Applied Catalyclis, 6 (1983) 41-51 Elsevier Science Publishers B.V., Amsterdam - Printed in The Netherlands
41
HYDROGENATION OF HIGHLY UNSATURATED HYDROCARBONS OVER HIGHLY DISPERSED PALLADIUM
CATALYST. PART I: BEHAVIOUR OF SMALL METAL PARTICLES
J.P. BOITIAUX, J. COSYNS and S. VASUDEVAN
Institut Fransais du Petrole, Rueil-Malmaison, France.
(Received 12 October 1982, accepted 20 January 1983)
ABSTRACT
Hydrogenation of 1-butyne over palladium catalysts with dispersions between 9 and 100% reveals that the reaction is sensitive to metallic dispersion. A similar sensitivity is also exhibited by 1,3-butadiene and isoprene, whereas I-butene is insensitive to dispersion. This behaviour of the highly unsaturated hydrocarbons is explained by the formation of a strong complex of these hydro- carbons with very small particles at high dispersion.
INTRODUCTION
The selective hydrogenation of acetylenics (I-butyne and vinylacetylene) in the
1,3-butadiene rich cut of the steam cracking reaction is a commercially attractive
process for meeting the stringent specification of polymer grade butadiene.
Although the literature abounds with work on the selective hydrogenation of acet-
ylene in the ethylene cut [1,23, there are very few publications, excluding patents,
on the selective hydrogenation of C4 cuts [3,4]. Kinetic studies of I-butyne
hydrogenation have been reported by Mann et al. [5-73 over different metals of
Group VIII. This study was however performed under conditions far removed from
those of industrial operations. Furthermore, there has been no work reported on
the influence of metallic dispersion on the hydrogenation of highly unsaturated
hydrocarbons. In a recent publication, we have shown that the hydrogenation of
1,3-butadiene is strongly influenced by the particle size [8]. We observed a marked
decrease in the turnover number (by a factor of 12), when the metallic dispersion
was increased from 20 to 100%. In this article we report a study of the influence
of dispersion on the kinetics of hydrogenation of other unsaturated hydrocarbons,
notably I-butyne, in order to genaralize the special behaviour of the small
particles.
EXPERIMENTAL
Materials
The 1-butyne used in our study was procured from Air Liquide (>95% pure). This
was further purified by passage through a bed of 4A + 13X molecular sieves. The
1-butyne was diluted in n-heptane (>99.8% pure) in order to obtain a concentration
’ 0166~9834/83/$03.00 0 1983 Elsevier Science Publishers B.V.
TABLE
1
Sumnary
of the
different
catalysts
used.
wt%
Support
area
Reduction
in
Desorption
Dispersion
b Turnover no.
Pd
/m2
g-'
I-Butyne hydrog.
H2/=C
O,,
/nm
Butene hydrog.
under
N2/'C
I%
activity/m01
s -1
for
hydrog.
of
activity/m01
g Pd-'
I-butyne/s-'
s-1
-1
o Pd
1 0.37
A-9
700
2 0.33
A-69
250
3 0.33
A-69
500
4 0.76
A-104
700
5 0.33
A-69
250
6 0.37
A-9
350
7 0.76
A-104
300
8 0.33
A-69
250
9 0.33
A-69
300
10
0.20
A-94
300
11
0.33
A-69
350
12
1.06
s-210
400
13
1.06
s-210
700
14
1.06
S-210
700
700
600
500
700
500
350
300
300
300
350
400
700
700
9 11.23
0.0517
60.5
20
4.2
0.0906
60.4
27
2.83
0.0717
28.3
27
2.83
0.0916
36.2
37
1.91
0.0376
11.33
44
1.54
0.0759
18.33
60
1.04
0.0696
12.33
67
0.91
0.0394
6.17
81
0.72
0.0510
6.83
85
0.67
0.0489
6.17
100
0.40
0.0555
5.83
56
1.13
0.0288
5.50
37
1.91
0.0582
16.67
37
1.91
0.0872
25.33
0.074
0.108
0.159
0.159
0.211
0.169
0.271
0.448
aSupport A
= alumina, S
= silica.
b Particle diameter calculated by assuming that the
crystallite
has
cubic
form with on side in contact
with the
support.
'Specific
activity for
the
hydrogenation
of I-butyne determined
at 70%
conversion.
48
of approximately 10% by weight of I-butyne. The hydrogen was of ultra pure grade
(>99.999%) and was further purified in a deoxo unit followed by 4A molecular
sieves.
The two precursors used for the preparation of the catalysts were palladium
acetylacetonate [Pd (CSH702)2] for alumina impregnation and palladium tetramine
nitrate [Pd (NH3141 (NO312 for silica impregnation. These were obtained from
Johnson Matthey, Paris.
Two types of alumina, an a-alumina and a y+_-alumina with
surface areas between 9 and 100 m* g -1
were used as supports in this study. The
silica had a surface area of 210 m* g -1
and a pore volume of 0.76 ml g-l.
Catalysts
Palladium based catalysts have been used in this study. The method of preparation
and the conditions of treatment employed to obtain a high dispersion have been
described in detail elsewhere C81 and are merely summarized here as follows. The
catalyst was prepared by wet impregnation of the alumina carrier with a known
quantity of palladium acetylacetonate dissolved in benzene. It was oven dried at
llO"C, air calcined at 300°C and reduced with hydrogen at temperatures between
300 and 8OO"C, according to the metal dispersion required.
The palladium on silica catalyst was prepared using the palladium tetramine
complex as precursor, as described in the literature C91. This catalyst was
calcined at 400°C and then reduced at two different temperatures to give two
different dispersions.
Table 1 summarizes the different catalysts used in this study, their conditions
of treatment, the metallic dispersions obtained by CO chemisorption and the mean
crystallite sizes (calculated on the basis of a fee structure). Some of these
catalysts were examined in an electron microscope (CTEM Jeol-120 X) and the average
crystallite diameter obtained was in close agreement with the diameter calculated
from CO chemisorption values.
Kinetic tests
Hydrogenation reactions were carried out in the liquid phase, in batch mode
in a CSTR reactor at 2 MPa (20 bar) constant pressure. The hydrogenation rate was
followed by recording the pressure drop in a constant volume hydrogen ballast,
upstream of the pressure regulator, as a function of time. Cooling water was
circulated in the reactor jacket in order to maintain the temperature at 20°C.
The hydrocarbon samples were analysed in an Intersmat IGC 112F chromatograph
provided with a flame ionization detector, using a 6 m 66' ODPN supported on
chromosat PAW column at room temperature.
44
RESULTS
Hydrogenation of l-butyne
In Figure 1 is reported the hydrogen consumption as a function of time for the
hydrogenation of 1-butyne over two catalysts with 9 and 67% metallic dispersion,
respectively. In both cases the hydrogenation started inediately, without any
induction period, and the rate increased as the reaction progressed. As the
hydrogenation rate varies with conversion, the catalyst activities should be
compared at the same conversion. In our study the 1-butyne hydrogenation rates
were evaluated at 70% butyne conversion. Curves A and B of Figure 1 reveal a
negative effect of the dispersion: 1-butyne hydrogenated more quickly on low
dispersion than on high dispersion catalysts.
I !
10 20 30 Tii(mn1 Tie (mud
FIGURE 1 Consumption of hydrogen vs. time during the hydrogenation of I-butyne
and I-butene over two catalysts of 9 and 67% dispersion.
FIGURE 2 I-butyne consumption and evolution of different products over a catalyst
of 85% dispersion.
Figure 2 shows the change of the reaction mixture composition with time over
a catalyst of 85% dispersion. During the hydrogenation of 1-butyne, the only
product of reaction was I-butene (up to a conversion of roughly 80%) if we except
the very small amounts of butane formed right from the beginning. No parallel
isomerization to E-butyne occurred. Once the 1-butyne had almost completely
disappeared, the 1-butene was consumed with a higher rate than the I-butyne (cf.
Figure 1 also). This I-butene hydrogenated into butane and isomerized into 2-
butenes (cis and trans) in two parallel ways. Unlike 1 -butyne, the 1 -butene
reaction did not change with time, the apparent order of reaction being nearly
equal to zero. Lastly, the 2-butenes formed hydrogenated (cis and trans success-
45
ively), but with a very slow rate. Thus the overall reaction scheme could be
represented as:
I-butyne4 I-butene __+ 2-butenes . l .
l * J / butane
Influence of the dispersion on the activity
I-butyne hydrogenation. As is seen in Figure 1, a highly dispersed catalyst
(67%) had an activity which was considerably lower than a catalyst having 9%
dispersion. In order to verify this strange behaviour of the small particles, we
carried out a series of hydrogenation tests over the whole range of dispersion.
We report the activity for the hydrogenation of 1-butyne, expressed as turnover
number (moles of 1-butyne converted per atom of palladium exposed per second).
The turnover number was determined at 70% conversion of 1-butyne and is plotted
in Figure 3 as a function of dispersion. We observed from the curve that the
activity remained constant up to 20% dispersion and decreased sharply thereafter.
The residual activity for very high dispersions close to 100% was around 12 times
lower. The nature of this curve is similar to the variation of activity for the
1,3-butadiene hydrogenation which we have reported earlier C83. Furthermore, we
I I
20 40 60 60 100 DkpanionM
16utene~6lltane l 16UtElW
L: H I------ ~16utem?exl r I
, 0.6 l /
20 40 60 60 100 aspniolorl
FIGURE 3 Variation of the turnover number as a function of dispersion for l-
butyne hydrogenation.
FIGURE 4 Variation of the hydrogenation activity for 1-butene as a function of
dispersion.
verified the variation of turnover number of I-butyne hydrogenation at different
conversions and found that at iso conversion the nature of the curve remained
identical.
I-butene hydrogenation. Referring again to Figure 1, we observed that, contrary
to l-butyne, the rate of hydrogenation of 1-butene (formed from I-butyne) was
higher at higher dispersions. In Figure 4 we plot the rate of hydrogenation of
1-butene (in moles of I-butene hydrogenated per second per gram of palladium) as
a function of dispersion and we observed that the activity increased linearly with
dispersion (i.e. the turnover number remained constant with dispersion). In order
to compare this activity of I-butene (ex 1-butyne) with pure 1-butene, we have
also included the values of the activity of pure I-butene hydrogenation at differ-
ent dispersions in Figure 4 and we find that the values are similar and lie on
the same line. This confirms that the turnover number of I-butene was not influ-
enced by particle size nor by the previous hydrogenation of the acetylenic compound.
Influence of dispersion on the selectivity
1-butyne hydrogenation. As reported previously, some butane was formed from
the beginning of the reaction. The extent of this formation increased with dis-
persion as is seen in Table 2, where the formation of butane at 90 and 99%
conversion of I-butyne is indicated. This behaviour is in line with the observat-
ions that at higher dispersions the I-butene hydrogenation rate remained high,
whereas the 1-butyne hydrogenation rate decreased sharply.
TABLE 2
Dispersion/% 9 44 60 85 100
% butane at 90% I-butyne conversion 2.4 2.5 2.8 3.2
4: butane at 99% 1-butyne conversion 10.20 13.0 24 27
1-butene hydrogenation. Pure l-butene and l-butene formed during the hydrogen-
ation of 1-butyne disappeared with similar rates (Figure 4). Nevertheless, the
similarity of behaviour is no so apparent if we consider the selectivities. The
ratios butane/z Z-butenes and tr-2-butene/cis-2-butene are plotted in Figure 5
for both feedstocks. Two observations can be made: firstly, the selectivities of
the parallel reactions remain constant over the whole range of dispersion and,
secondly, there was a significant difference in the hydrogenation/isomerization
ratio between pure I-butene and I-butene ex 1-butyne (values being 0,95 and 2.0
respectively). This fact is perhaps due to some inhibition of the double bond shift
induced by trace amounts of 1-butyne remaining on the catalytic surface as it is
well known that double bond shift is strongly inhibited by the presence of diolefins
or acetylenes.
41
2.4. .
2.0 . . *
1.6. ‘. 2TrBut~ne/ZCi&utem<~ 2Trans.Butene/2Cia.Buten~
v 1.2. y
0.6. 1 ButendIZButenes
0.4. 2 l :; :;-. t . . , t
I I. * * c 3 ” e 1 I. I. 0.. c 6 1 10 20 30 40 50 60 70 60 90 100 10 20 30 40 50 60 70 60 90100
Dispersion Dispersion ("/.I
FIGURE 5 Selectivity as a function of dispersion during the hydrogenation of
1-butene (pure and ex 1-butyne).
FIGURE 6 Selectivity as a function of dispersion during the hydrogenation of
1,3-butadiene.
1,3-butadiene hydrogenation. The influence of dispersion on the rate of
butadiene hydrogenation and on the butyne hydrogenation rate has been shown to
be similar [S]. In Table 3 the formation of butane at 90 and 99% conversion
of butadiene is shown. The influence of the dispersion on the selectivity
for consecutive reactions is similar for butadiene and for butyne.
TABLE 3 ~~ ~
Dispersion/% 15 37 44 60 81
% butane at 90% 1,3-butadiene conversion 0.45 0.60 1.50 2.30 2.10
% butane at 99% 1,3-butadiene conversion 2.0 3.7 3.9 7.8 8.7
Contrasting with these results, the selectivities for parallel reactions
(tr-2-butene/cis-2-butene and I-butene/z P-butenes) do not change with the metallic
dispersion, as is clearly seen from Figure 6. The difference between the trans/cis
ratios of the P-butenes formed from 1-butene (%1.6) and butadiene (12.0) may be
attributed to the predominance of the anti form (95%) in the butadiene.
DISCUSSION
A brief summary of our results is as follows: the turnover number for the
hydrogenation of I-butene (pure or ex 1-butyne) is constant, irrespective of the
dispersion. However, the turnover number for the hydrogenation of higher unsatur-
ated hydrocarbons, such as 1,3-butadiene and l-butyne, is strongly influenced by
48
the average particle size. In addition to
hydrogenation of isoprene and again found
dependent on dispersion and the nature of
butadiene or 1-butyne.
SsgO 5!6 125
these hydrocarbons, we also studied the
that the turnover number was strongly
the curve was similar to that of 1,3-
412 1:8 110 017 Ihm m
0 20 40 60 80 100
Dispdon 0
FIGURE 7 Relative variation of turnover number with respect to dispersion for the
hydrogenation of 1-butene,m ;l-butyne,n ;1,3_butadiene,+ and isoprene, A .
In Figure 7 we have plotted the variation of the relative turnover number as
a function of dispersion. The relative turnover number is the value obtained by
dividing the turnover number by its maximum value for each hydrocarbon. Thus, for
each hydrocarbon the maximum turnover number is normalised to the value of unity.
This figure demonstrates that at higher dispersion there is a spectacular decrease
in the activity of the hydrogenation of highly unsaturated hydrocarbons by a factor
of around 12 to 15. It is worthwhile emphazing that the hydrogenation studies
were performed over three different types of support, a-A1203, yt-A1203 and Si02,
their surface areas varying between 9 and 200 m2 g-l. The metal loading was varied
between 0.17 and 1.06 wt% and three different metal precursors, Pd(N03)2,
Pd(C5H702j2 and [Pt(NH3j41 (N03J2 were used. In spite of all these variations, the
turnover number seems to be strongly influenced only by the metallic dispersion.
As far as the selectivities are concerned, the consecutive formation of butane
increases with dispersion, whereas the selectivity for all parallel formations of
unsaturated intermediates does not vary with dispersion.
Several hypotheses can be proposed to explain these effects. Some of these are
as follows:
Polymerization. The higher dispersions could promote the polymerization of the
highly unsaturated hydrocarbons that would partially plug the catalytic surface.
49
Such an hypothesis can be easily eliminated as consecutive hydrogenation runs over
the same catalyst have been made with good reproducibility. Moreover, such a
trivial modification would certainly affect the hydrogenation of 1-butene coming
from 1-butyne.
Reducibility. The sharp decrease of turnover number obtained for dispersions
higher than 20% can not be solely explained by the presence of unreduced palladium
at high dispersions. With this interpretation, it is very difficult to explain
such a large effect on diolefin and alkyne hydrogenation (turnover number divided
by 10) while I-butene is not affected. Moreover, all catalysts with high dispersion
were prereduced at a temperature equal to or higher than 25O'C and controlled by
CO chemisorption measurement at room temperature. The stoichiometry observed is
close to one CO per palladium atom [83. In addition. 02-H2 titrations [9] have
shown that 30, is adsorbed on one Pd atom and 3/2 H2 is consumed by one palladium
atom during titration of this oxygen. Such stoichiometries can be explained only
if the major part of the palladium is in the reduced form.
Geometric effects. Geometric effects due to multiple site adsorption of the
hydrocarbons [lo] could be invoked as an hypothesis to explain the decrease in
activity at high dispersion, as multiple site adsorption normally becomes more
difficult as dispersion increases. This
results, wherein we find that the three
I-butyne, which probably have different
same manner with respect to dispersion.
parallel reactions remain constant with
by this hypothesis.
effect can not satisfactorily explain our
hydrocarbons butadiene, isoprene and
geometries of adsorption, behave in the
Furthermore, the selectivities of all
dispersion, which is again hardly explained
Support effects. It has been demonstrated by certain authors [11-123 that the
small metal particles attain the bulk properties only when they contain 100-300
atoms (corresponding to a diameter of 20 A). This would correspond to a dispersion
of about 50%. Certain authors proposed Cl33 that the metal-support interaction
becomes strong when the metal crystallite hasveryfew atoms (less than 200). Our
results demonstrate that the most spectacular fall in activity occurs between 20
and 40% dispersion, which would correspond to a total number of 500-6000 atoms
in the crystallite. With such a large number of atoms present, one can assume that
the particles show bulk metallic properties. In such particles the proportion of
atoms directly influenced by the support must be very low. Hence, even if some
support effect exists, it alone cannot explain the spectacular decrease of turn-
over number observed at dispersions higher than 20%. Hence it is difficult to
attribute the low activity to these type of effects.
Intrinsic metallic properties of the metallic site
If geometric and support effects can be, to a first approximation, neglected,
it is logical to suppose that this variation in activity is due to changes in the
electronic properties of the metal as dispersion increases. At high metallic
50
dispersions the surface atoms of small metal particles present a high coordinative
unsaturation. Under these conditions they can coordinate more strongly with
different species. Our earlier work on the infrared study of CO adsorption showed
that there is a displacement of the bands towards lower frequencies as the
dispersion increases from 27 to 86%, thus confirming a reinforcement of the M-CO
bond at higher dispersion [S].
FIGURE 8 Infrared spectra of the hydrogenation of I-butyne over two different
catalysts. 1, introduction of I-butyne; 2, introduction of hydrogen; 3, after
5 min; 4, after 15 min; 4', after 12 h.
We also tried-to simulate the hydrogenation of I-butyne in the IR cell and the
result of this study is given in Figure 8. On introduction of I-butyne along with
a stream of nitrogen over a catalyst wafer, we observe a peak at 2970 cm -1 , characteristic of adsorbed I-butyne. Over a low dispersion catalyst this peak
disappears completely in about 15 min when hydrogen is introduced, whereas over
a highly dispersed catalyst this peak does not disappear even after 12 h, thus
indicating the formation of a strong complex over the highly dispersed catalyst.
This type of formation of a strong complex with acetylenics and diolefins is known
to occur with metal complexes in coordination chemistry [14]. Over such homogeneous
catalysts the activity for the hydrogenation of butadiene and I-butyne is known
to be very low [15,16]. Thus it is logical to consider the highly dispersed catalyst
as a supported homogeneous catalyst. This type of comparison has already been made
in the literature 1173. Hence we suppose that the low activity shown by the highly
dispersed metal might be due to its electron deficient character. The surface atoms
51
of small particles coordinate more strongly with species which are electron donors.
This has been shown previously over platinum [18]. In our case we can consider
that highly unsaturated hydrocarbons are electron donors, as assumed by several
authors [14], thus explaining the formation of their strong complexes.
If too strong complexation with highly unsaturated hydrocarbons is the reason
why turnover is low at high dispersion, it would be possible, as in homogeneous
catalysis, to increase the activity and selectivity by adding a convenient electron
donating additive (ligand). We will show in a later paper how a nitrogen compound,
such as piperidine, can produce such a ligand effect.
ACKNOWLEDGEMENT
One of the authors (S.V) wishes to thank Engineers India Ltd. (India), for
study leave and the French Government for the grant of a scholarship to carry out
this work.
REFERENCES
1 W.T. McGown, C. Kemball, D.A. Whan and M.S. Scurrell, JCS Faraday Trans. I, 73 (1977) 627.
2 Al. Ammar and G. Webb, JCS Faraday Trans. I, 74 (1978) 195. 3 B. Nowicki, J. Klimeck and A. Masiarz, Przemysl Chemiczny, 55 (1976) 587. 4 H. Blume, R. Batz, R. Schubert and D. Bernhart, Chem. Techn., 25 (1973) 604. 5 R.S. Mann and K.C. Khulbe, J. Catal., IO (1968) 401. 6 R.S. Mann and K.C. Khulbe. J. Catal.. 13 (1969) 25.
17 18
19
R.S. Mann and K.C. Khulbe; J. Catal.; 17 (1970) 46. J.P. Boitiaux, J. Cosyns and S. Vasudevan, Proc. 3rd Int. Symp. on the Scientific Bases for the Preparation of Heterogeneous Catalysts, Belgium, Elsevier, (1982). S. Fuentes and F. Figueras, J. Chem. Sot. Faraday Trans. I, 18 (1978) 74. G. Webbs, in Comprehensive Chemical Kinetics, Vol. 20, Chap. 1. N.R. Avery and J.V. Sanders, J. Catal., 18 (1970) 129. D.N. Ross, K. Kinositha and P. Stonehart, J. Catal., 32 (1974) 163. J.R. Anderson, in Structure of Metallic Catalysts, Academic Press, (1975) 275. R. Ugo, Catal. Rev. Sci. Eng., 11 (1975) 225. E.W. Stern and P.K. Maples, J. Catal., 27 (1972) 120. V.M. Frolov, O.P. Parenago, L.P. Shokina and G.M. Gherkasis, React. Kinet. Catal. Lett., 16 (1981) 115. C. Carturan and G. Strukul, J. Catal., 57 (1979) 516. P. Gallezot, J. Datka, M. Primet and B. Imelik, Proc. 4th Int Cong. Catal., London, The Chemical Society, (1976), p. 697. S. Vasudevan, Thesis E.N.S.P.M. Paris (1982), Technip Ed.
本文献由“学霸图书馆-文献云下载”收集自网络,仅供学习交流使用。
学霸图书馆(www.xuebalib.com)是一个“整合众多图书馆数据库资源,
提供一站式文献检索和下载服务”的24 小时在线不限IP
图书馆。
图书馆致力于便利、促进学习与科研,提供最强文献下载服务。
图书馆导航:
图书馆首页 文献云下载 图书馆入口 外文数据库大全 疑难文献辅助工具