Copyright jp Kabegami

Product name Key Features XNR/H 6809 Standard type XNR6840V VaRTM(Infusion) type of XNR6840

*product under development

Product name Key Features XNR/H 6842 Standard type XNR6840P Prepreg type of XNR6840 Figure1:Hybrid molding(Prepreg & VaRTM)

*product under development

For Adhesive Product name Key Features XNR6852F Film sheet type, High toughness, High elongation

Figure2 :Film sheet adhesive

Product name Product name Product name XNR/H 6951-3 XNR/H 6950 XNR6830/H6841

Figure5 : Burning test(Before & After)

Figure3 :Groove filling and trimming Figure4 :Low density epoxy compound Figure6 : Image of light cover

Nagase ChemteX Corporation Nagase Co & LTD.,(Harima Second Factory) (Grobal Trading Company)Add :236, Tatshnocho-nakai, Add: 5-1, Nihonbashi-Kobunacho,tatsuno, Hyogo, 679-4124, Japan Chuo-ku,TokyoTEL: +81-791-63-1054 TEL:81-3-3665-3784FAX: +81-791-63-2302 FAX:81-3-3665-3980URL: http://www.nagasechemtex.co.jp URL:http://www.nagase.co.jp

For Interior-Lighting system-

DENATITEEPOXY RESIN for Aeronautics

For RTM / Infusion

For Prepreg

For Groove filling For Honeycomb Structure-Low density epoxy compound-

CFRP

Model

Trimming

ISO 9001

Contact person

Groove filling

Viscosity (mPa・s) at 25℃ Mix ratio Work time (min) Gel time (min)

Resin / Hardener / Mixture R : H (wt%) 25℃/ 40℃ /60℃ 60℃ / 80℃

XNR/H 6809 800 / 80 / 260 100 : 95 　- / 140 / 60 '- / 90 - / - / 130 (at 120℃) - 120(at 120℃) 100(at 150℃)

Flexural strength / modulus Impact strength Tg ISO 527-1 at 25℃ ISO178 at25℃ ISO179 25℃ DSC　　　　 　N/mm2 / Gpa / % 　　　　N/mm2 / Gpa KJ/m2 ℃

XNR/H 6809 135 / 3.2 27 115160 / 4.0 - 195

Viscosity (Pa・s) at 25℃ Mix ratio Work time (min) Gel time (min)

Resin / Hardener / Mixture R : H (wt%) 25℃/ 40℃ /60℃

XNR 6842 1200 / / - - / - / - 65min(110℃）

Flexural strength / Modulus Impact strength Tg Standard ISO 527-1 at 25℃ ISO 178 at25℃ ISO 179 25℃ DSC

Unit 　　　　 　N/mm2 / Gpa / % 　　　　　N/mm2 / Gpa KJ/m2 ℃

XNR 6842 102　 / 2.5 150 102

Form Thickness Work time (min) Curing requirement

(μm) 25℃/ 40℃ /60℃

Non-woven scrim 120~130 　- / - / -T-Peel Strength Impact strength Tg

ISO11339 at25℃ ISO179 25℃ DSCN/25mm KJ/m2 ℃

93 - 100

Viscosity (Pa・s) at 25℃ Mix ratio Work time (min) Gel time (min) Resin / Hardener / Mixture R : H (wt%) 25℃/ 40℃ /60℃ 60℃ / 80℃

408 / 80 / 300 100:22 30 / / 160 min (at 25℃)208 / 192 / 330 100:50 - / 160 / 60 - / -

10/0.55/6.3 100:160 / / - / 30Flexural strength / Modulus Impact strength Tg

Standard ISO 527-1 at 25℃ ISO 178 at25℃ ISO 179 at 25℃ DSCUnit 　　　　 　N/mm2 / Gpa / % 　　　　　N/mm2 / Gpa KJ/m2 ℃

/ - 85 / 　　　　　 / / - 208

131 / 3.3 17 92

Nagase ChemteX Corporation Nagase Co & LTD.,(Harima Second Factory) (Grobal Trading Company)Add :236, Tatshnocho-nakai, Add: 5-1, Nihonbashi-Kobunacho,tatsuno, Hyogo, 679-4124, Japan Chuo-ku,TokyoTEL: +81-791-63-1054 TEL:81-3-3665-3784FAX: +81-791-63-2302 FAX:81-3-3665-3980URL: http://www.nagasechemtex.co.jp URL:http://www.nagase.co.jp

XNR6840V(P)

XNR6840V(P)

XNR6852F

XNR6852F

XNR/H6951-3XNR/H6950XNR6830/H6841

ISO604 at 25℃

Unit N/mm2 / Gpa21 - / -

Unit Standard

For Adhesive

95 / 2.4 / 　　　　　 / -

For Groove filling / Honycomb Structure / Mould

ISO604 at 25℃

N/mm2 / GpaXNR/H6951-3XNR/H6950XNR6830/H6841

/ 　　　　　 / 68 / 2.1

85℃ 45min + 130℃ 1h4h 80℃ + 2h 120℃ + 6h 180℃

24h 25℃ + 5h 50℃

Tensile strength / Modulus / Elongation Compressive strength/modulus

Curing requirement

- / - / -

Compressive strength/modulus

115 / 3.1 ' 190 / 4.0

For RTM / Infusion

6h 80℃+ 2h 120℃

N/mm2 / Gpa

ISO 604 at 25℃

N/mm2 / Gpa 84 / 2.4

For Prepreg

2h 110℃ + 5h 150℃

Tensile strength / Modulus / Elongation Compressive strength/modulus

N/mm2

5h 150℃ + 5h 200℃

DENATITE

Curing requirement

EPOXY RESIN for Aeronautics

Curing requirement

Tensile strength / Modulus / Elongation

86 / 3.3 / 5.0

ISO604 at 25℃

Single Lap Shear Strength Compressive strength/modulus Standard

8hr/110℃, 3hr/120℃, 1hr/150℃

ISO4587 at 25℃

63 / 2.0 　 / 15

What do you expect our products? High Tg? High CAI property? etc.Please contact us and tell your request. We are going to make our product improve!