PAINT FAULTS, BITTINESS
INCLUSIONS, EITHERAIRBORN OR FROM
THE PAINT ITSELF.COULD BE PARTIALLYCURED PAINT, OUTOF SHELF LIFE.
7/29/2019 BGas Instruction
2/49
COATING FAULTS BLEEDINGTHE SOLVENT FROMTHE TOP COATSOFTENS THE UNDER
LYING MATERIALAND ALLOWS IT TOPASS INTO ANDTHROUGH THELAYER, CAUSINGDISCOLOURATION.BROWN FORBITUMEN, YELLOWFOR COAL TARS.
7/29/2019 BGas Instruction
3/49
COATING FAULTS BLISTERINGBLISTERS CAN BE FILLED WITH GAS,LIQUID OR
CRYSTALS
7/29/2019 BGas Instruction
4/49
COATING FAULTS CHALKING
DEGRADATION OF A
BINDER DUE TODISRUPTIVE FACTORSIN THE ENVIRONMENT
7/29/2019 BGas Instruction
5/49
COATING FAULTS CISSING
CAUSED BY
INADEQUATESURFACEPREPARATION.
A DIFFERENCE INSURFACE ENERGYCAUSES LOCAL LACK OFADHESION.
7/29/2019 BGas Instruction
6/49
COATING FAULTS CRACKING
COATING AGE ANDDIFFERENTIAL
EXPANSION
7/29/2019 BGas Instruction
7/49
COATING FAULTS CRATERING
BOWL SHAPEDDEPRESSIONS. CAUSED
BY ESCAPING SOLVENTOR GASES. PAINT IS OFTOO LOW A VISCOSITYTO FLOW AND FILL THEDEPRESSIONS
7/29/2019 BGas Instruction
8/49
COATING FAULTS CURTAINS, SAGS, RUNS AND TEARS
CAUSED BY OVERAPPLICATION. REMOVEOFFENDING EXCESS
MATERIAL, LIGHTLYABRADE, RECOAT.
7/29/2019 BGas Instruction
9/49
COATING FAULTS FLAKING
MATERIALPROGRESSIVELYGETS BRITTLE WITH
AGE, CRACKS ANDBEGINS TO DETACH
7/29/2019 BGas Instruction
10/49
COATING FAULTS HOLIDAYS
DEFINED AS BEING :-
A VOID, A MISS, ORAN UNCOATED AREA
7/29/2019 BGas Instruction
11/49
COATING FAULTS LIFTINGCAUSED BY SOLVENT STRENGTH AND ALSO LACK OF
OBSERVANCE OF STATED OVERCOATING TIME
7/29/2019 BGas Instruction
12/49
COATING FAULTS ORANGE PEEL
SIMILAR APPEARANCE TO A
CITRUS FRUIT SKIN
CAUSED BY PAINT VISCOSITY PROBLEMS OR BY
APPLICATOR TECHNIQUE
7/29/2019 BGas Instruction
13/49
COATING FAULTS ROPINESS
BRUSHMARKS
7/29/2019 BGas Instruction
14/49
COATING FAULTS WRINKLING ANDRIVELLING
7/29/2019 BGas Instruction
15/49
COLOUR MUNSELL AND BS 4800L= LUMINANCE, CHROMAa= FROM GREEN TO RED
b= FROM BLUE TO YELLOW
YELLOW THROUGH GREEN ,BLUE
PURPLE, RED AND BACK TO YELLOW
7/29/2019 BGas Instruction
16/49
HEALTH AND SAFETY DRAGER TUBE AND BELLOWS
7/29/2019 BGas Instruction
17/49
RUST GRADES
7/29/2019 BGas Instruction
18/49
RUST GRADES
7/29/2019 BGas Instruction
19/49
BLASTING GRADES A Sa 2.5 and Sa 3
7/29/2019 BGas Instruction
20/49
BLASTING GRADES B Sa 1 and Sa 2
7/29/2019 BGas Instruction
21/49
BLASTING GRADES B Sa 2.5 and Sa 3
7/29/2019 BGas Instruction
22/49
BLASTING GRADES, COMPARISONS
7/29/2019 BGas Instruction
23/49
BLASTING GRADES C Sa 1 and Sa 2
7/29/2019 BGas Instruction
24/49
BLASTING GRADES C Sa 2.5 and Sa 3
7/29/2019 BGas Instruction
25/49
BLASTING GRADES D Sa 1 and Sa 2
7/29/2019 BGas Instruction
26/49
BLASTING GRADES D Sa 2.5 and Sa 3
7/29/2019 BGas Instruction
27/49
DRY ABRASIVE BLASTINGMEASURING PRESSURE AT THE NOZZLE
HYPODERMIC NEEDLE
GAUGE
INSERT THE NEEDLETHROUGH THE HOSEWITH THE NEEDLE
TOWARDS THE NOZZLE,AT AN ANGLE OF APP.
45 DEGREES
7/29/2019 BGas Instruction
28/49
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING B St 2 and St 3
7/29/2019 BGas Instruction
29/49
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING C St 2 and St 3
7/29/2019 BGas Instruction
30/49
SURFACE PREPARATION
HAND AND POWER TOOL CLEANING D St 2 and St 3
7/29/2019 BGas Instruction
31/49
FLAME CLEANING
1, EXPANSION, co-efficient of expansion
2, DEHYDRATION, water evaporated away
3, HEAT PENETRATION, heat conducted into substrate
7/29/2019 BGas Instruction
32/49
SURFACE PREPARATION FLAME CLEANING
7/29/2019 BGas Instruction
33/49
PAINT TESTINGDENSITY THE DENSITY ( SG ) CUP
7/29/2019 BGas Instruction
34/49
PAINT TESTINGHEGMAN GRIND GAUGE
FOR FINENESS OF GRIND, DEGREE OF DISPERSION
7/29/2019 BGas Instruction
35/49
PAINT TESTING, VISCOSITY
ROTATIONAL VISCOMETERWITH ROTOTHINNERMEASURES DYNAMIC
VISCOSITY. UNITS, POISES
7/29/2019 BGas Instruction
36/49
PAINT TESTING. VISCOSITY
KREBS STORMER VISCOMETER
KINEMATIC VISCOSITY
DRIVEN BY A FALLING
WEIGHT, THE HEAVIER
THE WEIGHT THE
FASTER IT ROTATES.CRITERIA 200 RPM
UNITS STOKE OR POISE
7/29/2019 BGas Instruction
37/49
PAINT TESTING
FLOW VISCOSITY
A FORD FLOW CUP
FORD FLOW CUP IN ITS
RETORT AND SHOWINGTHE 4mm DIA HOLE
7/29/2019 BGas Instruction
38/49
PAINT TESTING VISCOSITY. FORD FLOW CUP
7/29/2019 BGas Instruction
39/49
PAINT FILM MEASUREMENT, WET FILMECCENTRIC WHEEL
7/29/2019 BGas Instruction
40/49
WET FILM THICKNESS MEASUREMENT
COMB GAUGES
7/29/2019 BGas Instruction
41/49
DESTRUCTIVE TEST GAUGES. THE SABERG TEST DRILL
7/29/2019 BGas Instruction
42/49
DFT MEASUREMENTS ELECTRONIC GAUGES
ELECTROPHYSIC
MINI TEST THE EXACTO
ELCOMETER
456
7/29/2019 BGas Instruction
43/49
DRY FILM THICKNESS MEASUREMENT, MAGNETIC.THE TINSLEY PENCIL
7/29/2019 BGas Instruction
44/49
DRY FILM THICKNESS MEASUREMENT, MAGNETIC,HORSESHOE GAUGE
7/29/2019 BGas Instruction
45/49
DRY FILM THICKNESS MEASUREMENT, MAGNETIC,
THE BANANA GAUGE MODEL 111
7/29/2019 BGas Instruction
46/49
DRY FILM THICKNESS MEASUREMENTS, MAGNETIC
THE BANANA GAUGE MODEL 211
SCALE MOVESTO THECURSER
7/29/2019 BGas Instruction
47/49
HEALTH AND SAFETY, COSHH REGULATIONSABBREVIATIONS
EH 40,GUIDANCE NOTES, HEALTH AND SAFETY EXECUTIVE
MEL, MAXIMUM EXPOSURE LIMIT
OEL,OCCUPATIONAL EXPOSURE LIMIT
OES,OCCUPATIONAL EXPOSURE STANDARD
LEL,LOWER EXPLOSIVE LIMIT
UEL,UPPER EXPLOSIVE LIMITRAQ,REQUIRED AIR QUANTITY
7/29/2019 BGas Instruction
48/49
DRY FILM THICKNESS MEASUREMENT
COLOUR CODED CALIBRATION SHIMS
PURPLE 25um
BLUE 50um
BROWN 125um
WHITE 250um
YELLOW 500um
nominal values
7/29/2019 BGas Instruction
49/49
FLEXIBILITY TEST CONICAL MANDREL