearest-neighborhoppingmode(reproducedwithpermissionfrom[30].Copyright2004bytheAmericanPhysicalSociety)
c06.indd 240 5/6/2006 06:08:10 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 241
Y2
σ εµ ε εDC d= ( ) ( )∫e n (6.22)
wheree istheelementarycharge,ñ(e)de istheconcentrationofelectronsinthestateswithenergiesbetweene ande +de andm(e)isthemobilityoftheseelectrons.
Ontheotherhand,oneusesthegeneralexpressionfortheDC conductivityintheformsDC=emn,wheren isthetotalconcentrationofthechargecarriers
n n= ( )-∞
∞
∫ dε ε , (6.23)
andn(e)=g(e)f(e)istheproductofthedensityofstatesg(e)andtheFermifunctionf(e)dependentonthepositionoftheFermienergyeF.
Thequantitym obtainedasm=sDC/en iscalledtobeproportionaltothe‘averagehoppingrate’⟨n⟩ :m ∝ (e/kT)⟨r2⟩⟨n⟩,where⟨r⟩ istheaveragelengthforlocalhoppingevents.Inotherwordsthe‘averagehoppingrate’⟨n⟩isdeterminedviathisrelation.AftercalculatingsDC viaEquation (6.22) andn viaEquation (6.23) andusing the expressionm =sDC/en it isclaimedthatm wascalculatedviaaveragingofhoppingrates.Wewouldjustliketoremarkthatthisdefinitionoftheaverageratelooksunjustified.Itisnotthedefinitionoftheaveragehopping rateused in [23]and ithasnothing todowith theaveragingprocedureused in[18–21]leadingtoEquation(6.10),whichisstilloftenclaimedascorrect(see,forinstance,[26–28]).
6.4.5 Saturation effects
Sofarwehavediscussed thedriftmobilityofchargecarriersunder theassumption thattheirconcentrationismuchlessthanthatofthelocalizedstatesintheenergyrangeessentialforhoppingtransport.Insuchacase,onecanassumethatcarriersperformhoppingmotionindependentlyfromeachotherandcalculatetheconductivityasaproduct
σ µDC = e n, (6.24)
wheren istheconcentrationofchargecarriersinthematerialandm istheirdriftmobilitycalculatedviaEquation(6.20)undertheassumptionthatthesystemisemptyandachargecarrierisnotaffectedbythepossibilitythatlocalizedstatescanbeoccupiedbyothercar-riers.Insucharegime,Equations(6.20)and(6.24)describethedependencesofthecon-ductivityontemperatureandonthevalueoftheparameterNa3,whilethedependenceoftheconductivityontheconcentrationofchargecarriersnislinearinaccordwithEquation(6.24). If,however, theconcentrationn ofchargecarriers is increased so that theFermienergyeF inthermalequilibriumorthequasi-Fermienergyunderstationaryexcitationislocatedenergeticallyhigherthantheequilibriumenergy⟨e∞⟩ determinedbyEquation(6.7),oneshoulduseamoresophisticatedtheoryinordertocalculatesDC.
Let us first estimate the critical concentration of charge carriers nc below which theconsiderationbasedon Equations (6.20) and (6.24) is valid. In order to estimatenc, thevalueoftheFermienergyeF shouldfirstbecalculated.ThepositionoftheFermilevelisdeterminedbytheequation
g
kTn
ε εε ε( )
-( )[ ]=
-∞
∞
∫d
1+exp F
(6.25)
c06.indd 241 5/6/2006 06:08:12 PM
242 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Atlown,forallenergiesinthedomaingivingthemaincontributiontotheintegralinEquation(6.25),theexponentialfunctioninthedenominatoroftheintegralislargecom-paredwithunity (thenondegeneratecase).Thenastraightforwardcalculation [50]givesfortheDOSdeterminedbyEquation(6.4)atlowtemperatures
ε σF -
-
1
2
2
kTkT
N
nln (6.26)
FromtheequationeF (nc)=⟨e∞⟩,where⟨e∞⟩ isdeterminedbyEquation(6.7),oneobtainsfornc theestimate
n NkT
c exp -
1
2
2σ (6.27)
Atn <nc,theFermilevelissituatedbelowtheequilibrationenergy,⟨e∞⟩,andthechargetransport can be described for independent carriers via Equations (6.20) and (6.24). Atn >nc, the theory for charge transport should be essentiallymodified.These argumentscanbeeasilyconvertedinorder toconsider thecaseofconstantconcentrationofchargecarriersandchangingtemperature.ThenatsomeparticulartemperatureTc equationeF (Tc)=⟨e∞⟩ willbefulfilled.AtT >Tc, thecarriermobilityandconductivitycanbedescribedbyEquations(6.20)and(6.24),whileatT <Tc,anessentialmodificationofthetheoryisneeded. Using Equations (6.7) and (6.26) and solving equationeF (Tc) = ⟨e∞⟩ for Tc, oneobtains[50]
Tk N n
c σ
21 2 1 2ln ( ) (6.28)
Inordertodevelopatheoryforhoppingtransportatn >nc (oratT <Tc)oneshouldtakeinto account explicitly the filling probabilities of the localized states by charge carriers.OnepossibilityistosolvethepercolationproblemwithtransitionratesbetweenlocalizedstatesdescribedbyEquation(6.6)thatincludesthevalueoftheFermienergyrelatedviaEquation (6.25) to the concentration of carriers, n [50, 51]. An alternative theoreticalapproachtodescribehoppingconductivityintheGaussianDOS,takingintoaccounttheoccupationoftheessentialfractionoflocalizedstatesbychargecarriers,wasrecentlysug-gestedbySchmechel[62,63].SchmechelextendedtheconceptoftransportenergydescribedinSection6.4.3takingintoaccountthepossibilitythatthelocalizedstatescanbeessentiallyfilledbychargecarriers.AnotherkindofpercolationapproachtotheproblemwassuggestedbyMartenset al.[61].Wewillnotdescribethesetheoriesindetail;theinterestedreadercanfindacomprehensiveanalysisofsomeofthemtheoriesintherecentpaperofCoehoornet al.[68].Wewouldlike,however,toemphasizeoneverypronouncedresultofthosetheo-ries.AssoonastheFermienergydeterminedbyEquation(6.25)liesessentiallyabovetheequilibration energy determined by Equation (6.7), the temperature dependence of theelectricalconductivity isno longerproportional toexp[-(Cs /kT)2]as in thecaseof lowcarrierconcentrationsatwhichEquations(6.9),(6.20)and(6.24)arevalid.Theconductiv-ityinsteadcloselyfollowstheroutineArrheniusbehavior[50,51].Forexample,thepercola-tionapproachpredictsatn >nc thetemperaturedependence[50,51]
c06.indd 242 5/6/2006 06:08:12 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 243
Y2
σ σ ε εDC
t F= - -
0 exp
kT (6.29)
wheres0 is thepreexponentialfactor,onlyslightlydependentontemperatureandontheconcentrationofsitesN;thetransportenergyet isdeterminedvia
ε σ β α σt = -
21 2 1 2
3
4
3
lnN
s kT kT (6.30)
wheres isthesolutionoftranscendentalequation
sN
s kT kT= -
ln1 2
3
4
3β α σ (6.31)
withb 0.045.TheFermienergyeF isdeterminedviatheequation[50,51]
ε σ σπ ε
F
F
= -( )
22
1 2 1 21 2lnN
n (6.32)
wheres istheenergyscaleoftheDOSinEquation(6.4).Itisworthnotingthattherearenumerousobservationsofasimpleactivatedtemperature
dependenceof theconductivity indisorderedorganicmaterials [69–72].Particularly theArrhenius temperature dependence of the conductivity is often observed in field-effecttransistors,wherechargecarrierconcentrationisusuallyhigh(see,forinstance,[34]).
Often the dependence ln(m) ∝ T -2 or ln(s) ∝ T -2 is considered as evidence for aGaussian DOS, while the Arrhenius temperature dependence ln(m) ∝ T -1 or ln(s) ∝ T -1isclaimedtoindicateapureexponentialDOS,whichwasdescribedin[14].Theim-portantconclusionfromtheaboveconsiderationisthepossibilitytoaccountsuccessfullyforbothkindsoftemperaturedependenceofhoppingconductivitydescribedbyEquations(6.2)and(6.3)intheframeworkoftheuniversaltheoreticalmodelbasedontheGaussianDOS.Thetemperaturedependenceoftheconductivityissensitivetotheconcentrationofchargecarriersn.
6.5 THEORETICAL TREATMENT OF CHARGE CARRIER TRANSPORT IN ONE-DIMENSIONAL DISORDERED ORGANIC SYSTEMS
Inthissectionweshowhowthehoppingchargetransportcanbedescribedtheoreticallyinone-dimensional(1D)disorderedorganicsolids.Particularinteresttothistopicistwo-fold. First, 1D disordered organic systems have been intensively studied experimentally,aiming at their applications in various electronic devices. Furthermore, in some vitallyimportantprocessessuchaselectrontransportalongDNAmoleculesorchargetransportin ionicchannels throughcellmembranes,charge transportcanbeeffectively treatedasone-dimensional.Second,inmanycaseshoppingtransportin1Dsystemscanbedescribed
c06.indd 243 5/6/2006 06:08:13 PM
244 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
theoretically with much higher precision than hopping transport in three-dimensionalsystems. Theoretical study of three-dimensional transport is complicated because it issometimesdifficulttofindthespatialstructureofthetransportpath[17].In1Dsystems,thisproblemdoesnotexist.Achargecarrierinsuchsystemsperformsaseriesofsuccessivetransition events between localized states placed on a 1D chain. Provided the rates forhoppingtransitionsbetweenlocalizedstatesandtheDOSfunctionareknown,theproblemof calculating the transport coefficients can be in many cases solved exactly. Using thisadvantageoftheprecisetheoreticaldescription,onecanclarifyvarioustransportphenom-enadiscoveredexperimentally.Amongsuchphenomenawewilldiscussthedependenceofthecarrierkineticcoefficientsontheappliedelectricfieldandinparticulartheratherpuz-zlingobservationofthedriftmobilityincreasingwithdecreasingfieldstrengthatlowfields[4,7,8,12,13,40].
In recentyearsparticular attentionhasbeendevoted to the studyof charge transportprocesses in columnar discotic liquid-crystalline glasses due to their potential technicalapplicationsforelectrophotographyandastransportmaterialsinlight-emittingdiodes[73,74].Dielectricmeasurementshaveclarifiedthatchargetransportinmostofsuchmaterialsis extremely anisotropic [75] so that it is reasonable to describe the transport of chargecarriersasa1Dprocess[76].Indeed,thevaluesofconductivityalongandperpendiculartothediscoticcolumnsdifferinsuchmaterialsbythreeordersofmagnitude[75].Experi-mentallyobserveddependencesoftheconductivityonthefrequency,onthestrengthoftheappliedelectricfield,andontemperatureshowthatanincoherenthoppingprocessis thedominanttransportmechanisminsuchmaterials[44,75,76].Ithasbeenfoundreasonabletodescribe the transportofchargecarriersasahoppingprocessviamoleculesarrangedinspatiallyordered1DchainswithaGaussiandistributionofsiteenergiesdescribedbyEquation(6.4)[44,76,77].
Letusfirstconsider, following[15,76],asimplestcaseallowingonlyhopstonearestneighborsandassumingthat1Dchainsoflocalizedstatesarespatiallyregular.Insuchacase,onecanomitther-dependenceoftransitionprobabilitiesusingtheeffectivepreexpo-nential factorn0 thatcontains the termexp(-2b/a),whereb is thedistancebetween theneighboringsitesontheconductingchain.TheMiller–Abrahamstransitionrateshaveinsuchacasetheform[15,76]
v vkT
ij i jj i j iε ε
ε ε ε ε, exp( ) = -
- + -
0
2 (6.33)
Otherformsoftransitionprobabilitieshavealsobeenconsideredintheliterature.Sekiand Tachiya [78] studied the 1D conduction with transition rates for charged carriersdescribedbytheMarkuslawthattakesintoaccountthepolaroneffect[79].Another,sym-metricformwasalsousedinordertoanalyzeanalyticallythefieldandtemperaturedepend-encesofthehoppingconductivityin1Dsystems[77]:
v vkT
i ii i
±±= -
-
1 0
1
2, exp
ε ε (6.34)
Two distinct models have been discussed in the literature with respect to the space–energy correlation of localized states responsible for charge transport. In the so-calledGaussian disordered model (GDM), which we considered in previous sections of this
c06.indd 244 5/6/2006 06:08:13 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 245
Y2
chapter,suchcorrelationsareneglected.Inthealternativecorrelateddisordermodel(CDM),itisassumedthatenergydistributionsofspatiallyclosesitesarecorrelated,forexample,duetodipoleorquadrupoleinteractions[77,80–82].
Muchattentionhasbeenpaidinrecentyearstothedependenceofthecarriermobilityontheelectricfield.Thisdependenceindisorderedorganicmaterialsinabroadrangeofhighfieldstrengthescanbefittedbythefunction µ ∝ ( )exp ,F F0 whereF0isaparameter[8]. It has been shown that in three-dimensional systems such field dependence can beexplainedonlyintheframeworkoftheCDM[77,80–82].Itischallengingtocheckthisresultbytheexactlysolvable1Dmodels.
Thestudyofthetemperaturedependenceofthedriftmobilityin1Dsystemsisalsoofgreatinterest.ResearchersagreethatthisdependenceintheemptysystemcanbedescribedbyEquation(6.9),althoughthereisnoagreementonthemagnitudeofthecoefficientC inthis formula. Ochse et al. [44] used the three-dimensional value C 2/3 for columnarsystemswith1Dtransport,whileBleylet al.[76]obtainedC 0.9intheircomputersimu-lationfor the1Dcasewithasymmetric transitionprobabilities.TheanalyticcalculationsofDunlapet al.[77]forsymmetricprobabilitiespredictC=1inthe1Dcase.Thevalueof C is decisive for characterization of the disorder parameters from comparison withexperimentaldatain1Dsystems.Weshowinthenextsubsectionanalyticalformulasthatallowonetocalculateexactlytransportcoefficientsin1Dsystemsforhoppingtransitionsbetweenthenearestsites.
6.5.1 General analytical formulas
Thesteady-statedriftvelocityofchargecarriersin1Dperiodicsystemswiththenumberofsites in theperiodN andthedistancebetweenthenearestsitesonthechainb canbewrittenexactlyusingthegeneralsolutionfoundbyDerrida[83]
v
Nbvv
vv
k k
k kk
N
k kk
Nk j k j
=-
+
+
+=
-
+-
=
-+ + -
∏
∑
1
1
1
10
1
11
0
11
,
,
,,
vvk j k jj
i
i
N
+ + +==
-
∏∑
, 111
1
(6.35)
ThisformulawasusedbyDunlapet al.[77]tostudythedriftmobilityina1Dsystemwithsymmetrictransitionrates.Thedriftmobilitym isrelatedtothesteady-statevelocityv as
µ υ=F
(6.36)
Howeverintheexperiments,thedriftmobilityisusuallyobtainedbythetime-of-flighttechnique[8].HerechargecarrierspassonlyoncethroughasampleoffinitethicknessanddriftmobilityiscalculatedbydividingthesamplelengthNb bythemeantransittime⟨t0N⟩ andelectricfieldF:
µ = Nb
t N F0
(6.37)
c06.indd 245 5/6/2006 06:08:14 PM
246 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
MurthyandKehr [84,85]havederived theanalyticalexpression for themean transittimeofcarriersthroughagivenchainofN +1sites:
t v vvvN k k
k
N
k kk
Nj j
j jj k
i
i k0 1
1
0
1
11
0
21
11
= ++-
=
-
+-
=
--
+= += +∑ ∑ ∏, ,
,
,11
1N -
∑ (6.38)
Thisformulagivesthetransittimeforachargecarrierthatstartsonsite0andfinishesonsiteN.Thetimeisaveragedovermanytransitsthroughthesamechainwithgivenvaluesoftransitionprobabilitiesnij.
OneshouldbecautiouswiththeapplicationofEquations(6.37)and(6.38)atlowelectricfields. Even without electric field, carriers starting at site 0 will pass through the finitesystemsolelydueto thediffusionprocess.At lowfields,diffusiondominates themotionofcarriersanditwouldbewrongtouseEquation(6.37).Moreappropriateinsuchacaseistheestimateofthemobilityviathediffusionformula
µ = e
kT
N b
t N
2 2
02 (6.39)
whichpresumesthevalidityoftheEinsteinrelationship.NotethatEquations(6.35)and(6.38)arevalidforanytypeofnearest-neighborhopping
ofnoninteracting carriers in1D systems.We show in thenext section the results of theexacttheoryappliedtoamodelsystemrepresentedbya1Dregularchainwithequalsiteenergies separated by barriers with random heights, a so-called random-barrier model(RBM). In the subsequent sectionsweconsidermore realisticmodels,GDMandCDM,withdistributionofsiteenergies.
6.5.2 Drift mobility in the random-barrier model
TransitionprobabilitiesbetweentheneighboringsitesundertheinfluenceofelectricfieldF intheRBMmodelaregivenbyexpressions
v vebF ebF
kTk k
k k, exp+ = - - + -
1 0
2 2
2
D D (6.40)
and
v vebF ebF
kTk k
k k+ = - + + +
1 0
2 2
2, exp
D D (6.41)
whereDk istheenergybarrierbetweensitesk andk +1.Inthelimitoflongchains,N >> 1,calculationofthedriftmobilityviaEquations(6.35)
and(6.36)orEquations(6.37)and(6.38)foranychainwithagivendistributionoftransi-tionratesisequivalenttotheaveragingofEquations(6.35)or(6.38)overallpossibledis-tributionsoftransitionratesdeterminedbydisorder.WeassumetheGaussiandistributionofbarrierheightswiththetypicalscales.Performingtheaveraging,oneobtainsthefol-lowingexpressionforthedriftmobilityintheinfinitechain[15]
c06.indd 246 5/6/2006 06:08:14 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 247
Y2
µ σσ
σ= -
-
+
-
v b
F kT
ebF
kT
ebF
kT0
2
11
2 2 8 2exp erf
eerf erf erfσ
σ21
8 8kT
ebF
kT
ebF ebF
- -
-
} ×exp
σσ
σσ
σ
{
+
-
- -
exp1
2 21
8 2
2
kT
ebF
kT
ebF
kTerf
-1
(6.42)
where erf(x) = (2/p) x0dy exp(-y2) is the error function. In Figure 6.9 the calculated
fielddependencesof thedriftmobilityare shown forparametersb=3.6Å,s=50meV,kT= 25meV [15].The solid line shows theexact solution for an infinite chaingivenbyEquation (6.42). All points in the figure correspond to mobilities for finite chains ofN = 500 sites averaged over 1000 different chains. Circles were obtained via Equations(6.37)and(6.38)whilesquarescamefromEquations(6.38)and(6.39).ResultsoftheMonteCarlocomputersimulations[16]areshownbycrossestodemonstratetheexcellentagree-mentof the simulation resultswith theanalytic theory.At lowfields, thedrift approachEquations(6.37and6.38)forfinitesystemsleadstoanincreaseofthecalculatedmobilitywithdecreasingfieldstrength.Similarresultswereobtainedforallconsideredmodelsofdisorderandvariousformsof the transitionprobabilitiesbetweenneighboringsites [15].This result is apparently artificial, reflecting the fact that charge carriers can penetratethroughafinitesystemviadiffusivemotion,evenintheabsenceofelectricfield.ByusingEquation(6.37)oneoverestimatesthemobilityatlowfields.ThesamehappenswhenusingEquation (6.39) at higher fields. Comparison of Equations (6.37) and (6.39) reveals thestrengthof theelectricfieldFc atwhicha transition from thediffusion-controlled to thedrift-controlledtransittakesplace:Fc 2kT/(eNb)[15].
Figure 6.9 Field dependence of the carrier mobility in the RBM with Gaussian distributionof barriers. The solid line represents exact solution for the infinite chain. Data shown by circlesandsquareswerecalculatedviaEquation(6.38)usingdrift(Equation6.37)anddiffusionrelations(Equation6.39),respectively.DatashownbycrosseswereobtainedbyMonteCarlosimulations[16](reproducedwithpermissionfrom[15].Copyright2001bytheAmericanPhysicalSociety)
c06.indd 247 5/6/2006 06:08:15 PM
248 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Atlowfields,thetransittimedoesnotdependonthestrengthoftheelectricfield,beingdeterminedmostlybydiffusion.UsingEquation(6.37)oneartificiallyobtainsanincreas-ingdriftmobilitywithdecreasingfieldF.Innumerouspublications,experimentalresultswerereportedthatshowanincreaseofthedriftmobilitywithdecreasingfieldatlowfields[11,86,87].Thiswasalwaysobservedathightemperatures,atwhichdiffusioncandomi-nate the motion of charge carriers. Experimental evidence for decreasing mobility withincreasingfieldisusuallyobtainedusingequationssimilartoEquation(6.37),wherethedriftmobility isdeterminedvia themeasured transit timebydividing thesample lengthbythevalueofthistimeandbythevalueofthefieldstrength.WebelievethatadiffusionequationsimilartoEquation(6.39)shouldbeusedatlowfieldsandhightemperatures.Inthethree-dimensionalcase,thisequationshouldbeslightlymodified,thoughtheconclu-sionisthesame:decreasingdriftmobilitywithincreasingfieldstrengthatlowfieldscanbeanartifactcausedbyusingthedriftequationinsteadofthediffusionequationfortheevaluationofthemobilityonthebasisofthemeasuredtransittime.ThisconclusionwasalsosuggestedbyHiraoet al.[88].Inthe1Dcalculations,thisideaisillustratedbyusingEquation (6.39) instead of Equation (6.37) for finite systems at low electric fields. TheresultisshownbysquaresinFigure6.9.Theexcellentagreementofthediffusionequationwiththeexactcalculationfortheinfinitesystematlowfieldsconfirmsourconclusion.Forthechosenparameters,thelineartransportregimewithmobilityindependentoftheelectricfieldisvaliduptoafieldstrengthofapproximately106V/cm,atwhichanarrownonlinearregimestartswiththemobilityincreasingwithelectricfield.Athigherelectricfields,thisregime is replaced by the trivial decrease of the mobility as F-1. At such high electricfields, all energybarriersbetween siteson the chain are eliminatedby thefield and thetransittimebecomesfieldindependent.Equation(6.37)predictsaF-1dependenceinthisregime.
6.5.3 Drift mobility in the Gaussian disorder model
In this section we consider a random-energy model with distribution of site energiesdescribedbyEquation(6.4),presumingthattherearenocorrelationsbetweenspatialposi-tionsofchainsitesandtheirenergies.ThismodeliscalledintheliteratureaGaussiandis-ordermodel(GDM).InEquation(6.33),thesiteenergiesekdependonthestrengthoftheelectricfieldF.Theyarerelatedtothezero-fieldsiteenergies,whichweheredenoteasjk,bytheexpressionek =jk - ekbF.InaccordancewithEquation(6.33),theratiooftheforwardnk,k+1andthebackwardhoppingratesnk+1,kforanypairofneighboringsitesis
v
v kTk k
k k
k k+
+
+= -
1
1
1,
,
expε ε
(6.43)
equivalenttoheconditionofthedetailedbalance.InsertingEquation(6.43)into(6.35),oneobtains
υ =- -( )[ ]
+ -( ) -( )+
-
=
-
∑bN ebNF kT
v kTiebF kT
k kk
N
k
1
11
0
1
exp
expexp
, jvv kTk i k i k ik
N
k
N
+ + + +=
-
=
-
-( )∑∑, exp10
1
0
1
j
(6.44)
c06.indd 248 5/6/2006 06:08:15 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 249
Y2
TheonlyrandomvariablesinEquation(6.44)arethezero-fieldsiteenergiesjkandtheforwardtransitionratesnk+i,k+i+1,whichinturndependonlyontheneighboringsiteenergiesjk+i andjk+i+1.Sinceinallproductsappearinginthesecondtermofthedenominator,jk isnotcorrelatedwithjk+i ornk+i,k+i+1, averagingoverdisordercanbecarriedout forexp(-jk/kT) and exp(jk+i/kT)n -1
k+i,k+i+1 separately. Straightforward calculations of v and ⟨t0N⟩thenleadviaEquation(6.37)totheexpressionforthedriftmobility[15]
µσ
σ σ= +
+
-
+ -
21
210
2v b
F
ebF
kT
ebF
kT kT
eberf erfexp
FF
kT
ebF
kT
ebF
kT
2
12
σ
σ
+
-
-
exp exp--
-
{
× + -
+ + +
1
12 2
12 2
expebF
kT
kT
ebF
kT
ebFerf erf
σσ
σσσ
}
-1
(6.45)
Atlowelectricfieldsthisexactexpressioncanbeapproximatedby
µ σ
v b
F kT
ebF
kT0
2
21exp exp-
-
(6.46)
whileathighfieldsmn0b/F.Interpolationbetweenbothapproximationsgives[15]
µ
σ
v b
F
kTebF
kT
0
2
2
1
1
2
1+ ( )
-
-
exp
exp (6.47)
Field dependences of the drift mobility in the GDM are shown in Figure 6.10 forb =0.36nm,s =50meV,andkT =25meV.ThesolidlinerepresentstheexactsolutionfortheinfinitechaingivenbyEquation(45),whiledashedlinesshowthelow-andthehigh-field approximations. One can easily check that for these parameters the interpolationformula(6.47)isinexcellentagreementwiththeexactsolution.Circlesandtrianglesinthefigureshowthecalculatedresultsforfinitesystemsof2000sitesaveragedover1000dif-ferentchains,onceusingtheaveragingofinversetransittimes(circles)andonceusingtheaveragingofinversevelocities(triangles).QualitativelytheseresultsinFigure6.10resemblethosefortherandom-barriermodeldescribedintheprevioussection.Inparticular,increaseofthemobilitywithdecreasingelectricfield,showninFigure6.10bycircles,iscausedbytheinvalidityofthedriftapproximationinfinitesystemsatlowfields.
InFigure6.11thefielddependencesofthedriftmobilityareshowninthePoole–Frenkelrepresentation(lnm versus F )fortwodifferenttemperaturesandtwodifferentaveragingprocedures.ThefigureclearlyshowsthatinthechosenmodelthecarriermobilityhardlycanbedescribedbythePoole–Frenkellawlnm∝ F . ThisconclusionisinagreementwiththeresultsofGarsteinandConwell[80],Dunlapet al.[77]andNovikovet al.[81,82].FollowingtheseauthorsweconsiderinSection6.5.5thedriftmobilityinthemodelwithcorrelateddisorder(CDM).Beforedoingso,wefocusinthenextsectiononthetem-peraturedependenceofthedriftmobilityatlowfieldsintheGDM.
c06.indd 249 5/6/2006 06:08:16 PM
250 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Figure 6.10 Fielddependenceofthecarriermobilityfornearest-neighbourhoppingwithMiller–AbrahamsratesbetweensiteswithGaussianenergydistribution.Solidlineshowstheexactsolutionforaninfinitechain.Dashedlinescorrespondtothelow-fieldandhigh-fieldapproximations.CirclesshowtheaveragedmobilitiescalculatedaccordingtoEquations(6.37)and(6.38).TrianglesrepresenttheresultsobtainedbyaveragingoftheinversemobilitiescalculatedbyEquations(6.36)and(6.44)forthesamechains(reproducedwithpermissionfrom[15].Copyright2001bytheAmericanPhysicalSociety)
Figure 6.11 Poole–Frenkel plots of the carrier mobilities. Circles show the averaged mobilitiescalculatedbyEquations(6.36)and(6.44);squaresshowthecorrespondingresultsobtainedbyaver-agingof the inversemobilitiesgivenbyEquation (6.48).Thenumberofchainswasc =104withN =500siteseach(reproducedwithpermissionfrom[15].Copyright2001bytheAmericanPhysicalSociety)
c06.indd 250 5/6/2006 06:08:16 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 251
Y2
6.5.4 Mesoscopic effects for the drift mobility
The low-fieldmobility forafinitechaindescribedbyEquations (6.44)and (6.36) in thelimitofF → 0isgivenbytheequation
µ = -( ) ( )
-+
-
=
-
=
- -
∑∑eb
kTN kT kT vk k k k
k
N
k
N22
11
0
1
0
1
exp exp ,j j11
(6.48)
For the infinite chain with transition rates described by Equation (6.33) the low-fieldmobilityintheGDMisexactlygivenby[15]
µ σ σ= -
+
-v eb
kT kT kT0
2 2 1
12
exp erf (6.49)
ThetemperaturedependenceofthedriftmobilitygivenbyEquation(6.49)isshownbythesolidlineinFigure6.12.Theslopeoflnm versus(s /kT)2inthiscurvediffersslightlyfrom-1duetothetemperaturedependenceofthepreexponentialfactorinEqution(6.49).ThisresultisingoodagreementwiththecomputersimulationsofBleylet al.[76]andwiththeanalyticcalculationsofDunlapet al.[77],althoughthelatteranalyticcalculationswerecarriedout forcorrelatedsystemswithsymmetric transitionratesdescribedbyEquation(6.34).Thisshowsthatin1DsystemsEquation(6.9)withC 1iscorrectandevenstableagainstthechoiceoftheformofthetransitionrates.
Thetemperaturedependencesofthelow-fielddriftmobilityinfinitesystemscalculatedaccordingtoEquation(6.48)arealsoshowninFigure6.12.Theseresultsarereallyremark-
Figure 6.12 Temperaturedependenceofthelow-fieldmobilityfors =50meV.Solidlinerepresentsthe solution for the infinite chain given in Equation (6.49). Circles and squares show the resultsobtainedbytheaveregingofmobilitiesandaveragingofinversemobilitiescalculatedbyEquation(6.48), respectively,withaveragingoverc =103chainsofN =2000sites.Upwardanddownwardtrianglesarethecorrespondingvaluesforc =104andN =200.DashedlineillustratesthetemperaturedependenceofthedriftmobilityintheformofEquation(6.9)withC =1(reproducedwithpermis-sionfrom[15].Copyright2001bytheAmericanPhysicalSociety)
c06.indd 251 5/6/2006 06:08:17 PM
252 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
able.Theyclearlyshowthatthetemperaturedependenceofthemobilityisrelatedtothesizeofthesystem.Thisisamanifestationofthemesoscopiccharacterofthehoppingtransportprobleminfinitesystems,whichismostpronouncedin1Dcases.Theaveragingoftransittimesorinversemobilitiesovervariousfinitechainscorrespondstothecalculationofthemobility ina longsystemconsistingofall thosechainsconnectedsequentiallyoneafteranother.Onthecontrary,theaveragingofthemobilitiesovervariousfinitechainscorre-sponds to thecalculationof thecarriermobility in thesysteminwhich thesechainsarearrangedinparalleltoeachother.Inthelattercase,the‘fast’chainswithuntypicallyshorttransittimesstronglycontributetotheaveragedvalueofthemobilityandtheydominatethetransportofchargecarriers.Thisistheveryessenceofthemesoscopiceffects[89].
Havinginmindanapplicationtodiscoticorganicdisorderedsystemswheremanyquasi-1Dcurrentchannelsareconnected inparallel,oneshouldconclude that the temperaturedependenceoftheelectricalcurrentinsuchsystemsdoeschangewiththethicknessofthesample.Forexample,comparisonbetweenthedataobtainedbytheaveragingofthemobil-ityvaluesforchainswithN =2000sitesandchainswithN =200suggeststhat,forshorterchainsandhenceforthethinnersamples,thetemperaturedependenceofthedriftmobilityshouldbeweakerthanthatforthickersamples.Indeed‘fast’channelsdominatingelectricalconductioninfinitesystemsariseduetothenarrowervariationofsiteenergiesthanintheinfinitesystems.Thiseffectiscausedbystatisticalfluctuationsintheenergydistribution[89].Closersiteenergiesleadtoaweakertemperaturedependence.
Themesoscopiccharacterof the temperaturedependenceof thecarrierdriftmobilitycanalsobeillustratedbythefollowingconsideration.Intheinfinite1Dchainwithhoppingtransitionsonly to thenearest-neighboringsites, thereexistsacharacteristicvalueof thelocalresistancethatdeterminestheoverallchainresistivity[90].Thecorrespondingenergyeopt ofoneoftheinvolvedsitesis,insomerespect,similartothetransportenergyintroducedintwo-andthree-dimensionalsystems.Indeed,letp(e)betheprobabilityforasitetohaveanenergyabovesomevaluee inaGaussianDOS.Thentheproduct
2 12
2 2
2
2- ( )[ ] -
( )
-
ppε ε
ε σ πεσ
d
d exp (6.50)
istheprobabilitydistributionthatoneoftheenergiesofaneighboringpairofsitesisbelowe,whereastheupperenergyliesintheintervalbetweene ande +de.Thisequationgivesthereforethedistributionofthenearest-neighborresistances.Averagingtheresistances,oneeasilyfindsthattheexponentoftheaverageresistivityisdeterminedbytheenergyeopt s2/kT andtheexponentisequalto2-1(s /kT)2+eopt/kT -e2
opt/2s2=(s /kT)2.ThisleadstoasymptotictemperaturedependencedescribedbyEquation(6.9)withC 1.Weseethatthis asymptotic temperature dependence of the drift mobility is determined by the siteswithenergies in thevicinityofeopts2/kT.Thisenergyincreaseswithdecreasingtem-peratureanditmighthappenthatinafinitesystemtherearenositeswithsuchhighenergiesaseopt.Ifso,thetemperaturedependenceoftheresistivityandthatofthecarriermobilityshouldbeweakerthanthedependencedescribedbyEquation(6.9)withC 1.Thiseffecthasrecentlybeenobservedinastraightforwardcomputersimulationofthenearest-neighborcarrierhoppingina1Dchain[91].Studyingafinitesystem,Pasveeret al.[91]obtainedaweakening of the temperature dependence of the carrier drift mobility with decreasingtemperatureinaccordwiththeabovearguments[90].
Thismesoscopiceffectshouldbetakenintoaccountwhenstudyingmaterialpropertiesatdifferentsamples.Fortime-of-flightstudies,researchersprefertodealwiththicksamples
c06.indd 252 5/6/2006 06:08:18 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 253
Y2
inordertoobtainlongertransittimesandtodeterminethedriftmobilitywithhigherpreci-sion.However, fordeviceapplications thinsamplesaremostlyused.Oneshouldbewellawarethatsomepropertiesofthethinsamplesusedfordeviceapplicationsmayessentiallydifferfromthoseofthicksamplesusedintheresearch.Itis,forinstance,trueforthetem-peraturedependencesoftheconductivity,asshownabove.
Sofarwehaveconsideredsystemswithoutcorrelationsbetweenspatialpositionsofsitesandtheirenergies.Inthenextsectionweabandonthisassumptionandconsidertheeffectsofsuchcorrelationsonthecarrierdriftmobility.
6.5.5 Drift mobility in the random-energy model with correlated disorder (CDM)
In order to construct a model with correlated disorder, we first generate provisional siteenergiesfk withaGaussiandistribution
g φσ πλ
φλσ
( ) = -
1
2 2
2
2exp (6.51)
wherelisanintegernumber.Thezero-fieldenergyj ofachargecarrieronsitek isthendeterminedbythearithmeticaverageofprovisionalenergiesf ofneighboringsites:
j φk k jj m
m
= +=-∑ (6.52)
Herel =2m +1isthecorrelationlengthinunitsoftheintersiteseparationb.ThisrecipetocreateasystemwithcorrelatedsiteenergiesissimilartothatsuggestedbyGarsteinandConwell[80].TheresultisthesetofsiteenergiesatzerofieldthathaveaGaussiandistributiondescribedbyEquation(6.4).Duetothecorrelation,twositeenergiesjk andjk+iarenotinde-pendentaslongasi ≤l.ThismakestheanalyticalcalculationofthedriftmobilityslightlymoreelaboratethaninthemodelwithoutcorrelationsdescribedinSections6.5.3and6.5.4.Nevertheless,onecanperformtheaveragingoverdisorderstraightforwardlyandobtainthefollowingexactresultforthecarrierdriftmobilityintheinfinite1Dchainintheform[15]
µ
σ λ
λ σ=
-
-
-
-
-
21
1
0
2
12
v b
F
kT
ebF
kT
kT
ebF
kT
exp
exp
+
+
-
-
12
1 2
12
erfλ
σ
λ σ
ebF
kT
ebF
kTexp + -
+
-
121 2
1 2
2
erfσ
λλ
σ
σ λ
kT
ebF
kT
ebF
kTexp
-
+ +
+ -
11
21 2
1 2
exp
exp
ebF
kTkT
ebF
ebF
kT
erfσ
λλ
σ
+ -
-
121 2
1 2 1
erfσ
λλ
σkT
ebF (6.53)
c06.indd 253 5/6/2006 06:08:18 PM
254 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
InFigure6.13thecorrespondingfielddependencesareplottedfordifferentcorrelationlengthsl forfinitechains(symbols)calculatedviaEquation(6.35)and(6.36)andfortheinfinitechaincalculatedviaEquation(6.53).ResultsforfinitechainsofN =103siteswereaveragedoverc =103realizationsofthechain.TheparticularshapeofthefielddependenceofthedriftmobilityintheCDMfortheinfinitesystemisconsideredindetailinthepapersofGarsteinandConwell[80],Dunlapet al.[77]andNovikovet al.[81,82]andwedonotdiscussithere.
Insteadwewould like to focusour attentionon theother aspect of thephenomenon,namely,ontheincreasingdifferencebetweentheresultsobtainedbyaveragingofmobilities(opensymbols inFigure6.13)and thoseobtainedbyaveraging the inversemobilitiesortransittimes(filledsymbolsinFigure6.13)withincreasingcorrelationlength.Thistrendisclearlyrelatedtothesmallernumberofhighbarriersinsystemswithlongercorrelationlengths,whichfavorsthemesoscopiceffects.TheincreaseofthecorrelationlengthintheCDMisanalogousto thedecreaseof the totalnumberofsites in thefinitechains in theGDM.
6.5.6 Hopping in 1D systems: beyond the nearest-neighbor approximation
So far we have considered hopping in various 1D systems, taking into account carriertransitionsonlybetween thenearest sites.Thequestion thenarisesofhow transitions tofurtherneighborsonthechaincanmodifytheresultsobtained.TheVRHphilosophytellsusthatthetemperaturedependenceoftheconductivityandthatofthecarrierdriftmobility
Figure 6.13 Influenceofthespace-energycorrelationsonthefielddependenceofthecarriermobil-ityatkT =15meVands =50meV.Thedifferentcorrelationlengthsarel =1(circles),l =3(squares),l = 11 (upward triangles), andl = 101 (downward triangles). Open symbols show the averagedmobilitiescalculatedbyEquation(6.44).Solidsymbolsshowthecorrespondingresultsobtainedbyaveraging of the inverse mobilities. Solid lines show the solutions for the infinite chain given byEquation(6.53)(reproducedwithpermissionfrom[15].Copyright2001bytheAmericanPhysicalSociety)
c06.indd 254 5/6/2006 06:08:18 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 255
Y2
shouldbedeterminedatlowtemperaturesbytransitionsofchargecarrierstofurtherneigh-bors than thenearestones.Theeffectof such long-distance tunneling transitionson thetemperaturedependencesofthekineticcoeffcientsin1DsystemswasstudiedanalyticallybyZvyaginet al.[90]andbycomputersimulationsbyKoharyet al.[16]andbyPasveeret al.[91].Zvyaginet al.[90]consideredonlytheGDMmodelandshowedthattransitionsto m neighbors beyond the nearest ones lead to the asymptotic temperature dependencedescribedbyEquation (6.9)with C m m= +( )1 2 . For instance,hopping to thesecondnearestneighborsleadstoEquation(6.9)withC = 3 4. However,thisasymptoticbehaviorwith C m m= +( )1 2 canhardlybeachievedatrealisticconditions.Zvyaginet al.[90]have shown that even at (s /kT)2 100, the coeffcient C in Equation (6.9) is closeto0.8.
Ananalogousresultontheweakeffectofdistanttransitionshasbeenobtainedbycom-putersimulations[16].Koharyet al.[16]studiedbycomputersimulationshoppingtransportin1DGDMandCDMsystemsusingtransitionratesintheformofEquation(6.5)insteadofEquation(6.33)thatwasusedforthenearest-neighborhopping.Inthesesimulationsthelatticeconstantb = 0.36nmwaschosenasknown fordiscotic liquid-crystallineglasses,andthevaluesofparametera inEquation(6.5)werevariedbetween0.1and0.3nm.Thisparameterdeterminesthedecaylengthofthecarrierwavefunctioninthelocalizedstates.Transitions to sixneighbors in eachdirectionwereallowed in the simulationprocedure.Themainresultof thesimulationsis thefollowing.FortheCDM,i.e., forasystemwithcorrelateddisorder,tunnelingtofurthersitesthanthenearestneighborsdoesnotplayanyessential role, while for the GDM, i.e., for uncorrelated systems, these distant hoppingtransitionsslightlyaffectthetransportcoeffcients.Theunimportanceofdistanttransitionsforsystemswithcorrelateddisorderisnotsurprising.Insuchsystems,energiesofneighbor-ingsitesareclosetoeachotherduetocorrelationeffects.Thusthevariable-rangehoppingis not significant for such systems, because the closest energy and space states are thenearestneighbors.Thequantitativeconfirmationof thisqualitativelyclearstatement[16]implies that forsystemswithcorrelateddisorderonecanuseanalytic theoriesdescribedaboveandonecanbesurethattherestrictionoftheanalytictheorywhichconsidersonlythenearest-neighborhoppingisnotessentialfortheresultsobtained.
Forsystemswithuncorrelateddisorder theresultof thesimulationisalsoratheropti-misticwithrespecttothevalidityoftheexactanalyticsolutionsdescribedabove.Evenforaratherhighvalueofthedecayconstanta =0.2nm,whichmakesthedistanthopsfavorable,themagnitudeof thecoeffcientC 0.9inEquation(6.9) isnotmuchdifferent fromitsvalueforthenearest-neighborhopping.Thus,evenforsystemswithuncorrelateddisorder,exactanalyticsolutionsobtainedinprevioussections,takingintoaccountonlythenearest-neighborhopping,givereasonablevaluesfortransportcoeffcients[16].
6.6 ON THE RELATION BETWEEN CARRIER MOBILITY AND DIFFUSIVITY IN DISORDERED ORGANIC SYSTEMS
High interestof researchers incharge transport inorganicdisorderedsystemsmotivatednumerousstudiesoftherelationbetweensuchkineticcoeffcientsasthemobilitym andthediffusion coeffcient D of charge carriers in such systems. However, one can find rathercontradictorystatementsonthissubjectinthescientificliteratureandthereforewewouldliketoclarifythisproblem.
c06.indd 255 5/6/2006 06:08:19 PM
256 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
Borsenbereger et al. [92] studied experimentally the behavior of the ratio eD/m in1,1-bis(di-4-tolylamionophenyl)cyclohexane (TAPC) and found that this ratio increasesapproximatelylinearlywithappliedelectricfieldathighfields.Inthelow-fieldregion,theratioeD/m becomesindependentofthefieldstrengthF.Nevertheless,thelimitingvalueofthis ratiodoesnotagreewith thatgivenby theclassicalEinstein relationship.The latterreads[93]
µ =e
kTD (6.54)
Also Monte Carlo computer simulations were carried out that claimed invalidity ofEquation(6.54)fortherelationbetweenthemobilityanddiffusivityofhoppingcarriersinarandomsystemwithGaussianenergydistributionofsiteenergies[94–96].Theamountofdisorderischaracterizedbytheenergyscales oftheDOSdescribedbyEquation(6.4).Withincreasingdisorderandfield,significantdeviationsfromEinstein’slawwereobtainedinthesimulations.TheseresultscontributedtothegeneralbeliefofmanyresearchersthattheEinsteinlawexpressedbyEquation(6.54)isviolatedinrandommedia.
Discussing thevalidityor invalidityof theEinstein relationship forhoppingelectronsoneshouldclearlydistinguishbetweentheequilibriumandnonequilibriumconditionsononehandandbetweenthedegenerateandnondegeneratesystemsofchargecarriersontheother.Furthermore,oneshoulddistinguishbetweentheregimeoflowelectricfieldswithfield-independenttransportcoeffcientsandtheregimeofhighfields,inwhichthenonlineareffects caused by electric fields become significant. Computer simulations [94–96] haveshownthatathighfieldsinanonlineartransportregimethediffusioncoeffcientD dependsmorestronglyontheelectricfieldthanthecarrierdriftmobilitym.ThereforetheratioeD/m increaseswithincreasingfieldandtherelationdescribedbyEquation(6.54)isviolated.Wewillnotconsiderthisnonlinearregimehereduetotherathercomplicateddefinitionofthediffusionconstantinthecaseofhighelectricfieldswhichcausestronganisotropyinthediffusion process. Interested readers can find the necessary information in the literature[94,95].Insteadwediscussbelowtheregimeoflowelectricfieldswithfield-independenttransportcoeffcientsDandm.
AsshowninSection2.5ofChapter2[14]Einstein’slawcannotbevalidinthestrongnonequilibriumconditionsatlowtemperatures,whentransportprocessesaregovernedbytheenergy-lossdownwardinenergyhoppingrelaxationofchargecarriers.Fortheenergy-losshoppingintheexponentialDOS,arelationbetweenD andm similartothatinEquation(6.54)wasfound,althoughthethermalenergykT inthisrelationisreplacedbytheenergyscaleoftheDOS(seeEquation2.53inChapter2[14]).Itis,unfortunately,notpossibletoobtainsucharelationfortheenergy-losshoppinginaGaussianDOS.TheexponentialDOSconsideredinChapter2[14]representstheonlyexceptionamongpossibleDOSfunctions,forwhichtherelationbetweenm (e)andD(e)isindependentofthelocalizationenergy2 and therefore the relationbetween theeffectiveD andm for thewhole systemofchargecarriersperformingtheenergy-losshoppingcanbeformulatedintheuniversalform(seeEquation2.53inChapter2[14]).ThereforewewillnotconsidernonequilibriumconditionsforhoppingintheGaussianDOSandrestrictourconsiderationheretostudyingthevalidityoftheEisnteinlawintheequilibriumconditions.
Theproblemof therelationbetweenD andm in thermalequilibriumforadisorderedsystemwithGaussianDOShasrecentlybeensolvedbyRoichmanandTessler[97].The
c06.indd 256 5/6/2006 06:08:19 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 257
Y2
authorsusedtheformuladerivedforageneralenergydistributionofchargecarriersandageneralDOSfunction[98,99]
µε
=∂∂
eDn
n1
F
(6.55)
where n is the total concentration of charge carriers and eF is the Fermi energy. UsingEquation (6.25),onecan rewrite thisexpression foragivendensityof statesg(e) in theform[97]
µε ε ε ε
ε ε
ε ε=
( ) -( )[ ]+ -( )[ ]{ }
( )+
-∞
∞
∫e
kTD
gkT
kT
g
F
F
d
d
exp
exp
ex
11
1
2
pp ε ε-( )[ ]-∞
∞
∫F kT
(6.56)
InthecasewhentheFermienergyisverylowandthemajorpartofthecarrierenergydistributionisfaraboveeF ,theFermidistributioncanbereplacedbytheBoltzmannfunc-tionand theratioof integrals inEquation(6.56)becomesunity.Thiscorresponds to thenondegenerate energy distribution of charge carriers. In such a case, the generalizedEinstein relationdescribedbyEquation (6.56)approaches theclassical form representedbyEquation (6.54).For theGaussianDOSdescribedbyEquation (6.4) thiscondition isvalidatsmalldisorderparameters fordeepFermienergy.InFigure6.14theratiomkT/eD isplotted forGaussianDOSasa functionof the ratioeF/kT fordifferentvaluesofs /kT (followingRoichmanandTessler [97]).Using for thedisorderparameter realisticvaluess 0.1eV,one comes to the conclusion that at room temperature the classicalEinsteinrelationcanholdonlyatrathersmallconcentrationsofchargecarriers.Computersimula-tionsfortheratiom /D insuchconditionsinGaussianDOSaredescribedin[100].Fora
Figure 6.14 Theratiom /D asafunctionof theFermileveleF/kT fordifferents /kT (reproducedwithpermissionfrom[97],Copyright2002,AmericanInstituteofPhysics)
c06.indd 257 5/6/2006 06:08:20 PM
258 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
degenerate system the generalized Einstein relation has to be calculated in its full formusingEquation(6.56)withg(e)describedbyEquation(6.4)[97].
Aquestioncouldariseastowhysomecomputersimulationsprovideresults that lookcontradictory to the above conclusions. For instance, it has been claimed on the basisof straightforward Monte Carlo computer simulations that, in disordered systems withGaussianDOS,hoppingmobilityanddiffusivitydonotobeytheclassicalEinsteinrelationgiven by Equation (6.54) even in the case of noninteracting carriers when the latter areconsideredas independententities [96].On theotherhand,Equation (6.56) forachargecarrierinanemptysystemshouldcoincidewithEquation(6.54).Thisproblemhasbeensolvedin[100],whereitwasshownthatincomputersimulationsthatdemonstrateapparentdeviationsfromEquation(6.54)thesystemofchargecarrierswasnotinthermalequilib-riumbecauseoftheparticularchoiceofthesimulationparameters.Assoonastheequilib-riumconditionswereestablished, the relationbetweenD andm for independent carriersbecameinagreementwithEquation(6.54)[100].
6.7 ON THE DESCRIPTION OF COULOMB EFFECTS CAUSED BY DOPING IN DISORDERED ORGANIC SEMICONDUCTORS
OneoftheinterestingtopicsinresearchondisorderedmaterialsistheeffectofCoulombpotentialsofchargedspeciesontransportproperties.Thedecisiveroleofsucheffectsforvarious charge transport phenomena has been clarified for hopping transport in dopedcrystallinematerialsandininorganicdisorderedmaterialssuchasamorphoussemiconduc-tors.Thistopichasalreadybecomeasubjectoftextbooks[17,101].Withrespecttodisor-deredorganicmaterialsthesituationisnotasfavorable,althoughCoulombeffectsinsuchmaterials can play even a more pronounced role. The dielectric constant of the organicmatrixisusuallyseveraltimessmallerthanthatininorganicmaterials.ThisshouldmakeCoulombeffectsmoresignificantinorganicmaterials.NotmuchhasbeendoneyetinthestudyofCoulombpotentialsinorganicdisorderedsolidsandonlyseveralinitialtreatmentshave been attempted so far (see, for instance [102]). Unfortunately, the results of thesetreatmentsareincontradictiontotheresultsonCoulombeffectsfromtextbooksdevotedtoinorganicmaterials.Thissituationresemblesthatoftheinitialstudyofhoppingtransportinorganics.Researchersbeganthisstudynottryingtousetheexperiencealreadygatheredinthefieldofinorganicsystems.Thereforewewouldliketoanalyzebrieflytheshortcom-ingsofthesuggestedtreatmentsofCoulombeffectsinorganicmaterialsinordertowarnresearcherswithrespecttopossibledrawbacksinsuchtreatments.
Ithasbeenestablishedexperimentallythatthedopingeffciencyofdisorderedmaterialsismuchlowerthanthatofcrystallinesemiconductors.Forexample,inamorphousinorganicsemiconductors, such as hydrogenated amorphous silicon, a-Si:H, the concentration ofimpuritiesasdeducedfromexperiments involvingelectronicstates isconsiderably lowerthanthatdeterminedfromthestudyoflocalbondingconfigurationsbyextendedX-rayfinestructureornuclearmagneticresonance[103].Alsoindisorderedorganicmaterialsithasbeenclaimedthatatlowdopinglevels,electrochemicaldopingismuchlesseffcientthanthe field-effect doping in which the same amount of charge carriers is injected into thesystemwithoutinducingchemicallyforeignimpurities[104,105].Moreover,atlowdopant
c06.indd 258 5/6/2006 06:08:20 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 259
Y2
concentrations,chemicaldopingcanevenleadtodecreasingcarriermobility[106].Athighdopinglevelsthemobilitysteeplyincreaseswithdopantconcentration[104–106].Qualita-tively this resultwas interpretedbyassuming that inchemicallydopedmaterialschargecarriers can be trapped by Coulomb potentials of ionized dopant species at low dopinglevels[105].Concomitantly,thecarriermobilitycouldbemuchsmallerthanthefield-effectmobilitymeasuredwithout introducingchargeddopants into thesample.Athighdopinglevels in theelectrochemicalprocess theenergy landscapemightbecomemoreuniform,leadingtotheincreaseofthecarriermobility[105].
Twoidenticalattempts[102,107]wererecentlyperformedinordertoputthisargumentontoaquantitativetheoreticalbasis.Webrieflydescribetheseattemptsandshowthattheset of equations suggested in such an approach is irrelevant for the description of theproblem under study since neither charge neutrality nor screening effects were properlytakenintoaccount.
TheauthorsconsideredanarrayoflocalizedstatesofthehostsystemwithsomehighconcentrationNt~1021cm-3andanarrayofdopantatomswithmuchlowerconcentrationNd~1018cm-3.Tobespecificwewillconsider thecaseofdonorsasdopantspecies.Thecaseofacceptorscanbe treated inananalogousway.Donorsaresupposed togive theirelectronsintolocalizedstatesofthehostsystemandtobecomepositivelycharged.Arkhipovet al. [102,107]considereda localizedstateandestimated theCoulombenergyshiftofthisstateduetothepresenceofthechargeddonorswithconcentrationNd.Theyconsideredthe contribution to the Coulomb potential from only the nearest donor. The probabilitydensity,w(r),ofhavinganearestdonoratadistancertoachosenlocalizedstateisdeter-minedbythePoissondistribution
w r r N N r( ) = -
4
4
32 3π π
d dexp (6.57)
The energy of the localized state under consideration is shifted downward by theCoulombpotentialofthenearestdonor.Lettheenergyofthislocalizedstateintheabsenceofdonorsbee.In[102,107]itisarguedthatinthedopedsystemtheenergyofthisstatebecomesequaltoE =e +Ec,where
Ee
rc = -
2
κ (6.58)
istheenergyshiftduetotheCoulombpotentialofthenearestdonor.InEquation(6.58)e istheelectronchargeandkisthedielectricconstantofthehostmaterial.AweakdopingwasconsideredwhentheconcentrationofdopantionsNdremainsmuchsmallerthanthetotaldensityofintrinsichoppingsitesNt.Theauthorsclaimthat,undertheseconditions,theenergyofalmosteverylocalizedstatewillbeessentiallyaffectedonlybythenearestdopantion.InsuchacaseonecaneasilyfindthedistributionG(E)ofsiteenergies,E =e +Ecfromthegivendensityofstates(DOS)forintrinsicenergiesg(e)andfromEquations(6.57)and(6.58)forthedistributionofCoulombenergiesEc.Duetotheeffectoftheposi-tivelychargeddonors,thedistributionG(E)appearsshiftedtolowerenergiesascomparedwiththedistributionofintrinsicenergiesg(e).Hencetheextraelectronssuppliedintothesystembychemicaldopingarenotforcedtofilltheintrinsicdensityofstates(thuspushing
c06.indd 259 5/6/2006 06:08:20 PM
260 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
theFermilevelupwards),butrathertheyfillthedensityofstatesalreadyshiftedtowardslowerenergiesbyCoulombpotentialsofthepositivelychargedonors[102,107].Thereforethe increaseof theFermi levelwithdopingoccursmuchmoreslowly thanwouldbe thecaseintheintrinsicDOSg(e)filledbythesameamountofelectrons.Afterhavingcalcu-latedG(E),Arkhipovet al. [102]studiedthehoppingtransportofelectrons, treatingthesystemasspatiallyhomogeneouswithDOSG(E).Wehavetopointoutthedeficiencyofsuchtreatment.
Inthepicturedescribedabove,oneassumesthatonlyasingledonor,namely,thenearestone,causestheCoulombshiftoftheenergyofalocalizedstateinthehostmaterial[102,107].In[102,107]itisclaimedthatthisassumptionisjustifiedbytheinequalityNd << Nt.MoreovertheauthorsclaimthatthisassumptionunderconditionNd << Nt isobvious[102].Wearguehoweverthatthisassumptionisneitherobvious,norcorrect.Ofcourse,thecon-tributionofdonorstotheCoulombpotentialonalocalizedsitedecreaseswiththedistancefromthesiteasr-1.However,thenumberofdonorsinasphereofradiusr aroundthechosensite increases as r3. Therefore, the contribution to the Coulomb potential of a chosenhoppingsitefrommoredistantdonorsthanthenearestoneincreasesproportionaltor2.Inthe absence of screening, as considered in [107], distant donors contribute more to theCoulombenergyshiftsonlocalizedstatesthanthenearestones.Theconditionexpressedvia inequalityNd << Nt is irrelevant for thisconclusion.Furthermore,oneshould realizethat,inthepicturesuggestedin[102,107],theenergydivergesifoneconsidersonlydonorsaschargedcentersandtakesintoaccounttheCoulombcontributionstotheenergyofanintrinsicsitefrommoreandmoredistantdonors.Thisisatrivialresultdiscussedinseveraltextbooks (see, for example, [17,101]). Inorder to avoid thedivergenceof theCoulombenergy,oneshouldnotrestricttheconsiderationtochargesofonlyagivenpolarityasdonein[102,107].Instead,oneshouldconsiderbothkindsofcharges—positiveandnegative—keepingthesystemelectricallyneutral.Herewithwecometotheimportantthoughtrivialquestion:areelectronselectricallycharged?Theanswertothisquestionisdefinitely‘yes’.Adonorbecomeschargedpositivelyonlybecauseitcangetridofavalenceelectron.In[102,107],electronsbroughtintothesystembydonorsweregivenjustapassiveroletofillthedensityof states shifted to lowerenergiesbypositivelychargeddonors.One should,however,takeintoaccountthatelectronsarealsochargedwithoppositepolaritytothatofthedonors.TheconcentrationofthenegativelychargedextraelectronsintroducedintothesystembydonorsisequaltothatofchargeddonorsNd.Theseelectronsarethecausefortheeffectontheenergiesofintrinsicsites,whichisexactlyoppositetothatofpositivelychargeddonorsexclusivelyconsidered in [102,107].Beingnegativelycharged,electronsshifttheenergiesofintrinsichoppingsitesupward.Theauthorsof[102,107]deliberatelytookintoaccountonlypositivecharges.Ifonewoulddothesame,takingintoaccountonlynegativechargesofextraelectrons,onewouldcometotheconclusionexactlyoppositetothatin[102,107],namelytotheconclusionthatDOSfunctionwouldbeshiftedupwardinenergywithrespecttothatinanundopedsample.Ofcourse,noneofsuchdeliberatecon-siderationscanbecorrect.Oneshouldconsideranelectricallyneutralsystem,takingintoaccountbothpositivelychargeddonors andnegativelychargedelectronsasdescribed intextbooks[17,101].Thecrucialpointinsuchtreatmentsisthequestionofthespatialdis-tributionofcharges.Donorsareassumedtobedistributedrandomlyinspace.Whataboutelectrons?
Letus,following[102,107],consideralightlydopedsamplewhenconditionNd << Nt isfulfilled.ThisassumptionisplausiblesinceestimatesgiveNd ~1018cm-3andNt ~ 1021cm-3
c06.indd 260 5/6/2006 06:08:21 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 261
Y2
[102,107].ConditionNd << Nt cannotjustifythatonlythenearestdonortoalocalizedstateshouldbetakenintoaccount,thoughthisstronginequalitywillhelpustoanswertheques-tionofwhereelectronsaresituated.ACoulombenergyshiftofanintrinsiclocalizedstatefromthenearestdonorisdescribedbyEquations(6.57)and(6.58).Itisdeterminedbythetypicaldistancebetweendonorsrd Nd
-1/3.InsertingsuchestimateinEquation(6.57),andtakingk=3asknownfororganicsemiconductors,oneobtainsthetypicalCoulombcon-tributiontotheenergyofalocalizedstatefromthenearestdonoroftheorderEc ~ 0.08eVforNd ~ 1018cm-3 [102,107].Since thewidthof theenergydistributiong(e)of intrinsichoppingsitesisoftheorderof~0.1eV,theeffectofCoulombcentresonintrinsiclocalizedstatesseemsessential.Weclaimhoweverthatintheabovepictureoneshouldconsidernotalocalizedstateandthenearestdonortoit,butratherthelocalizedstatewhichisthenearesttoadonor.While the typicaldistancebetweena localizedstateandthenearestdonor isdeterminedbythedistanceoftheorderrd Nd
-1/3, thedistancebetweenadonorandthenearestlocalizedstateisdeterminedbythedistancertN t
-1/3,whichismuchsmallerthanrd. Inserting such a value for rt into Equation (6.58) and taking for the concentration oflocalizedstatesthemagnitudeNt ~ 1021cm-3,assuggestedin[102,107],wefindthattheCoulombenergyshiftofthelocalizedstatenearesttoadonorEcisabout0.8eV.ThisvalueisbyanorderofmagnitudelargerthantheshiftEc ~ 0.08eVcausedonalocalizedstatebythedonornearesttoit.Inthegroundstateofthesystem,electronswouldtendtooccupydeeper energy levels and therefore theywill be situatedon the intrinsic sites,which areclosesttodopantions(donors).Thereforeoneshouldconcludethatallchargesbroughtintothesystembydonorsaregathered intodipoles formedbypositivelychargeddonorsandthenegativelycharged intrinsiccentersnearest to them.Onecouldsuppose that in [102,107]theeffectwithtypicalscaleofabout0.1eVwasconsidered,neglectingtheeffectwithtypicalscaleofabout1eV.Thesituationis,however,worse.Wehavejustseenthatduetotheeffectofthetypicalscaleof~1eV,theeffectofthescale~0.1eVconsideredin[102,107]doesnotexist,sincenotthepointcharges,butratherveryshortdipolesaffectlocalizedstatesintheintrinsicmaterial.Theextraelectronsbroughtbydonorsaretrappedintostateswithverydeepenergies( -1eVatNt =1021cm-3)whicharethenearesttodonors.Thismightbethereasonwhynoeffectofincreasingconductivityhasbeenobservedexperimen-tallyatlowdopantconcentrationswhenconditionNd <<Nt isfulfilled.TheeffectofheavydopingwhenthestronginequalityNd << Nt breaksdownneedsaspecialtreatment,whichisbeyondourscope.LetusinsteadestimatetheeffectofCoulombpotentialsonagivenintrinsiclocalizedstateinalightlydopedmaterial.
Following [102,107]weconsider agiven localized site in the intrinsicmaterial.Thedistancerd Nd
-1/3fromthislocalizedsitetothenearestdipoleisdeterminedbythecon-centrationofdipoles,whichisequaltotheconcentrationofdonorsNd.Thelengthofthedipoleisdeterminedbytheconcentrationoflocalizedstatesrt N t
-1/3.Thecontributionofsuchadipoletotheenergyofagivenlocalizedstateisoftheorder
Ee
r
r
rc -
2
κ d
t
d
(6.59)
ThisequationreplacestheestimategivenbyEquations(6.57)and(6.58).TheresultofEquation(6.59)fortheenergyshiftEc on‘alocalizedstate’isbyanorderofmagnitudesmallerthanthatobtainedin[102,107],sinceinEquation(6.59)theCoulombcontributionofapointchargeatadistancerd ismultipliedbyasmallfactorrt/rd,whichisequalto0.1
c06.indd 261 5/6/2006 06:08:21 PM
262 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
fortheratioNd/Nt =10-3chosenin[102,107].Thiscontributionislessthan0.001eVanditcanbeneglected.
One should emphasize that the study of the effects of Coulomb potentials on chargetransportindisorderedorganicmaterialsisstillinitsinitialphaseandmorestudyisneededto clarify the role of these effects. In particular, the calculation of transport propertiesaffectedbychargedistributionathighdopinglevelsisachallengingtheoreticalproblem,whichstillawaitsitssolution.
6.8 CONCLUDING REMARKS
Inthischapterwehavepresentedseveralbasicconceptsdevelopedfordescriptionofchargecarriertransportinorganicdisorderedsemiconductors,suchasmolecularlydoped,conju-gatedpolymers,andorganicglasses.Theseconceptsare,toagreatextent,analogoustothetheoreticalconceptsdevelopedearlierfordescriptionofchargetransportininorganicdis-orderedmaterialssuchasamorphousandmicrocrystallinesemiconductors.Therefore,wehavetriedtokeepthepresentationoftheseideasparalleltothatinChapter2ofthisbook[14].However,contrarytoChapter2,twoimportanttopicswerenotconsideredhere—thethermallystimulatedcurrentsandthenonlineartransporteffectsinhighelectricfields.Thedescriptionofthermallystimulatedcurrentsinorganicdisorderedmaterialscanbefoundin theworkofSchmechelandvonSeggern [108].Thedescriptionof thenonlinearfieldeffects in such materials can be found in [77, 80–82]. Furthermore, we focused in thischapter only on the description of the motion of charge carriers through the disorderedmaterial.Suchimportant topicsas the injectionofchargecarriersfromthecontacts intothesystemaswellasthedescriptionofthespace-charge-limitedcurrentsremainedbeyondour scope. Readers interested in these topics can find comprehensive descriptions, forexample,intherecentreviewarticleofH.Bäassler[4]andinChapter7ofthisbook[3].
Acomparisonbetweentheresultsof thischapterandthosedescribedinChapter2ofthisbookshow the roleof theDOSfunctionon the transportphenomena.Although thetransportconceptsusedinthesetwochaptersareverysimilartoeachother,someresultsforGaussianDOSdifferessentiallyfromthosefortheexponentialDOS.ThereforewehaveconsideredthechargetransporteffectsfortheGaussianDOSandfortheexponentialDOSintwoseparatechapters.
Acknowledgements
Theauthorsareindebtedtonumerouscolleaguesforstimulatingandenlighteningdiscus-sions.Inparticular,wewouldliketoexpressourgratitudetoIgorZvyagin(MoscowStateUniversity)forclarifyingtoustheroleofdistanthopsin1DsystemsandtoPeterThomas(PhilippsUniversityMarburg)forclosecollaborationontopicsdiscussedin thischapter.FinancialsupportoftheDeutscheForschungsgemeinschaft,oftheFondsderChemischenIndustrie,oftheOptodynamicCentreatthePhilippsUniversityMarburg,oftheEuropeanCommunity [IP ‘FULLSPECTRUM’ (Ref. N: SES6-CT-2003-502620)] and that of theEuropeanGraduateCollege‘Electron-ElectronInteractionsinSolids’Marburg–Budapestisgratefullyacknowledged.
c06.indd 262 5/6/2006 06:08:21 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 263
Y2
REFERENCES
[1] S.Roth,Hoppingconductioninelectricallyconductingpolymers.in:HoppingTransport in Solids.M.PollakandB.I.Shklovskii,(eds),Elsevier,1991,377.
[2] N.Naarmann,in:Electronic Properties of Conjugated Polymers.H.Kuzmany,M.Mehring,andS.Roth,(eds),Springer,Heidelberg,1987,12.
[3] E. von Hauff, C. Deibel, and V. Dyakonov, Device applications of organic materials. in:Charge transport in disordered solids with applications inelectronics.S.D.Baranovskii,(ed.),Wiley,2006.
[4] H. Bässler, Charge transport in random organic semiconductors. in: Semiconducting Poly-mers.G.HadziioannouandP.F.vanHutten,(eds),Wiley,NewYork,2000,365.
[5] G.HadziioannouandP.F.vanHutten,Semiconducting Polymers.Wiley,NewYork,2000. [6] C.Brabec,V.Dyakonov,J.Parisi,andN.S.Sariciftci,Organic Photovoltaics:Concepts and
Realization.Springer,Berlin,2003. [7] M.PopeandC.E.Swenberg,Electronic Processes in Organic Crystals andPolymers.Oxford
UniversityPress,Oxford,1999. [8] H.Bässler,Phys. Stat. Sol. (b), 175,15(1993). [9] P.M.Borsenberger,E.H.Magin,andJ.Shi,J. Phy. B, 217,212(1996). [10] P.M.Borsenberger,W.T.Greenbaum,andE.H.Magin,Physica B, 228,226(1996). [11] M.Abkowitz,Phil. Mag. B, 65,817(1992). [12] P.M.Borsenberger,E.H.Magin,M.vanderAuweraer,andF.C.deSchryver,Phys. Stat. Sol.
(a), 140,9(1993). [13] M.vanderAuweraer,F.C.deSchryver,P.M.Borsenberger,andH.Bässler,Adv. Matter., 6,
199(1994). [14] S.D.BaranovskiiandO.Rubel,Descriptionofchargetransportinamorphoussemiconductors.
in:Charge transport in disordered solids with applicationsin electronics.S.D.Baranovskii,(ed.),Wiley,2006.
[15] H. Cordes, S.D. Baranovskii, K. Kohary, P. Thomas, S. Yamasaki, F. Hensel, and J.H.Wendorff,Phys. Rev. B, 63,094201(2001).
[16] K. Kohary, H. Cordes, S.D. Baranovskii, P. Thomas, S. Yamasaki, F. Hensel, and J.H.Wendorff,Phys. Rev. B, 63,094202(2001).
[17] B.I. Shklovskii and A.L. Efros, Electronic Properties of Doped Semiconductors. Springer,Heidelberg,1984.
[18] V.I.ArkhipovandH.Bässler,Phil. Mag. Lett., 67,343(1993). [19] V.I.ArkhipovandH.Bässler,Phil. Mag. Lett., 69,241(1994). [20] V.I.ArkhipovandH.Bässler,Phil. Mag. B, 68,425(1993). [21] V.I.ArkhipovandH.Bässler,Phil. Mag. B, 70,59(1994). [22] V.I.Arkhipov,E.V.Emelianova,andH.Bässler,Phil. Mag. B, 81,985(2001). [23] V.I.Arkhipov,E.V.Emelianova,andH.Bässler,Phys. Rev. B, 64,125125(2001). [24] V.I. Arkhipov, E.V. Emelianova, and H. Bässler, J. Non-Cryst., Solids, 299–302, 1047
(2002). [25] V.I.Arkhipov,P.Heremans,E.V.Emelianova,G.J.Adriaenssens, andH.Bässler,J. Phys.:
Condens. Matter, 14,9899(2002). [26] I.I. Fishchuk, A. Kadashchuk, H. Bässler, and S. Nespurek, Phys. Rev. B, 67, 224303
(2003). [27] Y.RoichmanandN.Tessler,Synth. Metals, 135–136,443(2003). [28] Y.Roichman,Y.Preezant,andN.Tessler,Phys. Stat. Sol. (a), 201,1246(2004). [29] B.Ries,H.Bässler,andM.Silver,Phil. Mag. B, 54,141(1986). [30] O.Rubel,S.D.Baranovskii,P.Thomas,andS.Yamasaki,Phys. Rev. B, 69,014206(2004). [31] S.D.Baranovskii,H.Cordes,F.Hensel,andG.Leising,Phys. Rev. B, 62,7934(2000).
c06.indd 263 5/6/2006 06:08:22 PM
264 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
[32] W.D.Gill,J. Appl. Phys., 43,5033(1972). [33] W.D.Gill,inJ.StukeandW.Brenig,(eds),Proceedings of the Fifth InternationalConference
of Amorphous and Liquid Semiconductors,TaylorFrancis,London,1974,901. [34] G. Horowitz, Physics of organic field-effect transistors. in: Semiconducting polymers.
G.HadziioannouandP.F.vanHutten,(eds),Wiley,NewYork,2000,463. [35] S.J.SantosLemusandJ.Hirsch,Phil. Mag. B, 53,25(1986). [36] T.Holstein,Phil. Mag. B, 37,49(1978). [37] H.ScherandT.Holstein,Phil. Mag., 44,343(1981). [38] A.MillerandE.Abrahams,Phys. Rev., 120,745(1960). [39] B. Movaghar, M. Grünewald, B. Ries, H. Bäassler, and D. Würtz, Phys. Rev. B, 33, 5545
(1986). [40] H. Bässler, Transport and relaxation of excitations in random organic solids: Monte Carlo
simulationandexperiment. in:Advances in DisorderedSemiconductors.M.Pollak,andH.Fritzsche,(eds),Volume2.WorldScientific,Singapore,1990,491.
[41] G.Schönherr,H.Bässler,andM.Silver,Phil. Mag. B, 44,369(1981). [42] M.Grünewald,B.Pohlmann,B.Movaghar,andD.Würtz,Phil. Mag. B, 49,341(1984). [43] A.Nemeth-BuhinandC.Juhasz,inO.MilloandZ.Ovadyahu(eds),Hoppingand Related
Phenomena, Jerusalem,Israel,27–30August,1995. [44] A.Ochse,A.Kettner,J.Kopitzke,J.H.Wendorff,andH.Bässler,Phys.Chem. Chem. Phys.,
1,1757(1999). [45] C.GourdonandP.Lavallard,Phys. Stat. Sol. (b), 153,641(1989). [46] V.Ambegaokar,B.I.Halperin,andJ.S.Langer,Phys. Rev. B, 4,2612(1971). [47] N.W.Dalton,C.DombandM.F.Sykes,Proc. Phys. Soc., 83,496(1964). [48] C.DombandN.W.Dalton,Proc. Phys. Soc., 89,859(1966). [49] M.C.J.M.VissenbergandM.Matters,Phys. Rev. B, 57,12964(1998). [50] S.D.Baranovskii,I.P.Zvyagin,H.Cordes,S.Yamasaki,andP.Thomas,Phys. Stat. Sol. (b),
230,281(2002). [51] S.D.Baranovskii,I.P.Zvyagin,H.Cordes,S.Yamasaki,andP.Thomas,J.Non-Cryst. Solids,
299–302,416(2002). [52] B.HartensteinandH.Bässler,J. Non-Cryst. Solids, 190,112(1995). [53] D.Monroe,Phys. Rev. Lett., 54,146(1985). [54] M.Grünewald,andP.Thomas,Phys. Stat. Sol. (b),94,125(1979). [55] F.R.ShapiroandD.Adler,J. Non-Cryst. Solids, 74,189(1985). [56] B.I.Shklovskii,E.I.Levin,H.Fritzsche,andS.D.Baranovskii,Hoppingphotoconductivityin
amorphous semiconductors: dependence on temperature, electric field and frequency. in:Advances in Disordered Semiconductors. H. Fritzsche, (ed.), Volume 3. World Scientific,Singapore,1990,161.
[57] S.D.Baranovskii,P.Thomas,andG.J.Adriaenssens,J. Non-Cryst. Solids,190,283(1995). [58] S.D.Baranovskii,T.Faber,F.Hensel,andP.Thomas,J. Phys. C, 9,2699(1997). [59] V.I.Arkhipov,U.Wolf,andH.Bässler,Phys. Rev. B,59,7514(1999). [60] S.D.BaranovskiiandA.L.Efros,Sov. Phys. Semicond., 12,1328(1978). [61] H.C.F.Martens,I.N.Hulea,I.Romijn,H.B.Brom,W.F.Pasveer,andM.A.J.Michels,Phys.
Rev. B, 67,121203(2003). [62] R.Schmechel,Phys. Rev. B, 66,235206(2002). [63] R.Schmechel,J. Appl. Phys., 93,4653(2003). [64] D.M.Pai,J.F.Yanus,andM.Stolka,J. Phys. Chem., 88,4714(1984). [65] A.Kadashscuk,Y.Skryshevskii,A.Vakhnin,N.Ostapenko,V.I.Arkhipov,E.V.Emelianova,
andH.Bässler,Phys. Rev. B, 63,115205(2003). [66] V.I.Arkhipov,P.Heremans,E.V.Emelianova,G.J.Adriaenssens,andH.Bässler,Appl. Phys.
Lett., 82,3245(2003). [67] N.F.Mott,Phil. Mag., 19,835(1969).
c06.indd 264 5/6/2006 06:08:22 PM
CHARGETRANSPORTINDISORDEREDORGANICMATERIALS 265
Y2
[68] R.Coehoorn,W.F.Pasveer,P.A.Bobbert,andM.A.J.Michels,Phys. Rev.B, (2005)inprint. [69] P.M.BorsenbergerandD.S.Weiss,Organic Photoreceptors for Xerography.MarcelDekker,
NewYork,1998. [70] D.M.Pai,J. Chem. Phys., 52,2285(1970). [71] L.B.Schein,D.Glatz,andJ.C.Scott,Phys. Rev. Lett., 65,472(1990). [72] L.T.Pautmeier,J.C.Scott,andL.B.Schein,Chem. Phys. Lett., 197,568(1992). [73] A.Bacher,I.Bleyl,C.H.Erdelen,D.Haarer,W.Paulus,andH.W.Schmidt,Adv. Matter., 9,
1031(1997). [74] T.Christ,B.Glüsen,A.Greiner,A.Kettner,R.Sander,V.Stümpflen,V.Tsukruk,andJ.H.
Wendorf,Adv. Mater., 9,48(1997). [75] N.Boden,R.J.Bushby,J.Clements,B.Movaghar,K.J.Donovan,andT.Kreozis,Phys. Rev.
B, 52,13274(1995). [76] I.Bleyl,C.Erdelen,H.W.Schmidt,andD.Haarer,Phil. Mag. B, 79,463(1999). [77] D.H.Dunlap,P.E.Parris,andV.M.Kenkre,Phys. Rev. Lett.,77,542(1996). [78] K.SekiandM.Tachiya,Phys. Rev. B, 65,014305(2002). [79] R.A.Marcus,J. Chem. Phys., 24,966(1956). [80] Y.N.GarsteinandE.M.Conwell,Chem. Phys. Lett., 245,351(1995). [81] S.V.Novikov,D.H.Dunlap,V.M.Kenkre,P.E.Parris,andV.Vannikov,Phys. Rev. Lett., 81,
4472(1998). [82] S.V.Novikov,D.H.Dunlap,andV.M.Kenkre,Proc. SPIE, 3471,181(1998). [83] B.Derrida,J. Stat. Phys., 31,433(1983). [84] K.P.N.MurthyandK.W.Kehr,Phys. Rev. A, 40,2082(1989). [85] K.P.N.MurthyandK.W.Kehr,Phys. Rev. A, 41,1160(1990). [86] A.PeledandL.B.Schein,Chem. Phys. Lett., 153,422(1988). [87] L.B.Schein,Phil. Mag. B, 65,795(1992). [88] A.Hirao,H.Nishiwawa,andM.Sugiuchi,Phys. Rev. Lett., 75,1787(1995). [89] M.E.Raikhand I.Ruzin,Transmittancyfluctuations in randomlynonuniformbarriersand
incoherent mesoscopics. in: Mesoscopic Phenomena in Solids. B. Altshuler, P.A. Lee, andR.A.Webb,(eds),North-Holland,Amsterdam,1991,315.
[90] I.P.Zvyagin,S.D.Baranovskii,K.Kohary,H.Cordes,andP.Thomas,Phys.Stat. Sol. (b), 230,227(2002).
[91] W.F.Pasveer,P.A.Bobbert,andM.A.J.Michels,Phys. Stat. Sol. (c), 1,164(2004). [92] P.M. Borsenberger, L. Pautmeier, R. Richert, and H. Bässler, J. Chem. Phys., 94, 8276
(1991). [93] R.P.Feynman,R.B.Leighton,andM.Sands,The Feynman lectures onphysics.Volume1.
Addison-WesleyPublishing,PaloAlto,1963. [94] R.Richert,L.Pautmeier,andH.Bässler,Phys. Rev. Lett., 63,547(1989). [95] L.Pautmeier,R.Richert,andH.Bäassler,Phil. Mag. B, 63,587(1991). [96] J.M.CasadoandJ.J.Mejias,Phil. Mag. B, 70,1111(1994). [97] Y.RoichmanandN.Tessler,Appl. Phys. Lett., 80,1948(2002). [98] N.W.AschcroftandD.Mermin,Solid State Physics.Holt,RinehartandWinston,NewYork,
1988. [99] R.A.Smith,Semiconductors.CambrudgeUniversityPress,Cambridge,1978.[100] S.D. Baranovskii, T. Faber, F. Hensel, and P. Thomas, J. Non-Cryst. Solids, 227–230, 158
(1998).[101] H.OverhofandP.Thomas,Electronic Transport in Hydrogenated AmorphousSemiconduc-
tors.Springer,Heidelberg,1989.[102] V.I. Arkhipov, P. Heremans, E.V. Emelianova, and H. Bäassler, Phys. Rev. B, 71, 045214
(2005).[103] R.A. Street, Hydrogenated Amorphous Silicon. Cambridge Solid State Science Series,
CambridgeUniversityPress,1991.
c06.indd 265 5/6/2006 06:08:22 PM
266 CHARGETRANSPORTINDISORDEREDSOLIDS
Y2
[104] C. Tanase, E.J. Meijer, P.W.M. Blom, and D.M. de Leeuw, Phys. Rev. Lett., 91, 216601(2003).
[105] H.Shimotani,G.Diguet,andY.Iwasa,Appl. Phys. Lett., 86,022104(2005).[106] X. Jiang,Y.Harima,K.Yamashita,Y.Tada, J.Ohshita, andA.Kunai,Chem. Phys. Lett.,
364,616(2002).[107] V.I.Arkhipov,E.V.Emelianova,andG.J.Adriaenssens,Phys. Rev. B, 63,081202(2001).[108] R.SchmechelandH.vonSeggern,Phys. Stat. Sol. (a), 201,1215(2004).[109] S.D.BaranovskiiandO.Rubel,Descriptionofchargetransport indisorderedmaterials. in:
Handbook of Electronic and Photonic Materials. S. Kasap and P. Capper, (eds), Springer,2006.
[110] P.M.Borsenberger,W.T.Gruenbaum,E.H.Magin,S.A.Visser,andD.E.Schildkraut,Journal of Polymer Science Part B: Polymer Physics, 37,349(1999).
[111] P.M.Borsenberger,W.T.Gruenbaum,E.H.Magin,andS.A.Visser,Phys.Stat. Sol. (a), 166,835(1998).
[112] J.VeresandC.Juhasz,Phil. Mag. B, 75,377(1997).
c06.indd 266 5/6/2006 06:08:22 PM