Product DataManual
HEMPEL
HEMPEL
EXPLANATORY NOTES TO PRODUCT DATA SHEETSThe product data sheets comprise descriptions of the products, product data, and guidelines/recommendations for theiruse. The purpose is to contribute to the best possible results when using the products.
PRODUCT NAMES, QUALITY NUMBERS, AND SHADE NUMBERS.
PRODUCT NAMES: Generally the proprietary name of a Hempel paint is a collective name denoting thegroup and the generic type to which it belongs, thus:
Physically drying:
HEMPATEX® : Chlorinated rubber, acrylic (solvent-borne)HEMPANYL® : Vinyl, vinyl copolymerHEMUCRYL® : Acrylic (water-borne)
Chemically curing:
HEMPALIN® : Alkyd, modified alkyd (oxidatively drying)HEMPADUR® : Epoxy, modified epoxy (solvent-borne, solvent-free)HEMUDUR® : Epoxy (water-borne)HEMPATHANE® : Polyurethane (isocyanate)GALVOSIL® : Zinc silicate
Note: Where a proprietary name is not used the product name is preceeded by HEMPEL'S.
QUALITY NUMBERS: Each Hempel product is identified by a 5-digit quality number. The first two digits relateto the principal function and the generic type. The third and fourth digits are serialnumbers. The fifth digit identifies specific formulas with the same product, e.g. hightemperature curing/low, medium temperature curing, conformity to local legislation. Therefore, the first four digits define the end-user performance, ie the dried, cured paintmaterial. The fifth digit usually relates to the conditions of application, however, mayalso be used purely for logistic reasons.
First digit Function
0 - - - - Clear varnish, thinner
1 - - - - Primer for steel and other metals
2 - - - - Primer for non-metallic substrates
3 - - - - Paste product, high-solids material
4 - - - - Intermediate coating, high-build coating used with/without primer and finishing coat
5 - - - - Finishing coat
6 - - - - Miscellaneous
7 - - - - Antifouling paint
8 - - - - Miscellaneous
9 - - - - Miscellaneous
Second digit Generic type
- 0 - - - Asphalt, pitch, bitumen, tar
- 1 - - - Oil, oil varnish, long-oil alkyd
- 2 - - - Medium to long-oil alkyd
EXPLANATORY NOTES Page 1A/9
Issued: October 1999
HEMPEL
- 3 - - - Short-oil alkyd, styrenated alkyd, epoxyester, silicone alkyd, urethane alkyd
- 4 - - - Miscellaneous
- 5 - - - Reactive binder (non-oxidative), one or two-component
- 6 - - - Physically drying binder (solvent-borne) (other than - 0 - - -)
- 7 - - - Miscellaneous
- 8 - - - Aqueous dispersion, thinner
- 9 - - - Miscellaneous
Example: HEMPADUR 15570: 1 - - - - Primer for steel- 5 - - - Reactive binder- - 57 - Serial number- - - - 0 Standard formula
SHADE NUMBERS: Hempel paints are supplied in colours identified by a 5-digit, standard shade number asfollows:
White : 10000Whitish, grey : 10010-19980Black : 19990Yellow, cream, buff : 20010-29990Blue, violet : 30010-39990Green : 40010-49990Red, orange, pink : 50010-59990Brown : 60010-69990
Example:HEMPALIN PRIMER 12050-50410: 50410 = red shade
Hempel’s standard shade numbers do not directly correlate to official colour standardnumbers. However, colours corresponding to specific official standard colours may beestablished.
Frequently used colours/shades are displayed in HEMPEL’s colour cards.
The fifth digit may be used to identify specific formulas with the same shade, but adifferent type of pigments used, eg conformity to (local) legislation. 0 indicates astandard formulation, 6 lead-containing pigments.
Note: The shades of primers, many intermediates and antifoulings may fluctuate as adistinct shade is not important for such products.
Description: A short description of the product with emphasis on generic type, pigmentation, principalproperties, and certain limitations.
Recommended use: The purpose(s) for which the product is designed or particularly well suited. The productmay be specified for other uses in tailormade paint systems for specific purposes.
Service temperature: Indicates the maximum temperature that will have no immediate detrimental effect onthe paint.
A service temperature constantly near the maximum will result in a shorter lifetime ofthe specified paint system compared to the lifetime anticipated when operating atnormal temperatures. If service temperatures are often fluctuating between normaltemperatures and near maximum temperatures this will result in an additional decreasein the anticipated lifetime of the paint system ("accelerated ageing").
Most paints will change appearance when exposed to high temperatures, either by adirect change of colour or by loosing gloss.
EXPLANATORY NOTES Page 2A/9
Issued: October 1999
HEMPEL
Approvals, certificates: A list of official and semi-official certificates and approvals.
Other certificates and approvals than listed may be available from the nearest HEMPELoffice.
Availability: Delivery of certain products require notice in advance for logistic reasons. This isindicated by the expression “Local availability subject to confirmation”.
PHYSICAL CONSTANTS
Finish: The appearance of the paint film after drying under optimum conditions in laboratory, given as high gloss (>90), glossy (60-90), semi-gloss (30-60), semi-flat (15-30), or flat(<15). All figures are in gloss units and according to ASTM D 523-67 (specular gloss, 60degree geometry). The actual appearance will depend on the conditions duringapplication and drying/curing.
The finish indicated in the product data sheet is according to optimal conditions (ieapplication and measurements under standardized laboratory conditions).
Colours/shade nos: See SHADE NUMBERS. Certain physical constants may vary from one colour to another.
Volume solids: The Volume Solids (VS) figure expresses in percentage the ratio:
Dry film thicknessWet film thickness
The stated figure has been determined as the ratio between dry and wet film thicknessof the coating applied in the indicated thickness under laboratory conditions, where nopaint loss has been encountered.
For selected paints not drying too fast an alternative airless spray procedure is:
A paint is applied by airless spray in the indicated thickness to a smooth, degreasedsteel panel. Application and drying/curing conditions of the paint are (approx)23°C/73°F and 50% RH. A number of wet film thickness measurements are takenimmediately after application followed by a similar number of dry film thicknessmeasurements 7 days (approx 23°C/73°F, 50% RH) after application.
Volume solids are usually slightly higher than the theoretical value, which is found by acalculation based on the paint composition taking specific gravity and solid content ofeach individual raw material into consideration.
Volume solids take into account that small amounts of solvents are usually retained,and that air may be entrapped in the dry paint film either in the form of vacuoles or asinterstices in zinc silicates.
Volume solids are in better agreement with practical measurements of dry film thicknessthan the theoretical value.
Theoretical spreading rate: The theoretical spreading rate of the paint in a given dry film thickness on a completelysmooth surface is calculated as follows:
m²/litreVolume solids% x 10Dry film thickness (micron) =
or
sq.ft./US gallonVolume solids% x 16.04Dry film thickness (mils) =
1 mil is rounded off to 25 micron - the exact value is 25.4 micron.
In the product data sheet the Theoretical spreading rate is stated for an indicated dryfilm thickness (dft) that is usually specified for the product. Some products may bespecified in different dry film thicknesses for different purposes affecting the spreadingrate accordingly. Theoretical spreading rate cannot be given for paint materials used forsaturation of an absorbing substrate, wood, concrete, etc.
EXPLANATORY NOTES Page 3A/9
Issued: October 1999
HEMPEL
The Practical spreading rate is not given in the product data sheet as the variation is toogreat to be represented by one single figure.
Consumption factor: The practical consumption is estimated by multiplying the theoretical consumption with arelevant Consumption Factor (CF).
The Consumption Factor depends on a number of external conditions and cannot bestated in the product data sheet as the variation is too great to be represented by onesingle figure.
Practical consumption = Area x CFTheoretical spreading rate
The variation in the Consumption Factor is largely attributed to the following:
1) Waviness of paint film:
In order to ensure the specified minimum film thickness, a manually applied paintfilm will unavoidably a) show some waviness of the surface and b) a thicknessdistribution with an average value somewhat higher than the specified dry filmthickness in order to fulfil eg an 80:20 rule. This leads to a higher consumption thantheoretically calculated.
2) Complexity and size/shape of the surface to be calculated:
Complex, odd-shaped and small-sized surfaces are virtually impossible to paintwithout overspray and will therefore lead to higher consumption than theoreticallycalculated from the area square in question.
3) Surface roughness of the substrate:
Surface roughness of the substrate gives a "dead volume" to be filled up or in thecase of shopprimers a "surface area ratio" greater than one and will therefore causea higher consumption than theoretically calculated for a smooth substrate.
4) Physical losses:
Factors such as residues in cans, pumps and hoses, discarded paint due toexceeded pot life, wind loss, etc. will all contribute to a higher consumption.
The Practical spreading rate thus varies with method of application, skill of the painter,shape of the object to be painted, texture of the substrate, film thickness applied, andworking conditions.
In any case it is not beneficial to stretch the paint as much as possible, but rather to tryto obtain the specified thickness of the applied paint on the entire area.
Flash point: The lowest temperature at which a liquid liberates sufficient vapour to form a mixturewith the air near its surface which, if ignited, will make a small flash, but not catch fire.
The flash points of HEMPEL’S paints are measured according to the Setaflash method(closed cup). For two-component products flash points are normally given for the mixedproducts. The figures are given as a guidance with a view to local regulations forprecautions against fire during use.
Adding THINNER to a paint may change the flash point of the diluted material.
Specific gravity: The weight in kilogramme per litre at 25°C/77°F. An equivalent figure is given in lbs perUS gallon.
For two-component products the specific gravity is given for the mixed product.
The specific gravity may in practice vary in an interval of a few percent compared to thetheoretical value indicated in the product data sheet.
Dry to touch: Drying time in the product data sheet is “dry to touch” unless otherwise indicated.
For shopprimers a more relevant figure for "dry to handle" is given.
EXPLANATORY NOTES Page 4A/9
Issued: October 1999
HEMPEL
Drying times refer to a temperature of 20°C/68°F, 60-70% relative humidity, withadequate ventilation.
"Dry to touch": A slight pressure with a finger does not leave a mark and the surface does not feel sticky
"Dry to handle": The paint surface is suffiently hardened to be handled with care without coming off/being damaged.
The drying process until "dry to touch" is - for solvent (or water) containing paints - firstand foremost dependent on ventilation. Furthermore it depends on the temperature andon the film thickness of each coat applied.
All surfaces should be ventilated. It should be noted that waterborne paints have higherrequirements to ventilation than do solventborne paints.
In the case of physically drying paints, drying time is also influenced by the number ofcoats, the total film thickness of the system and the film thickness per coat. As a roughrule of thumb, twice the film thickness of a given single coat will require approx 4 timesthe drying time with the same amount of ventilation. This goes for both solvent andwaterborne paints.
It should be stressed that when apply applying more coats, entrapped solvents mayresult in a softer film than if only one coat is applied. This is especially relevant in thecase of physically drying paints.
Also temperature has much infuence on the drying/curing time. A temperature drop to10°C/18°F will roughly require twice the drying time for physically drying paints.
Fully cured: The curing time is given for two-component products at a (steel) temperature of20°C/68°F and provided adequate ventilation. The curing is accelerated at highertemperatures and retarded at lower temperatures. For some products the curing timesat different temperatures are given as a table in the product data sheet/in theApplication Instructions. For products where the curing time is given at 20°C/68°F only,the following rough rule of thumb can be utilized:
The curing time is roughly halved at an increase in temperature of 10°C/18°F, anddoubled at a decrease in temperature of 10°C/18°F.
Curing will stop almost completely below the temperature stated under applicationconditions as the lowest temperature at which the paint should be applied.
V.O.C.: The calculated weight of volatile organic content in gramme per litre. An equivalent figureis given in lbs per US gallon.
Alternatively, VOC can be indicated by a measured value.
For water-borne paints, two VOC figures are indicated:
1. VOC calculated on total wet paint.
2. VOC calculated omittting the water content in the wet paint (according to ASTM D3960).
Shelf life: The time the product will keep in good condition when stored under cover in original,sealed containers under normal storage conditions. Shelf life is indicated only if it is oneyear or less at 25°C/77°F. It will decrease at higher temperatures, eg will be almosthalved at 35°C/95°F.
If no specific limitation is given, a paint should not be stored for more than five years at25°C/77°F or three years at 35°C/95°F for one-component products and three years at25°C/77°F or two years at 35°C/95°F for two-component products from the date ofproduction.
Long-term storage and storage at high temperatures may require careful remixing of thepaint prior to application due to (slight) sediment in the can.
EXPLANATORY NOTES Page 5A/9
Issued: October 1999
HEMPEL
If storage conditions are unknown and in any other case in doubt about suitability of apaint material this can be rather easily verified by checking the following:
a. no corrosion of the inside unopened, undamaged cans
b. apparent viscosity in can: after remix, paint must not appear gelatinous or require excessive thinning prior to proper application
c. application in specified film thickness: a uniform, closed paint film is to be demonstrated
d. drying time to be within the limit specified in the product data sheet
The date of production is indicated in the first 3 digits of the batch number:The first digit indicates the year of production, the second and third digits indicate themonth of production.
APPLICATION DETAILS
Mixing ratio: Two-component, chemically curing products are supplied as BASE and CURING AGENT inthe correct mixing ratio. The mixing ratio must be strictly adhered to, also whensub-dividing. As a general rule, add the CURING AGENT to the BASE 30 minutes(induction time) before use (at 20°C/68°F), unless the pot life is (very) short, and stirwell. This is especially of importance when applying paints to low-temperture surfaces.In certain cases, more specific advice is given as to induction time.
It is very important for two component products that the prescribed amount of CURING AGENT is added to the BASE. In order to ensure this the indicated thinner may in mostcases beneficially be used to flush the CURING AGENT can. Once the material has beenmixed the curing will proceed. Therefore, only the quantity needed within the pot life ofthe mixture should be mixed at a time.
Application method: Gives the possible or recommended method(s) of application. As a general rule, the firstcoat of a rust-preventing primer should be applied by brush or airless spray to obtainbest possible wetting and penetration into the substrate.
Application by brush or roller usually demands more coats applied to achieve thespecified film thickness than application by airless spray equipment.
Thinner (max.vol): HEMPEL’S paints are delivered in such a way, that they are ready for application at20°C/68°F by brush or airless spray after stirring (for two-component products aftermixing of BASE and CURING AGENT). This goes for a given normal application range ofdry film thickness. If the paint is too thick, eg in cold weather or for special purposes egapplication in lower film thickness, the THINNER(S) indicated under this heading may beadded to give the required viscosity. The amount of thinner to be added, depends onprevailing temperature, spray method, etc. The usual maximum percentage is indicatedfor the respective application method. If more thinning is deemed necessary underspecial circumstances, consult nearest HEMPEL office.
Adding a small percentage of thinner will give no measurable difference in the filmthickness. There are cases, however, when a higher degree of thinning is necessary andjustified. It should then be kept in mind that adding thinner increases the quantity ofliquid paint without contributing to the solids content. Consequently, a proportionallyhigher wet film thickness must be applied when adding any significant amount of thinnerin order to obtain the specified dry film thickness.
VS% after thinning = VS% x 100% THINNER added + 100
EXPLANATORY NOTES Page 6A/9
Issued: October 1999
HEMPEL
Example: If 0.5 litre of THINNER is added to 20 litres of paint, then % THINNER added equals
0.5 x 10020 = 2.5%
VS% after thinning equals
VS% x 100102.5
Note: Avoid unnecessary eg habitual thinning.
Pot life: Roughly speaking, the pot life for solvent-borne paints depends on the painttemperature as follows:
The pot life is halved at an increase in temperature of 10°C/18°F, and doubled at adecrease in temperature of 10°C/18°F.
For HEMPADUR products the pot life is usually shorter for application by airless spraythan for brush application. This is due to the fact that the anti-sagging properties aregradually lost after expiration of the pot life indicated for airless application. Thus thehigh dry film thickness usually specified by airless spray application is only obtainablewithin the pot life indicated for airless application.
Note: Pot life cannot be extended by thinning.
In the case of water-borne, two-component epoxy products this rule of thumb will not fit.The temperature's influence on the pot life is noted in the relevant data sheets.
Nozzle orifice: A typical nozzle orifice (or a range of nozzle orifices) is indicated.
Nozzle pressure: A nozzle pressure generally suitable is given.
Note: Airless spray data are offered as a guidance and are subject to adjustment to suit the work at hand.
Cleaning of tools: Normally the indicated HEMPEL THINNER can be used for cleaning of tools after use.Where special cleaning agents are recommended it is indicated on the product datasheet.
Tools used in connection with waterborne paints may be difficult to clean. Therefore, it isespecially important to follow the instructions stated in the product data sheets.
Indicated film thickness, dry: Dry film thickness (dft) is indicated in a thickness frequently used in specifications. Note: Several products are specified in different film thicknesses for different purposes.
Checking of dry film thicknesses is, generally, done with gauges calibrated on smoothreference steel panels. Shopprimers are controlled according to a special procedure,which is available at your nearest Hempel office.
Indicated film thickness, wet: Wet film thickness (wft) is indicated in multiple of 25 micron (1 mil) in order to facilitatethe practical measurements with the wet film thickness gauge (comb gauge). Thesevalues are rounded off to the multiple of 25 which is regarded most relevant in eachcase.
Recoat interval: The time required or allowed to pass at 20°C/ 68°F or the relevant temperature rangefor the product in question before the subsequent coat is applied. The intervals arerelated to the temperature, film thickness, number of coats, type of future (in service)exposure and will be affected correspondingly. For maximum intervals the temperature inthis context is the highest surface temperature during the period. For some products theinterval is more critical in regard to intercoat adhesion than others. If the maximum
EXPLANATORY NOTES Page 7A/9
Issued: October 1999
HEMPEL
interval is exceeded it may be necessary to roughen the surface to ensure adhesion ofthe next coat. On the other hand, for some paint types the interval may not be critical inrespect of adhesion, but a primer coat should not be left unprotected for too long in anaggressive environment.
If nothing else is mentioned the indicated intervals refer to recoating with the samepaint. Other paints of different types may require other (recoating) intervals.
Minimum and any maximum intervals should always be adhered to if the paint system isto provide maximum protection.
Furthermore, beware of undesired influence of moisture and carbon dioxide on epoxyand polyurethane paints, which especially occurs at low temperatures and high humidity.This will result in a greasy surface preventing any adhesion of the subsequent coat.
After exposure of any painted surface in polluted environment thorough cleaning by highpressure fresh water hosing or another appropriate measure is always recommendedbefore recoating.
Different minimum and maximum recoating intervals are given for certain productsdepending on the later exposure, ie
• In atmospheric conditions mildmediumsevere
• In water
Details about recoat intervals are stated in the relevant painting specification.
SURFACE PREPARATION: The recommended degree of cleaning of the surface before painting. The degrees ofcleaning refer to ISO 8501-1:1988. Pictorial Surface Preparation Standards for Paintingof Steel Surfaces, unless otherwise indicated.
For some products a minimum surface profile is mandatory. The profile so specified isgiven with reference to one or more of the roughness comparators: Rugotest No. 3,Keane-Tator Comparator, or the ISO Comparator.
For previously painted surfaces the method and degree of preparatory cleaning isgenerally indicated.
APPLICATION CONDITIONS: If climatic or other limits, beyond what is dictated by normal good painting practice,apply to the use of a particular quality of paint, this is indicated under this heading. As a general rule, paint should never be applied under adverse weather conditions. Evenif the weather seems fit for painting there will be condensation if the temperature of thesubstrate is at or below the dew point (the temperature at which the atmospherichumidity condenses, e.g. as dew). To compensate for fluctuations the temperature ofthe surface should be at least a few degrees above the dew point during painting anddrying. 3°C/5°F is often quoted as safe.
Beware of ice on the surface at temperatures below the freezing point.
In confined spaces it may be necessary to remove solvent vapours or water vapours byproviding an adequate amount of fresh air constantly during application and drying, bothfor reasons of safety and health, and to assist evaporation.
Keep the paint temperated (room temperature) when applying during winter. If not, thepaint will require excessive thinning leading to an increased risk of sagging. Viscosity inany paint will increase if the temperature decreases.
PRECEDING COAT: Recommendations of some preceding paint(s) known to be compatible with the product.No limitation is implied. Other compatible products may be specified depending on thepurpose. In this context, shopprimers are regarded an integral part of the surfacepreparation.
EXPLANATORY NOTES Page 8A/9
Issued: October 1999
HEMPEL
SUBSEQUENT COAT: Recommendations of some subsequent paint(s) known to be compatible with theproduct. No limitation is implied. Other compatible products may be specified dependingon the purpose.´
REMARKS: Under this heading other relevant data or information are included.
SAFETY: Under this heading general safety precautions when handling or working with theproduct are given. Packings are provided with applicable safety labels which should beobserved. In addition, Material Safety Data Sheets, national or local safety regulationsshould always be followed.
ISSUED: Month and year of issue, current formula.
Note: The product data sheets are subject to change without notice and automaticallyvoid five years from issue.
Additional notes and definitions of some expressions used in the product data sheets:
Surface cleaning*Low pressure water cleaning (LP WC): up to 340 bar/5000 psiHigh pressure water cleaning (HP WC): 340-680 bar/5000-10.000 psiHigh pressure water jetting (HP WJ): 680-1700 bar/10.000-25.000 psiUltra-high pressure water jetting (UHP WJ): above 1700 bar/25.000 psi
*As defined in "Joint Surface Preparation Standard NACE No. 5/SSPC-SP 12, 1995".
Note: Wet abrasive blasting may be performed with low or high pressure fresh water towhich a relative small amount of abrasives is introduced, and in some cases inhibitorsare added to prevent flash rusting (however, as a general rule it is recommended not touse inhibitors when cleaning areas to be immersed during service. Surplus of inhibitorsmay lead to osmotic blistering).
A blast primer is a paint used for short term protection of a newly blast cleaned steelsurface of an assembled structure in order to ease the working procedures. In thiscontext blast primers are often regarded an integral part of the surface preparation.
A holding primer is a paint used to prolong (hold) the protective lifetime of a shopprimertill the specified paint system proper can be applied.
To apply a mist coat or flash coat is a two step application procedure used to minimizepopping when painting on a porous substrate. At first, one or two spray passes areapplied very thin to expel the air from the pores. As soon as this thin coat has flashedoff, the film is built up to the specified film thickness.
A tie coat is a layer of paint which improves the adhesion between coatings of differentgeneric types, eg to "bridge" between conventional and advanced coatings, or betweenepoxy and physically drying paints.
A sealer coat is a layer of paint which is used to seal off (fill the pores of) poroussurfaces such as zinc silicates and empty, insoluble matrix of certain antifoulings. In thisconnection it prevents disturbance of the balance between binder and active pigmentsof the new antifouling. Furthermore, certain paints may be used as sealer coats tominimize popping of the following coat(s) when painting a porous substrate.
When a paint is mentioned to be resistant to spillages and splashes of certainchemicals it is understood to be limited in both area and time. The spilt chemical mustbe removed as soon as possible and not remain on the surface more than 1-2 days.
When stating both metric and US figures the US figures may be rounded off when anexact figure is of less importance.
EXPLANATORY NOTES Page 9A/9
Issued: October 1999
HEMPEL
SURFACE PREPARATION STANDARDSAmong the several existing official and unofficial standards for cleaning of steelpreparatory to painting, one - viz.
The old SWEDISH STANDARDS INSTITUTION:Surface Preparations Standards for Painting Steel Surface (SIS 055900 - 1967) hasgained prominence and acceptance across the frontiers. So much so that it has servedas a model for and has even been adopted direct as national standard in othercountries. Its cleaning degrees Sa 2, Sa 2½, etc. being practically universallyrecognized, they are referred to throughout this book in recommendations for cleaningof steel.
The Swedish Standard, as it was usually called, was first to employ pictorialrepresentations of the specified cleaning degrees. It is now superseded byINTERNATIONAL STANDARD ISO 8501-1:1988. Yet with the same photos as used bythe SIS standard plus additionally four photos (flamecleaning) from the Germanstandard DIN 55928, Part 4, Supplement 4.
Other prominent standards, notably
STEEL STRUCTURES PAINTING COUNCIL (U.S.A.):Surface Preparation Specifications (SSPC-SP 2, 3, 5, 6, 7, and 10)
BRITISH STANDARDS INSTITUTION; Surface Finish of Blast-cleaned steel for Painting:(BS 4232 but now superseded by BS 7079)and DIN 55928, Protection of steel structures from corrosion by organic and metalliccoatings; preparation and testing of surfaces (Germany)
do also concern with the equipment, materials and procedures used to achieve thespecified finish.
The British Standard BS 4232 used drawings to indicate the (Second and Third quality)finishes, whereas the American and the German Standard use the same photos as ISO8501-1:1988. Yet, DIN 55928 includes photos of secondary surface preparation too.
Except for BS 4232 they all take into account the state of the raw steel surface beforecleaning, and grades the result accordingly:
A: Steel surface largely covered with adherent mill scale but little, if any, rust.
B: Steel surface which has begun to rust and from which the mill scale has begun toflake.
C: Steel surface on which the mill scale has rusted away or from which it can be scraped, but with slight pitting visible under normal vision.
D: Steel surface on which the mill scale has rusted away and on which general pitting is visible under normal vision.
A surface preparation method using high pressure water for cleaning is getting morecommon. The best definition of terms and surface preparation standards are presentedby "Joint Surface Preparation Standard NACE No. 5/SSPC-SP 12" from 1995.
For comparison of the standards see the following pages. The text of the individualStandards are quoted literally.
SURFACE PREPARATION STANDARDS Page 1B/7
Issued: March 2002
HEMPEL
ISO 8501-1:1988
Designation Description Sa 3 Blast-cleaning to visually clean steel.
When viewed without magnification, the surface shall be free from visible oil, greaseand dirt, and shall be free from mill scale, rust, paint coatings and foreign matter. Itshall have a uniform metallic colour. See photographs A Sa 3, B Sa 3, C Sa 3 and D Sa3.
Sa 2½ Very thorough blast-cleaning.When viewed without magnification, the surface shall be free from visible oil, greaseand dirt, and from mill scale, rust, paint coatings and foreign matter. Any remainingtraces of contamination shall show only as slight stains in the form of spots or stripes.See photographs A Sa 2½, B Sa 2½, C Sa 2½ and D Sa 2½.
Sa 2 Thorough blast-cleaning.When viewed without magnification, the surface shall be free from visible oil, greaseand dirt, and from most of the mill scale, rust, paint coatings and foreign matter. Anyresidual contamination shall be firmly adhering (see note 2 below). See photographs BSa 2, C Sa 2 and D Sa 2.
Sa 1 Light blast-cleaning.When viewed without magnification, the surface shall be free from visible oil, greaseand dirt, and from poorly adhering mill scale, rust, paint coatings and foreign matter(see note 2). See photographs B Sa 1, C Sa 1 and D Sa 1.
Notes:1. The term "foreign matter" may include water-soluble salts and welding residues.
These contaminants cannot always be completely removed from the surface by dry blast-cleaning, hand and power tool cleaning or flame cleaning; wet blast- cleaning or hydrojetting may be necessary.
2. Mill scale, rust or a paint coating is considered to be poorly adhering if it can be removed by lifting with a blunt putty knife.
St 3 Very thorough hand and power tool cleaning.As for St 2, but the surface shall be treated much more thoroughly to give a metallicsheen arising from the metallic substrate. See photographs B St 3, C St 3 and D St 3.
St 2 Thorough hand and power tool cleaning.When viewed without magnification, the surfaces shall be free from visible oil, greaseand dirt, and from poorly adhering mill scale, rust, paint coatings and foreign matter(see note 2). See photographs B St 2, C St 2 and D St 2.
Notes:1. For descriptions of surface preparation methods by hand and power tool cleaning,
including treatment prior to, and after, the hand and power tool cleaningprocedure, see ISO 8504-3.
2. Preparation grade St 1 is not included as it would correspond to a surface unsuitable for painting.
BS 7079-1990 Replaces BS 4232-1967. BS 7079-1990 is identical to ISO 8501-1: 1988.
SURFACE PREPARATION STANDARDS Page 2B/7
Issued: March 2002
HEMPEL
SSPC
Designation Description
SSPC-SP-5 1.1 A white Metal Blast Cleaned surface, when viewed without magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion products, and other foreign matter.
1.2 ACCEPTABLE VARIATIONS IN APPEARANCE THAT DO NOT AFFECT SURFACE CLEANLINESS as defined in Section 1.1 include variations caused by type of steel, original surface condition, thickness of the steel, weld metal, mill or fabrication marks, heat treating, heat affected zones, blasting abrasive, and differences in the blast pattern.
1.3 When painting is specified, the surface shall be roughened to a degree suitable for the specified paint system.
1.4 Immediately prior to paint application the surface shall comply with the degree of cleaning as specified herein.
1.5 SSPC-Vis 1-89 or other visual standards of surface preparation may be specified to supplement the written definition.
SSPC-SP-10 2.1 A Near-White Blast Cleaned surface, when viewed without magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion
products, and other foreign matter, except for staining as noted in Section 2.2.
2.2 Staining shall be limited to no more than 5 per cent of each square inch of surface area and may consist of light shadows, slight streaks, or minor discolorations caused by stains of rust, stains of mill scale, or stains of previously applied paint.
2.3 ACCEPTABLE VARIATIONS IN APPEARANCE THAT DO NOT AFFECT SURFACE CLEANLINESS as defined in sections 2.1 and 2.2 include variations caused by type of steel, weld metal, mill or fabrication marks, heat treating, heat affected zones, blasting abrasives, and differences in the blast pattern.
2.4 When painting is specified, the surface shall be roughened to a degree suitable for the specified paint system.
2.5 Immediately prior to paint application, the surface shall comply with the degree of cleaning as specified herein.
2.6 SSPC-Vis 1-89 or other visual standards of surface preparation may be specified to supplement the written definition.
SSPC-SP-6 3.1 A Commercial Blast Cleaned surface, when viewed without magnification, shall be free of all visible oil, grease, dirt, dust, mill scale, rust, paint, oxides, corrosion products, and other foreign matter, except for staining, as noted in Section 3.2.
3.2 Staining shall be limited to no more than 33 per cent of each square inch of surface area and may consist of light shadows, slight streaks, or minor discolourations caused by stains of rust, stains of mill scale, or stains of previously applied paint. Slight residues of rust and paint may also be left in the bottoms of pits if the original surface is pitted.
3.3 ACCEPTABLE VARIATIONS IN APPEARANCE THAT DO NOT AFFECT SURFACE CLEANLINESS as defined in Sections 3.1 and 3.2 include variations caused by type of steel, original surface condition, thickness of the steel, weld metal, mill orfabrication marks, heat treating, heat affected zones, blasting abrasive, and differences in the blast pattern.
SURFACE PREPARATION STANDARDS Page 3B/7
Issued: March 2002
HEMPEL
SSPC
Designation Description
SSPC-SP-6, cont. 3.4 When painting is specified, the surface shall be roughened to a degree suitable for the specified paint system.
3.5 Immediately prior to paint application, the surface shall comply with the degree of cleaning as specified herein.
3.6 SSPC-Vis 1-89 or other visual standards of surface preparation may be specified to supplement the written definition.
SSPC-SP-7 4.1 A Brush-Off Blast Cleaned surface, when viewed without magnification, shall be free of all visible oil, grease, dirt, dust, loose mill scale, loose rust, and loose paint. Tightly adherent mill scale, rust, and paint may remain on the surface. Mill scale, rust, and paint are considered tightly adherent if they cannot be removed by lifting with a dull putty knife.
4.2 The entire surface shall be subjected to the abrasive blast. The remaining mill scale, rust, or paint shall be tight.
4.3 When painting is specified, the surface shall be roughened to a degree suitable for the specified paint system.
4.4 Immediately prior to paint application, the surface shall comply with the degree of cleaning as specified herein.
4.5 SSPC-Vis 1-89 or other visual standards of surface preparation may be specified to supplement the written definition.
SSPC-SP-2 5.1 Hand tool cleaning is a method of preparing steel surfaces by the use of non-power hand tools.
5.2 Hand tool cleaning removes all loose mill scale, loose rust, loose paint, and other loose detrimental foreign matter. It is not intended that adherent mill scale, rust, and paint be removed by this process. Mill scale, rust, and paint are considered adherent if they cannot be removed by lifting with a dull putty knife.
5.3 SSPC-Vis 1-89 or other visual standards of surface preparation agreed upon by the contracting parties may be used to further define the surface.
DIN 55928 is not quoted (translated) but is fully in line with ISO 8501-1:1988 (exceptfor the extra standards as mentioned on page 10).
Comparing the standards, no doubt that Sa 3 and SSPC-SP-5 are identical in theirdemands to surface cleanliness. Also Sa 2½ and SSPC-SP-10 seem identical.
Concerning Sa 2 and SSPC-SP-6 these differ slightly, SSPC-SP-6 expressing moredemands to quality. SSPC-SP-6 requires remnants being stains only. Sa 2 states"residual contamination shall be firmly adhering".
Note: For SSPC the written specification takes preference - for ISO 8501-1:1988, thephotos.
SURFACE PREPARATION STANDARDS Page 4B/7
Issued: March 2002
HEMPEL
Joint Surface Preparation Standard NACE No. 5/SSPC-SP 12:
Surface preparation and cleaning of steel and other hard materials by high and ultrahighpressure water jetting prior to paint application.
Water jetting is a relatively new method of surface preparation. The standard deals withthe removal of visible and invisible contamination. After cleaning the surface will still bewet and flash rusting may occur on cleaned steel during the drying period. AdditionalHEMPEL-definitions of flash rust degrees are therefore described below.
Maintenance being the main area of use, any old coating remaining after water jettingmust be well adhering, intact and roughened by the treatment as well as compatible withthe new coating system to be applied.
As a general rule, coatings which are later to be exposed to severe mechanical and/orchemical exposures, like eg specially wear and impact resistent coatings and chemicallyresistent tank coatings, should not be applied to water jetted surfaces. Neither shouldcoatings for which protection relies upon metallic contact to the steel substrate, such aszinc rich primers be applied to water jetted surfaces.
WJ visual preparation grades:
WJ-1 Removal of all previously existing visible rust, coatings, millscale and foreign matters toa uniform matt metal finish.
WJ-2 UHP WJ cleaning to a uniform matt finish with at least 95% of the surface area beingfree of all previously existing visible residues and the remaining 5% only containing randomly dispersed stains of rust, coatings and foreign matters.
WJ-3 HP WJ or UHP WJ to a uniform matt finish with at least two-thirds of the surface beingfree of all visible residues (except millscale) and the remaining one-third only containingrandomly dispersed stains of previously existing rust, coatings and foreign matters.
WJ-4 Uniform removal of all loose rust, millscale and loose coatings.
SC-1 An SC-1 surface is free from all detectable contaminants as determined by usingavailable field test equipment whose sensitivity approximates laboratory equipment.Contaminants relevant in this standard are chlorides, iron-soluble salts and sulphates.
SC-2 An SC-2 surface has less than 7 microgram/cm² chloride contamination, less than 10microgram/cm² of soluble ferrous ions and/or less than 16 microgram/cm² sulphatecontamination as verified by field or laboratory analysis using reliable, reproducible testequipment.
SC-3 An SC-3 surface has less than 50 microgram/cm² chloride and sulphate contaminantsas verified by field or laboratory analysis using reliable, reproducible test equipment.
Definition of flash rust degree (Hempel standard):
Qualitative description
HEMPEL defines:
FR-1 A surface which, after surface preparation, has rusted to form a yellow-brown layer, butin such a small amount that the initial surface condition of the cleaning can just befaintly seen.
The rust may be evenly distributed or it may appear scattered over the surface.Furthermore, the rust layer is well adhering and will not readily come off to leave markson a dry hand, which is swept over the surface with a gentle pressure.
SURFACE PREPARATION STANDARDS Page 5B/7
Issued: March 2002
HEMPEL
FR-2 A surface which has rusted to form a red-brown layer and in an amount that hides theinitial surface condition of the cleaning.
The rust may be evenly distributed or it may appear scattered over the surface. Furthermore, the rust is reasonably well adhering and only minor amounts will come offto leave marks on a dry hand, which is swept over the surface with a gentle pressure.
FR-3 A surface which has rusted to a heavy red-brown layer that covers the surfacecompletely.
The rust is evenly distributed over the surface. Furthermore, the rust is loosely adheringand will easily come off and will leave significant marks on a dry hand, which is sweptover the surface with a gentle pressure.
SURFACE PREPARATION STANDARDS Page 6B/7
Issued: March 2002
HEMPEL
Quantitative description
With the purpose of establishing a reference, HEMPEL has developed a tape test todistinguish between the different flash rust degrees FR-1, FR-2 and FR-3, as definedabove.
Procedure
1. Select a spot on which to perform the test.
2. Attach a piece of tape (as specified in ASTM D 3359) in a length of at least 5 cm(2") and rub thoroughly with a fingertip - not a nail - to make the tape adherefirmly.
3. Peel off the tape and place it on a piece of white paper for reference.
4. Repeat steps 2. and 3. 9 times on exactly the same spot using a new piece oftape each time.
Assessment (after the 10th piece of tape)
The flash rust degree is assessed on the basis of the amount and type of rust presenton the 10th piece of tape and on the appearance of the test-spot relative to that of theadjacent areas.
HEMPEL defines:
FR-1 No rust on the tape.
No or only a slight change of the test-spot.
FR-2 Slight localized red-brown rust on the tape.
A significant change of the test-spot, possibly showing localized areas of black rust.
FR-3 Significant, uniform red-brown rust on the tape, also showing grains of black rust.
A significant change of the test-spot, also showing localized areas of black rust.
SURFACE PREPARATION STANDARDS Page 7B/7
Issued: March 2002
HEMPEL
CONVERSION TABLES
To convert From To Multiply by
Distance: mil micron 25 (25.4 is the correct value,but rounded in this book)
micron mill 0.04 (0.0394 is the correct value,but rounded in this book)
inches centimetre (cm) 2.54centimetre (cm) inches 0.3937feet metre 0.3048metre feet 3.2808yards metre 0.9144metre yards 1.0936nautical mile km 1.853km nautical mile 0.5396
Area: sq.ft. sq. metre (m²) 0.0929sq.metre (m²) sq.ft. 10.764
Volume: US gallon litre 3.785litre US gallon 0.264Imp. gallon litre 4.55litre Imp. gallon 0.22litre cu.ft. 0.0353cu.ft. litre 28.32
Area/Volume: m²/litre sq.ft./US gallon 40.74sq.ft./US gallon m²/litre 0.0245m²/litre sq.ft./Imp. gallon 48.93sq.ft./Imp. gallon m²/liter 0.0204
Weight: lbs kg 0.4536kg lbs 2.2046
Density: kg/litre lbs/US gallon 8.344lbs/US gallon kg/litre 0.1198
V.O.C.: g/litre lbs/US gallon 0.0083
Pressure: atm. bar 1.013atm. kp/cm² 1.033atm. p.s.i. 14.70bar atm. 0.987bar kp/cm² 1.02bar p.s.i. 14.50kp/cm² atm. 0.968kp/cm² bar 0.981kp/cm² p.s.i. 14.22kp/cm² MPa 0.098p.s.i. atm. 0.068p.s.i. bar 0.069p.s.i. kp/cm² 0.07
Notes: • atm. is the so called physical atmosphere (the pressure of 760 mm mercury).The technical atmosphere, at, is identical to kp/cm2.
• 1 bar = 105 Pa (Pascal) = 105 Newton/m².
• MPa = MegaPascal = 106 Pascal = MegaNewton/m².
• The so-called kilogram forces/cm² is considered equal to Kp/cm².
CONVERSION TABLES Page 1D/5
Issued: October 1999
HEMPEL
To convert From To Calculate
Temperature: Celcius Fahrenheit (9/5 x °C) + 32Fahrenheit Celcius 5/9 x (°F - 32)
Film thickness: Wet Drywft x VS%
100(micron)
Dry Wetdft x 100
VS%
wft = wet film thickness, dft = dry film thickness, VS% = Volume Solids
CALCULATION OF
Theoretical Spreading Rate (on completely smooth surface)
In m² per litre In sq.ft. per US gallon= VS% x 10desired dft (micron) = VS% x 16.04
desired dft (mil)
Theoretical Paint Consumption (on completely smooth surface)
In litre =area (m2) x desired dft (micron)
VS% x 10
In US gallon =area (sq.ft.) x desired dft (mil)
VS% x 16.04
Practical consumption:
The practical consumption is influenced by i) simple losses, by ii) additional consumption to fill up the "dead volume" ofthe surface roughness, but especially iii) by the "waviness" of the paint surface. However, the term "loss factor" is stillused in parallel with the term "consumption factor" to describe a relationship between the theoretical, calculatedconsumption and a practical either observed de-factor consumption or an "aimed at" consumption.
Practical consumption =area x consumption factortheoretical spreading rate
However, as
Consumption factor = (z = "loss" = simple loss + dead volume loss + waviness loss)100
100 z%
and
theoretical spreading rate =VS% x 10
DFT
the practical consumption could be written as
10 x DFT x areaVS% x (100-z%)
where it is very important to use the "loss"for z and not the consumption factor.
CONVERSION TABLES Page 2D/5
Issued: October 1999
HEMPEL
FORMULAS FOR ESTIMATINGSURFACE AREAS OF SHIPS
Bottom (incl. boottop): A = ((2 x d) + B) x Lpp x P
where d = draught maximum (as per Lloyd’s)B = breadth extreme (as per Lloyd’s)Lpp = length betw. perpendiculars (as per Lloyd’s)
P = 0.90 for big tankers, 0.85 for bulk carriers, 0.70-0.75 for dry cargo liners
or
A = Lpp x (Bm + 2 x D) x V
Bm x Lpp x D
where D = mean draft at paint line (m)Bm = breath moulded (m)Lpp = length between perpendicularsV = displacement (cubic metre) corresponding to the draft
Boottop: A = 2 x h x (Lpp + 0.5 x B)
where h = width of boottop (to be informed by owner)Lpp = length betw. perpendiculars (as per Lloyd’s)B = breadth extreme (as per Lloyd’s)
Topsides: A = 2 x H x (Loa + 0.5 x B)
where H = height of topsides (depth - draught) (as per Lloyd’s)Loa = length over all (as per Lloyd’s)B = breadth extreme (as per Lloyd’s)
Weather Decks incl. upper A = Loa x B x Ndecks on superstructure,foundation, hatches and where Loa = length over all (as per Lloyd’s)top of deck houses: B = breadth extreme (as per Lloyd’s)
N = 0.91 for big tankers and bulk carriers,0.88 for cargo liners, 0.84 for coasters, etc.
(accuracy depends on your choice of N which indicatesthe actual area in relation to its circumscribed rectangular)
CONVERSION TABLES Page 3D/5
Issued: October 1999
HEMPEL
ESTIMATING SIZE OF SURFACES:
15.915.014.113.412.712.111.611.110.610.29.89.49.18.88.5
161718192021222324252627282930
254.5127.284.863.650.942.436.431.828.325.423.121.219.618.217.0
123456789
101112131415
sq.m/ton
Plate thicknessmm
sq.m/ton
Plate thicknessmm
Plates:
The indicated values are for both sides. If one side only, reduce by half.
Pipes: Exterior area (sq.m/m):
pi x eD
pi = 3.14
eD = exterior diameter in metresiD
Interior area (sq.m/m):
eD pi x iD
pi = 3.14iD = interior diameter in metres
CONVERSION TABLES Page 4D/5
Issued: October 1999
HEMPEL
ESTIMATING SIZE OF SURFACES - BEAMS AND PROFILES, examples:
Disignation/ Size Weight Surface areashape kg/m sq.m/m sq.m/ton
HEB 100 20.4 0.57 27.8160 42.6 0.92 21.5220 71.5 1.27 17.8280 103.0 1.62 15.7360 142.0 1.85 13.0600 212.0 2.32 10.9
INP 80 5.94 0.30 51.2140 14.3 0.50 35.1200 26.2 0.71 27.1260 41.9 0.91 21.6340 68.0 1.15 16.9400 92.4 1.33 14.4
RHS 20x20 1.1 0.08 70.830x30 1.8 0.12 68.640x40 2.4 0.16 67.260x60 3.6 0.24 66.080x80 7.3 0.32 44.1
UNP 30 4.3 0.17 40.750 5.6 0.23 41.580 8.6 0.31 36.1
180 22.0 0.61 27.8280 41.8 0.89 21.3400 71.8 1.18 16.4
20x3 0.88 0.08 87.525x4 1.5 0.10 66.930x4 1.8 0.12 65.240x4 2.4 0.16 64.150x6 4.5 0.19 43.450x9 6.5 0.19 30.075x7 7.9 0.29 36.7
75x10 11.1 0.29 26.2100x10 15.1 0.39 25.8100x16 23.2 0.39 16.8150x15 33.8 0.59 17.3
In the case of the HEB beam, the first illustration, height and breadth are equal up to the size of 280. The "size" is theheight and equal to the profile number.
In the case of the INP beam, the "size" is the height and equal to the profile number.
In the case of the UNP beam, the "size" is the height and equal to the profile number.
In the case of the v-profile, the two flanges are reckoned equal, the second digit being the thickness of the steel.
CONVERSION TABLES Page 5D/5
Issued: October 1999
HEMPEL
KEY TO OFFICIAL AND SEMI-OFFICIAL CERTIFICATES, APPROVALS, ETC.,OF HEMPEL GROUP RECOMMENDED PRODUCTS AND SYSTEMS
Related to type of certificate
A. LOW FLAME SPREAD (SOLAS) / OTHER FIRE TESTS
A-3 SEE-BERUFGENOSSENSCHAFT, Hamburg, Germany(Conforms to the SOLAS Convention MSC 61 (67) and EU Directive 96/98/EC)
10220 - HEMPINOL 10220
12050 - HEMPALIN PRIMER 12050
13140 - HEMPEL’S UNI-PRIMER 13140
13200 - HEMPALIN PRIMER HI-BUILD 13200
15570 - HEMPADUR 15570
35490/ - HEMPADUR SPRAYGUARD 35490/3549335493
42460 - HEMPALIN UNDERCOAT 42460
45880 - HEMPADUR MASTIC 45880
51570 - HEMPEL'S SILVIUM 51570
52140 - HEMPALIN ENAMEL 52140
52220 - HEMPALIN ENAMEL HI-BUILD 52220
52360 - HEMPALIN DANREX 52360
53240 - HEMPALIN DECKPAINT 53240
55210 - HEMPATHANE TOPCOAT 55210
A-9 BUREAU VERITAS, France
12050 - HEMPALIN PRIMER 12050/HEMPALIN ENAMEL 52140
12050 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
12050 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
13140 - HEMPEL’S UNI-PRIMER 13140
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
15570 - HEMPADUR 15570
42460 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
45880 - HEMPADUR MASTIC 45880
52140 - HEMPALIN PRIMER 12050/HEMPALIN ENAMEL 52140
52140 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
52220 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
CERTIFICATES & APPROVALS (by type) Page 1/12
Issued: October 2001
HEMPEL
53240 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
53240 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
A-13 LONDON UNDERGROUND LIMITED, Great Britain
18030 - HEMUCRYL PRIMER HI-BUILD 1803/HEMUCRYL ENAMEL HI-BUILD 5803
58030 - HEMUCRUL PRIMER HI-BUILD 1803/HEMUCRYL ENAMEL HI-BUILD 5803
A-17 REGISTRO ITALIANO NAVALE (R.I.N.A.), Genoa, Italy(Conforms to the SOLAS Convention MSC 61 (67))
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
42460 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
45150 - HEMPADUR 45150
45150 - HEMPADUR 45150/HEMPATHANE TOPCOAT 55210
52140 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN UNDERCOAT 42460/HEMPALINE NAMEL 52140
55210 - HEMPADUR 45150/HEMPATHANE TOPCOAT 55210
A-20 DET NORSKE VERITAS, Denmark
10220 - HEMPINOL 10220
12050 - HEMPALIN PRIMER 12050/HEMPALIN ENAMEL 52140
12050 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
12050 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
15570 - HEMPADUR 15570
18030 - HEMUCRYL PRIMER HI-BUILD 18030/HEMUCRYL ENAMEL HI-BUILD 58030
42460 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
45880 - HEMPADUR MASTIC 45880
52140 - HEMPALIN PRIMER 12050/HEMPALIN ENAMEL 52140
52140 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
52220 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
53240 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
53240 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
58030 - HEMUCRUL PRIMER HI-BUILD 18030/HEMUCRYL ENAMEL HI-BUILD 58030
CERTIFICATES & APPROVALS (by type) Page 2/12
Issued: October 2001
HEMPEL
A-22 LLOYD’S REGISTER OF SHIPPING, Great Britain
52220 - HEMPALIN ENAMEL HI-BUILD 52220
A-24 DET NORSKE VERITAS, China
12050 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
12050 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
42460 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
52140 - HEMPALIN PRIMER 12050/HEMPALIN UNDERCOAT 42460/HEMPALIN ENAMEL 52140
52220 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
53240 - HEMPALIN PRIMER 12050/HEMPALIN DECKPAINT 53240
B. WELDING PRIMERS
B-1 LLOYD'S REGISTER OF SHIPPING, Great Britain
15280 - HEMPEL'S SHOPPRIMER E 1528
15300 - HEMPADUR PRIMER 1530
15360 - HEMPADUR ZINC 15360
15890 - HEMPEL'S SHOPPRIMER ZS 15890
B-2 DET NORSKE VERITAS, Norway
15280 - HEMPEL'S SHOPPRIMER E 1528 (only produced in DK)
15890 - HEMPEL'S SHOPPRIMER ZS 15890
B-3 GERMANISCHER Lloyd, Germany
15280 - HEMPEL'S SHOPPRIMER E 1528
15890 - HEMPEL'S SHOPPRIMER ZS 15890
B-5 AMERICAN BUREAU OF SHIPPING, USA
15890 - HEMPEL'S SHOPPRIMER ZS 1589
B-8 KOREAN REGISTER OF SHIPPING, Korea
15890 - HEMPEL'S SHOPPRIMER ZS 1589
B-9 BUREAU VERITAS, France
15890 - HEMPEL'S SHOPPRIMER ZS 1589
B-10 CHINA CLASSIFICATION SOCIETY, China
CERTIFICATES & APPROVALS (by type) Page 3/12
Issued: October 2001
HEMPEL
15280 - HEMPEL'S SHOPPRIMER E 15280
B-11 REGISTRO ITALIANO NAVALE (R.I.N.A.), Genoa, Italy
15890 . HEMPEL'S SHOPPRIMER ZS 15890
C. NON-TOXICITY OF WELDING FUMES
C-2 THE DANISH WELDING INSTITUTE, Denmark(Test reports)
15280 - HEMPEL'S SHOPPRIMER E 1528
15400 - HEMPADUR 1540
15890 - HEMPEL'S SHOPPRIMER ZS 1589
C-3 SCHWEISSTECHNISCHE LEHR- UND VERSUCHSANSTALT, Duisburg, Germany(Test reports)
15280 - HEMPEL'S SHOPPRIMER E 1528
15890 - HEMPEL'S SHOPPRIMER ZS 1589
D. NON-CONTAMINATION OF GRAIN CARGOES
D-1 NEWCASTLE OCCUPATIONAL HEALTH, Great Britain
13624 - HEMPAQUICK PRIMER 1362
15030 - HEMPADUR LTC 1503
15130 - HEMPADUR 1513
15400 - HEMPADUR 1540
15570 - HEMPADUR 1557
17630 - HEMPADUR 17630
35530 - HEMPADUR MULTI-STRENGTH 3553
45141/ - HEMPADUR 45141/HEMPADUR 4514345143
45150 - HEMPADUR 4515
45200 - HEMPADUR HI-BUILD 4520
45742 - HEMPADUR MULTI-STRENGTH 4574
45751 - HEMPADUR MULTI-STRENGTH 4575
45880/ - HEMPADUR MASTIC 458845881
46410 - HEMPATEX HI-BUILD 46410
52360 - HEMPALIN DANREX 5236
55210 - HEMPATHANE TOPCOAT 5521
CERTIFICATES & APPROVALS (by type) Page 4/12
Issued: October 2001
HEMPEL
56360 - HEMPATEX ENAMEL 5636
D-3 FOOD AND DRUG ADMINISTRATION, Washington, USA
15360 - HEMPADUR ZINC 15360
15400 - HEMPADUR 1540
15500 - HEMPADUR 15500
15700 - HEMPEL'S GALVOSIL 1570
17630 - HEMPADUR 17630
45141/ - HEMPADUR 45141/4514345143
45200 - HEMPADUR HI-BUILD 4520
45880/ - HEMPADUR MASTIC 45880/4588145881
51570 - HEMPEL'S SILVIUM 51570
52140 - HEMPALIN ENAMEL 52140 (white only)
52360 - HEMPALIN DANREX 52360
85671 - HEMPADUR 85671
D-5 CHINA CLASSIFICATION SOCIETY, China
15400 - HEMPADUR 15400
35530 - HEMPADUR MULTI-STRENGTH 35530
45200 - HEMPADUR HI-BUILD 45200
52360 - HEMPALIN DANREX 52360
E. CORROSION CONTROL
E-1 LLOYD'S REGISTER OF SHIPPING, London, Great Britain
CODE:Suitable for:B: Ballast waterRS: Refined spiritsC: Crude oilV: Void spaces
E-1.1 Recognised Corrosion Control Coatings
15030 - HEMPADUR LTC 1503 (B)
15130 - HEMPADUR 1513 (B & C)
15400 - HEMPADUR 1540 (B, RS & C)
15500 - HEMPADUR 15500
15700 - HEMPEL'S GALVOSIL 1570 (B, RS, C & V)
CERTIFICATES & APPROVALS (by type) Page 5/12
Issued: October 2001
HEMPEL
45141/ - HEMPADUR 4514 (B, RS & C)45143
45751 - HEMPADUR MULTI-STRENGTH 4575 (B)
E-1.2 Provisionally Recognized Corrosion Control Coatings
17630/ - HEMPADUR 1763 (B)17633
E-1.3 Low friction surface coating (applied to main ice belt) shell plating reduction of 1 mm
45751 - HEMPADUR MULTI-STRENGTH 45751
E-1.4 Recognized Ballast Tank Maintenance Coating
10880 - HEMPEL’S BALLAST COAT SH 10880
E-6 CHINA CLASSIFICATION SOCIETY, China
15300 - HEMPADUR PRIMER 15300
15360 - HEMPADUR ZINC 15360
E-8 MARITIME REGISTER OF SHIPPING, Russia
15030 - HEMPADUR LTC 1503
15130 - HEMPADUR 1513
15500 - HEMPADUR 1550
15700 - HEMPEL'S GALVOSIL 1570
17630 - HEMPADUR 1763
45143 - HEMPADUR 45143
45742 - HEMPADUR MULTI-STRENGTH 45742
E-9 GERMANISCHER LLOYD, Germany
CODE:Suitable for:B: Ballast waterN/B: NewbuildingMT: Maintenance
15030 - HEMPADUR LTC 15030 (B, N/B & MT)
15130 - HEMPADUR 15130 (B, N/B & MT)
15570 - HEMPADUR 15570 (B, N/B)
17630/ - HEMPADUR 17630/17633 (B, N/B & MT)17633
45141/ - HEMPADUR 45141/45143 (B, MT)45143
45150 - HEMPADUR 45150 (B, MT)
CERTIFICATES & APPROVALS (by type) Page 6/12
Issued: October 2001
HEMPEL
45742 - HEMPADUR MULTI-STRENGTH 45742 (B, N/B)
45751 - HEMPADUR MULTI-STRENGTH 45751 (B, N/B)
G. TANKS FOR SHIPPING OILS AND FATS
G-2 SCIENTIFIC & TECHNICAL SERVICES LTD., Great Britain(According to FDA Section 175.300)
15700 - HEMPEL'S GALVOSIL 15700
I. POTABLE WATER TANKS (PIPE LINES INTERNAL)
I-3 MINISTRY OF PUBLIC WORKS, State of Kuwait
15400 - HEMPADUR 1540
I-4 STATENS INSTITUT FOR FOLKEHELSE, Norway
15400 - HEMPADUR 1540
I-9 WATER RESEARCH CENTRE, Great Britain
35530 - HEMPADUR MULTI-STRENGTH 35530
85671 - HEMPADUR 85671
I-13 MINISTRY OF ELECTRICITY AND WATER, Kuwait
15400 - HEMPADUR 1540
I-15 MINISTRY OF HEALTH OF THE CZECH REPUBLIC, the Czech Republic
35530 - HEMPADUR MULTI-STRENGTH 3553
I-16 FOOD & ENVIRONMENT CONTROL CENTRE, Abu Dhabi, UAE
35530 - HEMPADUR MULTI-STRENGTH 3553
I-17 CHINA CLASSIFICATION SOCIETY, China
15400 - HEMPADUR 15400
35530 - HEMPADUR MULTI-STRENGTH 35530
I-18 LANDESHYGIENEINSTITUT GREIFSWALD, Germany
35530 - HEMPADUR MULTI-STRENGTH 3553
I-19 FOOD AND DRUG ADMINISTRATION, Washington, USA
15400 - HEMPADUR 1540
CERTIFICATES & APPROVALS (by type) Page 7/12
Issued: October 2001
HEMPEL
I-23 CAMERA DI COMMERCIO INDUSTRIA ARTIGIANATO E AGRICOLTURA, Trieste, Italy
15500 - HEMPADUR 15500 (incl. ethanol, olive oil and wine)
35530 - HEMPADUR MULTI-STRENGTH 35530 (incl. ethanol)
45150 - HEMPADUR 45150 (incl. ethanol)
45200 - HEMPADUR HI-BUILD 45200
I-24 STATE COMMITTEE OF SANITARY-EPIDEMIOLOGICAL INSPECTION OF RUSSIAN FEDERATION, Russia
15500 - HEMPADUR 1550
K. AVIATION FUEL K-1 Air BP, Great Britain
15400 - HEMPADUR 1540
K-2 BP ARABIEN AGENCIES, Dubai, U.A.E.
15400 - HEMPADUR 1540
K-4 SHELL INTERNATIONAL TRADING COMPANY, London, Great Britain
15400 - HEMPADUR 1540
N. CARRIAGE OF FOODSTUFFS
N-1 FOOD AND DRUG ADMINISTRATION, Washington D.C., USA"dry foodstuffs" according to Section 175.300 (refer to D-3)
05150 - HEMPADUR VARNISH 05150
15360 - HEMPADUR ZINC 15360
15400 - HEMPADUR 15400
15500 - HEMPADUR 15500
15700 - HEMPEL'S GALVOSIL 15700
17630 - HEMPADUR 17630
45141/ - HEMPADUR 45141/4514345143
45200 - HEMPADUR HI-BUILD 4520
45221 - HEMPADUR HI-BUILD 45221
45880/ - HEMPADUR MASTIC 45880/4588145881
52140 - HEMPALIN ENAMEL 52140 (white only)
52360 - HEMPALIN DANREX 52360
85671 - HEMPADUR 85671
CERTIFICATES & APPROVALS (by type) Page 8/12
Issued: October 2001
HEMPEL
N-2 CASE CONSULTING LABORATORIES, USA
15400 - HEMPADUR 1540
N-5 CSIRO FOOD RESEARCH LABORATORY, New South Wales, Australia
46410 - HEMPATEX HI-BUILD 4641 (dry foodstuff)
N-6 CHINA CLASSIFICATION SOCIETY, China
45200 - HEMPADUR HI-BUILD 4520
P. ACIDS AND SEWAGE WATER
P-1 MINISTRY OF PUBLIC WORKS, Kuwait
15400 - HEMPADUR 1540
S. SLIP COEFFICIENT
S-1 CORROSION CONTROL CONSULTANTS AND LABS, USA
15700 - HEMPEL'S GALVOSIL 1570
15780 - HEMPEL'S GALVOSIL 1578
S-2 FORSCHUNGS- UND MATERIALPRÜFUNGSANSTALT, Baden-Wüttemberg, Otto Graf-Institut, Germany(Test reports)
15700 - HEMPEL'S GALVOSIL 1570
V. QUALITY ASSURANCE SYSTEM
V-1 SSAB, Sweden
15280 - HEMPEL'S SHOPPRIMER E 15280
15890 - HEMPEL'S SHOPPRIMER ZS 15890
X. MISCELLANEOUS
X-1 CROATIAN REGISTER OF SHIPPING, Split, Croatia
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
13200 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
15130 - HEMPADUR 15130
15400 - HEMPADUR 15400
52220 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN ENAMEL HI-BUILD 52220
53240 - HEMPALIN PRIMER HI-BUILD 13200/HEMPALIN DECKPAINT 53240
CERTIFICATES & APPROVALS (by type) Page 9/12
Issued: October 2001
HEMPEL
X-3 DEPARTMENT OF HOUSING AND CONSTRUCTION, Melbourne, Australia
46370 - HEMPATEX HI-BUILD 4637
X-4 STATE COMMITTEE OF SANITARY- EPIDEMIOLOGICAL INSPECTION OF RUSSIAN FEDERATION, Russia
02220 - HEMPEL'S MARINE VARNISH 0222
05970 - HEMPADUR SEALER 05970
12050 - HEMPALIN PRIMER 12050
15030 - HEMPADUR LTC 15030
15130 - HEMPADUR 15130
15280 - HEMPEL'S SHOPPRIMER E 15280
15360 - HEMPADUR ZINC 15360
15500 - HEMPADUR 15500
15560 - HEMPADUR 15560
15570 - HEMPADUR 15570
15700 - HEMPEL'S GALVOSIL 15700
15890 - HEMPEL'S SHOPPRIMER ZS 15890
17360 - HEMPADUR ZINC 17360
17630 - HEMPADUR 17630
35250 - HEMPADUR FILLER 35250
35530 - HEMPADUR MULTI-STRENGTH 3553
42460 - HEMPALIN UNDERCOAT 42460
45141/ - HEMPADUR 45141/4514345143
45150 - HEMPADUR 45150
45182 - HEMPADUR 45182
45200 - HEMPADUR HI-BUILD 45200
45742 - HEMPADUR MULTI-STRENGTH 45742
45880 - HEMPADUR MASTIC 45880
46330 - HEMPATEX HI-BUILD 46330
46410 - HEMPATEX HI-BUILD 46410
52140 - HEMPALIN ENAMEL 52140
52360 - HEMPALIN DANREX 52360
53240 - HEMPALIN DECKPAINT 53240
55100 - HEMPATHANE ENAMEL 55100
55210 - HEMPATHANE TOPCOAT 55210
CERTIFICATES & APPROVALS (by type) Page 10/12
Issued: October 2001
HEMPEL
56360 - HEMPATEX ENAMEL 56360
74030 - HEMPEL’S ANTIFOULING ECONOMIC SP-SEA 74030
79051 - HEMPEL'S A/F NAUTIC SP-ACE 79051
79070 - HEMPEL'S ANTIFOULING NAUTIC SP-ACE 79070
85671 . HEMPADUR 85671
X-6 DEPARTMENT OF TRANSPORT, Australia
35490/ - HEMPADUR SPRAY-GUARD 354935493
X-11 CENTRALNONA. ISLJEDOVATELJSKI PROJ. INSTITUT MORSKE FLOTE (CNIIMF), Russia
13200 - HEMPALIN PRIMER HI-BUILD 1320
15030 - HEMPADUR LTC 1503
15130 - HEMPADUR 1513
15300 - HEMPADUR PRIMER 1530
15360 - HEMPADUR ZINC 1536
15400 - HEMPADUR 1540
15570 - HEMPADUR 1557
15590 - HEMPADUR 1559
15700 - HEMPEL'S GALVOSIL 1570
35530 - HEMPADUR MULTI-STRENGTH 3553
45141/ - HEMPADUR 451445143
45150 - HEMPADUR 4515
45200 - HEMPADUR HI-BUILD 4520
46330 - HEMPATEX HI-BUILD 4633
52140 - HEMPALIN ENAMEL 5214
52220 - HEMPALIN ENAMEL HI-BUILD 5222
52360 - HEMPALIN DANREX 5236
53240 - HEMPALIN DECKPAINT 5324
56360 - HEMPATEX ENAMEL 5636
X-15 MINISTRY OF MUNICIPAL AFFAIRS & AGRICULTURE, State of Qatar
15360 - HEMPADUR ZINC 15360
45150 - HEMPADUR 4515
CERTIFICATES & APPROVALS (by type) Page 11/12
Issued: October 2001
HEMPEL
X-16 DEUTSCHE BAHN, Germany
13200 - HEMPALIN PRIMER 1320
X-17 CHINA CLASSIFICATION SOCIETY, China
46370 - HEMPATEX HI-BUILD 46370
X-18 DET NORSKE VERITAS, Singapore(Qualification test)
35920 - HEMPEL'S POLYESTER GF 3592
Certificates approved with four-digit quality numbers have been listed with only 4 digits.
CERTIFICATES & APPROVALS (by type) Page 12/12
Issued: October 2001
HEMPEL
KEY TO OFFICIAL AND SEMI-OFFICIAL CERTIFICATES, APPROVALS, ETC.,OF HEMPEL GROUP RECOMMENDED PRODUCTS AND SYSTEMS
Related to product number
* HEMPEL'S MARINE VARNISH 02220 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspectionf of Russian Federation, Russia (X-4)
* HEMPADUR VARNISH 05150 * CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* HEMPADUR SEALER 05970 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspectionf of Russian Federation, Russia (X-4)
* HEMPINOL 10220 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)Det Norske Veritas, Denmark (A-20)
* HEMPEL’S BALLAST COAT SH 10880 * CORROSION CONTROL
Recognized Ballast Tank Maintenance Coating (E-1.4)
* HEMPALIN PRIMER 12050 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection of RussianFederation, Russia (X-4)
* HEMPALIN PRIMER 12050 * LOW FLAME SPREADHEMPALIN ENAMEL 52140
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)
* HEMPALIN PRIMER 12050 * LOW FLAME SPREADHEMPALIN DECKPAINT 53240
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
CERTIFICATES & APPROVALS (by product) Page 1/14
Issued: October 2001
HEMPEL
* HEMPALIN PRIMER 12050 * LOW FLAME SPREADHEMPALIN UNDERCOAT 42460HEMPALIN ENAMEL 52140 Bureau Veritas, France (A-9)
Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
* HEMPEL’S UNI-PRIMER 13140 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)Bureau Veritas, France (A-9)
* HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUS
Centralnona. Isljedovateljski Proj. Institut Morske Flote (CNIIMF),Russia (X-11)Deutsche Bahn, Germany (X-16)
* HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREADHEMPALIN UNDERCOAT 42460HEMPALIN ENAMEL 52140 Registro Italiano Navale - RINA, Italy (A-17)
* HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREADHEMPALIN HOLD PAINT 52220
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
* MISCELLANEOUS
Croatian Register of Shipping, Croatia (X-1)
* HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREADHEMPALIN DECKPAINT 53240
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)
* MISCELLANEOUS
Croatian Register of Shipping, Croatia (X-1)
* HEMPAQUICK PRIMER 13624 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
* HEMPADUR LTC 15030 * NON-CONTAMINATION OF GRAIN CARGOEScont. page 3
Newcastle Occupational Health, Great Britain (D-1)
CERTIFICATES & APPROVALS (by product) Page 2/14
Issued: October 2001
HEMPEL
* HEMPADUR LTC 15030 * CORROSION CONTROLcont.
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)Maritime Register of Shipping, Russia (E-8)Germanischer Lloyd, Germany (E-9)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection of Russian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPADUR 15130 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)Maritime Register of Shipping, Russia (E-8)Germanischer Lloyd, Germany (E-9)
* MISCELLANEOUS
Croatian Register of Shipping, Croatia (X-1)State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPEL’S SHOPPRIMER E 15280 * WELDING PRIMERS
Lloyd's Register of Shipping, Great Britain (B-1)Det Norske Veritas, Norway (B-2)Germanischer Lloyd, Germany (B-3)China Classification Society, China (B-10)
* QUALITY ASSURANCE SYSTEM
SSAB, Sweden (V-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection of Russian Federation, Russia (X-4)
* HEMPADUR PRIMER 15300 * WELDING PRIMERS
Lloyd's Register of Shipping, Great Britain (B-1)
* CORROSION CONTROL
China Classification Society, China (E-6)
* MISCELLANEOUS
Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
CERTIFICATES & APPROVALS (by product) Page 3/14
Issued: October 2001
HEMPEL
* HEMPADUR ZINC 15360 * WELDING PRIMERS
Lloyd's Register of Shipping, Great Britain (B-1)
* NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3)
* CORROSION CONTROL
China Classification Society, China (E-6)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection of Russian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)Ministry of Municipal Affairs & Agriculture, Qatar (X-15)
* HEMPADUR 15400 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)China Classification Society, China (D-5)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)
* POTABLE WATER TANKS (PIPE LINES INTERNAL)
Ministry of Public Works, Kuwait (I-3)Statens Institut for Folkehelse, Norway (I-4)Ministry of Electricity and Water, Kuwait (I-13)China Classification Society, China (I-17)Food and Drug Administration, USA (I-19)
* AVIATION FUEL
Air BP, Great Britain (K-1)BP Arabian Agencies, Dubai, UAE (K-2)Shell International Trading Company, Great Britain (K-4)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)Case Consulting Laboratories, USA (N-2)
* ACIDS AND SEWAGE WATER
Ministry of Public Works, Kuwait (P-1)
* MISCELLANEOUS
Croatian Register of Shipping, Croatia (X-1)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
CERTIFICATES & APPROVALS (by product) Page 4/14
Issued: October 2001
HEMPEL
* HEMPADUR 15500 * NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)Maritime Register of Shipping, Russia (E-8)
* POTABLE WATER TANKS (PIPE LINES INTERNAL)
Camera Di Commercio Industria Artigianato E Agricoltura, Italy (I-23)State Committee of Sanitary-Epidemiological Inspection of Russian Federation, Russia (I-24)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR FAST DRY 15560 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR 15570 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)
* NON-CONTAMINATION OF GRAIN CARGOE
Newcastle Occupational Health, Great Britain (D-1)
* CORROSION CONTROL
Germanischer Lloyd, Germany (E-9)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPADUR 15590 * MISCELLANEOUS
Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
CERTIFICATES & APPROVALS (by product) Page 5/14
Issued: October 2001
HEMPEL
* HEMPEL'S GALVOSIL 15700 * NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)Maritime Register of Shipping, Russia (E-8)
* TANKS FOR SHIPPING OILS AND FATS
Scientific & Technical Services Ltd., Great Britain (G-2)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* SLIP COEFFICIENT
Corrosion Control Consultants and Labs, USA (S-1)Forschungs- und materialprüfungsanstalt, Otto Graf-Institut, Germany (S-2)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPEL'S GALVOSIL 15780 * SLIP COEFFICIENT
Corrosion Control Consultants and Labs, USA (S-1)
* HEMPEL'S SHOPPRIMER ZS 15890 * WELDING PRIMERS
Lloyd's Register of Shipping, Great Britain (B-1)Det Norske Veritas, Norway (B-2)Germanischer Lloyd, Germany (B-3)American Bureau of Shipping, USA (B-5)Korean Register of Shipping, Korea (B-8)Bureau Veritas, France (B-9)Registro Italiano Navale - RINA, Italy (B-11)
* QUALITY ASSURANCE
SSAB, Sweden (V-1)
* HEMPEL'S SHOPPRIMER ZS 15890 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR ZINC 17360 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
CERTIFICATES & APPROVALS (by product) Page 6/14
Issued: October 2001
HEMPEL
* HEMPADUR 17630 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain (Provisionally Recognized Corrosion Control Coatings) (E-1.2)Maritime Register of Shipping, Russia (E-8)Germanischer Lloyd, Germany (E-9)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMUCRYL PRIMER HI-BUILD 18030 * LOW FLAME SPREADHEMUCRYL ENAMEL HI-BUILD 58030
London Underground Limited, Great Britain (A-13)Det Norske Veritas, Denmark (A-20)
* HEMPADUR FILLER 35250 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR SPRAY-GUARD 35490/35493 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUS
Marine Safety Agency, Australia (X-6)
* HEMPADUR MULTI-STRENGTH 35530 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)China Classification Society, China (D-5)
* POTABLE WATER TANKS (PIPE LINES INTERNAL)
Water Research Centre, Great Britain (I-9)Ministry of Health of the Czech Republic, The Czech Republic (I-15)Food and Environment Control Centre, UAE (I-16)China Classification Society, China (I-17)Hygiene-Institut Greifswald, Germany (I-18)Camera Di Commercio Industria Artigianato E Agricoltura, Italy (I-23)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Ministry of Health of the Czech Republic, The Czech Republic (X-11)
CERTIFICATES & APPROVALS (by product) Page 7/14
Issued: October 2001
HEMPEL
* HEMPEL'S POLYESTER GF 35920/35923 * MISCELLANEOUS
Det Norske Veritas, Singapore (X-18)
* HEMPALIN UNDERCOAT 42460 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
HEMPALIN PRIMER 12050 * LOW FLAME SPREAD* HEMPALIN UNDERCOAT 42460
HEMPALIN ENAMEL 52140 Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREAD* HEMPALIN UNDERCOAT 42460
HEMPALIN ENAMEL 52140 Registro Italiano Navale - RINA, Italy (A-17)
* HEMPADUR 45141/45143 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain(Recognized Corrosion Control Coatings) (E-1.1)Maritime Register of Shipping, Russia (E-8)Germanischer Lloyd, Germany (E-9)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPADUR 45150 * LOW FLAME SPREADcont. page 9
Registro Italiano Navale - RINA, Italy (A-17)
* NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
CERTIFICATES & APPROVALS (by product) Page 8/14
Issued: October 2001
HEMPEL
* HEMPADUR 45150 * CORROSION CONTROLcont.
Germanischer Lloyd, Germany (E-9)
* POTABLE WATER TANKS (PIPE LINES INTERNAL)
Camera Di Commercio Industria Argigianato E Agricoltura, Italy (I-23)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)Ministry of Municipal Affairs & Agriculture, Qatar (X-15)
* HEMPADUR 45150 * LOW FLAME SPREADHEMPATHANE TOPCOAT 55210
Registro Italiano Navale - RINA, Italy (A-17)
* HEMPADUR 45182 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR HI-BUILD 45200 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)China Classification Society, China (D-5)
* POTABLE WATER TANKS (PIPELINES INTERNAL)
Camera Di Commercio Industria Argigianato E Agricoltura, Italy (I-23)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)China Classification Society, China (N-6)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPADUR HI-BUILD 45221 * CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* HEMPADUR MULTI-STRENGTH 45742 * NON-CONTAMINATION OF GRAIN CARGOEScont. page 10
Newcastle Occupational Health, Great Britain (D-1)
* CORROSION CONTROL
Maritime Register of Shipping, Russia (E-8)Germanischer Lloyd, Germany (E-9)
CERTIFICATES & APPROVALS (by product) Page 9/14
Issued: October 2001
HEMPEL
* HEMPADUR MULTI-STRENGTH 45742 * MISCELLANEOUScont.
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPADUR MULTI-STRENGTH 45751 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
* CORROSION CONTROL
Lloyd's Register of Shipping, Great Britain (Recognized Corrosion Control Coatings) (E-1.1)Lloyd's Register of Shipping, Great Britain (low friction surface coating (applied in main ice belt) shell plating reduction of 1 mm (E-1.3)Germanischer Lloyd, Germany (E-9)
* HEMPADUR MASTIC 45880/45881 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)
* NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPATEX HI-BUILD 46330 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPATEX HI-BUILD 46370 * MISCELLANEOUS
Department of Housing and Construction, Australia (X-3)Department Morskog Transporta, Russia (X-7)China Classification Society, China (X-17)
* HEMPATEX HI-BUILD 46410 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
CERTIFICATES & APPROVALS (by product) Page 10/14
Issued: October 2001
HEMPEL
* CARRIAGE OF FOODSTUFFS
CSIRO Food Research Laboratory, Australia (N-5)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPEL'S SILVIUM 51570 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3)
* HEMPALIN ENAMEL 52140 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3) (white only)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1) (white only)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Morske Flote (CNIIMF),Russia (X-11)
HEMPALIN PRIMER 12050 * LOW FLAME SPREAD* HEMPALIN ENAMEL 52140
Bureau Veritas, France (A-9)
HEMPALIN PRIMER 12050 * LOW FLAME SPREADHEMPALIN UNDERCOAT 42460
* HEMPALIN ENAMEL 52140 Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREADHEMPALIN UNDERCOAT 42460
* HEMPALIN ENAMEL 52140 Registro Italiano Navale - RINA, Italy (A-17)
* HEMPALIN ENAMEL HI-BUILD 52220 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)Lloyd’s register of Shipping, great Britain (A-22)
CERTIFICATES & APPROVALS (by product) Page 11/14
Issued: October 2001
HEMPEL
* MISCELLANEOUS
Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREAD* HEMPALIN ENAMEL HI-BUILD 52220
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
* MISCELLANEOUS
Croatian Register of Shipping, Croatia (X-1)
* HEMPALIN DANREX 52360 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)Food and Drug Administration, USA (D-3)China Classification Society, China (D-5)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I. Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
* HEMPALIN DECKPAINT 53240 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF), Russia (X-11
HEMPALIN PRIMER 12050 * LOW FLAME SPREAD* HEMPALIN DECKPAINT 53240
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
CERTIFICATES & APPROVALS (by product) Page 12/14
Issued: October 2001
HEMPEL
HEMPALIN PRIMER HI-BUILD 13200 * LOW FLAME SPREAD* HEMPALIN DECKPAINT 53240
Bureau Veritas, France (A-9)Det Norske Veritas, Denmark (A-20)Det Norske Veritas, China (A-24)
* HEMPATHANE ENAMEL 55100 * MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPATHANE TOPCOAT 55210 * LOW FLAME SPREAD
See-Berufgenossenschaft, Germany (A-3)
* MISCELLANEOUSState Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
HEMPADUR 45150 * LOW FLAME SPREAD* HEMPATHANE TOPCOAT 55210
Registro Italiana Navale (R.I.N.A.), Italy (A-17)
* HEMPATEX ENAMEL 56360 * NON-CONTAMINATION OF GRAIN CARGOES
Newcastle Occupational Health, Great Britain (D-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)Centralnona. Isljedovateljski I Proj. Institut Morske Flote (CNIIMF),Russia (X-11)
HEMUCRYL PRIMER HI-BUILD 18030 * LOW FLAME SPREAD* HEMUCRYL ENAMEL HI-BUILD 58030
London Underground LImited, Great Britain (A-13)Det Norske Veritas, Denmark (A-20)
* HEMPEL'S ANTIFOULING * MISCELLANEOUSECONIMIC SP-SEA 74030
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPEL'S ANTIFOULING * MISCELLANEOUSNAUTIC SP-ACE 79051
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
* HEMPEL'S ANTIFOULING * MISCELLANEOUSNAUTIC SP-ACE 79070
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
CERTIFICATES & APPROVALS (by product) Page 13/14
Issued: October 2001
HEMPEL
* HEMPADUR 85671 * NON-CONTAMINATION OF GRAIN CARGOES
Food and Drug Administration, USA (D-3)
* POTABLE WATER TANKS (PIPE LINES INTERNAL)
Water Research Centre, Great Britain (I-9)
* CARRIAGE OF FOODSTUFFS
Food and Drug Administration, USA (N-1)
* MISCELLANEOUS
State Committee of Sanitary-Epidemiological Inspection ofRussian Federation, Russia (X-4)
Note:This list covers Group Products 2001, Marine, Protective, and Container.
CERTIFICATES & APPROVALS (by product) Page 14/14
Issued: October 2001
Product DataManual
HEMPEL
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S MARINE VARNISH 02220
Description: HEMPEL’S MARINE VARNISH 02220 is a quick-drying clear urethane alkyd varnish.
Recommended use: On new wood as well as over previously varnished wood, interior and exterior, above thewaterline.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent /00000
Finish: GlossyVolume solids, %: 46 ± 1Theoretical spreading rate: 18.4 m²/litre - 25 micron
738 sq.ft./US gallon - 1 milFlash point: 38°C/100°FSpecific gravity: 0.9 kg/litre - 7.5 lbs/US gallonDry to touch: 2-3 hours at 20°C/68°FV.O.C.: 430 g/litre - 3.6 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Best results will be obtained with a flat varnish brush. Spray application is possible with
most types of spray equipment after thinning, but this application method is mainlysubject to specific local conditions, so no general guidelines can be given.
Cleaning of tools: THINNER 08230
Indicated film thickness, dry: 25 micron/1.0 milIndicated film thickness, wet: 50 micron/2 mils
Recoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0222000000CO010
HEMPEL’S MARINE VARNISH 02220
SURFACE New wood: Saturate the dry surface with a commercial antimould fluid, preferably made fromPREPARATION: fungicide dissolved in white spirit. Apply one coat HEMPEL’S MARINE VARNISH 02220 thinned with
20% THINNER 08230. Apply a second coat HEMPEL'S MARINE VARNISH 02220 thinned 5-10%.Finally apply 3-5 coats HEMPEL'S MARINE VARNISH 02220 undiluted. For the best result rub withdry or wet fine sandpaper and dust off between coats for a smooth Finish.
Previously varnished wood: Wash surface with suitable cleaning agent. Do not use detergentsunless they are removed completely, as otherwise residues can spoil the drying properties and giveadhesion problems. Proceed as for new wood. In some cases the antimould treatment and the firstthinned coats can be omitted.Note: Ammonia water may discolour oak, mahogany and teak.
APPLICATION The surface must be completely clean and dry. Do not apply under humid conditions or atCONDITIONS: temperatures below 5°C/41°F. The moisture content in the wood should not exceed 16%.
SUBSEQUENT None.COAT:
REMARKS:Recoating: Maximum recoating intervals related to later conditions of exposure (20°C/68°F):
2 daysNone02220
MediumMild
AtmosphericRecoated with(Quality nos only)
20°C/68°FSurface temperature
If the maximum recoating interval is exceeded, rub down the surface to ensure adhesion.
Note: HEMPEL'S MARINE VARNISH 02220 is for professional use only.
Issued: October 1999 - 0222000000CO010HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0222000000CO010
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S FLAT MARINE VARNISH 02280
Description: HEMPEL'S FLAT MARINE VARNISH 02280 is a quick-drying clear, flat urethane alkydvarnish. It has good resistance to sea-water, sunlight and adverse weather conditions.The quality is related to Hempel's Marine Varnish 0228. By mixing the two varnishesabout 1:1, silk gloss finish will be obtained.
Recommended use: On new wood as well as over previously varnished wood, interior and exterior, above thewater line.
PHYSICAL CONSTANTS:
Finish: FlatColours: TransparentShade Numbers: 00000Volume by Solids: 41%Theoretical Spreading 16.4 m²/litre - 25 micronsRate: 658 sq.ft./US gallon - 1.0 milFlash Point: 38ºC/100ºF A-Pensky, closed cupSpecific Gravity: 0.9 kg/litre
7.5 lbs/US gallonDry to Touch: 2-3 hours at 20ºC/68°F
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:
Application Method: Best results will be obtained with a flat varnish brush. Spray application is possible withmost types of spray equipment after thinning, but this application method is mainlysubject to specific local conditions, so no general guidelines can be given.
Cleaning of Tools: Thinner 08230
Indicated Film Wet: 50-75 microns/2-3 milsThickness: Dry: 25 microns/1.0 mil
Recoat Interval: Min: 6 hours (20ºC/68°F)Max: 48 hours (20ºC/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0228000000
HEMPEL'S FLAT MARINE VARNISH 02280
Surface Preparation: New wood: Saturate the dry surface with a commercial antimould fluid, preferably made from fungi-cide dissolved in white spirit. Apply one coat Hempel's Flat Marine Varnish 02280 thinned with20% Thinner 08230. Apply a second coat Hempel's Flat Marine Varnish 02280 thinned 5-10%.Finally apply 3-5 coats Hempel's Flat Marine Varnish 02280 undiluted. Rub with dry or wet finesandpaper and dust off between coats for a smooth finish.
On absorbent surfaces, eg. deal (pine-wood), plywood or chipboard, substitute Hempel's MarineVarnish 02220 for the first 3 or 4 coats.
Previously varnished wood: Wash surface with one part ammonia water in six parts of fresh water.Do not use detergents unless they are removed completely, as otherwise residues can spoil thedrying properties and give adhesion problems. Proceed as for new wood. In some cases theantimould treatment and the first thinned coats can be omitted.
NOTE: Ammonia water may discolour oak, mahogany and teak.
Application The surface must be completely clean and dry. Do not apply under humid conditions or atConditions: temperatures below 5ºC/41ºF. The moisture content in the wood should not exceed 16%.
Subsequent Coat: None.
Remarks: If maximum recoat interval is exceeded, rub down surface to ensure adhesion.
Note: HEMPEL'S FLAT MARINE VARNISH 02280 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0228000000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S VARNISH 03330
Description: HEMPEL'S VARNISH 03330 is a quick drying clear acrylic modified alkyd varnish.
Recommended use: As a finishing coat on top rails of open top containers painted with vinyl, acrylic orchlorinated rubber based paints to which PVC tarpaulins otherwise may stick.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent/00000Finish: GlossyVolume solids, %: 32 ± 1Theoretical spreading rate: 12.8 m²/litre - 25 micron
513 sq.ft./US gallon - 1 milFlash point: 25°C/77°F
Specific gravity: 0.9 kg/litre - 7.5 lbs/US gallonDry to touch: 1 hour (approx.) at 20°C/68°FV.O.C.: 570 g/litre - 4.7 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Best results will be obtained with a flat varnish brush.
Spray application is possible with air spray after thinning with HEMPEL'S THINNER08080. Please consult your local Hempel representative.
Cleaning of tools: THINNER 08080
Indicated film thickness, dry: 25 micron/1 milIndicated film thickness, wet: 75 micron/3 mils
Recoat interval, min: not relevantRecoat interval, max.: none
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0333000000CO002
HEMPEL'S VARNISH 03330
SURFACE On aged coatings: Remove oil and grease with suitable detergent, e.g. HEMPEL'S NAVI WASHPREPARATION: 99330. Remove detergent residues, salts and other contaminants by high pressure hosing.
APPLICATION The surface must be completely clean and dry.CONDITIONS: Do not apply at temperatures below 5°C/41°F or above 85% relative humidity.
PRECEDING HEMPATEX HI-BUILD 46370, HEMPATEX HI-BUILD 46410 or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS:Recoating Minimum recoating interval for recoating of HEMPATEX HI-BUILD 46370 or HEMPATEX HI-BUILDIntervals: 46410 with HEMPEL'S VARNISH 03330 is 4-6 hours at 20°C/68°F.
By brush or roller application the varnish should be "laid on", i.e. exert only a light pressure on tooland do not rework already varnished areas.
Note: HEMPEL'S VARNISH 03330 is for professional use only.
Issued: October 1999 - 0333000000CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0333000000CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®VARNISH 05150CURING AGENT 95030
Description: HEMPADUR VARNISH 05150 is a solvent-free low molecular weight amine-cured epoxyvarnish. It is a low viscous product with good penetration properties. Good wearingqualities and easy to clean.
Recommended use: Treatment of wooden floors in containers to be in contact with dry foodstuffs.
Service temperatures: Related to substrate. HEMPADUR VARNISH 05150 itself resists a dry servicetemperature of maximum 140°C/284°F. Will anyhow yellow/darken in the case of suchtemperatures.
Certificates/Approvals: Complies with Section 175.300 of Food Additive Regulations (in respect of carriage ofdry foodstuffs) of the Code of U.S. Federal Regulations.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Transparent/00000Finish: High glossSolids content: 100%Theoretical spreading rate: 5.0 m²/litre - 200 micron
201 sq.ft./US gallon - 8 milsFlash point: >110°C/>230°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 16 (approx) hours at 20°C/68°F (ISO 1517)Dry to touch: 24 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 0 g/litre - 0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the HEMPEL book. Thetheoretical spreading rate has been calculated on the basis of a 100% solids volume.
APPLICATION DETAILS:Mixing ratio for 05150: Base 05159 : Curing agent 95030
7 : 3 by volumeApplication method: Brush, roller (See APPLICATION CONDITIONS)Thinner (max.vol.): See APPLICATION CONDITIONS overleafPot life: 1 hour (20°C/68°F)Cleaning of tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, dry: 200 micron/8 milsIndicated film thickness, wet: 200 micron/8 milsRecoat interval: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0515000000CO007
HEMPADUR VARNISH 05150
SURFACE The surfaces to be treated must be clean and dry and free from grease and oil. Remove loosePREPARATION: material.
New wood: If necessary the surface should be sanded. Carefully remove the dust. Previously varnished wood: If the type of old varnish is unknown, but hard and intact it might bepossible to apply HEMPADUR VARNISH 05150 on top. It is recommended first to apply HEMPADURVARNISH 05150 on a small area. If required, cleaning is done with a suitable detergent followed bya very careful removal of all remnants of detergent, dirt etc. Usually the surface will furthermoreneed sanding, followed by a careful removal of dust.
APPLICATION Surface saturation: It is recommended to saturate absorbent surfaces with a layer ofCONDITIONS: HEMPADUR VARNISH 05150 diluted 20-30% with THINNER 08570. May be topcoated after min.
approx. 6 hours (20°C/68°F).Application method: When treating floors, the mixture may be poured out on the surface and thenlevelled with a roller made of hard rubber or with a broad rubber scraper.Conditions: Use only where application and curing can proceed at temperatures above 10°C/50°F.Moisture content of the wood should be below 16%.
SUBSEQUENT U sually none.COAT:
REMARKS:Recoating: If two coats have to be applied then apply the second coat within 3 days at 20°C/68°F.
Avoid contamination between layers.
Notes: Exposure to sunshine will cause yellowing.
HEMPADUR VARNISH 05150 is for professional use only.
ISSUED: October 1999 - 0515000000CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0515000000CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®VARNISH 05170CURING AGENT 95040
Description: HEMPADUR VARNISH 05170 is a polyamide cured epoxy varnish. Good wearing qualitiesand easy to clean.
Recommended use: Treatment of wooden floors in containers to be in contact with dry foodstuffs.
Service temperatures: Related to substrate. HEMPADUR VARNISH 05170 itself resists a dry servicetemperature of maximum 140°C/284°F. Will anyhow yellow/darken in the case of suchtemperatures.
Certificates/Approvals: Complies with Section 175.300 of Food Additive Regulations (in respect of carriage ofdry foodstuffs) of the Code of U.S. Federal Regulations.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Transparent/00000Finish: FlatVolume solids, %: 46 ± 1Theoretical spreading rate: Not relevant (see REMARKS overleaf)Flash point: 26°C/79°FSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonDry to touch: 8 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 480 g/litre - 3.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 05170: Base 05179 : Curing agent 95040
3 : 1 by volumeApplication method: Brush, roller (See APPLICATION CONDITIONS)Thinner (max.vol.): See APPLICATION CONDITIONS overleafPot life: 4 hours (20°C/68°F)Cleaning of tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, dry: Not relevantIndicated film thickness, wet: Not relevant (see REMARKS overleaf)Recoat interval: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0517000000CR001
HEMPADUR VARNISH 05170
SURFACE The surfaces to be treated must be clean and dry and free from grease and oil. Remove loosePREPARATION: material.
New wood: If necessary the surface should be sanded. Carefully remove the dust.Previously varnished wood: If the type of old varnish is unknown, but hard and intact it might bepossible to apply HEMPADUR VARNISH 05170 on top. It is recommended first to apply HEMPADURVARNISH 05170 on a small area. If required, cleaning is done with a suitable detergent followed bya very careful removal of all remnants of detergent, dirt etc. Usually the surface will furthermoreneed sanding, followed by a careful removal of dust.
APPLICATION Surface saturation: It is recommended to saturate absorbent surfaces with a layer ofCONDITIONS: HEMPADUR VARNISH 05170 diluted 80% with THINNER 08570. May be topcoated after min.
approx. 20 hours (20°C/68°F).Application method: When treating floors, the mixture may be poured out on the surface and thenlevelled with a roller made of hard rubber.Conditions: Use only where application and curing can proceed at temperatures above 10°C/50°F.Moisture content of the wood should be below 16%.
SUBSEQUENT Usually none.COAT:
REMARKS:Film thickness: The main purpose of the treatment with HEMPADUR VARNISH 05170 is rather to impregnate the
wooden surface than to produce a lacquer layer on top of it. Recoating: If two coats have to be applied then apply the second coat within 3 days at 20°C/68°F.
Avoid contamination between layers.
Notes: Exposure to sunshine will cause yellowing.HEMPADUR VARNISH 05170 is for professional use only.
Issued: October 1999 - 0517000000CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0517000000CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®SEALER 05970CURING AGENT 95950
Description: HEMPADUR SEALER 05970 is a low molecular weight epoxy varnish cured with aromaticamine. It is a low viscous product with good penetration properties.
Recommended use: For saturation of well cleaned concrete surfaces before application of pigmented paints.Must be applied in such an amount that the surface is just saturated. The surfaceshould not appear smooth and even. HEMPADUR SEALER 05970 is especially developedfor use under heavy duty paint systems and chemical resistant coatings.
Service temperatures: Related to substrate and subsequent coat. HEMPADUR SEALER 05970 itself resists thefollowing temperatures:Dry: In water:Maximum: 140°C/284°F 60°C/140°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent, green/04200Finish: FlatVolume solids, %: 52 ± 1Theoretical spreading rate: Not relevant (See REMARKS overleaf)Flash point: 27°C/81°FSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonDry to touch: 2-4 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 430 g/litre - 3.6 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 05970: Base 05979 : Curing agent 95950
4 : 1 by volumeApplication method: Airless spray BrushThinner (max.vol.): 08450 (up to 50%) 08450 (up to 50%)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .017"-.021"Nozzle pressure: 100 bar/1450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: Not relevantIndicated film thickness, wet: Not relevant (See REMARKS overleaf)Recoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0597004200CO002
HEMPADUR SEALER 05970
SURFACE All possible slip agent, oil, grease and other contaminants must be removed by eg abrasivePREPARATION: blasting, volatilizing by flame cleaning or treatment with suitable detergent. Last mentioned in the
following way: Saturation of the surface with fresh water. Washing with detergent followed by freshwater hosing.Depending on construction and purpose, abrasive blast, high pressure water jet or treat theconcrete with power tools to obtain a rough and firm surface free of scum layer and othercontamination. Remove dust and loose material. If mechanical treatment is impossible, the surfacemay be treated with acid etching. For this purpose an approx. 5% w/w nitric or phosphoric acidsolution is recommended. Note: Strong acids, take necessary precautions, make sure that safetyregulations are obeyed! Prior to etching the concrete should be saturated with fresh water toprevent acid corrosion of the reinforcement bars. Leave the acid to act for 3-4 minutes and hosedown the surface with fresh water - preferably first a 5% w/w sodium hydroxide solution - and scrubcarefully. After that the surface must dry homogeneously and appear as an even, rough surfacefree of a loose outer layer. The surface must have a pH reaction of between 6.5 - 8.0. If any ofthese conditions are not fulfilled, the process must be repeated. The surface must be dried withgood ventilation for at least 2 days (65% relative humidity and 20°C/68°F). The pretreatment iscontrolled by scraping with a strong knife. The surface shall feel solid and hard, and the knife mustonly leave a clear scratch mark.
APPLICATION The concrete must be fully cured, eg 28 days for normal Portland cement, and completely dryCONDITIONS: with a humidity content in the surface below 4%. The concrete must also be controlled for absence
of capillary water action or for subsoil water.Use only where application and curing can proceed at temperatures above 10°C/50°F. Apply onlyon a dry surface, free of dust, grease, oil and other contamination - as described above. Inconfined spaces provide adequate ventilation during application and drying.
SUBSEQUENT According to specification.COAT:
REMARKS:Film thicknesses/ HEMPADUR SEALER 05970 is used for saturation of the absorbent concrete surface. ApplicationConsumption: should be initiated by assessing the degree of dilution in order to obtain a correct result, ie up to
approx 50%. The actual amount of thinner required will depend on temperatures, the surface andtype of the concrete and the actual application technique. Furthermore, a practical theoreticalspreading rate cannot be calculated. For practical purposes, approx. 14 m²/litre (570 sq.ft./USgallon) is indicated depending on the surface roughness, porosity of the concrete, and theapplication method.
Appearance: In any case a glossy surface must not appear and such a surplus of HEMPADUR SEALER 05970must be removed by sanding before painting takes place.
Note: HEMPADUR SEALER 05970 is for professional use only.
Issued: May 2000 - 0597004200CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0597004200CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S HI-VEE®LACQUER 06520
Description: HEMPEL'S HI-VEE LACQUER 06520 is a non-yellowing, clear varnish based on acrylicresin dissolved in white spirit. Physically drying. The inclusion of a UV absorber serves toprotect the preceding paint film against ultraviolet radiation.Further benefits are water and dirt repellent properties.
Recommended use: For protection of HEMPEL'S HI-VEE 56540, especially in outdoor exposure, to maintainthe high visibility (HI-VEE) of the fluorescent effect.Not recommended for surfaces subject to excessive wear.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Transparent/00000Finish: GlossyVolume solids, %: 27 ± 1Theoretical spreading rate: 10.8 m²/litre - 25 micron
433 sq.ft./US gallon - 1 milFlash point: 32°C/90°FSpecific gravity: 0.9 kg/litre - 7.7 lbs/US gallonDry to touch: 1-2 hours at 20°C/68°FV.O.C.: 580 g/litre - 4.8 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Best results are obtained with a flat varnish brush. Spray application is possible with
most types of spray equipment after thinning with THINNER 08230, but this applicationmethod is mainly subject to specific local conditions, so no general guidelines can begiven.
Cleaning of tools: THINNER 08230
Indicated film thickness, dry: 25 micron/1 milIndicated film thickness, wet: 100 micron/4 mils
Recoat interval, min: 3 hours (20°C/68°F)Recoat interval, max: none (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0652000000CO007
HEMPEL'S HI-VEE LACQUER 06520
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPEL'S HI-VEE 56540.COAT:
SUBSEQUENT None.COAT:
REMARKS: No maximum recoating interval, but after prolonged exposure to polluted atmosphere, removeaccumulated contamination by (high pressure) fresh water cleaning and allow to dry.
Note: HEMPEL'S HI-VEE LACQUER 06520 is for professional use only.
Issued: October 1999 - 0652000000CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0652000000CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S CONCRETE SILICONE 06910
Description: HEMPEL'S CONCRETE SILICONE 06910 is a solution of an oligomer siloxane providingwater-repellent surface of concrete and similar materials. It has good penetration,dries up without tack and has good resistance to alkali and sunlight. It makes thecapillary walls and cavities water-repellent, whereas no film is formed on the surface.Water and gas permeability remain basically unchanged. The water-repellent actionprovides added weatherability and resistance to dirt pick-up, etc.
Recommended use: As an almost invisible water-repellent surface proofing of concrete and other alkalineconstruction materials where the material's ability to breathe must be maintained.
PHYSICAL CONSTANTS:
Finish: TransparentColours: ColourlessShade Number: 00000Volume by Solids: 5%Theoretical Spreading Rate: See REMARKS overleafFlash Point: 12ºC/54ºF A-Pensky, closed cupSpecific Gravity: 0.8 kg/litre
6.7 lbs/US gallonDry to Touch: 30 (approx) minutes at 20ºC/68ºFShelf Life: 9 months at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:
Application Methods: Air spray or brush. Shake or stir well before use. See further instructions overleaf.Cleaning of Tools: Thinner 08080
Indicated film thickness, dry: Not relevantIndicated film thickness, wet: Not relevant
Recoating Interval: Min: 24 hours (20ºC/68ºF)Max: none (See REMARKS overleaf)
1/2
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0228000000
HEMPEL'S CONCRETE SILICONE 06910
Surface Apply only on a sound and intact, fully cured surface, which means at least 28 days for newPreparation: concrete. A weak outer skin, such as laitance or a carbonated layer must be removed, preferably
by blast cleaning. Smaller cracks (less than approx. 0.3 mm) will be protected while larger onesmust be repaired. Also, defective sealants must be repaired. A dirty surface must be cleaned,either by high pressure hosing or steam cleaning. Use of emulsifiers is not recommended as theseare difficult to remove completely and consequently impede the penetration. Cover windows anddoors, etc. during application.
Application The surface must be completely dry to give the best possible penetration. It is generallyConditions: recommended to carry out the work at the lowest possible relative humidity. For spray application,
nozzle pressure should be max. 0.5 bar/7 psi to avoid atomisation. To ensure a homogeneousimpregnation, application starts from the bottom and up and at such a slow pace as to keep anapprox. 30 cm/1 ft wide belt wet below the application zone itself. It is recommended to treat thesurface 2-3 times to obtain sufficient depth of impregnation. Leave the first coat to set (approx. 15minutes) before applying next coat.
Subsequent Coat: Normally none. If desired, overcoating can take place after approx. 24 hours. When overcoatingwith emulsion paint, care must be taken to obtain good wetting. This is best done by brush orroller application, or by waiting several months after the application of Hempel's Concrete Silicone06910.
Remarks: Hempel's Concrete Silicone 06910 is used for saturation of the absorbent concrete surface. Atheoretical spreading rate cannot therefore be calculated. For practical purposes, approximately1.5-2 m²/litre (60-80 sq.ft/US gallon) is indicated for firm concrete with a penetration depth of 2-3mm. For more porous surfaces, the spreading rate will be lower, and for more dense surfacehigher. Store in a dry and cool place, max. storage temperature 30ºC/86ºF.
Note: HEMPEL'S CONCRETE SILICONE 06910 is for professional use only.
Safety: Labelling according to EEC Regulations:Symbols: F HIGHLY FLAMMABLEContains: Organic solvents.
Avoid contact with skin and eyes. Do not breathe vapour/spray mist. Use only in well-ventilatedareas. If necessary, wear suitable respiratory protection. When using, do not eat, drink or smoke.Do not empty into drains. Take precautionary measures against static discharges. Keep out ofreach of children.
2/2
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 0228000000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPINOL®10220
Description: HEMPINOL 10220 is a physically drying, high-build, bituminous coating.
Recommended use: For inexpensive short to medium-term anticorrosive protection of interior and exteriorsteelwork not exposed to direct sunlight. Not resistant to continuous mechanical stress.
Availability: Part of Group Assortment. Local availability subject to confirmation.
Certificates/Approvals: Has a German and Danish EC-type Examination Certificate.
PHYSICAL CONSTANTS:Colours/Shade nos: Black /19990Finish: FlatVolume solids, %: 53 ± 1Theoretical spreading rate: 3.0 m²/liter - 175 micron
121 sq.ft./US gallon - 7 milsFlash point: 38°C/100°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 10 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 16 (approx.) hours at 20°C/68°FV.O.C.: 375 g/litre - 3.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (2%) 08080 (15%) 08080 (5%)Nozzle orifice: .021"-.025"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 175 micron/7 mils (See REMARKS overleaf)Indicated film thickness, wet: 325 micron/13 milsRecoat interval, min: When dryRecoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1022019990CO009
HEMPINOL 10220
SURFACE New steel: Abrasive blasting to minimum Sa 2 or mechanical cleaning to St 3.PREPARATION: For temporary protection, if required, use a suitable shopprimer. All damage of shopprimer and
contamination from storage and fabrication should be thoroughly cleaned prior to final painting. Forrepair and touch-up use HEMPINOL 10220.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting, power tool cleaning or water jetting. Dust off residues and allow the surface todry. Touch up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence the amount of thinning necessary, drying time andrecoating interval. Normal range is 125-200 micron/5-8 mils.
Note: HEMPINOL 10220 is for professional use only.
Issued: September 2000 - 1022019990CO009HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1022019990CO009
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPINOL* 10390
Description: HEMPINOL 10390 is a reinforced, physically drying, bituminous coating. It is flexible, water-resistant, and rust-preventing.
Recommended use: As a maintenance coating in potable water tanks coated with bituminous coatings.
Certificates: Certificates for contact with potable water available. Availability: Subject to confirmation.
PHYSICAL CONSTANTS:
Colours/Shade nos.: Black/19990Finish: Semi-gloss Volume solids: 54% Theoretical spreading rate: 4.3 m²/litre - 125 micron
173 sq.ft./US gallon - 5 milsFlash point: 38°C/100°F Specific gravity: 1.1 kg/litre - 9.1 lbs/US gallonDry to touch: 16 (approx.) hours at 20°C/68°FV.O.C.: 390 g/litre - 3.2 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS: Application method: Airless spray Brush Thinner (max.vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .021"-.025"Nozzle pressure: 200 bar/2800 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 125 micron/5 milsIndicated film thickness, wet: 225 micron/9 mils Recoat interval, min: When dry (See REMARKS overleaf)Recoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1039019990CO007
HEMPINOL 10390
SURFACE Maintenance: Remove oil and grease etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Remove all rust and loose material by
abrasive blasting or power tool cleaning. Dust off residues. Touch-up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT: SUBSEQUENT None or according to specification. COAT:
REMARKS: To avoid later problems with unpleasant taste of water it is of the utmost importance that the paintfilm is thoroughly dried as to remove all solvents (mineral spirit) before the tank is taken into use.As heavy layers of paint applied, for instance pools laying in corners and similar places, areextremely difficult to get dried properly such defects must be avoided. If observed, such areasmust be repaired by scraping followed by touch up to proper film thickness.
Stripe coating: It is recommended to apply at least two layers by brush on free edges, rough welds, reverse sidesand similar places difficult to cover by airless spray.
Recoatingintervals: Steel Minimum time
temperatures required
0°C/32°F 48 hours10°C/50°F 30 hours20°C/68°F 16 hours30°C/86°F 10 hours
These (minimum) intervals are only valid provided thati) HEMPINOL 1039 is applied in the specified dry film thickness of 125 micron. If higher thicknesses have been used substantially longer, drying time may be the result.
ii) Sufficient ventilation has been put into force (see below). Especially, it must be emphasized that all painted compartments of the tank are ventilated, not only just near to the openings.
Before taking the tank into use:1. All painted surfaces must be completely dry. A thorough inspection is required to verify this. If
not dry, drying and ventilation must continue. Warm, (dehumidified) air may be necessary to support the drying.
2. The tank must be cleaned properly. This will be subject to local/individual specification or regulation. Typically such one will call for a filling with water, allowed to stand for at least 24 hours. Drain and repeat procedure and finally flush with fresh water. If a hosing down with hot fresh water is performed, this should not be above 35-40°C in temperature.
Note: HEMPINOL 10390 is for professional use only.
Issued: January 1997-1039019990CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1039019990CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S BALLAST COAT SH 10880
Description: HEMPEL’S BALLAST COAT SH 10880 is a semi-hard, one-component, surface-tolerant,high-build coating. It is flexible, water resistant and corrosion-preventing.
Recommended use: For short to medium-term repair and maintenance of ballast tanks, cofferdams and voidspaces under conditions where abrasive blast cleaning is not feasible. Resistant tocathodic protection by sacrificial anodes. Resistant to foot traffic during survey of tanks,but not to continuous mechanical stress.
Availability: Part of Group Assortment. Local availability subject to confirmation.
Certificates/Approvals: Classification C1 by Marintek, Norway.Accepted by Lloyd’s Register of Shipping as a Maintenance Coating, Class 2.
PHYSICAL CONSTANTS:Colours/Shade nos: Alu-bronze/19820 - black/19990Finish: FlatVolume solids, %: 52 ± 1Theoretical spreading rate: 3.0 m²/liter - 175 micron
119 sq.ft./US gallon - 7 milsFlash point: 38°C/100°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 10 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 16 (approx.) hours at 20°C/68°FV.O.C.: 375 g/litre - 3.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (2%) 08080 (15%) 08080 (5%)Nozzle orifice: .021"-.025"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 175 micron/7 mils (See REMARKS overleaf)Indicated film thickness, wet: 325 micron/13 milsRecoat interval, min: When dryRecoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1088019820CO002
HEMPEL’S BALLAST COAT SH 10880
SURFACE Maintenance: Remove all oil and grease, mud and similar contaminants with suitable detergentPREPARATION: followed by (high pressure) fresh water cleaning. Remove rust scale and loose coating material by
abrasive blasting, power tool cleaning or water jetting to minimum Sa 1, St 2 (ISO 8501:1988) orWJ-4 (NACE No. 5/SSPC-SP 12). Existing epoxy or coal tar epoxy system to be uniformly matted bygrinding, abrasive sweep blasting or water jetting. Dust off residues. Allow the surface to dry. Thedurability of the system depends on the achieved degree of surface preparation. Insufficientremoval of scale will result in later flaking.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence the amount of thinning necessary, drying time andrecoating interval. Normal range is 125-200 micron/5-8 mils per coat in a two-coat system.Application of HEMPEL'S BALLAST COAT SH 10880 as a one-coat system is possible,recommended dry film thickness is 300 micron. The durability of a one-coat system is very muchinfluenced by the application method.
Curing before Ballast tanks may be filled when all painted surfaces are completely dry. It is recommended tofilling of tanks: ascertain the drying condition by a thorough inspection before filling.Maintenance: Regular maintenance of the coating is carried out touching up with HEMPEL'S BALLAST COAT SH
10880 to full film thickness after having prepared the surface as described above.
Note: HEMPEL’S BALLAST COAT SH 10880 is for professional use only.
Issued: May 2000 - 1088019820CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1088019820CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®PRIMER 12050
Description: HEMPALIN PRIMER 12050 is a relatively quick-drying, zinc phosphate primer, based onlong oil alkyd and urethane alkyd.
Recommended use: General purpose primer for HEMPALIN systems for protection of steel in mild to mediumatmospheric corrosive environments.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish and German authorities according toIMO resolution MSC 61 (67).Has a German and Danish EC-type Examination Certificate.Please see REMARKS overleaf.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Green/40760 - Red/50410Finish: FlatVolume solids, %: 49 ± 1Theoretical spreading rate: 12.3 m²/litre - 40 micron
491 sq.ft./US gallon - 1.6 milsFlash point: 38°C/100°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonDry to touch: 2-4 hours at 20°C/68°FV.O.C.: 410 g/litre - 3.4 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max.vol.): 08230 (5%) 08230 (5%) 08230 (5%)Nozzle orifice: .018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08230Indicated film thickness, dry: 40 micron/1.6 milIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1205040760CO016
HEMPALIN PRIMER 12050
SURFACE New steel: Abrasive blasting to minimum Sa 2. For temporary protection, if required,PREPARATION: use a suitable shopprimer. Damage of shopprimer and contamination from storage and fabrication
should be thoroughly cleaned prior to final painting. For repair and touch-up use HEMPALIN PRIMER12050.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Dust off residues. Touch up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT HEMPALIN system according to specification.COAT:
REMARKS: Some of the certificates are issued under the former quality number 1205.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 30-50 micron/1.2-2 mils.
Recoating: Recoating intervals related to later conditions of exposure:(40 micron/1.6 mils dry film thickness of HEMPALIN PRIMER 12050)
3 days7 days
nonenone
8 hrs2 days
5 hrs2 days
HEMPALIN, except 5324053240
MediumMildMediumMild
AtmosphericAtmosphericRecoated with(Quality Numbers only)
20°C/68°F20°C/68°FSteel temperature
MaximumMinimum
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion. Before recoating after exposure in contaminated environment, clean surfacethoroughly with (high pressure) fresh water hosing and allow to dry.
Note: HEMPALIN PRIMER 12050 is for professional use only.
Issued: May 2000 - 1205040760CO016HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1205040760CO016
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN* RED LEAD 12370
Description: HEMPALIN RED LEAD 12370 is a long-oil alkyd-based primer with red lead pigments.
Recommended use: As a new-construction and maintenance primer in HEMPALIN system on interior andexterior steel in mildly to moderately corrosive environment.Not suited for immersion.
Service temperatures: Maximum, dry: 100°C/212°F.
Approvals: Approved by Nippon Kaiji Kyokai, Tokyo as a low flame spread material.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Light red/50246Finish: Semi-flatVolume solids: 50%Theoretical spreading rate: 12.5 m²/litre - 40 micron 501 sq.ft./US gallon - 1.6 milsFlash point: 38°C/100°FSpecific gravity: 1.5 kg/litre - 12.5 lbs/US gallonDry to touch: 5-7 hours at 20°C/68°FV.O.C.: 400 g/litre - 3.3 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max.vol.): 08080 (5%) 08080 (15%) 08230 (5%)Nozzle orifice: .018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080 or 08230Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1237050246CO002
HEMPALIN RED LEAD 12370
SURFACE New steel: Abrasive blasting to minimum Sa 2, alternatively power tool cleaning to St 3. PREPARATION: Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and other
contaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Dust off residues. Touch up to full film thickness.Note: When scraping and wire-brushing on old RED LEAD, precautions must be taken against leadpoisoning (filter mask).
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT HEMPALIN System according to specification. COAT: REMARKS: Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 30-50 micron/1.2-2 mils.
Recoating: Recoating intervals related to later conditions of exposure:(40 micron/1.6 mils dry film thickness of HEMPALIN RED LEAD 12370)
5 days10 days
nonenone
24 hrs7 days
24 hrs7 days
HEMPALIN, except 53245324
MediumMildMediumMild
AtmosphericAtmosphericRecoated with(Quality Numbers only)
20°C/68°F20°C/68°FSteel Temperature
MaximumMinimum
Before recoating after exposure in contaminated environment, clean surface thoroughly with (highpressure) fresh water and allow to dry.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: HEMPALIN RED LEAD 12370 is for professional use only.
SAFETY: Handle with care. Before and during use, observe all safety labels on packaging and paintcontainers, consult HEMPEL Material Safety Data Sheets and follow all local or national safetyregulations. Harmful or fatal if swallowed; immediately seek medical assistance if swallowed. Avoidinhalation of possible solvent vapours or paint mist, as well as paint contact with skin and eyes.Apply only in well ventilated areas and ensure that adequate forced ventilation exists when applyingpaint in confined spaces or when the air is stagnant. Always take precautions against the risks offire and explosions.
Issued: September 1996 - 1237050246CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1237050246CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S UNI-PRIMER®13140
Description: HEMPEL’S UNI-PRIMER 13140 is a quick-drying, one-component, modified epoxy esterprimer with zinc phosphate rust-inhibiting pigments.
Recommended use: As a versatile primer on steel and metal surfaces for HEMPALIN or HEMPATEX in mild tomedium corrosive atmospheric environment. It provides the possibility of reducing thenumber of primers for maintenance.
Service temperature: Maximum, dry: 140°C/284°F (or as dictated by subsequent HEMPATEX topcoats).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light grey/12170 - Red/51320Finish: FlatVolume solids, %: 42 ± 1Theoretical spreading rate: 8.4 m²/litre - 50 micron
337 sq.ft./US gallon - 2 milsFlash point: 30°C/86°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: ¾ (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 2 (approx.) hours at 20°C/68°FV.O.C.: 520 g/litre - 4.3 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max.vol.): 08080 (5%) 08080 (10%) 08080 (10%)Nozzle orifice: .019"-.023"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S THINNER 08080Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 125 micron/5 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1314012170CO006
HEMPEL’S UNI-PRIMER 13140
SURFACE New steel: Abrasive blasting to minimum Sa 2½ is recommended. A suitable zinc-free or low-zincPREPARATION: shopprimer may be used for temporary protection if required. All damage of shopprimer and
contamination from storage and fabrication should be thoroughly cleaned prior to final painting. Forrepair and touch-up use HEMPEL’S UNI-PRIMER 13140.Smooth metal surfaces: Very careful degreasing and removal of other contaminants. Maintenance: Remove oil and grease etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water hosing. Remove all rust and other loose material byabrasive blasting or power tool cleaning. Feather edges to sound and intact areas. Dust offresidues. Touch up to full film thickness.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation.
In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT HEMPALIN or similar alkyds or HEMPATEX systems according to specification.COAT: Recoating with other qualities, see REMARKS below.
REMARKS:Substrate: Smooth metal surfaces and zinc-coated steel are only relevant as substrate in case of later mild
exposure conditions.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence amount of thinning necessary, drying time, andrecoating interval. Normal range is 25-80 micron/1-3.2 mils.
Recoating: Recoating intervals related to later conditions of exposure:(50 micron/2 mils dry film thickness of HEMPEL’S UNI-PRIMER 13140)
3 daysNone
NoneNone
2 hours6 hours
1 hour4 hours
HEMPALIN1)
HEMPATEX, HEMPALIN2)
MediumMildMediumMildRecoated withAtmosphericAtmospheric20°C/68°F20°C/68°FSteel temperatureMaximumMinimum
1) Dissolved in white spirit only2) Dissolved in aromatic solvents
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Recoating with Recoating with HEMPADUR and HEMPATHANE is possible, but should be done with as thin layersepoxy and P.U.: as possible to minimize the risk of lifting. Furthermore, in this case - used as a “bridge coating” - it
is recommended to apply HEMPEL’S UNI- PRIMER 13140 in 25 micron/1 mil dry film thicknessonly. Make a test patch to secure full compatibility between the old paint system and the new paintsystem.Minimum recoating interval (20°C/68°F) is 48 hours, maximum none.
Notes: Before recoating after exposure in contaminated environment, clean surface thoroughly with highpressure fresh water hosing and allow to dry.HEMPEL’S UNI-PRIMER 13140 is for professional use only.
Issued: May 2001 - 1314012170CO006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1314012170CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®PRIMER HI-BUILD 13200
Description: HEMPALIN PRIMER HI-BUILD 13200 is a quick-drying, urethane-modified alkyd primerwith zinc phosphate, rust-inhibiting pigments.
Recommended use: General purpose primer for HEMPALIN systems for protection of steel in mild to mediumatmospheric corrosive environments.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish and German authorities according toIMO resolution MSC 61 (67). Has a German and Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Yellow/22430 White/10000Finish: Flat FlatVolume solids, %: 45 ± 1 44 ± 1Theoretical spreading rate: 6.0 m²/litre - 75 micron 5.9 m²/litre - 75 micron
241 sq.ft./US gallon - 3.0 mils 235 sq.ft./US gallon - 3.0 milsFlash point: 31°C/88°F 31°C/88°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallon 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: 1 (approx.) hr at 20°C/68°F (ISO 1517) 1 (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 4 (approx.) hours at 20°C/68°F 4 (approx.) hours at 20°C/68°FV.O.C.: 450 g/litre - 3.7 lbs/US gallon 445 g/litre - 3.7 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush (touch up)Thinner (max.vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .021"-.023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 75 micron/3 milsIndicated film thickness, wet: 175 micron/7 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1320022430CO007
HEMPALIN PRIMER HI-BUILD 13200
SURFACE New steel: Abrasive blasting to Sa 2½ is recommended. For temporary protection, if required, usePREPARATION: a suitable zinc-free or low-zinc shopprimer. All damage of shopprimer and contamination from
storage and fabrication should be thoroughly cleaned prior to final painting. For repair and touch-upuse HEMPALIN PRIMER HI-BUILD 13200.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Dust off residues. Touch up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT HEMPALIN system according to specification.COAT:
REMARKS: Some of the certificates have been issued under the former quality number 1320.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 50-75 micron/2-3 mils.
Recoating: Recoating intervals related to later conditions of exposure:(75 micron/3 mils dry film thickness of HEMPALIN PRIMER HI-BUILD 13200)
3 daysNone
10 days
NoneNoneNone
8 hours8 hours5 days
5 hours5 hours5 days
HEMPALIN, except 53240 and 132001320053240
MediumMildMediumMildRecoated with
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean the surface thoroughly with(high pressure) fresh water and allow to dry.
Note: HEMPALIN PRIMER HI-BUILD 13200 is for professional use only.
Issued: October 1999 - 1320022430CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1320022430CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S RADIATOR COATING 134QA
Description: HEMPEL'S RADIATOR COATING 134QA is an epoxy ester coating, specially designed fordip or flow application on finned heat exchangers.
Recommended use: Protection of fins and other heat exchanging surfaces on radiators. Not suited forimmersion or in connection with impressed current cathodic protection.
Service Temperatures: Maximum, dry: 120°C/248°F.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Blue/31570Finish: GlossyVolume solids: 38%Theoretical spreading rate: 9.5m2/litre - 40 micron
406 sq.ft./US Gallon - 1.5 milsFlash point: 27°C/81°F. Specific gravity: 0.9 kg/litre - 7.4 lbs/US gallonDry to touch: 2 hours at 20°C/68°FV.O.C.: 504 g/litre - 4.2 lbs/US gallon Measured according to US Method 24
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes".
APPLICATION DETAILS:Application method: Dipping or flow coatingThinner (max.vol.): 08080 (30-50%)Noizzle orifice: N/ANozzle pressure: N/ACleaning of tools: THINNER 08080
Indicated film thickness, dry: 40 micron/1.5 milsIndicated film thickness, wet: 100 micron/4 mils
Recoat interval, min: 24 hoursRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 134QA31570
HEMPEL'S RADIATOR COATING 134QA
SURFACE All grease, oil, dirt and foreign matter must be removed with a suitable detergent such asPREPARATION: HEMPEL'S NAVI WASH 99330.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT NoneCOAT:
REMARKS:Film thickness: May vary depending on amount of thinner used. It is recommended to obtain 1.5 mils dry film
thickness.
Note: HEMPEL'S RADIATOR COATING 134QA is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 134QA31570
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPAQUICK®PRIMER 13624
Description: HEMPAQUICK PRIMER 13624 is a very quick-drying zinc phosphate pigmented alkydprimer.
Recommended use: As a rust preventing primer on steel, machinery parts, etc. where quick drying is needed,both as a workshop primer for temporary protection and as a general purpose primer infast drying alkyd-based systems for protection of steel in mild to medium atmosphericcorrosive environments.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Tested for non-contamination of grain cargo by Newcastle Occupational Health, GreatBritain.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade Nos: Light grey/12170 - Red/50710Finish: FlatVolume solids, %: 47 ± 1Theoretical spreading rate: 5.9 m²/liter - 80 micron
236 sq.ft./US gallon - 3.2 milsFlash point: 31°C/88°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: ½ (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 1 (approx.) hour at 20°C/68°FV.O.C.: 470 g/litre - 3.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (10%) 08080 (15%) 08080 (5%)Nozzle orifice: .021"-.023"Nozzle pressure: 150 bar/2175 psi
(Airless spray are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 80 micron/3.2 milsIndicated film thickness, wet: 175 micron/7 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1362412170CO002
HEMPAQUICK PRIMER 13624
SURFACE New Steel: Remove oil and grease etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to minimum Sa 2,
alternatively power tool cleaning to St 3 depending on the corrosion impact.On machinery: May be applied directly on steel and iron after degreasing and mechanical cleaning.Repair of damaged areas: Remove oil and grease etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning followed by fresh water cleaning. Touch up to full filmthickness.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation.
In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT Xylene-based HEMPALINs and similar alkyds or according to specification.COAT:
REMARKS: Certificate is issued under the former quality number 1362.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter the spreading rate and may influence the amount of thinning necessary, drying timeand recoating interval. Normal range is 40-80 micron/1.6-3.2 mils.
Recoating: Recoating intervals related to later conditions of exposure:(80 micron/3.2 mils dry film thickness of HEMPAQUICK PRIMER 13624)
NoneNone30 minutes15 minutesHEMPALIN*
MediumMildMediumMildRecoated with
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
*Dissolved in xylene only.
Notes: Before recoating after exposure to contaminated environment, the surface should be thoroughlycleaned by high pressure fresh water hosing and allow to dry.HEMPAQUICK PRIMER 13624 is for professional use only.
Issued: September 2000 - 1362412170CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1362412170CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®LTC 15030BASE 15039 with CURING AGENT 97030
Description: HEMPADUR LTC 15030 is a low temperature curing (LTC), two-component, polyamideadduct cured coal tar epoxy, which provides a very hard-wearing coating, highly resistantto sea water, crude oil, fuel oil, etc. Not resistant to aromatic hydrocarbons, includingsome grades of petrol, or stronger solvents. Aliphatic hydrocarbons will discolour.
Recommended use: For long-term protection of steel and concrete in severe corrosive environments andimmersed areas, e.g. on submerged surfaces, in crude and fuel oil tanks, and watertanks, when the application temperatures are below approx. 10°C/50°F.
Service temperatures: Dry: In oil: In water (no temperature gradient):Maximum: 90°C/194°F 60°C/140°F 45°C/113°F
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Approved by Lloyd's Register of Shipping and Bureau Veritas as a corrosion controlcoating.Approved as a ballast tank coating by Germanischer Lloyd, Germany.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Black/19990 - Brown/60430Finish: Semi-glossVolume solids, %: 61 ± 1Theoretical spreading rate: 4.9 m²/litre - 125 micron
196 sq.ft./US gallon - 5 milsFlash point: 25°C/77°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 4 (approx) hrs at 20°C/68°F (ISO 1517)
-10°C/14°F 0°C/32°F +10°C/50°FDry to touch: 60 hrs 24 hrs 12 hrsFully cured: 65 days 30 days 15 daysV.O.C.: 350 g/litre - 2.9 lbs/US gallonShelf life: 1 year (25°C/77°F) from time of production. Depending on storage conditions,
mechanical stirring may be necessary before usage.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15030: Base 15039 : Curing agent 97030
3 : 1 by volumeApplication method: Airless spray Air spray Brush (touch-up)Thinner (max.vol.): 08450 (5%) 08450 (10%) 08450 (5%)Pot life: 2 hours (10°C/50°F) 4 hours (10°C/50°F)Nozzle orifice: .021"-.023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 125 micron/5 mils (See REMARKS overleaf)Indicated film thickness, wet: 200 micron/8 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1503019990CO012
HEMPADUR LTC 15030
SURFACE New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½. For temporary
protection, if required, use suitable shopprimer. All damage of shopprimer and contamination fromstorage and fabrication should be thoroughly cleaned prior to final painting. For repair and touch-upuse HEMPADUR LTC 15030.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed by(high pressure) fresh water hosing. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment or acidetching. Seal surface with suitable sealer, e.g. HEMPADUR SEALER 05970 (Furthermore, see theProduct Data Sheet for 05970).Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly byabrasive blasting or power tool cleaning. As an alternative to dry cleaning, water jetting to sound,well adhering coat and/or to steel. Intact coat must appear with roughened surface after the waterjetting. By water jetting to steel, cleanliness shall be minimum WJ-2 (NACE No. 5/SSPC-SP 12). Aflash-rust degree of FR-2, preferably FR-1 (Hempel standard) is acceptable before application.Feather edges to sound and intact areas. Dust off residues. Touch up to full film thickness.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. HEMPADUR LTC 15030 may be applied and will cure at temperatures down to
-10°C/15°F. The temperature of the paint itself should preferably be above 10°C/50°F. If thetemperature of the paint is below 10°C/50°F thinning may be necessary, but this will cause lowerfilm build and slower drying. In confined spaces provide adequate ventilation during application anddrying.
PRECEDING Steel: None or according to specification.COAT: Concrete: HEMPADUR SEALER 05970.
SUBSEQUENT None or as per specification depending on area of use.COAT:
REMARKS: Certificates are issued under the former quality number 1503.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence the amount of thinning necessary, drying time andrecoating interval. Normal range is 100-125 micron/4-5 mils.
Recoating:
15 hours34 hours68 hours10 hours23 hours45 hours46330
4½ days10 days20 days12 hours27 hours54 hours15030, 45182
+10°C/50°F0°C/32°F-10°C/14°F+10°C/50°F0°C/32°F-10°C/14°F
MaximumMinimum125 micron/5 mils of 15030
Recoated with(Quality numbers only)
The maximum recoating intervals between layers of HEMPADUR LTC 15030 can be doubled on thecondition that the coating has not been exposed to sunlight, to water/condensation, or to (other)contamination before recoating. Furthermore the surface of the first layer of HEMPADUR LTC 15030 must be free of any exudations. This is secured by keeping the conditions of application,drying and curing, i.e. such as ventilation, temperature, filmthickness and thinning within the abovedescribed limits. Note that excessive temperatures also must be avoided. If the maximum intervalis exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
Note: Do not put tanks into use before the coating is properly cured. Bleeding may occur into subsequentcoat. The effect is cosmetic only and has no negative influence on neither the anticorrosive nor anyantifouling properties of the final paint system.HEMPADUR LTC 15030 is for professional use only.
Issued: March 2002 - 1503019990CO012HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1503019990CO012
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15100CURING AGENT 95100
Description: HEMPADUR 15100 is a two-component, amine-adduct cured high build coal tar epoxy. Ithas excellent resistance to wear and impact as well as to sea water, waste water, fueloil and to aliphatic solvents and it resists spillage of mineral acids and aromatichydrocarbon solvents.It has a higher resistance to elevated temperature and temperature gradients thanpolyamide cured coal tar epoxies.
Recommended use: HEMPADUR 15100 is recommended for long time corrosion protection of structural steeland concrete in severe corrosive and immersed environments. Typical areas are steelburied in aggressive soil, pipelines of steel and concrete, tanks containing fuel orlubrication oil, drill water, drill mud, warm water (see below) or steel and concrete insewage treatment plants.
Service temperatures: Dry: In water (maximum temperature gradient 35°C/63°F): Maximum: 100°C/212°F 90°C/194°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Black/19990 Brown/60420Finish: Semi-gloss Semi-glossVolume Solids, %: 55 ± 1 55 ± 1Theoretical spreading rate: 2.8 m²/litre - 200 micron 2.8 m²/litre - 200 micron
110 sq.ft./US gallon - 8 mils 110 sq.ft./US gallon - 8 milsFlash point: 13°C/56°F 13°C/56°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallon 1.4 kg/litre - 11.4 lbs/US gallonSurface dry: 4 (approx.) hrs at 20°C/68°F (ISO 1517) 4 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 6 (approx.) hours at 20°C/68°F 6 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°F 7 days at 20°C/68°FV.O.C.: 390 g/litre - 3.2 lbs/US gallon 390 g/litre - 3.2 lbs/US gallon
Shelf life: 1 year (25°C/77°F) from time of production. Depending on storage conditions,mechanical stirring may be necessary before usage.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15100: Base 15109 : Curing agent 95100
4 : 1 by volumeApplication method: Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%)Pot life: 2 hours (20°C/68°F) 6 hours (20°C/68°F)Nozzle orifice: .023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 200 micron/8 milsIndicated film thickness, wet: 350 micron/14 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1510019990CO005
HEMPADUR 15100
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection, a suitable shopprimer may bePREPARATION: used. All damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For repair and touch-up use HEMPADUR 15100.Depending on severity of later in-service exposure, abrasive blast sweeping or full removal by blastcleaning of intact shopprimer is recommended before coating with HEMPADUR 15100.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment or acidetching. Seal surface with suitable sealer, e.g. HEMPADUR SEALER 05970 (furthermore, pleasesee Product Data Sheet for 05970).Repair and maintenance: Remove oil and grease etc. with suitable detergent. Remove salt andother contaminants by high pressure fresh water cleaning. Clean damaged areas thoroughly byabrasive blasting or power tool cleaning. Feather edges to sound and intact areas. Dust offresidues. Touch up to full film thickness.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit. Apply only on a
dry and clean surface with a temperature above the dew point to avoid condensation. In confinedspaces provide adequate ventilation during application and drying.
PRECEDING Steel: None, HEMPADUR 15590 or according to specification.COAT: Concrete: HEMPADUR SEALER 05970.
SUBSEQUENT: None.COAT:
REMARKS:Service temperature: The natural tendency of epoxy coatings to become more sensitive to mechanical damage and
chemical exposure at elevated temperatures is also reflected in this product. Film thicknesses: Maybe specified in another film thickness than indicated depending on purpose and area of use. This will alter spreading rate and may influence amount of thinning necessary, drying time andrecoating interval. Normal range is 125-200 micron/5-8 mils.
Recoating: Recoating intervals related to later conditions of exposure:(200 micron/8 mils dry film thickness of HEMPADUR 15100)
36 hours*36 hours*6 hours6 hours15100
Waterimmersion
AtmosphericSevere
Waterimmersion
AtmosphericSevere
Recoated with(Quality number only)
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
*The maximum recoating interval between the layers of HEMPADUR 15100 can be prolonged to 4 days at 20°C/68°F on thecondition that the coating has not been exposed to sunlight, water/condensation or to (other) contamination before recoating. Furthermore, the surface of the first coat of HEMPADUR 15100 must be free of any exudations. This is secured bykeeping the conditions of application, drying and curing, ie such as ventilation, temperature, film thickness and thinning within the described limits. Note that excessive temperature during application/curing also must be avoided.
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: HEMPADUR 15100 is for professional use only.
Issued: May 2001 - 1510019990CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1510019990CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15130BASE 15139 with CURING AGENT 95140
Description: HEMPADUR 15130 is a two-component, polyamide cured coal tar epoxy which provides avery hardwearing coating, highly resistant to seawater and mineral oils. Limitedresistance to a number of solvents. Aliphatic hydrocarbons may be discoloured.
Recommended use: As a self-priming coating system for long-term protection of steel and concrete inseverely corrosive environment. It provides excellent protection as a lining in crude andfuel oil tanks.If the exposure is acidic or a temperature gradient is developed, it is recommended touse HEMPADUR 15100. For application at lower temperatures, ie in the interval from-10°C/14°F to +10°C/50°F, it is recommended to use HEMPADUR LTC 15030.
Service temperatures: Dry: Maximum 90°C/194°F (See REMARKS overleaf)Ballast water service: Resists normal ambient temperatures at sea*Other water service: 45°C/113°F (no temperature gradient)Other liquids: Contact HEMPEL*Avoid long-term exposure to negative temperature gradients.
Certificates/Approvals: Approved by Lloyd’s Register of Shipping, American Bureau of Shipping, Bureau Veritasand Maritime Register of Shipping, Russia, as a recognized corrosion control coating.Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Approved as a ballast tank coating by Germanischer Lloyd, Germany.Classification B1 by Marintek, Norway.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Black /19990 Brown/60430Finish: Semi-gloss Semi-glossVolume solids, %: 70 ± 1 70 ± 1Theoretical spreading rate: 5.6 m²/litre - 125 micron 5.6 m²/litre - 125 micron
225 sq.ft./US gallon - 5 mils 225 sq.ft./US gallon - 5 milsFlash point: 25°C/77°F 25°C/77°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallon 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 6 (approx) hrs at 20°C/68°F (ISO 1517) 5 (approx) hrs at 20°C/68°F (ISO 1517)Dry to touch: 7-8 hours at 20°C/68°F 6-7 hours at 20°C/68°FFully cured: 7 days at 20°C/68°F 7 days at 20°C/68°FV.O.C.: 295 g/litre - 2.4 lbs/US gallon 300 g/litre - 2.4 lbs/US gallonShelf life: 1 year (25°C/77°F) from time of production. Depending on storage conditions,
mechanical stirring may be necessary before usage.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15130: Base 15139 : Curing agent 95140
4 : 1 by volumeApplication method: Airless spray Brush (touch-up)Thinner (max.vol.): 08450 (5%) 08450 (5%)Pot life: 2 hours (20°C/68°F) 6 hours (20°C/68°F)Nozzle orifice: .023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 125 micron/5 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1513019990CO014
HEMPADUR 15130
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection, if required, use a suitablePREPARATION: shopprimer. All damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For repair and touch-up, use HEMPADUR 15130.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment or acidetching. Seal surface with suitable sealer, eg HEMPADUR SEALER 05970 (furthermore, see theProduct Data Sheet for HEMPADUR SEALER 05970).Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly byabrasive blasting or power tool cleaning. As an alternative to dry cleaning, water jetting to sound,well adhering coat and/or to steel. Intact coat must appear with roughened surface after the waterjetting. By water jetting to steel, cleanliness shall be minimum WJ-2 (NACE No. 5/SSPC-SP 12). Aflash-rust degree of FR-2, preferably FR-1 (Hempel standard) is acceptable before application.Feather edges to sound and intact areas. Dust off residues. Touch up to full film thickness.
APPLICATION Use only where application and curing can proceed at temperatures above 5°C/41°F.CONDITIONS: The temperature of the paint itself should preferably be above 15°C/59°F. Best results are
obtained at surface and paint temperatures of 15-25°C/59-77°F. Apply only on a dry and cleansurface with a temperature above the dew point to avoid condensation.In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT None or as per specification depending on area of use.COAT:
REMARKS: Certificates are issued under the former quality number 1513.Weathering/ The natural tendency of epoxy coatings to become more sensitive to mechanical damage andService chemical exposure at elevated temperatures is also reflected in this product. temperatures:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 125-200 micron/5-8 mils.
Recoating: The recoating intervals in hours for HEMPADUR 15130 (on condition of sufficient ventilation):
732
432
1148
648
254½ d
144½ d
397 d
217 d
MinMax
HEMPADUR qualities
714
411
1122
616
2548
1436
3976
2154
MinMax
HEMPATEX HI-BUILD46330
200125200125200125200125DFT of HEMPADUR 15130
30°C/86°F20°C/68°F10°C/50°F5°C/41°FSurface temperture
The maximum recoating interval between layers of HEMPADUR 15130 can be doubled on thecondition that the coating has not been exposed to sunlight, water/condensation, or to (other)contamination before recoating. Furthermore the surface of the first layer of HEMPADUR 15130must be free of any exudations. This is secured by keeping the conditions of application, drying andcuring, i.e. such as ventilation, temperature, film thickness and thinning within the above describedlimits. Note that excessive temperatures also must be avoided. If the maximum recoating intervalis exceeded, roughening of the surface is necessary to ensure intercoat adhesion.
Notes: Bleeding may occur into subsequent coats. The effect is cosmetic only and has no negativeinfluence on neither the anticorrosive nor the antifouling properties of the system.HEMPADUR 15130 is for professional use only.
Issued: March 2002 - 1513019990CO014HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1513019990CO014
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S WASH PRIMER 15200CURING AGENT 99200
Description: HEMPEL'S WASH PRIMER 15200 is a two-component reinforced etch primer containingphosphoric acid and corrosion-inhibitive pigments.
Recommended use: As a pre-treatment primer for oxidative and physically drying paints on galvanised steeland non-ferrous metals such as non-anodized aluminium in mildly to moderatelycorrosive environment. May also be used as a primer for eg., oxidative drying paints onstainless steel. HEMUCRYL TI-COAT 18200 may be used as an alternative to HEMPEL'SWASH PRIMER 15200.
AVAILABILITY: Subject to confirmation
PHYSICAL CONSTANTS:Finish: FlatColour: YellowShade Number: 22280Volume Solids: 7%Theoretical Spreading Rate 14 m²/litre - 5 microns
571 sq.ft./US gallon - 0.2 milFlash Point: 12ºC/54ºF Abel-Pensky, closed cupSpecific Gravity: 0.9 kg/litre
7.5 lbs/US gallonDry to Touch: 15 (approx) minutes at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing Ratio: BASE : HEMPEL'S WASH PRIMER 15209 4 parts by volume
CURING AGENT : 99200 1 part by volumeApplication Method: Airless Spray Air Spray BrushThinner (max.vol.): 08570 (25%) 08570 (25%) 08570 (15%)Pot-Life: 8 hours (20ºC/68ºF)Nozzle Orifice: 0.017" - 0.019"Nozzle Pressure: 75 bar/1100 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08570
Indicated film thickness, wet: Not relevantIndicated film thickness, dry: 5 microns/0.2 mil (See REMARKS overleaf)
Recoating Interval: Min: 24 hours (20ºC/68ºF)Max: 3 days (20ºC/68ºF) (See REMARKS overleaf)
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1520022280
HEMPEL'S WASH PRIMER 15200
Surface Stainless Steel: Steam cleaning.Preparation:
Galvanised Steel: Steam cleaning, or ammonia wash.
Non-anodized Aluminium: Steam cleaning, or washing with non-alkaline, chlorine-free detergent.Possible remnants of detergent to be removed by scrubbing and fresh water hosing.
Application Minimum temperature 5ºC/41°F. Relative humidity between 25-85%. In confined spacesConditions: provide adequate ventilation during application and drying.
Subsequent Coat: HEMPALIN or HEMPATEX systems as per specification.
Remarks: Service Temperature: Dry service temperature maximum 80ºC/176ºF. Dry peak temperature:maximum 100ºC/212ºF.
Film Thickness: 5 microns dry film thickness is maximum recommended. Higher film thickness willresult in poor cohesion. Sub-divide the area to be coated into smaller areas corresponding to thetheoretical spreading rate of the can size used. A non-hiding, transparent yellow shade of thesurface painted must be the result.
Recoating: Maximum recoating interval refers to exterior surfaces. No maximum on interiorsurfaces.
VOC: The Volatile Organic Compounds are 715 gr/litre, 6.0 lbs/US gallon.
Note: HEMPEL'S WASH PRIMER 15200 is for professional use only.
Safety: Packings are provided with applicable safety labels which should be observed. In addition, nationalor local safety regulations should be followed.
As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paint with skinand eyes, should be avoided. Forced ventilation should be provided when applying paint in confinedspaces or stagnant air. Even when ventilation is provided respiratory, skin, and eye protection arealways recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1520022280
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SHOPPRIMER E 15280CURING AGENT 95270
Description: HEMPEL’S SHOPPRIMER E 15280 is a two-component epoxy polyamide primer,pigmented with zincphosphate rust-inhibiting pigments. It is designed for automatic sprayapplication as well as manual application.
Recommended use: 1. As a shopprimer for protection of blastcleaned steel plate and other structural steelduring the storage and building period.
2. As an intermediate coat on zinc silicates or metal sprayed surfaces to minimizepopping.
Service temperatures: Maximum, dry: 140°C/284°F.
Certificates/Approvals: Approved as a welding primer by Lloyd’s Register of Shipping and Det Norske Veritas.Tested for non-toxicity of welding fumes by the Danish Welding Institute andSchweisstechnische Lehr- und Versuchsanstalt, Germany.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50890Finish: FlatVolume solids, %: 22 ± 1Theoretical spreading rate: See REMARKS overleafFlash point: 0°C/32°FSpecific gravity: 1.1 kg/litre
9.2 lbs/US gallonDry to handle: 5-10 min. at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 640 g/litre - 5.3 lbs/US gallon (According to EPA Fed Ref Method 24)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15280: Base 15289 : Curing agent 95270
2 : 1 by volumeApplication method: Airless spray Air spray Brush (touch up)Thinner (max.vol.): 08570 (20%) 08570 (20%) 08450 (20%) (See REMARKS overleaf)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .021"Nozzle pressure: 75 bar/1100 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: Shopprimer: Sealer:
15 micron/0.6 mils 25 micron/1 mil(See REMARKS overleaf) (See REMARKS overleaf)
Indicated film thickness, wet: not relevant 125 micron/5 mils
Recoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1528050890CO003
HEMPEL’S SHOPPRIMER E 15280
SURFACE New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to cleaning degree
specified for final coating system, usually Sa 2½. Apply immediately after cleaning. All damagedshopprimer and contamination from storage and fabrication should be thoroughly cleaned prior torecoating. For repair and touch-up use primer specified for final coating system.GALVOSILS: HEMPADUR 15280 can be applied when the "almost-cured" stage of the GALVOSIL isreached. Consult APPLICATION INSTRUCTIONS for the relevant GALVOSIL. Remove oil and greaseetc. with suitable detergent. Remove salt and other contaminants by high pressure fresh watercleaning. After exposure to high humidity, zinc salts, "white rust", must be removed carefully byhigh pressure fresh water cleaning, if necessary combined with scrubbing with stiff nylon brushes.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit. Maximum
steel temperature approximately 45°C/113°F. For shopprimer application at temperatures aboveapp. 45°C/113°F special measures must be taken (See "Thinning" under REMARKS below). Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation. In confined spaces provide adequate ventilation during application and drying.
PRECEDING COAT: None or HEMPEL'S GALVOSIL qualities according to specification.
SUBSEQUENT COAT: As per specification.
REMARKS: Certificates are issued under the former quality number 1528.Recommended dry film thickness: 20-25 micron/0.8-1 mil measured on a smooth test panel.
Theoretical On steel abrasive blasted to a profile, Ra = 12½ micron/0.5 mils, equivalent to Rugotest No. 3,spreading rate: N10a-b, or Keane-Tator Comparator, 3.0 mils segments, or ISO Comparator Medium (G), the
indicated 15 micron/0.6 mils film thickness corresponds to approximately 25 micron/1 milmeasured on a smooth test panel (see special instructions for this procedure). Corresponding“theoretical” spreading rate will be 8.4 m²/litre (337 sq.ft./US gallon). On steel abrasive blasted toa profile, Ra = 6.3 micron/¼ mil, equivalent to Rugotest No. 3, N9a, or Keane-Tator Comparator,2.0 mils segments, or ISO Comparator Fine (G) the indicated 15 micron/0.6 mils film thicknesscorresponds to approximately 20 micron/0.8 mils measured on a smooth test panel (see specialinstructions for this procedure). Corresponding "theoretical" spreading rate will be 10.5 m²/litre(428 sq.ft./US gallon). As sealer: 8.8 m²/litre (359 sq.ft./US gallon). The shopprimer should beapplied in a uniform film thickness. Avoid dry spray and exaggerated film thicknesses. Usualspecified film thickness when used as a sealer is 25 micron/1 mil. The corresponding spreadingrate is 8.4 m²/l (337 sq.ft./US gallon).
Air Spray: Air spray is usually performed by having a low pressure (e.q. 10:1) piston pump pumping theshopprimer under constant re-circulation.
"Sealer": The use of HEMPEL'S SHOPPRIMER E 15280 as a "sealer coat" on zinc silicate is primarilyintended for a recoat interval between the "sealer coat" and the subsequent coat being of mediumlength. In the case of a short recoat interval of HEMPEL'S SHOPPRIMER E 15280 the zinc silicatemust be fully cured (see relevant Product Data Sheet) before HEMPEL'S SHOPPRIMER E 15280 isapplied. Observe that long time exposure of the not fully coated system (i.e. zinc silicate plusHEMPEL'S SHOPPRIMER E 15280 only) to humid environment may cause "white rust" to developbeneath the thin paint film of 15280.
Recoating No maximum recoat interval for adhesion, but dictated by gradual breakdown and damageInterval: during exposure and fabrication.Thinning: When applied at higher temperatures extra thinning or use of thinner with slower flash-off time may
be needed to secure proper paint film formation. It is a must that a homogenous and smooth paintfilm is obtained.When used as a "sealer", dilute with minimum 10% THINNER 08700 to obtain optimal antipoppingproperties.
Notes: Before recoating after exposure in contaminated environment, clean the surface thoroughly by highpressure water cleaning and allow to dry.HEMPEL’S SHOPPRIMER E 15280 is for professional use only.
Issued: October 1999 - 1528050890CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1528050890CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®PRIMER 15300CURING AGENT 95040
Description: HEMPADUR PRIMER 15300 is a two-component polyamide-cured epoxy primer containingzinc phosphate as corrosion inhibiting pigment. It cures to a strong and rust-preventingcoating.
Recommended use: As a primer or intermediate coat in container systems. May be used as a generalpurpose epoxy primer according to painting specification.
Service temperatures: Dry: In water (no temperature gradient):Maximum: 140°C/284°F 35°C/95°F
Certificates/Approvals: Approved as a welding primer by Lloyd's Register of Shipping.
Availability: Generally for container newbuildings only.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50890 - Grey/12170Finish: FlatVolume solids, %: 52 ± 1Theoretical spreading rate: 13.0 m²/litre - 40 micron
521 sq.ft./US gallon - 1.6 milsFlash point: 26°C/79°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 1 (app.) hour at 20°C/68°F (ISO 1517)Dry to touch: 2-3 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 455 g/litre - 3.8 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15300: Base 15309 : Curing agent 95040
4 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): 08450 (25%) 08450 (50%) 08450 (5%)Pot life: 8 hours (20°C/68°F) (airless spray)
8 hours (20°C/68°F) (brush)Nozzle orifice: .021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1530050890CO003
HEMPADUR PRIMER 15300
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection, if required, use a suitablePREPARATION: shopprimer. All damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For repair and touch-up use HEMPADUR PRIMER. Othermetals and light alloys: Thorough degreasing and removal of any salty contamination. Abrasivesweeping to create a suitable dense anchor profile.Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to St 3 (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance of HEMPADUR PRIMER 15300. Featheredges to sound intact areas. Dust off residues. Touch up to full film thickness. On pit-corrodedsurfaces, excessive amounts of salt residues may call for high pressure water jetting, wet abrasiveblasting, alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally, dryabrasive blasting again.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F.CONDITIONS: The temperature of the paint itself should be 15°C/59°F or above to secure proper application
properties. In confined spaces provide adequate ventilation during application and drying. Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation.
SUBSEQUENT HEMPATEX HI-BUILD 46370 or according to specification.COAT:
REMARKS: Certificate has been issued under the former quality number 1530.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreService sensitive to mechanical damage and chemical exposure at elevated temperatures is alsoTemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and will influence the amount of thinning necessary, drying time andrecoating interval. Normal range dry is 25-75 micron/1-3 mils.
Recoating: Recoating intervals:Minimum (primarily only relevant for container coatings): 20 minutes’ flash-off time for 40micron/1.6 mils mils HEMPADUR PRIMER 15300 when topcoated with designed containercoatings, epoxy, polyurethane, acrylic or CR types.The minimum recoating interval only applies in the case of forced ventilation, proper applicationand if the completed paint system is thoroughly dry before exposed to aggressive environments.Maximum: Recoating interval for non-immersion services is 24 hours for acrylic or CRs, 3 days forPUs and none for epoxies.In the case of long recoating intervals, a completely clean surface is mandatory to ensure intercoatadhesion. Any dirt, oil and grease to be removed with eg suitable detergent followed by highpressure fresh water cleaning. Salts to be removed by fresh water hosing. Any degraded surfacelayer, as a result of a long exposure period, must be removed as well. Water jetting may berelevant to remove any degraded surface layer and may also replace the above-mentioned cleaningmethods when properly executed. Consult HEMPEL for specific advice if in doubt.To check whether the quality of the surface cleaning is adequate, a test patch may be relevant.
Note: HEMPADUR PRIMER 15300 is for professional use only.
Issued: May 2000 - 1530050890CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1530050890CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®ZINC 15341CURING AGENT 95740
Description: HEMPADUR ZINC 15341 is a two-component polyamide cured zinc epoxy paint. It curesto a strong and corrosion resistant coating.
Recommended use: For on-line application on containers. May be used as a zinc epoxy primer for otherpurposes according to separate painting specification.
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red-grey/19830Finish: Semi-flatVolume solids, %: 48 ± 1Theoretical spreading rate: 12 m²/litre - 40 micron
481 sq.ft./US gallon - 1.6 milsFlash point: 30°C/86°FSpecific gravity: 1.7 kg/litre - 14.2 lbs/US gallonSurface dry: ½ (app.) hours at 20°C/68°F (ISO 1517)Dry to touch: 2 (app.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 470 g/litre - 3.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15341: Base 15349 : Curing agent 95740
3 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): 08450 (5%) 08450 (15%) 08450 (5%)Pot life: 8 hours (20°C/68°F) (airless spray)
8 hours (20°C/68°F) (brush)Nozzle orifice: .017"-.021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautions against possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1534119830CO001
HEMPADUR ZINC 15341
SURFACE New steel: Remove oil and grease etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2 ½, ISO 8501-1:
1988.For temporary protection, if required, use suitable zinc shopprimer. All damage of shopprimer andcontamination from storage and fabrication should be thoroughly cleaned prior to final painting. Forrepair and touch-up use HEMPADUR ZINC 15341.Maintenance: Remove oil and grease etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose materialpreferably by dry abrasive blasting. Minor areas may be power tool cleaned.
APPLICATION : Use only where application and curing can proceed at temperatures above 10°C/50°F.CONDITIONS The temperature of the paint itself should be 15°C/60°F or above to secure proper application
properties. In confined spaces provide adequate ventilation during application and drying. Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation.
PRECEDING None, or according to specification.COAT:
SUBSEQUENT HEMPADUR or HEMPATEX as per specification.COAT:
REMARKS:Note: If used as anticorrosive protection under insulation of high temperature equipment it is very
important that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises. May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoating interval. Normal range is30-50 micron/1.2-2 mils.
Recoating: Recoating intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.A completely clean surface is mandatory to ensure intercoat adhesion, especially at long recoatingintervals. Any dirt, oil, grease, and other foreign matter must be removed with suitable detergentfollowed by (high pressure) fresh water cleaning. In addition, scrubbing with a stiff brush may benecessary to remove zinc corrosion products (white rust).
Thinning: Use of THINNER 08570 will give a slightly faster flash-off than with THINNER 08450, but with agreater risk of dry-spray.
Note: HEMPADUR ZINC 15341 is for professional use only.
Issued: May 2000 - 1534119830CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1534119830CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to product data sheet
HEMPADUR®ZINC 15341CURING AGENT 95740
Film thickness: Depending on area of use the dry film thickness may vary between 30 micron/1.2 miland up to 50 micron/2 mils. This will alter amount of thinning needed, spreading rate,drying time and recoating interval as described below.
Indicated film thicknesses are as follows:
Primer, When used as a primer in container systems the dry film thickness is approx. 30-40container systems: micron/1.2-1.6 mils corresponding to 60-80 micron/2.4-3.2 mils wet film thickness.
Dilute 5-10% for airless spray.
Spreading rates: The film thickness and the spreading rate are inversely proportional. By controlling thespreading rate, a check of the film thickness can be made.
Theoretical spreading rate calculated for undiluted paint with:
30 micron/1.2 mils is 16.0 m²/litre or 641 sq.ft./US gallon50 micron/2 mils is 9.6 m²/litre or 385 sq.ft./US gallon
Thinners: Airless spray: HEMPEL'S THINNER 08450 or 08570. Lowest nozzle pressure should beused when highest amount of thinner is added. THINNER 08570 is used for fast settingat application in shops. (Be aware of increased risk of dry spray).
Air spray: HEMPEL'S THINNER 08450.Application by brush: HEMPEL'S THINNER 08450.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1534119830CO001
HEMPADUR ZINC 15341
Physical data Drying time and recoating interval vary with film thickness, curing agent used, drying/versus temperature: curing temperatures and later exposure conditions.
15341 (CURING AGENT 95740) in dry film thicknesses of 30-40 micron/ 1.2-1.6 Mils:
5 days1½ day
Not relevant
10 days3 days
Not relevant
25 days7½ days
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating withHEMPATHANE qualities
None15 days15 days
None30 days30 days
None75 days75 days
Atmospheric, mediumAtmospheric, severe**Immersion**
Interval for recoating withHEMPADUR qualities
2 days1 day
Not relevant
4 days2 days
Not relevant
10 days5 days
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with58030
8 hours6 hours
Not relevant
16 hours12 hours
Not relevant
40 hours30 hours
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with46330, 46370, 46410
MAXIMUM recoating interval related to later conditions of exposure:
1 hour1½ hours3 hours
2 hours3 hours6 hours
5 hours8 hours15 hours
Atmospheric, mediumAtmospheric, severeImmersion*
Interval for recoating withHEMPADUR and HEMPATHANE qualities
7 minutes30 minutesNot relevant
15 minutes1 hour
Not relevant
40 minutes2½ hours
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with46330, 46370, 4641058030
MINIMUM recoating interval related to later conditions of exposure:
204
307
1 hour18
Drying time, approx minutesCuring time, approx days
30°C/86°F20°C/68°F10°C/50°FSurface temperature
* NOT relevant for HEMPATHANE Qualities** Depending on actual local conditions, extended maximum recoating intervals may apply.
Please contact HEMPEL for further advice.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1534119830CO001
HEMPEL Product Data
ProductDataData
ProductHEMPADUR ZINC 15341
The minimum recoating intervals assume sufficient ventilation and correct application. Incase of forced ventilation and/or drying at higher temperatures sufficient"flash-off"time should be allowed for. Approximately 30 micron/1.6 mils dry filmthickness count for minimum 15 minutes flash-off (at 20°C/68°F), approximately 50micron/3 mils: minimum 30 minutes (approx).
The short minimum recoating intervals when overcoated with 46330, 46370 and 46410are provided only in case the finished paint system is through dry before exposure to the environment.
If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion.
Before recoating after exposure in contaminated environment, irrespective of recoatinginterval, clean the surface thoroughly e.g. by (high pressure) fresh water hosing andallow to dry.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: May 2000 - 1534119830CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1534119830CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR* ZINC 15350CURING AGENT 95350
Description: HEMPADUR ZINC 15350 is a two-component, zinc rich epoxy primer with a high zinccontent in the dry film. It cures to a hard wearing and highly weather-resistant coating.Offers cathodic protection of local mechanical damage.
Recommended use: 1. As a versatile, long-life primer on steel for epoxy, vinyl and acrylic coating systems in moderately to severely corrosive environments.
2. For shoppriming and on-line application on containers.
Service temperatures: Maximum, dry: 180°C/356°F, however depending on the subsequent coat.
Approvals, certificates: Approved as a low flame spread material by Nippon Kaiji-Kyokai, Japan and See-Berufgenossenschaft, Germany.Approved as a welding primer by Lloyds Register of Shipping.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:
Colours/Shade nos: Grey/19840Finish: FlatVolume solids: 48%Theoretical spreading rate: 12.0 m²/litre - 40 micron
481 sq.ft./US gallon - 1.6 milsFlash point: 30°C/86°FSpecific gravity: 2.6 kg/litre - 21.6 lbs/US gallonSurface dry: 0.3 (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 3/4 (approx.) hour at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 476 g/litre - 4.0 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:
Mixing for 15350: Base 15359 : Curing agent 953504 : 1 by volume
Application method: Airless spray Air spray BrushThinner (max.vol.): 08450 (5%) 08450 (15%) 08450 (5%) (See REMARKS overleaf)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .017"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 mils (See REMARKS overleaf)Indicated film thickness, wet 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1535019840CO011
HEMPADUR ZINC 15350
SURFACE Remove oil and grease thoroughly with suitable detergent. Remove salt and other contaminantsPREPARATION: by (high pressure) fresh water cleaning.
Abrasive blasting to Sa 2½, ISO 8501-1: 1988 with a sharp-edged surface profile corresponding toRugotest No. 3, BN10, Keane-Tator Comparator, 3.0 G/S or ISO Comparator, Medium (G).
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface must also be above this limit. The temperature of the paint itself should
be 15°C/59°F or above. Apply only on a dry and clean surface with a temperature above the dewpoint to avoid condensation. In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT According to specification.COAT:
REMARKS: Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryimportant that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence amount of thinning necessary, drying time, andrecoating interval. Normal range dry is 15-50 micron/0.6-2.0 mils.
Recoating: Recoating intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry. In addition, scrubbing with a stiff brush may benecessary to remove zinc corrosion products (white rust).
Thinning: Use of THINNER 08460 will give a slightly faster flash-off than with THINNER 08450, but with agreater risk of dry-spray when conventional air spray is used.
Note: HEMPADUR ZINC 1535 is for professional use only.
SAFETY: Handle with care. Before and during use, observe all safety labels on packaging and paintcontainers, consult HEMPEL Material Safety Data Sheets and follow all local or national safetyregulations. Harmful or fatal if swallowed; immediately seek medical assistance if swallowed. Avoidinhalation of possible solvent vapours or paint mist, as well as paint contact with skin and eyes.Apply only in well ventilated areas and ensure that adequate forced ventilation exists when applyingpaint in confined spaces or when the air is stagnant. Always take precautions against the risks offire and explosions.
Issued: September 1996 - 1535019840CO011HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1535019840CO011
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to product data sheet
HEMPADUR* ZINC 15350CURING AGENT 95350
Film thickness: Depending on area of use the typical dry film thickness may vary between 15 micron/0.6 mil and up to 50 micron/2 mils. This will alter amount of thinning needed,spreading rate, drying time and recoating interval as described below.
Primer: When used as a general purpose primer, dry film thickness is 40-50micron/1.6-2 mils corresponding to 75-100 micron/3-4 mils wet film thickness.Thinning is normally not necessary.
Spreading rates: The film thickness and the spreading rate are inversely proportional. By controlling thespreading rate, the film thickness can be controlled.
Theoretical spreading rate at40 micron/1.6 mils is 12.0 m²/litre or 481 sq.ft./US gallon50 micron/2 mils is 9.6 m²/litre or 385 sq.ft./US gallon
Thinner: Airless spray: HEMPEL'S THINNER 08450 or 08570. Lowest nozzle pressure should beused when highest amount of thinner is added. THINNER 0857 is used for fast settingat application in shops. (Be aware of increased risk of dry spray).
Air spray: HEMPEL'S THINNER 08450.
Application by brush: HEMPEL'S THINNER 08450.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1535019840C0011
HEMPADUR* ZINC 15350
Physical data Drying time and recoating interval vary with film thickness, drying/curing temperatureversus temperature: and later exposure conditions.
HEMPADUR ZINC 15350 in a dry film thickness of 50 micron/2 mils:
None36 hours
None3 days
None7½ days
AtmosphericMediumSevere
Interval for recoating withHEMPATHANE qualities
None15 days
None30 days
None75 days
AtmosphericMediumSevere
Interval for recoating withHEMPADUR qualities
2 days1 day
4 days2 days
10 days5 days
AtmosphericMediumSevere
Interval for recoating with58030
8 hours6 hours
16 hours14 hours
40 hours30 hours
AtmosphericMediumSevere
Interval for recoating with46370, 46410
Maximum recoating interval related to later conditions of exposure:
90 minutes3 hours
3 hours6 hours
7½ hours15 hours
AtmosphericMediumSevere
Interval for recoating withHEMPADUR and HEMPATHANE qualities
10 minutes30 minutes
15 minutes1 hour
40 minutes2½ hours
AtmosphericMediumSevere
Interval for recoating with46370, 46410, 58030
Minimum recoating inerval related to later conditions of exposure:
40 minutes4 days
60 minutes7 days
2 hours14 days
Drying time, approxCuring time, approx
30°C/86°F20°C/68°F10°C/50°FSurface temperature
The above minimum recoating intervals assume sufficient ventilation and correctapplication. In case of forced ventilation and/or drying at higher temperatures, sufficient"flash-off" time should be allowed for. For approx 30 micron/1.6 mils minimum 15minutes, for approx 50 micron/3 mils minimum approx 30 minutes.
The short minimum recoating intervals when overcoated with 4637 and 4641 areprovided only in case the finished paint system is through dry before exposure to theenvironment.
If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion.
Before recoating after exposure in contaminated environment, irrespective of recoatinginterval, clean the surface throughly by eg (high pressure) fresh water hosing and allowto dry.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1535019840C0011
HEMPEL Product Data
ProductDataData
ProductHEMPADUR* ZINC 15350
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Issued: September 1996-1535019840C0011HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1535019840C0011
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®ZINC 15360CURING AGENT 95740
Description: HEMPADUR ZINC 15360 is a two-component polyamide cured zinc-rich epoxy primer. Itcures to a hard wearing and highly weather-resistant coating. Offers cathodic protectionof local mechanical damage.
Recommended use: For on-line application on containers. Can be used as a zinc-rich epoxy primer for otherpurposes according to separate painting specification.
Service temperatures: Maximum, dry: 160°C/320°F, however depending on the subsequent coat.
Certificates/Approvals: Approved as a welding primer by Lloyd's Register of Shipping.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red-grey/19830Finish: Semi-flatVolume solids, %: 50 ± 1Theoretical spreading rate: 12.5 m²/litre - 40 micron
501 sq.ft./US gallon - 1.6 milsFlash point: 30°C/86°FSpecific gravity: 2.3 kg/litre - 19.2 lbs/US gallonSurface dry: 30 minutes at 20°C/68°F (ISO 1517)Dry to touch: 2 (app.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 455 g/litre - 3.8 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15360: Base 15369 : Curing agent 95740
4 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): 08450 (30%) 08450 (50%) 08450 (5%)Pot life: 8 hours (20°C/68°F) (airless spray)
8 hours (20°C/68°F) (brush)Nozzle orifice: .017"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1536019830CO005
HEMPADUR ZINC 15360
SURFACE Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminants byPREPARATION: (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½ with a sharp-edged surface profile
corresponding to Rugotest No. 3, BN9a, Keane-Tator Comparator, 2.0 G/S or ISO Comparator,Medium (G).
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F TheCONDITIONS: temperature of the surface must also be above these limits, respectively.
The temperature of the paint itself should be 15°C/59°F or above. Apply only on a dry and cleansurface with a temperature above the dew point to avoid condensation. In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT According to specification.COAT:
REMARKS: Certificate has been issued under the quality number 1536.Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryimportant that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence amount of thinning necessary, drying time, andrecoating interval. Normal range is 15-50 micron/0.6-2.0 mils.
Recoating: Recoating intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry. In addition, scrubbing with a stiff brush may benecessary to remove zinc corrosion products (white rust).
Note: HEMPADUR ZINC 15360 is for professional use only.
Issued: May 2000 - 1536019830CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1536019830CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to product data sheet
HEMPADUR®ZINC 15360CURING AGENT 95740
Film thickness: Depending on the area of use the typical dry film thickness may vary between 15micron/0.6 mil and up to 50 micron/2 mils. This will alter amount of thinning needed,spreading rate, drying time and recoating interval as described below. Indicated film thicknesses are as follows:
Shopprimer, Containers: When used as a shopprimer in container systems a typical dry film thickness is 15micron/0.6 mil. Dilute 100-150% for airless spray, corresponding wet film thickness60-75 micron/2.4-3 mils. (Note: In the case of a high degree of thinning, the mixture isto be stirred constantly and recirculate until all paint has been used).
Primer, When used as a primer in container systems the dry film thickness is approx. 30-40container systems: micron/1.2-1.6 mils corresponding to 60-80 micron/2.4-3.2 mils wet film thickness.
Dilute 5-10% for airless spray.
Spreading rates: The film thickness and the spreading rate are inversely proportional. By controlling thespreading rate, a check of the film thickness can be made.
Theoretical spreading rate calculated for undiluted paint:
15 micron/0.6 mil is 33.3 m²/litre or 1337 sq.ft./US gallon30 micron/1.2 mils is 16.7 m²/litre or 668 sq.ft./US gallon50 micron/2 mils is 10.0 m²/litre or 401 sq.ft./US gallon
Thinner: Airless spray: HEMPEL'S THINNER 08450 or 08570. Lowest nozzle pressure should beused when highest amount of thinner is added. THINNER 08570 is used for fast settingat application in shops. (Be aware of increased risk of dry spray).
Air spray and application by brush: Usually only HEMPEL'S THINNER 08450.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1536019830CO004
HEMPADUR ZINC 15360
Physical data Drying time and recoating interval vary with film thickness, drying/curing temperature andversus temperature: later exposure conditions.
HEMPADUR ZINC 15360 in a dry film thicknesses of 30-40 micron/1.2-1.6 mils:
5 days1½ day
Not relevant
10 days3 days
Not relevant
25 days7½ days
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating withHEMPATHANE qualities
None15 days15 days
None30 days30 days
None75 days75 days
Atmospheric, mediumAtmospheric, severe**Immersion**
Interval for recoating withHEMPADUR qualities
2 days1 day
Not relevant
4 days2 days
Not relevant
10 days5 days
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with58030
8 hours6 hours
Not relevant
16 hours12 hours
Not relevant
40 hours30 hours
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with46330, 46370, 46410
MAXIMUM recoating interval related to later conditions of exposure:
1 hour1½ hours3 hours
2 hours3 hours6 hours
5 hours8 hours
15 hours
Atmospheric, mediumAtmospheric, severeImmersion*
Interval for recoating withHEMPADUR and HEMPATHANE qualities
7 minutes30 minutesNot relevant
15 minutes1 hour
Not relevant
40 minutes2½ hours
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with46330, 46370, 4641058030
MINIMUM recoating interval related to later conditions of exposure:
204
307
1 hour18
Drying time, approx minutesCuring time, approx days
30°C/86°F20°C/68°F10°C/50°FSurface temperature
* NOT relevant for HEMPATHANE Qualities** Depending on actual local conditions, extended maximum recoating intervals may apply.
Please contact HEMPEL for further advice.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1536019830CO004
HEMPEL Product Data
ProductDataData
ProductHEMPADUR ZINC 15360
The minimum recoating intervals assume sufficient ventilation and correct application. Incase of forced ventilation and/or drying at higher temperatures sufficient "flash-off"timeshould be allowed for. For approx.15 micron/1 mil dry film thickness count for minimum10 minutes flash-off (at 20°C/68°F), for approximately 30 micron/1.6 mils minimum 15minutes, for approximately 50 micron/3 mils minimum approximately 30 minutes.
The short minimum recoating intervals when recoated with 46330, 46370 and 46410are only provided in case the finished paint system is through dry before exposure to theenvironment.
If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion.
Before recoating after exposure in contaminated environment, irrespective of recoatinginterval, clean the surface thoroughly e.g. by (high pressure) fresh water hosing andallow to dry. It is very important that any possible zinc salts, "white rust", areremoved. Scrubbing with a stiff brush and plenty of water may be required.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: May 2000 - 1536019830CO004HEMPEL’S MARINE PAINTS A/S.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1536019830CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15400BASE 15409 with CURING AGENT 95100
Description: HEMPADUR 15400 is a two-component, amine adduct cured epoxy paint, which cures toa coating with excellent resistance to a wide range of chemicals as tabulated in separateCARGO PROTECTION GUIDE.
Recommended use: As a tank lining.
Service temperatures: Dry: In water (no temperature gradient):Maximum: 140°C/284°F 50°C/122°FWet service temperatures, other liquids:Consult the corresponding CARGO PROTECTION GUIDE.
Certificates/Approvals: Complies with Section 175.300 of U.S. Federal Regulations in respect of carriage of dryand wet foodstuffs.Approved by Lloyd's Register of Shipping as a recognized corrosion control coating.Approved by Kuwaiti, Chinese and Norwegian authorities for fresh water tanks.Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Tested for non-toxicity of welding fumes by the Danish Welding Institute.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000 - Light red/50900Finish: Semi-flatVolume solids, %: 48 ± 1Theoretical spreading rate: 6.0 m²/litre - 80 micron
241 sq.ft./US gallon - 3.2 milsFlash point: 26°C/79°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: 3 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 8-10 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 465 g/litre - 3.9 lbs/US gallonShelf life: 1 year (25°C/77°F) from time of production. Depending on storage conditions,
mechanical stirring may be necessary before usage.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15400: Base 15409 : Curing agent 95100
4 : 1 by volumeApplication method: Airless spray Brush (touch-up)Thinner (max.vol.): 08450 (5%) (See APPLICATION INSTRUCTIONS) 08450 (5%)Pot life: 2 hours (20°C/68°F) 4 hours (20°C/68°F)Nozzle orifice: .021"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 80 micron/3.2 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 10 hours (20°C/68°F)Recoat interval, max: 21 days (20°C/68°F)
Safety: Handle with care. Before and during use, observe all safety labels on packaging and paint containers, consult HEMPEL Material Safety Data Sheets and follow all local or national safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPADUR 15400
SURFACE Abrasive blasting to near white metal Sa 2½ with a surface profile corresponding to Rugotest No.PREPARATION: 3, BN10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator, Rough Medium (G). (Please do
also see Notes under REMARKS).
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F.CONDITIONS: A special curing agent 95990 may be available for curing between 5°C/41°F and 10°C/50°F if
required, see Application Instructions. The temperature of the surface and that of the paint itselfmust also be above this limit. Optimal spraying properties are obtained at paint temperatures of15-25°C/59-76°F. Apply only on a dry and clean surface with a temperature above the dew point toavoid condensation. Relative humidity max. 80%, preferably 40-60%. In confined spaces provideadequate ventilation during application and drying.
PRECEDING None, or as per specification.COAT:
SUBSEQUENT None, or as per specification.COAT:
REMARKS: Certificates are issued under the former quality number 1540.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is80-125 micron/3.2-5 mils.
Recoating: If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Curing: Do not put tanks into service until the paint system is completely cured - consult the correspondingCARGO PROTECTION GUIDE and APPLICATION INSTRUCTIONS.In the case of coating potable water tanks, it is a must that all solvents are evaporated and thatthe system is fully cured before the tanks are taken into use. It is furthermore recommended to fillthe tank twice with water, each time for a period of not less than 24 hours, and finally flush withfresh water.
Notes: This datasheet outlines the main guidelines and recommendations. For details the correspondingPAINTING SPECIFICATION must be consulted and strictly adhered to during execution of the work.The CARGO PROTECTION GUIDE and the corresponding PAINTING SPECIFICATION may be tailored tomeet other conditions than stipulated above. Such adjustments may include the degree of surfacepreparation, conditions of application, dry film thickness, and recoating interval.HEMPADUR 15400 is for professional use only.
Issued: March 2002 - 1540010000CO012HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®1540015400: BASE 15409 with CURING AGENT 9510015402: BASE 15409 with CURING AGENT 95990
Scope: These application instructions cover surface preparation, application equipment, andapplication of HEMPADUR 15400 as a tank coating.
The following are general rules, which may be supplemented with more detaileddescriptions when needed, for instance for major newbuildings/new constructions orextensive repair jobs.
Steel work: All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in weldings seams, undercuts, cracks,etc. should be avoided. If found, they must be remedied by welding and/or grinding.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specified filmthickness can be build-up on all surfaces. The radius of the rounding should beapproximately 1-2 mm.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988. Any laminations must be removed.
All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface preparation: Prior to abrasive blast cleaning of the steel, remove oil, grease, salts and othercontamination with a suitable detergent followed by (high pressure) fresh water hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing oftanks to be removed by fresh water and scrubbing with stiff brushes. Control for absenceof contamination according to separate guidelines.
On repair jobs, a rough blasting to remove all loosely adhering materials may be requiredbefore degreasing/washing is carried out.
Old steel: Even after a very thorough tank cleanings, pits may typically containcontamination in the form of remnants of old cargoes as well as water soluble salts. Forthis reason, repeated detergent washing plus abrasive blasting may be necessary:
After the first blasting, a very thorough vacuum cleaning is carried out in order to see ifany "cargo bleeding" occurs as well as controls for water soluble salts are made.Reference is made to separate instructions. Special care should be taken in evaluatingpitted areas.
To obtain full chemical resistance according to the CARGO PROTECTION GUIDE, the steelsurface must be abrasive blast cleaned according to ISO 8501-1: 1988, Sa 2½.
The resulting surface profile must be equivalent to Rugotest No. 3, min. BN 10,Keane-Tator Surface Comparator, G/S min. 3.0 or ISO/DIS 8503/1 rough MEDIUM (G).
Use steel grit, aluminium silicate or similar sharp-edged abrasives of a good quality freeof foreign matters, soft particles, and the like. Control for possible contaminationaccording to separate guidelines.
Steel grit with particle sizes of 0.2 - 1.2 mm or aluminium silicate of 0.4 - 1.8 mm willusually create the desired surface profile when the air pressure measured at the nozzle is 6 - 7 bar/85 -100 psi.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPADUR 15400The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
When the abrasive blasting is completed, remove residual grit and dust by vacuumcleaning. Abrasive particles not removed by vacuum cleaning are to be removed bybrushing with clean brushes followed by vacuum cleaning.
The importance of systematic working must be stressed when blasting. Poorly blastedareas covered with dust are very difficult to locate during the blast inspection made afterthe rough cleaning.
Shopprimed and previously painted surfaces: Existing coating materials to becompletely removed. Depending on the type of shopprimer and the requested chemicalresistance, the shopprimer should be removed completely or partly. Reference is made to HEMPEL's CARGO PROTECTION GUIDE/tank coating specification.
Note: Degree of steelwork finish and surface preparation are more detailed describedin HEMPEL’s Technical Standard for Tank Coating Work.
Application equipment: HEMPADUR 15400 is to be applied by airless spray equipment. Stripe coating and minorrepairs can be carried out by brushing.
Airless spray equipment: A large pump is preferred, with a pump capacity of 8-12Litres/minute.
Pump ratio: Min. 45:1Nozzle orifice: .018”-.021"Nozzle pressure: 200 bar (2900 psi)Hoses: To avoid excessive loss of pressure in long hoses, hoses with an
internal diameter of up to 0.5" can be used
(Spray data are indicative and subject to adjustment).
Thinning: If required: max. 10% of THINNER 08450, possibly higher if tendency to dust-spray willrequire more thinning eg at higher temperatures. Thinning should only be at the requiredlevel to avoid possible risk of solvent entrapment.
Only add thinner to the mixed paint.
Cleaning of equipment: The whole equipment to be cleaned thoroughly with HEMPEL’S TOOL CLEANER 99610after use.
Mixing, pot life: a. Mix the entire content of corresponding base and curing agent packings. If it isnecessary to mix smaller portions, this must be done properly by either weighingbase and curing agent in the prescribed weight ratio: 87 parts by weight of base and 13 parts by weight of curing agent or by volume: 4.0 parts by volume base and 1.0 parts by volume curing agent.
b. Stir the mixed paint thoroughly by means of a clean mechanical mixer until ahomogeneous mixture is obtained.
c. Allow the mixed paint to pre-react before application, see table below.
d. Use all mixed paint before the pot life is exceeded. The pot life depends on thetemperature of the paint as shown in table below (valid for a 20 litres can):
CURING 95100:
512
101½3
1524
2535
(30)(4)6
Induction time, minutesPot life, hours, airless SprayPot life, hours, brush
30°C/86°F2)25°C/77°F20°C/68°F15°C/59°F1)(10°C/50°F1)Temperature of mixed paint
1) At paint temperatures below 15°C/59°F the viscosity can be too high for airless spray application.2) Temperatures at 30°C/86°F and above should be avoided due to an enhanced risk of dry-spray and poor film
formation.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 15400
CURING 95990:
251½4
(30)(2)4
(35)(3)4
Induction time, minutesPot life, hours, airless SprayPot life, hours, brush
15°C/59°F1)(10°C/50°F1)(5°C/41°F1)Temperature of mixed paint
1) At painttemperatures below 15°C/59°F the viscosity can be too high for airless spray application.
Application procedure: The first full coat is usually applied immediately after vacuum cleaning. The first stripecoat afterwards. The final dry film thickness of the three coat system must be between240-500 micron.
The wet film thickness must be 175-200 micron and must be measured regularly.
Film-build/continuity: With this tank coating, it is of special importance that acontinuous, pinhole-free paint film is obtained at application of each coat. An applicationtechnique must be adopted to ensure good film formation on all surfaces and no dustspray. It is very important to use nozzles of the correct size, ie not too big. Select smallnozzles for spray application of complicated structures, while bigger nozzles may beused for regular surfaces. A proper, uniform distance of the spray gun to the surface,30-50 cm, should be aimed at. To obtain good and steady atomising, the viscosity of thepaint must be suitable and the spray equipment must be sufficient in output pressureand capacity. At high working temperatures, use of extra thinner may be necessary toavoid dust-spray.
The paint layer must be applied homogeneously and as close to the specification aspossible. The consumption of paint must be controlled and heavy layers must beavoided because of the risk of sags and cracks and solvent retention.
Furthermore, great care must be taken to cover edges, openings, rear sides of stiffenersetc. Thus, on these areas a stripecoat will usually be necessary.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, must be remedied.
Note: In the case of old, pit-corroded steel, application of a diluted, extra first coat isrecommended to obtain better "penetration" in the fine pits. For this purpose, it isrelevant to dilute approximately 10%. Application by brush is recommended and filmthickness so low that the surface is "saturated" only.
Stripe coating: All places difficult to cover properly by spray application should be stripe coated twice bybrushing. The first stripe coat is applied either before or after the first full coat. Thesecond stripe coat is most typically applied after the second full coat. Which procedureto follow depends on the actual working conditions. A sprayed coat using small spraynozzles with a narrow angle may substitute the second brush-applied stripe coat,however, lightening holes and similar, plus possible undercuts and similar will stilldemand brush- applied stripe coating.
Micro climate: The actual climate conditions at the substrate during application:
The minimum surface temperature is 10°C/50°F when using CURING AGENT 95100,5°C/41°F when using CURING AGENT 95990.
The maximum surface temperature should preferably be below approximately30°C/86°F. In a warm climate it is recommended to carry out application duringnight-time. Application at high temperatures, up to approximately 40°C/104°F, ispossible, but extra care must be taken to avoid poor film formation and excessivespraydust. Extra thinning may also be necessary.
The steel temperature must be above the dew point. As a rule of thumb, a steeltemperature which is 3°C/5°F above the dew point can be considered safe.
In confined spaces, supply an adequate amount of fresh air during application and dryingto assist the evaporation of solvent.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPADUR 15400
Drying and curing, In a dry film thickness of 80 micron, with a steel temperature of 20°C/68°F, a relative Ventilation: air humidity of maximum 80% and adequate ventilation, HEMPADUR 15400 will be dry to
touch after 8-10 hours. For similar drying conditions, the paint film will accept light trafficafter approximately 24 hours.
Correct film formation depends on an adequate ventilation during drying.
A good guideline for tank coating work is to ventilate to a calculated 10% of LEL duringapplication and until the coating is dry.
One litre undiluted HEMPADUR 15400 gives off in total 123 litres solvent vapour until itis completely dry.
The lower explosive limit, LEL, is 0.5%.
To reach a common safety requirement of 10% LEL, the theoretical ventilationrequirement is 250 m³ per litre paint.
Because solvent vapours are heavier than atmospheric air, effective ventilation requiresforced ventilation with exhaust from the lowest part of the tank.
During the following period until full curing a few air shifts per hour will suffice. Takeactions to avoid "pockets" of stagnant air.
Please contact HEMPEL for further advice.
Actual safety precautions may require stronger ventilation.
Curing time: Provided that adequate ventilation, recommended relative humidity, specified filmthickness, and recommended minimum recoating interval are kept, the following curingtimes are valid:
CURING AGENT 95100:
(2½ days)
(2½ days)
3½ days
3½ days
5 days
5 days
7 days
7 days
11 days
11 days
18 days
18 days
Curing timeFilling of tanks with water can betolerated after
(35°C/95°F)*30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
*Avoid application at elevated temperatures to avoid dry-spray and poor film formation.
CURING AGENT 95990:
11 days
11 days
18 days
18 days
25 days
25 days
Curing timeFilling of tanks with water can betolerated after
15°C/59°F10°C/50°F5°C/41°FSteel temperature
Recoating intervals: Provided observance of the above stated ventilation and relative humidity the followingrecoating intervals in relation to the (steel) temperature are valid:
CURING AGENT 95100:
4 hours10 days
5 hours14 days
7 hours18 days
10 hours21 days
14 hours25 days
30 hours28 days
MinimumMaximum
35°C/95°F30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
CURING AGENT 95990:
14 hours25 days
30 hours28 days
45 hours35 days
MinimumMaximum
15°C/59°F10°C/50°F5°C/41°FSteel temperature
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 15400
The maximum relative humidity before and between the coats should not exceed 80%and the steel temperature should always be above the dew point, in practice minimum3°C/5°F above the dew point.
The maximum intervals assume that the film formation is of good quality and without dryspray and that no kind of surface contamination exists except contamination which canbe removed completely by vacuum cleaning. Furthermore, the coating must not havebeen exposed to direct sunlight for more than maximum 2 days.
Conditions for Dry spray is not acceptable as this will reduce the protective characteristics of thepaint application work: paint and make later tank cleaning difficult. Dry spray can be avoided by using adequate
stagings, spraying equipment and methods.
Hold the spray gun at a right angle to and about 30-50 cm/1-1½ foot from the surfacemaking even parallel passes at a rate to produce the specified wet film thickness as perspecification.
Avoid dry spray (overspray creating excessive paint mist), e.g. by using a smaller fanangle, and the lowest possible pressure. A small fan angle should also be used, if sprayapplication is used, for "stripe coating" of for instance reverse sides of stiffeners. Each layer must be applied homogeneously and as near above the specification of 80micron dry film thickness as possible. The consumption of paint must be controlled, andheavy layers must be avoided because of the risk of sagging, cracks and solventretention.
Surface irregularities such as dry spray, sagging, exaggerated thickness or embeddeddust or abrasives will have to be remedied.
If sandpapering between layers, for instance on the bottom, is needed, great care mustbe taken to avoid damage of otherwise intact surfaces. When using mechanical meansonly lightweight equipment should be used, orbital sander is recommended. Yet, avoidsandpapering on top of welds or irregularities or near to vertical surfaces.
The finished coating must appear as a homogeneous surface without pores, runners orcontamination of any kind.
For the standard specification following applies to the dry film thickness:
The minimum dry film thickness is 240 micron, the maximum thickness to be aimed atis approximately 500 micron. The minimum dry film thickness is evaluated according tothe "80-20" rule, i.e. no more than 20% of the total number of individual measurementsmust be lower than the minimum dry film thickness, and the lowest individualmeasurement must be at least 80% of the minimum dry film thickness, ie 192 micron.Dry film thickness control is not to be carried out within the first 24 hours afterapplication of final coat (20°C, sufficient ventilation). The measurement must be carriedout using an electromagnetic dry film thickness gauge calibrated with shims placed on asmooth steel substrate. The maximum dry film thickness can be evaluated according tothe "80-20" rule.
Repairs: It is of great importance that all damage to the coating is repaired.
Repair shall be started up as soon as possible. Repair of mountings for stagings, etc.must take place in connection with the dismantling of the stagings, the tempo of whichshall be adjusted to the touch-up procedure.
It is important that the repaired areas, as well as the rest of the coated areas, are fullycured before the tank is taken into use or washed by the tank cleaning system.
The extent of damage to the coating can be evaluated by a sea water test. Wash thetanks with clean sea water by means of the tank cleaning machines until profiles and/orheating coils on tanktop is covered. Allow the water to stay for minimum 3 days, afterwhich period the tank is emptied and cleaned with clean fresh water to remove salts.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
HEMPADUR 15400
The repair process: General: Before mechanical treatment is started, surfaces to be repaired have to becleaned for any salts and other contamination.
Areas less than 5 x 5 cm.The surface preparation can be executed by grinding to a clean rough metal surface,feathering edges of intact coating and slightly sanding the adjacent surface.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up by brush to full film thickness with minimum 4 coats of HEMPADUR 15400.
Areas up to 1 square metreThe surface preparation must be executed by vacuum blasting or open nozzle blasting so that the steel has a proper roughness and a cleanliness to Sa 2½-3 according toISO 8501-1:1988. The overlapping zone must be sanded or sweep blasted to ensure agood adhesion of the new paint.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up by brush to full film thickness with minimum 4 coats or by spray 3 coatsHEMPADUR 15400.
Areas more than 1 square metre or areas where several damaged spots areconcentrated.Treatment: Repeat the original specification.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: March 2002 - 1540010000CO012HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 6 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1540010000CO012
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15500CURING AGENT 97580
Description: HEMPADUR 15500 is a two-component, amine adduct cured phenolic epoxy (novolac)paint, which cures to a coating with excellent resistance to a wide range of chemicals astabulated in separate CARGO PROTECTION GUIDE.
Recommended use: As a tank lining.
Service temperatures: Dry: In seawater (no temperature gradient):
Maximum: 160°C/320°F 50°C/122°FWet service temperatures, other liquids:Consult the corresponding CARGO PROTECTION GUIDE.
Certificates/Approvals: Approved by Lloyd's Register of Shipping and Maritime Register of Shipping, Russia, asa recognized corrosion control coating. Complies with Section 175.300 of the Code of Federal Regulations in respect of carriageof foodstuffs (FDA) for tanks larger than 2006 m³/530,000 US gallon.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Off-white/11630 - Light red/50900Finish: FlatVolume solids, %: 68 ± 1Theoretical spreading rate: 6.8 m²/litre - 100 micron
273 sq.ft./US gallon - 4 milsFlash point: 26°C/79°FSpecific gravity: 1.7 kg/litre - 14.2 lbs/US gallonSurface dry: 2-3 hrs at 20°C/68°F (ISO 1517)Dry to touch: 6 (approx.) hours at 20°C/68°FFully cured: 10 days at 20°C/68°F (See REMARKS overleaf)V.O.C.: 325 g/litre - 2.7 lbs/US gallon
Shelf life: 1 year (25°C/77°F) from time of production. Depending on storage conditions,mechanical stirring may be necessary before usage.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15500: Base 15509 : Curing agent 97580
8.9 : 1.1 by volume93.8 : 6.2 by weight
Application method: Airless spray Brush (touch-up)Thinner (max.vol.): 08450 08450 (See APPLICATION INSTRUCTIONS)Pot life: 3 hours (20°C/68°F)Induction time: 15 minutes (20°C/68°F) (see REMARKS overleaf)Nozzle orifice: .018"-.021"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 150 micron/6 milsRecoat interval, min: 36/24 hours (20°C/68°F)Recoat interval, max: 21 days (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPADUR 15500
SURFACE For optimum performance to the full range of chemicals in accordance with the main CARGOPREPARATION: PROTECTION GUIDE, abrasive blasting to very near white metal Sa 2½-3 with a surface profile
corresponding to Rugotest No. 3, BN10, Keane-Tator Comparator 3.0 G/S, or ISO ComparatorRough Medium (G).Consult separate APPLICATION INSTRUCTIONS.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. The steelCONDITIONS: temperature must never drop below this limit until full curing has taken place. The temperature of
the paint itself must be above 15°C/59°F, best results are obtained at 17-23°C/62-73°F. Relativehumidity max. 80%, preferably 40-60%. Apply on a dry and clean surface with a temperature abovethe dew point to avoid condensation. Provide adequate ventilation during application and drying inconfined spaces.Consult separate APPLICATION INSTRUCTIONS.
PRECEDING None.COAT:
SUBSEQUENT None.COAT:
REMARKS: Some of the certificates have been issued under the former quality number 1550.Film thicknesses: Minimum total dry film thickness for the system is 300 micron/12 mils. May be specified in higher
film thickness than indicated depending on purpose and area of use. This will alter spreading rateand influence drying time. For further information about film thicknesses, see separateAPPLICATION INSTRUCTIONS.
Recoating: Roughening of the surface is necessary if the maximum recoating interval is exceeded. Mixing: The thoroughly mixed BASE and CURING AGENT must be prereacted before application (15 minutes
at 20°C/68°F), at other temperatures, please see APPLICATION INSTRUCTIONS.Thinning: Keep thinning at an absolute minimum. Do not dilute the components separately - only the mixture.Curing: Resistance to the widest range of cargoes is provided by additional heat curing, see APPLICATION
INSTRUCTIONS and CARGO PROTECTION GUIDE.
Note: HEMPADUR 15500 is for professional use only.
Issued: September 2001 - 1550011630CR006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®15500CURING AGENT 97580
Scope: These application instructions cover surface preparation, application equipment, andapplication of HEMPADUR 15500 as a tank coating.
The following are general rules, which may be supplemented with more detaileddescriptions when needed, for instance for major newbuildings/new constructions orextensive repair jobs.
Steel work: All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in weldings seams, undercuts, cracks,etc. should be avoided. If found, they must be remedied by welding and/or grinding.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specified filmthickness can be build-up on all surfaces. The radius of the rounding should be minimum 2 mm.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988. Any laminations must be removed.
All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface preparation: Prior to abrasive blast cleaning of the steel, remove oil, grease, salts and othercontamination with a suitable detergent followed by high pressure fresh water hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing oftanks to be removed by fresh water and scrubbing with stiff brushes.
Control for absence of contamination according to separate guidelines.
On repair jobs, a rough blasting to remove all loosely adhering materials may be requiredbefore degreasing/washing is carried out.
Old steel: Even after a very thorough tank cleanings, pits may typically containcontamination in the form of remnants of old cargoes as well as water soluble salts. Forthis reason, repeated detergent washing plus abrasive blasting may be necessary. Afterthe first blasting, a very thorough vacuum cleaning is carried out in order to see if any"cargo bleeding" occurs as well as controls for water soluble salts (reference is made toseparate instructions) are made. Special care should be taken in evaluating pitted areas- ask for special guidelines.
Grit blast to min Sa 2½, ISO 8501-1:1988.
To obtain full chemical resistance according to the CARGO PROTECTION GUIDE, the steelsurface must be abrasive blast cleaned according to ISO 8501-1:1988, very near towhite metal Sa 2½-Sa 3. In practice, this requirement is to be understood as whitemetal Sa 3 at the moment of abrasive blasting, but allows a slight reduction at themoment of paint application.
The resulting surface profile must be equivalent to Rugotest No. 3, min. BN 10,Keane-Tator Surface Comparator, G/S min. 3.0 or ISO/DIS 8503/1 rough MEDIUM (G).
Use steel grit, aluminium silicate, or similar sharp edged abrasives of a good quality freeof foreign matters, soft particles, and the like. Control for possible contaminationaccording to separate guidelines.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPADUR 15500
In case steel grit is used this must furthermore be controlled so that a proper grain size distribution is maintained.
Steel grit with particle sizes of 0.2 - 1.2 mm or aluminium silicate of 0.4 - 1.8 mm will usually create the desired surface profile when the air pressure measured at the nozzleis 6 - 7 bar/85 -100 psi.
The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
When the abrasive blasting is completed, remove residual grit and dust by vacuum cleaning. Abrasive particles not removed by vacuum cleaning are to be removed bybrushing with clean brushes followed by vacuum cleaning.
The importance of systematic working must be stressed when blasting. Poorly blastedareas covered with dust are very difficult to locate during the blast inspection made afterthe rough cleaning.
Shopprimed and previously painted surfaces: All shopprimer or existing coatingmaterials to be completely removed. Avoid the use of zinc shopprimer wheneverPossible.
However, if the steel is shopprimed with zinc, it is very important that all zinc is removedby abrasive blast cleaning. Separate check procedures will be necessary to demonstratethe effectiveness of removal. More blast cleaning may be deemed necessary! Use of ared zinc shopprimer will facilitate the visual check of the blast cleaning and isconsidered necessary in order to obtain an acceptable surface preparation.
Note: Degree of steelwork finish and surface preparation are more detailed describedin HEMPEL’s Technical Standard for Tank Coating Work.
Application equipment: HEMPADUR 15500 is to be applied by airless spray equipment. Stripe coating and minorrepairs can be carried out by brushing.
Airless spray equipment: A large pump is preferred, with a pump capacity of 8-12Litres/minute.
Pump ratio: Min. 45:1Nozzle orifice: .018"-.021"Nozzle pressure: 200 bar (2900 psi)Hoses: To avoid excessive loss of pressure in long hoses, hoses with an
internal diameter of up to 0.5" can be used
(Spray data are indicative and subject to adjustment).
Thinning: If required: max. 10% of THINNER 08450, possibly higher if tendency to dry-spray willrequire more thinning eg at higher temperatures. Thinning should only be at the requiredlevel to avoid possible risk of solvent entrapment.
Only add thinner to the mixed paint.
Cleaning of equipment: The whole equipment to be cleaned thoroughly with HEMPEL’S TOOL CLEANER 99610after use.
Mixing, pot life: a. Mix the entire content of corresponding base and curing agent packings. If it isnecessary to mix smaller portions, this must be done properly by either weighingbase and curing agent in the prescribed weight ratio: 93.8 parts by weight of baseand 6.2 parts by weight of curing agent or by volume: 8.9 parts by volume base and1.1 parts by volume curing agent.
b. Stir the mixed paint thoroughly by means of a clean mechanical mixer until ahomogeneous mixture is obtained.
c. Allow the mixed paint to prereact before application, see table below.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 15500
d. Use all mixed paint before the pot life is exceeded. The pot life depends on the
(5 minutes)(1 hour)
10 minutes2 hours
15 minutes3 hours
(25 minutes)(4 hours)
Induction timePot life
(30°C/86°F2))25°C/77°F20°C/68°F(15°C/59°F1))Temperature of mixed paint
1) At 15°C/59°F and below, the viscosity can be too high for airless spray application.2) Temperatures at 30°C/86°F and above should be avoided due to a risk of dry-spray.
Application procedure: The first full coat is usually applied immediately after vacuum cleaning. The first stripecoat afterwards.
Film-build/continuity: With this tank coating intended for aggressive cargoes, it is ofspecial importance that a continuous, pinhole-free paint film is obtained at application ofeach coat. An application technique which will ensure good film formation and nodry-spray on all surfaces must be adopted.
It is very important to use nozzles of the correct size, ie not too big. Select small nozzlesfor spray application of complicated structures, while bigger nozzles may be used forregular surfaces.
A proper, uniform distance of the spray gun to the surface, 30-50 cm, should be aimedat. To obtain good and steady atomizing, the viscosity of the paint must be suitable andthe spray equipment must be sufficient in output pressure and capacity. At high workingtemperatures, use of extra thinner may be necessary to avoid dry-spray.
The paint layer must be applied homogenously and as close to the specification aspossible. The consumption of paint must be controlled and heavy layers must beavoided because of the risk of sags and cracks and solvent retention.
Furthermore, great care must be taken to cover edges, openings, rear sides of stiffenersetc. Thus, on these areas a stripecoat will usually be necessary.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, must be remedied.
Note: In the case of old, pit corroded steel, application of a diluted, extra first coat isrecommended to obtain better "penetration" in the fine pits. For this purpose, it isrelevant to dilute 5-10%. Application by brush is recommended and film thickness so lowthat the surface is "saturated" only.
Stripe coating: All places difficult to cover properly by spray application should be stripe coated twice bybrushing immediately before the spray application. Typically, first stripe coat is appliedafter the first full coat and the second stripe coat after the second full coat.
The second stripe coat with brush can be replaced with spray application with a smallnarrow nozzle, but still air slots and similar and possible undercuts (welds) and the likewill require brush application.
Film thicknesses: The final dry film thickness of the three coat system must be between 300-600 micron(max. 450 micron below 15°C)/12-24 mils (max. 18 mils below 59°F).
Corresponding to 100 micron/4 mils dry film thickness, the wet film thickness must be150-175 micron/6-7 mils and must be measured regularly.
Normally up to 200 micron/8 mils per coat may be accepted for 100 micron/4 milsspecifications, but at temperatures below 15°C/59°F, it is important not to exceed adry film thickness of 150 micron/6 mils in any area.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPADUR 15500
Micro climate: The actual climate conditions at the substrate during application:
The minimum surface temperature until full cure is 10°C/50°F.
To ensure an all-over steel temperature of minimum 10°C/50°F, special attention shouldbe paid to possible "cold bridges" eg stiffeners on deck.
In case of steel temperatures lower than 10°C/50°F there is a severe risk of incompletecuring, resulting in a too open film with reduced chemical resistance.
When the outside temperature is lower than 10°C/50°F, it is therefore recommended touse insulation mats on deck and in addition to aim at a general steel temperature of15°C/59°F to minimise the risk of (locally) too low steel temperatures.
Furthermore, the steel temperature should be kept reasonably constant - within therange of ± 3°C/5°F is recommended. Any changes of the outside temperature shouldtherefore be carefully monitored and heating equipment calibrated accordingly.
A sudden drop of the steel temperature shortly after application will result in solvententrapment and will cause a dry film containing vacuoles, ie resulting in reducedperformance.
The maximum surface temperature should preferably be below approximately30°C/86°F. In a warm climate it is recommended to carry out application duringnighttime. Application at high temperatures, up to approximately 40°C/105°F, ispossible, but extra care must be taken to avoid poor film formation and excessive spraydust.
The steel temperature must be above the dew point. As a rule of thumb, a steeltemperature which is 3°C/5°F above the dew point can be considered safe. The relativehumidity shall preferably be 40-60%, maximum 80%.
In confined spaces, supply an adequate amount of fresh air during application and dryingto assist the evaporation of solvent.
Drying and curing, In a dry film thickness of 100 micron/4 mils, with a steel temperature of 20°C/68°F, aVentilation: relative air humidity of maximum 80% and adequate ventilation, HEMPADUR 15500 will
be dry to touch after 4-6 hours. Under these drying conditions, the paint film will acceptlight traffic after approximately 16 hours.
Correct film formation depends on an adequate ventilation during drying.
A good guideline for tank coating work is to ventilate to a calculated 10% of LEL duringapplication and until the coating is dry.
One litre undiluted HEMPADUR 15500 gives off in total 82 litres solvent vapour until it iscompletely dry.
The lower explosive limit, LEL, is 1.0%.
To reach a common safety requirement of 10% LEL, the theoretical ventilationrequirement is 82 m³ per litre paint.
Because solvent vapours are heavier than atmospheric air, effective ventilation requiresforced ventilation with exhaust from the lowest part of the tank.
During the following period until full curing a few air shifts per hour will suffice. Takeactions to avoid "pockets" of stagnant air.
Please contact HEMPEL for further advice.Actual safety precautions may require stronger ventilation.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 15500
Curing time: Provided that adequate ventilation, recommended relative humidity, specified filmthickness, and recommended minimum recoating interval are kept, the following curingtimes are valid:
(6 days)7 days8 days10 days14 days18 daysCuring time
(35°C/95°F)*30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
*Avoid application at elevated temperatures to avoid dry-spray and poor film formation.
Post curing: Postcuring must take place within 3 months after final acceptance of thecoating/delivery of the vessel.
Postcuring is accomplished by carrying a hot cargo of mineral lube oil, vegetable oil oranimal oil at 60°C/140°F for 5 days or at 50°C/122°F for 10 days.
Postcuring may also be accomplished by carrying clean seawater of minimum45°C/113°F and maximum 50°C/122°F provided all adjacent ballast tanks are emptyand all adjacent cargo tanks are either empty or carrying a liquid cargo of minimum40°C/104°F. In case of seawater, postcuring time is 14 days.
Recoating intervals: Provided observance of the above stated ventilation and relative humidity the followingrecoating intervals in relation to the (steel) temperature are valid:
18 hours12 hours
14 days
24 hours16 hours
16 days
36 hours24 hours
21 days
60 hours40 hours
34 days
90 hours60 hours
53 days
Minimum after the first coatafter the second coat
Maximum:
30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°F Steel temperature
* Absolut minimum temperature recommended.
The maximum relative humidity before and between the coats should not exceed 80%and the steel temperature should always be above the dew point, in practice minimum3°C/5°F above the dew point.
Conditions for Dry spray is not acceptable as this will reduce the protective characteristics of the paintpaint application work: and make later tank cleaning difficult. Dry spray can be avoided by using adequate
stagings, spraying equipment and methods.
Hold spray gun at a right angle to and about 30-50 cm from surface making even parallelpasses at a rate to produce the specified wet film thickness as per specification.
Avoid dry spray (overspray creating excessive paint mist), e.g. by using a smaller fanangle, and the lowest possible pressure. A small fan angle should also be used, if sprayapplication is used, for "stripe coating" of for instance reverse sides of stiffeners.
Each layer must be applied homogeneously and as near above the specification of 100micron/4 mils dry film thickness, as possible. The consumption of paint must becontrolled, and heavy layers must be avoided because of the risk of sagging, cracks andsolvent retention.
Surface irregularities such as dry spray, saggings, exaggerated thickness or embeddeddust or abrasives will have to be remedied.
If a sandpapering between layers, for instance on the bottom, is needed, great caremust be taken to avoid damage of otherwise intact surfaces. When using mechanicalmeans only lightweight equipment should be used, orbital sander is recommended. Yet,avoid sandpapering on top of welds or irregularities or near to vertical surfaces. The finished coating must appear as a homogeneous surface without pores, runners orcontamination of any kind.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPADUR 15500
Control of For the standard specification the following applies to the dry film thickness:dry film thicknesses:
The minimum dry film thickness is 300 micron/12 mils, the maximum thickness isapproximately 600 micron/24 mils (below 15°C/59°F: 450 micron/18 mils). Theminimum dry film thickness is evaluated according to the "80-20" rule, ie no more than20% of the total number of individual measurements must be lower than the minimumdry film thickness, and the lowest individual measurement must be at least 80% of theminimum dry film thickness, ie 240 micron/9.6 mils. Dry film thickness control is not tobe carried out within the first 24 hours after application of final coat (20°C/68°F,sufficient ventilation). The measurement must be carried out using an electromagneticdry film thickness gauge calibrated with shims placed on a smooth steel substrate. Themaximum dry film thickness can also be evaluated according to the "80-20" rule.
Taking into use: Do not use the tank before the coating is properly cured. Reference is made to curingtime on page 5.
Repairs: It is of great importance that all damage to the coating is repaired.
Repair must be started up as soon as possible. Repair of mountings for stagings, etc.must take place in connection with the dismantling of the stagings, the tempo of which shall be adjusted to the touch-up procedure.
It is important that the repaired areas, as well as the rest of the coated areas, are fullycured before the tank is taken into use or washed by the tank cleaning system.
The extent of damage to the coating can be evaluated by a seawater test. Wash thetanks with clean seawater by means of the tank cleaning machines until profiles and/orheating coils on tanktop is covered. Allow the water to stay for minimum 3 days, afterwhich period the tank is emptied and cleaned with clean fresh water to remove salts.
The repair process: General: Before mechanical treatment is started, surfaces to be repaired have to becleaned for any salts and other contamination.
Areas less than 5 x 5 cm.
The surface preparation can be executed by grinding to a clean rough metal surface,feathering edges of intact coating and slightly sanding the adjacent surface.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up by brush to full film thickness with minimum 4 coats of HEMPADUR 15500.
Areas up to 1 sq.m.
The surface preparation must be executed by vacuum blasting or open nozzle blasting sothat the steel has a proper roughness and a cleanness to Sa 3 according to ISO8501:1988. The overlapping zone must be sanded or sweep blasted to ensure a goodadhesion of the new paint.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up by brush to full film thickness with minimum 4 coats or by spray 3 coatsHEMPADUR 15500.
Areas more than 1 sq.m. or areas where several damaged spots are concentrated.
Treatment: Repeat the original specification.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 6 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 15500
Safety: Handle with care. Before and during use, observe all safety labels on packaging and paintcontainers, consult HEMPEL Material Safety Data Sheets and follow all local or national safety regulations. Avoid inhalation, avoid contact with skin and eyes, and do not swallow. Takeprecautions against possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas.
Issued: February 2002 - 1550011630CR006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 7 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1550011630CR006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR 15520CURING AGENT 95080
Description: HEMPADUR 15520 is a two-component, polyamide cured epoxy paint.
Recommended use: As an intermediate coat on zinc silicates to minimize popping. HEMPADUR 15520 mayalso be used as a sealer coat on metal sprayed surfaces.
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Finish: FlatColour: RedShade Numbers: 50890Volume by Solids: 22%Theoretical Spreading 8.8 m²/litre - 25 micronsRate: 359sq.ft./US gallon - 1 milFlash Point: 30ºC/86ºF Abel-Pensky, closed cupSpecific Gravity: 1.1 kg/litre
9.2 lbs/US gallonSurface Dry: 0.5 (approx) hour at 20ºC/68ºF (ISO 1517)Dry to Touch: 1 (approx) hour at 20ºC/68ºFFully Cured: 7 days at 20ºC/68ºFShelf Life: 1 year at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing Ratio: BASE: HEMPADUR 15529 2.0 parts by volume
CURING AGENT: 95080 1.0 part by volumeApplication Method: Airless SprayThinner (max.vol.): 08700 (20%) (See REMARKS overleaf)Pot-Life: 8 hours (20ºC/68ºF)Nozzle Orifice: 0.021"Nozzle Pressure: 75 bar/1100 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, wet: 125 microns/5 milsIndicated film thickness, Dry: 25 microns/1 mil (See REMARKS overleaf)Recoat interval, min: 6 hours (20ºC/68ºF)Recoat interval, max: None (See REMARKS overleaf)
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenapplying pain in confined spaces or stagnant air. Even when ventilation is provided,respiratory, skin, and eye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1552050890
HEMPADUR 15520
Surface HEMPADUR 15520 can be applied when the "near-to-cured" stage of the GALVOSIL is reached. ForPreparation: GALVOSIL qualities such as 15700 - properly applied in 50 microns d.f.t. -this stage is reached
after 24 hours at 20ºC/68ºF and 75% RH. Remove oil and grease etc., with suitable detergent.Remove salt and other contaminants by high pressure fresh water cleaning. After exposure to highhumidity, zinc salts, "white rust" will have to be carefully removed by high pressure fresh watercleaning, if necessary combined with scrubbing with stiff nylon brushes. Consult APPLICATIONINSTRUCTIONS for the relevant GALVOSIL.
Application Use only where application and curing can proceed at temperatures above 10ºC/50ºF. TheConditions: temperature of the surface and that of the paint itself must also be above this temperature. Apply
only on a dry and clean surface with a temperature above the dew point to avoid condensation. Inconfined spaces provide adequate ventilation during application and drying.
Preceding Coat: HEMPEL'S GALVOSIL qualities according to specification.
Subsequent Coat: HEMPADUR, HEMPANYL, HEMPATEX, or HEMPATHANE qualities according to specification.
Remarks: Service Temperatures: Dry service temperature: max 60ºC/140ºF. Dry peak temperature: max.80ºC/175ºF.
Thinning: Should always be diluted at least 10% with THINNER 0870 for optimized anti-poppingproperties.
Film Thickness: May be specified in another film thickness than indicated depending on purposeand area of use. Normal range is 20-40 microns/0.8-1.6 mils. This will alter spreading rate andmay influence amount of thinning necessary, drying time and recoating interval. Excessive filmthickness should be avoided. Maximum dry film thickness recommended is 40 microns/1.6 mils.
Recoating Interval: The use of HEMPADUR 15520 as a "sealer coat on zinc silicate" is primarilyintended in case of a recoating interval between the "sealer coat" and the subsequent coat beingof medium length. In case of short recoating interval of HEMPADUR 15520, ie: less than 3 days at20ºC/68ºF and 75% RH, then the zinc silicate must be fully cured (see relevant product data sheet)before HEMPADUR 15520 is applied. After prolonged exposure of the zinc silicate to pollutedatmosphere, remove accumulated contamination with suitable detergent, followed by high pressurefresh water cleaning and/or scrubbing and allow to dry. Observe that long time exposure of the notfully coated system (ie zinc silicate plus HEMPADUR 15520 only) to humid environment may cause"white rust" to develop beneath the thin paint film of 15520.
V.O.C.: The Volatile Organic Compounds are 715 g/ltr, 6.0 lbs/US gallon.
Notes: Before overcoating after exposure in contaminated environment, clean surface thoroughly byhigh pressure water cleaning and allow to dry.
Note: HEMPADUR 15520 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1552050890
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataDataProduct HEMPADUR®15550
CURING AGENT 95360
Description: HEMPADUR 15550 is a two-component polyamide adduct-cured epoxy paint. It curesdown to -10°C/14°F to a strong coating with good adhesion properties.
Recommended use: As a primer for HEMPATEX, HEMPADUR and HEMPATHANE systems on hot dippedgalvanized surfaces. In moderately corrosive environments, HEMPADUR 15550 is alsosuited when roughening of the surface is not possible. Please see surface preparationoverleaf.
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50890Finish: FlatVolume solids, %: 43 ± 1Theoretical spreading rate: 8.6 m²/litre - 50 micron
345 sq.ft./US gallon - 2 milsFlash point: 22°C/72°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: ¾ (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 2 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 515 g/litre - 4.3 lbs/US gallon
Storage stability: ½ year from date of production. If exceeded, please contact HEMPEL for further advice.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15550: Base 15559 : Curing agent 95360
7 : 1 by volumeApplication method: Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .021"Nozzle pressure: 175 bar/2450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 125 micron/5 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1555050890CO004
HEMPADUR 15550
SURFACE Remove oil and grease etc. with suitable detergent. Remove salt and other contaminants by (highPREPARATION: pressure) fresh water cleaning. "White rust" must be removed by sandpapering or light abrasive
sweeping. In certain cases - related to the structure of the outer zinc layer - roughening of the galvanizedsurfaces will be necessary to secure adhesion.Concerning galvanizing it is recommended that fluxing takes place before dipping steel in the zinckettle. Furthermore, see REMARKS below.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. At the freezing point and below be aware of the risk of ice on the surface, which will
hinder adhesion.Use only where application and curing can proceed at temperatures above -10°C/14°F. Thetemperature of the surface must also be above this limit.The temperature of the paint itself should be 15-25°C/59-77°F.In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT COAT: HEMPADUR, HEMPATHANE or HEMPATEX qualities according to specification.
REMARKS:Passivation/: Ammonium chloride or any other passivation agent should not be present on the surface whensurface preparation: coating the galvanized surface.
Water should not be used for cooling down the steel.Cleaning of steel should not be initiated unless the steel temperature is below 30°C/86°F.
Application: As the galvanized zinc layer may be porous it is recommended to apply a mist coat of undilutedHEMPADUR 15550, allow air to escape, and then apply a full coat of HEMPADUR 15550 a fewminutes later.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 50-80 micron/2-3.2 mils.
Recoating: Recoating intervals related to later conditions of exposure:
12 hoursNone*3 days
24 hoursNone*
10 days*
NoneNoneNone
2 hours6 hours6 hours
15 minutes2 hours2 hours
15 minutes2 hours2 hours
HEMPATEXHEMPADUR
HEMPATHANE
SevereMediumMildSevereMediumMildRecoated with
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
*Except for mild climatic conditions avoid long-term exposure of galvanized steel only coated with a thin layer of paint as this maycreate white rust under the paint.
If the maximum recoating interval is exceeded, whatever the subsequent coat, roughening of thesurface is necessary to ensure optimum intercoat adhesion or in the case of recoating withcoatings other than HEMPADUR, apply a (thin) additional coat of HEMPADUR 15550 within theabove directions for recoating.A completely clean surface is mandatory to ensure intercoat adhesion, especially in the case oflong recoating intervals. Any dirt, oil and grease have to be removed with eg suitable detergentfollowed by high pressure fresh water cleaning. Salts to be removed by fresh water hosing.Any degraded surface layer, as a result of a long exposure period, must be removed as well.Water jetting may be relevant to remove any degraded surface layer and may also replace theabove-mentioned cleaning methods when properly executed. Consult HEMPEL for specific advice ifin doubt.To check whether the quality of the surface cleaning is adequate, a test patch may be relevant.
Note: HEMPADUR 15550 is for professional use only.
Issued: October 1999 - 1555050890CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1555050890CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15552CURING AGENT 97290
Description: HEMPADUR 15552 is a two-component polyamide adduct-cured epoxy paint. It cures to a flexible, well adhering coating with good abrasion and impact resistance. Contains zincphosphate. Cures down to -10°C/14°F.
Recommended use: As a primer for on-line application of reefer containers.As a primer for HEMPATEX, HEMPADUR and HEMPATHANE systems on hot dippedgalvanized surfaces and stainless steel in moderately corrosive environments.HEMPADUR 15552 is also suited when roughening of the surface is not possible.Please see surface preparation overleaf.
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Off-white/11630Finish: FlatVolume solids, %: 41 ± 1Theoretical spreading rate: 10.3 m²/litre - 40 micron
411 sq.ft./US gallon - 1.6 milsFlash point: 30°C/86°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 1 (app) hour at 20°C/68°F (ISO 1517)Dry to touch: 3 (app) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 535 g/litre - 4.4 lbs/US gallon
Shelf life: ½ year (25°C/77°F) from time of production. Depending on storage conditions,mechanical stirring may be necessary before usage.If the shelf life is exceeded please contact HEMPEL for further advice.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15552: Base 15556 : Curing agent 97290
3 : 1 by volumeApplication method: Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .017"-.019"Nozzle pressure: 175 bar/2450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1555211630CR001
HEMPADUR 15552
SURFACE Stainless steel surfaces or muffler grade steel surfaces (MGSS) of containers: Remove dirt, oilPREPARATION: and grease etc. with suitable detergent.
Remove salt and other contaminants by (high pressure) fresh water cleaning. It is very importantthat all contamination and dust are removed.Roughening of the surface is recommended for optimum adhesion.Galvanizing, zinc silicate painted or spray-metallized surfaces: Remove oil and grease, etc. withsuitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning.Zinc salts (white rust) must be removed by high pressure hosing combined with rubbing with a stiffnylon brush if necessary.It is recommended to recoat spray-metallized surfaces as soon as possible to avoid possiblecontamination.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. At the freezing point and below be aware of the risk of ice on the surface, which will
hinder adhesion.Use only where application and curing can proceed at temperatures above -10°C/14°F. Thetemperature of the surface must also be above this limit. The temperature of the paint itself should be 15-25°C/59-77°F.In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENTCOAT: HEMPADUR, HEMPATHANE or HEMPATEX qualities according to specification.
REMARKS:Passivation/: Ammonium chloride or any other passivation agent should not be present on the surface whensurface preparation: coating the galvanized surface.
Water should not be used for cooling down the steel.Cleaning of steel should not be initiated unless the steel temperature is below 30°C/86°F.
Application: As the galvanized zinc layer may be porous it is recommended to apply a mist coat of undilutedHEMPADUR 15552, allow air to escape, and then apply a full coat of HEMPADUR 15552 a fewminutes later.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 30-50 micron/1.2-2 mils, for containers normally 30 micron/1.2 mils.
Recoating: Recoating intervals related to later conditions of exposure (50 micron/2 mils dry):
12 hoursNone*3 days
24 hoursNone*
10 days*
NoneNoneNone
2 hours6 hours6 hours
15 minutes2 hours2 hours
15 minutes2 hours2 hours
HEMPATEXHEMPADUR
HEMPATHANE
SevereMediumMildSevereMediumMildRecoated with
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
*Except for mild climatic conditions avoid long-term exposure of galvanized steel coated with a thin layer of paint only as this maycreate white rust under the paint.
If the maximum recoating interval is exceeded, whatever the subsequent coat, roughening of thesurface is necessary to ensure optimum intercoat adhesion or in the case of recoating withcoatings other than HEMPADUR, apply a (thin) additional coat of HEMPADUR 15552 within theabove directions for recoating.A completely clean surface is mandatory to ensure intercoat adhesion, especially in the case oflong recoating intervals. Any dirt, oil and grease have to be removed with eg suitable detergentfollowed by high pressure fresh water cleaning. Salts to be removed by fresh water hosing. Any degraded surface layer, as a result of a long exposure period, must be removed as well.Water jetting may be relevant to remove any degraded surface layer and may also replace theabove-mentioned cleaning methods when properly executed. Consult HEMPEL for specific advice ifin doubt.To check whether the quality of the surface cleaning is adequate, a test patch may be relevant.
Note: HEMPADUR 15552 is for professional use only.Issued: October 2001 - 1555211630CR001
HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1555211630CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®FAST DRY 15560CURING AGENT 97560
Description: HEMPADUR FAST DRY 15560 is a two-component, polyamine adduct cured epoxy paintwith a very short drying time. Contains zinc phosphate.
Recommended use: As a quick drying primer or intermediate coat in HEMPADUR systems for especially fastrecoatable in-shop applications.Can be used for on-site work too if eg VOC compliance is requested.
Service temperatures: Maximum, dry: 140°C/284°F. See REMARKS overleaf.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/12170* Light grey/12430*
(MIO version) (See REMARKS overleaf)Finish: Flat FlatVolume solids, %: 62 ± 1 62 ± 1Theoretical spreading rate: 6.2 m²/litre - 100 micron 6.2 m²/litre - 100 micron
249 sq.ft./US gallon - 4 mils 249 sq.ft./US gallon - 4 milsFlash point: 27°C/81°F 27°C/81°FSpecific gravity: 1.4 kg/litre - 11.6 lbs/US gallon 1.5 kg/litre - 12.5 lbs/US gallonSurface dry: ½ (approx.) hr at 20°C/68°F (ISO 1517) ½ (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 1½-2 hours at 20°C/68°F 1½-2 hours at 20°C/68°FFully cured: 7 days at 20°C/68°F 7 days at 20°C/68°FV.O.C.: 330 g/litre - 2.7 lbs/US gallon 330 g/litre - 2.7 lbs/US gallon
(According to EPA Fed Ref Method 24) (According to EPA Fed Ref Method 24)
*Another shade: red 50630 may be available according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15560: Base 15569 : Curing agent 97560
4 : 1 by volumeApplication method: Airless spray Air Spray BrushThinner (max. Vol.): 08450 (5%) 08450 (15%) 08450 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .019"-.021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1556012170CO006
HEMPADUR FAST DRY 15560
SURFACE New steel (dry conditions): Abrasive blasting to Sa 2½. For temporary protection, if required, usePREPARATION: suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication
should be thoroughly cleaned prior to final painting. For repair and touch-up use HEMPADUR15560.Maintenance: Remove oil and grease, etc.with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material by wet ordry abrasive blasting or power tool cleaning. Feather edges to sound and intact areas. After wetabrasive blasting hose down the surface with fresh water and allow to dry. Touch up bare spots tofull film thickness.
APPLICATION Use only where application and curing can proceed at temperatures above 0°C/32°F.CONDITIONS: The temperature of the paint itself should be 15°C/60°F or above to secure proper application
properties.In confined spaces provide adequate ventilation during application and drying.
PRECEDING COAT: None, or according to specification.
SUBSEQUENTCOAT: HEMPADUR, HEMPATHANE, HEMPATEX or HEMUCRYL as per specification.
REMARKS:Shade: CURING AGENT 97560 will become darker during storage. This will result in a darker and more
yellowish shade than grey 12170. The colour change will have no influence on the performance.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become more sensitiveService to mechanical damage and chemical exposure at elevated temperatures is also reflected in thisTemperatures: product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is75-150 micron/3-6 mils.
Recoating: Recoating intervals related to later conditions of exposure:(Dry film thickness of HEMPADUR FAST DRY 15560 as indicated below)
8 hoursNone
3 days8 hours
8 hoursNone
10 days24 hours
1 hour1½ hours1½ hours1½ hours
15 minutes1 hour1 hour1 hour
2 hours3 hours3 hours2 hours
1 hour2 hours2 hours1 hour
HEMPATEXHEMPADUR
HEMPATHANE58030
SevereMediumSevereMediumSevereMediumRecoated with
AtmosphericAtmosphericAtmosphericExposure during service
20°C/68°F20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
Workshop application75 micron/3 mils
MinimumIn-field application*100 micron/4 mils
*In case of general maintenance involving epoxy systems of high total dry film thickness, the minimum recoating interval mayadvantageously be doubled up.
If the maximum recoating interval is exceeded, whatever the subsequent coat, roughening of thesurface is necessary to ensure optimum intercoat adhesion or in the case of recoating withcoatings other than HEMPADUR, apply a (thin) additional coat of HEMPADUR FAST DRY 15560within the above directions for recoating.A completely clean surface is mandatory to ensure intercoat adhesion, especially in the case oflong recoating intervals. Any dirt, oil and grease have to be removed with eg suitable detergentfollowed by high pressure fresh water cleaning. Salts to be removed by fresh water hosing.Any degraded surface layer, as a result of a long exposure period, must be removed as well.Water jetting may be relevant to remove any degraded surface layer and may also replace theabove-mentioned cleaning methods when properly executed. Consult HEMPEL for specific advice ifin doubt.To check whether the quality of the surface cleaning is adequate, a test patch may be relevant.
Note: HEMPADUR FAST DRY 15560 is for professional use only.
Issued: January 2002 - 1556012170CO006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1556012170CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15570BASE 15579 with CURING AGENT 95570
Description: HEMPADUR 15570 is a two component, polyamide-adduct cured epoxy paint, whichcures to a strong and highly corrosion resistant coating, at temperatures down to-10°C/14°F. The Micaceous Iron Oxide pigmented light grey 12430 quality is also wellsuited for application under humid conditions, on damp steel surfaces, and may beapplied on moist surfaces.
Recommended use: 1. As a maintenance and repair primer, intermediate, and/or finishing coat inHEMPADUR systems in severely corrosive environment. As a finishing coat where acosmetic appearance is of less importance.
2. As a low temperature curing epoxy primer, intermediate, and/or finishing coat inpaint systems according to specification. Well suited as a (blast) primer in coal tarepoxy systems.
Service temperatures: Dry: Maximum 140°C/284°F (See REMARKS overleaf)Ballast water service: Resists normal ambient temperatures at sea*Other water service: 40°C/104°F (no temperature gradient)Other liquids: Contact HEMPEL*Avoid long-term exposure to negative temperature gradients.
Certificates/Approvals: Tested for non-contamination of grain cargoes at the Newcastle Occupational Health,Great Britain.Has a German and Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light grey/12430* (MIO) - Red/50630*Finish: FlatVolume solids, %: 54 ± 1Theoretical spreading rate: 5.4 m²/litre - 100 micron
217 sq.ft./US gallon - 4 milsFlash point: 25°C/77°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 3-4 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 430 g/litre - 3.6 lbs/US gallon
*Another shade: grey 12170 may be available according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15570: Base 15579 : Curing agent 95570
3 : 1 by volumeApplication method: Airless spray Air Spray BrushThinner (max. Vol.): 08450 (5%) 08450 (15%) 08450 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .019"-.021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 200 micron/8 milsRecoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1557012430CO007
HEMPADUR 15570
SURFACE New steel (dry conditions): Abrasive blasting to Sa 2½. For temporary protection, if required, usePREPARATION: suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication
should be thoroughly cleaned prior to final painting. For repair and touch-up use HEMPADUR15570.Light alloys: Thorough degreasing and (light) abrasive sweeping to remove contamination and tosecure adhesion - surface profile depending on later exposure. Stainless steel: (Eg ballast tanks of chemical carriers) to be abrasive blast cleaned to a uniform,sharp, dense profile (Rugotest No. 3, BN9a, ISO Comparator Medium (G), Keane-Tator Comparator2.0 G/S) corresponding to Rz minimum 50 micron. Any salts, grease, oil, etc. to be removed beforeabrasive blasting is commended.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly by powertool cleaning to St 3 (minor areas) or by abrasive blasting to minimum Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance of HEMPADUR 15570. As an alternative to dry cleaning, water jetting to sound, well adhering coat and/or to steel. Intactcoat must appear with roughened surface after the water jetting. By water jetting to steel,cleanliness shall be WJ-3 to WJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No.5/SSPC-SP 12). A flash-rust degree of maximum FR-2 (atmospheric exposure) / FR-2, preferablyFR-1 (immersion) (Hempel standard) is acceptable before application. Feather edges to sound andintact areas. Dust off residues. Touch up bare spots to full film thickness when the surface hasreached the condition of being damp, may be moist.In case of wet abrasive blasting a suitable inhibitor may be used. Surplus inhibitor and residualabrasives and sludge must be removed by (high pressure) fresh water cleaning before recoating.Cleaning with hot water is recommended.Note 1: Inhibitors are generally not recommended for surfaces which will be immersed duringservice.Note 2: Damp surfaces: Water is not readily detectable, but the temperature of the surface isbelow the dew point. Moist surfaces: pools of water and droplets have been removed, but there isa noticeable film of water. Wet surfaces: Droplets or pools of water are present).
APPLICATION Use only where curing can proceed at temperatures above -10°C/14°F.CONDITIONS: At the freezing point and below be aware of the risk of ice on the surface, which will hinder the
adhesion.The temperature of the paint itself should be 15°C/60°F or above to secure proper applicationproperties.In confined spaces provide adequate ventilation during application and drying.Occurrence of standing water or droplets on the painted surface immediately after application mayresult in discolouration.
PRECEDING COAT: None, or according to specification.
SUBSEQUENT COAT: None, HEMPADUR, HEMPATHANE, HEMPATEX or HEMUCRYL as per specification.
REMARKS: Certificates are issued under the former quality number 1557.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreService sensitive to mechanical damage and chemical exposure at elevated temperatures is alsoTemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is50-125 micron/2-5 mils.
Recoating: Recoating intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry. If the maximum recoating interval is exceeded,roughening of the surface is necessary to ensure intercoat adhesion.
Note: HEMPADUR 15570 is for professional use only.
Issue: March 2002 - 1557012430CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1557012430CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®15570CURING AGENT 95570
Physical data Drying time and recoating interval vary with film thickness, temperature and laterversus temperature: exposure conditions, thus: In-field application:
(100 micron/4 mils dry film thickness of HEMPADUR 15570)
5 days1½ days
10 days3 days
20 days6 days
45 days14 days
90 days27 days
AtmosphericMediumSevere
Interval for recoating withHEMPATHANE qualities
NoneNone
23 days
NoneNone
30 days
NoneNone
60 days
NoneNone
(90 days)
NoneNone
(90 days)
Atmospheric, mediumAtmospheric, severeImmersion***
Interval for recoating withHEMPADUR qualities
1½ days1 days
3 days1½ days
6 days3 days
Not relevantNot relevant
Not relevantNot relevant
Atmospheric, mediumAtmospheric, severe
Interval for recoating with58030
6 hours4 hours
8 hours5 hours
16 hours10 hours
36 hours23 hours
3 days2 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating withHEMPATEX HI-BUILDs
MAXIMUM recoating interval related to later conditions of exposure:
3 hours3 hours6 hours
4 hours4 hours8 hours
8 hours8 hours
16 hours
18 hours18 hours36 hours
36 hours36 hours3 days
Atmospheric, mediumAtmospheric, severeImmersion**
Interval for recoating withHEMPADUR and HEMPATHANE qualities
1½ hours3 hours
2 hours4 hours
4 hours8 hours
9 hours18 hours
18 hours36 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating withHEMPATEX HI-BUILDs and 58030 (10°C/50°F or higher in the case of 58030)
MINIMUM recoating interval related to later conditions of exposure:
3 hours5 days
4 hours7 days
8 hours14 days
16 hours1 month
36 hours2 months
Drying time, approxCuring time, approx
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-10°C/14°FSurface temperature
** NOT relevant for HEMPATHANE Qualities.*** Depending on actual local conditions, extended maximum recoating intervals may apply.
Please contact HEMPEL for further advice.
Furthermore, please see page 2.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1557012430CO007
HEMPADUR 15570Workshop application:(75 micron/3 mils dry film thickness of HEMPADUR 15570)
1½ hours1½ hours6 hours
2 hours2 hours8 hours
4 hours4 hours16 hours
Atmospheric, mediumAtmospheric, severeImmersion*
Interval for recoating withHEMPADUR and HEMPATHANE qualities
10 minutes1½ hours
15 minutes2 hours
30 minutes4 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating withHEMPATEX HI-BUILDs58030
MINIMUM recoating interval related to later conditions of exposure:
1½ hours5 days
2 hours7 days
4 hours14 days
Drying time, approxCuring time, approx
30°C/86°F20°C/68°F10°C/50°FSurface temperature
* NOT relevant for HEMPATHANE Qualities
Maximum recoating intervals according to preceding table, page 1.
Maximum recoating intervals:If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion or in thecase of recoating with coatings other than HEMPADUR, apply a (thin) additional coat ofHEMPADUR 15570 within the above directions for recoating.
Long recoating intervals:A completely clean surface is mandatory to ensure intercoat adhesion, especially in thecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.
Any degraded surface layer, as a result of a long exposure period, must be removed aswell. Water jetting may be relevant to remove any degraded surface layer and may alsoreplace the above-mentioned cleaning methods when properly executed. ConsultHEMPEL for specific advice if in doubt.
To check whether the quality of the surface cleaning is adequate, a test patch may berelevant.
The short minimum recoating intervals when overcoated with 46330, 46370, 46410 and58030, HEMPADUR and HEMPATHANE in case of workshop application, are onlypossible if the finished paint system is through dry before exposure to the environment.
Before recoating after exposure in contaminated environment, irrespective of recoatinginterval, clean surface thoroughly e.g. by (high pressure) fresh water hosing and allow todry.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999 - 1557012430CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1557012430CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®15590/HEMPADUR®15591
Medium to high temperatures: 15590 with CURING AGENT 95100Low temperatures: 15591 with CURING AGENT 97430
Description: HEMPADUR 15590/15591 is a two-component epoxy primer coating especially for useon surfaces exposed to severe abrasion.
Recommended use: As a blast primer for heavy duty epoxy systems according to specification.HEMPADUR 15590 with CURING AGENT 95100, amine adduct, is for use intemperatures of 5°C/41°F, preferably 10°C/50°F or higher.HEMPADUR 15591 with CURING AGENT 97430, polyamide adduct, facilitates curing attemperatures between 10°C/50°F and -10°C/14°F.
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version; mixed product: 15590 15591Colours/Shade nos: Red/56880 Red/56880Finish: Semi-gloss Semi-glossVolume solids, %: 44 ± 1 45 ± 1Theoretical spreading rate: 11.0 m²/litre - 40 micron 11.3 m²/litre - 40 micron
441 sq.ft./US gallon - 1.6 mils 451 sq.ft./US gallon - 1.6 milsFlash point: 26°C/79°F 26°C/79°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallon 1.3 kg/litre - 10.8 lbs/US gallonDry to touch: 3 (approx.) hours at 20°C/68°F 9 (approx.) hours at 5°C/41°FFully cured: 7 days at 20°C/68°F 20 days at 5°C/41°FV.O.C.: 500 g/litre - 4.2 lbs/US gallon 475 g/litre - 3.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS: 15590 15591Mixing ratio: Base 15599 : Curing agent 95100 Base 15599 : Curing agent 97430
15 : 4 by volume 3 : 1 by volumeApplication method: Airless spray Air spray Airless spray Air sprayThinner (max.vol.): 08450 (5%) 08450 (15%) 08450 (5%) 08450 (15%)Pot life: 2 hours (20°C/68°F) 2 hours (20°C/68°F)Nozzle orifice: .021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: 1 month (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1559056880CO005/1559156880CO001
HEMPADUR 15590/HEMPADUR 15591
SURFACE New steel: Abrasive blasting to Sa 2½-3 depending on area of use. Minimum surface profilePREPARATION: corresponding to Rugotest No. 3, BN11a, Keane-Tator Comparator, 5.5 G/S, or ISO Comparator
Coarse (G) - or as per the specification for the subsequent coat(s). Oil and grease must beremoved with suitable detergent, salts and other contaminants by (high pressure) fresh watercleaning prior to blasting. After blasting, clean the surface carefully from abrasives and dust.Maintenance: On old steel surfaces having been exposed to salt water, excessive amounts of saltresidues in pittings may call for wet abrasive blasting followed by dry abrasive blasting.Alternatively, dry abrasive blasting followed by high pressure fresh water cleaning, drying, andfinally, dry abrasive blasting again.
APPLICATION Apply only to a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. For application of HEMPADUR 15590, minimum temperature is 5°C/41°F, preferably
above 10°C/50°F. Relative humidity maximum 80%, preferably below 60%. In case of application ofHEMPADUR 15591 use only where application and curing can proceed at temperatures higher than-10°C/ 14°F.The temperature of the paint itself should preferably be between 15°C/59°F and 25°C/77°F. In confined spaces provide adequate ventilation during application and drying.
PRECEDING None.COAT:
SUBSEQUENT HEMPADUR MULTI-STRENGTH or according to specification.COAT: 15590:
HEMPADUR MULTI-STRENGTH 35530 and HEMPADUR MULTI-STRENGTH 45750. May be used as ablast primer in HEMPADUR 15400 systems.15591:HEMPADUR MULTI-STRENGTH 45742.
REMARKS:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 30-50 micron/1.2-2 mils.The stated minimum recoating interval may be halved for areas not intended for water immersion.To secure good adhesion and the best possible mechanical properties, the following implies:• The coating has been applied in a dry film thickness as near as possible to the specified 40
micron.• The film formation has been of good quality and without any dry spray.• The drying and curing conditions have been according to APPLICATION CONDITIONS, please see
above. (In the case of long recoating intervals: until full curing has been obtained).• No kind of surface contamination exists, except loose dust, etc. which is possible to remove by
vacuum cleaning (tanks) / hosing down (exterior).The surface MUST be completely clean before recoating. The coating is checked carefully andshould be without patchy, whitish, and/or greasy formations, which can hinder adhesion ofsubsequent coat. Note: Exudation of curing agent causes the mentioned patchy, whitish,and/or greasy formations which will take place if HEMPADUR 15590/15591 is applied at lowtemperature without proper induction time and/or if the coating is exposed to water (rain,condensation) during drying and curing.
• Depending on actual local conditions, extended maximum recoating intervals may apply. Pleasecontact HEMPEL for further advice.
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion. Before recoating after exposure in contaminated environment, clean surfacethoroughly by (high pressure) fresh water hosing and allow to dry. HEMPADUR 15590/15591 willresist a hosing down of the surface 8 hours after application at a steel temperature of 20°C/68°F.
Note: HEMPADUR 15590/15591 is for professional use only.
Issued: May 2000 - 1559056880CO005/1559156880CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1559056880CO005/1559156880CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL®15700HEMPEL’S ZINC DUST 97170
Description: HEMPEL’S GALVOSIL 15700 is a two-component, solvent-borne, self-curing, inorganic zinc silicate with outstanding resistance against weathering and abrasion. It has excellent chemical resistance within the pH range 6-9. For service temperaturerange, see below. Applicable by airless spray. Offers cathodic protection of local mechanical damage.
Recommended use: 1. As a general purpose, heavy-duty, rust-preventing primer.2. As a single, complete coating for long-term protection of steel exposed to moderately
to severely corrosive environment and to abrasion.3. As a tank lining in accordance with the CARGO PROTECTION GUIDE.
Service temperatures: Dry conditions: • Resistant to permanent dry temperatures up to 500°C/932°F.• Resistant to occasional short-term heating (peak temperatures) up to
500°C/932°F while permanent service temperatures are otherwise below400°C/752°F.
• In the case of cyclic service conditions with regular periods of low and hightemperatures, the temperature should be kept below 400°C/752°F.
In the case of service temperatures above 400°C/752°F, it is of advantage to apply atopcoat of HEMPEL’S SILICONE ALUMINIUM 56910.Humid conditions: Please see REMARKS overleaf.
Certificates/Approvals: Complies with Section 175.300 of Food Additive Regulation (in respect of carriage ofdry foodstuffs) of the Code of Federal Regulations as found by review of the U.S. Foodand Drug Administration (FDA).Certificated by Scientific & Technical Services to comply with the requirements of lowmoisture fats and oil according to FDA.Approved by Lloyd's Register of Shipping as a recognized corrosion control coating.Meets the requirements laid down by ASTM A-490 Class "B" for Slip-Co-efficient andCreep Resistance.
Availability: Part of Group Assortment. Local availability subject to confirmation.PHYSICAL CONSTANTS:Colours/Shade nos: Metal grey/19840Finish: FlatVolume solids, %: 64 ± 1Theoretical spreading rate: 12.8 m²/litre - 50 micron
513 sq.ft./US gallon - 2 milsFlash point: 14°C/57°FSpecific gravity: 2.65 kg/litre - 22.1 lbs/US gallonDry to touch: 30 (approx.) min. at 20°C/68°F (65-75% RH)Fully cured: 3 (approx.) days at 20°C/68°F (65-75% RH) (See REMARKS overleaf)V.O.C.: 535 g/litre - 4.5 lbs/US gallonShelf life: 1 year (25°C/77°F) from time of production.
Shelf life is dependent on storage temperature. Shelf life is reduced at storagetemperatures above 25°C/77°F. Do not store above 40°C/104°F.Shelf life is exceeded if the liquid is gelled or if the mixed product forms gels beforeApplication.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15700: Liquid 15709 : zinc dust 97170
3.2 parts by weight : 6.8 parts by weight7.4 parts by volume : 2.6 parts by volume
Application method: Airless spray Air spray Brush (touch-up)Thinner (max.vol.): 08700 (30%) 08700 (50%) 08700 (10%)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .019"-.023"Nozzle pressure: 100 bar/1500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08700Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: None (See REMARKS overleaf)Safety: Handle with care. Before and during use, observe all safety labels on packaging and
paint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL’S GALVOSIL 15700
SURFACE Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (highPREPARATION: pressure) fresh water cleaning. Gritblasting to minimum Sa 2½ with a surface profile equivalent to
Rugotest No. 3, BN10a, Keane-Tator Comparator, min. 3.0 G/S, or ISO Comparator rough MEDIUM(G). In case of new steel to be exposed to no more than medium aggressive (industrial)environment and without any extraordinary demands to lifetime, a surface preparation degree ofSSPC-SP6 may suffice. Consult separate APPLICATION INSTRUCTIONS, and - as relevant - the corresponding PAINTINGSPECIFICATION for cargo tanks.
APPLICATION The surface must be completely clean and dry with a temperature above the dew point to avoidCONDITIONS: condensation.
At temperatures ranging from -10°C/15°F to 40°C/105°F.Curing needs minimum 65% relative humidity. Consult separate APPLICATION INSTRUCTIONS.
SUBSEQUENT As a tank coating: none. Otherwise according to specification.COAT:
REMARKS: Some of the certificates have been issued under the former quality number 1570.Service Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryTemperatures: important that NO moisture can penetrate during shut-down periods. This to avoid risk of "wet
corrosion" when the temperature rises.Wet service temperature, non-saline water: Maximum 60°C/140°F.
Tank coating: Wet service temperature, other liquids: Consult the corresponding CARGO PROTECTION GUIDE.Hot sea water washing and (low pressure) steam cleaning should never be executed on coatingswhich have not been in service for at least one month. Contact HEMPEL about temperaturespermissible.
Film thicknesses: If topcoated with a heavy- duty system, 50 micron/2 mils dry film thickness (75 micron/3 mils wet)is recommended. Consult separate APPLICATION INSTRUCTIONS before recoating. For long-term protection without topcoat, 75 micron/3 mils dry film thickness (100-125 micron/4-5mils wet) is generally recommended. In tanks 100 micron/4 mils dry film thickness (150 micron/6mils wet) is recommended but may be applied in 125 micron/5 mils dry film thickness (200micron/8 mils wet).
High temperature To avoid cracking it is important to keep the dry film thickness at maximum 40-50 micron/1.6-2Service: mils, especially in cases where service conditions include sudden temperature changes.Thinning: For application at high temperatures, a special thinner is available.Recoating: Minimum interval at 20°C/68°F, 65-75% RH for recoating with:
HEMPADUR (system/high-build) 3 days, full curing (see APPLICATION INSTRUCTIONS)HEMPADUR (25 micron/1 mil) 24 hoursRecoating intervals are strongly dependent on both temperature and humidity. Deviations from thestandard conditions may shorten or prolong the recoating intervals. Consult separate APPLICATIONINSTRUCTIONS.The recoating interval of 24 hours for 25 micron/1 mil HEMPADUR is only valid in case thesubsequent coat is applied more than 1 week after (20°C/68°F), 75% RH, humid weather.Otherwise, the minimum recoating interval is the same as for system/high-build.
Curing, cargo tanks: Before cargo tanks are taken into use, the coating must be completely through-cured. It isrecommended to carry out low pressure hosing of the tanks with (fresh) water 2-3 times at ambienttemperatures. Let the tanks remain wet between the washings. Reference is made to APPLICATIONINSTRUCTIONS.
Note: HEMPEL'S GALVOSIL 15700 is for professional use only.
Issue: October 1999 - 1570019840CO026HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPEL’S GALVOSIL®15700Scope: These application instructions cover surface preparation, application equipment, and
application of HEMPEL'S GALVOSIL 15700.
The following are general rules, which may be supplemented with more detaileddescriptions when needed, for instance for major newbuildings/new constructions orextensive repair jobs.
Steel work: For optimum performance, eg relevant for cargo tank coating, the following isrecommended:All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in weldings seams, undercuts, cracks,etc. should be avoided. If found, they must be remedied by welding and/or grinding.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specified filmthickness can be build-up on all surfaces. The radius of the rounding should beapproximately 1-2 mm. Any laminations must be removed.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988.
Note: Porous surfaces such as certain types of cast iron cannot be properly protectedwith zinc silicate. Deeply corroded steel may also be difficult to protect with a zincsilicate.
All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface preparation: Prior to abrasive blast cleaning of the steel, remove oil, grease, salts and othercontamination with a suitable detergent followed by high pressure fresh water hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing oftanks to be removed by fresh water and scrubbing with stiff brushes. Control for absenceof contamination according to separate guidelines.
On repair jobs, a rough blasting to remove all loosely adhering materials may be requiredbefore degreasing/washing is carried out.
Old steel: Even after a very thorough cleaning, pits may typically contain contaminationin the form of remnants of chemicals/water soluble salts. For this reason, repeateddetergent washing plus abrasive blasting may be necessary. After the first blasting, avery thorough vacuum cleaning is carried out in order to see if any "chemical bleeding"occurs as well as controls for water soluble salts (reference is made to separateinstructions) are made. Special care should be taken in evaluating pitted areas - ask forspecial guidelines.
Grit blast to min Sa 2½, ISO 8501-1:1988.
To obtain full chemical resistance according to the CARGO PROTECTION GUIDE, the steelsurface must be abrasive blast cleaned according to ISO 8501-1:1988, very near towhite metal Sa 2½-Sa 3. In practice, this requirement is to be understood as whitemetal Sa 3 at the moment of abrasive blasting, but allows for a slight reduction at themoment of paint application.
The resulting surface profile must be equivalent to Rugotest No. 3, min. BN 10a,Keane-Tator Surface Comparator, G/S min 3.0 or ISO/DIS 8503/1 rough MEDIUM (G).
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL’S GALVOSIL 15700
In case of new steel to be exposed to no more than medium aggressive (industrial)environment and without any extraordinary demands to lifetime, a surface preparationdegree of SSPC-SP6 may suffice.
Note: A lower surface profile than specified will cause reduced adhesion and increasedtendency to mud cracking.
Use steel grit, aluminium silicate, or similar sharp edged abrasives of a good qualityfree of foreign matters, soft particles, and the like. Control for absence of contaminationaccording to separate guidelines.
Steel grit with particle sizes of 0.2-1.2 mm or aluminium silicate of 0.4-1.8 mm willusually create the desired surface profile when the air pressure measured at the nozzleis 6-7 bar/85-100 psi.
The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
When the abrasive blasting is completed, remove residual grit and dust by vacuumcleaning. Abrasive particles not removed by vacuum cleaning are to be removed bybrushing with clean brushes followed by vacuum cleaning.
The importance of systematic working must be stressed when blasting. Poorly blastedareas covered with dust are very difficult to locate during the blast inspection made afterthe rough cleaning.
Old tank coatings: Must be completely removed. If the steel is pit corroded, the aboveguidelines for "Old steel" must be followed.
Shopprimed surfaces: When shoppriming is required only zinc silicate shopprimer suchas HEMPEL’S SHOPPRIMER ZS 15890 may be used and preferably in a reddish shade.
Before recoating with GALVOSIL 15700, intact shopprimer must be abrasive grit swept inorder to obtain specified roughness. A uniform sweep blasting is required, removingminimum 70% of the shopprimer followed by vacuum cleaning to remove accumulateddirt and zinc salts and to ensure adhesion.
Welds, rusty spots, burned areas, and all areas with other types of shopprimers thanzinc silicates of a type like HEMPEL'S SHOPPRIMER ZS 15890 must be completelyabrasive grit blasted as described above.
Application equipment: GALVOSIL 15700 can be applied by conventional spray equipment (pressure pot type),airless spray equipment, or by brush.
Conventional Spray equipment: Standard industrial spray equipment with mechanicalagitator and pressure regulators, air filters, and water traps.
Air hose: 10 mm (3/8") internal diameter.Material hose: 13 mm (1/2") internal diameter.
Hoses should be as short as possible, preferably not longer than 10 metres/30 feet.
Pot pressure: 2.5-5 bar (35-70 psi)Atomization pressure: 1.5-2.5 bar (20-35 psi)Nozzle orifice: 1.8-2.2 mm (.070"-.085")
(Spray-data are indicative and subject to adjustment).
Thinning, if required: max. 50% of THINNER 08700.
The pressure pot must be placed at the same level as or at a higher level than the spraygun when spraying, owing to the weight of the material. Alternatively a piston-pump (e.g.10:1) may be used instead of the pressure pot. This will facilitate the use of longerhoses or having the spray gun at a higher level than the pump.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL 15700
When painting undersides, the spray gun will need intermittent cleaning with THINNER08700 to prevent clogging of the nozzle.
With conventional spray application regulation of the pot and the atomizing air pressurescan be made as follows:
1. Shut off the atomizing air.
2. Regulate the pressure in the pot so that the material reaches approximately 60cm/20" horizontally out from the gun before falling to the ground.
3. Turn on the atomizing air using lowest possible pressure.
Airless spray equipment: A large, slow-working pump is preferred, e.g 30:1, with a pumpcapacity of 8-12 litres/minute. The in-line filter should be 60 mesh.
Gaskets: TeflonNozzle orifice: .019" through .023".Fan angle: 40° through 70°.Nozzle pressure: 100-150 bar (1400-2100 psi).
(Spray data are indicative and subject to adjustment).
Thinning, if required: max. 30% of THINNER 08700.
Thinning: The amount of thinning necessary will depend upon prevailing conditions: Temperature,humidity, wind/ventilation, method of spraying, spray equipment, etc.
In the case of a high level of thinning and/or long stops in application, the mixed paintmust be recirculated to avoid settlement of zinc particles in the spray hoses.
The coating must be wet and smooth just after application. Besides correct spraytechnique, the amount of thinner added must be selected securing this optimum filmFormation.
Too little thinning will typically lead to dry-spray and too much thinning to sagging andsettling of zinc particles in the can or in the spray hoses.
Cleaning of equipment: The whole equipment must be cleaned thoroughly with THINNER 08700 after use.
AddItionally for conventional spray-guns:
In the case of short stops, prevent packing of zinc around the needle by placing thespray gun in THINNER 08700 and let some air pass the spray gun. In the case of longerstops, clean the spray gun with THINNER 08700.
Mixing: a. Do not open packings until immediately before use. The entire content of the twopackings must be used for each batch to ensure a correct mixture. Left-overs inthe packings cannot be used later. Protect the ZINC DUST against moisturebefore mixing.
b. Before mixing, shake or stir the GALVOSIL 15709 LIQUID very thoroughly.
c. Pour the ZINC DUST slowly down into the LIQUID with constant mechanicalstirring. Do not mix in the reverse order. Continue stirring until the mixture is freeof lumps.
d. Strain the mixture through a screen, 60 - 80 mesh (250 - 160 DIN Norm. 4188).
Pot life: 8 hours at 20°C/68°F.
Temperature of paint: In a hot climate it is important that the cans with LIQUID are kept out of the sun and thatthe temperature of the liquid is kept below 30°C/86°F in order to avoid excessive drySpray.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL’S GALVOSIL 15700
Application procedure, Maintain constant agitation of the mixture until the batch is depleted.general:
The spray gun should be kept at a distance of 30-50 cm from the surface. Hold thespray gun at a right angle to the surface, making even, parallel passes with about 50%overlap.
Besides correct spray technique the amount of thinner added must be carefully adjustedto secure optimum film formation. The coating must be wet and smooth just afterapplication. It is important to avoid dry-spraying.
Select small nozzles (small orifice and small fan angle) for spray application ofcomplicated structures, while bigger nozzles may be used for regular surfaces.
The wet film thickness must be checked immediately after application, but it can only beused as a rough guidance because of the fast drying.
Application procedure, When used as a tank coating, HEMPEL'S GALVOSIL 15700 is normally specified in tank coating: 1 x 100 micron/1 x 4 mils - minimum 80 micron/3.2 mils, maximum 150 micron/6 mils.
To achieve a correct film formation within these limits, it is recommended to apply twocoats "wet-in-almost-dry":
Apply one coat and apply the second coat within 15-30 minutes before the first coat hasturned grey but is still dark.
When following this procedure, HEMPEL'S GALVOSIL 15700 must be thinnedapproximately 15% in order to avoid too high film thicknesses.
Too high film thicknesses on welds in corners must be smoothened by a flat brush,approximately 1" wide.
When coating tanks, it is of the utmost importance to avoid dry-spray, which is atypical indication of poor film formation.
Poor film formation of a one-coat tank coating system like HEMPEL'S GALVOSIL 15700may result in immediate failure.
Any dry-sprayed areas must be smoothened by scraping with a spatula (roundedcorners) or by light sandpapering or by using a cleaning sponge ("3M", "Scotch-brite"type).
After vacuum cleaning as necessary, the smoothened areas are applied a thin coat ofHEMPEL'S GALVOSIL 15700 achieved by using 20-25% thinning.
Note: If working conditions ask for it some hours may elapse between the first and thesecond coat provided that the relative humidity is kept constantly low, but it isrecommended to finalize the application as soon as possible and within the sameworking shift.
Stripe coating: All places difficult to cover properly by spray application must be stripe coated with abrush immediately before or after the spray application
Microclimate: The actual climatic conditions at the substrate during application and until acceptance:
The minimum surface temperature is -10°C/14°F.
The maximum recommended surface temperature is approx. 40°C/104°F. Higher steeltemperatures are acceptable provided dry-spray is avoided by (extra thinning and) properspray application. In extreme cases a reduction of the dry film thickness may also benecessary. In a warm climate it is recommended to carry out application duringnighttime.
The steel temperature must be above the dewpoint. As a rule of thumb a steeltemperature which is 3°C/5°F above the dewpoint can be considered safe.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL 15700
With temperatures at or below 0°C/32°F beware of ice on the surface, which will hinderthe adhesion, and use a capacitive RH-meter for measuring the relative humidity.
In confined spaces, supply an adequate amount of fresh air during application and dryingto assist the evaporation of solvent. All surfaces must be ventilated. However, avoidventilators blowing directly onto the freshly applied paint.
Drying and curing, Correct film formation depends on an adequate ventilation during drying. ventilation:
A good guideline for tank coating work is to ventilate to a calculated 10% of LEL duringapplication and until the coating is dry.
One litre undiluted HEMPEL’S GALVOSIL 15700 gives off in total 160 litres solventvapour until it is completely dry.
The lower explosive limit, LEL, is 0.5%.
To reach a common safety requirement of 10% LEL, the thoretical ventilationrequirement is 320 m³ per litre paint.
Because solvent vapours are heavier than atmospheric air, effective ventilation requiresforced ventilation with exhaust from the lowest part of the tank.
During the following period until full curing a few air shifts per hour will suffice. Takeactions to avoid "pockets" of stagnant air.
Please contact HEMPEL for further advice.
Actual safety precautions may require stronger ventilation.
It is recommended to keep the relative humidity low during application and drying.Thereafter, let the relative humidity raise by "natural means", i.e. the dehumidifiers arenotched off and normal ventilation used. However, it is recommended to letdehumidifiers run until dry film thicknesses have been checked - and if needed - rectifiedby an extra paint application.
Curing time: Curing is dependent on (steel) temperatures and relative humidities.
At 20°C/68°F and 65-75% RH, curing requires approximately 3 days. At lowertemperatures and relative humidity, curing time will increase considerably. Pleasecontact Hempel for further instructions.
The relative humidity should be minimum 65% - and the minimum temperature-10°C/14°F - during the period of curing. Hosing down of tanks can support curing, butshould if possible await the state of "near to complete" curing - please see below.
The coating will resist light showers after 1-2 hours at 20°C/68°F and 75% relativehumidity. Curing may be promoted at low humidity by hosing down the surface with water4 hours after application and keeping the surface constantly wet until curing is complete.If salt water is used, rinse with fresh water if the surface is to be overcoated.
State of curing: Can be checked by rubbing the coating with a rag soaked in THINNER 08700. If thecoating remains unaffected, state of curing is sufficient for recoating with other paintmaterials (when used as a cargo tank coating this state of curing may be described as"near to complete").
Full curing for cargo loading:
Before tanks are taken into use, the coating must be completely through-cured. Thisis secured by low pressure hosing/washing the tanks with (fresh) water 2-3 timesafter the above described condition of "near to complete curing" has been obtained.By using the tank washing equipment, the normal ½ hour cycle is applied with half aday to one day between washings. Let the tanks remain wet between the washing.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL’S GALVOSIL 15700
Full curing is confirmed by rubbing the coating with methyl ethyl ketone.
The coating will now be fully resistant according to the CARGO PROTECTION GUIDE,but as long as the porosities are not yet filled with zinc salts, absorption of cargoeswill take place, maybe making cleaning more difficult.
Curing may also be checked by scraping with e.g. a knife or a coin which shall produce abright mark leaving some loosened zinc dust but no irregular detachment.
Full hardness will be obtained after weathering for some time.
Recommended For long time protection, when topcoated with heavy-duty systems: film thickness: 50 micron/2 mils dry; 75 micron/3 mils wet, (undiluted).
For long time protection, without topcoat:75-100 micron/3-4 mils dry; 125-150 micron/5-6 mils wet, (undiluted).
In tanks: 100 micron/4 mils dry; 150 micron/6 mils wet, (undiluted), may be specified.
For a tank coating specification the film thickness should be controlled according to the80-20 rule, ie 80% of the dry film thickness measurements must be equal to or greaterthan the specified film thickness (100 micron/4 mils) and of those below the specifiedfilm thickness, no measurements must be lower than 80% of the 100 micron/4 mils.For narrow frames, girders and similar areas not being very accessible the film thicknesscould be controlled according to the 70-30 rule,
Too high dry film thickness, ie above approximately 150 micron/6 mils dry, should beavoided due to the risk of mud cracking or peeling. Please observe that according toaccepted rules of measuring "a measurement" is to be the mean of three single pointmeasurements taken in a close vicinity.
Note: Special care is necessary to ensure proper film thickness on welding seams,edges, corners, ribs, etc.
Extra coat (by itself): Too low film thickness can be made good by applying an extra coat of HEMPEL'SGALVOSIL 15700. Surface preparation procedure - if necessary - and dilution of paintaccording to page 4 "Application procedure, tank coating".
The maximum interval for applying an extra coat is 7 days provided that the relativehumidity is kept below 60%, absolute maximum is 65%, all the time until recoating andthat the painted surface is not exposed to open weather, contamination of the like.
Spreading rate: Theoretical (on a smooth surface):
513342257
12.88.56.4
234
5075100
sq.ft./US gallonm²/litredft, milsdft, micron
Practical (with a consumption factor of 1.8):
285190143
7.14.73.6
234
5075100
sq.ft./US gallonm²/litredft, milsdft, micron
Recoating interval HEMPEL’S GALVOSIL 15700 must be fully cured before recoating with a full paint(other paints): system. By recoating with sealer in 25 micron/1 mil only, the interval can be reduced to
eg 24 hours at 20°C/68°F and 65-75% RH provided that the following coats are appliedafter HEMPEL'S GALVOSIL 15700 is fully cured.
Topcoating procedure: Non-weathered zinc silicate coatings are porous and popping may occur in thesubsequent coat(s).
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 6 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL 15700
One way to reduce the risk of popping is to apply a mist coat as the first pass of thesubsequent coat, let the air escape, and then apply the remainder of the topcoat.
Some of HEMPEL's products will substantially reduce the risk of popping when applieddirectly on top of the zinc silicate. See painting specification.
Advanced paint systems are recommended for topcoating, e.g. HEMPADUR qualities.
Surface cleaning: The cleaning before topcoating depends on the condition of the surface:
1. Intact zinc silicate surface with sporadic formation of “white rust” (zinc corrosionProducts).
a. Remove oil, grease, dirt, etc. by detergent wash.
b. Remove "white rust" by high pressure fresh water cleaning 200-350 bar(2900-5000 psi) at a nozzle-to-surface distance of 15-20 cm (6-8").
If the surface is only slightly contaminated, corresponding to 1-2 monthsof exposure in a mildly corrosive environment, hosing down of the surfacewith fresh water and scrubbing with stiff brushes (nylon) may be sufficientand more practical. Check that the coating is through dry before recoating.
2. Zinc silicate surface with extreme formation of “white rust” which cannot beremoved as described above.
a. Remove oil, grease, dirt, etc. by detergent wash.
b. Abrasive blast sweep to remove "white rust", followed by vacuum cleaningto remove abrasives and dust.
c. Restore the zinc layer with any solvent borne GALVOSIL quality or zincepoxy (HEMPADUR ZINC).
3. Damaged areas, burns, weld spatters, etc.
a. Remove oil, grease, dirt, etc. by detergent wash.
b. Remove weld spatters.
c. Abrasive blasting to min. Sa 2½, followed by thorough removal ofabrasives and dust by vacuum cleaning.
d. Restore the zinc layer with any solvent borne GALVOSIL quality or zincepoxy (HEMPADUR ZINC).
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: February 2002 - 1570019840CO026HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 7 of 7HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1570019840CO026
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL®15780HEMPEL’S ZINC DUST 97170
Description: HEMPEL’S GALVOSIL 15780 is a two-component, medium-zinc, solvent-borne, self-curinginorganic zinc silicate coating. Applicable by airless spray.
Recommended use: As a general purpose rust-preventing primer in "high-build" paint systems for long-lifeprotection of steel exposed to moderately to severely corrosive environment.
Service temperatures: Maximum service temperature is depending on the subsequent coat.
Certificates/Approvals: Complies with Section 175.300 of Food Additive Regulations (in respect of carriage ofdry foodstuffs) of the Code of Federal Regulations as found by review of the U.S. Foodand Drug Administration.Meets the requirements laid down in ASTM A-490 Class "B" for Slip-Co-efficient andCreep Resistance.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/shade nos: Metal grey/19840Finish: FlatVolume solids, %: 62 ± 1Theoretical spreading rate: 12.4 m²/litre - 50 micron
497 sq.ft./US gallon - 2 milsFlash point: 14°C/57°FSpecific gravity: 2.4 kg/litre - 20.0 lbs/US gallonDry to touch: 30 (approx.) min. at 20°C/68°F (75% RH)Fully cured: 3 (approx.) days at 20°C/68°F (75% RH)V.O.C.: 515 g/litre - 4.3 lbs/US gallon
Shelf life: 6 months (25°C/77°F) from time of production.Shelf life is dependent on storage temperature. Shelf life is reduced at storagetemperatures above 25°C/77°F. Do not store above 40°C/104°F.Shelf life is exceeded if the liquid is gelled or if the mixed product forms gels beforeapplication.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS: Consult separate APPLICATION INSTRUCTIONSMixing ratio for 15780: Liquid 15789 : Zinc dust 971704.1 parts by weight : 5.9 parts by weight15.4 parts by volume : 3.8 parts by volumeApplication method: Airless spray Air spray Brush (touch-up)Thinner (max.vol.): 08700 (30%) 08700 (50%) 08700 (10%)Pot life: 12 hours (20°C/68°F)Nozzle orifice: .019" - .023"Nozzle pressure: 100 bar/1500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08700Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See SUBSEQUENT COAT overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
HEMPEL’S GALVOSIL 15780
SURFACE Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (highPREPARATION: pressure) fresh water cleaning. Gritblasting to minimum Sa 2½ with a surface profile equivalent to
Rugotest No. 3, BN10a, Keane-Tator Comparator, min. 3.0 G/S, or ISO Comparator roughMEDIUM (G). In case of new steel to be exposed to no more than medium aggressive (industrial)environment and without any extraordinary demands to lifetime, a surface preparation degree ofSSPC-SP6 may suffice.Consult separate APPLICATION INSTRUCTIONS.
APPLICATION AND From -10°C/15°F to 40°C/104°F.CURING Curing needs minimum 65% relative humidity. Consult separate APPLICATION INSTRUCTIONS.CONDITIONS:
SUBSEQUENT HEMPADUR systems according to specification. Recoating is expected to take place within 6COAT: months after application of HEMPEL’S GALVOSIL 15780.
REMARKS: Certificates are issued under the former quality number 1578.Note: If used as anticorrosive protection under insulation of high temperature equipment it is very
important that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Film thicknesses: 50 micron/2 mils dry film thickness is recommended, but 75 micron/3 mils dry film thickness (125micron/5 mil wet) may be specified, this will alter spreading rate and may influence drying time andrecoating interval.
Recoating intervals: Consult separate APPLICATION INSTRUCTIONS before recoating.
Minimum interval for recoating with: 20°C/68°F, 75% RHHEMPADUR (system/high-build) 72 hours (when fully cured)HEMPADUR (25 micron/1 mil) 24 hours
Recoating intervals are strongly dependent on both temperature and humidity, and deviations fromthe standard conditions may shorten or prolong the recoating interval. Consult separate APPLICATION INSTRUCTIONS.The recoating interval of 24 hours for 25 micron/1 mil HEMPADUR is only valid in case thesubsequent coat is applied more than 1 week after (20°C/68°F), 75% RH, humid weather.Otherwise, the minimum recoating interval is the same as for system/high-build.
Note: HEMPEL’S GALVOSIL 15780 is for professional use only.
Issued: December 2000 - 1578019840CO009HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description please refer to data sheet
HEMPEL’S GALVOSIL®15780Scope: This application instruction covers surface preparation, application equipment and
application of HEMPEL’S GALVOSIL 15780.
For optimum performance, the following is recommended:
Steel work: All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in weldings seams, undercuts, cracks,etc. should be avoided. If found, they must be remedied by welding and/or grinding.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specified filmthickness can be build-up on all surfaces. The radius of the rounding should beapproximately 1-2 mm. Any laminations must be removed.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988.
Note: Porous surfaces such as certain types of cast iron cannot be properly protectedwith zinc silicate. Deeply corroded steel may also be difficult to protect with a zincsilicate.
All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface preparation: Prior to abrasive blast cleaning of the steel, remove oil and grease and othercontamination with a suitable detergent followed by fresh water high pressure hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing(tanks) are removed by fresh water wash (scrubbing with stiff brushes).
Grit blast to min. Sa 2½, ISO 8501-1: 1988.
Surface profile equivalent to Rugotest No. 3, min. BN 10a Keane-Tator SurfaceComparator, G/S min 3.0 or ISO/DIS 8503/1 rough MEDIUM (G).
In case of new steel to be exposed to no more than medium aggressive (industrial)environment and without any extraordinary demands to lifetime, a surface preparationdegree of SSPC-SP6 may suffice.
Use steel grit, aluminium silicate or similar sharp edged abrasive of a good quality freeof foreign matters, soft particles and the like. Control for absence of contaminationaccording to separate guidelines.
The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
Steel grit with a particle size of 0.2-1.0 mm or aluminium silicate of 0.4-1.8 mm willusually create the desired surface profile when the airpressure measured behind thenozzle is 6-7 bars/85-100 psi.When blasting is completed, remove residual grit and dust by vacuum cleaning.
Note: Lower surface profile than specified will cause reduced adhesion and increasedtendency to mudcracking. On the other hand too high surface profile (steel grit) shouldbe avoided as this may introduce a risk of pin-point rusting.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
HEMPEL’S GALVOSIL 15780
Shopprimed surfaces:
If HEMPEL’S SHOPPRIMER ZS 15722 or other zinc silicate product is used forpreliminary protection, abrasive sweep intact surface before final coating with GALVOSIL15780 to remove accumulated dirt and zinc salt and to ensure adhesion.
Application: GALVOSIL 15780 can be applied by conventional spray (pressure pot type), airlessspray or brush.
Equipment:Conventional Spray: Standard industrial spray equipment with mechanical agitator andpressure regulators, air filters and water traps.
Air hose: 10 mm (3/8") internal diameter.Material hose: 13 mm (1/2") internal diameter.
Hoses should be as short as possible, preferably not longer than 10 metres (33").
Pot pressure: 2½-5 bar (37-72 p.s.i.)Atomization pressure: 1½-2½ bar (22-37 p.s.i.)Nozzle orifice: 1.8-2.2 mm (.070"-.085")
(Spray-data are indicative and subject to adjustment).
Thinning, if required: max. 50%. (See note below).
When spraying, the pressure pot must be placed at the same, or a higher level than thegun, due to the weight of the material. Alternatively a piston-pump (e.g. 10:1) may beused instead of the pressure pot. This will facilitate use of longer hoses or having thespraygun higher than the pump.
Maintain constant agitation of the mixture until the batch is depleted.
The spray gun should be kept at a maximum distance of 25-30 cm/1 foot from thesurface. Hold the spray gun at a right angle to the surface making even parallel passeswith about 50% overlap. Besides correct spray technique, the amount of thinner addedmust be carefully adjusted to secure optimum film formation. The coating must be wetand smooth just after application.
In case of painting undersides, the spray gun will need intermittent cleaning withTHINNER 08700 to prevent clogging of the nozzle.
At short stops, prevent packing of zinc around the needle by placing spraygun inthinner, letting some air pass the gun. At longer stops, clean spraygun with thinner.After use the hole equipment is cleaned thoroughly with THINNER 08700.
Airless Spray: A large slow-working pump is preferred, e.g 30:1, with a pump capacity of8-12 litres/minute. In-line filter 60 mesh.
Teflon gaskets.Nozzle orifice: 019" through .023", 40° through 70°.Nozzle pressure: 100-150 bar (1430-2100 p.s.i.).Thinning, if required: max. 30%. (See NOTE below).
(Spray data are indicative and subject to adjustment).
After use, the whole equipment is cleaned thoroughly with THINNER 08700.
Note: The amount of thinning necessary will depend upon prevailing conditions:temperature, humidity, wind/ventilation, method of spraying etc.
In the case of a high level of thinning and/or long stops in application, the mixed paintmust be recirculated to avoid settlement of zinc particles in the spray hoses.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL 15780
The coating must be wet and smooth just after application. Besides correct spraytechnique the amount of thinner added must be selected securing this optimum filmFormation.
Select small nozzles for spray application of complicated structures, bigger nozzles maybe used for regular surfaces.
Too little thinning will typically lead to dry-spray and too much thinning to sagging andsettling of zinc particles in the can.
Wet film thickness must be checked immediately after application, but can be used asa rough guidance only because of the fast drying.
Mixing: a. Do not open packings until immediately before use. The entire content of thepackings must be used for each batch to ensure a correct mixture. Left-overs inthe packings cannot be used later. Protect the ZINC DUST against moisturebefore mixing.
b. Before mixing, shake or stir the GALVOSIL 15789 LIQUID very thoroughly.
c. Pour the ZINC DUST slowly down into the LIQUID, with constant mechanicalstirring. Do not mix in reverse order. Continue stirring until mixture is free oflumps.
d. Strain the mixture through a screen, 60-80 mesh (250-160 DIN Norm. 4188).
Pot life: 12 hours (20°C/68°F)
Temperature of paint: In a hot climate it is important that the cans with LIQUID are kept out of the sun andthat the temperature of the liquid is kept below 30°C/86°F in order to avoid excessivedry spray.
Stripe coating: All places difficult to cover properly by spray should be stripe coated with brushimmediately before spray application - if necessary also after spray application.
Microclimate: (Actual climatic conditions at substrate).
During application: minimum surface temperature -10°C (14°F). Maximumrecommended temperature approx. 40°C (approximately 104°F), but higher steeltemperatures will be possible provided dry-spray is avoided by extra thinning and properspray application. In extreme cases reduction of dry film thickness may also benecessary.
Steel temperature has to be above the dew point. As a rule of thump a steeltemperature 3°C (5°F) above the dewpoint can be considered safe. At temperaturesbelow the freezing point extra care should be taken, in this case measurement ofrelative humidity has to be done with a capacitive RH-meter.
In confined spaces, supply an adequate amount of fresh air during application anddrying to assist solvent evaporation. Ventilation for this purpose is recommended to bea minimum corresponding to a few air shifts per hour along all surfaces. However, avoidventilators blowing directly onto the freshly applied paint.
After application until complete curing: minimum steel temperature -10°C (14°F),relative humidity minimum 65%.
Curing time: Curing is dependent on (steel) temperatures and relative humidities.
At 20°C/68°F and 75% RH, curing requires approximately 3 days. At lower temperaturesand relative humidity, curing time will increase considerably. Please contact Hempel forfurther instructions.
The coating will resist light showers after 1-2 hours at 20°C (68°F) and 75% relativehumidity.
To accelerate curing at lower humidity hose down surface with water 4 hours afterapplication and keep surface constantly wet until curing is complete.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
HEMPEL’S GALVOSIL 15780
Complete curing can be checked by rubbing the coating with a rag soaked in THINNER08700. If the coating remains unaffected, the curing is complete and ready forRecoating.
Also scraping with e.g. a knife must only give a bright mark, leaving some loosened zincdust, but no irregular detachment. Full hardness will first be obtained after weatheringfor some time.
Film thickness: Permanent protection, with topcoat:
Preferably 50 micron (2 mils) dry; 75 micron (3 mils) wet, however, 75 micron (3 mils)dry; approximately 125 micron (5 mils) wet, may be specified. In case of a long-termdurable paint system, the total thickness of the subsequent coat is to be at least 150micron/6 mils.
Special care should be taken to ensure proper thickness on welding seams, edges,corners, ribs, etc.
Extra coat Too low film thickness can be made good by applying an extra coat of HEMPEL'S(recoating with self): GALVOSIL 15780. Surface preparation procedure - if necessary - and dilution of paint
according to page 4 "Application procedure, tank coating".
The maximum interval for applying an extra coat is 7 days provided that the relativehumidity is kept below 60%, absolute maximum is 65%, all the time until recoating andthat the painted surface is not exposed to open weather, contamination of the like.
There is a risk of mudcracking or peeling with overthick coats (more than approx. 125micron/5 mils dry film thickness).
Spreading rate:
276184
6.94.6
(2)(3)
5075
Practical (consumptionfactor 1.8):
497331
12.48.3
(2)(3)
5075
Theoretical:(on smooth surface):
(sq.ft./US gallonm²/litre(Mils)Micron
Recoating For recoating advanced paint systems shall be used, e.g. HEMPADUR. (with other paints):
Recoating is expected to take place within 6 months after application of GALVOSIL15780.
Recoating interval: When fully cured (see CURING TIME).
Non-weathered zinc silicate coating are porous, and popping may occur in thesubsequent coat. The best way to avoid popping is to apply a mist coat in the first passof the topcoat. Let the air escape and apply the rest of the topcoat.
Some of HEMPEL's products will substantially reduce the risk of popping when applieddirectly on top of the zinc silicate. See painting specification.
Topcoating procedures depend on the condition of the surface as described below:
1. Intact zinc silicate with sporadic formation of "white rust".
a. Remove oil, grease, dirt etc. by detergent wash.
b. Remove “white rust” by high pressure water jetting with fresh water(250-300 bar (3625-4350 psi) at a nozzle distance of 15-20 cm (6-8")).
If the surface is only slightly contaminated, corresponding to 1-2 months of exposure ina mild climate, hosing down of the surface and scrubbing with stiff brushes (nylon) maybe more practical.Make sure that the film is through dry before recoating.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOSIL 15780
2. Zinc silicate surface with extreme formation of “white rust” which cannot beremoved as described above.
a. Remove oil, grease and dirt by a detergent wash (or solvent wash).
b. Sandsweeping for removal of contaminants. Thorough removal of dust byvacuum cleaning.
c. Touch up with any solvent borne GALVOSIL quality or HEMPADUR ZINC15360/15363/ HEMPEL’S ZINC PRIMER 16490.
3. Damaged areas, burns, weld spatter, etc.
a. Remove oil, grease and dirt by a detergent wash (or solvent wash).
b. Remove weld spatters.
c. Blasting to min. Sa 2½, thorough removal of dust by vacuum cleaning.
d. Restore the zinc layer with any solvent borne GALVOSIL quality or HEMPADURZINC 15360/15363/HEMPEL’S ZINC PRIMER 16490.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: May 2000 - 1578019840CO009HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1578019840CO009
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S GALVOSIL®S 15810(ONE-COMPONENT ZINC SILICATE)
Description: HEMPEL'S GALVOSIL S 15810 is a single component (S), solvent-borne, inorganic zincsilicate with outstanding resistance against weathering and abrasion. It has goodchemical resistance within the pH range 6-9. Withstands temperatures up to400C/750F. Offers cathodic protection of local mechanical damage.
Recommended use: 1. As a general purpose rust-preventing primer.
2. As a single, complete coating for long-term protection of steel exposed tomoderately to severely corrosive environment and to abrasion.
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Finish: FlatColours: Grey/Green According to assortment list, other shades may be available.Shade Nos: 42200Volume Solids: 70% Theoretical Spreading 14.0 m²/litre - 50 micronsRate: 570 sq.ft/US gallon - 2 milsFlash Point: 18/64 C/F Abel Pensky, closed cupSpecific Gravity: 2.9 kg/litre
24.2 lbs/US gallonDry to Touch: 30 (approx) minutes at 20ºC/68ºF (75% RH)Fully Cured: 3 days at 20ºC/68ºF (75% RH)Shelf Life: 6 months at 20ºC/68ºF (See REMARKS overleaf)
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:
Application Method: Airless Spray Air Spray Brush (touch-up)Thinner (max.vol.): 08700 (30%) 08700 (50%) 08700 (10%)Nozzle Orifice: 0.019"-0.023"Nozzle Pressure: 100 bar/1500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: THINNER 08700
Indicated film thickness, wet: 75 micron/3 milsIndicated film thickness, Dry: 50 micron/2 mils
Recoat interval, min: See REMARKS overleafRecoat interval, min: None - See REMARKS overleaf
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes should be avoided. Forced ventilation should be provided whenapplying paint in confined spaces or stagnant air. Even when ventilation is provided,respiratory, skin, and eye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
HEMPEL'S GALVOSIL®S 15810
Surface Gritblasting to minimum Sa 2½, with a surface profile equivalent to Rugotest No.3, BN10a.Preparation: Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough MEDIUM (G). Consult separate
APPLICATION INSTRUCTIONS.
Application At temperatures ranging from -5ºC/25ºF to 40ºC/105ºF.Conditions:
Curing needs minimum 50%, preferably above 65% relative humidity. Consult separateAPPLICATION INSTRUCTIONS.
Subsequent Coat: None, HEMPADUR, or HEMPANYL systems as per specification.
Remarks: If topcoated with a heavy-duty system 50 micron/2 mils dry film thickness (75 micron/3 mils wet)is recommended.
For long term protection without topcoat, 75 micron/3mils dry film thickness (100-125 micron/4-5mils wet) is generally recommended.
Minimum interval for overcoating with:
Hempadur (system/high-build) 48 hours (20ºC/68ºF, 75% RH)Hempadur (25 microns/1 mil) 24 hours (20ºC/68ºF, 75% RH)Hempanyl (system/high-build) 60 hours (20ºC/68ºF, 75% RH)Hempanyl (25 microns/1 mil) 24 hours (20ºC/68ºF, 75% RH)
Overcoating intervals are strongly dependent upon both temperature and humidity. Deviations fromthe standard conditions may shorten or prolong the overcoating intervals. Consult separateAPPLICATION INSTRUCTIONS.
The overcoating interval of 24 hours for 25 micron/1 mil HEMPADUR and HEMPANYL is only valid incase the subsequent coat is applied more than three days after, otherwise the minimumovercoating interval is the same as for system/high-build.
Store in a cool place and in original, unopened cans. Broken packings must be used within 4 hoursand cannot be stored for later use. Shelf life is reduced above 25ºC/75ºF. Do not store above40/105F.
Note: HEMPEL'S GALVOSIL®S 15810 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to product data sheet
HEMPEL'S GALVOSIL®S 15810(ONE-COMPONENT ZINC SILICATE)
For product description refer to the product data sheet.
Scope: These Application instructions cover surface preparation, application equipment andapplication of HEMPEL'S GALVOSIL S 15810.
The following are general rules, which may be supplemented with more detailsdescriptions when needed, for instance for major new buildings/new constructions orextensive repair jobs.
Steel Work: All welds must be free of pinholes and must be of highest quality so that they can beprotected by the paint. This means perfectly filled, smooth welds with a slightly wavysurface.
All welds must be complete and continuous without cracks and fissures which will causecoating discontinuity.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specific filmthickness can be build-up on all surfaces. The radius of the rounding should be approx.1-2 mm.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988.
Note: Porous surfaces such as certain types of cast iron cannot be properly protectedwith zincsilicate. Deeply pitcorroded steel may also be difficult to protect with azincsilicate.
All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface Preparation: Prior to abrasive blast cleaning of the steel, remove oil and grease and othercontamination with a suitable detergent followed by high pressure fresh water hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing oftanks to be removed by fresh water and scrubbing with stiff brushes.
Gritblast to min Sa 2 1/2, ISO 8501-1:1988, SSPC-SP-10. For severe exposures,gritblasting to Sa 3, ISO 8501-1:1988, SSPC-SP-5 is mandatory for optimum results.
The resulting surface profile must be equivalent to Rugotest No. 3, min. BN 10a (Ra-min.12.5 micron/0.5 mil), Keane-Tator Surface Comparator, G/S min 3.0. (Averagemaximum peak to valley roughness 75 micron/3 mils), or ISO/DIS 8503/1 roughMEDIUM (G).
Note: A lower surface profile than specified will cause reduced adhesion and increasedtendency to mudcracking. On the other hand too high surface profile (steel grit) shouldbe avoided as this will introduce a risk of pin-point rusting.
Use steel grit, silica sand, aluminium silicate, or similar sharp edged abrasives of a goodquality free of foreign matters, soft particles, and the like.
The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
Steel grit with particle sizes of 0.2 - 1.0 mm or aluminium silicate of 0.4 - 1.8 mm willusually create the desired surface profile when the air pressure measured at the nozzleis 6-7 bar/85-100 psi.
When the abrasive blasting is completed, remove residual grit and dust by vacuumcleaning.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
HEMPEL'S GALVOSIL®S 15810
Shopprimed surfaces: When shoppriming is required only straight zinc silicateshopprimer (such as HEMPEL'S SHOPPRIMER ZS 15720) may be used. HEMPEL'SGALVOSIL 15610, properly diluted, is also suitable for this purpose.
Before overcoating with GALVOSIL S 15810, intact shopprimer must be abrasivegritswept followed by vacuum cleaning to remove accumulated dirt and zinc salts and toensure adhesion.
Welds, rusty spots, burned areas, and all areas with other types of shopprimers than thestraight zinc silicates must be completely abrasive grit blasted as described above.
GALVOSIL S 15810 can be applied by conventional spray equipment (pressure pot type),spray equipment, or by brush.
Conventional Spray equipment: Standard industrial spray equipment with mechanicalagitator, pressure regulators, air filters, and water traps.
Air hose: 10 mm (3/8") internal diameterMaterial hose: 13 mm (½") internal diameter
Hoses should be as short as possible, preferably not longer than 10 meters/30 feet.
Pot pressure: 2.5-5 bar (35-70 psi)Atomization pressure: 1.5-2½ bar (20-35 psi)Nozzle orifice: 1.8-2.2 mm (.45"-.55")
(Spray-data are indicative and subject to adjustment).
Thinning, if required: max. 50% of THINNER 08700
Note: The amount of thinning necessary will depend upon prevailing conditions:temperature, humidity, wind/ventilation, method of spraying, etc.
The pressure pot must be placed at the same level as or at a higher level than the spraygun when spraying, owing to the weight of the material. Alternatively a piston pump (e.g.10:1) may be used instead of the pressure pot. This will facilitate the use of longerhoses or having the spray gun at a higher level than the pump.
At short stops, prevent packing of zinc around the needle by placing the spray gun inTHINNER 08700 and let some air pass the spray gun.
At longer stops, clean the spray gun with THINNER 08700.
The whole equipment to be cleaned thoroughly with THINNER 08700 after use.
Besides correct spray technique the amount of thinner added must be carefully adjustedto secure optimum film formation. The coating must be wet and smooth just afterapplication.
Select small nozzles for spray application of complicated structures, while bigger nozzlesmay be used for regular surfaces.
The wet film thickness must be checked immediately after application, but it can only beused as a rough guidance because of the fast drying.
When painting undersides, the spray gun will need intermittent cleaning with THINNER08700 to prevent clogging of the nozzle.
Airless spray equipment: A large, slow-working pump is preferred, e.g. 30:1, with a pumpcapacity of 8-12 litres/minute. The in-line filter should be 60 mesh.
Gaskets: TeflonNozzle orifice: 0.017" through 0.023"Fan angle: 40 through 70Nozzle pressure: 100-150 bar (1400-2100 psi)(Spray data are indicative and subject to adjustment)
Thinning, if required: Maximum 30% of THINNER 08700
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S GALVOSIL®S 15810
Note: The amount of thinning necessary will depend upon prevailing conditions:temperature, humidity, wind/ventilation, method of spraying, etc.
The whole equipment to be cleaned thoroughly with THINNER 08700 after use.
Besides correct spray technique the amount of thinner added must be carefully adjustedto secure optimum film formation. The coating must be wet and smooth just afterapplication.
Select small nozzles for spray application of complicated structures, while bigger nozzlesmay be used for regular surfaces.
The wet film thickness must be checked immediately after application, but it can only beused as a rough guidance because of the fast drying.
Storage Stability: 6 months at 20ºC/68ºF when stored in unopened packing. May be stored attemperatures between 5-40ºC/40-105ºF. However, the shelf life is reduced above25ºC/75ºF.
Store in a cool place.
Note: Opened packings of GALVOSIL S 15810 must be used within 4 hours and cannotbe stored for later use.
Stirring: When opening the packing, the product will appear as a soft sediment with a clear layeron top. This must be thoroughly stirred to a homogeneous state with a mechanicalmixer.
Pot Life: Refer to STORAGE STABILITY.
Procedure: Maintain constant agitation of the paint until the batch is depleted.
The spray gun should be kept at a maximum distance of 25-30 cm (1 foot) from thesurface. Hold the spray gun at a right angle to the surface, making even, parallelpasses with about 50% overlap
With conventional spray application regulation of the pot and the atomizing air pressurescan be made as follows:
1. Shut off the atomizing air2. Regulate the pressure in the pot so that the material reaches approximately 60
cm/20" horizontally out from the gun before falling to the ground3. Turn on the atomizing air using lowest possible pressure.
Stripe Coating: All places difficult to cover properly by spray application should be stripe coated with abrush immediately before the spray application - if necessary to obtain the specified filmthickness also after the spray application.
Micro Climate: The actual climatic conditions at the substrate during application:
The minimum surface temperature -5ºC/25ºF.
The maximum recommended surface temperature is approx. 40ºC/105ºF. Higher steeltemperatures are acceptable provided dry-spray is avoided by (extra thinning and) properspray application. In extreme cases a reduction of the dry film thickness may also benecessary.
The steel temperature must be above the dewpoint. As a rule of thumb a steeltemperature which is 3C/5F above the dewpoint can be considered safe.
With temperatures at or below the freezing point beware of ice on the surface, which willhinder the adhesion, and use a capacitive RH-meter for measuring the Relative Humidity.
In confined spaces, supply an adequate amount of fresh air during application and dryingto assist the evaporation of solvent. The ventilation for this purpose is recommended tobe at least what corresponds to a few air shifts per hour along all surfaces. Avoidventilators blowing directly onto the freshly applied paint.
After the application until complete curing the Relative Humidity should be minimum50%, preferably above 65%, and the minimum temperature -5ºC/25ºF.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
HEMPEL'S GALVOSIL®S 15810
Curing Time: Diagramme of curing depending on (steel) temperatures and relative humidities is foundon the last page.
The coating will resist light showers after 1-2 hours at 20ºC/68ºF and 75% relativehumidity. Curing may be promoted at low humidity by hosing down the surface with water10 hours after application and keeping the surface wet until curing is complete. If saltwater is used, rinse with fresh water if the surface is to be overcoated.
Complete curing can be checked by rubbing the coating with a rag soaked in THINNER08700. If the coating remains unaffected, the curing is complete.
Curing may also be checked by scraping with e.g. a knife or a coin which shall produce abright mark leaving some loosened zinc dust but no irregular detachment.
Full hardness will be obtained after weathering for some time.
Recommended Film For long term protection, with topcoat:Thickness: 50 micron/2 mils dry: 75 micron/3 mils wet. (undiluted).
For long term protection, without topcoat:75 micron/3 mils dry; 110 micron/4-4 mils wet, (undiluted)
Note: Special care is necessary to ensure proper film thickness on welding seams,edges, corners, ribs, etc.
There is a risk of mudcracking or peeling with heavier coats than approx. 90 micron/3.5mils dry film thickness.
Extra Coat: Too low film thickness can be made good by applying an extra coat, of diluted GALVOSILS 15810. This should be done before full curing is obtained.
Spreading Rate: Theoretical (on a smooth surface)
Dry Film Thickness Spreading Rate
50 microns (2 mils) 14.0 m²/litre (570 sq.ft/US gallon)75 microns (3 mils) 9.3 m²/litre (380 sq.ft/US gallon)
Practical (with a consumption factor of 1.8):
Dry Film Thickness Spreading Rate
50 microns (2 mils) 7.8 m²/litre (317sq.ft/US gallon)75 microns (3 mils) 5.2 m²/litre (211sq.ft/US gallon)
Overcoating Interval: GALVOSIL S 1581 must be fully cured before overcoating.
Topcoating Procedure: Non-weathered zinc silicate coatings are porous and popping may occur in thesubsequent coat(s). One way to reduce the risk of popping is to apply a mist coat asthe first pass of the topcoat, let the air escape, and then apply the remainder of thetopcoat.
Some of HEMPEL's products will substantially reduce the risk of popping when applieddirectly on top of the zinc silicate. Refer to the product data sheets for HEMPADURPRIMER 15520, HEMPANYL PRIMER 16060, and HEMPADUR HI BUILD 45230.Advanced paint systems are recommended for topcoating, e.g. HEMPADUR orHEMPANYL qualities.
In specifications with a high total film thickness the GALVOSIL S 15810 film thicknesscan advantageously be kept at 50 micron/2 mils.For many purposes GALVOSIL S 15810 may serve as a self-contained, protective coatingwhen applied in a dry film thickness of 75 micron/3 mils.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S GALVOSIL®S 15810
Surface The cleaning before topcoating depends on the condition of the surface:Cleaning:
1. Intact zinc silicate surface with sporadic formation of "white rust" (zinc corrosionproducts).
a. Remove oil, grease, dirt, etc. by detergent wash.b. Remove "white rust" by high pressure fresh water cleaning 200-350 bar
(2900-4300 p.s.i.) at a nozzle-to-surface distance of 15 - 20 cm (6-8"). If thesurface is only slightly contaminated, corresponding to 1- 2 months ofexposure in a mildly corrosive environment, hosing down of the surface withfresh water and scrubbing with stiff brushes (nylon) may be sufficient andmore practical.Check that the coating is thoroughly dry before overcoating.
2. Zinc silicate surface with extreme formation of "white rust" which cannot beremoved as described above.
a. Remove oil, grease, dirt, etc. by detergent wash.b. Abrasive sweep to remove "white rust", followed by vacuum cleaning to
remove abrasives and dust.c. Restore the zinc layer with any solvent borne GALVOSIL quality, HEMPADUR
ZINC 15360, or HEMPEL'S ZINC PRIMER 16490.
3. Damaged areas, burns, weld spatters, etc.
a. Remove oil, grease, dirt, etc. by detergent wash.b. Remove weld spatters.c. Abrasive blast to min. Sa 2 1/2, folowed by thorough removal of abrasives
and dust by vacuum cleaning.d. Restore the zinc layer with any solvent borne GALVOSIL quality, HEMPADUR
ZINC 15360, or HEMPEL'S ZINC PRIMER 16490.
Safety: Keep away from open flames and sparks. Use with adequate ventilation. In confinedareas, observe the usual precautions to prevent fire and damage to health. Use airmasks, safety goggles, and working gloves.
In case of contact with eyes, rinse immediately with plenty of water and seek medicaladvice. After contact with skin, wash immediately with plenty of (liquid) soap and water.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1581042200
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SHOPPRIMER ZS 15890HEMPEL’S LIQUID 99751
Description: HEMPEL’S SHOPPRIMER ZS 15890 is a two-component, low-zinc, solvent-borne ethylsilicate shopprimer, designed for automatic spray application. Especially suited, wherewelding (MIG/MAG) and gas-cutting properties are of importance.
Recommended use: For short to medium-term protection of blastcleaned steel plates and other structuralsteel during the storage, fabrication, and construction periods.
Certificates/Approvals: Approved as a welding primer by Lloyd's Register of Shipping, American Bureau ofShipping, Det Norske Veritas, Germanischer Lloyd, Korean Register of Shipping, BureauVeritas, RINA, Italy and Maritime Register of Shipping, Russia.See REMARKS overleaf.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Reddish grey/19890 - Grey/19840Finish: FlatVolume solids, %: 25 ± 1Theoretical spreading rate: See REMARKS overleafFlash point: 5°C/41°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonDry to handle: 3-4 minutes at 20°C/68°FFully cured: 4 days at 20°C/68°F (75% RH)V.O.C.: 620 g/litre - 5.15 lbs/US gallon
(According to EPA Fed Ref Method 24)
Shelf life: 6 months (25°C/77°F) from time of production.Shelf life is dependent on storage temperature. Shelf life is reduced at storagetempertures above 25°C/77°F. Do not store above 40°C/104°F or below 5°C/40°F.Shelf life is exceeded if the liquid is gelled or if the mixed product forms gels beforeApplication.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 15890: Base 15899 : Liquid 99751
2 : 3 by volumeApplication method: Airless spray Air spray Brush (touch-up)Thinner (max.vol.): 08570 or 08700 (30%) 08700 (30%) 08570 or 08700 (15%)
(See REMARKS overleaf)Pot life: 24 hours (20°C/68°F) (Closed container, constant stirring) (See REMARKS overleaf)Nozzle orifice: .019"-.023"Nozzle pressure: 80 bar/1200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08570 or 08700Indicated film thickness, dry: 15 micron/0.6 mil (See REMARKS overleaf)Indicated film thickness, wet: Not relevantRecoat interval, min: When fully curedRecoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
HEMPEL’S SHOPPRIMER ZS 15890
SURFACE Remove oil and grease with suitable detergent. Abrasive blasting to minimum Sa 2½ with aPREPARATION: surface profile equivalent to Rugotest No. 3, min. N9a, Keane-Tator Comparator, 2 mils segments
or ISO Comparator Medium (G,S).For special purposes gritblasting is necessary.
APPLICATION The surface must be completely clean and dry with a temperature above the dew point to avoidCONDITIONS: condensation. Minimum steel temperature 0°C/32°F, max. approximately 55°C/131°F:
Curing: Minimum temperature for curing 0°C/32°F, minimum 50%, preferably above 65% relativeHumidity.Consult separate APPLICATION INSTRUCTIONS.
SUBSEQUENT As per specification.COAT:
REMARKS: Certificates are issued under the former quality number 1589.Film thicknesses On steel abrasive blasted to a profile Ra = 12½ micron (½ mil), equivalent to Rugotest No. 3,and theoretical N10a-b, or Keane-Tator Comparator, 3 mils segments, the indicated 15 micron/0.6 mil filmspreading rates: thickness corresponds to approx. 25 micron/1 mil measured on a smooth test panel (see special
instructions for this procedure). The corresponding "theoretical" spreading rate will be 10.0m²/litre (401 sq.ft./US gallon) (reddish grey shade 19890).On steel abrasive blasted to a profile Ra = 6.3 micron (1/4 mil), equivalent to Rugotest No. 3,N9a, or Keane-Tator Comparator, 2 mils segments, the indicated 15 micron/0.6 mil film thicknesscorresponds to approx. 20 micron/0.8 mil measured on a smooth test panel (see specialinstructions for this procedure). The corresponding "theoretical" spreading rate will be 12.5m²/litre (501 sq.ft./US gallon) (reddish grey shade 19890).The shopprimer should be applied in a uniform film thickness. Avoid dry spray and exaggerated filmThicknesses.Depending on requested protective lifetime the dry film thickness may be varied. Minimum isapproximately 10 micron/0.4 mil, maximum 20 micron/0.8 mil as specified on a blasted surface.
Thinning: Selection of proper thinner is related to application conditions. At high temperatures, a specialTHINNER 08740 with a very slow flash-off may be used - please consult separate APPLICATIONINSTRUCTIONS.
Curing: Curing time is prolonged at relative humidity below 75%.Recoating: No maximum recoating interval for adhesion, but dictated by gradual breakdown and damage
during exposure and fabrication. Regarding treatment before recoating, please consult theAPPLICATION INSTRUCTIONS.
Shelf life: If shelf life is exceeded, it is usually possible to use the zincpaste (BASE), if any settling can beremixed. The LIQUID may be used provided it shows no signs of turbidity, but pot life will be verymuch shortened, see below. In any case, possible surpassing of storage time will be of 1-2 monthsmaximum (20°C/68°F) for the LIQUID.
Pot life: The pot life may be gradually reduced to 8 hours (20°C/68°F) as the liquid approaches the end ofits shelf life, assuming that it is stored under favourable conditions.
Note: HEMPEL'S SHOPPRIMER ZS 15890 is for professional use only.
Issued: October 1999 - 1589019890CO008HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPEL’S SHOPPRIMER ZS 15890HEMPEL'S LIQUID 99751
Scope: These Application Instructions cover surface preparation, application equipment, andapplication of HEMPEL’S SHOPPRIMER ZS 15890.
Surface preparation: a. Prior to abrasive blast cleaning of the steel, remove oil and grease and othercontamination with a suitable detergent, followed by high pressure fresh waterhosing.
b. Abrasive blasting to Sa 2½, ISO 8501-1: 1988.The abrasives must be capable of developing a surface profile equivalent toRugotest No. 3, N9a to N10a (Ra = 6-12.5 micron/1/4-1/2 mil), Keane-TatorSurface Comparator, 2-3 mils segments (average maximum peak to valleyroughness 50-75 micron/2-3 mils), or ISO Comparator, Medium (G,S).
Note: In case of abrasive blasting with shot instead of grit the resulting surfaceprofile will give lower adhesive values and thereby reduced mechanical propertiesof the coating. Recoating with heavy-duty systems such as HEMPADUR qualitiescan then generally be recommended only after a very thorough abrasivegritsweeping. Also for recoating with zinc silicates such as GALVOSIL 15700 athorough abrasive grit sweeping is mandatory to give the required surface profile.
c. When the abrasive blasting is completed, remove all grit and dust by vacuumcleaning.
Note: As abrasive blasted surfaces will rust rapidly, HEMPEL'S SHOPPRIMER ZS15890 must be applied immediately after the abrasive blasting and de-dusting. Ifre-rusting occurs, re-blasting is necessary.
Application equipment: HEMPEL’S SHOPPRIMER ZS 15890 can be applied by conventional spray equipment(pressure pot type only), airless spray equipment and brush.
Conventional spray equipment:Standard industrial spray equipment with mechanical agitator, pressure regulator, airfilters, and water traps.
Pot pressure: 2.5-5 bar (35-75 psi)Atomizing pressure: 1.5-2.5 bar (20-35 psi)Air hose: 10 mm (3/8") internal diameterMaterial hose: 13 mm (1/2") internal diameter
(Spray data are indicative and subject to adjustment).
Note: The hoses should be as short as possible, preferable not longer than 10metres/35 feet. Place the pressure pot at the same level as or at a higher level thanthe spray gun when spraying, owing to the weight of the paint.
The pressure pot may advantageously be replaced by a piston pump with a low ratio ofpressures.
In case of application stops, if possible re-circulate the paint through the hoses toavoid settling.
Clean all equipment promptly after use with the THINNER used.
Leave THINNER in the hoses when the equipment is not in use.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
HEMPEL’S SHOPPRIMER ZS 15890
Airless spray equipment:A large, slow-working, piston pump is recommended.
Gaskets: TeflonNozzle orifice: .019" through .023"Fan angle: 65° through 80°.Nozzle pressure: 80 bar (1200 psi).
(Spray data are indicative and subject to adjustment).
Note: During application stops, if possible re-circulate the paint through the hoses toavoid settling.
Clean all equipment promptly after use with the THINNER used.
Leave THINNER in the hoses when the equipment is not in use.
Mixing: a. Do not open packings until immediately before use. The entire content of the twopackings must be used for each batch to ensure a correct mixture. Left-overs inthe packings cannot be used later.
b. Before mixing, shake or stir the liquid very thoroughly.
c. Mix only in the proportions supplied. Do not vary or sub-divide.
d. Pour the liquid slowly into the zinc paste with constant mechanical stirring. Do notmix in the reverse order. Continue stirring until the mixture is free of lumps.
e. Strain the mixture through a screen, 60-80 mesh (250-160 DIN Norm. 4188).
f. For use in automatic shoppriming plants, adjust the mixture to a viscosity of15-18 sec/DIN 4 or equal with the prescribed thinner.
Thinning: Dilute the mixed product only.For airless spray application, add maximum 30% of THINNER.For conventional spray application, add maximum 30% of THINNER.For touch up by brush, add maximum 15% of THINNER.
Note: THINNER 08570 has a very fast flash-off which makes it suitable at lowtemperatures but gives risk for dry-spray at high temperatures. THINNER 08570 isgenerally not recommended for conventional spray application.
THINNER 08700 has a relative slow flash-off with good film formation at hightemperatures but slower drying at low temperatures.
If application takes place at high temperatures, ie 40-55°C/104-131°F, a specialTHINNER 08740 with even lower flash-off than THINNER 08700 should be used.Correct selection of thinner is dependent on the actual application conditions.
Pot life: 24 hours at 20°C/68°F in a tightly closed container.
Note: Prepare only the quantity that can be used within this period. Maintain constantagitation until the batch is depleted. After expiration of the pot life the mixture must notbe used even if it may appear to be unchanged.
The pot life may be gradually reduced to 8 hours (20°C/68°F) as the liquid approachesthe end of its shelf life, assuming that it is stored under favourable conditions.
Application: The coating must be wet and smooth just after application. Avoid dry-spray andexcessive film thicknesses, which especially may be encountered at manual sprayApplication.
Micro climate: Steel temperature: min 0°C/32°F, max . approximately 55°C/131°F.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SHOPPRIMER ZS 15890
Note: The temperature should be a few degrees above the dew point to avoidcondensation. At the freezing point beware of ice on the surface.
For application beyond the stated intervals contact HEMPEL for guidance.
Drying time: Dry to handle in 3-4 minutes at 20°C/68°F and sufficient ventilation in 15 micron/0.6mil dry film thickness.
Note: These figures apply when the temperature of the steel does not differ appreciablyfrom that of the surroundings.
Plates can be transported or stacked as soon as dry to handle.
Processing is only recommended when fully cured.
Curing time: Dependent on temperature and humidity.Relative humidity: min. 50%, preferably above 65%Min. temperature for curing is 0°C/32°F.At 20°C/68°F and min. 75% relative humidity the coating will be fully cured in 4 days.
At low humidities, curing can be promoted by hosing down the surface with water 24hours after application and by keeping the surface constantly wet until curing iscomplete.
Complete curing, in the sense of being ready for recoating, can be checked by rubbingthe coating with a rag soaked in THINNER 08700 used. If the coating remainsunaffected, the curing is complete.
Recoating interval: HEMPEL’S SHOPPRIMER ZS 15890 must be fully cured before recoating.
Recoating procedure: Remove oil and grease, dirt, etc. with suitable detergent followed by fresh water hosing.Remove weld spatters. Damaged areas, burns, etc. to be cleaned by rotary wirebrushing, by disc grinding, by abrasive sweeping, or by abrasive blasting according tospecification and touch up with the primer of the coating system proper. In case of"white rust" on intact surfaces, it is recommended to clean by fresh water hosing andscrubbing with stiff brushes.
It is risky to make a general cleaning of the exposed surface by grinding, and especiallyby wire-brushing as this process easily tends to give a smooth, polished surface towhich the adhesion of following coats usually will be reduced.
In any case abrasive grit sweep the entire surface if the subsequent coat is GALVOSIL15700 or similar, or if the shopprimer is polished (smooth) and the following paintsystem will be exposed to aggressive environments during service.
Especially if the paint system will be exposed to heavy wear - for instance aMULTI-STRENGTH-system - a very thorough abrasive grit sweeping is recommended, insevere cases a full reblasting.
Removal of dust is mandatory before recoating.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
HEMPEL’S SHOPPRIMER ZS 15890
Safety precautions: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999 - 1589019890CO008HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1589019890CO008
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX PRIMER 16320
Description: HEMPATEX PRIMER 16320 is a modified chlorinated rubber primer. Physically drying.It has good penetration and good water resistance. For service temperature range, seeREMARKS overleaf. Not suited in contact with animal or vegetable oils or solvents.
Recommended use: As a general purpose primer for Hempatex systems on interior and exterior steelworkexposed to moderately to severely aggressive marine and industrial environment.
PHYSICAL CONSTANTS:Finish: FlatColours: Green/RedShade Numbers: 41270/50890Volume by Solids: 46%Theoretical Spreading 9.2 m²/litre - 50 micronsRate: 375 sq.ft/US gallon - 2.0 milsFlash Point: 24ºC/75ºF A-Pensky, closed cup.Specific Gravity: 1.4 kg/litre
11.7 lbs/US gallonSurface Dry: 0.5 (approx) hour at 20ºC/68ºF (ISO 1517)Dry to Touch: 2 - 4 hours at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:
Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle Orifice: 0.023"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08080Indicated Film Wet: 100-125 microns/4-5 milsThickness: Dry: 50 microns/2.0 milsRecoating Interval: Min: when dry
Max: none (See REMARKS overleaf)
Safety: Packings are provided with applicable safety labels which should be observed. In addition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1632041270
HEMPATEX PRIMER 16320
Surface New steel: Abrasive blasting to Sa 2½ SSPC-SP-10. For temporary protection, if required,Preparation: use suitable shopprimer. All damage of shopprimer and contamination from
storage and fabrication should be thoroughly cleaned prior to final painting.For repair and touch-up use Hempatex Primer 16320.
Maintenance: Remove oil and grease with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning.. Remove all rust andloose material by abrasive blasting or power tool cleaning. Dust of residues.Touch up to full film thickness.
Application As dictated by normal good painting practice.Conditions: In confined spaces provide adequate ventilation during application and drying.
Subsequent Coat: Hempatex systems, or as per specification.
Remarks: Service Temperature:Tolerates temperatures up to 60ºC/140ºF in continuouse service andnon-continuously up to 80ºC/175ºF may cause film indentation. Whentemperature drops below, mechanical strength is recovered.
Film Thicknesses: May be specified in another film thickness than indicated depending onpurpose and area of use. This will alter spreading rate and may influencedrying time and recoating interval. Normal range is 40-50 microns/1.6-2.0mils.
Recoating Intervals: For multicoat application in 50 micron/2 mils dry film thickness per coat,recommended minimum recoating interval for the first coat is 4 hours at20C/68F.
V.O.C: The Volatile Organic Compounds are 492 gr/litre, 4.1 lbs/US gallon.
Note: Before overcoating after exposure in contaminated environment, clean surfacethoroughly by (high pressure) fresh water hosing and allow to dry.
Note: HEMPATEX PRIMER 16320 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1632041270
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S GALVOCOAT®16380
Description: HEMPEL'S GALVOCOAT 16380 is a cold-galvanizing paint based on a physically drying,synthetic binder with a high content of metallic zinc pigment which provides cathodicprotection of the steel.
Recommended use: 1. As a self-contained protective coating on steel in mild to moderately corrosiveatmosphere.
2. For repair of galvanized steel.
PHYSICAL CONSTANTS:Finish: FlatColours: Metal Grey (Other shades according to assortment list)Shade Numbers: 19840Volume by Solids: 53% Theoretical Spreading 7.1 m²/litre - 75 micronsRate: 284 sq.ft./US gallon - 3.0 milsFlash Point: 28ºC/82ºF A-Pensky, closed cup.Specific Gravity: 2.5 kg/litre
20.9 lbs/US gallonDry to Touch: 30 (approx) minutes at 20ºC/68ºF.
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle Orifice: 0.021"Nozzle Pressure: 150 bar/2175 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08080Indicated film thickness, wet: 150 microns/6 milsIndicated film thickness, Dry: 75 microns/3.0 milsRecoat interval, min: When dryRecoat interval, min: None (See REMARKS overleaf)
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1638019840
HEMPEL'S GALVOCOAT®16380
Surface New steel: Abrasive blasting to minimum Sa 2.Preparation:
Repair of galvanized steel or old zinc rich coating: Remove rust and other loose material by powertool cleaning to St 3.
Do not apply on other types of paint.
Application As dictated by normal good painting practice.Conditions: In confined spaces provide adequate ventilation during application and drying.
Subsequent Coat: Optional, for cosmetic reasons.As per specification.
Remarks: No maximum recoating interval, but if formation of zinc salts is noticed, hose down surface withfresh water and scrub with a stiff brush. Allow surface to dry before overcoating.
Note: HEMPEL'S GALVOCOAT 16380 is for professional use only.
Safety: Labelling according to EEC Regulations:Symbols: R10 FLAMMABLE
Do not breathe vapours/spray mist. Use only in well-ventilated areas. If necessary wear suitablerespiratory protection. Keep out of reach of children. Open with care, danger of overpressure.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1638019840
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ZINC PRIMER 16490
Description: HEMPEL’S ZINC PRIMER 16490 is a one-component, high molecular weight, quickdrying, phenoxy coating with a high content of zinc.
Recommended use: 1. As a protective primer on steel in severely corrosive environment. 2. For repair of GALVOSIL and other zinc rich coatings.
3. For repair of galvanized steel.
Service temperatures: maximum, dry: 120°C/248°F, however, depending on the subsequent coat.
Availability: Subject to confirmation. PHYSICAL CONSTANTS: Colours/Shade nos: Metal grey/19840Finish: Flat Volume solids: 34% Theoretical spreading rate: 9.7 m²/litre - 35 micron
390 sq.ft./US gallon - 1.4 milsFlash point: 7°C/45°F Specific gravity: 2.0 kg/litre - 16.7 lbs/US gallonSurface dry: 15 (approx.) minutes at 20°C/68°F (ISO 1517)Dry to touch: 30 (approx.) minutes at 20°C/68°FV.O.C.: 593 g/litre - 4.9 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS: Application method: Airless spray Brush Thinner (max. vol.): 08450 or 08710 (5%) 08450 (5%) Nozzle orifice: .019"-.021"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08450 or HEMPEL'S TOOL CLEANER 99610 Indicated film thickness, dry: 35 micron/1.4 milsIndicated film thickness, wet: 100 micron/4 mils
Recoat interval, min: 30 minutes (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1649019840CO006
HEMPEL’S ZINC PRIMER 16490
SURFACE New steel: Abrasive blasting to minimum Sa 2½, SSPC-SP-10 with a surface profile correspondingPREPARATION: to Rugotest No. 3, N9a to N10, preferably BN9a to BN10, Keane-Tator Comparator, 2.0 G/S or ISO
Comparator, Medium (G).Repair of galvanized steel or zinc-rich coating: Remove oil and grease, etc. with suitabledetergent. Remove salts and others contaminants by (high pressure) fresh water cleaning.Remove rust and loose material by abrasive blasting or power tool cleaning (avoid burnishing thesurface). Dust off residues.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
Tolerates low temperature application which, however, will increase drying time. At the freezingpoint and below be aware of the risk of ice on the surface, which will hinder the adhesion.In confined spaces provide adequate ventilation during application and drying.
PRECEDING None.COAT:
SUBSEQUENT Recommended are HEMPADUR or HEMPATEX Systems according to specification. COAT:
REMARKS: Note: Due to a risk of corrosion from possible moisture penetration, many experts advise againstthe use of zinc primers behind high temperature insulation.
Film thicknesses: May be specified in another filmthickness than indicated depending on purpose and area of use.Normal range is 25-35 micron/1.0-1.4 mils.
Recoating: If the coating has been exposed to the atmosphere for some time, the surface should bethoroughly hosed down and scrubbed with a stiff brush to remove “white rust” (zinc corrosionproducts) in addition to the usual cleaning for dirt, oil, grease, etc. Allow surface to dry beforerecoating.When overcoated, the entire paint system must be through dry and fully cured before fullmechanical strength is obtained.Care should be taken to avoid water contamination in the cans to prevent gelling or gassing.
Note: HEMPEL'S ZINC PRIMER 16490 is for professional use only.
Issued: September 1996 - 1649019840CO006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1649019840CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPATEX®MIO 16670
Description: HEMPATEX MIO 16670 is a chlorinated rubber-based paint, pigmented with micaceousiron oxide (MIO). Physically drying. It has good resistance to salt water, and a range ofchemicals. Is also suited for application under humid conditions, on damp steelsurfaces and may be applied on moist surfaces. For definition, see REMARKS overleaf.Not suited in contact with animal and vegetable oils or solvents. For servicetemperature range, see REMARKS overleaf.
Recommended ue: 1. As a primer on exterior steelwork in moderately to severely corrosive environment,including permanently submerged areas.
2. In multi-coat applications as both intermediate and finishing coat.
AVAILABILITY: Subject to confirmation
PHYSICAL CONSTANTS:Finish: FlatColours: Grey (Other colours according to assortment list)Shade Nos: 12430 Solids by Volume: 38% Theoretical Spreading 4.8 m²/litre - 80 micronsRate: 194 sq.ft./US gallon - 3.2 milsFlash Point: 24ºC/75ºF Abel-Pensky, closed cupSpecific Gravity: 1.4 kg/litre
11.7 lbs/US gallonSurface Dry: 1 (approx) hour at 20ºC/68ºF (ISO 1517)Dry to Touch: 8 (approx) hours at 20ºC/68ºFShelf Life: 1 year at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle Orifice: 0.021" - 0.023"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08080Indicated film thickness, wet: 225 microns/9 milsIndicated film thickness, dry: 80 microns/3.2 mils (See REMARKS overleaf)Recoat interval, min: 12 hours (20ºC/68ºF) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1667012430
HEMPATEX®MIO 16670
Inhibitors are generally not recommended for surfaces which will beimmersed.
Note:
Dry or wet abrasive blasting to Sa 2½. In case of wet abrasive blasting asuitable inhibitor eg: HEMPEL'S WET BLAST INHIBITOR 97670 may be used.Surplus inhibitor and residual abrasives and sludge must be removed by high pressure fresh water cleaning before overcoating.
For major repairwork/new steel(humid conditions):
Remove oil and grease etc., with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Removal of all rust andloose material by wet or dry abrasive blasting or power tool cleaning. Featheredges to sound and intact areas. After wet abrasive blasting hose down thesurface with fresh water. Touch up bare spots to full film thickness when thesurface has reached the condition of being damp, may be moist (seeREMARKS below).
Maintenance:
Abrasive blasting to Sa 2½, SSPC-SP-10. For temporary protection, ifrequired, use suitable shopprimer. All damage of shopprimer andcontamination from storage and fabrication should be thoroughly cleaned priorto final painting. For repair and touch-up use HEMPATEX MIO 16670
New steel:Surface Preparation:
Application The surface must be completely clean and dry at the time of application. Tolerates lowConditions: temperature application which, however, will increase drying time. At the freezing point and below,
be aware of the risk of ice on the surface, which will hinder the adhesion. In confined spacesprovide adequate ventilation during application and drying.
Subsequent Coat: HEMPATEX Systems, or as per specification depending on area of use.
Remarks: Service Temperature:Tolerates temperatures up to 60C/140F. In continuous service andnon-continuously up to 80C/175F. Being a thermoplastic product prolongeddirect contact at temperatures above approximately 40C/105F may cause filmindentation. When temperature drops below, mechanical strength isrecovered.
Definitions: Damp surface: Surface on which water is not readily detectable, but the temperature of thesurface is below the dew point.
Moist surface: Surface from which standing water and droplets have been removed, but onwhich there is a noticeable film of water.
Wet surface: Surface on which droplets or standing water is present.Occurrence of standing water or droplets on the painted surface immediatelyafter application may result in discolouration.
Film Thicknesses: May be specified in another film thickness than indicated depending onpurpose and area of use. Normal range is 40-100 microns/4.0 mils. Thiswill alter spreading rate and may influence amount of thinning needed, dryingtime and recoating interval.
Recoating Interval: In case of multi-coat application, drying time and minimum recoating intervalwill be influenced by the number of coats and by the thickness of each coatapplied - reference is made to the corresponding painting specification. Beforeovercoating after exposure in contaminated environment, clean surfacethoroughly by (high pressure) fresh water hosing and allow to dry.
V.O.C: The Volatile Organic Compounds are 560 g/litre, 4.6 lbs/US gallon.
Safety: Packings are provided with applicable labels which should be observed.In addition, national or local safety regulations should be followed.
As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paint with skinand eyes, should be avoided. Forced ventilation should be provided when applying paint inconfined spaces or stagnant air. Even when ventilation is provided, respiratory, skin, and eyeprotection are always recommended when spraying paint.
Note: HEMPATEX MIO 16670 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1667012430
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SILICONE ZINC 16900
Description: HEMPEL’S SILICONE ZINC 16900 is a heat resistant zinc pigmented silicone primer. Itis air drying at ambient temperature and resists temperatures up to 400°C/750°F. (SeeREMARKS overleaf)
Recommended use: As a primer for long-time corrosion protection of steel exposed to high temperatures(from 100°C/210°F to 400°C/750°F).
Service temperatures: Maximum service temperature is depending on the subsequent coat. When topcoatedwith HEMPEL’S SILICONE ALUMINIUM 56910 dry service temperature is max.400°C/750°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Metal grey/19840Finish: FlatVolume solids, %: 57 ± 1Theoretical spreading rate: 14.3 m²/litre - 40 micron
571 sq.ft./US gallon - 1.6 milFlash point: 25°C/77°FSpecific gravity: 2.6 kg/litre - 21.7 lbs/US gallonSurface dry: 1 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 2-3 hours at 20°C/68°FV.O.C.: 390 g/litre - 3.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .017"Nozzle pressure: 125 bar/1800 psi
(Airless spray data are indicative and subject to adjustments)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 40 micron/1.6 milIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 4 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1690019840CO004
HEMPEL’S SILICONE ZINC 16900
SURFACE Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and other PREPARATION: contaminants by high pressure fresh water cleaning.
Abrasive blasting to Sa 2½. If shopprimer is required, only zinc silicate type is recommended.
APPLICATION Clean and dry surface with a temperature above the dew point to avoid condensation. In confined CONDITIONS: spaces provide adequate ventilation during application and drying.
PRECEDING None, or zinc silicate shopprimer.COAT:
SUBSEQUENT HEMPEL’S SILICONE TOPCOAT 56900, HEMPEL’S SILICONE ALUMINIUM 56910, HEMPEL’SCOAT: SILICONE ACRYLIC 56940 or similar according to specification.
REMARKS: Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryimportant that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Do not expose the paint system to heat before it is through dry (minimum 24 hours at 20°C/68°F).Film thicknesses: It is recommended to avoid too high thicknesses of the paint as this will give a risk of blistering at
later heating. For high temperature service, the total dry film thickness of the paintsystem shouldpreferably be kept at 75 micron/3 mils.
Recoating May be recoated both at ambient temperature and after being heated for one hour to aIntervals: temperature above 200°C/392°F.
Before recoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
Note: HEMPEL’S SILICONE ZINC 16900 is for professional use only.
Issued: October 1999 - 1690019840CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1690019840CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®ZINC 17360CURING AGENT 97040
Description: HEMPADUR ZINC 17360 is a two-component, zinc rich epoxy primer. It cures to a hardwearing and highly weather-resistant coating. Offers cathodic protection of localmechanical damage.
Recommended use: As a "V.O.C.-compliant", versatile, long-term primer on steel for epoxy, vinyl and acryliccoating systems in medium to severely corrosive environments.
Service temperatures: Maximum, dry: 160°C/320°F, however, depending on the subsequent coat.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red-grey/19830Finish: FlatVolume solids, %: 65 ± 1Theoretical spreading rate: 13.0 m²/litre - 50 micron
521 sq.ft./S gallon - 2 milsFlash point: 24°C/75°FSpecific gravity: 2.7 kg/litre - 22.5 lbs/US gallonSurface dry: ½ (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 1 (approx.) hour at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 335 g/litre - 2.8 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 17360: Base 17369 : Curing agent 97040
4 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): 08450 (5%) 08450 (15%) 08450 (5%) (See REMARKS overleaf)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .017"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)
Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1736019830CO007
HEMPADUR ZINC 17360
SURFACE Remove oil and grease thoroughly with suitable detergent. Remove salt and other contaminantsPREPARATION: by high pressure fresh water cleaning.
Abrasive blasting to Sa 2½ with a sharp-edged surface profile corresponding to Rugotest No. 3,BN9a, Keane-Tator Comparator, 2.0 G/S, 2 S, or ISO Comparator, Medium (G).
APPLICATION Use only where application and curing can proceed at temperatures above -10°C/15°F. TheCONDITIONS: temperature of the surface must also be above this limit. The paint itself should be 15°C/59°F or
above. Apply only on a dry and clean surface with a temperature above the dew point to avoidCondensation.In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT As listed below in accordance with specification.COAT:
REMARKS: Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryimportant that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.Most typical range is 40-50 micron/1.6-2 mils, but thicknesses down to 15 micron/0.6 mils (extrathinning) and up to 80 micron/3.2 mils may be possible. This will alter spreading rate and mayinfluence amount of thinning necessary, drying time, and recoating interval.Recoating: Recoating intervals, 50 micron dry film thickness for HEMPADUR ZINC 17360:
Not relevantNot relevantNot relevant30 days*
Not relevant
8 hours5 hours8 hours
30 days*30 days*
12 hours8 hours12 hours
NoneNone
Not relevantNot relevantNot relevant
4 hoursNot relevant
1 hour1 hour1 hour4 hours4 hours
30 minutes30 minutes30 minutes
2 hours2 hours
5803046410. 46370
463301763045880
SevereMediumSevereMediumRecoated with
(Quality numbers only)
Waterimmersion**
AtmosphericWater
immersion**
Atmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
* Depending on actual local conditions, extended maximum recoating intervals may apply.Please contact HEMPEL for further advice.
** Water immersion service is only recommended if HEMPADUR ZINC 17360 is applied in maximum 30-40 micron/1.2-1.6 milsand recoated with en epoxy coating system in 250-300 micron/10-12 mils.
If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: Before recoating after exposure in contaminated environment, clean the surface thoroughly by highpressure fresh water hosing and allow to dry. In addition, scrubbing with a stiff brush may benecessary to remove zinc corrosion products (white rust).HEMPADUR ZINC 17360 is for professional use only.
Issued: March 2001 - 1736019830CO007HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1736019830CO007
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®17630/HEMPADUR®17633
17630: BASE 17639 with CURING AGENT 9733017633: BASE 17639 with CURING AGENT 98420
Description: HEMPADUR 17630/17633 is a two-component, high-build, polyamide adduct-curedepoxy paint which cures to a hard and tough coating with good resistance to abrasion,seawater and crude oils.
Recommended use: As a selfprimed coating for ballast water tanks and similar. As a primer for epoxysystems for atmospheric or in-water service. Suitable for application down to -10°C/15°F.HEMPADUR 17633 is intended for use in cold/temperate climates, HEMPADUR 17630is intended for use in temperate to warm climates.
Service temperatures: Dry: Maximum 120°C/248°F (See REMARKS overleaf)Ballast water service: Resists normal ambient temperatures at sea*Other water service: 40°C/104°F (no temperature gradient)Other liquids: Contact HEMPEL*Avoid long-term exposure to negative temperature gradients.
Certificates/Approvals: Classification B1 by Marintek, Norway.Approved by Lloyd’s Register of Shipping as a provisionally recognized corrosion controlcoating.Approved as a corrosion control coating by Maritime Register of Shipping, Russia.Approved as a ballast tank coating by Germanischer Lloyd, Germany.HEMPADUR 17630 has been tested for non-contamination of grain cargo at theNewcastle Occupational Health, Great Britain.HEMPADUR 17630 complies with Section 175.300 of the Code of Federal Regulationsin respect of carriage of dry foodstuffs (FDA) in spaces with an internal surface arealarger that 1000 m²/10.750 sq.ft.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version; mixed product: 17630 17633Colours/Shade nos: Grey/12170 - cream/20320 Grey/12170 - cream/20320Finish: Semi-flat Semi-flatVolume solids, %: 68 ± 1 68 ± 1Theoretical spreading rate: 4.5 m²/litre - 150 micron 4.5 m²/litre - 150 micron
182 sq.ft./S gallon - 6 mils 182 sq.ft./S gallon - 6 milsFlash point: 32°C/90°F 32°C/90°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallon 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 7-8 hours at 20°C/68°F 20 hours (app.) at 5°C/41°FFully cured: 7 days at 20°C/68°F 20 days at 5°C/41°FV.O.C.: 315 g/litre - 2.6 lbs/US gallon 315 g/litre - 2.6 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS: 17630 17633Mixing ratio: Base 17639 : Curing agent 97330 Base 17639 : Curing agent 98420
4 : 1 parts by volume 4 : 1 parts by volumeApplication method: Airless spray Brush Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%) 08450 (5%) 08450 (5%)Pot life: 2 hours (20°C/68°F) 2 hours (20°C/68°F)Induction time: See REMARKS overleafNozzle orifice: .019"-.023"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 150 micron/6 milsIndicated film thickness, wet: 225 micron/9 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: See separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004 / 1763312170CO001
HEMPADUR 17630/17633
SURFACE New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and other PREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½. For temporary
protection, if required, use a suitable shopprimer. All damage of shopprimer and contaminationfrom storage and fabrication should be thoroughly cleaned prior to final painting. For repair andtouch up, use HEMPADUR 17630.Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to St 3 (minor areas) or by abrasive blasting to min. Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance of HEMPADUR 17630/17633.As an alternative to dry cleaning, water jetting to sound, well adhering coat and/or to steel. Intactcoat must appear with roughened surface after the water jetting. By water jetting to steel,cleanliness shall be WJ-3 to WJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No.5/SSPC-SP 12). A flash-rust degree of maximum FR-2 (atmospheric exposure) / FR-2, preferablyFR-1 (immersion) (Hempel standard) is acceptable before application. Feather edges to sound andintact paint. Dust off residues. Touch up to full film thickness.On pit-corroded surfaces, excessive amounts of salt residues may call for water jetting or wetabrasive blasting, alternatively dry abrasive blasting followed by high pressure fresh water hosing,drying, and finally, dry abrasive blasting again.
APPLICATION Use only where application and curing can proceed at temperatures above -10°C/14°F (curingCONDITIONS: agent 98420) and 0°C/32°F (curing agent 97330). The temperature of the paint itself should be
above 15°C/59°F for proper application. Apply only on a dry and clean surface with a temperatureabove the dew point to avoid condensation.In confined spaces provide adequate ventilation during application and drying.
SUBSEQUENT None or according to specification.COAT:
REMARKS: Certificates are issued under the former quality number 1763.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreService sensitive to mechanical damage and chemical exposure at elevated temperatures is alsoTemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 125-200 micron/5-8 mils.
Mixing/ To facilitate proper application properties it is recommended to allow the thoroughly mixed BASEinduction time: and CURING AGENT to prereact before application. In case two-component spray-equipment is
used, paint material is to be heated. Consult separate APPLICATION INSTRUCTIONS.
Note: HEMPADUR 17630/17633 is for professional use only.
Issued: March 2002 - 1763012170CO004 / 1763312170CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004 / 1763312170CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®17630/HEMPADUR®17633
Medium to high temperatures: 17630 with CURING AGENT 97330Low to medium temperatures: 17633 with CURING AGENT 98420
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR 17630/17633.
Ballast tanks, steel work: For optimum performance the following is recommended:All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in welding seams, undercuts, etc.should be avoided. If found, they may necessitate extra stripe coating or filling (however,the classification societies' recommendations are to be followed).
All sharp edges to be broken or rounded depending on the actual conditions and thedesign lifetime. Laminations to be removed. However, rolled profiles, etc. from the steelmills normally have acceptably rounded edges.
All loose weld spatters to be removed.
Well adhering, scattered weld spatters are acceptable, but will need additional touch-up.If dense, they must be removed by grinding.
Requirements to the "surface quality" of welds according to WELD REPLICA NACE RP0178 minimum Grade E (NACE Standard RP0178-95).
Abrasive blasting/ Before blasting any deposits of grease or oil must be removed from the steel surfaceabrasive sweep blasting: with a suitable detergent followed by fresh water hosing. Minor spots of oil/grease may
be cleaned with thinner and clean rags - avoid smearing out the contamination. Possiblealkali weld deposits, chemicals used for testing of welds, soap residues from thepressure testing must be removed by fresh water hosing.
Repair:Before blasting, old steel surfaces must be checked for any contamination. Possibleblisters must be broken. If thick rust scale has been removed or deep pittings havebeen encountered, control procedures for contamination must be carried out. If stillcontaminated, the abrasive blast cleaned steel surface will need a repeated cleaning forsalts and/or oil/grease followed by final abrasive blast cleaning.
Newbuilding/new steelwork: To obtain full performance of the ballast tank coating,welds, burns, damaged and rusty shopprimer must be abrasive blast cleaned to Sa 2½.Minor areas mechanically cleaned to St 3.
If welds have previously been coated with a (shop)primer just after welding this(shop)primer must be removed by abrasive blasting (sweeping) in order to obtainoptimum performance.
Intact shopprimer:Zinc salted surfaces, deposits of black iron oxides of plasma cutting and similar foreignmatters to be removed by light abrasive sweep blasting. Chalk markings and platemarking of a non-compatible nature to be removed as well.
The shopprimer must have been checked randomly for excessive film thicknesses andareas detected to have film thicknesses above approx 40 micron/1.6 mils (as measureddirectly on the shopprimed surface with equipment calibrated on smooth steel) are to besweep blasted in order to remove most of the shopprimer.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004/1763312170CO001
HEMPADUR 17630/17633
Spot-checking for possible salt contamination of the surface to be executed before andafter abrasive sweep blasting.
When blasting, the importance of working systematically must be stressed. Poorlyblasted areas covered with dust are very difficult to locate during the blast inspectionmade after the rough cleaning.
In the case of abrasive blast cleaning, the surface profile must be equivalent toRugotest No. 3, BN9-BN10 or Keane-Tator Comparator, 3.0 G/S. According to ISO8503-1 the grade will be MEDIUM (G).
Note: If any doubt exists about the quality of the primary surface preparation (beforeshoppriming), the substrate must be re-blasted in situ as defined above.
Block assembly zones: Overlap zones must be treated with great care. Damage causedby possible over-blasting must be avoided, paint edges must be feathered andconsecutive layers of paint coatings given greater and greater overlaps - old layers beingroughened corresponding to these overlaps (when sand papering, use free-cut paper,grain size 80).
Furthermore, these areas may be either masked off with tape - to keep them as narrowas possible - or left with a thin zinc epoxy primer coat applied on these areas aftersecondary surface preparation at blockstage.
Secondary surface preparation of block assembly zones are preferably to be abrasivespot-blasted. However, mechanical cleaning to St 3 may be acceptable if zones arenarrow and an extra coat of HEMPADUR 17630/17633 is applied to these areas. Theprocedure of masking off with tape or using the zinc epoxy primer as described abovemay advantageously be used in case of mechanical cleaning.
Repair:Corroded pits deeper than approx 2 mm, but not repaired by welding, are recommendedto be filled with HEMPADUR EPOXY FILLER 35250 after blast priming has been carriedout.
Stainless Steel: (Ballast tanks of chemical carriers) to be abrasive blast cleaned to auniform, sharp, dense, profile (Rugotest No. 3, BN9-10, ISO Comparator Medium (G),Keane-Tator Comparator 2.0 G/S corresponding to Rz minimum 50 micron). Any salts,grease, oil etc. to be removed before abrasive blasting is commenced.
Water jetting: This procedure will primarily be relevant for repair jobs. However, the very good removalof water-soluble salts may also make it useful in other cases.
The resulting standard is to be equal to the WJ-2 (NACE No. 5/SSPC-SP 12 "SurfacePreparation and Cleaning of Steel and other Hard Materials by High and Ultra-HighPressure Water Jetting prior to Recoating", 1995).
Sufficient dehumidification equipment must be used to dry out the tanks as quickly aspossible between the water jetting and the coating application.
Local ventilators may be required to distribute the drying air evenly in tanks. All "slurry"is to be removed before it dries. New rust will be acceptable as discoloration only, notas powdery, loose rust. Acceptable degree of "flash rust" is maximum FR-2 (HEMPELstandard). Inhibitors are not to be used.
All surfaces must be free from contamination at the time of painting and the relativehumidity is to be below 85%.
Refurbishment: It is recommended to carry out rough abrasive blast cleaning - or water jetting - tofacilitate visual inspection and any necessary repair of the existing steel work. In thecase of pit-corroded tank bottoms this rough blasting will also provide a better basis fora decision between welding of corroded pits or repair by filling.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004/1763312170CO001
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 17630/17633
A main concern is the contamination from sea water (water-soluble, corrosive salts). Thepreventive method will be to include very thorough cleaning with plenty of fresh water,please see below.
The maximum allowable concentration of chlorides on steel surfaces immediatelybefore application is 7.0 microgrammes/cm² as detected by the "Bresle Method".
In the case of contamination, cleaning procedures must be repeated and/or improved.Especially pit-corroded steel will need special attention and the only possible way toremove contamination from the pits may often be to carry out very thorough cleaningwith fresh water after abrasive blast cleaning. After repeated control and drying, theentire surface will need abrasive blast cleaning to obtain the specified degree ofcleaning. Alternatively, the pit-corroded areas are cleaned by water jetting, any surplus ofwater is mopped up or removed by vacuum cleaning, allow to dry.
Note: Actual type of steel work and surface preparation is dependent on factors sucha shipyard technology, contractual specification, required lifetime, etc. Reference isalso made to HEMPEL’s Technical Standard for Ballast Tank Coating Work.
Application equipment: HEMPADUR 17630/17633, being a high viscosity material, may require specialmeasures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min 45:1Pump output: 12 litres/minute (theoretical)Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Filter: 60 mesh
Regular surfaces:Nozzle size: .021"-.023”Fan angle: 60-80°.Complicated surfaces:
Nozzle size: .019"Fan angle: 40°.
After finishing the application, clean the equipment immediately with HEMPEL’S TOOLCLEANER 99610.
Note: Increasing hose diameter may ease paint flow thereby improving the spray fan. Iflonger hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approximately 5% THINNER 08450 may be added, but thinning mustbe done with care as the maximum obtainable film thickness is reduced significantly byoverthinning.
Airless spray data are indicative and subject to adjustment.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004/1763312170CO001
Application: Film-build/continuity: With this ballast tank coating it is of special importance that acontinuous, pinhole-free paint film is obtained at application of each spray applied coat.An application technique which will ensure good film formation on all surfaces must beadopted. It is very important to use nozzles of the correct size, not too big, and to havea proper, uniform distance of the spray gun to the surface, 30-50 cm should be aimedat. Furthermore, great care must be taken to cover edges, openings, rear sides ofstiffeners etc. Thus, on these areas a stripe coat will usually be necessary. To obtaingood and steady atomising, the viscosity of the paint must be suitable and the sprayequipment must be sufficient in output pressure and capacity. At high workingtemperatures, use of extra thinner may be necessary to avoid dust-spray.
The paint layer must be applied homogeneously and as close to the specification aspossible. The consumption of paint must be controlled to avoid exaggerated filmthickness, eg by controlling paint consumption and/or measuring wet film thickness.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
Stripe coating: may either be applied by airless spray, (relatively small, narrow-anglednozzles) or by hand-tools. Apply the stripe coat as a uniform, regular film withoutexcessive brush or roller marks in order to avoid cratering by entrapped air.
Pot life/mixing/ When measured under standard conditions the pot life is 3 hours at 15°C/59°F and 2induction time: hours at 20°C/68°F. However, for a 20 litres/5 US gallons mix, the heat developed by(both curing agents): the chemical reaction between BASE and CURING AGENT may make the corresponding
practical pot life shorter.
a. Mix the entire content of corresponding base and curing agent packings. If it isnecessary to mix smaller portions, this must be done properly by either weighingbase and curing agent in the prescribed weight ratio: 86 parts by weight of baseand 14 parts by weight of curing agent or by volume: 4.0 parts by volume base and1.0 parts by volume curing agent.
b. Stir the mixed paint thoroughly by means of a clean mechanical mixer until ahomogeneous mixture is obtained.
c. Use all mixed paint before the pot life is exceeded. The pot life depends on thetemperature of the paint as shown in table below (valid for a 20 litres can):
1 hour1½ hours2 hours3 hoursPot life
30°C/86°F2)25°C/77°F20°C/68°F15°C/59°F1)Temperature of mixed paint
1) At 15°C/59°F and below, the viscosity can be too high for airless spray application.2) Temperatures above 30°C/86°F should preferably be avoided.
Induction time:At steel temperatures below 5°C/41°F the paint may advantageously be prereacted10-20 minutes before spray application (longer pre-reaction time at lower temperatures).
When two-component spray equipment is used, heating may be relevant to obtain aproper spray fan and a uniform and smooth paint film. This can either be done bypreheating the two-component paint or by using a flow-heater on the pressure side. Asan indication, a paint temperature of approx 40°C/104°F will be relevant, but has to beadjusted according to the actual conditions.
Physical data (HEMPADUR 17630 in a dry film thickness of 150 micron/6 mils):versus temperature:
2½ days5 days10 days20 daysInitial curing*
5 hours3½ days
7 hours7 days
14 hours14 days
32 hours28 days
Drying timeCuring time
30°C/86°F20°C/68°F10°C/50°F0°C/32°FSurface temperature
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004/1763312170CO001
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 17630/17633
(HEMPADUR 17633 in a dry film thickness of 150 micron/6 mils):
10 days20 days40 daysInitial curing*
14 hours14 days
32 hours28 days
63 hours56 days
Drying timeCuring time
10°C/50°F0°C/32°F-10°C/14°FSurface temperature
* When the state "initial curing" has been reached, the coating may exceptionally be exposedto ballast water provided it has been applied within the specified limits of film thicknessesand that all painted areas have been subject to thorough ventilation.
Recoating: Recoating intervals (provided proper ventilation)(150 micron/6 mils dry film thickness)
90 days*90 days54 hours
(90 days)*90 days
108 hours
36 hours36 hours36 hours
3 days3 days3 days
30 days*30 days12 hours
90 days*90 days24 hours
8 hours8 hours8 hours
16 hours16 hours16 hours
Recoted with:(quality no. only)
Itself (ballast tanks)4518246330
0°C/32°F-10°C/14°F0°C/32°F-10°C/14°F20°C/68°F10°C/50°F20°C/68°F10°C/50°FSteel temperatureMaximumMinimumMaximumMinimum
1763317630
*Depending on actual local conditions, extended maximum recoating intervals may apply. Please contact HEMPELfor further advice.
Maximum recoating intervals:If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion or in thecase of recoating with coatings other than HEMPADUR, apply a (thin) additional coat ofHEMPADUR 17630/17633 within the following directions for recoating:
• Long recoating intervals:A completely clean surface is mandatory to ensure intercoat adhesion, especially inthe case of long recoating intervals. Any dirt, oil and grease have to be removed witheg suitable detergent followed by high pressure fresh water cleaning. Salts to beremoved by fresh water hosing.
• Any degraded surface layer, as a result of a long exposure period, must beremoved as well. Water jetting may be relevant to remove any degraded surface layerand may also replace the above-mentioned cleaning methods when properlyexecuted. Consult HEMPEL for specific advice if in doubt.
To check whether the quality of the surface cleaning is adequate, a test patch may berelevant
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: December 2001 - 1763012170CO004/1763312170CO001HEMPEL’S MARINE PAINTS A/S.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1763012170CO004/1763312170CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®PRIMER HI-BUILD 18030
Description: HEMUCRYL PRIMER HI-BUILD 18030 is a water-borne, acrylic dispersion paint with goodanticorrosive properties. Especially suited for application by airless spray.
Recommended use: As a primer in water-borne paint systems on interior and exterior steelwork in mildly tomoderately corrosive environment.May also be used as a primer in water-borne paint systems on hot dip galvanized steel,aluminium, and stainless steel in mildly corrosive environment.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish authorities according to IMOresolution MSC 61 (67).Has a Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light grey/12170 - Red/50710Finish: FlatVolume solids, %: 43 ± 1Theoretical spreading rate: 5.7 m²/litre - 75 micron
230 sq.ft./US gallon - 3 milsFlash point: > 66°C/151°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: ½ (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 1½ (approx.) hour at 20°C/68°FV.O.C.: 22 g/litre - 0.2 lbs/US gallon
135 g/litre - 1.1 lbs/US gallon (ASTM D 3960 - water-reduced)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:
Application method: Airless spray Brush (touch-up)Thinner (max. Vol.): Fresh water (5%) HEMUCRYL BRUSH AGENT 99810 (3-8%)Nozzle orifice: .015"-.019"Nozzle pressure: 130 bar/1900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See APPLICATION INSTRUCTIONS)Indicated film thickness, dry: 75 micron/3 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 2 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1803012170CO009
HEMUCRYL PRIMER HI-BUILD 18030
SURFACE See separate HEMUCRYL APPLICATION INSTRUCTIONS.PREPARATION:
APPLICATION See separate HEMYCRYL APPLICATION INSTRUCTIONS.CONDITIONS:
SUBSEQUENT HEMUCRYL ENAMEL HI-BUILD 58030 or according to specification.COAT:
REMARKS:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 50-100 micron/2-4 mils. When used in 50 micron dry film thickness, 3-5% thinning will benecessary to secure proper film formation. For proper film formation the recommended nozzle sizesshould be used.
Brush application: Add 3-8% by volume of HEMUCRYL BRUSH AGENT 99810. Typical dry film thickness per coat willbe 30-40 micron/1.2-1.6 mils.
Recoating: No maximum recoating interval, but after prolonged exposure to polluted atmosphere removeaccumulated contamination by high pressure fresh water cleaning and allow to dry.
Other REMARKS: See separate HEMUCRYL APPLICATION INSTRUCTIONS.Note: HEMUCRYL PRIMER HI-BUILD 18030 is for professional use only.
Issued: December 2000 - 1803012170CO009HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1803012170CO009
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPEL’S HEMUCRYL product rangeScope: These Application Instructions cover surface preparation and application conditions of
HEMPEL’S HEMUCRYLs.
Surface preparation, New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherprimers: contaminants by (high pressure) fresh water cleaning. Abrasive blasting tominimum Sa 2½. For temporary protection, if required, use suitable shopprimer. Alldamaged shopprimer and contamination from storage and fabrication should bethoroughly cleaned prior to final painting. For repair and touch-up use the specifiedHEMUCRYL primer type.
Repair: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove rust and loose paint byabrasive blasting or power tool cleaning to St 3 before recoating. Touch up bare spotswith the specified HEMUCRYL primer type.
Aluminium: Very thorough degreasing, followed by (high pressure) fresh water cleaningto remove all salts and other contamination. Any anodizing must be completelyremoved. Thorough sand papering or abrasive sweeping with mineral abrasives isrecommended. Cast aluminium is recommended to be abrasive swept to a uniform,evenly grey appearance.
Stainless steel: Very thorough degreasing with alkaline degreaser, ie HEMPEL'S LIGHTCLEANER 99350, followed by fresh water hosing to remove all contamination.
Hot-dipped galvanized steel: Wet rubbing/grinding with ammonia water 1:20 followedby fresh water hosing. In the case this method is not feasible, the procedure asdescribed for stainless steel may be used.
Zinc silicate coated surfaces: Remove oil and grease, etc, with suitable detergent.Remove salt and other contaminants by high pressure fresh water cleaning. Afterexposure to high humidity, zinc salts ("white rust") must be removed carefully by (highpressure) fresh water cleaning - if necessary combined with scrubbing with stiff nylonbrushes. Consult the APPLICATION INSTRUCTIONS for the relevant GALVOSIL product.
Note:Among the HEMUCRYL primer types, HEMUCRYL TI-COAT 18200 is designed to be usedas the first coat on aluminium, hot-dop galvanized steel, stainless steel and on zincsilicate coated surfaces.
Surface preparation, Preceding coats should be sound and tightly adhering. Remove oil and grease withtopcoats: suitable detergent. Remove salts and other contaminants by (high pressure) fresh water
cleaning. Remove rust and loose material by abrasive blasting or power tool cleaning.Dust off residues. Touch up to full system before recoating with specified HEMUCRYLtopcoat type.
Concrete: Any oil, grease and other contaminants should be removed by eg volatilizingby flame cleaning or treatment with suitable detergent, the latter in the following way:
1) Saturation of the surface with fresh water2) Washing with suitable detergent followed by fresh water hosing
Remove loose material eg by stiff brushes or blasting, high pressure jetting or flamecleaning followed by fresh water hosing depending on circumstances. Three lastmentioned methods are also able to remove scum layer if necessary. After surfacepreparation the surface should feel solid and hard. Remove dust.
Saturate surface with suitable sealer, eg microdispersed acrylic type or by theHEMUCRYL topcoat diluted 15-20% with water.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
HEMPEL’S HEMUCRYL product range
Application conditions: Use only where application can proceed at temperatures above 5°C/41°F, preferablyabove 10°C/50°F. Apply on a clean and dry surface with a temperature above the dewpoint to avoid condensation.
Relative humidity: During application above 60%, preferably 75-90%, to avoid dry spray.If RH is below 60%, special thinner may be added in order to reduce dry spray. Duringdrying below 80%, preferably between 40-60%. (Contact HEMPEL for further advice).Good ventilation during application and drying is necessary. Especially during drying it isof utmost importance that sufficient ventilation is covering all parts of the surfacespainted. Ventilation requirements to remove water vapours liberated during applicationand drying are app 75 m³/litre of the paint at 20°C/68°F. (Relative humidity of the airsupply 40%).
REMARKS:Good painting practice: The durability/performance of water-borne coatings is to a very high degree depending
on the fulfilment of good painting practice. For instance application to riveted andskip-welded constructions will require extra care when coating sharp edges, rivetedjoints, etc. Avoid too high thicknesses per coat. Preferably apply an extra stripe coat.
"Edge effect": Furthermore, as water-borne paints have a high tendency to "withdraw" from sharpedges, etc., proper corrosion protection will be highly supported by careful rounding ofedges and that any joints are completely closed and tight.
Exposure to low temperatures If the painted items will be exposed to humidity/water at temperatures below 5-10°C/shortly after application: 41-50°F shortly after finishing the paint application, it is of utmost importance for later
good performance that following rules are complied with:
• Excessive film thickness must be avoided.
• The (last applied) paint layer must dry for at least 6 hours at 20°C/68°F - 40-60%RH, 12 hours at 10°C/50°F - 40-60% RH before exposure to temperatures below5°C/41°F and/or condensation/water exposure.
Avoid outdoor application in seasons with low night temperatures, frost and frost incombination with condensation or rain.
Shelf life/storage: Store at temperatures between 5°C-40°C/41°F-104°F. Shelf life is reduced attemperatures above 30°C/86°F. Do not expose to frost during storage and transport, orbefore the coating is dry.
Cleaning of tools: Tools must be cleaned immediately with lukewarm soap water and/or fresh waterfollowed by thoroughly rinsing to remove residues of detergent.Dried remains of paint can be removed with HEMPEL'S TOOL CLEANER 99610.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Note: Any deviations from the above of a particular HEMUCRYL will be stated in the productdata sheet for this paint.
Issued: December 2000HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®TI-COAT 18200
Description: HEMUCRYL TI-COAT 18200 is a water-borne acrylic dispersion paint with good adhesiveproperties.
Recommended use: In mild to moderate corrosive environment as a primer on hot dip galvanized steel,aluminium and stainless steel. See SUBSEQUENT COAT overleaf.
Service temperatures: Maximum, dry: 120°C/248°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50710Finish: FlatVolume solids, %: 38 ± 1Theoretical spreading rate: 19.0 m²/litre - 20 microns
762 sq.ft./US gallon - 0.8 milsFlash point: > 66°C/151°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: 15 (approx.) min. at 20°C/68°F (ISO 1517)Dry to touch: 30 (approx.) min. at 20°C/68°FV.O.C.: 40 g/litre - 0.3 lbs/US gallon
125/litre - 1.0 lbs/US gallon (ASTM D 3960 - water-reduced)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush (touch-up)Thinner (max. Vol.): Fresh water (5%) Fresh water (5%)Nozzle orifice: .015"-.017"Nozzle pressure: 130 bar/1900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See APPLICATION INSTRUCTIONS)Indicated film thickness, dry: 20 microns/0.8 milsIndicated film thickness, wet: 50 microns/2 milsRecoat interval, min: 24 hours (at 20°C/68°F) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1820050710CO008
HEMUCRYL TI-COAT 18200
SURFACE See separate HEMUCRYL APPLICATION INSTRUCTIONS.PREPARATION:
APPLICATION See separate HEMUCRYL APPLICATION INSTRUCTIONS.CONDITIONS:
SUBSEQUENT HEMUCRYL, HEMPALIN, HEMPATEX systems or HEMPATHANE topcoats according to specification.COAT:
REMARKS:Recoating: If the subsequent coat is a HEMUCRYL-system the minimum recoating interval can be reduced to 2
hours at 20°C/68°F and ventilation. Reference is made to separate HEMUCRYL APPLICATIONINSTRUCTIONS.
No maximum recoating interval, but after prolonged exposure to polluted atmosphere removeaccumulated contamination by high pressure fresh water cleaning and allow to dry.
Other REMARKS: See separate HEMUCRYL APPLICATION INSTRUCTIONS.Note: HEMUCRYL TI-COAT 18200 is for professional use only.
Issued: December 2000 - 1820050710CO008HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1820050710CO008
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPEL’S HEMUCRYL product rangeScope: These Application Instructions cover surface preparation and application conditions of
HEMPEL’S HEMUCRYLs.
Surface preparation, New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherprimers: contaminants by (high pressure) fresh water cleaning. Abrasive blasting tominimum Sa 2½. For temporary protection, if required, use suitable shopprimer. Alldamaged shopprimer and contamination from storage and fabrication should bethoroughly cleaned prior to final painting. For repair and touch-up use the specifiedHEMUCRYL primer type.
Repair: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove rust and loose paint byabrasive blasting or power tool cleaning to St 3 before recoating. Touch up bare spotswith the specified HEMUCRYL primer type.
Aluminium: Very thorough degreasing, followed by (high pressure) fresh water cleaningto remove all salts and other contamination. Any anodizing must be completelyremoved. Thorough sand papering or abrasive sweeping with mineral abrasives isrecommended. Cast aluminium is recommended to be abrasive swept to a uniform,evenly grey appearance.
Stainless steel: Very thorough degreasing with alkaline degreaser, ie HEMPEL'S LIGHTCLEANER 99350, followed by fresh water hosing to remove all contamination.
Hot-dipped galvanized steel: Wet rubbing/grinding with ammonia water 1:20 followedby fresh water hosing. In the case this method is not feasible, the procedure asdescribed for stainless steel may be used.
Zinc silicate coated surfaces: Remove oil and grease, etc, with suitable detergent.Remove salt and other contaminants by high pressure fresh water cleaning. Afterexposure to high humidity, zinc salts ("white rust") must be removed carefully by (highpressure) fresh water cleaning - if necessary combined with scrubbing with stiff nylonbrushes. Consult the APPLICATION INSTRUCTIONS for the relevant GALVOSIL product.
Note:Among the HEMUCRYL primer types, HEMUCRYL TI-COAT 18200 is designed to be usedas the first coat on aluminium, hot-dop galvanized steel, stainless steel and on zincsilicate coated surfaces.
Surface preparation, Preceding coats should be sound and tightly adhering. Remove oil and grease withtopcoats: suitable detergent. Remove salts and other contaminants by (high pressure) fresh water
cleaning. Remove rust and loose material by abrasive blasting or power tool cleaning.Dust off residues. Touch up to full system before recoating with specified HEMUCRYLtopcoat type.
Concrete: Any oil, grease and other contaminants should be removed by eg volatilizingby flame cleaning or treatment with suitable detergent, the latter in the following way:
1) Saturation of the surface with fresh water2) Washing with suitable detergent followed by fresh water hosing
Remove loose material eg by stiff brushes or blasting, high pressure jetting or flamecleaning followed by fresh water hosing depending on circumstances. Three lastmentioned methods are also able to remove scum layer if necessary. After surfacepreparation the surface should feel solid and hard. Remove dust.
Saturate surface with suitable sealer, eg microdispersed acrylic type or by theHEMUCRYL topcoat diluted 15-20% with water.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
HEMPEL’S HEMUCRYL product range
Application conditions: Use only where application can proceed at temperatures above 5°C/41°F, preferablyabove 10°C/50°F. Apply on a clean and dry surface with a temperature above the dewpoint to avoid condensation.
Relative humidity: During application above 60%, preferably 75-90%, to avoid dry spray.If RH is below 60%, special thinner may be added in order to reduce dry spray. Duringdrying below 80%, preferably between 40-60%. (Contact HEMPEL for further advice).Good ventilation during application and drying is necessary. Especially during drying it isof utmost importance that sufficient ventilation is covering all parts of the surfacespainted. Ventilation requirements to remove water vapours liberated during applicationand drying are app 75 m³/litre of the paint at 20°C/68°F. (Relative humidity of the airsupply 40%).
REMARKS:Good painting practice: The durability/performance of water-borne coatings is to a very high degree depending
on the fulfilment of good painting practice. For instance application to riveted andskip-welded constructions will require extra care when coating sharp edges, rivetedjoints, etc. Avoid too high thicknesses per coat. Preferably apply an extra stripe coat.
"Edge effect": Furthermore, as water-borne paints have a high tendency to "withdraw" from sharpedges, etc., proper corrosion protection will be highly supported by careful rounding ofedges and that any joints are completely closed and tight.
Exposure to low temperatures If the painted items will be exposed to humidity/water at temperatures below 5-10°C/shortly after application: 41-50°F shortly after finishing the paint application, it is of utmost importance for later
good performance that following rules are complied with:
• Excessive film thickness must be avoided.
• The (last applied) paint layer must dry for at least 6 hours at 20°C/68°F - 40-60%RH, 12 hours at 10°C/50°F - 40-60% RH before exposure to temperatures below5°C/41°F and/or condensation/water exposure.
Avoid outdoor application in seasons with low night temperatures, frost and frost incombination with condensation or rain.
Shelf life/storage: Store at temperatures between 5°C-40°C/41°F-104°F. Shelf life is reduced attemperatures above 30°C/86°F. Do not expose to frost during storage and transport, orbefore the coating is dry.
Cleaning of tools: Tools must be cleaned immediately with lukewarm soap water and/or fresh waterfollowed by thoroughly rinsing to remove residues of detergent.Dried remains of paint can be removed with HEMPEL'S TOOL CLEANER 99610.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Note: Any deviations from the above of a particular HEMUCRYL will be stated in the productdata sheet for this paint.
Issued: December 2000HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMUDUR®18500CURING AGENT 97710
Description: HEMUDUR 18500 is a water-borne two-component polyamine cured epoxy primercontaining corrosive inhibiting pigment. It cures to a strong and rust-preventing coat.
Recommended use: In mildly to moderately corrosive environments as a general purpose primer on steelconstructions (see REMARKS overleaf).
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11150Finish: Semi-flatVolume solids, %: 53 ± 1Theoretical spreading rate: 7.1 m²/litre - 75 micron
283 sq.ft./US gallon - 3 milsFlash point: > 66°C/151°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 2 (approx) hours at 20°C/68°FDry to touch: 4 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 25 g/litre - 0.2 lbs/US gallon
60 g/litre - 0.5 lbs/US gallon (ASTM D 3960 - water-reduced)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 18500: Base 18509 : Curing agent 97710
2 : 3 by volumeApplication method: Airless spray BrushThinner (max.vol.): Fresh water (5%) Fresh water (5%)Pot life: 1 hour (20°C/68°F) (See REMARKS overleaf)
30 minutes (15°C/59°F)Nozzle orifice: .015"-.019" (See REMARKS overleaf)Nozzle pressure: Min. 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See REMARKS overleaf)Indicated film thickness, dry: 75 micron/3 mils (See REMARKS overleaf)Indicated film thickness, wet: 150 micron/6 milsRecoating: Recoating intervals related to later conditions of exposure:
(75 micron/3 mils dry film thickness of HEMUDUR 18500)
24 hours*3 weeks*
1 week*None*
None*None*
6 hours6 hours
6 hours6 hours
2 hours2 hours
HEMUCRYLHEMUDUR
SevereMediumMildSevereMediumMildRecoated with
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
* Before recoating, clean the surface thoroughly for all contamination.To check adequate quality of thepreparatory cleaning, a test patch is recommended before actual recoating.
If the maximum interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1850011150CO001
HEMUDUR 18500
SURFACE New steel: Remove oil and grease etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to minimum Sa 2½. For
temporary protection, if required, use suitable shopprimer. All damaged shopprimer andcontamination from storage and fabrication should be thoroughly cleaned prior to final painting. Forrepair and touch-up use HEMUDUR 18500.Repair: Remove oil and grease etc. with suitable detergent. Remove salt and other contaminantsby (high pressure) fresh water cleaning. Remove rust and loose paint by abrasive blasting or powertool cleaning to St 3 (minor areas) before recoating. Touch up bare spots with HEMUDUR 18500.
APPLICATION Use only where application and curing can proceed at temperatures above 15°C/59°F.CONDITIONS: Apply on a clean and dry surface with a temperature above the dew point to avoid condensation.
Relative humidity: During drying below 80%, preferably between 40-60%. Good ventilation duringapplication and drying is necessary. During drying it is of the utmost importance that sufficientventilation is covering all parts of the surfaces painted. Ventilation requirements to remove thewater vapours liberated during application and drying are approx. 75 m³/litre of paint at20°C/68°F. (Relative humidity of the air supply 40%.)
PRECEDING None, HEMPADUR ZINC 15360, HEMUDUR ZINC 18560 or according to specification.COAT:
SUBSEQUENT HEMUDUR, HEMUCRYL or according to specification.COAT:
REMARKS:Application: For proper film formation the recommended nozzle sizes should be used.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence amount of thinning necessary, drying time andrecoating interval. Normal range is 50-100 micron/2-4 mils. Application at lower film thicknessesis possible, but requires thinning for proper film formation.
Good painting: The durability/performance of water-borne coatings is to a very high degree depending on thepractice: fulfilment of good painting practice. For instance application to riveted and skip-welded
constructions will require extra care when coating sharp edges, riveted joints, etc. Avoid too highthicknesses per coat. Preferably apply an extra stripe coat.
"Edge effect": As water-borne paints have a high tendency to "withdraw" from sharp edges, etc., proper corrosionprotection will be highly supported by careful rounding of edges and that any joints are completelyclosed and tight.
Exposure to low If the painted items will be exposed to humidity/water at temperatures below 15°C/59°F shortlytemperature shortly after finishing the paint application, it is of utmost importance for later good performance thatafter application: the following rules are complied with:
• Excessive film thickness must be avoided• The (last applied) paint layer must dry for at least 6 hours at 20°C/68°F - 40-60% RH before
exposure to temperatures below 15°C/59°F and/or condensation/water exposure.Avoid outdoor application in seasons with low night temperatures especially in combination withcondensation or rain.
Cleaning of tools: Tools must be cleaned immediately with lukewarm soap water and/or fresh water followed bythoroughly rinsing to remove residues of detergent. Dried paint residues may be removed withHEMPEL’S TOOL CLEANER 99610.
Shelf life/storage: Store at temperatures between 5-40°C/41-105°F. The shelf life is reduced at temperatures above30°C/86°F. Do not expose to frost during storage and transport.
Pot life: The pot life time is not indicated eg by an increase in viscosity. Although the paint still looksusable after 1 hour at 20°C/68°F, it is important that the paint is no longer used as itsprotective properties are dramatically reduced after this time. Be aware that the pot life willdecrease when the temperature decreases, eg to 30 minutes at 15°C/59°F. Use eg an alarmclock to indicate when the pot life has been exceeded.
Note: HEMUDUR 18500 is for professional use only.
Issued: September 2000 - 1850011150CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1850011150CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMUDUR®ZINC 18560ZINC POWDER 97110
CURING AGENT 97700
Description: HEMUDUR ZINC 18560 is a three-component, water-borne, zinc rich epoxy primer. Itcures to a strong and anticorrosive coating that offers cathodic protection of localmechanical damage.
Recommended use: In moderately to severely atmospheric exposure as an anticorrosive primer forwaterborne paint systems.
Service temperatures: Maximum, dry: 140°C/284°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/19840Finish: FlatVolume solids, %: 51 ± 1Theoretical spreading rate: 10.2 m²/litre - 50 micron
409 sq.ft/US gallon - 2 milsFlash point: > 66°C/151°FSpecific gravity: 2.5 kg/litre - 20.9 lbs/US gallonSurface dry: 1 (approx) hour at 20°C/68°F (ISO 1517)Dry to touch: 2 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 10 g/litre - 0.1 lbs/US gallon
16 g/litre - 0.1 lbs/US gallon (ASTM D 3960 - water reduced)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 18560: BASE 18569, 4.3 parts by volume : ZINC POWDER 97110, 17.0 parts by weight (totally
6.7 parts by volume) : CURING AGENT 97700, 3.3 parts by volume.Add ZINC POWDER 97110 slowly while stirring to BASE 18569. Stir constantly with anefficient mechanical mixer and continue until a homogeneous mixture is obtained. Thenmix with CURING AGENT 97700.
Application method: Airless spray Brush (touch-up)Thinner (max.vol.): Fresh water (10%) Fresh water (5%)Pot life: 3 hours (20°C/68°F) (See REMARKS overleaf)
1½ hours (15°C/59°F)Nozzle orifice: .015"-.019"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment).Cleaning of tools: Fresh water (See REMARKS overleaf)Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 100 micron/4 milsRecoating: Recoating intervals related to later conditions of exposure:
(50 micron/2 mils dry film thickness of HEMUDUR 18560, steel temp. 20°C/68°F)
24 hours**3 weeks**
1 week**None**
None**None**
3 hours3 hours
3 hours3 hours
2 hours2 hours*
HEMUCRYLHEMUDUR
SevereMediumMildSevereMediumMildRecoated with
AtmosphericAtmospheric
MaximumMinimum
* HEMUDUR ZINC 18560 can be recoated with HEMUDUR 18500 with a mininimum recoating interval of 10minutes if both layers are specified in 30 micron/1.2 mils dry film thickness and are fully dried beforeapplying a third coat.
** The surface must be completely clean before recoating. In the case of "white rust", scrubbing with a stiff brush and plenty of water may be necessary.
If the maximum recoating interval is exceeded, roughening of the surface is necessaryto ensure intercoat adhesion
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1856019840CO001
HEMUDUR ZINC 18560
SURFACE Remove oil and grease thoroughly with suitable detergent. Remove salt and other contaminantsPREPARATION: by high pressure fresh water cleaning. Abrasive blasting to Sa 2½ with a sharp-edged surface
profile corresponding to Rugotest No. 3, BN9a, Keane-Tator Comparator, 2.0 G/S or ISOComparator, Medium (G).
APPLICATION Use only where application and curing can proceed at temperatures above 15°C/59°F.CONDITIONS: Apply to a clean and dry surface with a temperature above the dew point to avoid condensation.
Relative humidity: During drying below 80%, preferably between 40-60%.Good ventilation during application and drying is necessary.During drying it is of utmost importance that sufficient ventilation is covering all parts of thesurfaces painted. Ventilation requirements to remove the water vapours liberated during applicationand drying are approx. 75 m³/litre of paint at 20°C/68°F. (Relative humidity of the air supply 40%.)
SUBSEQUENT HEMUDUR, HEMUCRYL or according to specification.COAT:
REMARKS: Note: If used as anticorrosive protection under insulation of high temperature equipment it is veryimportant that NO moisture can penetrate during slow-down periods. This to avoid risk of "wetcorrosion" when the temperature rises.
Application: For proper film formation the recommended nozzle sizes should be used.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence amount of thinning necessary, drying time andrecoating interval. Normal range is 30-75 micron/1.2-3.0 mils.
Good painting: The durability/performance of waterborne coatings is to a very high degree depending on thepractice: fulfilment of good painting practice. For instance application to riveted and skip-welded
constructions will require extra care when coating sharp edges, riveted joints, etc. Avoid too highthicknesses per coat. Preferably apply an extra stripe coat.
"Edge effect": As water-borne paints have a high tendency to "withdraw" from sharp edges, etc., proper corrosionprotection will be highly supported by careful rounding of edges and that any joints are completelyclosed and tight.
Exposure to low If the painted items will be exposed to humidity/water at temperatures below 15°C/59°F shortlytemperature shortly after finishing the paint application, it is of utmost importance for later good performance thatafter application: the following rules are complied with:
• Excessive film thickness must be avoided• The (last applied) paint layer must dry for at least 6 hours at 20°C/68°F - 40-60% RH before
exposure to temperatures below 15°C/59°F and/or condensation/water exposure.Avoid outdoor application in seasons with low night temperatures especially in combination withcondensation or rain.
Cleaning of tools: Tools must be cleaned immediately with lukewarm soap water and/or fresh water followed bythoroughly rinsing to remove residues of detergent. Dried paint residues may be removed withHEMPEL’S TOOL CLEANER 99610.
Shelf life/storage: Store at temperatures between 5-40°C/41-104°F. The shelf life is reduced at temperatures above30°C/86°F. Do not expose to frost during storage and transport.
Pot life: The pot life time is not visible eg by an increase in viscosity. Although the paint still looksusable after 3 hours at 20°C/68°F, it is important that the paint is no longer used as itsprotective properties are dramatically reduced after this time. Be aware that the pot life willdecrease when the temperature decreases eg to 1½ hour at 15°C/59°F. Use eg an alarm clockto indicate when the pot life has been exceeded. Temperatures indicated are understood as thecommon temperature for both paint material and the steel to be painted.
Note: HEMUDUR ZINC 18560 is for professional use only.
Issued: September 2000 - 1856019840CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1856019840CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®E.V. PRIMER 19151Former name: Werofa Spezial E-Firnis 19151D
Description: HEMPATEX E.V. PRIMER 19151 is a paint based on a special resin for temporarycorrosion protection of high temperature equipment.
Recommended use: As a temporary corrosion protection during storage and fabrication of high temperatureequipment such as pipes, heating coils and hot ventilation channels.When heated, the paint decomposes slowly under moderate release of gases.
Approvals, certificates: Approved as a welding primer according to DAST-Richtlinie 006 (20 micron/0.8 mil dryfilm thickness).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50670Finish: FlatVolume solids, %: 48 ± 1 (DIN 53219)Theoretical spreading rate: 8 m²/litre - 60 micron
321 sq.ft./US gallon - 2.4 milsFlash point: 24°C/77°FSpecific gravity: 1.6 kg/litre - 13.4 lbs/US gallonDry to touch: 30 (approx) minutes at 20°C/68°FV.O.C.: 405 g/litre - 3.4 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush RollerThinner (max.vol.): 08080 (5%) 08080 (5%) 08080 (5%)Nozzle orifice: .013"-0.017"Nozzle pressure: 130 bar/1885 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL'S THINNER 08080Indicated film thickness, dry: 60 micron/2.4 milsIndicated film thickness, wet: 125 micron/5 milsRecoat interval, min: When dryRecoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1915150670CS002
HEMPATEX E.V. PRIMER 19151
SURFACE Remove oil and grease etc. with suitable detergent.PREPARATION: Remove salt and loose material.
Blast cleaning will improve the anticorrosion properties.
APPLICATION AND Clean and dry surface with temperature above the dew point to avoid condensation. Use onlyCURING where application and drying can proceed at temperatures above 0°C/30°F with a relativeCONDITIONS: humidity below 80% RH.
SUBSEQUENT NoneCOAT:
REMARKS: May be specified in another film thickness than indicated depending on purpose. This will alterspreading rate and may influence drying time.
Note: HEMPATEX E.V. PRIMER 19151 is for professional use only.
Issued: October 1999 - 1915150670CS002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 1915150670CS002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®FILLER 35250CURING AGENT 95250
Description: HEMPADUR FILLER 35250 is a two-component, solvent-free, epoxy filler,which - whenfully cured - is resistant to water, aliphatic hydrocarbons, and related products. Can beapplied in thick coats up to approximately 5 mm without runs or sags.
Recommended use: 1. As a filler for metals, hardwood, and other rigid materials.2. For filling of pinholes in weldings and similar irregularities in steel work not laterexposed to strong chemicals.
Service temperatures: Dry: In water (no temperature gradient):Maximum: 140°C/284°F 35°C/95°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light grey/19810Finish: Semi-glossSolids content: 100%Flash point: 92°C/198°FSpecific gravity: 1.6 kg/litre - 13.4 lbs/US gallonDry to touch: 8 (approx.) hours at 20°C/68°FFully cured: 5 (approx.) days at 20°C/68°FV.O.C.: 10 g/litre - 0.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the HEMPEL book. Thetheoretical spreading rate has been calculated on the basis of a 100% solids volume.
APPLICATION DETAILS:Mixing ratio for 35250: Base 35259 : Curing agent 95250
1 : 1 by volumeApplication method: Putty knife, or similar.Thinner (max.vol.): Do not dilutePot life: 1 hour (20°C/68°F)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Recoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: 24 hours (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3525019810CO006
HEMPADUR FILLER 35250
SURFACE Metal: Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminantsPREPARATION: by (high pressure) fresh water cleaning. Abrasive blasting, power tool cleaning or sanding,
depending on material and condition of the surface. Pitted steel should be blast cleaned and/orground with high speed burrs. Round off sharp edges. Finally clean the area with HEMPEL’STHINNER 08450. Priming after abrasive blast cleaning can be done with a thin layer of egHEMPADUR 15590.
APPLICATION Use only where application and curing can proceed at temperatures above 5°C/41°F.CONDITIONS: The temperature of the substrate should also be above this limit. Apply only on a dry and clean
surface with a temperature above the dew point to avoid condensation.
SUBSEQUENT Can be recoated with HEMPALIN, HEMPATEX or HEMPADUR qualities according to specification.COAT: High-gloss finishes such as HEMPATHANE TOPCOAT, should not be applied directly on top of
HEMPADUR FILLER 35250. An intermediate coat eg of a suitable HEMPADUR coating isrecommended.
REMARKS: Mix and stir the two components thoroughly until an even light grey colour is achieved, whereafterthe filler is ready for use.Do not mix more than is necessary for use within the pot life.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.May be sanded after 16 hours (20°C/68°F).
Note: HEMPADUR FILLER 35250 is for professional use only.
Issued: October 1999 - 3525019810CO006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3525019810CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®35440CURING AGENT 95800
Description: HEMPADUR 35440 is a two-component epoxy/amine adduct coating with a high solidscontent. Resistant to a wide range of chemicals as tabulated in separate RESISTANCEGUIDE.
Recommended use: As a tank lining.
PHYSICAL CONSTANTS:Finish: GlossyColours: Light Green/Light RedShade Numbers: 42070/50900Volume by Solids: 91%Theoretical Spreading Rate 3.6 m²/litre - 250 microns
146 sq.ft./US gallon - 9.9 milsFlash Point: 40C/104F A-Pensky closed cupSpecific Gravity: 1.3 kg/litre
10.8 lbs/US gallonDry to Touch: 28 - 30 hours at 20ºC/68ºFFully Cured: 7 days at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing Ratio: Base : Hempadur 35449 1.3 parts by volume
Curing Agent : 95800 1 part by volumeApplication Method: Airless Spray BrushThinner (max.vol.): 08460 (5%) 08460 (5%)Pot-Life: 1 hour (20ºC/68ºF)Nozzle Orifice: 0.021"Nozzle Pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Hempel's Tool Cleaner 99610
Indicated film thickness, wet: approx. 275 microns/11 milsIndicated film thickness, dry: 250 microns/10 mils (See REMARKS overleaf)
Recoat interval, min: 30 hours (20ºC/68ºF)Recoat interval, max: 3 days (20ºC/68ºF) (See REMARKS overleaf)
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3544042070
HEMPADUR® 35440
Surface If used self-primed: Abrasive blasting to Sa 3 with an anchor pattern equivalent to Rugotest No.3,Preparation: BN11a, or Keane-Tator Comparator 5.5 G/S. Blasting residues to be moved by vacuum cleaning.
With some exceptions, depending on intended cargoes, shopprimer should not be applied or, ifused for temporary protection, should be blasted off. Contact Hempel for advice.
Application Use only where application and curing can proceed at temperatures above 5ºC/41ºF. TheConditions: temperature of the surface and that of the paint itself must also be within these limits. Apply only
on a dry and clean surface with a temperature above the dew point to avoid condensation. Inconfined spaces provide adequate ventilation during application and drying. Relative humiditymaximum 90%.
Preceding Coat: Hempadur 15400 or according to specification.
Subsequent Coat: None, or according to specification.
Remarks: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoating interval.Do not dilute components separately - only the mixture. Thinning should be kept to an absoluteminimum. If maximum recoating interval is exceeded, roughening of the surface is necessary toensure intercoat adhesion.Do not put tanks into service until coating is properly cured. Consult DIRECTIONS FOR USE OFHEMPADUR 15400 AS INTERIOR TANK LINING.
Note: HEMPADUR 35440 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3544042070
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®SPRAY-GUARD®35490/HEMPADUR®SPRAY-GUARD®35493
High temperatures: 35490 with CURING AGENT 95690Medium temperatures: 35493 with CURING AGENT 95790
Description: HEMPADUR SPRAY-GUARD 35490/35493 is a solvent-free, two-component, epoxycoating. It cures to a hard, abrasion-resistant, protective coating. It can be sprayapplied in one coat at a minimum film thickness of 2.5 mm (100 mils).
Recommended use: As a heavy duty coating on steel and concrete exposed to severe corrosive conditionsand/or abrasion such as splashzones, decks and ramps. Colour retention will be ofminor importance.CURING AGENT 95690 suited for application at temperatures above 20°C/68°F.CURING AGENT 95790 suited for application at temperatures between 10°C/50°F and20°C/68°F.Conforms with NORSOK M-501, system no. 4 (high temperature version).
Service temperatures: Dry: In water (no temperature gradient):Maximum: 140°C/284°F 35°C/95°FSee REMARKS overleaf.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey-green/41690Finish: Semi-gloss, texturedSolids content: 100%Theoretical spreading rate: 0.4 m²/litre - 2.5 mm
16.0 sq.ft./US gallon - 100 milsFlash point: > 60°C/140°FSpecific gravity: 1.9 kg/litre - 15.8 lbs/US gallonSurface dry: See REMARKS overleafDry to touch: See REMARKS overleafFully cured: See REMARKS overleafV.O.C.: 0 g/litre - 0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the HEMPEL book.The theoretical spreading rate has been calculated on the basis of a 100% solids volume.
APPLICATION DETAILS: 35490 35493Mixing ratio: Base 35499 : Curing agent 95690 Base 35499 : Curing agent 95790
5.6 : 1.0 by volume; 23.0 : 2.0 by weight 5.7 : 1.0 by volume; 23.0 : 2.15 by weightApplication method: Spray (small areas: notched trowel) Spray (small areas: notched trowel)
(Consult separate Application Instructions) (Consult separate Application Instructions)Thinner (max. Vol.): Do not dilute (see REMARKS overleaf) Do not dilute (see REMARKS overleaf)Pot life: See REMARKS overleaf See REMARKS overleafRecommended equipment: Air spray by worm-pump equipment, by hose pump or by modified piston pump.
(Consult separate Application Instructions)For small areas Quick Spray Hopper Gun.
Cleaning of tools: HEMPEL’S TOOL CLEANER 99610.Indicated film thickness, dry: 2.5 mm/100 milsIndicated film thickness, wet: 2.5 mm/100 milsRecoating interval, min: See REMARKS overleafRecoating interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/3549341690CO002
HEMPADUR SPRAY-GUARD 35490/35493
SURFACE Steel: Abrasive blasting to Sa 2½ or Sa 3 depending on area of use.PREPARATION: Surface profile corresponding to Rugotest No. 3 BN11, Keane-Tator Comparator 5.5 G/S, or ISO
Comparator, Coarse (G). Oil and grease must be removed with suitable detergent, salt and othercontaminants by (high pressure) fresh water cleaning prior to blasting. After blasting clean thesurface carefully from abrasives and dust. The blasted and cleaned surface may advantageouslybe primed with HEMPADUR 15590.Concrete: Remove slip agent and other possible contaminants by emulsion cleaning followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment, flamecleaning or acid etching. Seal surface with suitable sealer, e.g. HEMPADUR SEALER 05970(furthermore, see Product Data Sheet for 05970). Further information about surface preparation tobe found in separate APPLICATION INSTRUCTIONS for 35490/35493.
APPLICATION Use only on a clean and dry surface with a temperature above the dew point to avoidCONDITIONS: condensation when application and curing can proceed as listed:
about 3 days at 10°C/50°Fabout 3 days at 20°C/68°FDry to handle:
about 8 hrs at 10°C/50°Fabout 8 hrs at 20°C/68°FDry to touch:
about 3 hrs at 10°C/50°Fabout 3 hrs at 20°C/68°FSurface dry (ISO 1517):
7 days at 10°C/50°F7 days at 20°C/68°FFully cured:
2°C/36°F10°C/50°FCuring will proceed down to:
10°C/50°F20°C/68°FMinimum appl temperature of substrate:
Curing agent 95790Curing agent 95690Cured with
To facilitate stirring and mixing, the material temperature should in no case be less than approx20°C/68°F.
PRECEDING COAT: None, HEMPADUR SEALER 05970, HEMPADUR 15590, or according to specification.
SUBSEQUENTCOAT: None, or HEMPADUR qualities according to specification. In case a "smoothening" of the surfaceis required, HEMPADUR MULTI-STRENGTH 45750 may be used.
REMARKS:Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Film thicknesses: May be specified and applied in higher film thicknesses than indicated. Not recommended below
2.5 mm /100 mils, since HEMPADUR SPRAY-GUARD 35490/35493 will not form a close andpinhole-free film at lower film thicknesses.
Adhesion: Proper adhesion is obtained by applying HEMPADUR SPRAY-GUARD 35490/35493 directly to thesteel. If a blast primer is required, HEMPADUR 15590 is recommended.
Thinning: Do not dilute as this will influence adhesion and cohesion of the paint system.
Pot life:
1 hour30 minutesNot relevantWith curing agent 95790
Not relevant1 hour30 minutesWith curing agent 95690
10°C/50°F20°C/68°F30°C/86°FMaterial temperature
Recoating interval:
8 hours2 months
4 hours1 month
2 hours2 weeks
MinMax
With curing agent 95790
Not relevant2 months
8 hours1 month
4 hours2 weeks
MinMax
With curing agent 95690
10°C/50°F20°C/68°F30°C/86°FSubstrate temperature
In the case of contamination before recoating, very careful cleaning is a must.Repair work should include recoating of a part of the surrounding, intact, original paint, which mustbe cleaned and roughened prior to application.For further details consult separate Application Instructions.
Note: HEMPADUR SPRAY-GUARD 35490/35493 is for professional use only.
Issued: May 2000 - 3549041690CO007/3549341690CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/3549341690CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®SPRAY-GUARD®35490/HEMPADUR®SPRAY-GUARD®35493
High temperatures: 35490 with CURING AGENT 95690Medium temperatures: 35493 with CURING AGENT 95790
Scope: These Application Instructions cover surface preparation and application in connectionwith HEMPADUR SPRAY-GUARD 35490/35493.
Surface preparation: Steel: Heavily scaled surfaces may advantageously be descaled mechanically (e.g.hammering) prior to abrasive blasting.
Rough welds and sharp edges should be ground and rounded off prior to abrasiveblasting. Weld spatters to be removed.
Prior to blast cleaning the steel, remove oil, grease, and other contamination withsuitable detergent followed by (high pressure) fresh water cleaning. Other chemicalcontamination shall be neutralized and/or flushed.
Alkali deposits on new welding seams to be removed with fresh water.All steel surfaces to be protected must be abrasive gritblasted to minimum "near whitemetal", Sa 2½, ISO 8501-1:1988.
For very severe service conditions, abrasive gritblasting to "white metal", Sa 3, ISO8501-1: 1988 can be necessary.
The minimum required surface profile is Ra = 25 micron, corresponding to Rugotest No.3, BN11, Keane-Tator Comparator 5.5 G/S, or ISO Comparator Coarse (G). The profileis obtained with sharp, angular abrasives.
All blasted surfaces must be cleaned from dust, abrasives, etc. prior to painting.HEMPADUR 15590 may be used as blast primer according to specification.
Concrete: The concrete must be of good quality and fully cured, eg 28 days for normalPortland cement, and completely dry with a humidity content in the surface below 4%.The concrete must also be controlled for absence of capillary water action or for subsoilwater.
Minimum pull-off value should normally be 20 kilopond/cm² measured after surfacepreparation. Any cracks, crevices and voids must be repaired.
All possible slip agent, oil, grease and other contaminants must be removed by egabrasive blasting, volatilizing by flame cleaning or treatment with suitable detergent. Thelast mentioned in the following way: Saturation of the surface with fresh water. Washingwith detergent followed by fresh water hosing.
Depending on construction and purpose, abrasive blast, high pressure water jet or treatthe concrete with power tools to obtain a rough and firm surface free of scum layer andother contamination. Remove dust and loose material.
If mechanical treatment is impossible, the surface may be treated with acid etching. Forthis purpose an approx. 5% w/w nitric or phosphoric acid solution is recommended.
Note: Strong acids, take necessary precautions, make sure that safety regulations areObeyed!
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/ 3549341690CO002
HEMPADUR SPRAY-GUARD 35490/35493
Prior to etching the concrete should be saturated with fresh water to prevent acidcorrosion of the reinforcement bars. Leave the acid to act for 3-4 minutes and hosedown the surface with fresh water - preferably first a 5% w/w sodium hydroxide solutionand scrub carefully. After that the surface must dry homogenously and appear as aneven, rough surface free of a loose outer layer. The surface must have a pH reaction ofbetween 6.5-8.0. If any of these conditions are not fulfilled, the process must berepeated. The surface must be dried with good ventilation for at least 2 days at 65%relative humidity and 20°C/68°F.
Pretreatment is controlled by scraping with a strong knife. The surface must feel solidand hard, and the knife must only leave a clear scratch mark.
Seal the surface with HEMPADUR SEALER 05970 in such a way that the surface is justsaturated. Any surplus must be removed (do also see the Product Data Sheet forHEMPADUR SEALER 05970).
Application equipment: The following pumps are recommended for application of HEMPADUR SPRAY-GUARD35490/35493:
For major jobs:
a. Worm pump type, vertically situated, eg:PUTZMEISTER SPRAY BOY IIModel no. 20975.005 (air driven)Worm pump, electrically or air driven. Pump house D 4 1/2, Art. 70829004.Mantel material, benzene resistant, Neoprene, 70827006.Best working temperatures between 10°C/50°F and 30°C/86°F
b. Hose pump ("Carrousel" pump), eg:BREDEL Hosepump type SP 40. Pump hose 40 mm in diameter, preferably ofsynthetic rubber. Electrically or air driven. Motorpower for instance 1.5 kW,geared to give an output speed of 7-55 rpm.Best working temperatures between 10°C/50°F and 30°C/86°F.
c. Piston pump type with hopper, eg:GROVER MFG CORP. Model 473 TSDModified, divorced piston pump 10:1 (7.5:1 can also be used).Best working temperatures above 20°C/68°F
For small as well as major jobs:
d. GRACO President, Modified Model 225-841, 10:1 Piston Pump.
For repair and small constructions:
e. PUTZMEISTER QUICK SPRAY.
Note: Other Hopper guns are available.
Spray guns:Ball Valve guns from Maskin A/B Tumac, Sweden
No. 04131.001, Putzmeister, West Germany
Serie 22517, Grover, Texas
Nozzle Orifice:3-7 mm depending on circumstances
Material Hose:Internally lined hose is recommended e.g. Uniroyal Mamili SAE 16CR 1T 3434. Lengthup to 15 metres/50 feet.For piston pumps max. 10 metres/35 feet.For hose pump max. 20 metres/70 feet.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/ 3549341690CO002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR SPRAY-GUARD 35490/35493
Mixing machine:For large jobs the use of a mixing machine is recommended, e.g.:PENNINE G5 Mixer from: PENNINE Industrial Equipment Ltd., Great Britain.
Note: Other spray and mixing equipment than above mentioned may be usable.
Do not dilute.
Application by trowel is possible, but primarily relevant for small horizontal areas. Usea wide-notched trowel with an opening of 10 mm to ensure that a sufficient filmthickness has been achieved. Smoothen out with a plain spatula dipped in THINNER08080. Keep a uniform pressure with the spatula. Finally, if a textured surface isrequired, the wet coating is rolled over with a textured nylon roller dipped in THINNER08080.
Mixing: HEMPADUR SPRAY-GUARD 35490/35493 is delivered in two components, viz:BASE 35499 and CURING AGENT 95690 for use at temperatures above 20°C/68°F, orBASE 35499 and CURING AGENT 95790 for use at temperatures between 20°C/68°Fand 10°C/50°F.
Stir the base thoroughly several minutes with a powerful, mechanical mixer.Add the content of the smaller can, the CURING AGENT, into the larger can and stiragain. Minimize the residues in the small can.
It is important to ensure that all BASE material is homogeneously incorporated into themixture after which HEMPADUR SPRAY-GUARD 35490/35493 is ready for application.
If it is necessary to mix smaller portions than supplied, then extreme care must betaken to ensure that BASE as well as CURING AGENT separately are made completelyhomogenous by thorough stirring before subdividing.
The mixing ratio is:
"Medium temperatures", 35493:BASE, HEMPADUR SPRAY-GUARD 35499 : 10.7 parts by weight or 5.7 parts by volumeCURING AGENT 95790 : 1.0 part by weight or 1.0 part by volume.
"High temperatures", 35490:BASE, HEMPADUR SPRAY-GUARD 35499 : 11.5 parts by weight or 5.6 parts by volumeCURING AGENT 95690 : 1.0 part by weight or 1.0 part by volume.
Pot life: CURING AGENT 95690 CURING AGENT 95790At 30°C/86°F: 30 minutes At 20°C/68°F: 30 minutesAt 25°C/77°F: 45 minutes At 15°C/59°F: 45 minutesAt 20°C/68°F: 1 hour At 10°C/50°F: 1 hour
Do not mix more material than can be used during the pot life at the prevailingtemperature. In hot climate it is recommended to mix only one set at a time just prior touse.
Procedure: Worm and hose type pump:Flush the pump with HEMPEL’S TOOL CLEANER 99610.Empty the pump. Mix and add HEMPADUR SPRAY-GUARD 35490 or 35493 to thehopper.
Nozzle orifice: Approximately 5 mm, air pressure 4-6 bar/60-90 psi.
Pressure, air driven machinery, worm type pump:Airmotor: 1.5-2 bar/20-30 psi
The best distance between gun and substrate is 25-50 cm/1-2 feet.
The hopper must be completely free of previous mixture before re-loading withHEMPADUR SPRAY-GUARD 35490 or 35493.
To avoid material being pressed into the air chamber of the gun, turn on the atomizingair before starting the pump.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/ 3549341690CO002
HEMPADUR SPRAY-GUARD 35490/35493
Piston pump:Flush the pump and the hose with HEMPEL’S TOOL CLEANER 99610.Remove HEMPEL’S TOOL CLEANER 99610 from the pump by opening lower ball valve.Mix HEMPADUR SPRAY-GUARD 35490 or 35493 and load the pump.
Nozzle orifice: Approximately 7 mm.
Air pressure:Nozzle: 3-6 bar/45-90 psiInput, 10:1 pump: 1.5-4 bar/20-60 psiOpen the relax-a-valve a little before spraying.
The best distance between gun and substrate is 25-40 cm/1-1.5 foot.
Stop of Even for short interruptions of spraying it is important to stop the gun and the pumpspray application: simultaneously to prevent paint build-up in hoses and gun. Automatic devices for this
purpose can be delivered as standard for most equipment.If the nozzle is blocked, the following procedure is mandatory:• Remove and clean cap and nozzle separately.• Circulate the material at equal pressures (do not increase the pressure on the
material hose).
Control of wet The applied paint film thickness must be measured immediately after application withfilm thickness: a wet film thickness gauge suitable for this range of thicknesses (scale: 1-5 mm/40-200
mils).
Besides, control of consumption in relation to the area coated is carried out regularly.Theoretically, a film thickness of 2.5 mm corresponds to a consumption of 2.5 litresHEMPADUR SPRAY-GUARD 35490 or 35493 per square metre.
Additional material must be applied in case the thickness is insufficient, and in case ofimproper film formation.
Equipment cleaning: Thorough cleaning of equipment is essential for a continuous, problem-free operation.
During application:Keep the sides of the hopper free of "old" material by scraping the sides regularly.
After application:Immediately after finishing the application pump a high viscosity lubricating oil throughthe equipment to press out the sandy remnants of HEMPADUR SPRAY-GUARD 35490/35493 to avoid settling around fittings, nozzle, piston, etc. Then follow by flushingpump, hose, and the relax-valve, if any, with HEMPEL’S TOOL CLEANER 99610.Take cup and nozzle off the gun and flush the system at maximum speed.
To ease cleaning insert a sponge in the material hose and pump it through the hoseseveral times. In case the material hose is not internally lined finalize by rinsing withhigh viscosity lubricating oil to prevent drying out of the hose. If the above-mentionedprecautions are not taken, there is a risk of problematic starting-up later on.
Take the pump house apart and ensure it is thoroughly clean. In mortar type machinerylubricate the worm. Leave the pump unassembled after cleaning.
For the piston pump types HEMPADUR SPRAY-GUARD 35490/35493 will cause arelatively high degree of wearing of packings for which reason extra sets should alwaysbe at hand.
Check of the dry film: The dry film is checked all over for discontinuities and correct minimum thickness with aHigh Voltage Holiday Detector operating at 12 KV. These checks can take place onHEMPADUR SPRAY-GUARD 35490 after curing with CURING AGENT 95690 for minimum24 hours at 20°C/68°F, on HEMPADUR SPRAY-GUARD 35493 after curing with CURINGAGENT 95790 for minimum 24 hours at 10°C/50°F.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/ 3549341690CO002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR SPRAY-GUARD 35490/35493
Discontinuities and areas with too low film thickness showing spark discharge must betouched up.
Touch-up: For repair and touch-up HEMPADUR SPRAY-GUARD 35490/35493 can be used. Onminor spots HEMPADUR SPRAY-GUARD 35490/ 35493 may be applied by spatula. Largeareas are repaired by applying the specified film thickness after proper surfacepreparation as described above.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999 - 3549041690CO007/ 3549341690CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3549041690CO007/ 3549341690CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductINSTRUCTIONS FOR MANUAL APPLICATION OFSupplementary to the Product Data Sheet with Application Instructions
HEMPADUR®SPRAY-GUARD®35490/HEMPADUR®SPRAY-GUARD®35493
Surface preparation: According to Product Data Sheet.
HEMPADUR 15590 in a dry film thickness of 50 micron can be used as a blast primer,reference is made to the Product Data Sheet.
Application: After careful mixing, HEMPADUR SPRAY-GUARD 35490/35493 is applied by awidenotched trowel with 10 mm clearance.
In order to close notches from trowelling and to obtain a uniform layer, smoothen with aspatula dipped into HEMPEL'S THINNER 08080. Keep a uniform pressure with theSpatula.
To obtain a non-skid surface, roll the surface with a nylon roller with hair of a mediumlength. Should be dipped into HEMPEL'S THINNER 08080.
Checking: The film thickness is checked by measuring the wet film as well as by calculating theconsumption corresponding to the area. Theoretically, a film thickness of 2.5 mmcorresponds to 2.5 litres of HEMPADUR SPRAY-GUARD 35490/35493 per square metre.The coating is checked all over for pinholes by high-voltage pinhole detection with 12kilovolt. Where sparks are observed the spots are marked and repaired with specifiedthickness as a minimum.
Issued: October 1999HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MULTI-STRENGTH®35530CURING AGENT 95530
Description: HEMPADUR MULTI-STRENGTH 35530 is a solvent-free, two-component, high-build,polyamine cured epoxy paint, which cures to a coating with good resistance to freshwater, sea water, crude oil, and to abrasion.Applicable in thick coats by standard heavy duty airless spray equipment.Harmless to grain cargo.
Recommended use: 1. As a heavy duty coating on steel exposed to abrasion where solvent-free materialsare required. Full colour retention will be of secondary importance.If solvent containing paints are accepted, HEMPADUR MULTI-STRENGTH 45751Substitutes.
2. As a lining in potable water tanks and pipelines. Please see Certificates/Approvals.For application in warm climates. Please see APPLICATION CONDITIONS overleaf.
Service temperatures: Dry: In fresh water (directly on steel):Maximum: 140°C/284°F 35°C/95°F (no temperature gradient)See REMARKS overleaf.
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Approved by Water Research Centre, Great Britain, for potable water up to 23°C/73°F.Approved by Ministry of Electricity & Water, Bahrain, for potable water.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/10500 - Red/51320Finish: Semi-glossSolids content: 100%Theoretical spreading rate: 3.3 m²/litre - 300 micron
134 sq.ft./US gallon - 12 milsFlash point: > 100°C/212°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 12 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 24 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 0 g/litre - 0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the HEMPEL book. Thetheoretical spreading rate has been calculated on the basis of a 100% solids volume.
APPLICATION DETAILS:Mixing ratio for 35530: Base 35539 : Curing agent 95530
3 : 1 by volumeStir CURING AGENT before adding it to the BASE.
Application method: Airless spray Brush (touch up)(Consult the separate APPLICATION INSTRUCTIONS)
Thinner (max.vol.): Do not dilute (Consult the separate APPLICATION INSTRUCTIONS)Pot life: 1 hour (20°C/68°F) (Consult the separate APPLICATION INSTRUCTIONS)Nozzle orifice: .019" -.031"Nozzle pressure: min. 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 300 micron/12 mils (See REMARKS overleaf)Indicated film thickness, wet: 300 micron/12 milsRecoat interval, min: See REMARKS overleaf and separate APPLICATION INSTRUCTIONSRecoat interval, max: See REMARKS overleaf and separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
HEMPADUR MULTI-STRENGTH 35530
SURFACE When used as a heavy duty coating or in potable water tanks and pipelines:PREPARATION: Abrasive blasting to min. Sa 2½. Grit-blasted surfaces: recommended profile is Rz minimum 100
micron/4 mils - maximum 150 micron/6 mils corresponding to ISO Comparator Coarse (G). Oil andgrease must be removed with suitable detergent, salts and other contaminants by (high pressure)fresh water hosing prior to blasting. After blasting, clean the surface carefully from abrasives anddust.On old steel surfaces having been exposed to salt water, excessive amounts of salt residues inpittings may call for abrasive blasting, high pressure fresh water hosing, drying, and finally, dryabrasive blasting again. Alternatively, water jetting may be used provided the steel surface hasalready the surface profile as described above.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment, flamecleaning or acid etching. Seal surface with suitable sealer, eg HEMPADUR SEALER 05970(furthermore, please see Product Data Sheet for 05970).
APPLICATION Use only where application and curing can proceed at temperatures above10°C/50°F.CONDITIONS: The temperature of the paint itself must be above 15°C/59°F for proper application. In-can
temperature of the paint should preferably be below 25°C/77°F.Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation. Relative humidity max 85%.For application in warm climates, HEMPADUR MULTI-STRENGTH 45751 may preferably replaceHEMPADUR MULTI-STRENGTH 35530 as a heavy duty coating. For potable water tanks and pipesplease check local product assortment.
PRECEDING COAT: None, HEMPADUR SEALER 05970, HEMPADUR 15590 or according to specification.SUBSEQUENTCOAT: None, HEMPADUR or HEMPATHANE qualities as per specification.
REMARKS: Certificates have been issued under the former quality number 3553.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become more sensitiveservice to mechanical damage and chemical exposure at elevated temperatures is also reflected in thisTemperatures: product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 200-300 micron/8-12 mils.
Recoating: Recoating intervals related to later conditions of exposure:(300 micron/12 mils dry film thickness of HEMPADUR MULTI-STRENGTH 35530)
5 daysNot relevant
5 days24 hours
24 hoursNot relevant
24 hours12 hours
HEMPADURHEMPATHANE
SevereSevereRecoated with
Waterimmersion
AtmosphericWaterimmersion
Atmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
Mix and stir the two components until an even colour is achieved, whereafter the paint is ready foruse. If improved colour stability is requested for exposure to sunshine, it is recommended totopcoat with e.g. HEMPATHANE TOPCOAT 55210.
Potable water tanks: See APPLICATION INSTRUCTIONS, as to time before taking into use and post treatment of coatedsurfaces to be in contact with potable water.
Note: HEMPADUR MULTI-STRENGTH 35530 is for professional use only.
Issued: November 2001 - 3553010500CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®MULTI-STRENGTH®35530CURING AGENT 95530
Scope: These Application Instructions cover surface preparation, application equipment, andapplication details for HEMPADUR 35530.
Surface preparation: Steel: Abrasive blasting to min. Sa 2½. Grit-blasted surfaces: recommended profile is Rzminimum 100 micron/4 mils - maximum 150 micron/6 mils corresponding to ISOComparator Coarse (G). Oil and grease must be removed with suitable detergent, saltsand other contaminants by (high pressure) fresh water hosing prior to blasting. Afterblasting, clean the surface carefully from abrasives and dust. HEMPADUR 15590 may beused as a blast primer/hold-coat.
On old steel surfaces having been exposed to salt water, excessive amounts of saltresidues in pittings may call for dry abrasive blasting, high pressure fresh water hosing,drying, and finally, dry abrasive blasting again. Alternatively, water jetting may be usedprovided the steel surface has already the surface profile as described above.
In case of extensively pit-corroded surfaces (tank bottoms): Remove oil and greasewith suitable detergent. Blasting to Sa 2, ISO 8501-1: 1988. Pittings on tank bottomsare often omega-shaped (typically in the case of chloride-induced corrosion) for whichreason the following procedure is recommended:
After rough cleaning for dust and abrasives, the tank surfaces are to be thoroughly highpressure fresh water hosed. Let the water remain in the tank so that all pit corrodedareas are covered by approx 5 cm/2" of water.
After 24 hours the water is removed by wet vacuum cleaning and the tank is dried.If needed, i.e. if there is still salt contamination to be found in the pits, the washingtreatment has to be repeated. After cleaning, the surfaces are blasted to min. Sa 2½with a surface roughness profile as described above. After blasting clean the surfacecarefully for abrasives and dust. Special care must be taken when cleaning the tankbottom.
Concrete: The concrete must be of good quality and fully cured, eg 28 days for normalPortland cement, and completely dry with a humidity content in the surface below 4%.The concrete must also be controlled for absence of capillary water action or for subsoilwater.
Minimum pull-off value should normally be 20 kilopond/cm² measured after surfacepreparation. Any cracks, crevices and voids must be repaired.
All possible slip agent, oil, grease and other contaminants must be removed by egabrasive blasting, volatilizing by flame cleaning or treatment with suitable detergent. Thelast mentioned in the following way: Saturation of the surface with fresh water. Washingwith suitable detergent followed by fresh water hosing.
Depending on construction and purpose, abrasive blast, high pressure water jet or treatthe concrete with power tools to obtain a rough and firm surface free of scum layer andother contamination. Remove dust and loose material.
If mechanical treatment is impossible, the surface may be treated with acid etching. Forthis purpose an approx. 5% w/w nitric or phosphoric acid solution is recommended.
Note: Strong acids, take necessary precautions, make sure that safety regulations areObeyed!
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
HEMPADUR MULTI-STRENGTH 35530
Prior to etching the concrete should be saturated with fresh water to prevent acidcorrosion of the reinforcement bars. Leave the acid to act for 3-4 minutes and hosedown the surface with fresh water - preferably first a 5% w/w sodium hydroxide solution- and scrub carefully. After that the surface must dry homogenously and appear as aneven, rough surface free of a loose outer layer. The surface must have a pH reaction ofbetween 6.5-8.0. If any of these conditions are not fulfilled, the process must berepeated. The surface must be dried with good ventilation for at least 2 days at 65%relative humidity and 20°C/68°F. The pretreatment is controlled by scraping with astrong knife. The surface must feel solid and hard, and the knife must only leave a clearscratch mark.
Seal the surface with HEMPADUR SEALER 05970 in such a way that the surface is justsaturated. Surplus must be removed (do also see the Product Data sheet forHEMPADUR SEALER 05970).
Application equipment: HEMPADUR MULTI-STRENGTH 35530, being a solventfree, high viscosity material,requires special measures to be taken at application.
Standard airless heavy duty spray equipment:
Pump ratio: min 45:1 (See Note below)Pump output: 12 litres/minute (theoretical)Input pressure: min 6 bar/90 psiSpray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .023" through .031"Fan angle: 40-60°.
Complicated surfaces:Nozzle size: .019" through .023"Fan angle: 40°
Note: Avoid the use of a suction hose. Use an interchangeable pipe, which makes itpossible to remove cured paint If longer spray hoses are necessary the pump ratio mustbe raised to 60:1 or more, yet the high output capacity of the pump must be maintained.
Thinning: Alternatively 1-2% THINNER 08450 may be added, but thinning must be done with careas the antisagging properties are drastically reduced by overthinning. Do NOT usethinning when coating surfaces to be in contact with potable water.
Airless spray data are indicative and subject to adjustment.
Mixing: Stir the CURING AGENT 95530 well before mixing with BASE. Continue the mixing until acomplete uniform colour is achieved.
Hot airless spray equipment:
Use the same airless spray pump as described above.
On the output side of the pump an electrically heated, explosion proof, high pressure,material heater is fitted. For instance 2500 Watt, max. working pressure well above 300bar (4-1 safety factor) equipment.
Spray hoses: 45 metres/150 feet, 3/8" internal diameter.3 metres/10 feet, 1/4" internal diameter.
Regular surfaces:Nozzle size: .023" through .031"Fan angle: 40-60°
Complicated surfaces:Nozzle size: .019" through .023".Fan angle: 40°.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MULTI-STRENGTH 35530
Procedure for hot airless spray:
a) Follow the supplier’s instructions for the use of the heater.
b) At surrounding temperatures below approximately 15°C/59°F start by heating upthe hoses by recirculation of THINNER 08450 or HEMPEL’S TOOL CLEANER99610.
c) Keep THINNER 08450 or HEMPEL'S TOOL CLEANER 99610 readily available forfast cleaning of the equipment.
d) Start spraying immediately after proper mixing and mechanical stirring of BASE35539 and CURING AGENT 95530.
e) Adjust the heater to approximately 50°C/122°F and check this temperature atshort intervals.
f) The spraying should as far as possible run continuously. At any break longer than2-3 minutes, switch off the heat and flush the equipment immediately andthoroughly with one of the solvents mentioned above under c).
g) After finishing the application, switch off the heat and clean the equipmentimmediately with THINNER 08450 or HEMPEL'S TOOL CLEANER 99610.Continue the cleaning by re-circulation for at least 30 minutes.
Pit-corroded surfaces: In case of extensive pit corrosion (old tank bottoms) it isadvisable to apply the first coat by brush. The coating must be worked well into all pitsfacilitating a good wetting of the steel and closing the porosities. The following coat(s)can be applied by brush as well as by airless spray (as per above) securing full coveringof the uneven/rough surface.
Pot life: When measured under standard conditions the pot life is one hour at 20°C/68°F.However, for a 20 litres/5 US gallons mix, the heat developed by the chemical reactionbetween BASE and CURING AGENT is so intense that the corresponding practical pot lifeis substantially shorter.
Therefore:
• Irrespective of equipment, use the paint immediately after mixing. At a normalapplication speed the 20 litres/5 US gallons are used in approx. 10 minutes.
• Keep an eye on the paint temperature frequently for instance by touching the canwith your hand. If it feels more than hand warm, discard the paint and flush theequipment immediately irrespective of type of spray equipment.
Paint temperature: If the in-can temperature is below approximately 15°C/59°F viscosity will be too high forapplication. If the paint temperature at mixing is 25°C/77°F or higher a substantial riskof shortened pot life and curing in can/spray equipment exists. When working in warm,sub-tropical/ tropical climates a refrigerated container can be used for storing/cooling of the paint before application.
Application: Film-build/continuity: With this typical one-coat tank coating it is of great importancethat a continuous, pinhole-free paint film is obtained. An application technique which willensure good film formation on all surfaces must be adopted. It is very important to usenozzles of the correct size, not too big, and to have a proper, uniform distance of thespray gun to the surface, 30-50 cm should be aimed at. Furthermore, great care must betaken to cover edges, openings, rear sides of stiffeners etc. The usual way of obtainingthis result is to spray-coat all these areas separately followed by a full coat all over.Furthermore, stripe coating by brush will typically be required. To obtain good and steadyatomizing, the viscosity of the paint must be suitable and the spray equipment must besufficient in output pressure and capacity.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
HEMPADUR MULTI-STRENGTH 35530
The paint layer must be applied homogenously and as close to the specification aspossible. The consumption of paint must be controlled to avoid exaggerated filmthickness, eg by controlling paint consumption and/or measuring wet film thickness.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
Stripe coating: Edges, corners, manual welds, and places difficult to cover properly by spray applicationshould be stripe coated (touched up) either before or after the spray application.
One or two stripe coats will usually be necessary, but depending on actual conditions.
HEMPADUR MULTI-STRENTGH 35530 may be slightly thinned with THINNER 08450,except for stripe coating of surfaces to be in contact with potable water.
Extra film thickness: Extra thickness - extra layer(s) - may be necessary in case of severely pitted and/orwhere very high degrees of antiabrasive properties are needed.
Two- coat application: When applied in two coats it is an advantage to apply the first coat thicker than thesecond coat, for instance 300 micron for first, 200 micron for the second layer.
Recoating intervals: Within a maximum of 85% Relative Humidity the following recoatingintervals apply (d=days h=hours):
4 h8 h
4½ h9 h
6 h12 h
8 h16 h
12 h24 h
19 h38 h
30 h60 h
MinMaxHEMPATHANE qualities
8 hours36 hours
9 hours44 hours
12 h2½ d
16 h3½ d
24 h5 d
38 h8 d
60 h13 d
MinMaxHEMPADUR qualities
40/10435/9530/8625/7720/6815/5910/50Steel temperature °C/°F
The layer of HEMPADUR MULTI-STRENGTH 35530 must NOT be exposed to (steel)temperatures below 10°C/50°F, to condensing humidity nor to relative humidities higherthan 85% before recoating.
Curing table: The following curing times apply:
2 days1 day
2½ days1 day
3½ days1½ days
5 days2 days
7 days3 days
11 days5 days
18 days7½ days
Fully cured"Initial curing"
40/10435/9530/8625/7720/6815/5910/50Steel temperature °C/°F
Time before taking Tanks or pipelines should generally not be taken into use before HEMPADURinto use: MULTI-STRENGTH 35530 is fully cured (see above).
Full curing is mandatory in case of potable water service.
Exposure to ballast water and crude oil may exceptionally take place after an "initialcuring" time as listed above.
Water resistance: HEMPADUR MULTI-STRENGTH 35530 is resistant to light showers and condensationafter an initial curing time as listed:
15 hours20 hours24 hours32 hours60 hoursMinimum time
30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
Note: HEMPADUR 35530 must not be exposed to water or high humidity betweenstripe coating and full coating respectively between full coating and any necessarysecond full coating as there is a certain risk of curing agent exudation which will hinderadhesion. If exudation is present on the surface this must be removed by very thoroughcleaning. Cleaning should be carried out by hand-warm fresh water washing at apressure of approx 60 bar. Such cleaning must not take place before the minimumcuring time for obtaining water resistance as listed above has elapsed. Contact thenearest Hempel office for further details.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MULTI-STRENGTH 35530
Ventilation during Ventilation is not required for drying/curing of the coating, but some ventilation isApplication: recommended in order to remove eg spraydust from application.
Minimum out-docking When the painted surface will be exposed to abrasion shortly after out-docking, theinterval of ships: recommended minimum drying/curing time before out-docking is:
(1½)(2)2½3½5812½Minimum days
(40/104)(35/95)30/8625/7720/6815/5910/50Steel temperature °C/°F
When out-docking takes place into water with a temperature at or above 10°C/50°F, andsufficient time afterwards is allowed for full cure before the coating is exposed toabrasion, the recommended minimum time before out-docking is:
(1)(1)1½2357½Minimum days
(40/104)(35/95)30/8625/7720/6815/5910/50Steel temperature °C/°F
Notes:1. The temperatures in the tables above are mean values, but the temperature during
curing should at no time come below 10°C/50°F.2. Curing will proceed under water when the water temperature is above 10°C/50°F.
Remarks: Stripe coating is recommended in tanks.
In case of deep pittings higher film thickness is recommended on areas with pittings.
Post treatment of coated After complete curing, i.e. minimum 7 days at 20°C/68°F, and before being takensurfaces to be in contact into use, the surfaces must be cleaned properly. This will be subject to local/individualwith potable water: specification or regulation but at least for tanks a careful hosing down with clean fresh
water (max. 40°C/104°F if warm water is used) and/or - if possible - by filling with waterallowed to stand for at least 24 hours. Drain and repeat the procedure, and finally flushwith clean fresh water. Desinfication by for instance chlorination can be very aggressivetowards the coating and separate instructions are available.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: October 2001 - 3553010500CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3553010500CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S EPOXY KNIFING FILLER 355QA CURING AGENT 955QA
Description: HEMPEL'S EPOXY KNIFING FILLER 355QA is a solvent free high epoxy compound. Itcures to a hard and tough coat which is resistant to abrasion, water, various solventsand oils. HEMPEL'S EPOXY KNIFING FILLER 355QA does not sink even when applied inthick layers. It adheres well to concrete and steel. Meets F.D.A. requirements.
Recommended use: As a filler for repairing cracks and blow holes and a great variety of other purposes.
PHYSICAL CONSTANTS:Finish: Semi-glossColours: Pastel BlueShade Numbers: 18E50Volume by Solids: 100%Theoretical Spreading Not relevantRate:Flash point: NoneSpecific gravity: 1.6 kg/litre
13.3 lbs/US gallonDry to Touch: 2 - 3 hours at 20ºC/68ºFFully Cured: 7 days at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing ratio: Base 355Q9 : Curing Agent 955QA
1 : 1 by volumeApplication Method: Spatula or Putty knifeThinner (max.vol.) Do not dilutePot-life: 1 hour (20ºC/68ºF)Cleaning of Tools: HEMPEL'S TOOL CLEANER 99610
Recoating Interval, min: 12 hours (20ºC/68ºF)Recoating Interval, max: Max: 30 days (20ºC/68ºF) See REMARKS overleaf
Safety: As general rule, inhalation of solvent vapours or paint mist and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided; respiratory, skin and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3544042070
HEMPEL'S EPOXY KNIFING FILLER 355QA
SURFACE Metal: Remove oil and grease with Hempel's Navi Wash 99330. Abrasive blasting, powerPREPARATION: tool cleaning or sanding, depending on material and condition of surface.
Concrete: Depending on construction and purpose, abrasive blast or treat the concrete with power tools to obtain a rough and firm surface free of laitance and other contaminants. Removedust and loose material. If mechanical treatment is impossible, the surface may be treated withacid etching. For this purpose, an approximate 5% w/w nitric or phosphoric acid solution isrecommended. Protect face and hands from these strong acids.
Prior to etching, the concrete should be soaked with water to prevent acid corrosion of the re-inforcement bars. Leave the acid to act for 3-4 minutes and hose down the surface with freshwater - preferably first with a 5% w/w sodium hydroxide solution - and scrub carefully. After that, thesurface must dry homogenously and appear as an even, rough surface with an appearance of finesandpaper, free of a loose outer layer. The surface must have a pH reaction of between 6.8 - 8.0.If any of these conditions are not fulfilled, the process must be repeated. The surface must bedried with good ventilation for at least two (2) days at 65% relative humidity and 20ºC/68ºF. Thepre-treatment is controlled by scraping with a strong knife. The surface shall feel solid and hard andthe knife must only leave a clear scratch mark. The cleaned surface should be saturated withHempadur Sealer 05970.
APPLICATION Use only where application and curing can proceed at temperatures above 5ºC/41ºF.CONDITIONS: The temperature of the surface and that of the material itself must also be within the
limit.Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation.
PRECEDING COAT: None
SUBSEQUENT COAT: As per specification, depending on area of use.
REMARKS: Maximum time before recoating with Hempadur qualities is 48 hours at 20ºC/68ºF. If maximumrecoat interval is exceeded, roughening of the surface is necessary to ensure intercoat adhesion.May be sanded after approximately 20 hours (20ºC/68ºF). Repair of previously painted surfaceshould include overcoating of a part of the surrounding intact, original paint which must be cleanedand roughened prior to application.
Note: HEMPEL'S EPOXY KNIFING FILLER 355QA is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 355QA18E50
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S COAL TAR EPOXY MASTIC 35670(formerly 356SA)
CURING AGENT 98670 (formerly 957SA)
Description: HEMPEL'S COAL TAR EPOXY MASTIC 35670 is a high solids, high-build polyamidecured coal tar epoxy coating with excellent resistance to sea water, crude oil, various soilchemicals and soil stress.
Recommended use: As a long-life protective coating on steel and concrete in severe corrosive environment,e.g., on submerged surfaces, crude oil and slop tanks, ballast tanks, splash zones,sewage systems, etc. Excellent resistance to chemical attack encountered on both steeland concrete buried pipes.
Approval: Saudi Aramco approved product under APCS-3.
PHYSICAL CONSTANTS:Colours/Shade nos.: Black/19990
Red-brown/60420Finish: Semi-gloss
Semi-glossVolume solids: 96%
96%Theoretical spreading rate: 4.8 m²/litre - 200 microns 4.8 m²/litre - 200 microns
193 sq.ft./US gallon - 8 mils 193 sq.ft./US gallon - 8 milsFlash point: 25°C/77°F
25°C/77°FSpecific gravity: 1.5 kg/litre - 12.5 lbs/US gallon 1.5 kg/litre - 12.5 lbs/US gallonDry to touch: 8-10 hours at 20°C/68°F 8-10 hours at 20°C/68°FFully cured: 7 days at 20°C/68°F 7 days at 20°C/68°F
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS: Mixing ratio: Base 35679 : Curing agent 98670
4 : 1 by volumeApplication method: Airless spray Brush/RollerThinner (max. vol.): 0845 (5%) 0845 (15%)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .021" - .023"Nozzle pressure: 250 bar/3625 psi
(Airless spray data are indicative and subject to adjustment.)Cleaning of tools: HEMPEL'S TOOL CLEANER 9961Indicated film thickness, dry: 200-300 microns/8 - 12 milsIndicated film thickness, wet: 225-325 microns/9 - 13 milsRecoat interval, min.: 24 hours (20°C/68°F)Recoat interval, max.: 7 days (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local or national safety regulation. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3567019990SA001
HEMPEL'S COAL TAR EPOXY MASTIC 35670
SURFACE New steel: Abrasive blasting to minimum ISO 8501-1:1988 Standard Sa 2½. For temporaryPREPARATION: protection, if required, use suitable shopprimer. All damage of shopprimer and contamination from
storage and fabrication, should be thoroughly cleaned prior to final painting.
For repair and touch-up, use HEMPEL'S COAL TAR EPOXY MASTIC 35670.
Repair and Maintenance: Remove salt and other contaminants by high pressure fresh waterhosing. Clean damaged areas thoroughly by abrasive blasting or power tool cleaning. Featheredges to sound and intact areas. Touch up to full film thickness.
Concrete: Must be dry and free of dust and laitance. All traces of release agents must beremoved.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit. Best results
are obtained at 15-20°C/59-68°F. Apply only on a dry and clean surface with a temperature abovethe dew point to avoid condensation. In confined spaces, provide adequate ventilation duringapplication and drying.
PRECEDING COAT: On concrete - HEMPADUR SEALER 0597On steel - None or as per specification
SUBSEQUENT None or as per specification depending on area of use.COAT:
REMARKS:Recoating/Overcoating: The best time for recoating and overcoating is when the paint film is still slightly tacky. This curing
stage is reached after 8 hours at 20°C/68°F under good ventilation. At 20°C/68°F, surfacetemperature and good ventilation, the following maximum recoating intervals apply.:
With HEMPADUR : 7 daysWith HEMPANYL : 24 hoursWith HEMPATEX : 16 hours
If maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: Bleeding may occur into subsequent coat. The effect is only cosmetic and has no negativeinfluence on the anti-corrosive properties of the system.
HEMPEL'S COAL TAR EPOXY MASTIC 35670 is for professional use only.
Issued: January 1999-3567019990SA001HEMPEL PAINTS (SAUDI ARABIA) W.L.L.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3567019990SA001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®GLASSFLAKE 35851CURING AGENT 97652
Description: HEMPADUR GLASSFLAKE 35851 is a two-component, high solids, glass flake pigmentedpolyamide/amine cured epoxy paint with good wetting properties and low waterpermeability. It is selfpriming and forms a hard and tough coating which has goodresistance against abrasion and impact as well as to seawater, mineral oils, aliphatichydrocarbons and splashes from petrol, jet fuel, lubrication oil and related products.
Recommended use: As a coating for steel exposed to abrasion and/or severe corrosive environment.
Service temperatures: Dry: Maximum 140°C/284°F (See REMARKS overleaf)In seawater: Maximum 50°C/140°F (No temperature gradient)Other liquids: Contact Hempel
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/12340 - Red/50630Finish: Semi-glossVolume solids, %: 75 ± 1Theoretical spreading rate: 3.8 m²/litre - 200 micron
150 sq.ft./US gallon - 8 milsFlash point: 25°C/77°FSpecific gravity: 1.6 kg/litre - 13.4 lbs/US gallonDry to touch: 7-8 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 255 g/litre - 2.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 35851: Base 35858 : Curing agent 97652
3 : 1 by volumeApplication method: Airless spray Brush (touch-up)Thinner (max.vol.): 08450 (2%) 08450 (2%)Pot life: 1 hour (20°C/68°F)Nozzle orifice: .021"-.023"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 200 micron/8 milsIndicated film thickness, wet: 275 micron/11 milsRecoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: 30 days
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3585112340CR001
HEMPADUR GLASSFLAKE 35851
SURFACE New steel, "heavy duty use": Abrasive blasting to min. Sa 2½. Grit-blasted surfaces:PREPARATION: recommended profile is Rz minimum 100 micron - maximum 150 micron, corresponding to ISO
Comparator Coarse (G). Oil and grease must be removed with suitable detergent, salts and othercontaminants by (high pressure) fresh water hosing prior to blasting. After blasting, clean thesurface carefully from abrasive and dust.Repair and maintenance: Remove oil and grease etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly byabrasive blasting or power tool cleaning (minor areas only). Feather edges to sound intact areas.Dust off residues. Touch-up to full film thickness.On old ship bottoms and similar pit corroded surfaces, excessive amounts of salt residues maycall for dry abrasive blasting, high pressure fresh water hosing, drying, and finally, dry abrasiveblasting again. Alternatively, water jetting may be used provided the steel surface has already thesurface profile as described above: New steel, "heavy duty use".
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. The CONDITIONS: temperature of the paint itself should be above 15°C/59°F, preferably above 20°C/68°F for proper
application. Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation. Relative humidity max. 90%.
In confined spaces provide adequate ventilation during application and drying.
PRECEDING None, but HEMPADUR 15590 can be used as a "blast primer"COAT:
SUBSEQUENT None, or HEMPADUR-paint as per specification, depending on area of use.COAT:
REMARKS:Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal rangedry is 150-250 micron/6-10 mils.It is recommended to use heavy airless spray equipment with a pump transmission rate of 60:1(approximately), and a theoretical output of min. 12 litres per minute.
Recoating: The long maximum recoating interval for HEMPADUR will be reduced if the coating is more thanjust scarcely exposed to direct sunshine before recoating.If the interval is exceeded, roughening of surface is necessary to ensure intercoat adhesion.
Thinning: Normally not to be diluted.Note: HEMPADUR GLASSFLAKE 35851 is for professional use only.
Issued: July 2001 - 3585112340CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3585112340CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S POLYESTER GF 35920HARDENER 99020
Description: HEMPEL’S POLYESTER GF 35920 is a high solid, two-component heavy duty liningsystem based on isophthalic polyester acrylic copolymer reinforced with glass flakes.Applicable in thick coats by standard heavy duty airless spray equipment.
Recommended use: 1. As rust preventing coating for areas exposed to high abrasion and impact.2. As rust preventing coating for areas requiring short interval between application
and seawater immersion - 6 hours at 20°C/68°F is required.
Service temperatures: Dry: In water (maximum temperature gradient 35°C/63°F):Maximum: 140°C/284°F 80°C/176°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Finish: FlatColours/Shade nos: Off-white/11630 - Yellow/20820 (RAL 1006)Volume solids, %: 90 (See REMARKS overleaf)Theoretical spreading rate: 1.4 m²/litre - 650 micron
56 sq.ft./US gallon - 26 milsFlash point: 26°C/79°FSpecific gravity: 1.2 kg/litre - 10.2 lbs/US gallonDry to touch: 4 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 35 g/litre - 0.3 lbs/US gallon
Shelf life: 6 months (25°C/77°F) from time of production.Shelf life is dependent on storage temperature. Shelf life is reduced at storagetemperatures above 25°C/77°F. Do not store above 40°C/104°F.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: Base 35929 : Hardener 99020
97.5 : 1.5 by volumeApplication method: Airless spray Brush/roller (See separate Application instructions)Thinner: Do not dilute (See separate Application instructions)Pot life: 45 minutes (20°C/68°F) (See separate Application instructions)Nozzle orifice: .030"-.060" (Reversible)Nozzle pressure: min 275 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Styrene and methyl ethyl ketone (See separate Application instructions)Indicated film thickness, dry: 650 micron/26 milsIndicated film thickness, wet: 725 micron/29 milsRecoating interval, min: with itself: 2 hours (20°C/68°F); others: 16 hours (20°C/68°F)Recoating interval, max: 3 days (20°C/68°F)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3592011630
HEMPEL’S POLYESTER GF 35920
SURFACE New steel: Abrasive blasting to min. Sa 2½.PREPARATION: Minimum surface profile corresponding to Rugotest No. 3, BN 11, Keane-Tator Comparator, 5.5
G/S, or ISO Comparator Coarse (G). Oil and grease must be removed by suitable detergent, saltsand other contaminants by (high pressure) fresh water hosing prior to blasting. After blasting cleanthe surface carefully from abrasives and dust.Maintenance: On old exposed areas excessive amounts of soluble salt residues (in pittings) maycall for water jet cleaning or wet abrasive blasting followed by dry abrasive blasting. Alternatively dryabrasive blasting, high pressure fresh water hosing, drying and finally, dry abrasive blasting again.
APPLICATION Use only when application and curing can proceed at temperatures above 10°C/50°F.CONDITIONS: The in-can temperature of the polyester material should be between 15°C/59°F and 25°C/77°F to
facilitate proper application properties.Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation. Relative humidity max. 85%. In confined spaces provide adequate ventilation duringapplication and curing.
PRECEDING None.COAT:
SUBSEQUENT None, or solvent-based coatings as per specification.COAT:
REMARKS:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
Normal range dry is 650-750 micron/26-30 mils. Absolute minimum is 500 micron/20 mils.Maximum not more than 1250 micron/50 mils.
Volume solids: Theoretically, the products contains 100% solid.By practical spray application, however, one of the reactive components added in surplus will belost as volatile in an amount of approx 0.035 kg per litre.Furthermore, the curing process is accompanied by a contraction of approximately 6%. These twofactors result in a volume solids of 90% and a spreading rate of 1.4 m²/l at 650 micron.By extremely unfavourable application conditions, higher losses may result in a "theoretical"spreading rate of approximately 1.2 m²/l at 650 micron. The curing is, however, not affected by thehigher loss.
Note: HEMPEL’S POLYESTER GF 35920 is for professional use only.
Issued: July 2000 - 3592011630HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3592011630
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPEL'S POLYESTER GF 35920HARDENER 99020
Scope: These Application Instructions cover surface preparation, application equipment, andapplication details for HEMPEL'S POLYESTER GF 35920.
Surface preparation: New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½.Minimum surface profile corresponding to Rugotest No. 3, BN11, Keane-TatorComparator, 5.5 G/S, or ISO Comparator Coarse (G). After blasting, clean the surfacecarefully from abrasives and dust.
On pit-corroded surfaces, excessive amounts of salt residues may call for dry abrasiveblasting, high pressure fresh water hosing, drying, and finally, dry abrasive blasting againas described above.
Application equipment: HEMPEL'S POLYESTER GF 35920, being a high-viscosity material, requires specialmeasures to be taken at application.
Standard airless heavy-duty spray equipment:
Pump ratio: min 45:1 (See Note below)Pump output: min. 12 litres/minute (theoretical)Input pressure: min. 6 bar/90 psiSpray hoses: max. 15 metres/50 feet, 3/8" internal diameter, nylon lined
max. 3 metres/10 feet, 1/4" internal diameterRegular surfaces:Nozzle size: .030" through .060"
reversible tipFan angle: 40-60°
Note: Avoid the use of a suction hose. Use an interchangeable pipe, which makes itpossible to remove cured paint.
The pump should preferably be fitted with leather seals although Teflon (PTFE) seals areacceptable for small jobs.
If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internaldiameter) can be added. The pump ratio must be raised to 60:1 or more, yet, the highoutput capacity of the pump must be maintained. Before application starts, the filtershould be removed and hoses should be washed with styrene.
Thinning: Alternatively max. 5% styrene may be added, but thinning must be done with care as theanti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Mixing: Steel temperature between 10°C/50°F and 20°C/68°F:Add ½ a bottle of HARDENER 99020 into the BASE 35929 and mix for 1 minute. Addthe second half of HARDENER 99020 and continue to stir until contents are thoroughlymixed (approx. 2 minutes).
Before start-up, the pump must be flushed with styrene.
At spray stop the equipment should be flushed out using a small amount of styrene,followed by methyl ethyl ketone (MEK) for at least 15 minutes. Where spraying is tocontinue, flush with styrene.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3592011630
HEMPEL'S POLYESTER GF 35920
The pump should work fast during flushing operations and care taken to ensure thatequipment is throughly cleaned.
Steel temperature at and above 20°C/68°F:
1. Add the content of 1 bottle of RETARDER 99190 and mix thoroughly by mechanicalagitation with BASE 35929 only.
After mixing RETARDER 99190 with BASE 35929 it is essential that at least 5minutes are allowed before commencing the addition of the HARDENER 99020.
2. HARDENER 99020 should then be added as described on page 1.
UNDER NO CIRCUMSTANCES RETARDER 99190 SHOULD BE ADDED AFTER THEHARDENER 99020 HAS BEEN ADDED. THIS WILL TOTALLY NEGATE THE CURINGREACTION.
Pot life: When measured under standard conditions the pot life is 45 minutes at 20°C/68°F.However, for a 20 litres/5 US gallons mix, the heat developed by the chemical reactionis so intense that the corresponding practical pot life is substantially shorter.
Therefore:• Irrespective of equipment, use the paint immediately after mixing. At a normal
application speed the 20 litres/5 US gallons are used in approx. 10 minutes.
• Keep an eye on the paint temperature frequently for instance by touching the canwith your hand. If it feels more than hand warm, discard the paint and flush theequipment immediately irrespective of type of spray equipment.
Paint temperature: If the temperature in the can is below approximately 15°C/59°F, the viscosity will be toohigh for application. If the paint temperature when mixing is 25°C/77°F or higher, asubstantial risk of shortened pot life and curing in can/spray equipment exists. Whenworking in warm, subtropical/tropical climates a refrigerated container can be used forstoring/cooling of the paint before application.
Stripe coating: Edges, corners, manual welds, and places difficult to cover properly by spray applicationshould be stripe coated (touched up) either before or after the spray application.One or two stripe coats will usually be necessary, but depending on actual conditions.
Extra film thickness: Extra thickness - extra layer(s) - may be necessary in case of severely pitted and/orwhere very high degrees of antiabrasive properties are needed.
Indicated film thickness: 1500 micron on splash zone areas, 1000 micron on immersed areas below splashzone, and 750 micron on decks are recommend.
Recoating intervals: Within a maximum of 85% Relative Humidity the following recoating intervals apply:
(6 hours)(1 day)
8 hours1½ days
12 hours2 days
16 hours3 days
24 hours5 days
32 hours7½ days
MinMax
With other paints(solvent-based)
(45 min.)(1 day)
1 hour1½ hour
1½ hours2 days
2 hours3 days
3 hours5 days
5 hours7½ days
MinMax
With 35920
(35°C/95°F)30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
The polyester MUST NOT be exposed to (steel) temperatures below 10°C/50°F nor tocondensation or Relative Humidity higher than 85% before recoating.
Cleaning of tools: The equipment should be flushed out and cleaned using styrene followed by methyl ethylketone (MEK).
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3592011630
HEMPEL Product Data
ProductDataData
ProductCuring table: The following curing times apply:
(2½ days)3½ days5 days7 days11 days18 daysFully cured
(35°C/95°F)30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
Time before taking When the painted surface will be exposed to heavy duty service (e.g. exposure tointo service: chemicals, heavy wear and tear), the recommended minimum curing time is:
(1 day)1½ days2 days3 days5 days7½ daysMinimum
(35°C/95°F)30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
If not exposed to heavy duty service (eg exposure to light traffic only):
(8 hours)12 hours16 hours24 hours40 hours60 hoursMinimum
(35°C/95°F)30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
HEMPEL'S POLYESTER GF 35920 is resistant to immersion in calm seawater after aninitial curing time as listed hereunder.
(3 hours)4 hours5 hours6 hours10 hours15 hoursMinimum
(35°C/95°F)30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
Notes:
1. The temperatures in the tables above are mean values, but the temperatureduring curing should at no time come below 10°C/50°F.
2. Curing will proceed under water when the water temperature is above10°C/50°F.
3. Less curing than stated above before exposure to seawater may result in significantdiscoloration of the surface.
Remarks: Stripe coating is recommended on surfaces difficult to cover properly by spray.In case of deep pittings higher film thickness is recommended on areas with pittings.To secure sufficient curing at low surface temperatures as well as to secure apinhole-free paint film at any temperature, the product should always be applied in a wetfilm thickness above 600 micron.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: August 2001 - 3592011630HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 3HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3592011630
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S VINYL ESTER GF 359QACURING AGENT 990QA
Decription: HEMPEL'S VINYL ESTER GF 359QA is a two component cold cured vinyl-ester/acryliccopolymer, reinforced with glass flakes. Applicable in thick coats by standard heavy dutyairless spray equipment.
Recommended use: Immersed environments where superior resistance to chemical attack is required,vinyl-ester us suitable for most chemical environments within the pH range of 0 to 13and is unaffected by demineralised water. It also has excellent resistance to mostsolvents. May be used in aggressive atmospheric or spillage conditions.
PHYSICAL CONSTANTS:Finish: FlatColour: Off-whiteShade Number: 11630Volume by Solids: 90% Please refer to additional paragraph titled "Volume Solids" overleaf. Theoretical 1.33 m²/litre - 750 micronSpreading: 54.18 sq.ft./US gallon - 30 mllsFlash Point: 28ºC/82ºF Abel-Pensky, closed cupSpecific Gravity: 1.19 kg/litre
9.93 lbs/US gallonDry to Touch: 4 hours at 20ºC/68ºFFully Cured: 4 days at 20ºC/68ºFShelf Life: 6 months at 20ºC/68ºF
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Mixing Ratio: Base : 359Q9 98 parts by volume
Curing Agent : 990QA 2 parts by volumeApplication Method: Airless spray Brush / roller (See separate Application Instructions)Thinner: Do not dilute (See separate Application Instructions)Pot-Life: 45 minutes at 20ºC/68ºFNozzle Orifice: 0.030"-0.060" ReversibleNozzle Pressure: Min. 275 bar / 4000 psi
(Airless spray data are indicative and subject to adjustment) Cleaning of Tools: Styrene Monomer, Methyl Ethyl Ketone, Methyl Iso Butyl Ketone before gelIndicated film thickness, wet: 750 micron/30 milsIndicated film thickness, dry: 750 micron/30 milsRecoat interval, min: 2 hours (20ºC/68ºF)Recoat interval, max: 3 days (20ºC/68ºF)
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, Material Safety Data Sheet(s) should be consulted and national or local safetyregulations should be followed. As a general rule, inhalation of solvent vapours or paintmist, and contact of liquid paint with skin and eyes should be avoided. Forcedventilation should be provided when working with solvent-borne materials in confinedspaces or stagnant air. Even when ventilation is provided, respiratory, skin, and eyeprotection are always recommended when spraying paint. Necessary precautionsagainst the risk of fire or explosions must be taken.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 359QA11630
HEMPEL'S VINYL ESTERu GF 359QA
Surface New steel: Abrasive blasting to mininimum Sa 2½ according to ISO 8501-1:1988. MinimumPreparation: surface profile corresponding to Rugotest No. 3, BN 11, Keane-Tator Comparator,
5.5 G/S, or ISO Comparator Coarse (G). Oil and grease must by removed bysuitable detergent, salts and other contaminants by (high pressure) fresh waterhosing prior to blasting. After blasting clean the surface carefully from abrasivesand dust.
Maintenance: On old exposed areas excessive amounts of soluble salt residues (in pitting) maycall for wet abrasive blasting followed by dry abrasive blasting. Alternative dryabrasive blasting, high pressure fresh water hosing, drying and finally, dryabrasive blasting again.
Application Use only when application and curing can proceed at temperatures above 10ºC/50ºF. Apply on aConditions: dry and clean surface with a temperature above the dew point to avoid condensation. Relative
humidity max. 85%.
Preceding Coat: None.
Subsequent Coat: None, or Hempel's Vinyl Ester GF 359QA
Temperature Range: Immersed: 110ºCDry: 175ºC (No known lower limit)
Remarks: May be specified in another film thickness than indicated depending on purpose and area of use. Ifthe specification calls for a subsequent coat, the best time for overcoating is when the applied coatis still tacky.
Volume solids: Theoretically, the products contains 100% solid. By practical spray application, however, one of thereactive components added in surplus will be lost as volatile in an amount of 0.035 kg per litre.
Furthermore, the curing process is accompanied by a contraction of approximately 6%. These twofactors result in a volume solids of 90% and a spreading rate of 1.4 m²/litre at 650 micron.
By extremely unfavourable application conditions, higher losses may result in a "theoretical"spreading rate of approximately 1.2 m²/litre at 650 micron. The curing is, however, not affected bythe higher loss.
Note: HEMPEL'S VINYL ESTER GF 359QA is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 3544042070
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to product data sheet
HEMPEL'S VINYL ESTER GF 359QACURING AGENT 990QA
Scope: These application instructions cover surface preparation, application equipment and applicationdetails for Hempel's Vinyl Ester GF 359QA.
Surface New Steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherPreparation: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, ISO
8501-1:1988, SSPC-SP-10. Minimum surface profile corresponding to Rugotest No. 3, BN11,Keane-Tator Comparator, 5.5 G/S, or ISO Compartor Coarse (G). After blasting, clean the surfacecarefully from abrasive and dust.
On pit-corroded surfaces: Excessive amounts of salt residues may call for dry abrasive blasting,high pressure fresh water hosing, drying, and finally, dry abrasive blasting again as describedabove.
Application Hempel's Vinyl Ester GF 359QA, being a solvent-free, high viscosity material, requires specialEquipment: measures to be taken at application.
Standard airless heavy-duty spray equipment:
Pump ratio: min. 45:1 (see note below)Pump output: min. 12 litres / minute (theoretical)Input pressure: min. 6 bar / 90 psiSpray hoses: max. 15 metres /50 feet, 3/8" internal diameter, nylon lined max. 3 metres
/ 10 feet, 1/4" internal diameterRegular surfaces:Nozzle size: 0.30"-0.60" reversible cleaning headFan angle: 40-60.
Note: Avoid the use of a suction hose. Use an interchangeable pipe, which makes it possible toremove cured paint.
The pump should preferably be fitted with leather seals although Teflon (PTFE) seals areacceptable for small jobs.
If longer spray hoses are necessary the pump ratio must be must be raised to 60:1 or more, yet,the high output capacity of the pump must be maintained. Before application starts, the filtershould be removed and hoses should be washed with styrene.
Thinning: Alternatively, max. 5% styrene may be added, but thinning must be done with care as theantisagging properties are drastically reduced by overthinning. Gel time will be extendedespecially at low temperatures. Airless spray data are indicative and subject to adjustment.
Mixing: Paint temperature below 20ºC/68ºFAdd ½ a bottle of Curing Agent 990QA into the Base 359QA and mix for 1 minute. Add thesecond half of Curing Agent 990QA and continue to stir until contents are thoroughly mixed(approx. 2 minutes).
Before start-up, the pump must be flushed with styrene.
At spray stop the equipment should be flushed out using a small amount of styrene, followed by methyl ethyl ketone (MEK) for at least 15 minutes. Where spraying is to continue, the secondary flush with MEK is not required. The pump should be stroked rapidly during flushing operations and care taken to ensure that equipment is thoroughly cleaned.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 3
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 359QA11630
HEMPEL'S VINYL ESTER GF 359QA
Paint temperature at and above 20C/68F
Add the content of 1 bottle of Retarder and mix thoroughly by mechanical agitation. After mixingRetarader with Base 359QA it is essential that at least 5 minutes are allowed before commencingthe addition of the Curing Agent 990QA.
Curing Agent 990QA should then be added as described above. Under no circumstances Retardershould be added after the Curing Agent 990QA has been added. This will totally negate the curingreaction.
Pot Life: When measured under standard conditions the pot life is 45 minutes at 20ºC/68ºF. However, for a20 litres/5 US gallon mix, the heat developed by the chemical reaction between Base and CuringAgent is so intense that the corresponding practical pot life is substantially shorter.
Therefore: - Irrespective of equipment, use the paint immediately after mixing. At a normalapplication speed the 20 litres/5 US gallon are used in approximately 10 minutes.
- Keep an eye on the paint temperature frequently for instance by touching the canwith your hand. If it feels more than hand warm, discard the paint and flush theequipment immediately irrespective of type of spray equipment.
Paint If in-can temperature is below approximately 15ºC/59ºF viscosity will be too high for application.Temperature: If paint temperature at mixing is 25ºC/77ºF or higher a substantial risk of shortened potlife and
curing in can/spray equipment exists. When working in warm, subtropical/tropical climates arefrigerated container can be used for storing/cooling of the paint before application.
Stripe Coating: Edges, corners, manual welds, and places difficult to cover properly by spray application should bestripe coated (touched up) either before or after the spray application. One or two stripe coats willusually be necessary, but depending on actual conditions.
Extra Film Thickness: Extra thickness / extra layer(s) - maybe necessary in case of severely pitted and/or where very highdegrees of antiabrasive properties are needed.
Indicated 1500 micron on splash zone areas, 1000 micron on immersed areas below splash zone,Film Thickness: and 750 micron on decks are recommended. The maximum film thickness per coat is 750 micron
for vertical surfaces.
Recoating Intervals: Within a maximum of 90% Relative Humidity the following recoating intervals apply (d=days,h=hours):
(27 hours)36 hours2 days3 days5 days7.5 daysMax. interval(30min)45 min1 hour1½ hours3 hours4 hoursMin. interval
(35ºC/95ºF)30ºC/86ºF25ºC/77ºF20ºC/68ºF15ºC/59ºF10ºC/50ºCTemp. of Steel at
The layer of Hempel's Vinyl Ester GF 359QA MUST NOt be exposed to (steel) temperatures below10ºC/50ºF, condensing humidity nor Relative Humidities higher than 85% before overcoating.
Curing Table: The following curing times apply:
1 days1.5 days2 days3 days5 days7.5 daysInitial curing2.5 days3.5 days5 days7 days11 days18 daysFully cured
(35ºC/95ºF)30ºC/86ºF25ºC/77ºF20ºC/68ºF15ºC/59ºF10ºC/50ºCTemp. of Steel at
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 3
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 359QA11630
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S VINYL ESTER GF 359QA
Time Before Taking When the painted surface will be exposed to heavy duty service (e.g. exposure to chemicals,Into Service: heavy wear and tear), the recommended minimum curing time is:
1 day)1.5 days2 days3 days5 days7.5 daysMin. time(35ºC/95ºF)30ºC/86ºF25ºC/77ºF20ºC/68ºF15ºC/59ºF10ºC/50ºCTemp. of Steel at
If not exposed to heavy duty service (e.g. exposure to light traffic):
(8 hours)12 hours16 hours24 hours40 hours60 hoursMin. time(35ºC/95ºF)30ºC/86ºF25ºC/77ºF20ºC/68ºF15ºC/59ºF10ºC/50ºCTemp. of Steel at
Hempel's Vinyl Ester GF 359QA is resistant to immersion in calm seawater after an initial curingtime as listed hereunder.
(3 hours)4 hours5 hours6 hours8 hours15 hoursMin. time
(35ºC/95ºF)30ºC/86ºF25ºC/77ºF20ºC/68ºF15ºC/59ºF10ºC/50ºCTemp. of Steel/Water at
Note: 1. The temperatures in the tables above are mean values, but the temperatureduring curing should at no time come below 10C/50F.
2. Curing will proceed under water when the water temperature is above10C/50F.
Ventilation The following ventilation is recommended during application and drying for full coating ofDuring Application: tanks and void spaces:
Size of tank/void space Number of airshifts:100 m³/3300 cub. feet 4-10 times per hour400 m³/13300 cub. feet 2-5 times per hour1000 m³/33000 cub. feet 1-3 times per hour4000 m³/133000 cub. feet 1 times per hour
The ventilation is not needed for the drying/curing of the coating, but recommended in order toremove e.g. spray dust from application.
Remarks Stripe coating is recommended in tanks.In case of deep pittings higher film thickness is recommended on areas with pittings. To securesufficient curing at low surface temperatures, the product should always be applied in a wet filmthickness above 600 micron.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 3
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 359QA11630
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®UNDERCOAT 42460
Description: HEMPALIN UNDERCOAT 42460 is a fairly quick-drying alkyd paint.
Recommended use: As a general purpose undercoating in alkyd paint systems on exterior and interiorsteelwork, wood, plaster, etc. in mildly to moderately corrosive environment.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish and German authorities accordingto IMO resolution MSC 61 (67).Has a German and Danish EC-type Examination certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: White/10000Finish: FlatVolume solids, %: 53 ± 1Theoretical spreading rate: 13.3 m²/litre - 40 micron
531 sq.ft./US gallon - 1.6 milsFlash point: 38°C/100°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 4 (approx.) hours at 20°C/68°FV.O.C.: 385 g/litre - 3.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08230 (5%) 08230 (15%) 08230 (5%) (See REMARKS overleaf)Nozzle orifice: .015"-.018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08230Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: See REMARKS overleafRecoat interval max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4246010000CO017
HEMPALIN UNDERCOAT 42460
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPALIN PRIMERS or according to specification.COAT:SUBSEQUENT HEMPALIN ENAMELS or according to specification.COAT:REMARKS: Some of the certificates have been issued under the former quality number 4246.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal rangedry is 30-40 micron/1.2-1.6 mils.
Thinning: THINNER 08080 may be used for spray application, howeer, with a certain risk of wrinkling of apreceding fresh HEMPALIN coat.
Recoating: Recoating intervals related to later conditions of exposure:(40 micron/1.6 mils dry film thickness of HEMPALIN UNDERCOAT 42460)
7 daysNone8 hours5 hoursHEMPALIN (white spirit only)
MediumMildMediumMild
AtmosphericAtmosphericRecoated with
20°C/68°F20°C/68°FSurface Temperature
MaximumMinimum
If this maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean surface thoroughly by (highpressure) fresh water cleaning and allow to dry.
Note: HEMPALIN UNDERCOAT 42460 is for professional use only.
Issued: October 1999 - 4246010000CO017HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4246010000CO017
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®45141/HEMPADUR®45143
45141: BASE 45148 with CURING AGENT 9782045143: BASE 45148 with CURING AGENT 97430
Description: HEMPADUR 45141/45143 is a two-component, polyamide adduct cured epoxy paint withgood wetting properties and low water permeability. It is selfpriming and forms a hardand tough coating which has good resistance against abrasion and impact as well as toseawater, mineral oils, aliphatic hydrocarbons and splashes from petrol and relatedproducts. Harmless to grain cargoes.
Recommended use: 1. As a high build primer, intermediate and/or finishing coat in (heavy duty) paintsystems according to specification. (As a finishing coat where a cosmeticappearance is of less importance).
2. For repair and maintenance work at application temperatures above -10°C/15°F onhatch covers, decks, in cargo holds, etc.
3. As a ballast tank coating.HEMPADUR 45143 is intended for use in cold/temperate climates, HEMPADUR 45141for warmer climates - see APPLICATION CONDITIONS overleaf.
Service temperatures: Dry: Maximum 150°C/302°F (See REMARKS overleaf)Ballast water service: Resists normal ambient temperatures at sea*Other water service: 40°C/104°F (no temperature gradient)Other liquids: Contact HEMPEL*Avoid long-term exposure to negative temperature gradients.
Certificates/Approvals: See REMARKS overleaf.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version; mixed product: 45141 45143Colours/Shade nos: Red/50630* Red/50630*Finish: Semi-gloss Semi-glossVolume solids, %: 60 ± 1 60 ± 1Theoretical spreading rate: 4.0 m²/litre - 150 micron 4.0 m²/litre - 150 micron
160 sq.ft./US gallon - 6 mils 160 sq.ft./US gallon - 6 milsFlash point: 25°C/77°F 25°C/77°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallon 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 4 (approx.) hrs at 20°C/68°F (ISO 1517) 5 (approx.) hrs at 5°C/41°F (ISO 1517)Dry to touch: 7 (approx.) hours at 20°C/68°F 11 (approx.) hours at 5°C/41°FFully cured: 7 (approx.) days at 20°C/68°F 20 (approx.) days at 5°C/41°FV.O.C.: 385 g/litre - 3.2 lbs/US gallon 385 g/litre - 3.2 lbs/US gallon
*Other shades inlcuding a MIO version, colour no. 12430, according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS: 45141 45143Mixing ratio: Base 45148 : Curing agent 97820 Base 45148 : Curing agent 97430
3 : 1 by volume 3 : 1 by volumeApplication method: Airless spray Brush Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%) 08450 (5%) 08450 (5%)
(See REMARKS overleaf) (See REMARKS overleaf)Pot life: 2 hrs (20°C/68°F) 4 hrs (20°C/68°F) 2 hrs (15°C/59°F) 4 hrs (15°C/59°F)
(See REMARKS overleaf) (See REMARKS overleaf)Nozzle orifice: .019"-.023"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or THINNER 08450Indicated film thickness, dry: 150 micron/ 6 mils (See REMARKS overleaf)Indicated film thickness, wet: 250 micron/10 milsRecoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO002/4514150630CO003
HEMPADUR 45141/45143
SURFACE New steel: When used selfprimed surface preparation as to specification. When being an integralPREPARATION: part in heavy duty systems abrasive blasting to Sa 2½. Reference is made to separate
APPLICATION INSTRUCTIONS.New steel, ballast tanks and similar areas: Abrasive blasting to Sa 2½. For temporary protection,if required, use a suitable shopprimer. All damage of shopprimer and contamination from storageand fabrication should be thoroughly cleaned prior to final painting - preferably by abrasive blasting.For repair and touch-up, use HEMPADUR 45141/45143.Stainless steel: (Ballast tanks in chemical carriers) to be abrasive blasted to a uniform, sharp,dense profile, ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts,grease, oil, etc. to be removed before abrasive blasting is commenced.Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to St 3 (spot-repairs) or by abrasive blasting to min. Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance of HEMPADUR 45141/45143.As an alternative to dry cleaning, water jetting to sound, well adhering coat and/or to steel. Intactcoat must appear with roughened surface after the water jetting. By water jetting to steel,cleanliness shall be WJ-3 to WJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No.5/SSPC-SP 12). A flash-rust degree of maximum FR-2 (atmospheric exposure) / FR-2, preferablyFR-1 (immersion) (Hempel standard) is acceptable before application. Feather edges to sound andintact paint. Dust off residues. On pit-corroded surfaces, excessive amounts of salt residues maycall for water jetting, wet abrasive blasting, alternatively dry abrasive blasting, high pressure freshwater hosing, drying, and finally, dry abrasive blasting again.
APPLICATION Apply only on a dry an clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. HEMPADUR 45143 is intended for curing conditions down to -10°C/14°F,
HEMPADUR 45141 is to be selected in warmer climates. A shift from 45143 to 45141 is mostconvenient to take place when the temperature is between 15°C/59°F and 25°C/77°F, however,HEMPADUR 45141 may be used for curing conditions down to 0°C/32°F in cases where surfacesare not to be immersed. Optimal spraying properties are obtained at paint temperatures of18-22°C/64-72°F. In warm climates, the paint should be stored in a cool place. At painttemperatures below 15°C/59°F or in the case of very long spray hoses, thinning may be necessary.This will cause lower film build and longer drying time.In confined spaces provide adequate ventilation during application and drying.
PRECEDING COAT: None or according to specification.SUBSEQUENT COAT: None or according to specification.REMARKS: See separate APPLICATION INSTRUCTIONS.Certificates/ Certificates have been issued under the former quality number 4514.Approvals: Approved by Lloyd's Register of Shipping as a recognised corrosion control coating. Tested for
non-contamination of grain cargo at the Newcastle Occupational Health, Great Britain.Approved as a ballast tank coating by Germanischer Lloyd, Germany.Classified as a class 1 material according to BS 476, Part 7: 1987 (fire testing).Accepted as a corrosion control coating by Maritime Register of Shipping, Russia.Complies with Section 175.300 of the Code of Federal Regulations in respect of carriage of dryfoodstuffs (FDA) in spaces with an internal surface area larger than 1000 m²/10,750 sq.ft.
Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Colour: Light shades will have a tendency to yellow when exposed to sunshine.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 125-175 micron/5-7 mils.
Thinning: Thinning above 5% may cause lower film build and slower drying/curing. Mix the componentsthoroughly.
Induction time: If the paint temperature, as an exception, is below approx. 10°C/50°F, allow the mixture topre-react 30 minutes before use.
Recoating: Recoat intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry.If the maximum recoat interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: HEMPADUR 45141/45143 is for professional use only.
Issued: March 2002 - 4514350630CO002/4514150630CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO002/4514150630CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®45141/HEMPADUR®45143
45141: BASE 45148 with CURING AGENT 9782045143: BASE 45148 with CURING AGENT 97430
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR 45141/45143.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning is recommended.However, HEMPADUR 45141/45143 may be applied on rusty steel surfaces wherehigher performance is needed than obtainable with conventional coatings but wheremechanical cleaning and dust removal can only be carried out (beside the removal ofsalts and of oily contaminants).
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
REPAIR AND MAINTENANCE:
Spot-repairs:Clean damaged areas thoroughly by power tool cleaning to St 3 or by abrasive blastingto minimum Sa 2, preferably Sa 2½. Improved surface preparation will improve theperformance of HEMPADUR 45141/45143. As an alternative to dry cleaning, waterjetting to sound, well adhering coat and/or to steel. Intact coat must appear withroughened surface after the water jetting. By water jetting to steel, cleanliness shall beWJ-3 to WJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No.5/SSPC-SP 12). A flash-rust degree of maximum FR-2 (atmospheric exposure) / FR-2,preferably FR-1 (immersion) (Hempel standard) is acceptable before application. Featheredges to sound and intact areas. Brush off loose material. Touch up to full filmthickness.
Compatibility: HEMPADUR 45141/45143 may be used in connection with other genericpaint systems than epoxy and polyurethanes.
In any case it is a must that the old paint system is tightly adhering and is properlyprepared before the touch-up is performed. It is recommended to make a test patch.
Full coating:
Compatibility with old system: HEMPADUR 45141/45143 may exceptionally be applieddirectly on top of an old alkyd paint system provided this is tightly adhering. It isfurthermore preferable that the old system is less than approximately 500 micron in filmthickness. A test patch should always be performed before fullcoating is decided. Evenold chlorinated rubber and vinyl systems may be overcoated but with an inherent risk oflater tendency to "liftings" along mechanical damage and similar weaknesses.Removal of old system: Full coating after mechanical removal of an old paint system ispossible too. Yet, it must be considered that mechanical cleaning may produce a verysmooth surface giving reason to reduced adhesive forces.
Note: Another risk is left over of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a continuous oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paintmaterial may flake off.
When used for immersion service:1. Abrasive blasting to Sa 2½. After abrasive blasting, clean the surface carefully from
abrasives and dust. For temporary protection, if required, use suitable shopprimer.All damage to shopprimer and contamination from storage and fabrication should bethoroughly cleaned prior to final painting.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO001/4514150630CO003
HEMPADUR 45141/45143
Stainless steel: (Ballast tanks in chemical carriers) to be abrasive blasted to auniform, sharp, dense profile, ISO Comparator Medium (G), corresponding to Rzminimum 50 micron. Any salts, grease, oil, etc. to be removed before abrasiveblasting is commenced.
2. If the HEMPADUR 45141/45143 will form an integral part of heavy duty systems(impact and antiabrasion purposes) best performance will be obtained by applying itdirectly to the blast-cleaned steel, subsidiary using HEMPADUR 15590 as "blastprimer".
Note: On old steel surfaces having been exposed to salt water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
Application equipment: HEMPADUR 45141/45143 being a high viscosity material, may require specialmeasures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min 45:1Pump output: 12 litres/minute (theoretical)Input pressure: min. 6 bar/90 psiSpray hoses: max 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Filter: 60 mesh
Regular surfaces:Nozzle size: .021"-.023"Fan angle: 60-80°.
Complicated surfaces (and touch up):Nozzle size: .019"Fan angle: 40°.
After finishing the application, clean the equipment immediately with HEMPEL’S TOOLCLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approximately 5% THINNER 08450 may be added, but thinning mustbe done with care as the maximum obtainable film thickness is reduced significantly byoverthinning.
Airless spray data are indicative and subject to adjustment.
Application: Film-build/continuity: With this paintmaterial applied in one/few coat(s) it is of specialimportance that a continuous, pinhole-free paint film is obtained at application of eachcoat. An application technique which will ensure good film formation on all surfacesmust be adopted. It is very important to use nozzles of the correct size, not too big, andto have a proper, uniform distance of the spray gun to the surface, 30-50 cm should beaimed at. Furthermore, great care must be taken to cover edges, openings, rear sides ofstiffeners etc. Thus, on these areas a stripecoat will usually be necessary. To obtaingood and steady atomizing, the viscosity of the paint must be suitable and the sprayequipment must be sufficient in output pressure and capacity. At high workingtemperatures, use of extra thinner may be necessary to avoid dust-spray.
The paint layer must be applied homogenously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks and solventretention. The paint consumption must be controlled.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO001/4514150630CO003
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 45141/45143
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
On poorly prepared surfaces it is always recommended to apply first coat by brush.Extra thinning will facilitate the penetration of the paint material but will also require anextra layer to be applied.
Wet/dry film thickness: The thixotropic nature of HEMPADUR 45141/45143 may give a rather "wavy"surface ofthe paint just after application. This smoothens at drying but can make it necessary tolet the wet film readings be of a higher value than indicated. In many cases, the wet filmthickness reading should be 25-50 micron/1-2 mils higher than calculated. As the wavysurface becomes more smooth at drying this extra wet film thickness readings will notcause a higher paint consumption than otherwise stipulated.
Pot life: When measured under standard conditions the pot life is 2 hours at 15°C/59°F whenusing CURING AGENT 97430. However, for a 20 litres/5 US gallons mix, the heatdeveloped by the chemical reaction between BASE and CURING AGENT may make thecorresponding practical pot life shorter.
At these temperatures therefore: Irrespective of equipment, use the paint immediatelyafter mixing. (At a normal application speed the 20 litres/5 US gallons are used inapprox. 10 minutes.) Anyhow, at paint temperatures, as an exception, being lower than15°C/59°F allow the mixture to pre-react approximately 30 minutes before use. Afterthis induction time, apply the paint immediately.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: March 2002 - 4514350630CO001/4514150630CO003HEMPEL’S MARINE PAINTS A/S
Attached: Tables of "physical data versus temperature"
In relation to recoating intervals the following is very important:
Maximum recoating intervals:If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion or in thecase of recoating with coatings other than HEMPADUR, apply a (thin) additional coat ofHEMPADUR 45141/45143 within the following directions for recoating:
• Long recoating intervals:A completely clean surface is mandatory to ensure intercoat adhesion, especially inthe case of long recoating intervals. Any dirt, oil and grease have to be removed witheg suitable detergent followed by high pressure fresh water cleaning. Salts to beremoved by fresh water hosing.
• Any degraded surface layer, as a result of a long exposure period, must beremoved as well. Water jetting may be relevant to remove any degraded surface layerand may also replace the above-mentioned cleaning methods when properlyexecuted. Consult HEMPEL for specific advice if in doubt.
To check whether the quality of the surface cleaning is adequate, a test patch may beRelevant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO001/4514150630CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPADUR 45141/45143
Physical data (HEMPADUR 45141 in a dry film thickness of 150 micron/6 mils):
versus temperature:
5 days36 hours
Not relevant
10 days3 days
Not relevant
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with HEMPATHANE qualities
NoneNone
15 days
NoneNone
30 days
Atmospheric, mediumAtmospheric, severeImmersion***
Interval for recoating with HEMPADUR qualities
36 hours18 hours
3 days1½ days
Atmospheric MediumSevere
Interval for recoating with 58030
5 hours5 hours
10 hours10 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 56360
6 hours6 hours
12 hours12 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 46410
MAXIMUM recoating intervalrelated to later conditions of exposure:
4 hours5 hours6 hours
8 hours9 hours
12 hours
Atmospheric, mediumAtmospheric, severeImmersion**
Interval for recoating with HEMPADUR andHEMPATHANE qualities
6 hours6 hours
11 hours11 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 58030
3 hours4 hours
6 hours8 hours
Atmospheric, mediumAtmospheric, severe
Interval recoating with 46410, 56360
MINIMUM recoating interval related to later conditions of exposure:
3½ hours3½ days
7 hours7 days
Drying timeCuring time
30°C/86°F20°C/68°FSurface temperature
* Not relevant for HEMPATHANE qualities.** Depending on actual local conditions, extended maximum recoating intervals may apply.
Please contact HEMPEL for further advice.
Furthermore, please see page 3.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO001/4514150630CO003
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 45141/45143
Physical data (HEMPADUR 45143 in a dry film thickness of 150 micron/6 mils):versus temperature:
10 days3 days
20 days6 days
45 days15 days
90 days30 days
Atmospheric. mediumAtmospheric, severe
Interval for recoating with HEMPATHANE qualities
NoneNone
30 days
NoneNone
60 days
NoneNone
90 days
NoneNone
(90 days)
Atmospheric, mediumAtmospheric, severeImmersion***
Interval for recoating with HEMPADUR qualities
3 days1½ days
6 days3 days
Not relevantNot relevant
Not relevantNot relevant
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 58030
7½ hours7½ hours
15 hours15 hours
34 hours34 hours
2½ days2½ days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 56360
10 hours10 hours
20 hours20 hours
45 hours45 hours
4 days4 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 46410
MAXIMUM recoating interval related to later conditions of exposure:
4 hours5 hours
8 hours10 hours
18 hours23 hours
36 hours45 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR and HEMPATHANE qualities
6 hours6 hours
12 hours12 hours
Not relevantNot relevant
Not relevantNot relevant
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 58030
3 hours4 hours
6 hours8 hours
14 hours18 hours
28 hours36 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 46410, 56360
MINIMUM recoating interval related to later conditions of exposure:
4 hours7 days
7 hours14 days
14 hours28 days
35 hours2 months
Drying timeCuring time
20°C/68°F10°C/50°F0°C/32°F-10°C/14°FSurface temperature
* Not relevant for HEMPATHANE qualities.** Depending on actual local conditions, extended maximum recoating intervals may apply.Please contact HEMPEL for further advice.
Furthermore, please see page 3.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4514350630CO001/4514150630CO003
HEMPEL Product Data
ProductDataData
Product HEMPADUR®45150BASE 45159 with CURING AGENT 95450
Description: HEMPADUR 45150 is a two-component, high solids, polyamine cured epoxy paint withgood self-priming properties.
Recommended use: Especially for repair and maintenance work when high demands to surface preparationcannot be obtained completely and where good compatibility with existing paint systemis required. Facilitates furthermore a high dry film thickness per touch-up coat.May be used as a high build primer, intermediate and/or finishing coat in paint systemsaccording to specification when a low solvent content and high film thickness per coatare required. As a finishing coat where a "cosmetic appearance" is only of lessimportance.
Service temperatures: Dry: In water (no temperature gradient):Maximum: 80°C/176°F 30°C/86°FSee REMARKS overleaf.
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Classified as class 1 material according to BS 476: Part 7: 1987 (fire testing).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50630* - Grey/12170*Finish: Semi-glossVolume solids, %: 82 ± 1Theoretical spreading rate: 4.1 m²/litre - 200 micron
164 sq.ft./US gallon - 8 milsFlash point: 41°C/106°FSpecific gravity: 1.4 kg/litre - 11.4 lbs/US gallonSurface dry: 6 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 14 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 170 g/litre - 1.4 lbs/US gallon
*Another shade grey 11480 according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 45150: Base 45159 : Curing agent 95450 (see REMARKS overleaf)
1 : 1 by volumeApplication method: Airless spray BrushThinner (max.vol.): 08450 (5%) 08450 (5%) (See separate APPLICATION INSTRUCTIONS)Pot life: 2 hrs (20°C/68°F) 3 hrs (20°C/68°F) (See REMARKS overleaf)Nozzle orifice: .019"-.023"
(See separate APPLICATION INSTRUCTIONS)Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or THINNER 08450Indicated film thickness, dry: 200 micron/8 mils (See REMARKS overleaf)Indicated film thickness, wet: 250 micron/10 mils (See REMARKS overleaf)Recoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
HEMPADUR 45150
SURFACE Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andPREPARATION: other contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly by
power tool cleaning to St 3 (spot-repairs) or by abrasive blasting to min. Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance of HEMPADUR 4515. As an alternativeto dry cleaning, water jetting to sound, well adhering coat and/or to steel. Intact coat must appearwith roughened surface after the water jetting. By water jetting to steel, cleanliness shall be WJ-3 toWJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No. 5/SSPC-SP 12). A flash-rustdegree of maximum FR-2 (atmospheric exposure) / FR-2, preferably FR-1 (immersion) (Hempelstandard) is acceptable before application. Feather edges to sound intact areas. Dust off residues.Touch up to full film thickness.On pit-corroded surfaces, excessive amounts of salt residues may call for high pressure waterjetting or wet abrasive blasting, alternatively dry abrasive blasting followed by high pressure freshwater hosing, drying, and finally, dry abrasive blasting again. Please see APPLICATIONINSTRUCTIONS.New steel: When used as intermediate and/or finishing coat surface preparation as to ProductData Sheet for the preceding primer coat (HEMPADUR primers). When used selfpriming surfacepreparation as to specification.GALVOSILS: Please see APPLICATION INSTRUCTIONS.
APPLICATION Apply only on a dry and clean surface. Use only where application and curing can proceed atCONDITIONS: temperatures above approx. 15°C/59°F. The temperature of the paint itself should also be
minimum 15°C/59°F.At high temperatures use the product immediately after a thorough mixing and stirring. SeeREMARKS below.In confined spaces provide adequate ventilation during application and drying.
PRECEDING COAT: None or according to specification. HEMPADUR 45150 may be used directly on zinc silicates ormetal-sprayed surfaces - reference is made to APPLICATION INSTRUCTIONS.
SUBSEQUENT COAT: None or according to specification.
REMARKS: Please see separate APPLICATION INSTRUCTIONS.Certificates have been issued under the former quality number 4515.
Weathering/ The natural tendency of epoxy coatings to chalk in ourdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is also reflectedtemperatures: in this product.Colour: Light shades will have a tendency to yellow when exposed to sunshine and darken when exposed
to heat.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
For airless spray application normal range is 150-250 micron/6-10 mils. This will alter spreadingrate and may slightly influence drying time and recoating interval. Concerning measurement of wetfilm thickness, please consult separate APPLICATION INSTRUCTIONS.For application by brush, obtainable dry film thicknesses are up to 100-125 micron/4-5 mils percoat.
Curing agent: Note: At certain stockpoints, HEMPADUR 45150 may be supplied with an alternative, low-viscosityCURING AGENT 95454 in order to facilitate spray application in a dry film thickness of 75-150micron/3-6 mils. This curing agent can be used for brush application too if a smooth surface isrequired. Contact HEMPEL for further advice.
Pot life: The pot life is dependent on packing size and temperature. For bigger packings and a temperatureat 35°C/95°F the pot life will be reduced to approx. 15 minutes.Recoating: Recoat intervals related to later conditions of exposure: Consult separate APPLICATIONINSTRUCTIONS.Before recoating after exposure in contaminated environment, clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry.If the maximum recoat interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Note: HEMPADUR 45150 is for professional use only.
Issued: March 2002 - 4515050630CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®45150BASE 45159 with CURING AGENT 95450
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR 45150.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning or water jetting isrecommended. However, HEMPADUR 45150 may be applied to steel surfaces whereless good surface preparation is possible, but where higher performance is requiredthan obtainable with conventional coatings.
The high solids content of HEMPADUR 45150 reduces the risk of solvent entrapmentwhich, together with its flexibility, highly improves its compatibility with coatings of othergeneric types.
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
REPAIR AND MAINTENANCE:
Spot-repairs:
Clean damaged areas thoroughly by power tool cleaning to St 3 or by abrasive blastingto minimum Sa 2, preferably Sa 2½. Improved surface preparation will improve theperformance of HEMPADUR 45150. As an alternative to dry cleaning, water jetting tosound, well adhering coat and/or to steel. Intact coat must appear with roughenedsurface after the water jetting. By water jetting to steel, cleanliness shall be WJ-3 toWJ-2 (atmospheric exposure) / minimum WJ-2 (immersion) (NACE No. 5/SSPC-SP 12). Aflash-rust degree of maximum FR-2 (atmospheric exposure) / FR-2, preferably FR-1(immersion) (Hempel standard) is acceptable before application. Feather edges to soundand intact areas. Brush off loose material. Touch up to full film thickness.
Compatibility: HEMPADUR 45150 may be used in connection with other generic paintsystems than epoxy and polyurethanes.
In any case it is a must that the old paint system is tightly adhering and is properlyprepared before the touch-up is performed. It is recommended to make a test patch.
Full coating:
Compatibility with old system: Due to its low solvent content HEMPADUR 45150 maybe applied directly on top of an old alkyd paint system provided this is tightly adhering. Itis furthermore preferable that the old system is less than approximately 500 micron infilm thickness. A test patch should always be performed before fullcoating is decided.Even old chlorinated rubber and vinyl systems may be recoated but with a risk of latertendency to “liftings” along mechanical damage and similar weaknesses. This is mainlydue to the difference in physical properties of the underlying old, thermoplastic paint filmcompared to the new HEMPADUR 45150.
Removal of old system: Full coating after complete mechanical removal of an old paintsystem is possible too. Yet, it must be considered that mechanical cleaning mayproduce a very smooth surface giving reason to reduced adhesive forces.
Note: Another risk is left over of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a continuous oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paintmaterial may flake off.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
HEMPADUR 45150
When used for immersion service, repair:Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughlyby power tool cleaning to St 3 (minor areas) or by abrasive blasting to min Sa 2,preferably Sa 2½. Improved surface preparation will improve the performance ofHEMPADUR 45150. As an alternative to dry cleaning, water jetting to minimum WJ-3,preferably WJ-2 (NACE No. 5/SSPC-SP 12), may be used. A flash rust degree ofmaximum FR-2 (HEMPEL standard) is acceptable before application. Feather edges tosound intact areas. Dust off residues. Touch up to full film thickness.
Note: On old steel surfaces having been exposed to salt water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
NEW STEEL:
When used as intermediate and/or finishing coat surface preparation as to Product DataSheet for the preceding primer coat (HEMPADUR primers). When used selfprimingsurface preparation as to specification.
When applied to GALVOSILS:
HEMPADUR 45150 can be applied when the GALVOSIL has cured sufficiently forrecoating. Consult APPLICATION INSTRUCTIONS for the relevant GALVOSIL. Remove oiland grease etc. with suitable detergent. Remove salt and other contaminants by highpressure fresh water cleaning. After exposure to high humidity, zinc salts, "white rust",must be removed carefully by high pressure fresh water cleaning, if necessary combinedwith scrubbing with stiff nylon brushes.
Application equipment: HEMPADUR 45150 being a relatively high viscosity material, may require specialmeasures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min 45:1Pump output: 12 litres/minute (theoretical)Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .021" through .025"Fan angle: 60°.
Complicated surfaces (and touch up):Nozzle size: .019" through .021"Fan angle: 40°.
After finishing the application, clean the equipment immediately with THINNER 08450 orHEMPEL’S TOOL CLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approx. 5% THINNER 08450 may be added, but thinning must bedone with care as the anti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 45150
Application: Film-build/continuity: With this paintmaterial applied in one/few coat(s) it is of specialimportance that a continuous, pinhole-free paint film is obtained at application of eachcoat. An application technique which will ensure good film formation on all surfacesmust be adopted. It is very important to use nozzles of the correct size, not too big, andto have a proper, uniform distance of the spray gun to the surface, 30-50 cm should beaimed at. Furthermore, great care must be taken to cover edges, openings, rear sides ofstiffeners etc. Thus, on these areas a stripecoat will usually be necessary. To obtaingood and steady atomizing, the viscosity of the paint must be suitable and the sprayequipment must be sufficient in output pressure and capacity. At high workingtemperatures, use of extra thinner may be necessary to avoid dust-spray.
The paint layer must be applied homogenously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks and solventretention. The paint consumption must be controlled.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
On poorly prepared surfaces it is always recommended to apply the first coat by brush.Extra thinning will facilitate the penetration of the paint material, but will also require anextra layer to be applied.
Non-popping on zinc-silicate (GALVOSILS) or on spray-metallized surfaces: DiluteHEMPADUR 45150 with minimum 30% THINNER 08450 and apply a flash coat. Afterapproximately 24 hours (20°C/68°F), a full coat of HEMPADUR 45150 is applied. Thisprocedure only applies to HEMPADUR 45150 or HEMPADUR 45150/HEMPATHANE55210 systems.
Wet/dry film thickness: Please note that the thixotropic nature of HEMPADUR 45150 may give a rather "wavy"surface of the paint just after application - especially when using the "high-build"CURING AGENT 95450. This smoothens at drying, but can make it necessary to let thewet film readings be of a higher value than indicated. In many cases the wet filmthickness. reading should be 25-50 micron/1-2 mils higher than calculated. As the wavysurface becomes more smooth at drying, this extra wet film thickness. readings will notcause a higher paint consumption than otherwise stipulated.
Pot life: When measured under standard conditions the pot life is 2 hours at 20°C/68°F.However, for a 20 litres/5 US gallons mix, and used under warm climate conditions (upto approximately 35°C/95°F) the heat developed by the chemical reaction betweenBASE and CURING AGENT may make the corresponding practical pot life shorter.Therefore: Irrespective of equipment, use the paint immediately after mixing. (At anormal application speed the 20 litres/5 US gallons are used in approximately 10minutes.)
Application at low For temperatures below 15°C/59°F reference is made to Product Data Sheet forTemperatures: HEMPADUR 45143.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: March 2002 - 4515050630CO005HEMPEL’S MARINE PAINTS A/S
Attached: Table of "physical data versus temperature"
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPADUR 45150
Physical data HEMPADUR 45150 in a dry film thickness of 200 micron/8 mils:versus temperature:
None3 days
None6 days
None10 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPATHANE qualities
NoneNone
45 days
NoneNone
90 days
NoneNone
5 months
Atmospheric, mediumAtmospheric, severeImmersion***
Interval for recoating with HEMPADUR qualities
3½ days2 days
7 days4 days
12 days7 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 58030
8 hours6 hours
16 hours12 hours
27 hours20 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 56360
12 hours12 hours9 hours
24 hours24 hours18 hours
40 hours40 hours30 hours
Atmospheric, mediumAtmospheric, severeImmersion*
Interval for recoating with 46330 and 46410
MAXIMUM recoating interval related to later conditions of exposure:
6 hours8 hours8 hours
12 hours16 hours16 hours
20 hours27 hours27 hours
Atmospheric, mediumAtmospheric, severeImmersion**
Interval for recoating with HEMPADUR and HEMPATHANE qualities
8 hours8 hours
16 hours16 hours
27 hours27 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with 58030
2 hours3 hours4 hours
4 hours6 hours8 hours
7 hours10 hours14 hours
Atmospheric, mediumAtmospheric, severeImmersion*
Interval for recoating with 46330, 46410, 56360
MINIMUM recoating interval related to later conditions of exposure:
7 hours3½ days
14 hours7 days
24 hours12 days
Drying timeCuring time
30°C/86°F20°C/68°F15°C/59°CSurface temperature
* Only 46330 are recommended for this exposure** NOT relevant for HEMPATHANE Qualities*** Depending on actual local conditions, extended maximum recoating intervals may apply.
Please contact HEMPEL for further advice.
Maximum recoating intervals:If the maximum recoating interval is exceeded, whatever the subsequent coat,roughening of the surface is necessary to ensure optimum intercoat adhesion or in thecase of recoating with coatings other than HEMPADUR, apply a (thin) additional coat ofHEMPADUR 45150 within the above directions for recoating.Long recoating intervals:A completely clean surface is mandatory to ensure intercoat adhesion, especially in thecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.Any degraded surface layer, as a result of a long exposure period, must be removed aswell. Water jetting may be relevant to remove any degraded surface layer and may alsoreplace the above-mentioned cleaning methods when properly executed. Consult HEMPEL for specific advice if in doubt.To check whether the quality of the surface cleaning is adequate, a test patch may beRelevant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 4HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4515050630CO005
HEMPEL Product Data
ProductDataData
Product HEMPADUR®45182CURING AGENT 98180
Description: HEMPADUR 45182 is a two-component, low-temperature curing, modified polyamideadduct cured epoxy.
Recommended use: For marine and protective use as a "tie coat" between epoxy and physically dryingcoatings. For marine use also as a “sealer” of old antifouling.
Service temperatures: Maximum, dry: 80°C/176°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Yellowish grey/25150Finish: FlatVolume solids, %: 46 ± 1Theoretical spreading rate: 4.6 m²/litre - 100 micron
184 sq.ft./US gallon - 4 milsFlash point: 23°C/73°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonDry to touch: 6 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 490 g/litre - 4.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 45182: Base 45187 : Curing agent 98180
4 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max.vol.): 08450 (5%) 08450 (5%)Pot life: 3 hours (20°C/68°F)Nozzle orifice: .023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subejct to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 225 micron/9 milsRecoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: Antifoulings: 3 days (20°C/68°F)
Other topcoats, for areas above water: according to separate painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4518225150CR001
HEMPADUR 45182
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection if required use suitablePREPARATION: shopprimer. Any damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For priming purposes, specified HEMPADUR paint.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning.When used as “tie coat”: remove all rust and other loose material by abrasive blasting orpowertool cleaning. Feather edges to sound and intact areas. Dust off residues. Touch up to fullfilm thickness with specified HEMPADUR paint (see REMARKS below).When used as “sealer” on old antifouling: a very careful high pressure freshwater cleaning -orjetting, if needed - to remove possible leached layer of antifouling and make sure that old layers ofweak intercoat adhesion (“sandwich” structure”) really is removed.
APPLICATION Use only where application and curing can proceed at temperatures higher than -10°C/14°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit. Apply only on
a dry and clean surface with a temperature above the dew point to avoid condensation.In confined spaces such as sea chest or stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR systems according to specification or old antifouling system well cleaned and in goodCOAT: condition.
SUBSEQUENT Antifouling or other physically drying solvent based paints according to specification.COAT:
REMARKS:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal rangedry is 75-125 micron/3-5 mils. As “sealer” typically to be specified in 50 -75 micron/2-3 mils dryfilm thickness. Thinning may be required to facilitate proper film formation.
Film thicknesses, HEMPADUR 45182 is designed for recoating with antifoulings in any normal specified totalsubsequent coats: film thicknesses. HEMPADUR 45182 is not designed for recoating with heavy duty epoxy systems.
Later maintenance of paint systems with HEMPADUR 45182 as a part of the system is accordinglymost conveniently carried out by touch-up with a “mastic” type epoxy and with a proper overlap ofintact surrounding paint system.
Recoating: A completely clean surface is mandatory to ensure intercoat adhesion, especially in the case oflong recoating intervals. Any dirt, oil and grease have to be removed with eg suitable detergentfollowed by high pressure fresh water cleaning. Salts to be removed by fresh water hosing. Anydegraded surface layer, as a result of a long exposure period, must be removed as well. Waterjetting may be relevant to remove any degraded surface layer and may also replace theabove-mentioned cleaning methods when properly executed. To check whether the quality of thesurface cleaning is adequate, a test patch may be relevant. A thin extra coat of HEMPADUR 45182may advantageously be applied if there is any doubt about suitability of cleaning process.
Note: HEMPADUR 45182 is for professional use only.
Issued: June 2001 - 4518225150CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4518225150CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®HI-BUILD 45200BASE 45209 with CURING AGENT 95040
Description: HEMPADUR HI-BUILD 45200 is a two-component, high build epoxy paint. It forms a hardand tough coating resistant to seawater, mineral oils and splashes from petrol andrelated products.
Recommended use: As an intermediate or finishing coat designed for on-line application of containers.
Service temperatures: Dry:Maximum: 140°C/284°FSee REMARKS overleaf.
Certificates/Approvals: Complies with Section 175.300 of U.S. Federal Regulations in respect of carriage of dryfoodstuffs.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/12170*Finish: Semi-flatVolume solids, %: 59 ± 1Theoretical spreading rate: 7.4 m²/litre - 80 micron
296 sq.ft./US gallon - 3.2 milsFlash point: 26°C/79°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: 2 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 5-7 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 395 g/litre - 3.3 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: Base 45209 : Curing agent 95040
3 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max. Vol.): 08450 (10%) 08450 (10%)
(See REMARKS overleaf)Pot life: 5 hours (20°C/68°F) (airless)
8 hours (20°C/68°F) (brush)Nozzle orifice: .018"-.021"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 80 micron/3.2 mils (see REMARKS overleaf)Indicated film thickness, wet: 150 micron/6 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4520012170CO011
HEMPADUR HI-BUILD 45200
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection, if required, usePREPARATION: suitable shopprimer. All damage of shopprimer and contamination from storage and fabrication
should be thoroughly cleaned prior to final painting. For repair and touch-up use HEMPADURHI-BUILD 45200 or other specified HEMPADUR paint.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and other loose material byabrasive blasting or powertool cleaning. Feather edges to sound and intact areas. Dust offresidues. Touch up to full film thickness.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Use only when application and curing can proceed at temperatures above
10°C/50°F, preferably above 15°C/59°F. The temperature of the surface must also be above thislimit. The temperature of the paint itself should be 15°C/60°F or above to secure properapplication properties. In confined spaces provide adequate ventilation during application andDrying.
PRECEDING None, HEMPADUR PRIMER 15300, HEMPADUR ZINC 15360 or according to specification.COAT:
SUBSEQUENT None, HEMPATHANE qualities or according to specification.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreService sensitive to mechanical damage and chemical exposure at elevated temperatures is also reflectedtemperatures: in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 60-90 micron/2.4-3.6 mils for use on containers. For other uses (contact Hempel) normal rangeis 100-125 micron/4-5 mils which is achieved by none or limited diluting at application.
Recoating interval: According to relevant container painting specification.
Note: HEMPADUR HI-BUILD 45200 is for professional use only.
Issued: April 2002 - 4520012170CO011HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4520012170CO011
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®HI-BUILD 45221BASE 45225 with CURING AGENT 97220
Description: HEMPADUR HI-BUILD 45221 is a two-component, high build epoxy paint. It forms a hardand tough coating resistant to abrasion, impact, seawater, diesel oil, splashes frompetrol and related products. Limited resistance to vegetable oils and strong solventssuch as ketones and esters. Not recommended for acids, alkalies, or strong oxidizingSolutions.
Recommended use: As an intermediate or finishing coat designed for on-line application of containers.
Service temperatures: Maximum, dry: 140°C/284°F.
Certificates/Approvals: Complies with Section 175.300 of the Code of Federal Regulations in respect of carriageof dry foodstuffs.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11150Finish: Semi-flatVolume solids, %: 49 ± 1Theoretical spreading rate: 8.2 m²/litre - 60 micron
327 sq.ft./US gallon - 2.4 milsFlash point: 22°C/72°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 1 (app.) hour at 20°C/68°F (ISO 1517)Dry to touch: 4 (app.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 465 g/litre - 3.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 45221: Base 45225 : Curing agent 97220
3 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max. Vol.): 08450 (5%) 08450 (5%)Pot life: 8 hours (20°C/68°F) 12 hours (20°C/68°F)Nozzle orifice: .017"-.021"Nozzle pressure: 200 bar/3000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 60 micron/2.4 mils (see REMARKS overleaf)Indicated film thickness, wet: 125 micron/5 mils
Recoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4522111150CO001
HEMPADUR HI-BUILD 45221
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Use only when application and curing can proceed at temperatures above
10°C/50°F, preferably above 15°C/59°F.The temperature of the paint itself should preferably be between 18°C/64°F and 25°C/77°F tosecure proper application properties.In confined spaces provide adequate ventilation during application and drying.
PRECEDING None, HEMPADUR PRIMER 15300, HEMPADUR ZINC 15360 or according toCOAT: specification.
SUBSEQUENT None, HEMPATHANE qualities, HEMPATEX HI-BUILD 46370 or according to specification.COAT:
REMARKS:Colours: To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in eg
red, orange, yellow and green.Certificates have been issued under the former quality number 4522.
Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is30-60 micron/1.2-2.4 mils.
Application: If zinc silicate primer preceedes, HEMPADUR HI-BUILD 45221 is to be applied by a specialflash-coat technique. Cover the zinc silicate with a mist-coat of 45221 in a thicknesscorresponding to max. 40 micron dry film thickness - appearance being of a patchy nature. Let theair escape and apply full coat according to specification maximum 10 minutes (20°C/68°F) later.
Recoating According to relevant container painting specification.interval:
Note: HEMPADUR HI-BUILD 45221 is for professional use only.
Issued: April 2002 - 4522111150CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4522111150CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR* HI-BUILD 45230CURING AGENT 95040
Description: HEMPADUR HI-BUILD 45230 is a two-component, high build, polyamide cured epoxypaint. It forms a hard and tough coating resistant to seawater, splashes of mineral oilsand aliphatic hydrocarbons. Limited resistance to vegetable and animals oils, aromatichydrocarbons and stronger solvents. Not resistant to alkalies, acids, and oxidizingmaterials.
Recommended use: In moderate to severely corrosive environments as an intermediate or finishing coatdirectly on cured zinc silicate (GALVOSIL products) or similar surfaces to minimizepopping.As a finishing coat where a cosmetic appearance is of less importance.For shop application or for use below 10°C/50°F. CURING AGENT 95570 can substituteCURING AGENT 95040 - please see overleaf.
Service temperatures: Maximum, dry: 140°C/284°F, see REMARKS overleaf.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light grey/12170Finish: Semi-flatVolume solids: 61%Theoretical spreading rate: 6.1 m²/litre - 100 micron
245 sq.ft./US gallon - 4 milsFlash point: 25°C/77°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonSurface dry: 3 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 8-10 hours at 20°C/68°FFully cured: 1 week at 20°C/68°FV.O.C.: 367 g/litre - 3.1 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Mixing ratio for 45230: Base 45239 : Curing agent 95040
3 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max. vol.): 08700 (5%) 08700 (5%)Pot life: 2 hours (20°C/68°F) 6 hours (20°C/68°F)Nozzle orifice: .018"-.021"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment) Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: See REMARKS overleaf Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4523012170CO00
HEMPADUR HI-BUILD 45230
SURFACE Zinc silicate coated surfaces: Remove oil and grease etc. with suitable detergent. Remove saltPREPARATION: and other contaminants by (high pressure) fresh water cleaning. After exposure to high humidity,
zinc salts ("white rust") will have to be carefully removed by high pressure fresh water cleaning, ifnecessary combined with scrubbing with stiff nylon brushes. Consult the APPLICATIONINSTRUCTIONS for the relevant GALVOSIL product.
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit. Apply only on
a dry and clean surface with a temperature above the dew point to avoid condensation. In confined spaces provide adequate ventilation during application and drying.Note: For curing at temperatures below 10°C/50°F and down to -10°C/14°F, CURING AGENT95570 can be used. Mixing ratio 45239:95570 = 3.0:1.0 parts by volume. Can also substitute forshop application where fast drying and shorter recoating intervals are required. Please contactHempel for further advice.
PRECEDING COAT: HEMPEL’S GALVOSIL qualities, or according to specification.SUBSEQUENTCOAT: None, or as listed below under recoating intervals, according to specification.
For other qualities, consult nearest HEMPEL office.REMARKS:Weathering: A tendency to chalk in outdoor exposure does not detract from the protective properties.Service Even though the service temperature is kept below the specified maximum, it should be noted thattemperatures: the higher the temperature, the more sensitive the paint will be to mechanical and/or chemical
exposure. Combined thermal/mechanical and/or chemical exposure may therefore increase therisk of damage.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 50-100 micron/2-4 mils. However, to obtain optimum anti-popping properties on top of zincsilicates (GALVOSIL) apply HEMPADUR HI-BUILD 45230 in a dry film thickness of at least 75micron/3 mils. It is recommended to apply a mist coat of the non-diluted HEMPADUR HI-BUILD45230, let the air escape, and then a few minutes later apply the full coat of HEMPADUR HI-BUILD45230. At temperatures below approximately 25°C/77°F this procedure is especially recommended.
Recoating: Recoating intervals related to later conditions of exposure:(100 micron/4 mils dry film thickness of HEMPADUR HI-BUILD 45230)
Not relevantNot relevantNot relevantNot relevant
12 hours16 hours3 days
30 days*
16 hours24 hours10 days
None
Not relevantNot relevantNot relevantNot relevant
6 hours8 hours16 hours16 hours
6 hours6 hours12 hours12 hours
563604641055210
45200. 45230
WaterimmersionSevereMedium
WaterimmersionSevereMedium
Recoated with(quality numbers only)
AtmosphericAtmospheric
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
*If the coating has been subjected to direct sunlight for a short period only, the maximum recoating interval may be prolonged.
Before recoating after exposure in contaminated environment clean the surface thoroughly by (highpressure) fresh water hosing and allow to dry. If the maximum recoating interval is exceeded,roughening of the surface is necessary to ensure intercoat adhesion.
Note: HEMPADUR HI-BUILD 45230 is for professional use only.
Issued: September 1997-4523012170CO00HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4523012170CO00
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MULTI-STRENGTH®45540CURING AGENT 97531
Description: HEMPADUR MULTI-STRENGTH 45540 is an amine-adduct cured epoxy coating. It is ahard, impact and abrasion resistant coating eg for splash zones.
Recommended use: As a self-primed, high build coating primarily for maintenance of eg splash zones, jettypilings and bridge underdecks.
Service temperatures: Dry: In water (no temperature gradient):Maximum: 140°C/284°F 80°C/176°F (See REMARKS overleaf)
Certificates/Approvals: Conforms with NORSOK M-501, rev. 4, system no. 7 below splash zone.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Black/19990Finish: GlossyVolume solids, %: 84 ± 1Theoretical spreading rate: 2.4 m²/litre - 350 microns
96 sq.ft./US gallon - 14 milsFlash point: 14°C/57°FSpecific gravity: 1.7 kg/litre
14.2 lbs/US gallonSurface dry: 4 (approx.) hours at 20°C/68°FDry to touch: 6 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 170 g/litre - 1.4 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 45540: Base 45549 : Curing agent 97531
4 : 1 by volumeApplication method: Airless sprayThinner (max.vol.): 08450 (5%)Pot life: 1 hour at 20°C/68°FNozzle orifice: .021"-.023"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 350 micron/14 milsIndicated film thickness, wet: 425 micron/17 milsRecoat interval, min: 16 hours (20°C/68°F)Recoat interval, max: 5 days (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4554019990CR002
HEMPADUR MULTI-STRENGTH 45540
SURFACE New steel (dry conditions): Abrasive blasting to Sa 2½, (ISO 8501-1:1988) with a surface profilePREPARATION: equivalent to Rugotest No. 3 BN 10b, Keane-Tator Comparator 3.0 G/S or ISO Comparator, ROUGH
MEDIUM (G).Remove any oil, grease and other contaminants by detergent and salts by high fresh water hosingprior to abrasive blasting.Maintenance: Remove oil and grease, etc.with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material by wet ordry abrasive blasting or for minor areas power tool cleaning. Feather edges to sound and intactareas. After wet abrasive blasting hose down the surface by hot water rinsing ("steam cleaning").Touch up bare spots to full film thickness when the surface has become visually dry.
APPLICATION HEMPADUR MULTI-STRENGTH 45540 may be applied and will cure at temperatures down toCONDITIONS: 5°C/41°F.
The temperature of the paint itself should be above 15°C/59°F. The best result is obtained at20-30°C/68-86°F.In confined spaces provide adequate ventilation.
PRECEDING None.COAT:
SUBSEQUENT None or according to specification.COAT:
REMARKS:Weathering/ The natural tendency of epoxy coatings to chalk in ourdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is also reflectedtemperatures: in this product.Colour: Light shades will have a tendency to yellow when exposed to sunshine and darken when exposed
to heat.Service Maximum peak temperature in water is 90°C/194°F.temperatures:Recoating: If the maximum recoat interval is exceeded, roughening of the surface is necessary to ensure
adhesion.
Note: HEMPADUR MULTI-STRENGTH 45540 is for professional use only.
Issued: January 2002 - 4554019990CR002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4554019990CR002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S LIGHT PRIMER 45550CURING AGENT 95360
Description: HEMPEL'S LIGHT PRIMER 45551 is a two component polyamide adduct cured epoxyhigh build coating. It forms a hard and tough coating resistant to water and petroleumproducts.
Recommended use: As a primer on steel, aluminium, glassfibre, soft and hard woods including plywood andferro-cement.
PHYSICAL CONSTANTS:Finish: FlatColours: Off White/GreyShade Numbers: 11630/12170Volume by Solids: 51% Theoretical spreading rate: 8.5 m²/litre - 60 microns
346 sq.ft/US gallon - 2.4 milsFlash Point: 25/77 C/F A Pensky, closed cupSpecific Gravity: 1.3 kg/litre
10.9 lbs/US gallonDry to Touch: 2-3 hours at 20ºC/68ºFFully Cured: 7 (approx.) days at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf
APPLICATION DETAILS:Mixing Ratio: Base: Hempel's Light Primer 45559 2 parts by volume
Curing Agent: 95360 1 part by volumeApplication Method: Brush/Roller Airless SprayPot Life: 6 hours (20ºC/68ºF) 2 hours (20ºC/68ºF)Thinner (max.vol.): 08450 (5%) 08450 (5%)Nozzle Orifice: 0.019" - 0.023"Nozzle Pressure: 175 bar/2450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08450Indicated film thickness, wet: 120 micronsIndicated film thickness, dry: 60 micronsRecoat interval, min: 1 hour (20ºC/68ºF)Recoat interval, max: 30 days
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed. As a general rule,inhalation of solvent vapours or paint mist, and contact of liquid paint with skin and eyesshould be avoided. Forced ventilation should be provided when working with solventborne materials in confined spaces or stagnant air. Even when ventilation is provided,respiratory, skin and eye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4555011630
HEMPEL'S LIGHT PRIMER 45551
Surface Iron Steel: Remove oil, grease, etc. with suitable detergent. Remove salt and other Preparation: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa
2½, SCPC-SP10. Small areas may be mechanically grinded to leave a metallicallyclean and rough surface.
Aluminium: Remove oil, grease, etc. with suitable detergent for aluminium surfaces, e.g.Hempel's Light Clean 99350, followed by (high pressure) fresh water cleaning.Abrasive seeeping with non-metallic abrasive to produce a unifiormly roughenedsurface.
Plywood: Sand the surface carefully and remove dust. Saturate the surface, especially theedges, with Hempadur Sealer 05991 - remove surplus to avoid a glossy layer ofsealer after drying.
Glassfibre: Degrease the surface with Hempel's Light Clean 99350. Grind the surface withsandpaper No. 180, remove dust.
Overcoating: When Hempel's Light Primer 45551 is applied in 60 micron dry film thickness the followingrecoat/overcoating intervals are valid:
Recoat Intervals: 10ºC/50ºF 20ºC/68ºF 30ºC/86ºF
Epoxies min. 8 hours 4 hours 3 hoursmax. 60 days 30 days 20 days
Polyurethane min. 8 hours 4 hours 3 hoursmax. 6 days 3 days 2 days
If the maximum recoat interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Application Apply only where application and curing can proceed at temperatures above 5ºC/41ºF. Conditions: Temperature of the surface and that of the paint itself must be above the same limit. Best result
is obtained at temperatures between 15-20ºC/59-68ºF. The surface must be clean and dry and itstemperature must be above the dew point to avoid condensation. In confined spaces provideadequate ventilation during application and drying.
Subsequent Coat: According to specification.
Remarks: Before overcoating after exposure in contaminated environments, clean surface thoroughly by highpressure fresh water hosing and allow to dry. Abrading the surface prior to the application ofsubsequent coats may be necessary.
Note: HEMPEL'S LIGHT PRIMER 45551 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4555011630
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®MIO 45670CURING AGENT 95040
Description: HEMPADUR MIO 45670 is a two-component, polyamide cured epoxy paint, pigmentedwith micaceous iron oxide (MIO). Resistant to water, mineral oils, aliphatichydrocarbons, and to abrasion and impact. Limited resistance to aromatichydrocarbons and stronger solvents, and to acidic and oxidizing materials.
Recommended use: 1. As a primer or an intermediate coat in HEMPADUR Systems in severely corrosiveenvironment.
2. As a heavy duty finishing coat, eg on helicopter decks and on other structuralsteel.
3. As a primer on galvanised steel and light alloys for HEMPADUR Systems inmoderately corrosive environment.
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Finish: Semi FlatColour: Dark GreyShade Number: 12130Volume by Solids: 55%Theoretical Spreading 7.3 m²/litre - 75 micronsRate: 299 sq.ft./US gallon - 3 milsFlash Point: 26C/79F Abel-Pensky, closed cupSpecific Gravity: 1.4 kg/litre
11.7 lbs/US gallonSurface Dry: 2 (approx) hours at 20ºC/68ºF (ISO 1517)Dry to Touch: 6 - 8 hours at 20ºC/68ºFFully Cured: 1 week at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing Ratio: BASE : HEMPADUR MIO 45679 3 parts by volume
CURING AGENT : 95040 1 part by volumeApplication Method: Airless Spray Brush (touch up)Thinner (max.vol.): 08450 or 08460 (5%) 08450 (5%)Pot-Life: 6 hours (20C/68F)Nozzle Orifice: 0.023"Nozzle Pressure: 200 bar/2900 psi (Airless spray data are indicative and subject to adjustment)Cleaning of Tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, wet: 150 micron/6 milsIndicated film thickness, dry: 75 micron/3 mils (See REMARKS overleaf)Recoat interval, min: 10 hours (20ºC/68ºF)Recoat interval, max: See REMARKS overleaf
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed. As a general rule,inhalation of solvent vapours or paint mist, and contact of liquid paint with skin andeyes, should be avoided. Forced ventilation should be provided when applying paint inconfined spaces or stagnant air. Even when ventilation is provided respiratory, skin, andeye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4567012130
HEMPADUR®MIO 45670
Surface New steel: Abrasive blasting to Sa 2½ SSPC-SP-10. For temporary protection, if Preparation: required, use suitable shopprimer. All damage of shopprimer and contamination from storage and
fabrication should be thoroughly cleaned prior to final painting. For repair and touch-up useHEMPADUR MIO 45670. Galvanized steel and light alloys: Thorough degreasing and light abrasivesweeping to secure optimal adhesion.Maintenance: Remove oil and grease etc., with suitable detergent. Remove salt and othercontaminants by high pressure fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Feather edges to sound and intact areas. Dust offresidues. Touch up to full film thickness.
Application & Use only where application and curing can proceed at temperatures above 10ºC/50ºF. Curing Conditions: The temperature of the surface and that of the paint itself must also be above this limit. At
temperatures below 15ºC/59ºF mix the components thoroughly and allow the mixture to pre-react30 minutes before use. Furthermore, a special curing agent 95420 is available for use between-10ºC/14ºF and 10ºC/50ºF. Apply only on a dry and clean surface with a temperature above thedew point to avoid condensation. Relative humidity maximum 80%. In confined spaces provideadequate ventilation during application and drying.
Preceding Coat: None, HEMPADUR ZINC 15360, HEMPADUR PRIMER 15300, or according to specification.Subsequent Coat: None, or polyamide cured HEMPADUR, or as per specification depending on area of use.
Remarks:Service Dry service temperature: max. 120ºC/248ºF.Temperature: Dry peak temperature: max. 140ºC/284ºF.Film Thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
Normal range is 40-100 microns. This will alter spreading rate and may influence amount ofthinning, drying time and recoating interval. When used as a blast primer a dry film thickness of 40microns/1.6 mils is recommended.
Recoating Intervals: On surfaces later on exposed to (periodical) immersion, heavy condensation, great variationsin temperature, chemical attack, and/or abrasion, the following recoating intervals apply to obtainoptimum performance (75 microns dft - sufficient ventilation).
Intervals at 20ºC/68ºF for Recoating with: Minimum MaximumHempadur qualities 10 hours 30 daysHempathane qualities 10 hours 3 daysHempanyl Hi-Build 46220 10 hours 48 hoursHempatex Hi-Build 46330 6 hours 36 hoursHempatex Hi-Build 46370 6 hours 24 hoursHempanyl Hi-Build 46610 6 hours 36 hours
Under other service conditions no maximum recoating interval for HEMPADUR and HEMPATHANEqualities. If the maximum recoating interval is exceeded, roughening of the surface is necessary toensure intercoat adhesion.
V.O.C: The Volatile Organic Compounds are 415 g/litre, 3.5 lbs/US gallon.Notes: Before overcoating after exposure in contaminated environment, clean the surfacethoroughly by high pressure fresh water hosing and allow to dry.
Note: HEMPADUR®MIO 45670 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4567012130
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MULTI-STRENGTH®45751/45753Medium to high temperatures: 45751: BASE 45755 with CURING AGENT 97652Low to medium temperatures: 45753: BASE 45755 with CURING AGENT 98750
Description: HEMPADUR MULTI-STRENGTH 45751/45753 is a self-priming, two-component,high-build, epoxy-polyamide/amine paint which cures to an abrasion and corrosionresistant coating. Applicable by standard heavy duty airless spray equipment.
Recommended use: As a heavy duty coating for areas exposed to abrasion and aggressive corrosive climatesuch as ramps, ship hulls and holds of bulk carriers.As a ballast tank coating for special purposes such as chemical carriers carrying hotcargoes and other purposes where “pure epoxy coating” is requested.As a finishing coat where a cosmetic appearance is of less importance.HEMPADUR MULTI-STRENGTH 45751 is intended for use in warm climates.HEMPADUR MULTI-STRENGTH 45753 is intended for use in cold climates - seeAPPLICATION CONDITIONS overleaf.
Service temperatures: Dry: Maximum 140°C/284°F (See REMARKS overleaf)Ballast water service: Resists normal ambient temperatures at sea*Other water service: 50°C/140°F (no temperature gradient)Other liquids: Contact HEMPEL*Avoid long-term exposure to negative temperature gradients.
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health, GreatBritain.Approved by Lloyd’s Register of Shipping as a recognized corrosion control coating.Approved as a ballast tank coating by Germanischer Lloyd, Germany.Classification B1 by Marintek, Norway.Recognized by Lloyd’s Register of Shipping as a low friction surface coating for shipsnavigating in first year ice conditions. Conforms with Norsok M-501, system no. 7.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version; mixed product: 45751 45753Colours/Shade nos: Grey/12340 - Red/50630 Grey/12340 - Red/50630Finish: Semi-gloss Semi-glossVolume solids, %: 79 ± 1 76 ± 1Theoretical spreading rate: 4.0 m²/litre - 200 micron 3.8 m²/litre - 200 micron
158 sq.ft./US gallon - 8 mils 152 sq.ft./US gallon - 8 milsFlash point: 27°C/81°F 27°C/81°FSpecific gravity: 1.6 kg/litre - 13.4 lbs/US gallon 1.6 kg/litre - 13.4 lbs/US gallonDry to touch: 7-8 hours at 20°C/68°F 8-10 hours at 10°C/50°FFully cured: 7 days at 20°C/68°F 14 days at 10°C/50°FV.O.C.: 255 g/litre - 2.1 lbs/US gallon 240 g/litre - 2.0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: 45751 45753Base 45755 : Curing agent 97652 Base 45755 : Curing agent 98750
3 : 1 by volume 3 : 1 by volumeApplication method: Airless sprayThinner (max.vol.): 08450 (5%) (See PRECEDING COAT overleaf and separate APPLICATION INSTRUCTIONS)Pot life: 1 hour (20°C/68°F) 1 hour (20°C/68°F)Nozzle orifice: .021"-.023" .021"-.023"Nozzle pressure: 250 bar/3600 psi 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 200 micron/8 mils 200 micron/8 milsIndicated film thickness, wet: 250 micron/10 mils 275 micron/11 milsRecoat interval, min: 6 hours (20°C/68°F) 12 hours (10°C/50°F)Recoat interval, max: See REMARKS overleaf See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
HEMPADUR MULTI-STRENGTH 45751/45753
SURFACE New steel:PREPARATION: "Heavy duty use": Abrasive blasting to min. Sa 2½. Grit-blasted surfaces:
recommended profile is Rz minimum 100 micron - maximum 150 micron, corresponding to ISOComparator Coarse (G). Oil and grease must be removed with suitable detergent, salts and othercontaminants by (high pressure) fresh water hosing prior to blasting. After blasting, clean thesurface carefully from abrasive and dust.Ballast tanks and similar areas: Abrasive blasting to Sa 2½. For temporary protection, if required,use a suitable shopprimer. Damage of shopprimer and contamination from storage and fabricationshould be thoroughly cleaned prior to final painting. The best performance will be obtained byabrasive spot-blasting of welds, rusty spots, etc. and by abrasive sweep blasting of the intactshopprimer. For repair and touch-up use HEMPADUR MULTI-STRENGTH 45751/45753.Stainless steel: (Ballast tanks in chemical carriers) to be abrasive blasted to a uniform, sharp,dense profile, ISO Comparator Medium (G), corresponding to Rz minimum 50 micron. Any salts,grease, oil, etc. to be removed before abrasive blasting is commenced.Repair and maintenance:The actual purpose and conditions may make other types and degrees of surface preparation thanthe above described relevant. Reference is made to separate application instructions.
APPLICATION Use only where application and curing can proceed at temperatures above -10°C/14°F forCONDITIONS: HEMPADUR MULTI-STRENGTH 45753 and above 10°C/50°F for HEMPADUR MULTI-STRENGTH
45751. The temperature of the paint itself should be above 15°C/59°F, preferably above20°C/68°F for HEMPADUR MULTI-STRENGTH 45751, for proper application. Apply only on a dryand clean surface with a temperature above the dew point to avoid condensation. Relativehumidity max. 90%. In confined spaces provide adequate ventilation during application and drying.
PRECEDING None, but HEMPADUR 15590 can be used as a "blast primer" for HEMPADUR MULTI-STRENGTHCOAT: 45751. HEMPADUR MULTI-STRENGTH 45753 can be used as a "blast primer” for HEMPADUR
MULTI-STRENGTH 45753 when diluted 15-25% with HEMPEL’S THINNER 08450.SUBSEQUENT COAT: None, or HEMPADUR-paint as per specification, depending on area of use.REMARKS:Colour ofCuring Agent:The curing agent 98750 has a tendency to become darker at storage. This has no influence on
performance, but may influence the shade of the mixed product.Some certificates have been issued under the former quality numbers 45750 or 4575.HEMPADUR MULTI-STRENGTH 45751 is identical with the former 45750 except that mixing ratioand thixotropy properties have been adjusted to specific demands of application, for instance dualfeed two component spray equipment and supply in 1000 litres paint containers.
Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal rangedry is 150-250 micron/6-10 mils.It is recommended to use heavy airless spray equipment with a pump transmission rate of 60:1(approximately), and a theoretical output of min. 12 litres per minute.
Recoating: Recoating intervals related to later conditions of exposure:(200 micron/8 mils dry film thickness of HEMPADUR MULTI-STRENGTH 45751/45753I
N/R6 days20 daysN/R10 hours8 hoursN/R3 days10 daysN/R5 hours4 hoursHEMPATHANE Topcoat
60 daysNoneNone12 hours10 hours8 hours30 daysNoneNone6 hours5 hours4 hoursHEMPADUR
SevereMediumSevereMediumSevereMediumSevereMedium Immer-sion
AtmosphericImmer-sion
AtmosphericImmer-sion
AtmosphericImmer-sion
Atmospheric
Recoated with
10°C/50°F20°C/68°FSurface temp.
MaximumMinimumMaximumMinimum
Curing agent 98750Curing agent 97652
Recoating: The long maximum recoating interval for HEMPADUR will be reduced if the coating is more thanjust scarcely exposed to direct sunshine before recoating.If the interval is exceeded, roughening of surface is necessary to ensure intercoat adhesion.Thinning: Normally not to be diluted.
Note: HEMPADUR MULTI-STRENGTH 45751/45753 is for professional use only.
Issued: April 2002 - 4575112340CO002/4575312340C0001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPADUR MULTI-STRENGTH®45751/HEMPADUR MULTI-STRENGTH®45753
45751: BASE 45755 with CURING AGENT 9765245753: BASE 45755 with CURING AGENT 98750
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR MULTI-STRENGTH 45751/45753.
Surface preparation: The specific type and degree of surface preparation depends on type and condition ofthe actual substrate and on desired performance. The better the surface preparation thebetter the performance, but it will not always be economic feasible to go for the highestdegree within a given type of surface preparation.
For use as a heavy duty coating:Bulk cargoholds, fender areas, hulls of ice-going vessels, ramps, splash zones etc.:New steel:Abrasive blasting to min. Sa 2½. Grit-blasted surfaces: Recommended profile is Rzminimum 100 micron/4 mils - maximum 150 micron/6 mils corresponding to ISOComparator Coarse (G). Oil and grease must be removed with suitable detergent, saltsand other contaminants by (high pressure) fresh water hosing prior to blasting. Afterblasting, clean the surface carefully from abrasive and dust. HEMPADUR 15590 may beused as a blast primer/hold-coat (min. temperature 10°C/50°F) or alternativelyHEMPADUR MULTI-STRENGTH 45751 or HEMPADUR MULTI-STRENGTH 45753 (fortemperatures below 10°C/50°F) diluted 15-25% with HEMPEL’S THINNER 08450.Old steel:For old steel with widespread surface corrosion, often in the state of large areas of fine,dense pit-corrosion - like Grade D, ISO 8501-1:1988 an overall degree of cleaningcorresponding to Sa2 can be the economical optimum treatment of surfaces exposed tocombined mechanical abrasion/impact and atmospheric corrosion in marineenvironments. May advantageously be combined with a thorough fresh water hosing - orreplaced by a water jetting - (degree WJ-2 according to NACE No.5/SSPC-SP 12) as longas the formation of flash rust is low, (maximum degree FR2 as per internal HEMPELstandard).
The fresh water cleaning will assist in removal of salt residues, yet total removal of saltsembedded in the pittings will in practise, on large areas, be extremely difficultirrespective of method of cleaning.
In cases where elimination of risk of osmotic blistering is important, for instancefrequently/permanently immersed surfaces or fresh water exposure a combined dryabrasive blasting, to remove “black scale” and water jetting (minimum WJ-2) may berelevant (possible formation of flash rust to be maximum, FR1).
After water jetting as surface preparation it is recommended to apply a dilutedHEMPADUR MULTI-STRENGTH 45751/45753 (15-25% THINNER 08450) as an (extra)first coat. Surfaces to be dry at application.
Concrete: The concrete must be of good quality and fully cured, eg 28 days for normalPortland cement, and completely dry with a humidity content in the surface below 4%.The concrete must also be controlled for absence of capillary water action or for subsoilwater.
Minimum pull-off value should normally be 20 kilopond/cm² measured after surfacepreparation. Any cracks, crevices and voids must be repaired (see below).All possible slip agent, oil, grease and other contaminants must be removed by egabrasive blasting, volatilising by flame cleaning or treatment with suitable detergent.The last mentioned in the following way: Saturation of the surface with fresh water.Washing with suitable detergent followed by fresh water hosing.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
HEMPADUR MULTI-STRENGTH 45751/45753
Depending on construction and purpose, abrasive blast, high pressure water jet or treatthe concrete with power tools to obtain a rough and firm surface free of scum layer andother contamination and possible old paint/lining. Remove dust and loose material.
If mechanical treatment is impossible, the surface of new concrete may be treated withacid etching. For this purpose an approx. 5% w/w nitric or phosphoric acid solution isrecommended.
Note: Strong acids, take necessary precautions, make sure that safety regulations areobeyed!
Prior to etching the concrete should be saturated with fresh water to prevent acidcorrosion of the reinforcement bars. Leave the acid to act for 3-4 minutes and hosedown the surface with fresh water - preferably first a 5% w/w sodium hydroxide solution- and scrub carefully. After that the surface must dry homogeneously and appear as aneven, rough surface free of a loose outer layer. The surface must have a pH reaction ofbetween 6.5-8.0. If any of these conditions are not fulfilled, the process must berepeated. The surface must be dried with good ventilation for at least 2 days at 65%relative humidity and 20°C/68°F. The pre-treatment is controlled by scraping with astrong knife. The surface must feel solid and hard, and the knife must only leave a clearscratch mark.
Cracks, voids and crevices must be opened and made good down to firm and hardmaterial. After sealing - as described below - fill these openings with a suitable epoxymortar.
Seal the surface with HEMPADUR SEALER 05970 in such a way that the surface is justsaturated. Surplus must be removed (do also see the Product Data sheet for HEMPADURSEALER 05970).
For use as a ballast tank coating:Ballast tanks, steel work: For optimum performance the following is recommended:
All welding seams must have a surface finish which ensures that the quality of the paintsystem will be maintained in all respects. Holes in welding seams, undercuts, etc.should be avoided. If found, they may necessitate extra stripe coating or filling (however,the classification societies' recommendations are to be followed).
All sharp edges to be broken or rounded depending on the actual conditions and thedesign lifetime. Laminations to be removed. However, rolled profiles, etc. from the steelmills normally have acceptably rounded edges.
All loose weld spatters to be removed.
Well adhering, scattered weld spatters are acceptable, but will need additional touch-up.If dense, they must be removed by grinding.
Requirements to the "surface quality" of welds according to WELD REPLICA NACE RP0178 minimum Grade E (NACE Standard RP0178-95).
Ballast tanks, Before blasting any deposits of grease or oil must be removed from the steel surfacesurface preparation: with a suitable detergent followed by fresh water hosing. Minor spots of oil/grease may
be cleaned with thinner and clean rags - avoid smearing out the contamination. Possiblealkali weld deposits, chemicals used for testing of welds, soap residues from thepressure testing must be removed by fresh water hosing.
Newbuilding/new steelwork: To obtain full performance of the ballast tank coating,welds, burns, damaged and rusty shopprimer must be abrasive blast cleaned to Sa 2½.Minor areas mechanically cleaned to St 3.
If welds have previously been coated with a (shop)primer just after welding this(shop)primer must be removed by abrasive blasting (sweeping) in order to obtainoptimum performance.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MULTI-STRENGTH 45751/45753
Intact shopprimer:Zinc salted surfaces, deposits of black iron oxides of plasma cutting and similar foreignmatters to be removed by light abrasive sweep blasting. Chalk markings and platemarking of a non-compatible nature to be removed as well.
The shopprimer must have been checked randomly for excessive film thicknesses andareas detected to have film thicknesses above approx 40 micron/1.6 mils (as measureddirectly on the shopprimed surface with equipment calibrated on smooth steel) are to besweep blasted in order to remove most of the shopprimer.
Spot-checking for possible salt contamination of the surface to be executed before andafter abrasive sweep blasting.
When blasting, the importance of working systematically must be stressed. Poorlyblasted areas covered with dust are very difficult to locate during the blast inspectionmade after the rough cleaning.
The surface profile to be equivalent to Rugotest No. 3, BN9-BN10 or Keane-TatorComparator, 3.0 G/S. According to ISO 8503-1 the grade will be MEDIUM (G).
Note: If any doubt exists about the quality of the primary surface preparation (beforeshoppriming), the substrate must be re-blasted in situ as defined above.
Block assembly zones: Overlap zones must be treated with great care. Damage causedby possible over-blasting must be avoided, paint edges must be feathered andconsecutive layers of paint coatings given greater and greater overlaps - old layers beingroughened corresponding to these overlaps (when sandpapering, use free-cut paper,grain size 80).
Furthermore, these areas may be either masked off with tape - to keep them as narrowas possible - or left with a thin zinc epoxy primer coat applied on these areas aftersecondary surface preparation at blockstage.
Secondary surface preparation of block assembly zones are preferably to be abrasivespot-blasted. However, mechanical cleaning to St 3 may be acceptable if zones arenarrow and an extra coat of HEMPADUR MULTI-STRENGTH 45751/45753 dilutedapprox. 10-15% is applied to these areas as the first coat. The procedure of maskingoff with tape or using the zinc epoxy primer as described above may advantageously beused in case of mechanical cleaning.
Stainless Steel: (Ballast tanks of chemical carriers) to be abrasive blast cleaned to auniform, sharp, dense, profile (Rugotest No. 3, BN9, ISO Comparator Medium (G),Keane-Tator Comparator 2.0 G/S corresponding to Rz minimum 50 micron). Any salts,grease, oil etc. to be removed before abrasive blasting is commenced.
Refurbishment: It is recommended to carry out rough abrasive blast cleaning - or water jetting - tofacilitate visual inspection and any necessary repair of the existing steel work. In thecase of pit-corroded tank bottoms this rough blasting will also provide a better basis fora decision between welding of corroded pits or repair by filling.Corroded pits deeper than approx. 2 mm, but not repaired by welding, are recommendedto be filled with HEMPADUR EPOXY FILLER 35250 after blast priming has been carriedout.
At refurbishment, a main concern is the contamination from sea water (water-soluble,corrosive salts). The preventive method will be to include very thorough cleaning withplenty of fresh water, please see below.
The maximum allowable concentration of chlorides on steel surfaces immediatelybefore application is 7.0 microgrammes/cm² as detected by the "Bresle Method".
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
HEMPADUR MULTI-STRENGTH 45751/45753
In the case of contamination, cleaning procedures must be repeated and/or improved.Especially pit-corroded steel will need special attention and the only possible way toremove contamination from the pits may often be to carry out very thorough cleaningwith fresh water after abrasive blast cleaning. After repeated control and drying, theentire surface will need abrasive blast cleaning to obtain the specified degree ofcleaning. Alternatively, the pit-corroded areas are cleaned by water jetting, any surplus ofwater is mopped up or removed by vacuum cleaning, allow to dry.
Note: Actual type of steel work and surface preparation is dependent on factors sucha shipyard technology, contractual specification, required lifetime, etc. Reference isalso made to HEMPEL’s Technical Standard for Ballast Tank Coating Work.
Application equipment: HEMPADUR MULTI-STRENGTH 45751/45753, being a high viscosity material, mayrequire special measures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min 45:1Pump output: 12 litres/minute (theoretical)Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Filter: 60 mesh
Regular surfaces: Ballast tanks Exterior hull and similar large regular areasNozzle size: .021"-.023” .023”-.027”Fan angle: 60-80° 60°-80°
Complicated surfaces:Nozzle size: .019"Fan angle: 40°.
After finishing the application, clean the equipment immediately with HEMPEL’S TOOLCLEANER 99610.
Note: Increasing spray hose diameter may ease paint flow thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approximately 5% THINNER 08450 may be added, but thinning mustbe done with care as the maximum obtainable film thickness is reduced significantly byoverthinning. Airless spray data are indicative and subject to adjustment.
Application: Film-build/continuity: It is especially important that a continuous, pinhole-free paint filmis obtained at application of each spray applied coat. An application technique which willensure good film formation on all surfaces must be adopted. It is very important to usenozzles of the correct size, not too big, and to have a proper, uniform distance of thespray gun to the surface, 30-50 cm should be aimed at. Furthermore, great care mustbe taken to cover edges, openings, rear sides of stiffeners etc. Thus, on these areas astripecoat will usually be necessary. To obtain good and steady atomising, the viscosityof the paint must be suitable and the spray equipment must be sufficient in outputpressure and capacity. At high working temperatures, use of extra thinner may benecessary to avoid dust-spray.The paint layer must be applied homogeneously and as close to the specification aspossible. Avoid exaggerated film thickness.Saggings/“pools” of paint in corners are to be remedied to avoid later crackings and asa general rule highest acceptable dry film thickness will be 3 times the specified filmthickness or 1000 micron.The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
Stripe coating: may either be applied by airless spray, (relatively small, narrow-anglednozzles) or by hand-tools. Apply the stripe coat as a uniform, regular film withoutexcessive brush or roller marks in order to avoid cratering by entrapped air.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MULTI-STRENGTH 45751/45753
Pot life/mixing/ When measured under standard conditions the pot life is 2 hours at 15°C/59°F and 1induction time: hours at 20°C/68°F. However, for a 20 litres/5 US gallons mix, the heat developed by(both curing agents): the chemical reaction between BASE and CURING AGENT may make the corresponding
practical pot life shorter.
a. Mix the entire content of corresponding base and curing agent packings. If it isnecessary to mix smaller portions, this must be done properly by either weighingbase and curing agent in the prescribed weight ratio: 143 parts by weight of baseand 20 parts by weight of curing agent or by volume: 4.0 parts by volume base and1.0 parts by volume curing agent.
b. Stir the mixed paint thoroughly by means of a clean mechanical mixer until ahomogeneous mixture is obtained.
c. Use all mixed paint before the pot life is exceeded. The pot life depends on thetemperature of the paint as shown in table below (valid for a 20 litres can):
(1/4 hour)½ hour1 hour2 hoursPot life
30°C/86°F 2)25°C/77°F20°C/68°F15°C/59°F 1)Temperature of mixed paint
1) At 15°C/59°F and below, the viscosity will be too high for airless spray application.2) Temperatures above 30°C/86°F should be avoided.
Induction time:At Steel temperatures below 5°C/41°F the paint may advantageously be prereacted 10minutes before spray application (longer prereaction time at lower steel temperatures).
When two-component spray equipment is used, heating may be relevant to obtain aproper spray fan and a uniform and smooth paint film. This can either be done bypreheating the two-component paint or by using a flow-heater on the pressure side. Asan indication, a paint temperature of approx 40°C/104°F will be relevant, but has to beadjusted according to the actual conditions.
Physical data (HEMPADUR MULTI-STRENGTH 45751 in a dry film thickness of 200 micron/8 mils):versus temperature:
2½ day5 days13 daysInitial curing*
4 hours3½ day
8 hours7 days
20 hours18 days
Drying timeCuring time*
30°C/86°F20°C/68°F10°C/50°FSurfacee temperature
(HEMPADUR MULTI-STRENGTH 45753 in a dry film thickness of 200 micron/8 mils):
2½ day23 days45 daysInitial curing*
4 hours3½ day
23 hours32 days
45 hours63 days
Drying timeCuring time*
10°C/50°F0°C/32°F-10°C/14°FSurfacee temperature
* Filling of ballasttanks/exposure to water: ask for special instructions.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: April 2002 - 4575112340CO002/4575312340C0001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4575112340CO002/4575312340C0001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR MIO 457HSCURING AGENT 95881
Description: HEMPADUR M.I.O. 457HS is a two-component polyamide adduct cured, high solids,high build epoxy paint. It forms a hard and tough coating and has good wettingproperties. Low temperature curing.
Recommended use: As a selfprimed paint system or as an intermediate or finishing coat in epoxy systemsin medium to severely corrosive atmospheric environment and where a high solid,M.I.O. content is required.As a finishing coat where the usual outdoor cosmetic appearance of epoxy paints isacceptable.May be used directly on cured zinc silicate (GALVOSIL products) or spray- metallizedsurfaces to minimize popping.
Service temperatures: Maximum, dry: 120°C/248°F
Availability: Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version, mixed product: 457HSColours/Shade nos: Grey/12430Finish: Semi--glossVolume solids, %: 80 ± 1Theoretical spreading rate: 5.3 m²/litre - 150 micron
214 sq.ft./US gallon - 6 milsFlash point: 28°C/82°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 3 (approx) hours at 30°C/86°FFully cured: 5 days at 30°C/86°FV.O.C.: 215 g/litre - 1.8 lbs/US gallon
*(Other shades according to assortment list)
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: Base 457H9 : Curing agent 95881
3 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max. vol.): THINNER 08450 (See REMARKS overleaf)Pot life: 1½ hour (30°C/86°F) (Airless spray)
2 hours (30°C/86°F) (Brush)(See separate APPLICATION INSTRUCTIONS)
Nozzle orifice: .017"-.023"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment) Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or HEMPEL'S THINNER 08450Indicated film thickness, dry: 150 micron/6 mils (see REMARKS overleaf)Indicated film thickness, wet: 200 micron/8 milsRecoat interval, min: As per separate APPLICATION INSTRUCTIONSRecoat interval, max: As per separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
HEMPADUR M.I.O. 457HS
SURFACE New steel: When used as an intermediate or finishing coat please refer to the data sheet for thePREPARATION: preceding HEMPADUR primer. When used as a primer please refer to the specification. For "heavy
duty" purposes, abrasive blasting to minimum Sa 2½ is recommended.Zinc silicate painted or spray-metallized surfaces: Remove oil and grease, etc. with suitabledetergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Zinc salts(white rust) must be removed by high pressure hosing combined with rubbing with a stiff nylonbrush if necessary. It is recommended to recoat spray-metallized surfaces as soon as possible toavoid possible contamination.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment or acidetching. Seal surface with suitable sealer, eg HEMPADUR SEALER 05970 (furthermore, please seeProduct Data Sheet for 05970).Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to St 3 (spot-repairs) or by abrasive blasting to min. Sa 2, preferably to Sa 2½.Improved surface preparation will improve the performance ofHEMPADUR M.I.O. 457HS. As analternative to dry cleaning, water jetting to min. WJ-2 (NACE No. 5/SSPC-SP 12), may be used. Aflash-rust degree of maximum FR-2 (Hempel standard) is acceptable before application. Featheredges to sound and intact paint. Dust off residues.On pit-corroded surfaces, excessive amounts of salt residues may call for water jetting, wetabrasive blasting, alternatively dry abrasive blasting, high pressure fresh water hosing, drying, andfinally, dry abrasive blasting again.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Use only when application and curing can proceed at temperatures above
10°C/50°F. The temperature of the paint itself should be 15°C/59°F or above, but advantageouslybelow approximately 30°C/86°F to secure proper application properties. Optimal sprayingproperties are obtained at a paint temperature of 18-22°C/64-72°F. In warmer climates, the paintshould be stored in a cool place and the paint temperature should preferably be kept below30°C/86°F. In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT:SUBSEQUENT None or according to specification.COAT:
REMARKS:Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.Film thicknesses/ May be specified in another film thickness than indicated depending on purpose and area of use.thinning: This will alter spreading rate and may influence drying time and recoating interval. Normal range dry
is 125-200 micron/5-8 mils. May be specified in lower film thickness for which purpose additionalthinning is required, please see separate APPLICATION INSTRUCTIONS. Avoid application ofexcessive film thicknesses.
Application onto zinc It is recommended to apply HEMPADUR M.I.O. 457HS by using a "mist-coat" procedure providedsilicate or spray- the paint temperature is approximately above 20°C/68°F: A thin, undiluted coat is applied (themetallized surfaces: mist coat) and after a few minutes, a second coat is applied in the full specified film thickness. If(thinning): the paint temperature is below 20°C/68°F, thinning (max 15%) may be required.
Note: HEMPADUR M.I.O. 457HS is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR MIO 457HSCURING AGENT 95881
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR MIO 457HS.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning is recommended.However, HEMPADUR MIO 457HS may be applied to rusty steel surfaces where higherperformance is required than obtainable with conventional coatings but where onlymechanical cleaning and dust removal can be carried out (beside the removal of saltsand of oily contaminants).
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
NEW STEEL:
When used as intermediate and/or finishing coat, surface preparation according toProduct Data Sheet for the preceding primer coat (HEMPADUR primers). When used aselfpriming coat, surface preparation according to specification.
When applied to GALVOSILS:
HEMPADUR MIO 457HS can be applied when the GALVOSIL is cured. ConsultAPPLICATION INSTRUCTIONS for the relevant GALVOSIL. Remove oil and grease etc. withsuitable detergent. Remove salt and other contaminants by high pressure fresh watercleaning. After exposure to high humidity, zinc salts, "white rust", must be removedcarefully by high pressure fresh water cleaning, if necessary combined with scrubbingwith stiff nylon brushes.
REPAIR AND MAINTENANCE:
Spot-repairs:
Clean damaged areas thoroughly by power tool cleaning to St 3 or by abrasive blastingto minimum Sa 2, preferably Sa 2½. Improved surface preparation will improve theperformance of HEMPADUR MIO 457HS. As an alternative to dry cleaning, water jettingto minimum WJ-2 (NACE No. 5/SSPC-SP12), may be used. A flash-rust degree ofmaximum FR-2 (Hempel standard) is acceptable before application. Feather edges tosound and intact areas. Brush off loose material. Touch up to full film thickness.
Compatibility: HEMPADUR MIO 457HS may be used in connection with other genericpaint systems than epoxy and polyurethanes.
It is recommended to make a test patch. In any case it is a must that the old paintsystem is tightly adhering and is properly prepared before the touch-up is performed.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 4
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
HEMPADUR MIO 457HS
Full coating:
Compatibility with old system: In general full compatibility can be expected with oldepoxy systems. A test patch should always be performed before fullcoating is decided. Ifthe old epoxy is not weathered/chalked or if it is topcoated with polyurethane, it isrecommended to roughen the surface before recoating. Furthermore, very thoroughcleaning is a must. Any dirt, chalked surface material, oil and grease should be removedwith suitable detergent followed by high pressure fresh water hosing of the entiresurface.
Removal of old system: Full coating after complete mechanical removal of an old paintsystem is possible too. Yet, it must be considered that mechanical cleaning by discgrinding or by rotating wire brushing may produce a very smooth surface giving reason toreduced adhesive forces.
Note: Another risk is left over of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a continuous oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paintmaterial may flake off.
Note: On old steel surfaces having been exposed to salt water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
Application equipment: HEMPADUR MIO 457HS being a high solids and a relatively high viscosity material, mayrequire special measures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min. 45:1Pump output: 12 litres/minute (theoretical)
Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .021" through .023"Fan angle: 60°.
Complicated surfaces (and touch up):Nozzle size: .017" through .021"Fan angle: 40°.
After finishing the application, clean the equipment immediately with THINNER 08450 orHEMPEL’S TOOL CLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approx. 5% THINNER 08450 may be added, but thinning must bedone with care as the anti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Induction time: In case of a paint temperature at 15°C/59°F or below, it is an advantage to allow thetwo components to prereact before application. This is especially relevant in the case ofsubstrate temperatures below 15°C/59°F.
In case of a paint temperature at 15°C/59°F, an induction time of 15 minutes isrecommended. In case of a paint temperature at 10°C/50°F, an induction time of 25minutes is recommended. In order to obtain proper application properties, the painttemperature should preferably never be below 10°C/50°F.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 4
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MIO 457HS
Application: Film-build/continuity: With this paintmaterial applied in one/few coat(s) it is of specialimportance that a continuous, pinhole-free paint film is obtained at application of eachcoat. An application technique which will ensure good film formation on all surfacesmust be adopted. It is very important to use nozzles of the correct size, not too big, andto have a proper, uniform distance of the spray gun to the surface, 30-50 cm should beaimed at. Furthermore, great care must be taken to cover edges, openings, rear sides ofstiffeners etc. Thus, on these areas application of a stripecoat will therefore be goodpainting practice. To obtain good and steady atomizing, the viscosity of the paint mustbe suitable and the spray equipment must be sufficient in output pressure and capacity.At high working temperatures, use of extra thinner may be necessary to avoiddust-spray.
The paint layer must be applied homogeneously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks and solventretention. The paint consumption must be controlled.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
On poorly prepared surfaces it is always recommended to apply the first coat by brush.Extra thinning will facilitate the penetration of the paint material, but will also require anextra layer to be applied.
Wet/dry film thickness: Please note that the thixotropic nature of HEMPADUR MIO 457HS may give a rather"wavy" surface of the paint just after application. This smoothens at drying, but canmake it necessary to let the wet film readings be of a higher value than indicated. Inmany cases the wet film thickness, reading should be 25-50 micron/1-2 mils higherthan calculated. As the wavy surface becomes more smooth during drying these extrawet film thickness readings will not cause a higher paint consumption than otherwisestipulated.
Film thickness/thinning: HEMPADUR MIO 457HS is normally specified in 125-200 micron/5-8 mils. Depending onambient conditions, usually maximum 5% thinning with THINNER 08450 is relevant,however, increasing at high temperatures. May be specified down to 75 micron/3 mils.To obtain optimum film formation in film thicknesses lower than 125 micron/5 mils dryfilm thickness additional thinning with 5-10% THINNER 08450 is recommended.
Pot life: When measured under standard conditions the pot life is 1½ hours at 30°C/86°F forHEMPADUR MIO 457HS. However, for a 20 litres/5 US gallons mix, and used underwarm climate conditions, the heat developed by the chemical reaction between BASEand CURING AGENT may make the corresponding practical pot life shorter.Therefore: At high temperatures, use the paint immediately after mixing irrespective ofequipment.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Attached: Tables of "physical data versus temperature"
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 4
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPADUR MIO 457HS
Physical data Drying time and recoating interval vary with film thickness, temperature and laterversus temperature: exposure conditions:
HEMPADUR MIO 457HS in a dry film thickness of 100-150 micron/4-6 mils:
3 hours4 hours
4 hours5 hours
5 hours7 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR, HEMPATHANE and HEMPATEX qualities
MINIMUM recoating interval related to later conditions of exposure:
2 hours3 days
3 hours5 days
4 hours7 days
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
* 1) Avoid sudden drops in (substrate) temperatures during drying/initial curing.2) If faster handling is required at lower temperatures, HEMPADUR 45143 may be used.
HEMPADUR MIO 457HS in a dry film thickness of 200 micron/8 mils:
4 hours6 hours
5 hours8 hours
7 hours10 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR, HEMPATHANE and HEMPATEX qualities
MINIMUM recoating interval related to later conditions of exposure:
4 hours3 days
5 hours5 days
6 hours7 days
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
MAXIMUM recoating intervals of HEMPADUR MIO 457HS (independent on dry filmthickness):
6 hours9 hours12 hoursAtmospheric
Interval for recoating with HEMPATEX qualities
7 days1 day
14 days2 days
21 days3 days
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMPATHANE topcoats
NoneNone
NoneNone
NoneNone
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR qualities
MAXIMUM recoating interval related to later conditions of exposure:
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
°Depending on actual local conditions, extended maximum recoating intervals may apply. Please contact HEMPEL forfurther advice.
Besides the notes stated under the tables for minimum recoating intervals, the followingapplies:
A completely clean surface is mandatory to ensure intercoat adhesion, especially inthecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.
Any degraded surface layer, as a result of a long exposure period, must be removedas well. Water jetting may be relevant to remove any degraded surface layer and mayalso replace the above-mentioned cleaning methods when properly executed. ConsultHEMPEL for specific advice if in doubt.
To check whether the quality of the surface cleaning is adequate, a test patch may berelevant.
In case of recoating with HEMPATHANE, a prolonged maximum recoating intervaldepends on a very clean surface as stated above. If such cleaning is difficult to carryout, it should be observed that a thin, fresh coat of HEMPADUR MIO 457HS will providethe best possible adhesion to the old surface.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 4
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 457HS12430
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MASTIC 45880/HEMPADUR®MASTIC 45881
High temperatures: 45881 with CURING AGENT 95881Low to medium temperatures: 45880 with CURING AGENT 95880
Description: HEMPADUR MASTIC 45880/45881 is a two-component polyamide adduct cured, highsolids, high build epoxy paint. It forms a hard and tough coating and has good wettingproperties. Low temperature curing.
Recommended use: As a selfprimed paint system or as an intermediate or finishing coat in epoxy systemsin medium to severely corrosive atmospheric environment and where a high solidcontent is required.The MIO (micaceous iron oxide) pigment version may be specified where extendedrecoating properties for polyurethane topcoats are requested (typically travel coating).As a topcoat where the usual outdoor cosmetic appearance of epoxy paints isacceptable.May be used directly on cured zinc silicate (GALVOSIL products) or spray-metallizedsurfaces to minimize popping.
Service temperatures: Maximum, dry: 120°C/248°F
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health,Great Britain.Complies with Section 175.300 of the Code of Federal Regulations in respect ofcarriage of dry foodstuffs (FDA) in spaces with an internal surface area larger than 1000m²/10,750 sq.ft.HEMPADUR MASTIC 45881 is in accordance with Aramco’s specification APCS 26 and26T.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Version, mixed product: 45880 45881Colours/Shade nos: Grey/12170* Grey/12170*Finish: Semi--gloss Semi--glossVolume solids, %: 77 ± 1 77 ± 1Theoretical spreading rate: 5.1 m²/litre - 150 micron 5.1 m²/litre - 150 micron
206 sq.ft./US gallon - 6 mils 206 sq.ft./US gallon - 6 milsFlash point: 35°C/95°F 35°C/95°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallon 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 4 (approx) hours at 20°C/68°F 3 (approx) hours at 30°C/86°FFully cured: 7 days at 20°C/68°F 5 days at 30°C/86°FV.O.C.: 220 g/litre - 1.8 lbs/US gallon 220 g/litre - 1.8 lbs/US gallon
*Other shades including a MIO version, colour no. 12430, according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:45880 45881
Mixing ratio: Base 45889 : Curing agent 95880 Base 45889 : Curing agent 958813 : 1 by volume 3 : 1 by volume
Application method: Airless spray Brush (touch up) Airless spray Brush (touch up)Thinner (max. Vol.): Depending on purpose usually less than 5% THINNER 08450 (See REMARKS overleaf)Pot life: 1 hour (20°C/68°F) (Airless spray) 1½ hour (30°C/86°F) (Airless spray)
2 hours (20°C/68°F) (Brush) 2 hours (30°C/86°F) (Brush)(See separate APPLICATION INSTRUCTIONS) (See separate APPLICATION INSTRUCTIONS)
Nozzle orifice: .017"-.023" (See separate APPLICATION INSTRUCTIONS)Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or HEMPEL'S THINNER 08450Indicated film thickness, dry: 150 micron/6 mils (see REMARKS overleaf)Indicated film thickness, wet: 200 micron/8 milsRecoat interval, min: According to separate APPLICATION INSTRUCTIONSRecoat interval, max: According to separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170CO006
HEMPADUR MASTIC 45880/45881
SURFACE New steel: When used as an intermediate or finishing coat please refer to the data sheet for thePREPARATION: preceding GALVOSIL or HEMPADUR primer. When used as a primer please refer to the
specification.Zinc silicate painted or spray-metallized surfaces: Remove oil and grease, etc. with suitabledetergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Zinc salts(white rust) must be removed by high pressure hosing combined with rubbing with a stiff nylonbrush if necessary. It is recommended to recoat spray-metallized surfaces as soon as possible toavoid possible contamination.Concrete: Remove slip agent and other possible contaminants by emulsion washing followed byhigh pressure hosing with fresh water. Remove scum layer and loose matter to a hard, rough anduniform surface, preferably by abrasive blasting, possibly by other mechanical treatment or acidetching. Seal surface with suitable sealer, eg HEMPADUR SEALER 05970 (furthermore, please seeProduct Data Sheet for 05970).Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to minimum St 2 (spot-repairs) or by abrasive blasting to min. Sa 2, preferablyto Sa 2½. Improved surface preparation will improve the performance of HEMPADUR MASTIC45880/45881. As an alternative to dry cleaning, water jetting to min. WJ-3 (NACE No. 5/SSPC-SP12), may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptable beforeapplication. Feather edges to sound and intact paint. Dust off residues.On pit-corroded surfaces, excessive amounts of salt residues may call for water jetting, wetabrasive blasting, alternatively dry abrasive blasting, high pressure fresh water hosing, drying, andfinally, dry abrasive blasting again.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Use only when application and curing can proceed at temperatures above
-10°C/14°F for HEMPADUR MASTIC 45880 and above approx 25°C/77°F for HEMPADUR MASTIC45881. The temperature of the paint itself should be 15°C/59°F or above, but advantageouslybelow approximately 30°C/86°F to secure proper application properties. Optimal sprayingproperties are obtained at a paint temperature of 18-22°C/64-72°F. In warmer climates, the paintshould be stored in a cool place and the paint temperature should preferably be kept below30°C/86°F. In confined spaces provide adequate ventilation during application and drying. In caseswhere faster drying at very low temperatures is required, HEMPADUR MASTIC 45880 mayadvantageously be replaced by HEMPADUR 45143. Please also see separate APPLICATION
INSTRUCTIONS.PRECEDING andSUBSEQUENT COAT: None or according to specification.REMARKS: Certificates have been issued under the former quality number 4588.Colours/Colour- Certain lead-free red and yellow colours may discolour when exposed to chlorine- containingstability: atmosphere.
Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.Like other epoxy coatings in white/whitish colour a yellowing may take place in cases of applicationunder unfavourable weather conditions, especially sudden drops in temperature during drying andintial cure and/or lack of ventilation.
Weathering/service The natural tendency of epoxy coatings to chalk in outdoor exposure and to become more sensitivetemperatures: to mechanical damage and chemical exposure at elevated temperatures is also reflected in this
product.Film thicknesses/ May be specified in another film thickness than indicated depending on purpose and area of use.thinning: This will alter spreading rate and may influence drying time and recoating interval. Normal range dry
is 125-200 micron/5-8 mils. May be specified in lower film thickness for which purpose additionalthinning is required, please see separate APPLICATION INSTRUCTIONS. Avoid application ofexcessive film thicknesses.
Application onto zinc It is recommended to apply HEMPADUR MASTIC 45880/45881 by using a "mist-coat" proceduresilicate or spray- provided the paint temperature is approximately above 20°C/68°F: A thin, undiluted coat is appliedmetallized surfaces (the mist coat) and after a few minutes, a second coat is applied in the full specified film(thinning): thickness. If the paint temperature is below 20°C/68°F, thinning (max 15%) may be required.Note: HEMPADUR MASTIC 45880/45881 is for professional use only.
Issued: December 2001 - 4588012170CO009/ 4588112170CO006 - IndustryHEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPADUR®MASTIC 45880/HEMPADUR®MASTIC 45881
High temperatures: 45881 with CURING AGENT 95881Low to medium temperatures: 45880 with CURING AGENT 95880
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR MASTIC 45880/45881.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning is recommended.However, HEMPADUR MASTIC 45880/45881 has “surface tolerant” properties andoffers higher performance than many other coatings when applied to surfacesmechanically cleaned only (salts, oil, grease etc. shall always be removed).
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
NEW STEEL:
When used as intermediate and/or finishing coat, surface preparation according toProduct Data Sheet for the preceding primer coat (HEMPADUR primers). When used asa selfpriming coat, surface preparation according to specification.
When applied to GALVOSILS:
HEMPADUR MASTIC 45880/45881 can be applied when the GALVOSIL is cured.Consult APPLICATION INSTRUCTIONS for the relevant GALVOSIL. Remove oil and greaseetc. with suitable detergent. Remove salt and other contaminants by high pressurefresh water cleaning. After exposure to high humidity, zinc salts, "white rust", must beremoved carefully by high pressure fresh water cleaning, if necessary combined withscrubbing with stiff nylon brushes.
REPAIR AND MAINTENANCE:
Spot-repairs:
Clean damaged areas thoroughly by power tool cleaning to minimum St 2 (spot-repairs)or by abrasive blasting to minimum Sa 2, preferably Sa 2½. Improved surfacepreparation will improve the performance of HEMPADUR MASTIC 45880/45881. As analternative to dry cleaning, water jetting to minimum WJ-2 (NACE No. 5/SSPC-SP12),may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptablebefore application. Feather edges to sound and intact areas. Brush off loose material.Touch up to full film thickness.
Compatibility: HEMPADUR MASTIC 45880/45881 may be used in connection withother generic paint systems than epoxy and polyurethanes.
It is recommended to make a test patch. In any case it is a must that the old paintsystem is tightly adhering and is properly prepared before the touch-up is performed.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
HEMPADUR MASTIC 45880/45881
Full coating:
Compatibility with old system: In general full compatibility can be expected with oldepoxy systems. A test patch should always be performed before fullcoating is decided.If the old epoxy is not weathered/chalked or if it is topcoated with polyurethane, it isrecommended to roughen the surface before recoating. Furthermore, very thoroughcleaning is a must. Any dirt, chalked surface material, oil and grease should beremoved with suitable detergent followed by high pressure fresh water hosing of theentire surface.
Removal of old system: Full coating after complete mechanical removal of an old paintsystem is possible too. Yet, it must be considered that mechanical cleaning by discgrinding or by rotating wire brushing may produce a very smooth surface giving reasonto reduced adhesive forces.
Note: Another risk is remains of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a further oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paintmaterial may flake off.
Note: On old steel surfaces having been exposed to salty water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
Application equipment: HEMPADUR MASTIC 45880/45881 being a high solids and a relatively high viscositymaterial, may require special measures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min. 45:1Pump output: 12 litres/minute (theoretical)
Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .021" through .023"Fan angle: 60°.
Complicated surfaces (and touch up):Nozzle size: .017" through .021"Fan angle: 40°.
After finishing the application, clean the equipment immediately with THINNER 08450or HEMPEL’S TOOL CLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approx. 5% THINNER 08450 may be added, but thinning must bedone with care as the anti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Induction time: Should the paint temperature as an exception be 15°C/59°F or below, it is anadvantage to allow the two components to prereact before application. This isespecially relevant in the case of substrate temperatures also being below 15°C/59°F.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MASTIC 45880/45881
In case of a paint temperature at 15°C/59°F, an induction time of 15 minutes isrecommended. In case of a paint temperature at 10°C/50°F, an induction time of 25minutes is recommended. In order to obtain proper application properties, the painttemperature should preferably never be below 10°C/50°F.
Application: Film-build/continuity: With this paintmaterial applied in one/few coat(s) it is of specialimportance that a continuous, pinhole-free paint film is obtained at application of eachcoat. An application technique which will ensure good film formation on all surfacesmust be adopted. It is very important to use nozzles of the correct size, not too big, andto have a proper, uniform distance of the spray gun to the surface, 30-50 cm should beaimed at. Furthermore, great care must be taken to cover edges, openings, rear sidesof stiffeners etc. Thus, on these areas application of a stripecoat will therefore be goodpainting practice. To obtain good and steady atomizing, the viscosity of the paint mustbe suitable and the spray equipment must be sufficient in output pressure andcapacity. At high working temperatures, use of extra thinner may be necessary to avoiddust-spray.
The paint layer must be applied homogeneously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks andsolvent retention. The paint consumption must be controlled.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
On poorly prepared surfaces it is always recommended to apply the first coat by brush.Extra thinning will facilitate the penetration of the paint material, but will also require anextra layer to be applied.
Wet/dry film thickness: Please note that the thixotropic nature of HEMPADUR MASTIC 45880/45881 may givea rather "wavy" surface of the paint just after application. This smoothens at drying, butcan make it necessary to let the wet film readings be of a higher value than indicated.In many cases the wet film thickness, reading should be 25-50 micron/1-2 mils higherthan calculated. As the wavy surface becomes more smooth during drying these extrawet film thickness readings will not cause a higher paint consumption than otherwisestipulated.
Film thickness/thinning: HEMPADUR MASTIC 45880/45881 is normally specified in 125-200 micron/5-8 mils.Depending on ambient conditions, usually maximum 5% thinning with THINNER 08450is relevant, however, increasing at high temperatures to ensure proper film formationand avoid dust spray. May be specified down to 75 micron/3 mils. To obtain optimumfilm formation in film thicknesses lower than 125 micron/5 mils dry film thicknessadditional thinning with 5-10% THINNER 08450 is recommended.
Pot life: When measured under standard conditions the pot life is 1 hour at 20°C/68°F forHEMPADUR MASTIC 45880 respectively 1½ hours at 30°C/86°F for HEMPADURMASTIC 45881. However, for a 20 litres/5 US gallons mix, and used under warmclimate conditions, the heat developed by the chemical reaction between BASE andCURING AGENT may make the corresponding practical pot life shorter.Therefore: At high temperatures, use the paint immediately after mixing irrespective ofequipment.
Attached: Tables of "physical data versus temperature"
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
HEMPADUR MASTIC 45880/45881
Physical data Drying time and recoating interval vary with film thickness, temperature and laterversus temperature: exposure conditions:
HEMPADUR MASTIC 45880 in a dry film thickness of 100-150 micron/4-6 mils:
4 hours5 hours
5 hours7 hours
12 hours18 hours
N/RN/R
N/RN/R
N/RN/R
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMUCRYL topcoats
4 hours5 hours12 hours30 hours4 days8 daysAtmospheric, medium or severe
Interval for recoating with HEMPATEX qualities
4 hours5 hours
5 hours7 hours
12 hours18 hours
30 hours42 hours
4 days6 days
8 days12 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR and HEMPATHANE qualities
MINIMUM recoating interval related to later conditions of exposure:
3 hours5 days
4 hours7 days
10 hours14 days
24 hours1 month
3 days2½ months
6 days5 months
Drying time (approx)Curing time (approx)
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°F-10°C/14°FSurface temperature:
Notes:• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that the
substrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used.• In case of low temperatures, it is recommended that HEMPADUR MASTIC 45880 has been given a proper
induction time before application. Under such conditions, consider paint temperature equal to substratetemperature and follow the rules given on page 2.
HEMPADUR MASTIC 45880 in a dry film thickness of 200 micron/8 mils:
5 hours8 hours
7 hours10 hours
18 hours25 hours
N/RN/R
N/RN/R
N/RN/R
Atmospheric, mediumAtmospheric, severe
MINIMUM Interval for recoating with HEMUCRYL topcoats
5 hours7 hours18 hours42 hours5 days10 daysAtmospheric, medium or severe
Interval for recoating with HEMPATEX qualities
5 hours8 hours
7 hours10 hours
18 hours25 hours
42 hours60 hours
5 days7 days
10 days14 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR and HEMPATHANE qualities
MINIMUM recoating interval related to later conditions of exposure:
4½ hours5 days
6 hours7 days
15 hours14 days
36 hours1 month
6 days2½ months
12 days5 months
Drying time (approx)Curing time (approx)
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°F-10°C/14°FSurface temperature:
Notes:• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that the
substrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used.• In case of low temperatures, it is recommended that HEMPADUR MASTIC 45880 has been given a proper
induction time before application. Under such conditions, consider paint temperature equal to substratetemperature and follow the rules given on page 2/3.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MASTIC 45880/45881
HEMPADUR MASTIC 45880 (independent on dry film thicknesses):
2 days1 day
3 days1½ days
6 days3 days
N/RN/R
N/RN/R
N/RN/R
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMUCRYL topcoats9 hours12 hours30 hours72 hours10 days20 days
Atmospheric,medium and severe
Interval for recoating with HEMPATEX qualities
14 days2 days
21 days3 days
4 weeks6 days
2 months14 days
3 months21 days
4 months4 weeks
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMPATHANE topcoats
NoneNone
NoneNone
NoneNone
NoneNone
NoneNone
NoneNone
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR qualitiesMAXIMUM recoating interval related to later conditions of exposure:
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°F-10°C/14°FSurface temperature:
HEMPADUR MASTIC 45881 in a dry film thickness of 100-150 micron/4-6 mils:
3 hours4 hours
4 hours5 hours
5 hours7 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR, HEMPATHANE, HEMPATEX and HEMUCRYL qualities
MINIMUM recoating interval related to later conditions of exposure:
2 hours3 days
3 hours5 days
4 hours7 days
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
* 1) Avoid sudden drops in (substrate) temperatures during drying/initial curing.2) If faster handling is required at lower temperatures, HEMPADUR 45143 may be used.
HEMPADUR MASTIC 45881 in a dry film thickness of 200 micron/8 mils:
4 hours6 hours
5 hours8 hours
7 hours10 hours
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR, HEMPATHANE, HEMPATEX and HEMUCRYL qualities
MINIMUM recoating interval related to later conditions of exposure:
4 hours3 days
5 hours5 days
6 hours7 days
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
HEMPADUR MASTIC 45881 (independent on dry film thickness):
1 day12 hours
2 days1 day
3 days1½ days
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMUCRYL topcoats
6 hours9 hours12 hoursAtmospheric
Interval for recoating with HEMPATEX qualities
7 days1 day
14 days2 days
21 days3 days
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMPATHANE topcoats
NoneNone
NoneNone
NoneNone
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPADUR qualities
MAXIMUM recoating interval related to later conditions of exposure:
40°C/104°F30°C/86°F20°C/68°FSurface temperature:
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
HEMPADUR MASTIC 45880/45881
Specific Notes for overcoating with HEMPATHANE TOPCOATS:
°i) Depending on actual local conditions, extended maximum recoating intervals mayapply. Please contact HEMPEL for further advice.
°ii) The MIO version, colour no. 12430, may provide extended recoating properties ifHEMPADUR MASTIC 45880/45881 in shade 12430 is applied in a film thicknessthat allows a MIO structure to develop. This is typically achieved in a dry filmthickness range of 50-100 micron/2-4 mils for which reason further thinning isrelevant. Reference is made to page 3.
Prior to application of HEMPATHANEs it is mandatory to clean the surface thoroughly toensure that any contamination in the rough MIO surface structure is removed.
To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant. However, such a test is not the final proof of long-term durability, but if theresult is doubtful, repeated cleaning will be relevant. A more safe solution could be torefresh the surface with a new thin (diluted) coat of HEMPADUR MASTIC 45880/45881.
The MIO concept is typically for use as a “travel coat” on industrial objects.
The dark shade of the MIO pigment should be taken into account when selectingsubsequent shades.
For typical marine coatings, prolonged overcoating intervals can be obtained by usingHEMPADUR 45080 as a preceding coat.
General notes on prolonged recoating intervals:
Besides the notes stated under the tables for minimum recoating intervals, thefollowing applies:
A completely clean surface is mandatory to ensure intercoat adhesion, especially inthecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.
Any degraded surface layer, as a result of a long exposure period, must be removedas well. Water jetting may be relevant to remove any degraded surface layer and mayalso replace the above-mentioned cleaning methods when properly executed. ConsultHEMPEL for specific advice if in doubt.
To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant, however, this test patch should not be a final proof of the durability of thecoating systems.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: June 2001 - 4588012170CO009/ 4588112170C0006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 6 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588012170CO009/ 4588112170C0006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MARINE MASTIC 45880CURING AGENT 95880
Description: HEMPADUR MARINE MASTIC 45880 is a two-component, high solids, high build epoxymastic paint. It is selfpriming, has good wetting properties, and forms a hard and toughcoating with good resistance to abrasion, spillage of mineral oils and to seawater. Lowtemperature curing.
Recommended use: As a high build primer, intermediate and/or finishing coat in epoxy systems according tospecification - typically when a low solvent content and high film thickness per coat arerequired.As a general performance coating for onboard touch-up, repair and maintenance workand full refurbishment of exterior hull, cargo holds (dry and wet), weather decks,topsides and superstructure when a need for few products outweighs more specialisedcoatings.As a finishing coat where the cosmetic appearance of epoxy paints is acceptable.
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health,Great Britain.Classified as class 1 material according to BS 476: Part 7: 1987 (fire testing).Complies with Section 175.300 of the Code of Federal Regulations in respect ofcarriage of dry foodstuffs (FDA) in spaces with an internal surface area larger than 1000m²/10,750 sq.ft.Has a German and Danish EC-type Examination Certificate.Service temperatures: Dry: Maximum 120°C/248°F (See REMARKS overleaf)
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11480 - Green/40640 - Red/50630*Finish: Semi--glossVolume solids, %: 77 ± 1Theoretical spreading rate: 3.9 m²/litre - 200 micron
154 sq.ft./US gallon - 8 milsFlash point: 35°C/95°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 6 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 220 g/litre - 1.8 lbs/US gallon
*Other shades may be available - subject to prior confirmation.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: Base 45889 : Curing agent 95880
3 : 1 by volumeApplication method: Airless spray Hand tools (touch up)Thinner (max. vol.): Depending on purpose usually less than 5% THINNER 08450 (See REMARKS overleaf)Pot life: 1 hour (20°C/68°F) (Airless spray)
2 hours (20°C/68°F) (Brush)(See separate APPLICATION INSTRUCTIONS)
Nozzle orifice: .017"-.023" (See separate APPLICATION INSTRUCTIONS)Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or HEMPEL'S THINNER 08450Indicated film thickness, dry: 200 micron/8 mils (see REMARKS overleaf)Indicated film thickness, wet: 275 micron/11 milsRecoat interval, min: According to separate APPLICATION INSTRUCTIONSRecoat interval, max: According to separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPADUR MARINE MASTIC 45880
SURFACE New steel: When used as an intermediate or finishing coat please refer to the data sheet for thePREPARATION: preceding GALVOSIL or HEMPADUR primer. When used as a primer please refer to the
specification.Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to minimum St 2 (spot repairs) or by abrasive blasting to min. Sa 2, preferablyto Sa 2½. Improved surface preparation will improve the performance of HEMPADUR MARINEMASTIC 45880. As an alternative to dry cleaning, water jetting to min. WJ-3 (NACE No. 5/SSPC-SP12), may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptable beforeapplication. Feather edges to sound and intact paint. Dust off residues.When used for immersion service, repair: As above, yet St 3 (spot repairs) or Sa 2½ or WJ-2 isrecommended.On pit-corroded surfaces, excessive amounts of salt residues may call for water jetting, wetabrasive blasting, alternatively dry abrasive blasting, high pressure fresh water hosing, drying, andfinally, dry abrasive blasting again.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Recommended lowest temperature is 0°C/32°F, yet curing takes place down to
-10°/14°F. The temperature of the paint itself should be 15°C/59°F or above, but belowapproximately 30°C/86°F to secure proper application properties. Optimal spraying properties areobtained at a paint temperature of 18-22°C/64-72°F. In warm climates, the paint should be storedin a cool place. In confined spaces provide adequate ventilation during application and drying.In cases where faster drying at very low temperatures is required, HEMPADUR MARINE MASTIC45880 may advantageously be replaced by HEMPADUR 45143. Please also see separateAPPLICATION INSTRUCTIONS.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None or according to specification.COAT:
REMARKS: Certificates have been issued under the former quality number 4588.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.
Film thicknesses/ May be specified in another film thickness than indicated depending on purpose and area of use.Thinning: This will alter spreading rate and may influence drying time and recoating interval. Normal range dry
is 125-200 micron/5-8 mils. Avoid application of excessive film thicknesses.May be specified in lower film thickness for which purpose additional thinning is required, pleasesee separate APPLICATION INSTRUCTIONS. If the paint temperature is below 20°C/68°F, extrathinning (max 15%) may also be required.
Two coats: The typical dry film thickness for a two coat system is 150 micron/6 mils each coat.Application onto zinc It is recommended to apply HEMPADUR MARINE MASTIC 45880 by using a "mist-coat" proceduresilicate or spray- provided the paint temperature is above approximately 20°C/68°F: A thin, undiluted coat ismetallized surfaces: applied (the mist coat) and after a few minutes, a second coat is applied in the full specified film
thickness.
Note: HEMPADUR MARINE MASTIC 45880 is for professional use only.
Issued: December 2001 - 4588011480CO006 - MarineHEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPADUR®MARINE MASTIC 45880CURING AGENT 95880
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR MARINE MASTIC 45880.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning is recommended.However, HEMPADUR MARINE MASTIC 45880 has “surface tolerant” properties andoffers higher performance than many other coatings when applied to surfacesmechanically cleaned only (salts, oil, grease etc. shall always be removed).
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
REPAIR AND MAINTENANCE:
When used for atmospheric exposure:
Spot-repairs:Clean damaged areas thoroughly by power tool cleaning to minimum St 2 (spot-repairs)or by abrasive blasting to minimum Sa 2, preferably Sa 2½. Improved surfacepreparation will improve the performance of HEMPADUR MARINE MASTIC 45880. As analternative to dry cleaning, water jetting to minimum WJ-3 (NACE No. 5/SSPC-SP12),may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptablebefore application. Feather edges to sound and intact areas. Brush off loose material.Touch up to full film thickness.
Compatibility: HEMPADUR MARINE MASTIC 45880 may be used in connection withother generic paint systems than epoxy and polyurethanes.It is recommended to make a test patch. In any case it is a must that the old paintsystem is tightly adhering and is properly prepared before the touch-up is performed.
Full coating:Compatibility with old system: In general full compatibility can be expected with oldepoxy systems. A test patch should always be performed before fullcoating is decided. Ifthe old epoxy is not weathered/chalked or if it is top coated with polyurethane, it isrecommended to roughen the surface before recoating. Furthermore, very thoroughcleaning is a must. Any dirt, chalked surface material, oil and grease should be removedwith suitable detergent followed by high pressure fresh water cleaning of the entiresurface.
Removal of old system: Full coating after complete mechanical removal of an old paintsystem is possible too. Yet, it must be considered that mechanical cleaning by discgrinding or by rotating wire brushing may produce a very smooth surface giving reason toreduced adhesive forces.
Note: Another risk is remains of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a further oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paint material may flake off.
When used for immersion service, repair:Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughlyby power tool cleaning to St 3 (minor areas) or by abrasive blasting to min Sa 2,preferably Sa 2½. Improved surface preparation will improve the performance ofHEMPADUR MARINE MASTIC 45880. As an alternative to dry cleaning, water jetting tominimum WJ-2 (NACE No. 5/SSPC-SP 12), may be used. A flash rust degree ofmaximum FR-2 preferably FR-1 (HEMPEL standard) is acceptable before application.Feather edges to sound intact areas. Dust off residues. Touch up to full film thickness.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPADUR MARINE MASTIC 45880
Note: On old steel surfaces having been exposed to sea water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
NEW STEEL:
When used as intermediate and/or finishing coat, surface preparation according toProduct Data Sheet for the preceding primer coat (HEMPADUR primers). When used as aself priming coat, surface preparation according to specification.
Application equipment: HEMPADUR MARINE MASTIC 45880 being a high solids and a relatively high viscositymaterial, may require special measures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min. 45:1Pump output: 12 litres/minute (theoretical)
Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .021" through .023"Fan angle: 60°.
Complicated surfaces (and touch up):Nozzle size: .017" through .021"Fan angle: 40°.
After finishing the application, clean the equipment immediately with THINNER 08450 orHEMPEL’S TOOL CLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approximately 5% THINNER 08450 may be added, but thinning mustbe done with care as the anti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Induction time: In case of a paint temperature at 15°C/59°F or below, it is an advantage to allow thetwo components to prereact before application. This is especially relevant in the case ofsubstrate temperatures also being below 15°C/59°F.
In case of a paint temperature at 15°C/59°F, an induction time of 15 minutes isrecommended. In case of a paint temperature at 10°C/50°F, an induction time of 25minutes is recommended. In order to obtain proper application properties, the painttemperature should preferably never be below 10°C/50°F.
Application Film-build/continuity: With this paint material applied in one/few coat(s) it is of speciallarger surfaces: importance that a continuous, pinhole-free paint film is obtained at application of each
spray applied coat. An application technique which will ensure good film formation on allsurfaces must be adopted. It is very important to use nozzles of the correct size, not toobig, and to have a proper, uniform distance of the spray gun to the surface, 30-50 cmshould be aimed at. Furthermore, great care must be taken to cover edges, openings,rear sides of stiffeners etc. Thus, on these areas application of a stripe coat willtherefore be good painting practice. To obtain good and steady atomizing, the viscosityof the paint must be suitable and the spray equipment must be sufficient in outputpressure and capacity. At high working temperatures, use of extra thinner may benecessary to avoid dust-spray.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MARINE MASTIC 45880
The paint layer must be applied homogeneously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks and solventretention. The paint consumption must be controlled.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
At application with hand tools, brush, but especially by roller the natural tendency to amore uneven paint film obtained by these methods, is to be counteracted by more coatsapplied. If at all possible each coat is to be applied across the preceding one - ingeneral follow good painting practise.
Brush application: On poorly prepared surfaces it is always recommended to apply the first coat by brush.Extra thinning will facilitate the penetration of the paint material, but will also require anextra layer to be applied.
Wet/dry film thickness Please note that the thixotropic nature of HEMPADUR MARINE MASTIC 45880 may givespray application: a rather "wavy" surface of the paint just after application. This smoothens at drying, but
can make it necessary to let the wet film readings be of a higher value than indicated. Inmany cases the wet film thickness reading should be 25-50 micron/1-2 mils higher thancalculated. As the wavy surface becomes more smooth during drying this apparentlyhigher wet film thickness will not cause a higher paint consumption than otherwiseStipulated.
Film thickness/thinning: HEMPADUR MARINE MASTIC 45880 is normally specified in 125-200 micron/5-8 mils.The typical film thickness for a two coat system is 150 micron/6 mils each coat. Usuallya maximum of 5% thinning with THINNER 08450 is relevant. However, depending onambient conditions, additional thinning may be required. May be specified down to 75micron/3 mils. To obtain optimum film formation in film thicknesses lower than 125micron/5 mils dry film thickness additional thinning with 5-10% THINNER 08450 isRecommended.
Pot life: When measured under standard conditions the pot life is 1 hour at 20°C/68°F forHEMPADUR MARINE MASTIC 45880. However, for a 20 litres/5 US gallons mix, andused under warm climate conditions, the heat developed by the chemical reactionbetween BASE and CURING AGENT may make the corresponding practical pot lifeshorter.Therefore: At high temperatures, use the paint immediately after mixing irrespective ofequipment.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: December 2001 - 4588011480CO006 - MarineHEMPEL’S MARINE PAINTS A/S
Attached: Tables of "physical data versus temperature"
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
Physical data Drying time and recoating interval vary with film thickness, temperature and laterversus temperature: exposure conditions:
HEMPADUR MARINE MASTIC 45880 in a dry film thickness of 100-150 micron/4-6 milstypically touch up by brush
3 hours4 hours
4 hours5 hours
5 hours7 hours
12 hours18 hours
N/AN/AAtmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
Interval for recoating with HEMUCRYL topcoats
3 hours3 hours
4 hours4 hours
5 hours5 hours
12 hours12 hours
30 hours30 hours
4 days4 days
Atmospheric, medium or severeImmersion*
Interval for recoating with HEMPATEX qualities
3 hours4 hours
4 hours5 hours
5 hours7 hours
12 hours18 hours
30 hours42 hours
4 days6 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPATHANE qualities
3 hours4 hours5 hours
4 hours5 hours6 hours
5 hours7 hours8 hours
12 hours18 hours22 hours
30 hours42 hours50 hours
4 days6 days7 days
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with HEMPADUR qualities
MINIMUM recoating interval related to later conditions of exposure:
2 hours3 days
3 hours5 days
4 hours7 days
10 hours14 days
24 hours1 month
3 days2½ months
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposureNotes:• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that the
substrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used• In case of low temperatures, it is recommended that HEMPADUR MARINE MASTIC 45880 has been given a
proper induction time before application. Under such conditions consider paint temperature equal to substratetemperature and follow the rules given on page 2.
HEMPADUR MARINE MASTIC 45880 in a dry film thickness of 200 micron/8 mils,typically by airless spray:
4 hours6 hours
5 hours8 hours
7 hours10 hours
18 hours25 hours
N/AN/AAtmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
Interval for recoating with HEMUCRYL topcoats
4 hours4 hours
5 hours5 hours
7 hours7 hours
18 hours18 hours
42 hours42 hours
5 days5 days
Atmospheric, medium or severeImmersion*
Interval for recoating with HEMPATEX qualities
4 hours6 hours
5 hours8 hours
7 hours10 hours
18 hours25 hours
42 hours60 hours
5 days7 days
Atmospheric, medium Atmospheric, severe
Interval for recoating with HEMPATHANE qualities
4 hours6 hours8 hours
5 hours8 hours
10 hours
7 hours10 hours12 hours
18 hours25 hours30 hours
42 hours60 hours3 days
5 days7 days8 days
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with HEMPADUR qualities
MINIMUM recoating interval related to later conditions of exposure:
4 hours3 days
5 hours5 days
6 hours7 days
15 hours14 days
36 hours1 month
6 days2½ months
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposureNotes:
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPEL Product Data
ProductDataData
Product• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that thesubstrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used.• In case of low temperatures, it is recommended that HEMPADUR MARINE MASTIC 45880 has been given a
proper induction time before application. Under such conditions consider paint temperature equal to substratetemperature and follow the rules given on page 2.
MAXIMUM recoating intervals dry film thickness):
36 hours18 hours
2 days1 day
3 days1½ days
6 days3 days
N/AN/A
N/AN/A
Atmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:Interval for recoating with HEMUCRYL topcoats
6 hours6 hours
9 hours9 hours
12 hours12 hours
30 hours30 hours
72 hours72 hours
10 days10 days
Atmospheric, medium and severeImmersion*
Interval for recoating with HEMPATEX qualities
10 days36 hours
14 days2 days
21 days3 days
4 weeks6 days
2 months14 days
3 months21 days
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMPATHANE topcoats
NoneNone
15 days
NoneNone
23 days
NoneNone
30 days
NoneNone
60 days
NoneNone
90 days
NoneNone
90 days
Atmospheric, mediumAtmospheric, severeImmersion°
Interval for recoating with HEMPADUR qualitiesMAXIMUM recoating interval related to later conditions of exposure:
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposure°) Depending on actual local conditions, extended maximum recoating intervals may
apply. Please contact HEMPEL for further advice.
Specific Notes for overcoating with HEMPATHANE TOPCOATS:Prior to application of HEMPATHANES it is mandatory to clean the surface thoroughly.To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant. However, such a test is not the final proof of long-term durability, but if theresult is doubtful, repeated cleaning will be relevant. A more safe solution could be torefresh the surface with a new thin (diluted) coat of HEMPADUR MARINE MASTIC 45880.
General notes on prolonged recoating intervals:Besides the notes stated under the tables for minimum recoating intervals, the followingapplies:A completely clean surface is mandatory to ensure intercoat adhesion, especially in thecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.
Any degraded surface layer, as a result of a long exposure period, must be removedas well. Water jetting may be relevant to remove any degraded surface layer and mayalso replace the above-mentioned cleaning methods when properly executed. ConsultHEMPEL for specific advice if in doubt.To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant, however, this test patch should not be a final proof of the durability of thecoating.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®MARINE MASTIC 45880CURING AGENT 95880
Description: HEMPADUR MARINE MASTIC 45880 is a two-component, high solids, high build epoxymastic paint. It is selfpriming, has good wetting properties, and forms a hard and toughcoating with good resistance to abrasion, spillage of mineral oils and to seawater. Lowtemperature curing.
Recommended use: As a high build primer, intermediate and/or finishing coat in epoxy systems according tospecification - typically when a low solvent content and high film thickness per coat arerequired.As a general performance coating for onboard touch-up, repair and maintenance workand full refurbishment of exterior hull, cargo holds (dry and wet), weather decks,topsides and superstructure when a need for few products outweighs more specialisedcoatings.As a finishing coat where the cosmetic appearance of epoxy paints is acceptable.
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health,Great Britain.Classified as class 1 material according to BS 476: Part 7: 1987 (fire testing).Complies with Section 175.300 of the Code of Federal Regulations in respect ofcarriage of dry foodstuffs (FDA) in spaces with an internal surface area larger than 1000m²/10,750 sq.ft.Has a German and Danish EC-type Examination Certificate.Service temperatures: Dry: Maximum 120°C/248°F (See REMARKS overleaf)
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11480 - Green/40640 - Red/50630*Finish: Semi--glossVolume solids, %: 77 ± 1Theoretical spreading rate: 3.9 m²/litre - 200 micron
154 sq.ft./US gallon - 8 milsFlash point: 35°C/95°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 6 (approx) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 220 g/litre - 1.8 lbs/US gallon
*Other shades may be available - subject to prior confirmation.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio: Base 45889 : Curing agent 95880
3 : 1 by volumeApplication method: Airless spray Hand tools (touch up)Thinner (max. vol.): Depending on purpose usually less than 5% THINNER 08450 (See REMARKS overleaf)Pot life: 1 hour (20°C/68°F) (Airless spray)
2 hours (20°C/68°F) (Brush)(See separate APPLICATION INSTRUCTIONS)
Nozzle orifice: .017"-.023" (See separate APPLICATION INSTRUCTIONS)Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610 or HEMPEL'S THINNER 08450Indicated film thickness, dry: 200 micron/8 mils (see REMARKS overleaf)Indicated film thickness, wet: 275 micron/11 milsRecoat interval, min: According to separate APPLICATION INSTRUCTIONSRecoat interval, max: According to separate APPLICATION INSTRUCTIONS
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPADUR MARINE MASTIC 45880
SURFACE New steel: When used as an intermediate or finishing coat please refer to the data sheet for thePREPARATION: preceding GALVOSIL or HEMPADUR primer. When used as a primer please refer to the
specification.Repair and maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughly bypower tool cleaning to minimum St 2 (spot repairs) or by abrasive blasting to min. Sa 2, preferablyto Sa 2½. Improved surface preparation will improve the performance of HEMPADUR MARINEMASTIC 45880. As an alternative to dry cleaning, water jetting to min. WJ-3 (NACE No. 5/SSPC-SP12), may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptable beforeapplication. Feather edges to sound and intact paint. Dust off residues.When used for immersion service, repair: As above, yet St 3 (spot repairs) or Sa 2½ or WJ-2 isrecommended.On pit-corroded surfaces, excessive amounts of salt residues may call for water jetting, wetabrasive blasting, alternatively dry abrasive blasting, high pressure fresh water hosing, drying, andfinally, dry abrasive blasting again.
APPLICATION Apply only on a dry and clean surface with a temperature above the dew point to avoidCONDITIONS: condensation. Recommended lowest temperature is 0°C/32°F, yet curing takes place down to
-10°/14°F. The temperature of the paint itself should be 15°C/59°F or above, but belowapproximately 30°C/86°F to secure proper application properties. Optimal spraying properties areobtained at a paint temperature of 18-22°C/64-72°F. In warm climates, the paint should be storedin a cool place. In confined spaces provide adequate ventilation during application and drying.In cases where faster drying at very low temperatures is required, HEMPADUR MARINE MASTIC45880 may advantageously be replaced by HEMPADUR 45143. Please also see separateAPPLICATION INSTRUCTIONS.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None or according to specification.COAT:
REMARKS: Certificates have been issued under the former quality number 4588.Weathering/ The natural tendency of epoxy coatings to chalk in outdoor exposure and to become moreservice sensitive to mechanical damage and chemical exposure at elevated temperatures is alsotemperatures: reflected in this product.
Film thicknesses/ May be specified in another film thickness than indicated depending on purpose and area of use.Thinning: This will alter spreading rate and may influence drying time and recoating interval. Normal range dry
is 125-200 micron/5-8 mils. Avoid application of excessive film thicknesses.May be specified in lower film thickness for which purpose additional thinning is required, pleasesee separate APPLICATION INSTRUCTIONS. If the paint temperature is below 20°C/68°F, extrathinning (max 15%) may also be required.
Two coats: The typical dry film thickness for a two coat system is 150 micron/6 mils each coat.Application onto zinc It is recommended to apply HEMPADUR MARINE MASTIC 45880 by using a "mist-coat" proceduresilicate or spray- provided the paint temperature is above approximately 20°C/68°F: A thin, undiluted coat ismetallized surfaces: applied (the mist coat) and after a few minutes, a second coat is applied in the full specified film
thickness.
Note: HEMPADUR MARINE MASTIC 45880 is for professional use only.
Issued: December 2001 - 4588011480CO006 - MarineHEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPADUR®MARINE MASTIC 45880CURING AGENT 95880
Scope: These Application Instructions cover surface preparation, application equipment andapplication details for HEMPADUR MARINE MASTIC 45880.
Surface preparation: General: In order to obtain best performance, abrasive blast cleaning is recommended.However, HEMPADUR MARINE MASTIC 45880 has “surface tolerant” properties andoffers higher performance than many other coatings when applied to surfacesmechanically cleaned only (salts, oil, grease etc. shall always be removed).
Remove oil and grease with suitable detergent, salt and other contaminants by (highpressure) fresh water cleaning.
REPAIR AND MAINTENANCE:
When used for atmospheric exposure:
Spot-repairs:Clean damaged areas thoroughly by power tool cleaning to minimum St 2 (spot-repairs)or by abrasive blasting to minimum Sa 2, preferably Sa 2½. Improved surfacepreparation will improve the performance of HEMPADUR MARINE MASTIC 45880. As analternative to dry cleaning, water jetting to minimum WJ-3 (NACE No. 5/SSPC-SP12),may be used. A flash-rust degree of maximum FR-2 (Hempel standard) is acceptablebefore application. Feather edges to sound and intact areas. Brush off loose material.Touch up to full film thickness.
Compatibility: HEMPADUR MARINE MASTIC 45880 may be used in connection withother generic paint systems than epoxy and polyurethanes.It is recommended to make a test patch. In any case it is a must that the old paintsystem is tightly adhering and is properly prepared before the touch-up is performed.
Full coating:Compatibility with old system: In general full compatibility can be expected with oldepoxy systems. A test patch should always be performed before fullcoating is decided. Ifthe old epoxy is not weathered/chalked or if it is top coated with polyurethane, it isrecommended to roughen the surface before recoating. Furthermore, very thoroughcleaning is a must. Any dirt, chalked surface material, oil and grease should be removedwith suitable detergent followed by high pressure fresh water cleaning of the entiresurface.
Removal of old system: Full coating after complete mechanical removal of an old paintsystem is possible too. Yet, it must be considered that mechanical cleaning by discgrinding or by rotating wire brushing may produce a very smooth surface giving reason toreduced adhesive forces.
Note: Another risk is remains of a hard black rustscale being cleaned to an apparentbrightness without showing any adhesive defects. Yet, the exposure to open air duringcleaning may have started a further oxidation of the hard black rust making itmechanically weak and of poor adhesion to the underlying steel surface. Later, duringservice, the scale plus overlaying paint material may flake off.
When used for immersion service, repair:Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Clean damaged areas thoroughlyby power tool cleaning to St 3 (minor areas) or by abrasive blasting to min Sa 2,preferably Sa 2½. Improved surface preparation will improve the performance ofHEMPADUR MARINE MASTIC 45880. As an alternative to dry cleaning, water jetting tominimum WJ-2 (NACE No. 5/SSPC-SP 12), may be used. A flash rust degree ofmaximum FR-2 preferably FR-1 (HEMPEL standard) is acceptable before application.Feather edges to sound intact areas. Dust off residues. Touch up to full film thickness.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPADUR MARINE MASTIC 45880
Note: On old steel surfaces having been exposed to sea water, excessive amounts ofsalt residues in pittings may call for high pressure water jetting, wet abrasive blasting,alternatively dry abrasive blasting, high pressure fresh water hosing, drying, and finally,dry abrasive blasting again.
NEW STEEL:
When used as intermediate and/or finishing coat, surface preparation according toProduct Data Sheet for the preceding primer coat (HEMPADUR primers). When used as aself priming coat, surface preparation according to specification.
Application equipment: HEMPADUR MARINE MASTIC 45880 being a high solids and a relatively high viscositymaterial, may require special measures to be taken at application.
Recommended airless spray equipment:
Pump ratio: min. 45:1Pump output: 12 litres/minute (theoretical)
Input pressure: min. 6 bar/90 psiSpray hoses: max. 100 metres/300 feet, ½” internal diameter
max. 30 metres/100 feet, 3/8" internal diametermax. 6 metres/20 feet, 1/4" internal diameter
Regular surfaces:Nozzle size: .021" through .023"Fan angle: 60°.
Complicated surfaces (and touch up):Nozzle size: .017" through .021"Fan angle: 40°.
After finishing the application, clean the equipment immediately with THINNER 08450 orHEMPEL’S TOOL CLEANER 99610.
Note: Increasing hose diameter may increase paint flow, thereby improving the sprayfan. If longer hoses are necessary it may be necessary to raise the pump ratio to 60:1,maintaining the high output capacity of the pump.
Alternatively up to approximately 5% THINNER 08450 may be added, but thinning mustbe done with care as the anti-sagging properties are drastically reduced by overthinning.
Airless spray data are indicative and subject to adjustment.
Induction time: In case of a paint temperature at 15°C/59°F or below, it is an advantage to allow thetwo components to prereact before application. This is especially relevant in the case ofsubstrate temperatures also being below 15°C/59°F.
In case of a paint temperature at 15°C/59°F, an induction time of 15 minutes isrecommended. In case of a paint temperature at 10°C/50°F, an induction time of 25minutes is recommended. In order to obtain proper application properties, the painttemperature should preferably never be below 10°C/50°F.
Application Film-build/continuity: With this paint material applied in one/few coat(s) it is of speciallarger surfaces: importance that a continuous, pinhole-free paint film is obtained at application of each
spray applied coat. An application technique which will ensure good film formation on allsurfaces must be adopted. It is very important to use nozzles of the correct size, not toobig, and to have a proper, uniform distance of the spray gun to the surface, 30-50 cmshould be aimed at. Furthermore, great care must be taken to cover edges, openings,rear sides of stiffeners etc. Thus, on these areas application of a stripe coat willtherefore be good painting practice. To obtain good and steady atomizing, the viscosityof the paint must be suitable and the spray equipment must be sufficient in outputpressure and capacity. At high working temperatures, use of extra thinner may benecessary to avoid dust-spray.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPEL Product Data
ProductDataData
ProductHEMPADUR MARINE MASTIC 45880
The paint layer must be applied homogeneously and as close to the specification aspossible. Avoid exaggerated film thickness due to the risk of sagging, cracks and solventretention. The paint consumption must be controlled.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, should be remedied.
At application with hand tools, brush, but especially by roller the natural tendency to amore uneven paint film obtained by these methods, is to be counteracted by more coatsapplied. If at all possible each coat is to be applied across the preceding one - ingeneral follow good painting practise.
Brush application: On poorly prepared surfaces it is always recommended to apply the first coat by brush.Extra thinning will facilitate the penetration of the paint material, but will also require anextra layer to be applied.
Wet/dry film thickness Please note that the thixotropic nature of HEMPADUR MARINE MASTIC 45880 may givespray application: a rather "wavy" surface of the paint just after application. This smoothens at drying, but
can make it necessary to let the wet film readings be of a higher value than indicated. Inmany cases the wet film thickness reading should be 25-50 micron/1-2 mils higher thancalculated. As the wavy surface becomes more smooth during drying this apparentlyhigher wet film thickness will not cause a higher paint consumption than otherwiseStipulated.
Film thickness/thinning: HEMPADUR MARINE MASTIC 45880 is normally specified in 125-200 micron/5-8 mils.The typical film thickness for a two coat system is 150 micron/6 mils each coat. Usuallya maximum of 5% thinning with THINNER 08450 is relevant. However, depending onambient conditions, additional thinning may be required. May be specified down to 75micron/3 mils. To obtain optimum film formation in film thicknesses lower than 125micron/5 mils dry film thickness additional thinning with 5-10% THINNER 08450 isRecommended.
Pot life: When measured under standard conditions the pot life is 1 hour at 20°C/68°F forHEMPADUR MARINE MASTIC 45880. However, for a 20 litres/5 US gallons mix, andused under warm climate conditions, the heat developed by the chemical reactionbetween BASE and CURING AGENT may make the corresponding practical pot lifeshorter.Therefore: At high temperatures, use the paint immediately after mixing irrespective ofequipment.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: December 2001 - 4588011480CO006 - MarineHEMPEL’S MARINE PAINTS A/S
Attached: Tables of "physical data versus temperature"
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
Physical data Drying time and recoating interval vary with film thickness, temperature and laterversus temperature: exposure conditions:
HEMPADUR MARINE MASTIC 45880 in a dry film thickness of 100-150 micron/4-6 milstypically touch up by brush
3 hours4 hours
4 hours5 hours
5 hours7 hours
12 hours18 hours
N/AN/AAtmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
Interval for recoating with HEMUCRYL topcoats
3 hours3 hours
4 hours4 hours
5 hours5 hours
12 hours12 hours
30 hours30 hours
4 days4 days
Atmospheric, medium or severeImmersion*
Interval for recoating with HEMPATEX qualities
3 hours4 hours
4 hours5 hours
5 hours7 hours
12 hours18 hours
30 hours42 hours
4 days6 days
Atmospheric, mediumAtmospheric, severe
Interval for recoating with HEMPATHANE qualities
3 hours4 hours5 hours
4 hours5 hours6 hours
5 hours7 hours8 hours
12 hours18 hours22 hours
30 hours42 hours50 hours
4 days6 days7 days
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with HEMPADUR qualities
MINIMUM recoating interval related to later conditions of exposure:
2 hours3 days
3 hours5 days
4 hours7 days
10 hours14 days
24 hours1 month
3 days2½ months
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposureNotes:• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that the
substrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used• In case of low temperatures, it is recommended that HEMPADUR MARINE MASTIC 45880 has been given a
proper induction time before application. Under such conditions consider paint temperature equal to substratetemperature and follow the rules given on page 2.
HEMPADUR MARINE MASTIC 45880 in a dry film thickness of 200 micron/8 mils,typically by airless spray:
4 hours6 hours
5 hours8 hours
7 hours10 hours
18 hours25 hours
N/AN/AAtmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
Interval for recoating with HEMUCRYL topcoats
4 hours4 hours
5 hours5 hours
7 hours7 hours
18 hours18 hours
42 hours42 hours
5 days5 days
Atmospheric, medium or severeImmersion*
Interval for recoating with HEMPATEX qualities
4 hours6 hours
5 hours8 hours
7 hours10 hours
18 hours25 hours
42 hours60 hours
5 days7 days
Atmospheric, medium Atmospheric, severe
Interval for recoating with HEMPATHANE qualities
4 hours6 hours8 hours
5 hours8 hours
10 hours
7 hours10 hours12 hours
18 hours25 hours30 hours
42 hours60 hours3 days
5 days7 days8 days
Atmospheric, mediumAtmospheric, severeImmersion
Interval for recoating with HEMPADUR qualities
MINIMUM recoating interval related to later conditions of exposure:
4 hours3 days
5 hours5 days
6 hours7 days
15 hours14 days
36 hours1 month
6 days2½ months
Drying time (approx)Curing time (approx)
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposureNotes:
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
HEMPEL Product Data
ProductDataData
Product• Avoid sudden drops in (substrate) temperatures during drying/initial curing. It is especially important that thesubstrate temperature does not drop significantly before application of the acrylic or polyurethane finish andthat proper ventilation is maintained.
• If faster handling or recoating at lower temperatures is required, HEMPADUR 45143 may be used.• In case of low temperatures, it is recommended that HEMPADUR MARINE MASTIC 45880 has been given a
proper induction time before application. Under such conditions consider paint temperature equal to substratetemperature and follow the rules given on page 2.
MAXIMUM recoating intervals dry film thickness):
36 hours18 hours
2 days1 day
3 days1½ days
6 days3 days
N/AN/A
N/AN/A
Atmospheric, mediumAtmospheric, severe
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:Interval for recoating with HEMUCRYL topcoats
6 hours6 hours
9 hours9 hours
12 hours12 hours
30 hours30 hours
72 hours72 hours
10 days10 days
Atmospheric, medium and severeImmersion*
Interval for recoating with HEMPATEX qualities
10 days36 hours
14 days2 days
21 days3 days
4 weeks6 days
2 months14 days
3 months21 days
Atmospheric, medium°Atmospheric, severe°
Interval for recoating with HEMPATHANE topcoats
NoneNone
15 days
NoneNone
23 days
NoneNone
30 days
NoneNone
60 days
NoneNone
90 days
NoneNone
90 days
Atmospheric, mediumAtmospheric, severeImmersion°
Interval for recoating with HEMPADUR qualitiesMAXIMUM recoating interval related to later conditions of exposure:
40°C/104°F30°C/86°F20°C/68°F10°C/50°F0°C/32°F-5°C/23°FSurface temperature:
* Only HEMPATEX HI-BUILD 46330 is recommended for this exposure°) Depending on actual local conditions, extended maximum recoating intervals may
apply. Please contact HEMPEL for further advice.
Specific Notes for overcoating with HEMPATHANE TOPCOATS:Prior to application of HEMPATHANES it is mandatory to clean the surface thoroughly.To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant. However, such a test is not the final proof of long-term durability, but if theresult is doubtful, repeated cleaning will be relevant. A more safe solution could be torefresh the surface with a new thin (diluted) coat of HEMPADUR MARINE MASTIC 45880.
General notes on prolonged recoating intervals:Besides the notes stated under the tables for minimum recoating intervals, the followingapplies:A completely clean surface is mandatory to ensure intercoat adhesion, especially in thecase of long recoating intervals. Any dirt, oil and grease have to be removed with egsuitable detergent followed by high pressure fresh water cleaning. Salts to be removedby fresh water hosing.
Any degraded surface layer, as a result of a long exposure period, must be removedas well. Water jetting may be relevant to remove any degraded surface layer and mayalso replace the above-mentioned cleaning methods when properly executed. ConsultHEMPEL for specific advice if in doubt.To determine whether the quality of the surface cleaning is adequate, a test patch maybe relevant, however, this test patch should not be a final proof of the durability of thecoating.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 5HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4588011480CO006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®HI-BUILD 46330
Description: HEMPATEX HI-BUILD 46330 is based on chlorinated rubber. Physically drying. Resistantto salt water, splashes of mineral oils, aliphatic solvents and a wide range ofchemicals, but not to animal and vegetable oils or aromatic solvents.
Recommended use: Selfprimed, or as an intermidiate or finishing coat on steel structures in moderately toseverely corrosive environment, including permanently submerged surfaces.
Service temperatures: Maximum, dry: 80°C/176°F (see remarks overleaf).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11480 - Red/50630Finish: FlatVolume solids, %: 42 ± 1Theoretical spreading rate: 5.3 m²/litre - 80 micron
211 sq.ft./US gallon - 3.2 milsFlash point: 32°C/90°FSpecific gravity: 1.4 kg/litre - 11.7 lbs/US gallonDry to touch: 8 (approx.) hours at 20°C/68°FV.O.C.: 510 g/litre - 4.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush (touch-up)Thinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .021"-.023"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 80 micron/3.2 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 8 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4633011480CO001
HEMPATEX HI-BUILD 46330
SURFACE New steel: Abrasive blasting to Sa 2½. For temporary protection, if required, use suitablePREPARATION: shopprimer. All damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For repair and touch-up use HEMPATEX HI-BUILD 46330.Maintenance: Remove oil and grease , etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Dust off residues. Touch up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None, or HEMPATEX system as per specification.COAT: Ship bottoms: Antifouling according to specification.
REMARKS:Service As HEMPATEX HI-BUILD 46330 is a thermoplastic product, prolonged mechanical exposure attmperatures: temperatures above approximately 40°C/105°F may cause film indentation. When temperature
drops below, mechanical strength is recovered.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range dryis 40-100 micron/1.6-4 mils. A series of maintenance jobs may result in build up of a too high totalfilm thickness which may cause blister formation due to "entrapped" solvents. As each coat mayalso retain solvents, it is generally recommended not to apply HEMPATEX HI-BUILD 46330 inexcessive film thickness.
Recoating: In case of multi-coat application, drying time and minimum recoating interval will be influenced bythe number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification.No maximum recoating interval, but before recoating after exposure in contaminated environment,clean the surface thoroughly by high pressure fresh water cleaning and allow to dry.
Note: HEMPATEX HI-BUILD 46330 is for professional use only.
Issued: October 1999 - 4633011480CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4633011480CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®HI-BUILD 46370
Description: HEMPATEX HI-BUILD 46370 is a physically drying high build paint with optimum colourretention. Based on acrylic resin and chlorinated plasticizer. Resistant to salt water,splashes of aliphatic hydrocarbons, animal and vegetable oils.
Recommended use: 1. As an exterior finishing coat on containers.2. As an intermediate or finishing coat in HEMPATEX systems in moderately to
severely corrosive environment.
Service temperatures: Maximum, dry: 80°C/175°F (see REMARKS overleaf).
Availability: Normally available on orders for container newbuildings only.
PHYSICAL CONSTANTS:Colours/Shade Nos: White/10000*Finish: Semi-flatVolume solids, %: 40 ± 1Theoretical spreading rate: 4.7 m²/litre - 85 micron
189 sq.ft./US gallon - 3.4 milsFlash point: 25°C/77°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: ½ (approx) hour at 20°C/68°F (ISO 1517)Dry to touch: 4 (approx) hours at 20°C/68°FV.O.C.: 530 g/litre - 4.4 lbs/US gallon
*Concerning other shades, reference is made to HEMPEL'S CONTAINER COLOUR CARD.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max. Vol.): 08080 (20%) 08080 (30%) 08080 (5%)Nozzle orifice: .017"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 85 micron/3.4 mils (See REMARKS overleaf)Indicated film thickness, wet: 200 micron/8 milsRecoat interval, min: 4 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4637010000CO016
HEMPATEX HI-BUILD 46370
SURFACE Repair and Maintenance: Remove oil and grease etc. with suitable detergent. Remove salt andPREPARATION: other contaminants by high pressure fresh water cleaning. Followed by:
For steel: Remove all rust and loose material by abrasive blasting or power tool cleaning. Dust offresidues. Touch up bare spots with e.g. suitable primer followed by HEMPATEX HI-BUILD 46370 tofull film thickness.For other metals, concrete: Reference is made to the corresponding painting specification and tothe Product Data Sheet for the primer/sealer.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPADUR ZINC 15360, HEMPADUR PRIMER 15300 or according to specification.COAT:
SUBSEQUENT None, HEMPATEX ENAMEL 56360, or as per specification depending on area of use.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Service As HEMPATEX HI-BUILD 46370 is a thermoplastic product, prolonged mechanical exposure attemperatures: temperatures above approx. 40°C/104°F may cause film indentation. When temperature drops
below, mechanical strength is recovered.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoat interval. Normal range is75-100 microns/3-4 mils. A series of maintenance jobs may result in build up of a too high totalfilm thickness which may cause blister formation due to "entrapped" solvents. As each coat mayalso retain solvents, it is generally recommended not to apply HEMPATEX HI-BUILD 46370 inexcessive film thickness.
Recoating: In case of multicoat application, drying time and minimum recoat interval are influenced by theactual film thickness and number of coats applied. Reference is made to the correspondingpainting specification.No maximum recoating interval, but before recoating after exposure in contaminated environment,clean the surface thoroughly by high pressure fresh water hosing and allow to dry.
Note: HEMPATEX HI-BUILD 46370 is for professional use only.
Issued: April 2002 - 4637010000CO016HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4637010000CO016
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®HI-BUILD 46410Description: HEMPATEX HI-BUILD 46410 is a physically drying high build paint with good colour
retention as a semi-flat finish. Based on acrylic resin, alkyd and non-chlorinatedplasticizer. Contains zinc phosphate. Resistant to salt water, splashes of aliphatichydrocarbons, animal and vegetable oils.
Recommended use: 1. As a primer, intermediate or finishing coat in HEMPATEX-systems in moderatelycorrosive environment.
2. As a selfprimed repair and touch-up coating for containers as well as other caseswhere a fast and economic repair job is desired.
3. As a finishing coat for containers.
Service temperatures: Maximum, dry: 80°C/176°F (See REMARKS overleaf).
Certificates/Approvals: Approved by CSIRO, Australia for carriage of foodstuffs.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/11480* - Red/50630*Finish: Semi-flatVolume solids, %: 42 ± 1Theoretical spreading rate: 4.2 m²/litre - 100 micron
168 sq.ft./US gallon - 4 milsFlash point: 24°C/75°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: 1 (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 4 (approx.) hours at 20°C/68°FV.O.C.: 515 g/litre - 4.3 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max. Vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .017"-.021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 225 micron/9 milsRecoat interval, min: When dry (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4641011480CO003
HEMPATEX HI-BUILD 46410
SURFACE New steel: Remove oil and grease etc. with suitable detergent. Remove salt and otherPREPARATION: contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½. For temporary
protection, if required, use suitable shopprimer. All damage of shopprimer and contamination fromstorage and fabrication should be thoroughly cleaned prior to final painting. For repair and touch-upuse HEMPATEX HI-BUILD 46410.Repair and maintenance: Remove oil and grease etc. with suitable detergent. Remove salt andother contaminants by (high pressure) fresh water cleaning.Remove all rust and loose material by abrasive blasting or power tool cleaning. Dust off residues.Touch up bare spots with HEMPATEX HI-BUILD 46410 to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None, or according to specification.COAT:
SUBSEQUENT None, or as per specification.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to sulphide and chlorine-
Containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Service As HEMPATEX HI-BUILD 46410 is a thermoplastic product, prolonged, mechanical exposure attemperatures: temperatures above approx. 40°C/104°F may cause film indentation. When temperature drops
below, mechanical strength is recovered.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is75-125 micron/3-5 mils. To obtain an even dry film thickness (of 125 micron), application in twopasses (wet-in-wet) is recommended. If applied by roller, e.g. as deckcoating, usual dry filmthickness is approx. 50 microns per coat. A series of maintenance jobs may result in build up of atoo high total film thickness which may cause blister formation due to "entrapped" solvents. Aseach coat may also retain solvents, it is generally recommended not to apply HEMPATEX HI-BUILD46410 in excessive film thickness.
Deck coating: If a skid-proof surface is desired, sprinkle HEMPEL'S ANTI-SLINT 67500 evenly on the first coat ofHEMPATEX HI-BUILD 46410 while still wet (consumption approx. 2.5 kg/5.5 lbs to 25 m² /270sq.ft.). When the paint is dry, sweep up surplus grit and apply a second coat of HEMPATEXHI-BUILD 46410. Antiskid properties can also be obtained by mixing 1.0 kg of HEMPEL'S ANTISLIPBEADS 67420 into 20 litre of HEMPATEX HI-BUILD 46410.
Recoating: For multicoat application minimum recoating interval is influenced by the actual film thickness andnumber of coats applied. Reference is made to the corresponding painting specification.No maximum recoating interval, but before recoating after exposure in contaminated environment,clean the surface thoroughly by high pressure fresh water hosing and allow to dry.
Note: HEMPATEX HI-BUILD 46410 is for professional use only.
Issued: April 2002 - 4641011480CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4641011480CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPANYL* HI-BUILD 46640GALVOGRIP
Description: HEMPANYL HI-BUILD 46640 is a physically drying high build paint. Based on modifiedvinyl resins.For service temperature range, see below.
Recommended use: As a primer and finishing coat on galvanized surfaces like handrails and sheeting in
mild to medium corrosive environment also in the special situations where rougheningof the surface is not possible.
Service temperatures: Maximum, dry: 80°C/176°F (See REMARKS overleaf).
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/50710Finish: Semi-flatVolume solids: 39%Theoretical spreading rate: 3.9 m²/litre - 100 micron
156 sq.ft./US gallon - 4 milsFlash point: 22°C/72°FSpecific gravity: 1.3 kg/litre - 10.9 lbs/US gallonDry to touch: 4 (approx.) hours at 20°C/68°FV.O.C.: 553 g/litre - 4.6 lbs/US gallon
*Other shades according to assortment list.
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Application method: Airless spray Brush/RollerThinner (max. vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .013"-.018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 milsIndicated film thickness, wet: 275 micron/11 milsRecoat interval, min: 12 hoursRecoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4664050710CO001
HEMPANYL HI-BUILD 46640
SURFACE Remove oil and grease etc. with suitable detergent. Remove salt and other contaminants by (highPREPARATION: pressure) fresh water cleaning. "White rust" must be removed by sandpapering or light abrasive
sweep blasting. It is very important that all contamination and possible passivation layers areremoved in order to obtain proper adhesion.In certain cases - related to the structure of the outer zinc layer - roughening of the surface will benecessary to secure adhesion.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None or according to specification.COAT:
SUBSEQUENT None or according to specification.COAT:
REMARKS: As HEMPANYL HI-BUILD 46640 is a thermoplastic product, prolonged, direct contact attemperatures above approx. 40°C/104°F may cause film indentation. When temperature dropsbelow, mechanical strength is recovered.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoat interval. Normal range dry is75-100 micron/3-4 mils.No maximum recoat interval, but before recoating after exposure in contaminated environment,clean the surface thoroughly by high pressure fresh water hosing and allow to dry.
Note: HEMPANYL HI-BUILD 46640 is for professional use only.
Issued: September 1996-4664050710CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4664050710CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®HI-BUILD 46820
Description: HEMPATEX HI-BUILD 46820 is based on acrylic resin, physically drying. Optimum colourretention. Resistant to salt water, splashes of aliphatic hydrocarbons, animal andvegetable oils.
Recommended use: 1. As a finishing coat on structural steel in moderately to severely corrosiveenvironments.
2. As a finishing coat on containers, rolling stocks, etc.Note about application and touch-up, please see REMARKS overleaf.
Service temperatures: Maximum, dry: 80°C/176°F (see REMARKS overleaf).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/17700 Light alu./19000Finish: Semi-flat Semi-flatVolume solids, %: 33 ± 1 31 ± 1Theoretical spreading rate: 4.1 m²/litre - 80 micron 3.9 m²/litre - 80 micron
165 sq.ft/US gallon - 3.2 mils 155 sq.ft/US gallon - 3.2 milsFlash point: 25°C/77°F 25°C/77°FSpecific gravity: 1.0 kg/litre - 8.4 lbs/US gallon 1.0 kg/litre - 8.4 lbs/US gallonDry to touch: 3-4 hours at 20°C/68°F 3-4 hours at 20°C/68°FV.O.C.: 590 g/litre - 4.9 lbs/US gallon 605 g/litre - 5.0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush (touch up)Thinner (max. Vol.): 08080 (5%) 08080 (20%) 08080 (5%)Nozzle orifice: .017"-.021" (See REMARKS overleaf)Nozzle pressure: 175 bar/2500 psi (See REMARKS overleaf)
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 80 microns/3.2 mils (See REMARKS overleaf)Indicated film thickness, wet: 250 microns/10 milsRecoat interval, min.: When dry (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4682019000CO005
HEMPATEX HI-BUILD 46820
SURFACE Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (highPREPARATION: pressure) fresh water cleaning. Remove all rust and loose material by abrasive blasting or power
tool cleaning. Dust off residues. Prime/touch up with suitable primer followed by HEMPATEX46820 to full film thickness.
APPLICATION The surface must be completely clean and dry, its temperature must be above the dew point toCONDITIONS: avoid condensation. In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPADUR PRIMER 15300, HEMPADUR ZINC 15360 or according to specification.COAT:
SUBSEQUENT None or according to specification.COAT:
REMARKS:Service Being a thermoplastic product, prolonged direct contact at temperatures above approximatelytemperatures: 40°C/104°F may cause film indentation. When temperature drops below, mechanical strength is
recovered.Application: Way of application will influence the appearance of the paint film. Spray application, especially by
conventional spray, will facilitate optimum appearance. If applied by brush, use a flat brush notmore than 10 cm/4" wide. After the paint has been distributed it should be laid off with lightstrokes and in one direction only. If the paint is worked too much with brush or roller, it will becomestreaky and grayish and loose its lustre.Irrespective of measures taken during application, touch-up may, however, cause areas ofdifferent visual appearance as to different gloss or sheen.This effect is cosmetic only and has no influence on the protective properties.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoat interval. Normal range is60-100 micron/2.4-4 mils. A series of maintenance jobs may result in build up of a too high totalfilm thickness which may cause blister formation due to "entrapped" solvents. As each coat mayalso retain solvents, it is generally recommended not to apply HEMPATEX HI-BUILD 46820 inexcessive film thickness.In any case, avoid exaggerated filmthicknesses. For this reason it is also recommended to uselowest possible nozzle orifice and pressure when applied by airless spray.
Recoating: In case of multi-coat application, drying time and minimum recoat interval will be influenced by thenumber of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification.Before recoating after exposure in contaminated environment, clean the surface thoroughly byhigh pressure fresh water cleaning and allow to dry.
Note: HEMPATEX HI-BUILD 46820 is for professional use only.
Issued: April 2002 - 4682019000CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4682019000CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR* 47190CURING AGENT 95570
Description: HEMPADUR 47190 is a two-component, modified epoxy especially suited for recoatingwith tin-free, selfpolishing antifoulings.
Recommended use: For exterior hull.In HEMPADUR systems as a tie/sealer coat before application of tin-free antifoulingNAUTIC/COMBIC.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Black/19990Finish: Flat Volume solids: 43%Theoretical spreading rate: 8.6 m²/litre - 50 micron
345 sq.ft./US gallon - 2 milsFlash point: 21°C/70°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonDry to touch: 5 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 507 g/litre - 4.2 lbs/US gallon
The physical constants are subject to normal manufacturing tolerances. Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Mixing ratio for 47190: Base 47199 : Curing agent 95570
5 : 1 by volumeApplication method: Airless spray Brush (touch up)Thinner (max.vol.): 08460 (5%) 08406 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subejct to adjustment) Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 50 micron/2 milsIndicated film thickness, wet: 125 micron/5 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: NAUTIC/COMBIC: 6 days (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4719019990CS002
HEMPADUR 47190
APPLICATION Recommended minimum application and curing temperatures are 10°C/50°F. The temperature ofCONDITIONS: the paint itself should be above 10°C/50°F. The best results are obtained at 15-20°C/60-68°F.
Apply only on a dry and clean surface with a temperature above the dew point to avoidcondensation. In confined spaces such as sea chest or stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR 15130, HEMPADUR 45140, HEMPADUR 17080, HEMPADUR MULTI-STRENGTH orCOAT: according to specification.
SUBSEQUENT Antifouling as per specification. COAT:
REMARKS:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoat interval.Overcoatability: HEMPADUR 47190 is suited for recoating with NAUTIC/COMBIC tin-free only.
Avoid overlappings with primers at touch-ups along section welds etc. Cover by tape to secure anarrow transition zone along bare areas to be primed later on.
Recoating If the maximum recoat interval is exceeded, roughening/special cleaning of the surface is usuallyintervals: necessary to ensure intercoat adhesion - contact nearest HEMPEL office for further information.
Note: HEMPADUR 47190 is for professional use only.
Issued: September 1996-4719019990CS002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 4719019990CS002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S SILVIUM®51570
Description: HEMPEL'S SILVIUM 51570 is an oleoresinous general purpose aluminium paint withgood light reflection.
Recommended use: As a finishing coat on steel and woodwork exterior and interior in mild to moderatelycorrosive environment where an aluminium surface or light reflection is desired, and/orfor moderately hot surface.
Service temperatures: Maximum, dry: 200°C/390°F.
Certificates/Approvals: Complies with Section 175.300 of Food Additive Regulations (in respect of carriage ofdry foodstuffs) of the Code of Federal Regulations as found by review of the U.S. Foodand Drug Administration.Approved by German authorities as a low flame spread material according to IMOresolution MSC 61 (67).Has a German EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Aluminium/19000Finish: Glossy (See REMARKS overleaf)Volume solids, %: 38 ± 1Theoretical spreading rate: 15.2 m²/litre - 25 micron
610 sq.ft./US gallon - 1 milFlash point: 38°C/100°FSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonDry to touch: 5 (approx.) hours at 20°C/68°FV.O.C.: 500 g/litre - 4.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max. vol.): Do not dilute (See REMARKS overleaf)Nozzle orifice: .017"Nozzle pressure: 100 bar/1500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness. dry: 25 micron/1 milIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5157019000CO010
HEMPEL'S SILVIUM 51570
SURFACE Sound and intact areas primed with eg HEMPALIN or other suitable alkyd primers (temperaturePREPARATION: range: see PRECEDING COAT below) can be recoated directly after all contamination from storage
and fabrication has been thoroughly removed. For other areas remove all rust and loose material bypower tool cleaning to St 3 or abrasive blasting to Sa 2.Maintenance: Remove oil and grease etc. with suitable detergent.Remove salt and other contaminants by (high pressure) fresh water cleaning. Remove all rust andloose material by abrasive blasting or power tool cleaning.Dust off residues. Touch up with recommended primer.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING Steel surface temperature: Preceding coat:COAT:
Below 120°C/248°F HEMPALIN PRIMERS120°-200°C/248°-390°F Self primed
SUBSEQUENT None.COAT:
REMARKS: Certificates have been issued under the former quality number 5157.Application: Spray application is recommended.
For brush application use a flat brush not more than 10 cm/4" wide. Do not dilute. After the painthas been laid on, it should be distributed with light strokes and in one direction only. If the paint isworked too much with brush or roller, it will become streaky and greyish and loose its lustre. Theeffect is cosmetic only and has no influence on the protective properties.
Finish: At high temperatures HEMPEL'S SILVIUM 51570 will become greyish and loose its lustre. Thiseffect is cosmetic only and has no influence on the protective properties.
Note: HEMPEL'S SILVIUM 51570 is for professional use only.
Issued: May 2000 - 5157019000CO010HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5157019000CO010
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®ENAMEL 52140
Description: HEMPALIN ENAMEL 52140 is a glossy alkyd enamel which forms a weather resistantcoating. It is flexible and resistant to salt water and spillage of mineral oil and otheraliphatic hydrocarbons.
Recommended use: As a general purpose finishing coat in alkyd systems on exterior and interior steeland woodwork in mildly to moderately corrosive environment.As a finishing coat in engine rooms including tanktops, main engines and auxiliarymachinery.
Service temperatures: Maximum, dry: 120°C/248°F (these temperatures may cause yellowing/discoloration).
Certificates/Approvals: Approved as a low flame spread material by Danish, German, Belgian and Italianauthorities according to IMO resolution MSC 61 (67).Has a German and Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000* Black/19990*Finish: Glossy GlossyVolume solids, %: 46 ± 1 43 ± 1Theoretical spreading rate: 15.3 m²/litre - 30 micron 14.3 m²/litre - 30 micron
615 sq.ft./US gallon - 1.2 mils 575 sq.ft./US gallon - 1.2 milsFlash point: 38°C/100°F 38°C/100°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallon 0.9 kg/litre - 7.5 lbs/US gallonSurface dry: 2½ (approx) hrs at 20°C/68°F (ISO 1517) 2½ (approx) hrs at 20°C/68°F (ISO 1517)Dry to touch: 6-8 hours at 20°C/68°F 6-8 hours at 20°C/68°FV.O.C.: 430 g/litre - 3.6 lbs/US gallon 455 g/litre - 3.8 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max. vol.): 08230 (5%) 08230 (15%) 08230 (5%) (See REMARKS overleaf)Nozzle orifice: .018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08230Indicated film thickness, dry: 30 micron/1.2 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5214010000CO016
HEMPALIN ENAMEL 52140
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PREDEDING HEMPALIN PRIMER 12050, HEMPALIN PRIMER HI-BUILD 13200, HEMPALIN UNDERCOAT 42460 orCOAT: according to specification.
SUBSEQUENT None.COAT:
REMARKS: Certificates have been issued under the former quality number 5214.Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Film thicknesses: May be specified in other filmthicknesses than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoat interval. Normal range 30-40micron/1.2-1.6 mils.
Thinning: THINNER 08080 may be used for spray application, however, with a certain risk of wrinkling of thepreceding fresh coat of HEMPALIN.
Recoating: Recoat intervals related to later conditions of exposure:(30 micron/1.2 mils dry film thickness of HEMPALIN ENAMEL 52140)
5 daysNone8 hours8 hours52140
MediumMildMediumMild
AtmosphericAtmosphericRecoated with(quality numbers only)
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
If the maximum recoat interval is exceeded, roughening of the surface is recommended to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean the surface thoroughly by(high pressure) fresh water hosing and allow to dry.
Note: HEMPALIN ENAMEL 52140 is for professional use only.
Issued: April 2002 - 5214010000CO016HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5214010000CO016
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®ENAMEL HI-BUILD 52220
Description: HEMPALIN ENAMEL HI-BUILD 52220 is an alkyd paint, which can be applied in high filmthickness by airless spray.
Recommended use: As a finishing coat in HEMPALIN Systems on interior and exterior steel in mildly tomoderately corrosive environment.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish authorities according to IMOresolution MSC 61 (67).Has a German and Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000Finish: GlossyVolume solids, %: 47 ± 1Theoretical spreading rate: 7.8 m²/litre - 60 micron
314 sq.ft/US gallon - 2.4 milsFlash point: 38°C/100°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 2½ (approx) hours at 20°C/68°F (ISO 1517)Dry to touch: 6-8 hours at 20°C/68°FV.O.C.: 435 g/litre - 3.6 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush (touch up)Thinner (max.vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .021"-.023"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 60 micron/2.4 mils (See REMARKS overleaf)Indicated film thickness, wet: 125 micron/5 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5222010000CO004
HEMPALIN ENAMEL HI-BUILD 52220
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPALIN PRIMER HI-BUILD 13200 or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: Certificate has been issued under the former quality number 5222.Recoating: Recoat intervals related to later conditions of exposure:
(60 micron/2.4 mils dry film thickness of HEMPALIN ENAMEL HI-BUILD 52220)
5 daysNone16 hours12 hours52220
MediumMildMediumMild
AtmosphericAtmosphericRecoated with(quality number only)
20°C/68°F20°C/68°FSurface temperature
MaximumMinimum
If the maximum recoat interval is exceeded, roughening of the surface is recommended to ensureintercoat adhesion.Before recoating after exposure in contaminated environment, clean surface thoroughly by (highpressure) fresh water hosing and allow to dry.May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoat interval.Do not expose liquid paint to temperatures above 40°C/104°F neither during storage nor inconnection with application.
Note: HEMPALIN ENAMEL HI-BUILD 52220 is for professional use only.
Issued: October 1999 - 5222010000CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5222010000CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®CABINFLAT 52260
Description: HEMPALIN CABINFLAT 52260 is an alkyd paint for interior surfaces.
Recommended use: As a decorative finishing coat on interior steel and woodwork, fibre-board, etc, in mildlycorrosive environment.
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Finish: FlatColour: WhiteShade Number: 10000Volume by Solids: 46%Theoretical spreading rate: 15.3 m²/litre - 30 microns
615 sq.ft./US gallon - 1.2 milsFlash Point: 38C/100F Abel-Pensky, closed cupSpecific Gravity: 1.5 kg/litre
12.5 lbs/US gallonDry to Touch: 4 - 6 hours at 20ºC/68ºFV.O.C: 431 - 3.6 g/litre - lbs/US gallon
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray Brush/RollerThinner (max.vol.): 08080 (5%) 08080 (15%) 08230 (5%)Nozzle Orifice: 0.015" - 0.018"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: THINNER 08080Indicated film thickness, wet: 75 micron/3 milsIndicated film thickness, dry: 30 micron/1.2 milsRecoat interval, min: 8 hours (20ºC/68Fº) Recoat interval, max: None
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, Material Safety Data Sheet(s) should be consulted and national or local safetyregulations should be followed. As a general rule, inhalation of solvent vapours or paintmist, and contact of liquid paint with skin and eyes should be avoided. Forcedventilation should be provided when working with solvent-borne materials in confinedspaces or stagnant air. Even when ventilation is provided, respiratory, skin, and eyeprotection are always recommended when spraying paint. Necessary precautions againstthe risk of fire or explosion must be taken.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 -5226010000
HEMPALIN®CABINFLAT 52260
Application As dictated by normal good painting practice.Conditions: In confined spaces provide adequate ventilation during application and drying.
Preceding Coat: HEMPALIN PRIMER 12050, HEMPALIN PRIMER HI-BUILD 13200, HEMPALIN UNDERCOAT 42460, oraccording to specification.
Subsequent Coat: None.
Remarks: Dry Service Temperature: Periodical, maximum: 100ºC/212ºF - Peak, maximum: 120ºC/248ºF.Approved as a low flame spread material by British and Japanese authorities.
Note: HEMPALIN®CABINFLAT 52260 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 -5226010000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®CABINSILK 52280
Description: HEMPALIN CABINSILK 52280 is an alkyd paint for interior surfaces.
Recommended use: As a decorative finishing coat on interior steel and woodwork, fibre-board, etc. Notsuited for outdoor use.
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Finish: Semi-glossColours: White - Other shades according to assortment list.Shade Numbers: 10000Volume by Volume: 46% Theoretical spreading rate 15.3 m²/litre - 30 microns
615 sq.ft./US gallon - 1.2 milsFlash Point: 38/100 C/F A-Pensky, closed cupSpecific Gravity: 1.3 kg/litre
10.8 lbs/US gallonDry to Touch: 4 - 6 hours at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08230 (5%)Nozzle Orifice: 0.015" - 0.018"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: THINNER 08080Indicated film thickness, wet: 75 micron/3 milsIndicated film thickness, dry: 30 micron/1.2 milsRecoat interval, min: 8 hours (20ºC/68ºF)Recoat interval, max: None
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed. As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided, respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 -5228010000
HEMPALIN®CABINSILK 52280
Application As dictated by normal good painting practice. In confined spaces provide adequate ventilationConditions: during application and drying.
Preceding HEMPALIN PRIMER 12050, HEMPALIN PRIMER HI-BUILD 13200, HEMPALIN UNDERCOAT 42460, orcoat: according to specification.
Subsequent None.coat:
Remarks: Approved by national maritime authorities as a "very low flame-spread material" for use inpassenger ships, etc., in conformity with the SOLAS Convention.
Note: HEMPALIN®CABINSILK 52280 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 -5228010000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®DANREX®52360
Description: HEMPALIN DANREX 52360 is a versatile, alkyd-based, economy paint with fairly goodpenetration into rough and porous substrate.Harmless to grain cargo.
Recommended use: 1. As a self-primed paint system on interior steel and woodwork, e.g. in dry cargoHolds.
2. As a primer for alkyd-based paint systems in mild environment.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by German authorities according to IMOresolution MSC 61 (67).Tested for non-contamination of grain cargo at the Newcastle Occupational Health,Great Britain.Complies with Section 175.300 of Food Additive Regulations (in respect of carriage ofdry foodstuffs) of the Code of U.S. Federal Regulations (FDA).Has a German EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Grey/10670 Red/50610Finish: Semi-gloss Semi-glossVolume solids, %: 56 ± 1 57 ± 1Theoretical spreading rate: 14.0 m²/litre - 40 micron 14.3 m²/litre - 40 micron
561 sq.ft./US gallon - 1.6 mils 571 sq.ft./US gallon - 1.6 milsFlash point: 38°C/100°F 38°C/100°FSpecific gravity: 1.3 kg/litre - 10.8 lbs/US gallon 1.3 kg/litre - 10.8 lbs/US gallonDry to touch: 6-8 hours at 20°C/68°F 6-8 hours at 20°C/68°FV.O.C.: 365 g/litre - 3.0 lbs/US gallon 360 g/litre - 3.0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application methods: Airless spray Air spray Brush/RollerThinner (max. vol.): 08230 (5%) 08230 (15%) 08230 (5%) (See REMARKS overleaf)Nozzle orifice: .018"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08230Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5236010670CO011
HEMPALIN DANREX 52360
SURFACE New steel: Abrasive blasting to minimum Sa 2. For temporary protection, if required, use suitablePREPARATION: shopprimer. All damage of shopprimer and contamination from storage and fabrication should be
thoroughly cleaned prior to final painting. For repair and touch-up use HEMPALIN DANREX 52360.Maintenance: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove all rust and loose material byabrasive blasting or power tool cleaning. Dust off residues. Touch up to full film thickness.
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING None, HEMPALIN PRIMER 12050 or according to specification.COAT:
SUBSEQUENT HEMPALIN DANREX 52360 is normally used as a self-contained system.COAT: May be recoated with oil or alkyd based paints according to specification, eg:
Interior: HEMPALIN HOLD PAINT 51560.Exterior: (HEMPALIN UNDERCOAT 42460 followed by) alkyd-based finishing coat(s).
REMARKS: Certificates have been issued under the former quality number 5236.Before recoating after exposure in contaminated environment, clean surface thoroughly by (highpressure) fresh water hosing and allow to dry.
Thinning: THINNER 08080 may be used for spray application, however, with a certain risk of wrinkling of apreceding fresh HEMPALIN coat.
Note: HEMPALIN DANREX 52360 is for professional use only.
Issued: October 1999 - 5236010670CO011HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5236010670CO011
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataDataProductHEMPEL'S QD ENAMEL 530QA
Description: HEMPEL'S QD ENAMEL 530QA is a medium oil alkyd based fast drying enamel withexcellent gloss, colour retention, weather and abrasion resistance.
Recommended use: As a general purpose, on-line production finishing coat where a gloss finish is required.
PHYSICAL CONSTANTS:Colours/Shade nos: Blue/370QAFinish: GlossyVolume solids: 40%Theoretical spreading rate: 13.3 m²/litre - 30 micron* Flash point: 30°C/88°F Pensky closed cupSpecific gravity: 1.02 kg/litre Dry to touch: 30 minutes (20°C)
*The theoretical spreading rate has been calculated for the stated volume solids and dryfilm thickness.A practical spreading rate will depend on the actual dry film thickness, the nature of thesubstrate, and the relevant consumption factor.The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes".
APPLICATION DETAILS:Application method: Brush Air sprayThinner (max. vol.): 08230(5%) 08030(10%)Cleaning of tools: 08230 08030Indicated film thickness, dry: 30 micronIndicated film thickness, wet: 75 micronRecoat interval, min: 8 hours (20°C)Recoat interval, max: 5 days (20°C)
Surface condition: The surface shall be free of all grease, oil, salts, etc. Remove mill scale, loose rust,etc. By abrasive blast cleaning (Sa 2 minimum) or by mechanical cleaning (St 3minimum).
Remarks: Use only where application and drying can proceed at temperatures above 5°C, prefera-bly above 10°C.
Drying data given is on the assumption that proper ventilation and relative humiditybelow 65% is provided.
Note: HEMPEL'S QD ENAMEL 530QA is for professional use only.
SAFETY: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 530QA370QA
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPALIN®DECKPAINT 53240
Description: HEMPALIN DECKPAINT 53240 is a quick-drying, styrenated alkyd paint. Hardwearing andresistant to sunlight, salt water, and to oil splashes, but not to aromatic hydrocarbons,such as certain types of petrol (gasoline). For a skid-proof surface, see REMARKSoverleaf.
Recommended use: As a general purpose finishing coat, interior and exterior, on steel decks, stairways,catwalks, etc., in mildly to moderately corrosive environment.
Service temperatures: Maximum, dry: 120°C/248°F.
Certificates/Approvals: Approved as a low flame spread material by Danish and German authorities accordingto IMO resolution MSC 61 (67).Has a German and Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Green/40640 Red/50630Finish: Semi-gloss Semi-glossVolume solids, %: 42 ± 1 41 ± 1Theoretical spreading rate: 14.0 m²/litre - 30 micron 13.7 m²/litre - 30 micron
561 sq.ft./US gallon - 1.2 mils 548 sq.ft./US gallon - 1.2 milsFlash point: 28°C/82°F 28°C/82°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallon 1.1 kg/litre - 9.2 lbs/US gallonDry to touch: 1 (approx.) hour at 20°C/68°F 1 (approx.) hour at 20°C/68°FV.O.C.: 490 g/litre - 4.1 lbs/US gallon 495 g/litre - 4.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max. vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .018"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 30 micron/1.2 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 2 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: 4 hours (20°C/68°F) (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5324040640CO016
HEMPALIN DECKPAINT 53240
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPALIN PRIMER 12050 or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: Certificates have been issued under the former quality number 5324.Recoating: Recoating should take place when the first coat is dry and within 4 hours. If this interval is
exceeded, do not recoat until after two weeks. No maximum interval for adhesion.Before recoating after exposure in contaminated environment, clean surface thoroughly by (highpressure) fresh water cleaning and allow to dry.If a skid-proof surface is desired, sprinkle HEMPEL’S ANTI-SLINT 67500 evenly over the first coat ofHEMPALIN DECKPAINT 53240 while still wet. (Consumption: approximately 7.5 kg 67500 to 20litres of paint). When the paint is dry, sweep up surplus grit and apply a second coat of HEMPALINDECKPAINT 53240.Anti-skid properties can also be attained by mixing 1.0 kg of HEMPEL'S ANTI-SLIP BEADS 67420into 20 litre of HEMPALIN DECKPAINT 53240.
Note: HEMPALIN DECKPAINT 53240 is for professional use only.
Issued: October 1999 - 5324040640CO016HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5324040640CO016
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATHANE®ENAMEL 55100BASE 55109 with CURING AGENT 95370
Description: HEMPATHANE ENAMEL 55100 is a two-component, high-gloss acrylic polyurethaneenamel with good gloss and colour retention.
Recommended use: As a glossy decorative finishing coat on a variety of substrates such as steel,aluminium, glassfibre, reinforced polyester, plywood, hardwood etc. in severelycorrosive atmospheric environment.Minimum temperature for curing is -10°C/14°F.
Service temperatures: Maximum, dry: 120°C/248°F (see REMARKS overleaf).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000*Finish: High-glossVolume solids, %: 52 ± 1Theoretical spreading rate: 14.9 m²/litre - 35 micron
596 sq.ft./US gallon - 1.4 milFlash point: 31°C/88°FSpecific Gravity: 1.3 kg/litre - 10.8 lbs/US gallonSurface dry: 2½ (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 4-5 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 440 g/litre - 3.7 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 55100: Base 55109 : Curing agent 95370
7 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): See REMARKS overleaf See REMARKS overleaf 08080 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .017"-.019"Nozzle pressure: 75-100 bar /1100 -1450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080 or 08510Indicated film thickness, dry: 35 micron/1.4 milIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5510010000CO005
HEMPATHANE ENAMEL 55100
APPLICATION The surface must be completely clean and dry at the time of application, and its temperature mustAND CURING be above the dew point to avoid condensation. Minimum temperature for curing is -10°C/14°F.CONDITIONS: At the freezing point and below, be aware of the risk of ice on the surface which will hinder the
adhesion. Light rain, high humidity and/or condensation during application and the following 16hours (20°C/68°F) may adversely affect the film formation. The humidity of plywood/hardwoodshould not exceed 16% w/w.In confined spaces provide adequate ventilation during application and drying.
PRECEDING COAT: HEMPADUR HI-BUILD 45200/45201, HEMPADUR 45304, HEMPADUR MASTIC 45880 or accordingto specification.
SUBSEQUENT COAT: None.REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Service At service temperatures above 100°C/212°F, slight discoloration may be expected.temperatures:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is20-40 micron/0.8 -1.6 mils.
Thinning: The type and amount of thinner depend on application conditions, application method,temperature, ventilation, and substrate. THINNER 0808 is recommended in general. THINNER08510 may be used alternatively depending on local conditions.Airless spray: 15-20% thinning is recommended. Under extreme conditions more than 25% may benecessary to obtain satisfactory film formation.Conventional air spray: Dilute to a viscosity of 17-20 s/DIN 4 (approx 35% by volume). Use lowestpossible air pressure and a small nozzle.For both kinds of spray application the best result is obtained by applying a mist coat ofHEMPATHANE ENAMEL 55100 at first, and then 2-15 minutes later apply to full film thicknessgiving a uniform film formation. Do not exaggerate the film thickness.
2 months3 months(6 months)(6 months)(6 months)Max*
6 hours8 hours16 hours1½ day3 daysMinRecoating interval,recoating 55100 with 55100
5 days7 days14 days32 days(2 months)Fully cured, 70% RH
12 hours16 hours32 hours3 days(7 days)Resist condensing humidity/ light showers after:
3 hours5 hours9 hours20 hours45 hoursDry to touch, approx.
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-10°C/14°FSurface temperature
Physical data versus temperatures (35 micron/1.4 mil dry film thickness - sufficient ventilation):Recoatingand drying/curingtime:
*The maximum recoating intervals apply to surfaces exposed to very severe conditions of periodical immersion, heavycondensa-tion, great variations in temperatures, chemical attack and/or abrasion during service life of the coating system. Underother conditions no maximum recoating interval. A completely clean surface is anyhow mandatory to ensure intercoat adhesion,especially at long recoating intervals. Any dirt,oil, and grease has to be removed. e.g. with suitable detergent. Salts to beremoved by fresh water hosing. To check an adequate quality of the surface cleaning a test patch is recommended beforeactual recoating.If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion. In the case of recoating with other paint materials maximum will be 1-3 days(20°C/68°F) depending on type.
Notes: CURING AGENT 95370 is sensitive to moisture. Store in a dry place and keep the can tightly closeduntil use. Open curing agent cans with caution as overpressure might exist. Even small traces ofwater in the mixed paint will reduce the pot-life and result in film defects.HEMPATHANE ENAMEL 55100 is for professional use only.
Issued: April 2002 - 5510010000CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5510010000CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATHANE®TOPCOAT 55210BASE 55219 with CURING AGENT 95370
Description: HEMPATHANE TOPCOAT 55210 is a two-component, semi-gloss acrylic polyurethanecoating with good gloss and colour retention.
Recommended use: As a finishing coat for protection of structural steel in severely corrosive atmosphericenvironment, where light-fastness and gloss retention are required.Minimum temperature for curing is -10°C/14°F.
Service temperatures: Maximum, dry: 120°C/248°F (see REMARKS overleaf).
Certificates/Approvals: Approved as a low flame spread material by German and Italian authorities according toIMO resolution MSC 61 (67).Has a German EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000* Blue/30840*Finish: Semi-gloss Semi-glossVolume solids, %: 52 ± 1 51 ± 1Theoretical spreading rate: 10.4 m²/litre - 50 micron 10.2 m²/litre - 50 micron
417 sq.ft./US gallon - 2 mils 409 sq.ft./US gallon - 2 milsFlash point: 33°C/92°F 33°C/92°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallon 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 2½ (approx.) hrs at 20°C/68°F (ISO 1517) 2½ (approx.) hrs at 20°C/68°F (ISO 1517)Dry to touch: 8 (approx.) hours at 20°C/68°F 8 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°F 7 days at 20°C/68°FV.O.C.: 440 g/litre - 3.7 lbs/US gallon 450 g/litre - 3.7 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 55210: Base 55219 : Curing agent 95370
7 : 1 by volumeApplication method: Airless spray BrushThinner (max. vol.): See REMARKS overleaf 08080 (5%)Pot life: 4 hours (20°C/68°F)Nozzle orifice: .017"-.019"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080 or 08510Indicated film thickness, dry: 50 micron/2 mils (See REMARKS overleaf)Indicated film thickness, wet: 100 micron/4 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5521010000CO009
HEMPATHANE TOPCOAT 55210
APPLICATION The surface must be completely clean and dry at the time of application, and its temperature mustAND CURING be above the dew point to avoid condensation. Minimum temperature for curing is -10°C/14°F.CONDITIONS: At the freezing point and below, be aware of the risk of ice on the surface which will hinder the
adhesion. High humidity and/or condensation during application and the following 16 hours(20°C/68°F) may adversely affect the film formation.In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPADUR 45141/45143, HEMPADUR HI-BUILD 45200/45201, HEMPADUR MASTIC 45880 orCOAT: according to specification.
SUBSEQUENT None.COAT:
REMARKS: Certificate has been issued under the former quality number 5521.Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Service At service temperatures above 100°C/212°F, slight discoloration may be expected.temperatures:Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoating interval. Normal range is40-60 micron/1.6-2.4 mils.
Thinning: The type and amount of thinner depend on application conditions, application method,temperature, ventilation, and substrate. THINNER 08080 is recommended in general. THINNER08510 may be used alternatively depending on local conditions.Airless spray: 5-15% thinning is recommended. Under extreme conditions up to more than 20%may be necessary to obtain satisfactory film formation.The best result is obtained by applying a mist coat of HEMPATHANE ENAMEL 55210 at first, andthen 2-15 minutes later apply to full film thickness giving a uniform film formation. Do notexaggerate the film thickness.
Electrostatic spray: 10% thinning with specified thinner is recommended. Please contact HEMPEL for further advice.
NoneNoneNoneNoneNoneMax
12 hours16 hours32 hours3 days6 daysMinRecoating interval,recoating 55210 with 55210
5 days7 days14 days32 days(2 months)Fully cured, 70% RH
12 hours16 hours32 hours3 days(7 days)Resist condensing humidity/ light showers after*:
6 hours8 hours16 hours36 hours3 daysDry to touch, approx.
30°C/86°F20°C/68°F10°C/50°F0°C/32°F-10°C/14°FSurface temperature
Physical data versus temperatures:Recoatingand drying/curingtime:
*Faster drying and curing may be obtained by using an "accelerator" - consult HEMPEL for further advice.
A completely clean surface is mandatory to ensure intercoat adhesion, especially at longrecoating intervals. Any dirt,oil, and grease has to be removed, e.g. with suitable detergent.Salts to be removed by fresh water hosing. To check an adequate quality of the surface cleaninga test patch is recommended before actual recoating.
Notes: CURING AGENT 95370 is sensitive to moisture. Store in a dry place and keep the can tightly closeduntil use. Open curing agent cans with caution as overpressure might exist. Even small traces ofwater in the mixed paint will reduce the pot-life and result in film defects.
HEMPATHANE TOPCOAT 55210 is for professional use only.
Issued: April 2002 - 5521010000CO009HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5521010000CO009
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATHANE®ENAMEL 55280CURING AGENT 95370
Description: HEMPATHANE ENAMEL 55280 is a high gloss two component acrylic polyurethaneenamel with excellent gloss and colour retention. Resistant to water, impact, abrasionand marine and industrial corrosive atmosphere.
Recommended use: As a finishing coat on a wide variety of rigid substrates such as steel, aluminium,glassfibre reinforced polyester, plywood and hardwood, where light fastness and glossretention are desired.
PHYSICAL CONSTANTS:Finish: High-glossColours: WhiteShade Numbers: 10000Volume Solids: 48%Theoretical Spreading 9.6 m²/litre - 50 micronsRate: 385 sq.ft./US gallon - 8 milsFlash Point: 31ºC/88ºF A-Pensky, closed cupSpecific Gravity: 1.2 kg/litre
10.3 lbs/US gallonDry to Touch: 3-4 hours at 20ºC/68ºFFully Cured: 7 (approx) days at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Mixing Ratio: Base : Hempathane Enamel 55289 6 parts by volume
Curing Agent : 95370 1 part by volumeApplication Method: Air Spray BrushThinner: 08900 (15%) Do not dilutePot-life: 8 hours (20ºC/68ºF)Cleaning of Tools: Hempel's Tool Cleaner 99610Indicated film thickness, wet: 100 micron/4 milsIndicated film thickness, dry: 50 micron/2 mils (See REMARKS overleafRecoat interval, min: 12 hours (20ºC/68ºF)Recoat interval, max: 3 months (20ºC/68ºF) (See REMARKS overleaf)
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed. As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided, respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5528010000
HEMPATHANE ENAMEL 55280
Surface Preceding coats should be sound and tightly adhering. Remove oil and grease by detergentPreparation: wash and salts by high pressure fresh water hosing and allow surface to dry. Remove rust and
loose material by abrasive blasting or power tool cleaning. Dust off the surface. Touch up to fullsystem before overcoating with HEMPATHANE ENAMEL 55280.
Application Clean and dry surface with a temperature above the dew point to avoid condensation. Conditions: Minimum temperature for curing is 2ºC/35ºF. High humidity during application and for 24 hours
thereafter will adversely affect film formation.
Preceding Coat: HEMPADUR HI BUILD 45200 or according to specification. In general HEMPATHANE ENAMEL55280 can be applied over epoxy, polyester and urethane coatings, even after aging. Aged alkydcoatings may also be overcoated. In any case, a test patch is recommended to determine if liftingor adhesion will be a problem. For heavy duty service, roughening of existing chemically curedcoating may be necessary before topcoating with HEMPATHANE ENAMEL 55280.
Subsequent Coat: None, or according to specification.
Remarks: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence minimum recoating interval. The indicatedmaximum recoating interval refers to overcoating with itself (for overcoating with other qualities,ask for special guidelines). The interval applies to surfaces exposed to periodical immersion,heavy condensation, chemical attack and / or abrasion during service life of the coating system.Under other conditions no maximum interval. In any case a completely clean surface is mandatoryto ensure intercoat adhesion, especially at long recoating intervals. Any dirt, oil and grease has tobe removed, e.g. by detergent cleaning, followed by high pressure fresh water hosing. Salts to beremoved by fresh water hosing. To ensure an adequate quality of the surface cleaning, a testpatch is recommended before actual overcoating. If maximum recoating interval (see above) isexceeded, roughening of the surface is necessary to ensure intercoat adhesion.
CURING AGENT 95370 is sensitive to moisture. Store in a cool, dry place. Keep the can tightlyclosed after use. Trace of water in the mixed paint will reduce the pot-life.
Note: HEMPATHANE ENAMEL 55280 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5528010000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S GALVOTOP 55700
Description: HEMPEL’S GALVOTOP 55700 is a solvent borne, one-component, self-curing inorganicsilicate topcoat, pigmented with inert pigments. It forms a hard inorganic film with goodresistance to many petrochemical products, to nuclear radiation and to hightemperatures.
Recommended use: 1. As a topcoat on HEMPEL'S GALVOSIL 15700 and similar zinc silicate primers for long-term protection of steel structures exposed to nuclear radiation and/or high temperatures up to 400°C/752°F.
2. Selfprimed for colouring purposes on blast cleaned steel at temperatures up to 600°C/1100°F on areas not exposed to abrasion, impact or water/condensing humidity.
Service temperatures: Maximum dry surface temperature is approx. 400°C/752°F as dictated by theunderlying zinc silicate primer. (Please consult Data Sheet for HEMPEL'S GALVOSIL15700). The white shade may, however, turn darker when heated above 250°C/482°F.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000Finish: FlatVolume solids: 52%Theoretical spreading rate: 6.9 m²/litre - 75 micron
278 sq.ft./US gallon - 3.0 milFlash point: 14°C/57°FSpecific gravity: 1.4 kg/litre
11.7 lbs/US gallonSurface dry: 30 (approx) minutes at 20°C/68°F (ISO 1517)Dry to touch: 2-4 hours at 20°C/68°F (75% RH)Fully cured: 3 (approx) days at 20°C/68°F (75% RH)V.O.C.: 635 g/litre - 5.3 lbs/US gallon
Shelf life: 9 months from time of production (25°C/77°F).Shelf life is dependent on storage temperature. Shelf life is reduced at storagetemperatures above 25°C/77°F. Do not store above 40°C/104°F.Shelf life is exceeded if the liquid is gelled or if the mixed product forms gels beforeapplication.
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempel Book.
APPLICATION DETAILS:Application method: Air spray BrushThinner (max.vol.): 08700 (10%) 08700 (5%)Cleaning of tools: THINNER 08700Indicated film thickness, dry: 75 micron/3.0 mils (See REMARKS overleaf)Indicated film thickness, wet: 150 micron/6.0 milsRecoat interval, min.: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5570010000CS002
HEMPEL’S GALVOTOP 55700
SURFACE As topcoat: Remove oil and grease etc. thoroughly with suitable detergent. Remove white rustPREPARATION: formation, salts and other contaminants by high pressure fresh water cleaning, if necessary by the
assistance of scrubbing with stiff nylon brushes.Selfprimed: Remove oil, grease, etc. with suitable detergent. Remove salts and othercontaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½.
APPLICATION Apply on a clean and dry surface with a temperature above the dew point to avoid condensation. CONDITIONS: In confined spaces provide adequate ventilation during application and drying. Use only where
appliction and curing can proceed at temperatures above 0°C/32°F. The temperature of thesurface and that of the paint itself must also be above this limit.
PRECEDING HEMPEL'S GALVOSIL 15700 or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS:Film thicknesses: It is recommended to avoid too high thicknesses of the paint. May be specified in another film
thickness than indicated. This will alter spreading rate and may influence drying time and recoatinterval. Normal range is 40-75 micron/1.6-3.0 mils.
Curing: Curing needs minimum 50%, preferably above 65% relative humidity. At 75% relative humidity thecoating is fully cured in 3 days (20°C/68°F).
First exposure Do not expose the paint system to severe heat before it is fully cured.to heat:Recoating: HEMPEL'S GALVOTOP 55700 is normally recommended in a single coat. Touch-up of insufficient
film thickness can be done after minimum 30 minutes (20°C/68°F). No maximum recoat interval,but surfaces must be completely clean of all contamination.
Shelf life/storage: HEMPEL'S GALVOTOP 55700 is sensitive to moisture. Store in a dry place and keep cans tightlyclosed until use. Shelf life is reduced at temperatures above 25°C/77°F. Do not store attemperatures above 40°C/105°F.
Note: HEMPEL’S GALVOTOP 55700 is for professional use only.
Issued: August 1997-5570010000CS002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5570010000CS002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ENAMEL 55850CURING AGENT 97550
Description: HEMPEL’S ENAMEL 55850 is a two-component oxiraneester based topcoat. Resistantto splashes of petrol, mineral oils, and mild acids. VOC-compliant.
Recommended use: As a finishing coat in two-pack anti-corrosive systems where safety rules preclude theuse of isocyanate cured paints. In moderately to severely atmospheric environments.
Service temperatures: Maximum, dry: 140°C/282°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000*Finish: GlossyVolume solids, %: 64 ± 1Theoretical spreading rate: 10.7 m²/litre - 60 micron
428 sq.ft./US gallon - 2.4 milsFlash point: 43°C/105°FSpecific gravity: 1.4 kg/litre
11.7 lbs/US gallonSurface dry: 3 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 8-10 hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 340 g/litre - 2.8 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 55850: Base 55859 : Curing agent 97550
2 : 1 by volumeApplication method: Airless spray Air spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Pot life: 8 hours (20°C/68°F)Nozzle orifice: .018"-.021"Nozzle pressure: 175 bar/2500 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 60 micron/2.4 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 24 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5585010000CO003
HEMPEL’S ENAMEL 55850
APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the surface and that of the paint itself must also be above this limit.
Apply only on a dry and completely clean surface with a temperature above the dew point to avoidcondensation.In confined spaces provide adequate ventilation during application and drying.
PRECEDING According to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.This will alter spreading rate and may influence drying time and recoat interval. Normal range is50-75 micron/2.0-3.0 mils.
Recoating: Maximum recoat interval related to later conditions of exposure:
3 monthsNoneNone55850
SevereMediumMildRecoated with
(quality number only)
Atmospheric
20°C/68°FSteel temperature
A completely clean surface is anyhow mandatory to ensure intercoat adhesion, especially at longrecoat intervals. Any dirt, oil and grease has to be removed, e.g. with suitable detergent. Salts tobe removed by fresh water hosing. To check an adequate quality of the surface cleaning a testpatch is recommended before actual recoating.The test patch reveals insufficient intercoat adhesion, roughening of the surface is necessary.If the maximum recoat interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Gloss: A slight tendency to chalk in outdoor exposure does not detract from the protective properties.
Note: HEMPEL'S ENAMEL 55850 is for professional use only.
Issued: October 1999 - 5585010000CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5585010000CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATHANE®TOPCOAT 55910CURING AGENT 97050
Description: HEMPATHANE TOPCOAT 55910 is a very flexible, two-component polyurethane topcoat.
Recommended use: As a VOC-compliant, high-build finishing coat for protection of structural steel incorrosive environment, especially for maintenance purposes.
Service temperatures: Maximum, dry: 120°C/248°F (see REMARKS overleaf)
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000Finish: GlossyVolume solids, %: 66 ± 1Theoretical spreading rate: 6.6 m²/litre - 100 micron
265 sq.ft./US gallon - 4 milsFlash point: 31°C/88°FSpecific gravity: 1.5 kg/litre - 12.5 lbs/US gallonSurface dry: 3 (approx.) hours at 20°C/68°F (ISO 1517)Dry to touch: 5 (approx.) hours at 20°C/68°FFully cured: 7 days at 20°C/68°FV.O.C.: 330 g/litre - 2.7 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 55910: Base 55919 : Curing agent 97050
7 : 1 by volumeApplication method: Airless spray (see REMARKS overleaf) Brush (see REMARKS overleaf)Thinner (max.vol.): 08080 (5%) 08080 (5%)Pot life: 2 hours (20°C/68°F)Nozzle orifice: .017"-.021"Nozzle pressure: 175 bar/2540 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080/08880Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 150 micron/6 milsRecoat interval, min: 11 hours (20°C/68°F)Recoat interval, max: None (see REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5591010000CR001
HEMPATHANE TOPCOAT 55910
APPLICATION The surface must be completely clean and dry at the time of application, and its temperature mustCONDITIONS: be above the dew point to avoid condensation. Minimum temperature for curing is -10°C/14°F.
At the freezing point and below, be aware of the risk of ice on the surface which will hinder theadhesion. High humidity and/or condensation during application and the following 24 hours(20°C/68°F) may adversely affect the film formation.In confined spaces provide adequate ventilation during application and drying.
PRECEDING According to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS:Service At service temperatures above 90°C/176°F, HEMPATHANE TOPCOAT 55910 will become more soft.temperatures: Furthermore, discoloration may occur.Colours: Certain lead-free red and yellow colours may discolour when exposed to sulphide and chlorine
containing atmosphere.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
Normal range dry is minimum 75 micron/3 mils (undiluted), maximum 125 micron/5 mils. This willalter spreading rate and may influence drying time and recoat interval.
Recoat interval: Maximum recoating interval: A completely clean surface is mandatory to ensure intercoatadhesion, especially at long recoat intervals. Any dirt,oil, and grease has to be removed. e.g.with suitable detergent followed by (high pressure) fresh water cleaning. Salts to be removed byfresh water hosing.To check an adequate quality of the surface cleaning a test patch is recommended before actualrecoating.In case of recoating with other paint materials maximum will be 1-3 days (20°C/68°F) dependingon type.
Notes: CURING AGENT 97050 is sensitive to moisture. Store in a dry place and keep the can tightly closeduntil use. Open curing agent cans with caution as overpressure might exist. Even small traces ofwater in the mixed paint will reduce the pot life and result in film defects.
HEMPATHANE TOPCOAT 55910 is for professional use only.
Issued: July 2001 - 5591010000CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5591010000CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPAFLEX®ANTI-STAIN 56220
Description: HEMPAFLEX ANTI-STAIN 56220 is a modified finishing coat for epoxy and acrylic basedpaint systems. Physically drying. Resistant to salt water and splashes of aliphatichydrocarbons.A smooth surface and special chemical compounds minimize surface contaminationsuch as rust runners.
Recommended use: As an exterior finishing coat in HEMPATEX and HEMPADUR systems in moderately toseverely corrosive environment.
Service temperatures: Maximum, dry: 80°C/175°F (See REMARKS overleaf).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade Nos: Cream/20320 (Other shades according to assortment list)Finish: GlossyVolume solids, %: 36 ± 1Theoretical spreading rate: 10.3 m²/litre - 35 micron
412 sq.ft./US gallon - 1.4 milsFlash point: 23°C/73°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: 1 (approx) hr at 20°C/68°F (ISO 1517)Dry to touch: 3-4 hours at 20°C/68°FV.O.C.: 565 g/litre - 4.7 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Brush/RollerThinner (max. vol.): 08080 (5%) (See REMARKS overleaf)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 35 micron/1.4 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 4 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.Issued: October 1999
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5622020320CO001
HEMPAFLEX ANTI-STAIN 56220
APPLICATION As dictated by normal good painting practice. Dry and clean surface with a temperature aboveCONDITIONS: the dew point.In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPATEX, HEMPADUR qualities, or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS:Service As HEMPAFLEX ANTI-STAIN 56220 is a thermoplastic product, prolonged mechanical exposure attemperatures: temperatures above approx. 40°C/105°F may cause film indentation. When the temperature drops
below, the mechanical strength is recovered.Before recoating after exposure in contaminated environment, clean the surface thoroughly by highpressure fresh water hosing and allow to dry.
Airless spray: Airless spray application will be possible provided the following precautions are taken:Dilute the paint before application (approx 10%), avoid too high film thicknesses (ie not morethan 40 micron/1.6 mils). Use a spray method based on many passes with a fast movement ofthe spray gun. In this way a smooth, uniform appearance can be obtained.Recommended nozzle orifice: .017"-.019".Nozzle pressure: 150 bar/2200 psi.To check optimal spray conditions, a test patch is recommended prior to actual full-scaleapplication.
Note: HEMPAFLEX ANTI-STAIN 56220 is for professional use only.
Issued: October 1999 - 5622020320CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5622020320CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®BELT/DECK COATING 56240
Description: HEMPATEX BELT/DECK COATING 56240 is a quick-drying chlorinated rubber paint.Physically drying. Hardwearing and resistant to sunlight, salt water,splashes of mineraloils, of aliphatic solvents, and a number of chemicals. Not suited in contact with animaland vegetable oils or aromatic solvents. For service temperature range, see REMARKSoverleaf. For a skid-proof surface see REMARKS overleaf.
Recommended use: 1. As a finishing coat in the boottop area.2. As a general purpose finishing coat on steel decks, stairways, catwalks, etc., in
mildly to moderately corrosive environment.
PHYSICAL CONSTANTS:Finish: Semi-glossColours: Red/Grey Other shades according to assortment listShade Nos: 50630/11480Solids by Volume: 40%Theoretical spreading rate: 8 m²/litre - 50 microns
326 sq.ft./US gallon - 2.0 milsFlash Point: 26/79 C/F A-Pensky, closed cupSpecific Gravity: 1.2 kg/litre
10. lbs/US gallonDry to Touch: 3 - 4 hours at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle Orifice: 0.021" - 0.025"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08080Indicated film thickness, wet: 125 micron/5 milsIndicated film thickness, dry: 50 micron/2 milsRecoat interval, min: 4 hours (20ºC/68ºF)Recoat interval, max: None (See REMARKS overleaf)
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 56240 50630
HEMPATEX®BELT/DECK COATING 56240
Application As dictated by normal good painting practice.Conditions: In confined spaces provide adequate ventilation during application and drying.
Preceding Coat: Hempatex Primers or according to specification.
Subsequent Coat: None.
Remarks: Before overcoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
This product is thermoplastic. It tolerates up to 60ºC/140ºF in continuous service, non-continuousup to 80ºC/176ºF. Its mechanical properties will gradually be affected at temperatures aboveapproximately 40ºC/104ºF where a natural softening will commence making the paint film sensitiveto mechanical stress. When temperature drops below, mechanical strength is recovered. If askid-proof surface is desired, sprinkle Hempel's Anti-Slint 65700 evenly over the first coat ofHempatex Belt/Deck Coating 5624 while still wet. (Consumption: 7.5 kg 67500 to 20 litres ofpaint). When the paint is dry, sweep up surplus grit and apply a second coat of HempatexBelt/Deck Coating 56240.
Anti-skid properties can also be attained by mixing 1.2kg of Hempel's Anti Slip Beads 67420 into20 litres of Hempatex Beld/Deck Coating 56240. Approved as a low flame spread materialconforming to the SOLAS Convention.
Note: HEMPATEX BELT/DECK COATING 56240 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 56240 50630
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®DECK COATING 56250 NON-SKID
Description: HEMPATEX DECK COATING 56250 NON-SKID is a quick-drying chlorinated rubber paint,containing an anti-slip aggregate. Physically drying. Resistant to abrasion, seawaterand the weather. Not suited in contact with animal and vegetable oils or aromaticsolvents. For service temperature range, see REMARKS overleaf.
Recommended use: As a skid-proof finishing coat on steel decks, steel and concrete floors, stairways,footbridges, in mildly to moderately corrosive marine and industrial environment.
PHYSICAL CONSTANTS:Finish: FlatColour: Green Other shades according to assortment listShade No: 40640Solids by Volume: 45%Theoretical Spreading Rate: 9 m²/litre - 50 microns
361 sq.ft./US gallon - 2.0 milsFlash Point: 26C/79F A-Pensky, closed cupSpecific Gravity: 1.0 kg/litre
8.3 lbs/US gallonDry to Touch: 3 - 4 hours at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle Orifice: 0.023" - 0.027"Nozzle Pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Thinner 08080
Indicated film thickness, wet: 100-125 micron/4-5 milsIndicated film thickness, dry: 50 micron/2 mils
Recoat interval, min: When dryRecoat interval, max: None (See REMARKS overleaf
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5625040640
HEMPATEX DECK COATING 56250 NON-SKID
Application As dictated by normal good painting practice.Conditions: In confined spaces provide adequate ventilation during application and drying.
Preceding Coat: Hempatex Primers or according to specification.
Subsequent Coat: None.
Remarks: Before overcoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
This product is thermoplastic. It tolerates up to 60ºC/140ºF in continuous service, non-continuousup to 80ºC/176ºF. Its mechanical properties will gradually be affected at temperatures aboveapproximately 40ºC/104ºF where a natural softening will commence making the paint film sensitiveto mechanical stress. When temperature drops below, mechanical strength is recovered.
Note: HEMPATEX DECK COATING 56250 NON-SKID is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5625040640
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPATEX®ENAMEL 56360
Description: HEMPATEX ENAMEL 56360 is a finishing coat based on acrylic resin andnon-chlorinated plasticizer for optimum gloss and colour retention. Physically drying.Resistant to salt water, splashes of aliphatic hydrocarbons and animal and vegetableoils.
Recommended use: As an interior and exterior finishing coat in HEMPATEX systems in moderately toseverely corrosive environment.
Service temperatures: Maximum, dry: 80°C/176°F (see REMARKS overleaf).
Certificates/Approvals: Tested for non-contamination of grain cargo at the Newcastle Occupational Health,Great Britain.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Black/19990* Orange/50040*Finish: Semi-gloss Semi-glossVolume solids, %: 31 ± 1 33 ± 1Theoretical spreading rate: 8.9 m²/litre - 35 micron 9.4 m²/litre - 35 micron
355 sq.ft./US gallon - 1.4 mils 378 sq.ft./US gallon - 1.4 milsFlash point: 25°C/77°F 25°C/77°FSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallon 1.0 kg/litre - 8.3 lbs/US gallonSurface dry: 1 (approx.) hr at 20°C/68°F (ISO 1517) 1 (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 3-4 hours at 20°C/68°F 3-4 hours at 20°C/68°FV.O.C.: 610 g/litre - 5.1 lbs/US gallon 595 g/litre - 4.9 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray Brush/RollerThinner (max. vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .017"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 35 micron/1.4 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 4 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5636019990CO010
HEMPATEX ENAMEL 56360
APPLICATION As dictated by normal good painting practice. Dry and clean surface at a temperature above theCONDITIONS: dew point.
In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPATEX HI-BUILD qualities, or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: Certificate has been issued under the former quality number 5636.Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Service As HEMPATEX ENAMEL 56360 is a thermoplastic product, prolonged direct contact attemperatures: temperatures
above approx. 40°C/104°F may cause film indentation. When the temperature drops below, themechanical strength is recovered.
Film thicknesses: A series of maintenance jobs may result in build up of a too high total film thickness which maycause blister formation due to "entrapped" solvents. As each coat may also retain solvents, it isgenerally recommended not to apply HEMPATEX ENAMEL 56360 in excessive film thickness.
Recoating: Before recoating after exposure in contaminated environment, clean the surface thoroughly by highpressure fresh water hosing and allow to dry.Overlapping with certain other paints may cause cracking. Refer to Remarks of relevant PaintingSpecification.
Skid-proof If a skid-proof surface is desired, sprinkle HEMPEL'S ANTI-SLINT 67500 evenly on the first coat ofsurfaces: HEMPATEX ENAMEL 56360 while still wet (consumption approx. 2.5 kg/5.5 lbs to 25 m²/270
sq.ft.). When the paint is dry, sweep up surplus grit and apply a second coat of HEMPATEX ENAMEL56360. Antiskid properties can also be obtained by mixing 1.0 kg of HEMPEL'S ANTISLIP BEADS67420 into 20 litres of HEMPATEX ENAMEL 56360.
Note: HEMPATEX ENAMEL 56360 is for professional use only.
Issued: April 2002 - 5636019990CO010HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5636019990CO010
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPATEX®56430
Description: HEMPATEX 56430 is a physically drying paint with optimum colour retention. Based onacrylic resin alkyd. Resistant to salt water, splashes of aliphatic solvents, animal andvegetable oils.
Recommended use: 1. As an exterior finishing coat on containers.2. As a finishing coat in HEMPATEX systems in moderately to severely corrosive
environment.
Service temperatures: Maximum, dry: 80°C/175°F (see REMARKS overleaf).
Availability: Normally only available on orders for container newbuildings.
PHYSICAL CONSTANTS:Colours/Shade nos: Orange/54406*Finish: FlatVolume solids, %: 39 ± 1Theoretical spreading rate: 9.8 m²/litre - 40 micron
391 sq.ft./US gallon - 1.6 milsFlash point: 24°C/75°FSpecific gravity: 1.2 kg/litre
10.0 lbs/US gallonSurface dry: 15 (approx.) minutes at 20°C/68°F (ISO 1517)Dry to touch: 1 (approx.) hour at 20°C/68°FV.O.C. 545 g/litre - 4.5 lbs/US gallon
*Concerning other shades, reference is made to HEMPEL'S CONTAINER COLOUR CARD.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max. vol.): 08080 (5%) 08080 (15%) 08080 (5%)Nozzle orifice: .017"-.021"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 40 micron/1.6 mils (See REMARKS overleaf)Indicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 1 hour (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5643054406CS002
HEMPATEX 56430
APPLICATION The surface must be completely clean and dry, its temperature must be above the dew point toCONDITIONS: avoid condensation.
In confined spaces provide adequate ventilation during application and drying.
PRECEDING HEMPADUR PRIMER 15300, HEMPATEX HI-BUILD 46410 or according to specification.COAT:
SUBSEQUENT None, or as per specification depending on area of use.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.As HEMPATEX 56430 is a thermoplastic product, prolonged mechanical exposure at temperaturesabove approx. 40°C/104°F may cause film indentation. When temperature drops below, themechanical strength is recovered.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.Normal range is 30-50 micron/1.6-2 mils.This will alter spreading rate and may influence dryingtime and recoat interval. A series of maintenance jobs may result in build up of a too high total filmthickness which may cause blister formation due to "entrapped" solvents. As each coat may alsoretain solvents, it is generally recommended not to apply HEMPATEX HI-BUILD 56430 in excessivefilm thickness.
Recoating: In case of multicoat application minimum recoat interval is influenced by the actual film thicknessand number of coats applied. Reference is made to the corresponding painting specification.No maximum recoat interval, but before recoating after exposure in contaminated environment,clean the surface thoroughly by high pressure fresh water hosing and allow to dry.
Note: HEMPATEX HI-BUILD 56430 is for professional use only.
Issued: April 2002 - 5643054406CS002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5643054406CS002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S VEHICLE ENAMEL 564QA
Description: HEMPEL'S VEHICLE ENAMEL 564QA is an alkyd based enamel with excellent gloss,colour retention and weather resistance. It is flexible and resistant to petrol, salt waterand other aliphatic hydrocarbons.
Area of use: Exterior
Substrates: Steel.As a general purpose finishing coat on exterior steel surfaces, mainly used a finishinglacquer in the automotive industry.
PHYSICAL CONSTANTS:Colours/Shade nos: White Black Maroon Yellow Blue Red
10000 19990 579QA 21910 30140 50800Volume solids: 45% 40% 45% 45% 40% 40%Finish: GlossyTheoretical spreading rate: 15 m2/litre - 30 micron*Flash point: 30°C A-Pensky closed cupSpecific gravity: 1.2 kg/litreDry to touch: 1 hour (20°C)
*The theoretical spreading rate has been calculated for the stated volume solids and dryfilm thickness.A practical spreading rate will depend on the actual dry film thickness, the nature of the substrate and the relevant consumption factor.
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory notes".
APPLICATION DETAILS:Application method: Air spry BrushThinner (max. vol.): 08080(10%) 08080 (5%)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 30 micron/1.2 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 5 hours (20°C)Recoating interval, max: 8 hours (20°C)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local or national safety regulation. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 564QA10000
HEMPEL'S VEHICLE ENAMEL 564QA
Surface condition: Before overcoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water housing and allow to dry.
Preceding coat: Hempel's Uni Primer 13140
Remarks: Drying data is given on the assumption that proper ventilation is provided.
Note: HEMPEL'S VEHICLE ENAMEL 564QA is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 564QA10000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPEL'S HI-VEE®56540
Description: HEMPEL'S HI-VEE 56540 is a non-hiding, but strongly day-light reflecting acrylic paintwith fluorescent pigments which give intense colour impression and high visibility(HI-VEE). It has no effect in darkness, and it needs HEMPEL'S HI-VEE LACQUER 06520on top in order to improve the light fastness.
Recommended use: For life-saving equipment and for warning purposes such as protruding or movingobjects, etc.
Service temperatures: Maximum, dry: 80°C/176°F (see REMARKS overleaf).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shades nos: Orange/50180*Finish: Semi-glossVolume solids, %: 44 ± 1Theoretical spreading rate: 11.0 m²/litre - 40 micron
441 sq.ft./US gallon - 1.6 milsFlash point: 38°C/100°FSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonDry to touch: 1-2 hours at 20°C/68°FV.O.C.: 450 g/litre - 3.7 lbs/US gallon
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max. vl.): 08230 (5%) 08230 (15%) 08230 (5%)Nozzle orifice: .015"-.018"Nozzle pressure: 150 bar/2200 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08230Indicated film thickness, dry: 40 micron/1.6 milsIndicated film thickness, wet: 100 micron/4 milsRecoat interval, min: 2 hours (20°C/68°F)Recoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5654050180CO002
HEMPEL'S HI-VEE 56540
APPLICATION As dictated by normal good painting practice.CONDITIONS: In confined spaces provide adequate ventilation during application and drying.
PRECEDING White, preferably flat HEMPATEX paint or according to specification. HEMPEL'S HI-VEE 56540 isCOAT: applied on a white surface in order to obtain optimum light reflection.
SUBSEQUENT HEMPEL'S HI-VEE LACQUER 06520, which contains ultra-violet radiation absorbing filter.COAT:
REMARKS: As HEMPEL'S HI-VEE 56540 is a thermoplastic product, prolonged mechanical exposure attemperatures above approx. 40°C/104°F may cause film indentation. When temperature dropsbelow, the mechanical strength is recovered.Do not expose liquid paint to temperatures above 40°C/104°F neither during storage nor inconnection with application.
Note: HEMPEL'S HI-VEE 56540 is for professional use only.
Issued: October 1999 - 5654050180CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5654050180CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ACRYLIC STOVING ENAMEL 567QA
Description: HEMPEL’S ACRYLIC STOVING ENAMEL 567QA is a thermosetting, acrylic, self-primedenamel containing rust-inhibiting, zinc phosphate pigments.
Recommended use: As a self-primed, hard-wearing finishing coat on steel panel boards and householdappliances, for exterior and interior use.
PHYSICAL CONSTANTS:
Colours/Shade nos: White/10000 (60-70 units @ 60º)Finish: GlossyVolume solids: 40%Theoretical spreading rate: 16.0 m²/litre - 25 micron
641 sq.ft./US gallon - 1 milsFlash point: 27°C/81°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonDry to touch: 15 minutes at 180°C/356°F
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:
Application method: Air sprayThinner (max.vol.): 08080 (15%)Nozzle orifice: 1.2 mmCleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 25 micron/1 milsIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: When dryRecoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 567QA1000000001
HEMPEL’S ACRYLIC STOVING ENAMEL 567QA
SURFACE Galvanized Steel: Degrease Hempel’s Light Clean 99350 and fresh water. Rinse with freshwater.
PREPARATION: Remove possible zinc salts by light abrasive sweeping or power tool cleaning. If the steel isprepared by acid pickling method, make sure that rinsing is carried out with fresh, clean water.Before applying any paint, the surface must be completely dry. Pay special attention to water andmoisture in crevices and voids.
APPLICATION Apply to specified film thickness. Bake at 180ºC/356ºF for approximately 15 minutes. When theCONDITIONS: painted substrate has reached room temperature after stoving, it is fully cured. Provide adequate
ventilation during application and drying.
PRECEDING None.COAT:
SUBSEQUENT None, or as per specification.COAT:
REMARKS: Before overcoating after exposure in contaminated environment, clean surface thoroughly. Lightsanding will ensure proper intercoat adhesion.
Note: HEMPEL’S ACRYLIC STOVING ENAMEL 567QA is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 567QA1000000001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S TRAFFIC & AIRFIELD MARKING PAINT 56880(FEDERAL STANDARD TT-P-85E)
Description: HEMPEL'S TRAFFIC AND AIRFIELD MARKING PAINT 56880 is a colour stable, styrenatedalkyd based coating which is especially suited for asphalt and concrete. It dries quicklyand causes no bleeding. It forms a tough film, resistant to wear and impact, water,petrol (gasoline), mineral oils etc.
Recommendation: As a marking paint on cement, concrete, bituminous pavement, tiles, etc., andpreviously painted areas of this type. Can be used with or without glass beads.
PHYSICAL CONSTANTS:Finish: FlatColours: White Yellow Other shades according to assortment listShade Number: 10000 21410Volume by Solids: 58% 58%Theoretical Spreading 3.1 3.1 m²/litre - 190 micronsRate: 122 122 fts/US gallon - 7.6 milsFlash Point: 27/82 C/F A-Pensky, closed cupSpecific Gravity: 1.5 1.5 kg/litre
12.5 12.5 lbs/US gallonDry to Touch: 30 30 min. at 20ºC/68ºF
APPLICATION DETAILS:Application Method: Airless Spray Air Spray BrushThinner (max.vol.): 08030 (5%) 08030 (5%) 08030 (5%)Nozzle Orifice: 0.021" - 0.023"Nozzle Pressure: 150 bar/2175 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: Hempel's Thinner 08030Indicated film thickness, wet: 325 micron/13 milsIndicated film thickness, dry: 190 micron/7.6 mils (according to specification)Recoat interval, min: When dryRecoat interval, max: None
Safety: As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes should be avoided. Forced ventilation should be provided whenworking with solvent-borne materials in confined spaces or stagnant air. Even whenventilation is provided, respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5688010000
HEMPEL'S TRAFFIC AND AIRFIELD MARKING PAINT 56880
Surface Asphalt should be fully cured and properly compressed. Salt, dust, dirt and other contaminationPreparation: should be removed from surfaces to be painted.
Application As dictated by normal, good painting practice.Conditions:
Preceding Coat: None.
Subsequent Coat: None.
Remarks: For light reflection, add glass beads (Hempel's Traffic Glass Beads 97770). Consumption up to 12kg/26 lbs of glass beads per 20 litres/5 US gallons of paint.
The beads should be sprinkled into the wet paint surface of the traffic line by the "drop-on" methodwhich will give immediate and continuing reflection.
If the asphalt is not fully cured and compressed properly, there will be the risk of cracking andlifting of the edges of the paint lines.
HEMPEL'S TRAFFIC AND AIRFIELD MARKING PAINT 56880 should preferably be sprayed withoutthinning to achieve the best possible results.
Note: HEMPEL'S TRAFFIC AND AIRFIELD MARKING PAINT 56880 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5688010000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SILICONE TOPCOAT 56900
Description: HEMPEL’S SILICONE TOPCOAT 56900 is a heat resistant paint, pigmented with inertpigments.
Recommended use: For long-term protection of hot pipelines, exhaust pipes, smoke stacks and other hotsurfaces up to 200°C/392°F. In corrosive environment see PRECEDING COAT overleaf.
Service temperatures: Maximum, dry: 200°C/392°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000 Black/19990Finish: Semi-flat (See REMARKS overleaf) Semi-flat (See REMARKS overleaf)Volume solids, %: 59 ± 1 55 ± 1Theoretical spreading rate: 23.6 m²/litre - 25 micron 22.0 m²/litre - 25 micron
946 sq.ft./US gallon - 1.0 mil 882 sq.ft./US gallon - 1.0 milFlash point: 25°C/77°F 25°C/77°FSpecific gravity: 1.5 kg/litre - 12.5 lbs/US gallon 1.2 kg/litre - 10.0 lbs/US gallonSurface dry: 1 (approx.) hr at 20°C/68°F (ISO 1517) 1 (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 2-4 hours at 20°C/68°F 2-4 hours at 20°C/68°FV.O.C.: 375 g/litre - 3.1 lbs/US gallon 400 g/litre - 3.3 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (25%) 08080 (40%) 08080 (25%) (See REMARKS overleaf)Nozzle orifice: .017"Nozzle pressure: 125 bar/1800 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 25 micron/1 mil (See REMARKS overleaf)Indicated film thickness, wet: 50 micron/2 milsRecoat interval, min.: 24 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max.: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5690010000CO001
HEMPEL’S SILICONE TOPCOAT 56900
SURFACE Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and otherPREPARATION: contaminants by (high pressure) fresh water cleaning.
Abrasive blasting to Sa 2½. If shopprimer is required, only zinc silicate type is recommended.
APPLICATION Clean and dry surface with a temperature above the dew point to avoid condensation. In confinedCONDITIONS: spaces provide adequate ventilation during application and drying.
PRECEDING Can be used directly on blast-cleaned steel. For maximum corrosion protection, a primer coat ofCOAT: one of the following paints is recommended (40 micron/1.6 mil dry film thicknesses):
HEMPEL’S SILICONE ZINC 16900 or HEMPEL’S GALVOSIL 15700.
SUBSEQUENT None.COAT:
REMARKS:Gloss: After exposure to heat the gloss is reduced.Thermoplasticity: The paint film is somewhat thermoplastic also after heating.Film thicknesses: It is recommended to avoid too high thicknesses of the paint as this will give a risk of blistering at
later heating. THINNER 08080 must be added at application to secure the low dry film thickness.High temperature For high temperature service, the total dry film thickness of the paint system should preferably beservice: kept at 75 micron/3 mils as maximum.First exposure Do not expose the paint system to heat before it is through dry (minimum 24 hours atto heat: 20°C/68°F).Recoating: May be recoated when through dry (24 hours at 20°C/68°F).
Before recoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
Zinc silicate primer: If HEMPEL’S SILICONE TOPCOAT 56900 is applied on zinc silicate coatings, such as HEMPEL’SGALVOSIL 15700, popping may occur after application or after first heating up.The best way to avoid popping is to apply a mist coat in the first pass of HEMPEL’S SILICONETOPCOAT 56900. Let the air escape and apply the full coat of HEMPEL'S SILICONE TOPCOAT56900.
Note: HEMPEL’S SILICONE TOPCOAT 56900 is for professional use only.
Issued: June 2001 - 5690010000CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5690010000CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SILICONE ALUMINIUM 56910
Description: HEMPEL’S SILICONE ALUMINIUM 56910 is a heat resistant aluminium pigmented paint.
Recommended use: For long-term protection of hot pipelines, exhaust pipes, smoke stacks and other hotsurfaces. In corrosive environment see PRECEDING COAT overleaf.
Service temperatures: Maximum, dry: 600°C/1112°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTSColours/Shade nos: Aluminium/19000Finish: Semi-flat (See REMARKS overleaf)Volume solids, %: 35 ± 1Theoretical spreading rate: 14.0 m²/litre - 25 micron
561 sq.ft./US gallon - 1.0 milFlash point: 25°C/77°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: 1 (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 2-4 hours at 20°C/68°FV.O.C.: 590 g/litre - 4.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (5%) 08080 (15%) 08080 (5%) (See REMARKS overleaf)Nozzle orifice: .017"Nozzle pressure: 125 bar/1800 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 25 micron/1 mil (See REMARKS overleaf)Indicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 24 hours (20°C/68°F) (See REMARKS overleaf)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5691019000CO004
HEMPEL’S SILICONE ALUMINIUM 56910
SURFACE Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and otherPREPARATION: contaminants by (high pressure) fresh water cleaning.
Abrasive blasting to Sa 2½.
APPLICATION Clean and dry surface with a temperature above the dew point to avoid condensation. In confinedCONDITIONS: spaces provide adequate ventilation during application and drying.
PRECEDING Can be used directly on blast-cleaned steel. For maximum corrosion protection, a primer coat ofCOAT: one of the following paints is recommended (40 micron/1.6 mil dry film thicknesses):
HEMPEL’S SILICONE ZINC 16900 or HEMPEL’S GALVOSIL 15700.This will lower the heat resistance, reference is made to the product data sheets for the mentionedPrimers.
SUBSEQUENT None.COAT:
REMARKS:Gloss: After exposure to heat the gloss is reduced.Film thicknesses: It is recommended to avoid too high thicknesses of the paint as this will give a risk of blistering at
later heating. THINNER 08080 must be added at application to secure the low dry film thickness.Curing: To obtain full curing HEMPEL’S SILICONE ALUMINIUM 56910 requires heating to minimum
200°C/392°F for at least 5 days as the coating will otherwise exhibit certain thermoplasticity.High temperature For high temperature service, the total dry film thickness of the paint system should preferably beservice: kept at 75 micron/3 mils as maximum.First exposure Do not expose the paint system to heat before it is through dry (minimum 24 hours atto heat: 20°C/68°F).Recoating: May be recoated when through dry (24 hours at 20°C/68°F) or after being heated for one hour to
approximately 200°C/392°F.Before recoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
Zinc silicate primer: If HEMPEL’S SILICONE ALUMINIUM 56910 is applied on zinc silicate coatings, such as HEMPEL’SGALVOSIL 15700, popping may occur after application or after first heating up.The best way to avoid popping is to apply a mist coat in the first pass of HEMPEL’S SILICONEALUMINIUM 56910. Let the air escape and apply the full coat of HEMPEL'S SILICONE ALUMINIUM56910.
Note: HEMPEL’S SILICONE ALUMINIUM 56910 is for professional use only.
Issued: March 2002 - 5691019000CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5691019000CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S SILICONE ACRYLIC 56940
Description: HEMPEL’S SILICONE ACRYLIC 56940 is a heat resistant acrylic modified silicone paint.It is air drying at ambient temperature.
Recommended use: For long-term protection of hot pipelines, exhaust pipes, smoke stacks and other hotsurfaces up to 200°C/390°F, resist short time exposure up to 300°C/570°F. Whenheated to above 200°C/390°F for longer periods a certain discolouration may occur,which do not affect the protective properties of the product. In corrosive environmentsee PRECEDING COAT overleaf.
Service temperatures: Maximum, dry: 300°C/572°F
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Aluminium/19000Finish: Semi-flat (see REMARKS overleaf)Volume solids, %: 29 ± 1Theoretical spreading rate: 11.6 m²/litre - 25 micron
465 sq.ft./US gallon - 1.0 milFlash point: 25°C/77°FSpecific gravity: 1.1 kg/litre - 9.2 lbs/US gallonSurface dry: ½ (approx.) hr at 20°C/68°F (ISO 1517)Dry to touch: 1-2 hours at 20°C/68°FV.O.C.: 605 g/litre - 5.0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Air spray BrushThinner (max.vol.): 08080 (15%) 08080 (25%) 08080 (15%)
(See REMARKS overleaf)Nozzle orifice: .017"Nozzle pressure: 125 bar/1800 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 25 micron/1 mil (see REMARKS overleaf)Indicated film thickness, wet: 50-100 micron/2-4 mils (depending on colour)Recoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5694019000CO002
HEMPEL’S SILICONE ACRYLIC 56940
SURFACE Remove oil and grease etc. thoroughly with suitable detergent. Remove salts and otherPREPARATION: contaminants by high pressure fresh water cleaning.
Abrasive blasting to Sa 2½, SSPC-SP-10. If shopprimer is required, only zinc silicate type isrecommended.
APPLICATION Clean and dry surface with a temperature above dewpoint to avoid condensation. In confinedCONDITIONS: spaces provide adequate ventilation during application and drying.
PRECEDING Can be used directly on blast-cleaned steel. For maximum corrosion protection, a primer coat ofCOAT: one of the following paints is recommended (40 micron/1.6 mil dry film thicknesses):
HEMPEL’S SILICONE ZINC 16900 or HEMPEL’S GALVOSIL 15700.
SUBSEQUENT None.COAT:
REMARKS:Gloss: After exposure to heat the gloss is reduced.
Thermoplasticity: The paint film is somewhat thermoplastic also after heating.Film thicknesses: It is recommended to avoid too high thicknesses of the paint as this will give a risk of blistering at
later heating. THINNER 0808 must be added at application to secure the low dry film thickness.High temperature For high temperature service, the total dry film thickness of the paint system should preferably beservice: kept at 75 micron/3 mils as maximum.First exposure Do not expose the paint system to heat before it is through dry (minimum 24 hours at
to heat: 20°C/68°F).Recoating: May be recoated when through dry (8 hours at 20°C/68°F) or after being heated for one hour to
approximately 200°C/392°F.Before overcoating after exposure in contaminated environment, clean surface thoroughly by highpressure fresh water hosing and allow to dry.
Zinc silicate If HEMPEL’S SILICONE ACRYLIC 56940 is applied on zinc silicate coatings, such as HEMPEL’Sprimer: GALVOSIL 15700, popping may occur after application or after first heating up.
The best way to avoid popping is to apply a mist coat in the first pass of HEMPEL’S SILICONEACRYLIC 56940. Allow the air to escape and apply the full coat of HEMPEL’S SILICONE ACRYLIC56940.
Note: HEMPEL’S SILICONE ACRYLIC 56940 is for professional use only.
Issued: October 1999 - 5694019000CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5694019000CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®ENAMEL HI-BUILD 58030
Description: HEMUCRYL ENAMEL HI-BUILD 58030 is a water-borne, acrylic dispersion based paint.Itdries to a non-yellowing and glossy coating with low dirt pick-up, good weatheringproperties, and high gloss retention.Especially suited for application by airless spray.
Recommended use: As a glossy, finishing coat in water-borne paint systems, interior and exterior, in mildly tomoderately corrosive environment. For use on buildings the relatively high resistance todiffusion of water vapour and carbon dioxide should be taken into account.For handrails and the similar, a chemically curing coating is alternatively recommended.
Service temperatures: Maximum, dry: 120°C/248°F.
Approvals: Approved as a low flame spread material by British and Canadian authorities.Approved as a low flame spread material by Danish authorities according to IMOresolution MSC 61 (67).Has a Danish EC-type Examination Certificate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000*Finish: GlossyVolume solids, %: 44 ± 1Theoretical spreading rate: 5.9 m²/litre - 75 micron
235 sq.ft/US gallon - 3 milsFlash point: > 66°C/151°FSpecific gravity: 1.2 kg/l itre - 10.0 lbs/US gallonSurface dry: ¾ (approx.) hour at 20°C/68°F (ISO 1517)Dry to touch: 1½ (approx.) hour at 20°C/68°F (See REMARKS overleaf)V.O.C.: 5 g/litre - 0.0 lbs/US gallon
125 g/litre - 1.0 lbs/US gallon (ASTM D 3960 - water reduced)
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush (touch-up)Thinner (max.vol): Fresh water (5%) HEMUCRYL BRUSH AGENT 99810 (3-8%)Nozzle orifice: 015"-.019" (See APPLICATION INSTRUCTIONS)Nozzle pressure: 130 bar/1900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See APPLICATION INSTRUCTIONS)Indicated film thickness, dry: 75 micron/3 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 2 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5803010000CO013
HEMUCRYL ENAMEL HI-BUILD 58030
SURFACE See separate HEMUCRYL APPLICATION INSTRUCTIONS.PREPARATION:
APPLICATION See separate HEMUCRYL APPLICATION INSTRUCTIONS.CONDITIONS:
PRECEDING HEMUCRYL PRIMER HI-BUILD 18030, HEMUDUR 18500 or according to specification.COAT: Other paints may precede but consult nearest HEMPEL office. Certain types of aged, solvent based
coatings can be recoated after a careful cleaning. A testpatch is recommended. Aged, chemicallycured coatings (alkyd, epoxy, polyurethane etc.) may also precede. Yet, only recommended in caseof later mild exposure - roughening may be necessary and a test patch is recommended.
REMARKS: Certificates have been issued under the former quality number 5803.Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine-containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.To obtain full opacity, an extra coat may be necessary, especially for certain lead-free colours in egred, orange, yellow and green.
Film thicknesses: May be specified in another film thickness than indicated. This will alter spreading rate and mayinfluence drying time and recoating interval. Normal range is 50-100 micron/2-4 mils dry filmthickness. When used in 50 micron dry film thickness, 3-5% thinning will be necessary to secureproper film formation. Beware of overthinning, which may cause formation of fisheyes.
Application: For proper film formation the recommended nozzle sizes should be used.If application is done by roller/brush, apply liberally. Use brushes with synthetic fibres. Rollersshould either be mohair or felt.For brush application, add 3-8% by volume of HEMUCRYL BRUSH AGENT 99810.
Recoating: No maximum recoating interval, but after prolonged exposure to polluted atmosphere removeaccumulated contamination by high pressure fresh water cleaning and allow to dry.Other REMARKS: See separate HEMUCRYL APPLICATION INSTRUCTIONS.
HEMUCRYL ENAMEL HI-BUILD 58030 is for professional use only.
Issued: April 2002 - 5803010000CO013HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5803010000CO013
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®TOPCOAT HI-BUILD 58230
Description: HEMUCRYL TOPCOAT HI-BUILD 58230 is a water-borne, acrylic dispersion based paint. Itdries to a non-yellowing and semi-flat coating with low dirt pick-up and good weatheringproperties. It has a fairly good resistance to spillage of chemicals and to washing.Especially suited for application by airless spray.
Recommended use: As a finishing coat in water-borne paint systems, interior and exterior, in mildly tomoderately corrosive environment. For use on buildings the relatively high resistance todiffusion of water vapour and carbondioxide should be taken into account.
Service temperatures: Maximum, dry: 120°C/248°F.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000*Finish: Semi-flatVolume solids, %: 42 ± 1Theoretical spreading rate: 5.6 m²/litre - 75 micron
225 sq.ft/US gallon - 3 milsFlash point: > 66°C/151°FSpecific gravity: 1.2 kg/litre - 10.0 lbs/US gallonDry to touch: 1½ (approx.) hour at 20°C/68°F (See REMARKS overleaf)V.O.C.: 2 g/litre - 0.0 lbs/US gallon
115 g/litre - 1.0 lbs/US gallon (ASTM D 3960 - water reduced)
*Other shades according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush (touch-up)Thinner (max.vol): Fresh water (5%) HEMUCRYL BRUSH AGENT 99810 (3-8%)Nozzle orifice: 015"-.019" (See APPLICATION INSTRUCTIONS)Nozzle pressure: 130 bar/1900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See APPLICATION INSTRUCTIONS)Indicated film thickness, dry: 75 micron/3 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 2 hours (20°C/68°F)Recoat interval, max: None (See REMARKS overleaf)
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5823010000CO003
HEMUCRYL TOPCOAT HI-BUILD 58230
SURFACE See separate HEMUCRYL APPLICATION INSTRUCTIONS.PREPARATION:
APPLICATION See separate HEMUCRYL APPLICATION INSTRUCTIONS.CONDITIONS:
PRECEDING HEMUCRYL PRIMER HI-BUILD 18030 or HEMUDUR 18500.COAT: Other paints may precede but consult nearest HEMPEL office. Certain types of aged, solvent
based coatings can be recoated after a careful cleaning. A testpatch is recommended.Aged, chemically cured coatings (alkyd, epoxy, polyurethane etc.) may also precede. Yet, onlyrecommended in case of later mild exposure - roughening may be necessary and a testpatch isrecommended.
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to chlorine- containing
atmosphere.Leaded colours may become discoloured when exposed to sulphide-containing atmosphere.
Film thicknesses: May be specified in another film thickness than indicated. This will alter spreading rate and mayinfluence drying time and recoating interval. Normal range dry is 50-100 micron/2-4 mils dry filmthickness. When used in 50 micron dry film thickness, 3-5% thinning will be necessary to secureproper film formation.
Application: For proper film formation the recommended nozzle sizes should be used.If application is done by brush/roller, apply liberally. Use brushes with synthetic fibres. Rollersshould either be mohair or felt.For brush/roller application, add 3-8% by volume of HEMUCRYL BRUSH AGENT 99810.
Recoating: No maximum recoating interval, but after prolonged exposure to polluted atmosphere removeaccumulated contamination by high pressure fresh water cleaning and allow to dry.
Other REMARRKS: See separate HEMUCRYL APPLICATION INSTRUCTIONS.
HEMUCRYL TOPCOAT HI-BUILD 58230 is for professional use only.
Issued: March 2001 - 5823010000CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5823010000CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product data description refer to the product data sheet
HEMPEL’S HEMUCRYL product rangeScope: These Application Instructions cover surface preparation and application conditions of
HEMPEL’S HEMUCRYLs.
Surface preparation, New steel: Remove oil and grease, etc. with suitable detergent. Remove salt and otherprimers: contaminants by (high pressure) fresh water cleaning. Abrasive blasting tominimum Sa 2½. For temporary protection, if required, use suitable shopprimer. Alldamaged shopprimer and contamination from storage and fabrication should bethoroughly cleaned prior to final painting. For repair and touch-up use the specifiedHEMUCRYL primer type.
Repair: Remove oil and grease, etc. with suitable detergent. Remove salt and othercontaminants by (high pressure) fresh water cleaning. Remove rust and loose paint byabrasive blasting or power tool cleaning to St 3 before recoating. Touch up bare spotswith the specified HEMUCRYL primer type.
Aluminium: Very thorough degreasing, followed by (high pressure) fresh water cleaningto remove all salts and other contamination. Any anodizing must be completelyremoved. Thorough sand papering or abrasive sweeping with mineral abrasives isrecommended. Cast aluminium is recommended to be abrasive swept to a uniform,evenly grey appearance.
Stainless steel: Very thorough degreasing with alkaline degreaser, ie HEMPEL'S LIGHTCLEANER 99350, followed by fresh water hosing to remove all contamination.
Hot-dipped galvanized steel: Wet rubbing/grinding with ammonia water 1:20 followedby fresh water hosing. In the case this method is not feasible, the procedure asdescribed for stainless steel may be used.
Zinc silicate coated surfaces: Remove oil and grease, etc, with suitable detergent.Remove salt and other contaminants by high pressure fresh water cleaning. Afterexposure to high humidity, zinc salts ("white rust") must be removed carefully by (highpressure) fresh water cleaning - if necessary combined with scrubbing with stiff nylonbrushes. Consult the APPLICATION INSTRUCTIONS for the relevant GALVOSIL product.
Note:Among the HEMUCRYL primer types, HEMUCRYL TI-COAT 18200 is designed to be usedas the first coat on aluminium, hot-dop galvanized steel, stainless steel and on zincsilicate coated surfaces.
Surface preparation, Preceding coats should be sound and tightly adhering. Remove oil and grease withtopcoats: suitable detergent. Remove salts and other contaminants by (high pressure) fresh water
cleaning. Remove rust and loose material by abrasive blasting or power tool cleaning.Dust off residues. Touch up to full system before recoating with specified HEMUCRYLtopcoat type.
Concrete: Any oil, grease and other contaminants should be removed by eg volatilizingby flame cleaning or treatment with suitable detergent, the latter in the following way:
1) Saturation of the surface with fresh water2) Washing with suitable detergent followed by fresh water hosing
Remove loose material eg by stiff brushes or blasting, high pressure jetting or flamecleaning followed by fresh water hosing depending on circumstances. Three lastmentioned methods are also able to remove scum layer if necessary. After surfacepreparation the surface should feel solid and hard. Remove dust.
Saturate surface with suitable sealer, eg microdispersed acrylic type or by theHEMUCRYL topcoat diluted 15-20% with water.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
HEMPEL’S HEMUCRYL product range
Application conditions: Use only where application can proceed at temperatures above 5°C/41°F, preferablyabove 10°C/50°F. Apply on a clean and dry surface with a temperature above the dewpoint to avoid condensation.
Relative humidity: During application above 60%, preferably 75-90%, to avoid dry spray.If RH is below 60%, special thinner may be added in order to reduce dry spray. Duringdrying below 80%, preferably between 40-60%. (Contact HEMPEL for further advice).Good ventilation during application and drying is necessary. Especially during drying it isof utmost importance that sufficient ventilation is covering all parts of the surfacespainted. Ventilation requirements to remove water vapours liberated during applicationand drying are app 75 m³/litre of the paint at 20°C/68°F. (Relative humidity of the airsupply 40%).
REMARKS:Good painting practice: The durability/performance of water-borne coatings is to a very high degree depending
on the fulfilment of good painting practice. For instance application to riveted andskip-welded constructions will require extra care when coating sharp edges, rivetedjoints, etc. Avoid too high thicknesses per coat. Preferably apply an extra stripe coat.
"Edge effect": Furthermore, as water-borne paints have a high tendency to "withdraw" from sharpedges, etc., proper corrosion protection will be highly supported by careful rounding ofedges and that any joints are completely closed and tight.
Exposure to low temperatures If the painted items will be exposed to humidity/water at temperatures below 5-10°C/shortly after application: 41-50°F shortly after finishing the paint application, it is of utmost importance for later
good performance that following rules are complied with:
• Excessive film thickness must be avoided.
• The (last applied) paint layer must dry for at least 6 hours at 20°C/68°F - 40-60%RH, 12 hours at 10°C/50°F - 40-60% RH before exposure to temperatures below5°C/41°F and/or condensation/water exposure.
Avoid outdoor application in seasons with low night temperatures, frost and frost incombination with condensation or rain.
Shelf life/storage: Store at temperatures between 5°C-40°C/41°F-104°F. Shelf life is reduced attemperatures above 30°C/86°F. Do not expose to frost during storage and transport, orbefore the coating is dry.
Cleaning of tools: Tools must be cleaned immediately with lukewarm soap water and/or fresh waterfollowed by thoroughly rinsing to remove residues of detergent.Dried remains of paint can be removed with HEMPEL'S TOOL CLEANER 99610.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Note: Any deviations from the above of a particular HEMUCRYL will be stated in the productdata sheet for this paint.
Issued: December 2000HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPATONE* 58280
Description: HEMPATONE 58280 is a flat vinyl acetate copolymer based emulsion paint.
Recommended use: As a decorative finish on interior walls. May be used exterior in mild climates.
Service temperatures: Maximum, dry: 60°C/140°F, however, may give off smell at these temperatures.
Availability: Subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: White/10000 (Other shades according to assortment list)Finish: FlatVolume solids: 39%Theoretical spreading rate: 13.0 m²/litre - 30 micron
521 sq.ft./US gallon - 1.2 milFlash point: > 66°C/151°FSpecific gravity: 1.4 kg/liter - 11.7 lbs/US gallonDry to touch: 1 (approx.) hour at 20°C/68°FV.O.C.: 54 g/litre - 0.4 lbs/US gallon
132 g/litre - 1.1 lbs/US gallon (ASTM D 3960)
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempe Book.
APPLICATION DETAILS:Application method: Airless spray BrushThinner (max.vol.): Water (5%) Water (5%) (See REMARKS overleaf)Nozzle orifice: .018"-.023"Nozzle pressure: 100 bar/1450 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: Fresh water (See REMARKS overleaf)Indicated film thickness, dry: 30 micron/1.2 milIndicated film thickness, wet: 75 micron/3 milsRecoat interval, min: 1 hour (20°C/68°F)Recoat interval, max: None
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5828010000CO011
HEMPATONE 58280
SURFACE New plaster and concrete: Remove oil and grease with suitable detergent. Remove salts andPREPARATION: other contaminants by (high pressure) fresh water cleaning. Dust-off loose material. Apply two
coats of HEMPATONE 58280, first coat diluted 10-20% with fresh water.Asbestos cement and old, weathered concrete, distempered walls and whitewashed surfaces:Brush off loose material with a stiff brush. Saturate the surface with a suitable sealer. When dryapply two coats of HEMPATONE 58280.New wood (pine, fir, etc) and fibre board, interior: Patch knots with shellac. Treat with anti-mouldagent, if necessary. Apply two coats of HEMPATONE 58280, the first coat diluted with 10-20%fresh water, second coat undiluted.Steel fittings, etc.: One or two coats of HEMPALIN PRIMER 12050 or HEMUCRYL PRIMER 18100.Previous painted surfaces: Wash down with ammonia water solution. Apply one or two coats ofHEMPATONE 58280. Old coats should be sound and tightly adhering.
APPLICATION As dictated by normal good painting practice.CONDITIONS: Do not apply below 5°C/41°F.
SUBSEQUENT None.COAT:
REMARKS:Colours: Certain lead-free red and yellow colours may discolour when exposed to sulphide and chlorine-
containing atmosphere.Film thicknesses: May be specified in another film thickness than indicated depending on purpose and area of use.
This will alter spreading rate and may influence drying time and recoat interval. Normal range dry is30-40 micron/1.2-1.6 mils.
Application: Apply liberally by brush/roller. Use brushes with synthetic fibres. Rollers should either be mohair orfelt.
Ventilation: Under humid conditions ample ventilation with dry air (40-60% RH) is required to remove watervapours in the drying phase.It is important that sufficient ventilation is covering all parts of the surfaces painted. Ventilationrequirement to remove the water vapour liberated during application and drying is:- At 10°C/50°F: Approximately 150 m3/litre (20.000 cuft/US gallon) of paint- At 20°C/68°F: Approximately 75 m3/litre (10.000 cuft/US gallon) of painton the condition that the relative humidity of the air supply is 40%.
Recoating: No maximum recoat interval, but after prolonged exposure to polluted atmosphere removeaccumulated contamination by high pressure fresh water cleaning and allow to dry.
Shelf life/storage: Store at temperatures between 5°C-40°C/41°F-104°F. Shelf life is reduced at temperatures above30°C/85°F. Do not expose to frost during storage and transport, or before the coating is dry.
Notes: Clean tools carefully with fresh water or lukewarm soap water immediately after use.Dried remains of paint can be removed with HEMPEL'S NAVI WASH 99330, undiluted, or preferablywith HEMPEL'S TOOL CLEANER 99610.
HEMPATONE 58280 is for professional use only.
Issued: March 1998 - 5828010000CO011HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 5828010000CO011
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTI-SLIP BEADS 67420
Description: HEMPEL’S ANTI-SLIP BEADS 67420 are hollow, aluminium silicate spheres (“glasspearls”) of diameters between 5 and 200 micron.
Recommended use: To obtain anti-skid properties on decks and other areas where a skid-proof surface isrequired. To be mixed with the paint before application.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colour: Off-white/greyishSpecific gravity: 0.7 kg/litre (approx.)Particle shape: Spherical
Remarks: Store under dry and clean conditions.Use approximately the following amount in weight of HEMPEL’S ANTI-SLIP BEADS67420:
Approx. 0.8 kg/1.8 lbs of HEMPEL'S ANTI-SLIP BEADS 67420 into 20 litres or 5 USgallons of HEMPATEX ENAMEL 56360.
Approx. 1.0 kg/2.2 lbs of HEMPEL’S ANTI-SLIP BEADS 67420 into 20 litres or 5 USgallons of HEMPATEX HI-BUILD 46410 or of HEMPALIN DECKPAINT 53240.
Approx. 1.2 kg/2.6 lbs of HEMPEL'S ANTI-SLIP BEADS 67420 into 20 litres or 5 USgallons of HEMPATHANE TOPCOAT 55210.
Approx. 1.3 kg/2.9 lbs of HEMPEL'S ANTI-SLIP BEADS 67420 into 20 litres or 5 USgallons of HEMPADUR HI-BUILD 45200/45201.
HEMPEL’S ANTI-SLIP BEADS 67420 must be stirred thoroughly into the paint until auniform mixture has been obtained.
Apply the mixture by brush, by roller, or by conventional spray equipment using pressurevessel and large nozzle orifice.
Note: HEMPEL'S ANTI-SLIP BEADS 67420 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 67420
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTI-SLINT®67500
Description: HEMPEL’S ANTI-SLINT 67500 is flame dried silica sand of which the average particlesize is approximately 0.5 millimetre.
Recommended use: To obtain anti-skid properties on decks and other areas where a skid-proof surface isrequired.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colour: GreyishSpecific gravity: 2.7 (approx.) kg/litreParticle shape: Grit
Remarks: Being heavy and rather coarse HEMPEL’S ANTI-SLINT 67500 should not be stirred intothe paint before its application. For such purpose use HEMPEL'S ANTI-SLIP BEADS67420.HEMPEL’S ANTI-SLINT 67500 should be sprinkled evenly on the surface immediatelyupon application of the penultimate coat of the paint system while the paint is still wet.Consumption approximately 2.5 kg/5.5 lbs of HEMPEL’S ANTI-SLINT 67500 to 25 sq.m/270 sq.feet.When the paint is dry, sweep up surplus grit and apply the final coat.HEMPEL’S ANTI-SLINT 67500 should be kept dry and clean.Do not mix contaminated sweepings with new supplies.
Note: HEMPEL'S ANTI-SLINT 67500 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 67500
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING COMBIC®7199BTIN-FREE
Description: HEMPEL’S ANTIFOULING COMBIC 7199B is a tin-free, self-polishing antifouling, whichhas a high content of cuprous oxide and organic bioactive material.
Recommended use: As antifouling to be used when paints containing tin are not suitable. As an antifoulingfor maintenance of bottom on vessels operating in global trade and with short idleperiods.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50300 - Red/51110Finish: FlatVolume solids, %: 58 ± 1Theoretical spreading rate: 5.8 m²/litre - 100 micron
233 sq.ft./US gallon - 4 milsFlash point: 23°C/73°FSpecific gravity: 1.8 kg/litre - 15.0 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 375 g/litre - 3.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf) Brush/Roller (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .023"-.027"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL'S THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 8 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7199B50300CO003
HEMPEL’S ANTIFOULING COMBIC 7199B
SURFACE Existing organotin copolymer based selfpolishing antifouling: Remove possible oil and greasePREPARATION: etc. with suitable detergent, followed by careful high pressure fresh water cleaning. Ensure that any
possible leached surface layer is removed effectively.Allow the surface to dry before recoating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingantifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
In confined spaces such as sea chests and stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPATEX HI-BUILD 46330 or according to specification.COAT:
SUBSEQUENT None.COAT:
REMARKS: This product contains heavy particles. Stir well before use.By providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process.
Colour: The colour of the system changes in accordance with the colours of the coats applied.The initial colour may vary within the same shade. Most pronounced in shade 50300. The finalcolour will appear after exposure to saltwater. This has no influence on the antifoulingperformance. Light red 50300 turns whitish in direct contact with seawater.Indicated film thickness will vary according to specification. This will alter spreading rate and mayinfluence drying time. In case of multi-coat application, drying time and minimum recoat interval willbe influenced by the number of coats and by the thickness of each coat applied - reference is madeto the corresponding painting specification.Range and control of dry film thickness: 80 micron/3.2 mils to 125 micron/5 mils. Keep thinningto a minimum to ensure that correct film thickness is obtained. The proper way of governing thefilm thickness is to sub-divide the areas to be painted and calculate the amount of paint to beapplied on each sub-divided area. The exact amount of paint calculated must be applied evenly onthe area. For further information, please consult the corresponding painting specification.Recommended number of coats: As per specification depending on existing hull condition, tradingpattern, and intended service life.No maximum recoat interval, but after prolonged exposure to polluted atmosphere, removeaccumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat.If roller/brush application exceptionally is utilized (e.g. to line cut) more coats are necessary toachieve the recommended film thickness.Undocking: Minimum undocking time depends on number of coats applied, film thickness, and theprevailing temperature. For further information, please consult the corresponding paintingspecification.Maximum undocking time depends on the atmospheric conditions (UV-radiation, temperature,degree of air pollution, etc.). It is important to carry out a thorough high pressure fresh watercleaning after prolonged exposure. Exposure to the atmosphere up to 6 months normally presentsno problem when such cleaning is carried out.
Note: HEMPEL'S ANTIFOULING COMBIC 7199B is for professional use only.
Issued: September 2000 - 7199B50300CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7199B50300CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING ECONOMIC SP-SEA 74030
Description: HEMPEL’S ANTIFOULING ECONOMIC SP-SEA 74030 is a high-build, high-solids,self-polishing antifouling. It is based on organotin copolymer reinforced with extrabio-active compounds.Due to its self-renewing effect this product maintains an effective bio-active surfaceduring its entire service life.Gives a certain surface smoothing.
Recommended use: As an economic selfpolishing antifouling for vessels with medium to high speed andactivities.Suitable for upgrading the antifouling system on old vessels without costly surfacepreparation.The actual specification is based on input of the operational parameters into our"Computer Aided Specification" (CAS) system.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50300 - Red/51110 (see REMARKS overleaf)Finish: FlatVolume solids, %: 56 ± 1Theoretical spreading rate: 5.6 m²/litre - 100 micron (see REMARKS overleaf)
225 sq.ft/US gallon - 4.0 milsFlash point: 31°C/88°FSpecific gravity: 1.5 kg/litre - 12.5 lbs/US gallonDry to touch: 3-4 hours at 20°C/68°FV.O.C.: 395 g/litre - 3.3 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush/Roller (See REMARKS overleaf)Thinner (max. Vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .023"-.027"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval, min: 6 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7403050300CO003
HEMPEL’S ANTIFOULING ECONOMIC SP-SEA 74030
SURFACE Existing organotin copolymer based selfpolishing antifouling: Remove possible oil and greasePREPARATION: etc. with suitable detergent, followed by careful high pressure fresh water cleaning. Ensure that any
possible leached surface layer is removed effectively.Allow the surface to dry before recoating.Existing non-selfpolishing antifouling: Remove possible oil and grease, etc. with suitabledetergent, followed by high pressure fresh water cleaning, also to remove possible weak structureof leached antifouling. Allow the surface to dry before recoating. Whether or not to use a sealercoat depends on the type and condition of the existing antifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
In confined spaces such as sea chests and stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR 45182, HEMPATEX HI-BUILD 46330, or according to specification.COAT:
SUBSEQUENT None, or as per specification.COAT:
REMARKS: This product contains heavy particles. Stir well before use.By providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process.
Colour: The colour of the system changes in accordance with the colours of the coats applied. The initialcolour may vary within the same shade. Most pronounced in shade 50300. The final colour willappear after exposure to saltwater. This has no influence on the antifouling performance. Light red50300 changes to whitish in direct contact with seawater.Indicated film thickness will vary according to specification. This will alter spreading rate and mayinfluence drying time. In case of multi-coat application, drying time and minimum recoat interval willbe influenced by the number of coats and by the thickness of each coat applied - reference ismade to the corresponding painting specification.Range and control of dry film thickness: 60 micron/2.4 mils to 150 micron/6.0 mils per coat.Keep thinning to a minimum to ensure that correct film thickness is obtained. The proper way ofgoverning the film thickness is to sub-divide the areas to be painted and calculate the amount ofpaint to be applied on each sub-divided area. The exact amount of paint calculated must beapplied evenly on the area. For further information, please consult the corresponding paintingspecification.Recommended number of coats and total maximum film thickness: The CAS system puts certainlimitations on painting specifications based on HEMPEL’S ANTIFOULING ECONOMIC SP-SEA 74030.The HEMPEL office in charge will be able to make an exact specification.Recoating: No maximum recoat interval, but after prolonged exposure to polluted atmosphere,remove accumulated contamination by high pressure fresh water cleaning and allow to dry beforeapplying next coat.If roller/brush application exceptionally is utilized (eg to line cut) more coats are necessary toachieve the recommended film thickness.Undocking: Minimum undocking time depends on number of coats applied, film thickness, and theprevailing temperature. For further information, please consult the corresponding paintingspecification.Maximum undocking time depends on the exposure conditions, degree of air pollution, etc. Themost important factor is to carry out a thorough high pressure fresh water cleaning after prolongedexposure. Outfitting of up to 6 months followed by such cleaning normally presents no problem.Longer outfitting periods to be evaluated from case to case. The recommended maximumundocking interval relates to vertical bottom only. Flat bottom, which has not been exposed todirect sunlight, will for all normal practical building schedules have a no-maximum value.
Note: HEMPEL'S ANTIFOULING ECONOMIC SP-SEA 74030 is for professional use only.
Issued: December 2000 - 7403050300CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7403050300CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S ANTIFOULING HARD RACING 76500
Description: HEMPEL'S ANTIFOULING HARD RACING 76500 is a vinyl-based antifouling with a highcontent of copperand organotin compounds.
Recommended use: As an antifouling for boats of glassfibre, wood, plywood, steel and ferro-cement. Do not use on aluminium and other light alloy metal.
PHYSICAL CONSTANTS:Finish: FlatColour: Black White Red (Other shades according to assortment list)Shade Number: 19990 10000 51170Volume by Solids: 42% 43% 43%Theoretical Spreading Rate: 10.5 10.8 10.8 m²/litre - 40 micron
428 440 440 sq.ft./US gallon - 1.6 milFlash Point: 24ºC/75ºF 24ºC/75ºF 24ºC/75ºF A-Pensky closed cupSpecific Gravity: 1.3 1.3 1.3 kg/litre
10.9 10.9 10.9 lbs/US gallonDry to touch: 2 (approx) 2 (approx) 2 (approx) hours at 20ºC/68ºF
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless Spray Air Spray Brush/Roller/Paint padThinner (max.vol.): 08880 (5%) 08880 (5%) 08880 (5%)Nozzle Orifice: 0.018" - 0.023" Nozzle Pressure: 150 bar/2100 psi
(Airless spray data are indicative and subject to adjustment)Indicated film thickness, wet: Approx. 100 micron/4 milsIndicated film thickness, dry: 40 micron/1.6 milsRecoat interval, min: 2 hours (20ºC/68ºF)Recoat interval, max: None (see REMARKS overleaf)
Safety: Packings are provided with applicable labels which should be observed.In addition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenapplying paint in confined spaces or stagnant air. Even when ventilation is provided,respiratory, skin, and eye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7650019990
HEMPEL'S ANTIFOULING HARD RACING 76500
Application The surface must be completely clean and dry.Application should only take place in dry weatherwith temperatures above 50ºC/41ºF and the temperature of the surface should be above the dewpoint to avoid condensation. Avoid direct sunlight. In confined spaces provide adequate ventilationduring application and drying.
Preceding coat: Depends on the substrate. See data sheet for HEMPEL'S LIGHT PRIMER 45550, HEMPEL'SBOTTOM PRIMER 26030 or HEMPEL'S BARRIER PRIMER 16670.
Remarks: The antifouling contains heavy pigments and must therefore be stirred well before and during use.Keep thinning to a minimum to ensure that the correct film thickness is obtained. 2-3 coats (120micron dry film thickness) recommended. When applied by air spray, roller or paint pad an extracoat may be necessary to obtain correct film thickness. The boat may be launched when the paintis dry. Launching may be postponed up to 3 months. If so, the bottom must be thoroughly washedand, if necessary, lightly rubbed down. If a new coat of HEMPEL'S ANTIFOULING HARD RACING76500 is applied after prolonged exposure to polluted atmosphere remove accumulatedcontamination by fresh water hosing and allow surface to dry before painting.
Note: HEMPEL'S ANTIFOULING HARD RACING 76500 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2
HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7650019990
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S ANTIFOULING COMBIC 76990
Description: Hempel's Antifouling Combic 76990 is a high build, high solids self-polishing bottompaint. The organotin polymer and the high content of cuprous oxide make it suitable forlong term protection under severe fouling conditions. By it's self-renewing effect, thisproduct maintains a continually bio-active surface during it's entire service life.
Recommended use: As an antifouling for bottom and boottop on vessels operating in global trading and withshort to medium idle periods.
PHYSICAL CONSTANTS:Finish: Flat FlatColour: Light Red Red Other shades according to assortment list.Shade Number: 50300 51110Volume by Solids: 47% 49Theoretical Spreading See remarks overleafRate:Flash Point: 22ºC/72ºF 22ºC/72ºF A-Pensky closed cupSpecific Gravity: 1.8 1.8 kg/litreDry to touch: See remarks overleaf
For surface preparation, application conditions and coating system see overleaf.
APPLICATION DETAILS:Application Method: Airless SprayThinner (max.vol.): 08080 (5%)Nozzle Orifice: 0.023" - 0.027" Nozzle Pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: THINNER 08080Indicated film thickness: See REMARKS overleafRecoat interval: See REMARKS overleaf
Safety: Packings are provided with applicable labels which should be observed.In addition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenapplying paint in confined spaces or stagnant air. Even when ventilation is provided,respiratory, skin, and eye protection are always recommended when spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7699050300
HEMPEL'S ANTIFOULING COMBIC 76990
Application The surface must be completely clean and dry at the btime of application and it'sConditions: temperature must be above the dew point to avoid condensation. Tolerates low temperature
application which will, however, increase drying time. In confined spaces provide adquateventilation during application and drying.
Preceding coat: HEMPANYL TAR 16280, HEMPATEX MIO 16670 or according to specification. Renewal: remove any oil and grease with water miscible, mild detergent followed by high pressurehosing. Allow surface tvo dry before recoating. Old coatings must be sound and well adhering.
Subsequent Coat: None or according to specification
Remarks:Indicated Dry Film Wet 200 microns/8.0 mils 300 microns/12.0 mils Thickness Dry 100 microns/4.0 mils 150 microns/6.0 mils
Theoretical 5.1 3.4 m²/litreSpreading Rate 208 139 sq.ft/US gallonDry to Touch 3-4 6-8 hours at 20ºC/68ºFRecoating Interval Min 6 10 hours at 2OºC/68ºF(first layer) Max none none see below
This product contains heavy particles. Stir well before use. Indicated film thickness will vary according to specification. Range of dry film thickness 100microns/4.0 mils to 150 microns/6.0 mils. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of controlling the film thickness is to subdivide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area.Recommended Number of Coats as per specification depending on trading pattern and intendedservice life. No maximum recoating interval, but after prolonged exposure to polluted atmosphereremove accumulated contamination with fresh water hosing and allow surface to dry beforeapplying next coat.Undocking interval The ship may be floated when the paint is dry. Minimum undocking timedepends on number of coats applied, film thickness and the prevailing temperature. Maximum 3months.In providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process. The colour of the system changes in accordance with the colours of the coatsapplied. Light red 50300 changes to whitish shortly after immersion.
Note: HEMPEL'S ANTIFOULING COMBIC 76990 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7699050300
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING NAUTIC®SP-ACE 79031
Description: HEMPEL’S ANTIFOULING NAUTIC SP-ACE 79031 is a high-build, high-solids self-polishingantifouling. It is based on an organotin copolymer reinforced with extra bio-activecompounds.The copolymer hydrolyses in seawater and releases bio-active compounds at acontrolled and constant rate. This self-renewing effect ensures that a bio-activeinterface to the seawater is produced and maintained constantly during the entireservice life of the system. The system provides a certain control of roughness.
Recommended use: As a high performance fouling control coating for ship hulls operating worldwide atmedium to high speed. This product is especially suited for vessels with high activityand short port calls, ie will cover the need for most deep-sea trading vessels.The actual selection and specification of HEMPEL's selfpolishing antifoulings is basedon input of the operational parameters into our "Computer Aided Specification System"(CAS).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50300 - Red/51110 (see REMARKS overleaf)Finish: FlatVolume solids, %: 56 ± 1
Theoretical spreading rate: 4.7 m²/litre - 120 micron187 sq.ft/US gallon - 4.8 mils
Flash point: 31°C/88°FSpecific gravity: 1.7 kg/litre- 14.2 lbs/US gallonDry to touch: 5 (approx.) hours at 20°C/68°FV.O.C.: 395 g/litre - 3.3 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf) Brush/Roller (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .023"-.027"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 120 micron/4.8 mils (see REMARKS overleaf)Indicated film thickness, wet: 225 micron/9 milsRecoat interval, min: 7 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7903150300CO004
HEMPEL’S ANTIFOULING NAUTIC SP-ACE 79031
SURFACE Existing organotin copolymer based selfpolishing antifouling: Remove possible oil and greasePREPARATION: etc. with suitable detergent, followed by careful high pressure fresh water cleaning. Ensure that any
possible leached surface layer is removed effectively.Allow the surface to dry before recoating.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
In confined spaces such as sea chests and stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR 45182 or according to specification.COAT:
SUBSEQUENT None or as per specification.COAT:
REMARKS: This product contains heavy particles. Stir well before use.By providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process.
Colour: The colour of the system changes in accordance with the colours of the coats applied. The initialcolour may vary within the same shade. Most pronounced in shade 50300. The final colour willappear after exposure to saltwater. This has no influence on the antifouling performance. Light red50300 changes to whitish in direct contact with seawater.Indicated film thickness will vary according to specification. This will alter spreading rate and mayinfluence drying time. In case of multi-coat application, drying time and minimum recoat interval willbe influenced by the number of coats and by the thickness of each coat applied - reference ismade to the corresponding painting specification.Range and control of dry film thickness: 60 micron/2.4 mils to 160 micron/6.4 mils. Keepthinning to a minimum to ensure that correct film thickness is obtained. The proper way ofgoverning the film thickness is to sub-divide the areas to be painted and calculate the amount ofpaint to be applied on each sub-divided area. The exact amount of paint calculated must beapplied evenly on the area. For further information, please consult the corresponding paintingspecification.If roller/brush application exceptionally is utilized (e.g. to line cut) more coats are necessary toachieve the recommended film thickness.Recommended number of coats: As per specification depending on existing hull condition, tradingpattern and intended service life.Recoat interval: No maximum recoat interval, but after prolonged exposure to pollutedatmosphere, remove accumulated contamination by high pressure fresh water cleaning and allowto dry before applying next coat.Undocking: Minimum undocking time depends on number of coats applied, film thickness, and theprevailing temperature. For further information, please consult the corresponding paintingspecification.Maximum undocking time depends on the exposure conditions, degree of air pollution, etc. Themost important factor is to carry out a thorough high pressure fresh water cleaning after prolongedexposure. Outfitting of up to 6 months followed by such cleaning normally presents no problem.Longer outfitting periods to be evaluated from case to case. The recommended maximumundocking interval relates to vertical bottom only. Flat bottom, which has not been exposed todirect sunlight, will for all normal practical building schedules have a no-maximum value.
Note: HEMPEL'S ANTIFOULING NAUTIC SP-ACE 79031 is for professional use only.
Issued: December 2000 - 7903150300CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7903150300CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING NAUTIC®SP-ACE 79051
Description: HEMPEL'S ANTIFOULING NAUTIC SP-ACE 79051 is a high-build, high-solids self-polishingantifouling. It is based on an organotin copolymer reinforced with extra bio-activecompounds.The copolymer hydrolyses in seawater and releases bio-active compounds at a controlledand constant rate. This self-renewing effect ensures that a bio-active interface to theseawater is produced and maintained constantly during the entire service life of thesystem. The system provides a certain control of roughness.
Recommended use: As a high performance fouling control coating for ship hulls operating worldwide atmedium speed. This product is especially suited for vessels with moderate to highactivity and frequent port calls.The actual selection and specification of HEMPEL's selfpolishing antifoulings is basedon input of the operational parameters into our "Computer Aided Specification System"(CAS).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50300 - Red/51110 (see REMARKS overleaf)Finish: FlatVolume solids, %: 54 ± 1Theoretical spreading rate: 4.5 m²/litre - 120 micron
180 sq.ft./US gallon - 4.8 milsFlash point: 31°C/88°FSpecific gravity: 1.7 kg/litre - 14.2 lbs/US gallonDry to touch: 5 (approx.) hours at 20°C/68°FV.O.C.: 410 g/litre - 3.4 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf) Brush/Roller (see REMARKS overleaf)Thinner (max. vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .023"-.027"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 120 micron/4.8 mils (see REMARKS overleaf)Indicated film thickness, wet: 225 micron/9.0 milsRecoat interval, min: 7 hours (20°C/68°F)Recoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7905150300CO004
HEMPEL’S ANTIFOULING NAUTIC SP-ACE 79051
SURFACE Existing organotin copolymer based selfpolishing antifouling: Remove possible oil and greasePREPARATION: etc. with suitable detergent, followed by careful high pressure fresh water cleaning. Ensure that any
possible leached surface layer is removed effectively.Allow the surface to dry before recoating.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
In confined spaces such as sea chests and stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR 45182 or according to specification.COAT:
SUBSEQUENT None or as per specification.COAT:
REMARKS: This product contains heavy particles. Stir well before use.By providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process.
Colour: The colour of the system changes in accordance with the colours of the coats applied. The initialcolour may vary within the same shade. Most pronounced in shade 50300. The final colour willappear after exposure to saltwater. This has no influence on the antifouling performance. Light red50300 changes to whitish in direct contact with seawater.Indicated film thickness will vary according to specification. This will alter spreading rate and mayinfluence drying time. In case of multi-coat application, drying time and minimum recoat interval willbe influenced by the number of coats and by the thickness of each coat applied - reference ismade to the corresponding painting specification.Range and control of dry film thickness: 60 micron/2.4 mils to 160 micron/6.4 mils. Keepthinning to a minimum to ensure that correct film thickness is obtained. The proper way ofgoverning the film thickness is to sub-divide the areas to be painted and calculate the amount ofpaint to be applied on each sub-divided area. The exact amount of paint calculated must beapplied evenly on the area. For further information, please consult the corresponding paintingspecification.If roller/brush application exceptionally is utilized (e.g. to line cut) more coats are necessary toachieve the recommended film thickness.Recommended number of coats: As per specification depending on existing hull condition, tradingpattern, and intended service life.Recoat interval: No maximum recoat interval, but after prolonged exposure to pollutedatmosphere, remove accumulated contamination by high pressure fresh water cleaning and allowto dry before applying next coat.Undocking: Minimum undocking time depends on number of coats applied, film thickness, and theprevailing temperature. For further information, please consult the corresponding paintingspecification.Maximum undocking time depends on the exposure conditions, degree of air pollution, etc. Themost important factor is to carry out a thorough high pressure fresh water cleaning after prolongedexposure. Outfitting of up to 6 months followed by such cleaning normally presents no problem.Longer outfitting periods to be evaluated from case to case. The recommended maximumundocking interval relates to vertical bottom only. Flat bottom, which has not been exposed todirect sunlight, will for all normal practical building schedules have a no-maximum value.
Note: HEMPEL'S ANTIFOULING NAUTIC SP-ACE 79051 is for professional use only.
Issued: April 2002 - 7905150300CO004HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7905150300CO004
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING NAUTIC®SP-ACE 79070
Description: HEMPEL’S ANTIFOULING NAUTIC SP-ACE 79070 is a high-build, high-solids self-polishingantifouling. It is based on an organotin copolymer reinforced with extra bio-activecompounds.The copolymer hydrolyses in seawater and releases bio-active compounds at a controlledand constant rate. This self-renewing effect ensures that a bio-active interface to theseawater is produced and maintained constantly during the entire service life of thesystem. The system provides a certain control of roughness.
Recommended use: As a high performance fouling control coating for vessels operating at low speed or havea low activity such as FPSO's and certain ferries.The actual selection and specification of HEMPEL's selfpolishing antifoulings is basedon input of the operational parameters into our "Computer Aided Specification System"(CAS).
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Red/51110* - light red/50300* (see REMARKS overleaf)Finish: FlatVolume solids, %: 56 ± 1Theoretical spreading rate: 4.7 m²/litre - 120 micron
187 sq.ft/US gallon - 4.8 milsFlash point: 27°C/81°FSpecific gravity: 1.7 kg/litre - 14.2 lbs/US gallonDry to touch: 5 hours (approx) at 20°C/68°FV.O.C.: 420 g/litre - 3.6 lbs/US gallon
*Another shade: black 19990 according to assortment list.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray Brush/Roller (See REMARKS overleaf)Thinner (max. vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .023"-.027"Nozzle pressure: 250 bar/3600 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 120 micron/4.8 mils (See REMARKS overleaf)Indicated film thickness, wet: 225 micron/9 milsRecoat interval, min.: 7 hours (20°C/68°F)Recoat interval, max.: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7907051110CO001
HEMPEL’S ANTIFOULING NAUTIC SP-ACE 79070
SURFACE Existing organotin copolymer based selfpolishing antifouling: Remove possible oil and greasePREPARATION: etc. with suitable detergent, followed by careful high pressure fresh water cleaning. Ensure that any
possible leached surface layer is removed effectively.Allow the surface to dry before recoating.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation.
In confined spaces such as sea chests and stagnant air under large flat bottoms provide adequateventilation during application and drying.
PRECEDING HEMPADUR 45182 or according to specification.COAT:
SUBSEQUENT None, or as per specification.COAT:
REMARKS: This product contains heavy particles. Stir well before use.By providing a constantly active surface during its lifetime, this antifouling is gradually sacrificed inthe process.
Colour: The colour of the system changes in accordance with the colours of the coats applied. The initialcolour may vary within the same shade. Most pronounced in shade 50300. The final colour willappear after exposure to saltwater. This has no influence on the antifouling performance. Light red50300 changes to whitish in direct contact with seawater.Indicated film thickness will vary according to specification. This will alter spreading rate and mayinfluence drying time. In case of multi-coat application, drying time and minimum recoat interval willbe influenced by the number of coats and by the thickness of each coat applied - reference ismade to the corresponding painting specification.Range and control of dry film thickness: 60 micron/2.4 mils to 160 micron/6.4 mils. Keepthinning to a minimum to ensure that correct film thickness is obtained. The proper way ofgoverning the film thickness is to sub-divide the areas to be painted and calculate the amount ofpaint to be applied on each sub-divided area. The exact amount of paint calculated must beapplied evenly on the area. For further information, please consult the corresponding paintingspecification.If roller/brush application exceptionally is utilized (e.g. to line cut) more coats are necessary toachieve the recommended film thickness.Recommended number of coats: As per specification depending on existing hull condition, tradingpattern and intended service life.Recoat interval: No maximum recoat interval, but after prolonged exposure to pollutedatmosphere, remove accumulated contamination by high pressure fresh water cleaning and allowto dry before applying next coat.Undocking: Minimum undocking time depends on number of coats applied, film thickness, and theprevailing temperature. For further information, please consult the corresponding paintingspecification.Maximum undocking time depends on the exposure conditions, degree of air pollution, etc. Themost important factor is to carry out a thorough high pressure fresh water cleaning after prolongedexposure. Outfitting of up to 6 months followed by such cleaning normally presents no problem.Longer outfitting periods to be evaluated from case to case. The recommended maximumundocking interval relates to vertical bottom only. Flat bottom, which has not been exposed todirect sunlight, will for all normal practical building schedules have a no-maximum value.
Note: HEMPEL'S ANTIFOULING NAUTIC SP-ACE 79070 is for professional use only.
Issued: September 2000 - 7907051110CO001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 7907051110CO001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING GLOBIC®81900TIN-FREE
Description: HEMPEL’S ANTIFOULING GLOBIC 81900 is a high solids, tin-free and self-polishingantifouling. Polishing takes place based on an ion exchange resulting in a hydrolysableactivated layer. An inorganic fibre reinforcement of the resin matrix ensures effectivepolishing control and mechanical strength. A powerful bioactive mixture and itsself-renewing effect makes it suitable for protection in the severe fouling conditions ofcoastal waters. The system provides a certain control of roughness.
Recommended use: As a tin-free antifouling for bottom and boottop on vessels operating in coastal trade atlow to medium speeds and (down to) low to medium activity with medium to long idleperiods in temperate climate, short to medium idle periods in tropical climate.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos.: Brown/60600 - Red/51110Finish: FlatVolume solids, %: 58 ± 1Theoretical spreading rate: 5.8 m²/litre - 100 micron
233 sq.ft./US gallon - 4 milsFlash point: 19°C/66°FSpecific gravity: 2.0 kg/litre - 16.6 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 370 g/litre - 3.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf)Thinner (max. vol.): 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8190051110CR006
HEMPEL’S ANTIFOULING GLOBIC 81900
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingantifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.PRECEDING COAT: HEMPADUR 45182, HEMPATEX HI-BUILD 46330 or according to specification.SUBSEQUENTCOAT: None or according to specification.REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surface
during its lifetime, this antifouling is gradually sacrificed in the process.Colour: The GLOBIC’s are never tinted and as the high load of cuprous oxide influences the shade a
certain variation from batch to batch is allowable. Exposure to humid weather shortly afterapplication is likely to cause discolouration. This is a surface phenomenon only and has noinfluence on performance nor recoatability.
Redocking: At redocking, HEMPEL'S ANTIFOULING GLOBIC 81900 can be recoated after thoroughcleaning and removal of any poorly adhering surface layer on the antifouling.Reference is made to SURFACE PREPARATION above. If recoated with other types of antifouling,other surface preparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influence dryingtime. In case of multi-coat application, drying time and minimum recoat interval will be influencedby the number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.number of coats: No maximum recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat. As for other physically drying paints the final hardness will be obtained a few days afterapplication of the last coat. Precautions must be made taking this into account during e.g. outdocking.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service conditions. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL’S ANTIFOULING GLOBIC 81900 is for professional use only.
Issued: April 2002 - 8190051110CR006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8190051110CR006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING GLOBIC®81920TIN-FREE
Description: HEMPEL’S ANTIFOULING GLOBIC 81920 is a high solids, tin-free and self-polishingantifouling. Polishing is based on an ion exchange, resulting in a hydrolysable activatedlayer. An inorganic fibre reinforcement of the resin matrix ensures effective polishingcontrol and mechanical strength. A powerful bioactive mixture and its self-renewingeffect makes it suitable for protection on deep-sea vessels. The system provides acertain control of roughness.
Recommended use: As a tin-free antifouling for bottom and boottop on vessels operating at medium to highspeed and activity with short idle periods.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Brown/60600 - Red/51110Finish: FlatVolume solids, %: 58 ± 1Theoretical spreading rate: 5.8 m²/litre - 100 micron
233 sq.ft./US gallon - 4 milsFlash point: 22°C/72°FSpecific gravity: 2.0 kg/litre - 16.6 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 375 g/litre - 3.1 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf)Thinner (max. vol.): 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8192051110CR006
HEMPEL’S ANTIFOULING GLOBIC 81920
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingantifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.PRECEDING COAT: HEMPATEX HI-BUILD 46330, HEMPADUR 45182 or according to specification.SUBSEQUENT COAT: None or according to specification.REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surface
during its lifetime, this antifouling is gradually sacrificed in the process.Colour: The GLOBIC’s are never tinted and as the high load of cuprous oxide influences the shade a
certain variation from batch to batch is allowable. Exposure to humid weather shortly afterapplication is likely to cause discolouration. This is a surface phenomenon only and has noinfluence on performance nor recoatability.
Redocking: At redocking, HEMPEL'S ANTIFOULING GLOBIC 81920 can be recoated after thoroughcleaning and removal of any poorly adhering surface layer on the antifouling.Reference is made to SURFACE PREPARATION above. If recoated with other types of antifouling,other surface preparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influence dryingtime. In case of multi-coat application, drying time and minimum recoat interval will be influencedby the number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.number of coats: No maximum recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat. As for other physically drying paints the final hardness will be obtained a few days afterapplication of the last coat. Precautions must be made taking this into account during e.g. outdocking.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service condition. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL’S ANTIFOULING GLOBIC 81920 is for professional use only.
Issued: April 2002 - 8192051110CR006HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8192051110CR006
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING GLOBIC®81950TIN-FREE
Description: HEMPEL’S ANTIFOULING GLOBIC 81950 is a high solids, tin-free and self-polishingantifouling. Polishing is based on an ion exchange, resulting in a hydrolysable activatedlayer. An inorganic fibre reinforcement of the resin matrix ensures effective polishingcontrol and mechanical strength. A powerful bioactive mixture and its self-renewingeffect makes it suitable for protection on deep-sea vessels. The system provides acertain control of roughness.
Recommended use: As a tin-free antifouling for bottom and boottop on vessels operating at medium to highspeed and high activity with short idle periods.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Brown/60600 - Red/51110Finish: FlatVolume solids, %: 60 ± 1Theoretical spreading rate: 6.0 m²/litre - 100 micron
241 sq.ft./US gallon - 4 milsFlash point: 25°C/77°FSpecific gravity: 2.0 kg/litre - 16.7 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 355 g/litre - 2.9 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8195051110CR008
HEMPEL’S ANTIFOULING GLOBIC 81950
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingantifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.PRECEDING COAT: HEMPATEX HI-BUILD 46330, HEMPADUR 45182 or according to specification.
SUBSEQUENT COAT: None or according to specification.
REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surfaceduring its lifetime, this antifouling is gradually sacrificed in the process.
Colour: The GLOBIC’s are never tinted and as the high load of cuprous oxide influences the shade acertain variation from batch to batch is allowable. Exposure to humid weather shortly afterapplication may cause discolouration. This is a surface phenomenon only and has no influence onperformance nor recoatability.
Redocking: At redocking, HEMPEL'S ANTIFOULING GLOBIC 81950 can be recoated after thoroughcleaning and removal of any poorly adhering surface layer on the antifouling.Reference is made to SURFACE PREPARATION above. If recoated with other types of antifouling,other surface preparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:Equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influence dryingtime. In case of multi-coat application, drying time and minimum recoat interval will be influencedby the number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.number of coats: No maximum recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat. As for other physically drying paints the final hardness will be obtained a few days afterapplication of the last coat. Precautions must be made taking this into account during e.g. outdocking.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service conditions. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL’S ANTIFOULING GLOBIC 81950 is for professional use only. Issued: April 2002 - 8195051110CR008
HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8195051110CR008
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING GLOBIC®81970TIN-FREE
Description: HEMPEL’S ANTIFOULING GLOBIC 81970 is a high solids, tin-free and self-polishingantifouling. Polishing is based on an ion exchange, resulting in a hydrolysable activatedlayer. An inorganic fibre reinforcement of the resin matrix ensures effective polishingcontrol and mechanical strength. A powerful bioactive mixture and its self-renewingeffect makes it suitable for protection on deep-sea vessels. The system provides acertain control of roughness.
Recommended use: As a tin-free antifouling for bottom and boottop especially on vessels operating atmedium to high speed and high activity with short idle periods and with long drydockingIntervals.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Brown/60600 - Red/51110Finish: FlatVolume solids, %: 57± 1Theoretical spreading rate: 5.7 m²/litre - 100 micron
229 sq.ft./US gallon - 4 milsFlash point: 24°C/75°FSpecific gravity: 1.9 kg/litre - 15.9 lbs/US gallonDry to touch: 2 hours at 20°C/68°FV.O.C.: 385 g/litre - 3.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They aresubject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf) Brush/Roller (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%) 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8197060600CR001
HEMPEL’S ANTIFOULING GLOBIC 81970
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingAntifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.
PRECEDING COAT: HEMPADUR 45182 or according to specification.SUBSEQUENT COAT: None or according to specification.
REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surfaceduring its lifetime, this antifouling is gradually sacrificed in the process.
Colour: The GLOBIC’s are never tinted and as the high load of cuprous oxide influences the shade acertain variation from batch to batch is allowable. Exposure to humid weather shortly afterapplication is likely to cause discolouration. This is a surface phenomenon only and has noinfluence on performance nor recoatability.
Redocking: At redocking, HEMPEL'S ANTIFOULING GLOBIC 81970 can be recoated after thoroughcleaning and removal of any poorly adhering surface layer on the antifouling.Reference is made to SURFACE PREPARATION above. If recoated with other types of antifouling,other surface preparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influence dryingtime. In case of multi-coat application, drying time and minimum recoat interval will be influencedby the number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.number of coats: No maximum recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat. As for other physically drying paints the final hardness will be obtained a few days afterapplication of the last coat. Precautions must be made taking this into account during e.g. Outdocking.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service conditions. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL'S ANTIFOULING GLOBIC 81970 is for professional use only.Issued: April 2002 - 8197060600CR001
HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8197060600CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING OCEANIC®84920TIN-FREE
Description: HEMPEL’S ANTIFOULING OCEANIC 84920 is a high solids, tin-free, self-polishingantifouling. Polishing is based on an ion exchange, resulting in a hydrolysable activatedlayer. An inorganic fibre reinforcement of the resin matrix ensures effective polishingcontrol and mechanical strength.
Recommended use: As an economic tin-free antifouling for bottom and boottop on vessels operating atmedium to high speed and activity with short idle periods, and with drydocking interval ofup to 36 months on vertical sides and up to 60 months on flat bottom.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50220 - Brown/60700 (see REMARKS overleaf)Finish: FlatVolume solids, %: 56 ± 1Theoretical spreading rate: 5.6 m²/litre - 100 micron
225 sq.ft./US gallon - 4 milsFlash point: 20°C/68°FSpecific gravity: 1.8 kg/litre - 15.0 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 390 g/litre - 3.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8492050220CR001
HEMPEL’S ANTIFOULING OCEANIC 84920
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingAntifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature must CONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.PRECEDING COAT: HEMPATEX HI-BUILD 46330, HEMPADUR 45182 or according to specification.SUBSEQUENT COAT: None or according to specification.
REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surfaceduring its lifetime, this antifouling is gradually sacrificed in the process.
Colour: The initial colour may vary within the same shade. Most pronounced in shade 50220. The finalcolour will appear after exposure to saltwater. This has no influence on the antifoulingperformance. Light red 50220 changes to yellowish and brown 60700 to greyish in direct contactwith seawater.
Redocking: At redocking, HEMPEL'S ANTIFOULING OCEANIC 84920 can be recoated after thorough cleaningand removal of any poorly adhering surface layer on the antifouling. Reference is made toSURFACE PREPARATION above. If recoated with other types of antifouling, other surfacepreparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:Equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influence dryingtime. In case of multi-coat application, drying time and minimum recoat interval will be influencedby the number of coats and by the thickness of each coat applied - reference is made to thecorresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.number of coats: No maximum, recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service conditions. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL’S ANTIFOULING OCEANIC 84920 is for professional use only.
Issued: January 2002 - 8492050220CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8492050220CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S ANTIFOULING OCEANIC®84950TIN-FREE
Description: HEMPEL’S ANTIFOULING OCEANIC 84950 is a high solids, tin-free, self-polishingantifouling. Polishing is based on an ion exchange, resulting in a hydrolysable activatedlayer. An inorganic fibre reinforcement of the resin matrix ensures effective polishingcontrol and mechanical strength.
Recommended use: As an economic tin-free antifouling for bottom and boottop on deep-sea going vesselsoperating at medium to high speed and high activity with short idle periods, and withdrydocking interval of up to 36 months on vertical sides and up to 60 months on flatBottom.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Light red/50220 - Brown/60700 (see REMARKS overleaf)Finish: FlatVolume solids, %: 57 ± 1Theoretical spreading rate: 5.7 m²/litre - 100 micron
229 sq.ft./US gallon - 4 milsFlash point: 24°C/75°FSpecific gravity: 1.8 kg/litre - 15.0 lbs/US gallonDry to touch: 4-5 hours at 20°C/68°FV.O.C.: 385 g/litre - 3.2 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subject to normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1.Further reference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Application method: Airless spray (see REMARKS overleaf)Thinner (max. Vol.): 08080 (5%)Nozzle orifice: .027"-.031"Nozzle pressure: 270 bar/4000 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: THINNER 08080Indicated film thickness, dry: 100 micron/4 mils (See REMARKS overleaf)Indicated film thickness, wet: 175 micron/7 milsRecoat interval: As per painting specification
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8495050220CR001
HEMPEL’S ANTIFOULING OCEANIC 84950
SURFACE Newbuilding: as per relevant painting specification.PREPARATION: Maintenance:
Existing old selfpolishing or ablative antifouling: Remove possible oil and grease etc. withsuitable detergent, followed by high pressure fresh water cleaning for a thorough removal of anypossible weak structure of leached antifouling.Allow the surface to dry before coating.Sealer: Whether to use a sealer coat or not depends on the type and condition of the existingantifouling.
APPLICATION The surface must be completely clean and dry at the time of application and its temperature mustCONDITIONS: be above the dew point to avoid condensation. In confined spaces such as sea chests and
stagnant air under large flat bottoms provide adequate ventilation during application and drying.
PRECEDING COAT: HEMPATEX HI-BUILD 46330, HEMPADUR 45182 or according to specification.SUBSEQUENT COAT: None or according to specification.
REMARKS: This product contains heavy particles. Stir well before use. By providing a constantly active surfaceduring its lifetime, this antifouling is gradually sacrificed in the process.
Colour: The initial colour may vary within the same shade. Most pronounced in shade 50220. The finalcolour will appear after exposure to saltwater. This has no influence on the antifoulingperformance. Light red 50220 changes to yellowish and brown 60700 to greyish in direct contactwith seawater.
Redocking: At redocking, HEMPEL'S ANTIFOULING OCEANIC 84950 can be recoated after thoroughcleaning and removal of any poor adhering surface layer or leached layer on the antifouling.Reference is made to SURFACE PREPARATION above. If recoated with other types of antifouling,other surface preparation methods may be required - contact HEMPEL.
Application Standard airless heavy-duty spray equipment:Equipment: Pump ratio: min 45:1 (see Note below)
Pump output: min 12 litres/minute (theoretical)Spray hoses: max 15 metres/50 feet, 3/8" internal diameter
max 3 metres/10 feet, 1/4" internal diameterNote: If longer spray hoses are necessary, up to 50 metres/150 feet hose (½" internal diameter)can be added. The pump ratio must be raised to 60:1 or more, however, the high output capacityof the pump must be maintained.A reversible nozzle is recommended.Filter: Surge tank filter should be 60 mesh (250 micron/10 mils), tip filter should be removed.Filter to be cleaned at regular intervals.
Film thicknesses: Range and control of dry film thickness: 80 micron/3.2 mils to 150 micron/6 mils. Indicated filmthickness will vary according to specification. This will alter spreading rate and may influencedrying time. In case of multi-coat application, drying time and minimum recoat interval will beinfluenced by the number of coats and by the thickness of each coat applied - reference is madeto the corresponding painting specification. Keep thinning to a minimum to ensure that correct filmthickness is obtained. The proper way of governing the film thickness is to sub-divide the areas tobe painted and calculate the amount of paint to be applied on each sub-divided area. The exactamount of paint calculated must be applied evenly on the area. For further information, pleaseconsult the corresponding painting specification.
Recommended As per specification depending on existing hull condition, trading pattern, and intended service life.Number of coats: No maximum recoat interval, but after prolonged exposure to polluted atmosphere, remove
accumulated contamination by high pressure fresh water cleaning and allow to dry before applyingnext coat.
Undocking: Minimum undocking time depends on number of coats applied, film thickness, the prevailingtemperature and the subsequent exposure/service conditions. For further information, pleaseconsult the corresponding painting specification. Maximum undocking time depends on theatmospheric conditions (UV radiation, temperature, degree of atmospheric pollution, etc.).Exposure to the atmosphere in up to 6 months normally presents no problems but extraordinarycontamination may call for a freshwater high pressure hosing - contact Hempel.
Note: HEMPEL’S ANTIFOULING OCEANIC 84950 is for professional use only.
Issued: January 2002 - 8495050220CR001HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8495050220CR001
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®85530CURING AGENT 97530
Description: HEMPADUR 85530 (NAP-GARD 70055) is an amine-adduct, cured epoxy coating. It is ahard, impact and abrasion resistant coating for exterior pipelines. The material hasexcellent properties in respect of temperature resistance, chemical resistance andcathodic disbondment resistance.
Recommended use: Field-applied renovation and repair coating. As a self-primed, high build coating forprotection of exterior steel pipes in severely corrosive environment, including permanentimmersion. HEMPADUR 85530 is an excellent material for repair of coatings which havefailed in service and can be applied to lines while in service temperatures up to90ºC/194ºF.
PHYSICAL CONSTANTS:Finish: GlossyColours: RedShade Numbers: 50700Volume by Solids: 80%Theoretical Spreading Rate: 2.3 m²/litre - 350 microns
92 sq.ft./US gallon - 14.0 milsFlash Point: 29ºC/84ºF, A-Pensky, closed cupSpecific Gravity: 1.6 kg/litre
13.3 lbs/US gallon Dry to Touch: 16 hours at 20ºC/68ºFFully Cured: 7 days at 20ºC/68ºF
For surface preparation, application conditions and coating system, see overleaf.
APPLICATION DETAILS:Mixing Ratio: Base : Hempadur 85539 4 parts by volume
Curing Agent : 97530 1 part by volumeApplication Method: Airless SprayThinner (max.vol.): 08450 (5%)Pot-Life: 4 hours (20ºC/68ºF)Nozzle Orifice: 0.021"-0.023"Nozzle Pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of Tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, wet: 450 micron/18 milsIndicated film thickness, dry: 350 micron/14 milsRecoat interval, min: 16 hours (20ºC/68ºF)Recoat interval, max: 5 days (20ºC/68ºF) (See REMARKS overleaf)
Safety: As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent borne materials in confined spaces or stagnant air. Even whenventilation is provided, respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8553050700
HEMPADUR® 85530
Surface Abrasive blasting to minimum Swedish Standard Sa 2½ with a surface profile corresponding toPreparation: Rugotest No.3, BN 10b or Keane Tator Comparator 3.0, G.S.
Remove any oil, grease and other contaminants by detergent and salts by high pressure freshwater hosing prior to abrasive blasting.
Application The surface must be completely dry and clean with a temperature above the dew point to avoidConditions: condensation. The minimum temperature of the substrate and the temperature of the paint itself
should be above 10ºC/50ºF. The best result is obtained at 20-25ºC/68-77ºF. Maximum steeltemperature at 90ºC/194ºF. Relative humidity - maximum = 85%.In confined spaces, provide adequate ventilation during application and drying.
Preceding Coat: None.
Subsequent Coat: None, or according to specification.
Remarks: The product complies with ARAMCO Engineering Standard APCS-113.
Recoating: The indicated recoat intervals will normally only apply in connection with touch-up to lowdry film thickness.
If maximum recoat interval is exceeded, roughening of the surface is necessary to ensureadhesion.
ARAMCO approved product under APCS 113.
Note: HEMPADUR 85530 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8553050700
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPADUR®PATCH COMPOUND 85540CURING AGENT 97540
Description: HEMPADUR PATCH COMPOUND 85540 (NAP-GARD 70056) is an amine-adduct, curedepoxy coating. It is a hard, impact and abrasion resistant coating for the exterior ofpipelines. The material has excellent properties with respect to temperature resistance,chemical resistance and cathodic disbondment resistance.
Recommended use: Patch compound for repair of damaged coated areas and welded areas. As aself-primed, high build coating for protection of exterior of steel pipes in severelycorrosive environments -including permanent immersion.
HEMPADUR PATCH COMPOUND 85540 (NAP-GARD 70056) is an excellent material forrepair of coatings which have failed in service and can be applied to lines while inservice with temperatures up to 90C/194F.
PHYSICAL CONSTANTS:Finish: GlossyColours: RedShade Numbers: 50700Volume by Solids: 100%Theoretical Spreading Rate: 1.6m²/litre - 625 microns
64 sq.ft./US gallon - 25.0 milsFlash Point: N/ASpecific Gravity: 1.6kg/litre
13.3 lbs/US gallon Dry to Touch: 3 hours at 20ºC/68ºFFully Cured: 7 days at 20ºC/68ºF
The physical constants are subject to normal manufacturing tolerances.Further reference is made to "Explanatory Notes" in the Hempel Book.For surface preparation, application conditions and coating system, see overleaf.
APPLICATION DETAILS:Mixing Ratio: Base : Hempadur 85549 1 part by volume
Curing Agent : 97540 1 part by volumeApplication Method: Spatula or BrushThinner (max.vol.): No thinning requiredPot-Life: 45 minutes (20C/68F)Cleaning of Tools: HEMPEL'S TOOL CLEANER 99610Indicated film thickness, wet: 625 micron/25 milsIndicated film thickness, dry: 625 micron/25 milsRecoat interval, min: 3 hours (20ºC/68ºF)Recoat interval, max 5 days (20ºC/68ºF) (See REMARKS overleaf)
Safety: As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintwith skin and eyes, should be avoided. Forced ventilation should be provided whenworking with solvent borne materials in confined spaces or stagnant air. Even whenventilation is provided, respiratory, skin, and eye protection are always recommendedwhen spraying paint.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8554050700
HEMPADUR®PATCH COMPOUND 85540
Surface Abrasive blasting to minimum Swedish Standard Sa 2½. Remove any oil, grease and otherPreparation: contaminants by detergent and salts by high pressure fresh water hosing prior to abrasive blasting.
Application The surface must be completely dry and clean with a temperature above the dew point to avoidConditions: condensation. The minimum temperature of the substrate and the temperature of the paint itself
should be above 10C/50F. The best result is obtained at 20-25C/68-77F. Maximum steeltemperature at 90C/194F. Relative humidity - maximum = 85%.
In confined spaces, provide adequate ventilation during application and drying.
Preceding Coat: None.
Subsequent Coat: None.
Remarks: The product complies with ARAMCO Engineering Standard APCS-113.
Recoating: Yhe indicated recoat intervals will normally only apply in connection with touch-up to lowdry film thickness. If maximum recoat interval is exceeded, roughening of the surface is necessary to ensureadhesion.
ARAMCO approved product under APCS 113.
Note: HEMPADUR PATCH COMPOUND 85540 is for professional use only.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8554050700
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
Product HEMPADUR®85671CURING AGENT 97371
Description: HEMPADUR 85671 is a two-component, amine adduct cured phenolic epoxy (novolac)coating with very good adhesion and high temperature, water and chemical resistance.
Recommended use: As an interior lining in tanks, pipelines etc. for hot water, brine, crude oil, etc.For coating of potable water tanks.As a primer coat in specific painting systems.
Service temperatures: Dry: In water (maximum gradient 15°C/59°F):Maximum: 160°C/320°F 90°C/194°FMay be specified for design temperatures up to 260°C/500°F dry.For higher temperatures see REMARKS overleaf.
Certificates/Approvals: HEMPADUR 85671 is in accordance with ARAMCO's specificationAPCS 2A, 2B and 2C(See REMARKS overleaf).Approved for use in potable water tanks by the Water Research Centre, England.Approved for aviation fuel storage tanks by ExxonMobil Aviation International Ltd.,England.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Off-white/11630, Light red/50900Finish: FlatVolume solids, %: 68 ± 1Theoretical spreading rate: 6.8 m²/litre - 100 micron
273 sq.ft./US gallon - 4 milsFlash point: 24°C/75°FSpecific gravity: 1.7 kg/litre - 14.2 lbs/US gallonSurface dry: 2-3 hours at 20°C/68°FDry to touch: 6 (approx.) hours at 20°C/68°FFully cured: 10 days at 20°C/68°FV.O.C.: 320 g/litre - 2.7 lbs/US gallon
Shelf life: ½ year (25°C/77°F) from time of production. Depending on storage conditions,mechanical stirring may be necessary before usage.If the shelf life is exceeded please contact HEMPEL for further advice.
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
APPLICATION DETAILS:Mixing ratio for 85671: Base 85675 : Curing agent 97371
8.8 : 1.2 by volume13.8 : 1.0 by weight
Application method: Airless spray. Spinning disc. Brush (touch-up)Thinner (max.vol.): 08450 (See APPLICATION INSTRUCTIONS)Pot life: 3 hours (20°C/68°F) (See REMARKS overleaf)Induction time: 15 minutes (20°C/68°F) (see REMARKS overleaf)Nozzle orifice: .018"-.021"Nozzle pressure: 200 bar/2900 psi
(Airless spray data are indicative and subject to adjustment)Cleaning of tools: HEMPEL’S TOOL CLEANER 99610Indicated film thickness, dry: 100 micron/4 mils (see REMARKS overleaf)Indicated film thickness, wet: 150 micron/6 milsRecoat interval, min: See REMARKS overleafRecoat interval, max: See REMARKS overleaf
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPADUR 85671
SURFACE For optimum performance abrasive blasting to very near white metal Sa 2½-3, with a surfacePREPARATION: profile corresponding to Rugotest No. 3, BN10, Keane-Tator Comparator 3.0 G/S, or ISO
Comparator Rough Medium (G).APPLICATION Use only where application and curing can proceed at temperatures above 10°C/50°F. TheCONDITIONS: temperature of the paint itself must be above 15°C/59°F, best results are obtained at
17-23°C/62-73°F. Relative humidity max. 80%, preferably 40-60%. Apply on a dry and cleansurface with a temperature above the dew point to avoid condensation. Furthermore, reference ismade to special APPLICATION INSTRUCTIONS.Provide adequate ventilation during application and drying in confined spaces.
PRECEDING COAT: None.SUBSEQUENT COAT: None.
REMARKS:High temperature May be used under insulation, pipes and the like in one or two-coat systems. Dry film thicknessesService: should not exceed 250 micron/10 mils. However, at temperatures above 175°C/350°F, max
260°C/500°F, it is recommended to apply max 125 micron/5 mils.The coating should be cured for at least 7 days at 20°C/68°F before exposure to hightemperatures. The coating will discolour at high service temperatures.
Film thicknesses: The minimum total dry film thickness for the system is normally 300 microns/12 mils. May bespecified in other film thicknesses than indicated depending on purpose and area of use. This willalter spreading rate, influence drying time and minimum recoating intervals. The specification mayread up to 125 micron/5 mils dry film thickness per coat, exceptionally 150 micron/6 mils.
Pot life: As per Aramco's requirements, gel time is above 8 hours at a can temperature of 23°C/73°F andabove 2 hours at a can temperature of 40°C/164°F. For optimum spray application properties, themixture should be used within 2 hours at 20°C/68°F.
Recoating MInimum:Intervals: Non-potable water service: 36 hours (20°C/68°F) between the first and second coat, 24 hours
(20°C/68°F) between the second and third coat.Potable water service: 3 days (20°C/68°F) between coats.Maximum:21 days (20°C/68°F).If the maximum recoating interval is exceeded, roughening of the surface is necessary to ensureintercoat adhesion.
Notes to • • The coating is to be applied in a dry film thickness as near as possible to the specified 100application and micron/4 mils (or higher if specified).Recoating: Film formation of each coat has to be of good quality, free from defects such as pinholes and
without any dry spray.• Drying and curing conditions have to be according to APPLICATION CONDITIONS until ful
Curing has been obtained.• No kind of surface contamination must exist except loose dust, abrasives, loose dry-spray,
which is possible to remove by vacuum cleaning before overcoating.The surface MUST be completely clean before overcoating.
• The coating must only be (exceptionally) exposed to strong, direct sunlight (ultraviolet light) inshort periods.
• The coating is to be checked carefully and should have no patchy, whitish, and/or greasyformation, which can hinder adhesion of the subsequent coat.
Note: Exudation of the curing agent causes the mentioned patchy, whitish, and/or greedyformation, which will take place if HEMPADUR 85671 is applied at low temperatures without properinduction time and/or if the coating is exposed to water (rain, condensation) during drying andCuring.
Mixing: The thoroughly mixed BASE and CURING AGENT must be prereacted before application (15minutes at 20°C/68°F). Keep thinning at an absolute minimum. Do not dilute the componentsseparately -only the mixture.
Disclaimer: Any reference to a company standard or specification in this Technical Product Data sheet shallnot be construed as a recommendation by that company to purchase.
Note: HEMPADUR 85671 is for professional use only.
Issued: February 2002 - 8567111630CR002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 2HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductAPPLICATION INSTRUCTIONSFor product description refer to the product data sheet
HEMPADUR®85671CURING AGENT 97371
Scope: These appliation instructions cover surface preparation, application equipment, andapplication of HEMPADUR 85671.
The following are general rules, which may be supplemented with more detaileddescriptions when needed, for instance for major newbuildings/new constructions or extensive repair jobs.
Steel work: For optimum performance, the following is recommended:All welding seams must have a surface finish which ensures that the quality of the paint system will be maintained in all respects. Holes in weldings seams, undercuts, cracks,etc. should be avoided. If found, they must be remedied by welding and/or grinding.
All weld spatters must be removed.
All sharp edges must be removed or rounded off in such a way that the specified film thickness can be built up on all surfaces. The radius of the rounding should be minimum2 mm.
The steel must be of first class quality and should not have been allowed to rust morethan corresponding to grade B of ISO 8501-1:1988. Any laminations must be removed.All steel work (including welding, flamecutting, grinding) must be finished before thesurface preparation starts.
Surface preparation: Prior to abrasive blast cleaning of the steel, remove oil, grease, salts and othercontamination with a suitable detergent followed by high pressure fresh water hosing.Alkali deposits on new welding seams as well as soap traces from pressure testing oftanks to be removed by fresh water and scrubbing with stiff brushes.
Control for absence of contamination according to separate guidelines.
On repair jobs, a rough blasting to remove all loosely adhering materials may be requiredbefore degreasing/washing is carried out.
Old steel: Even after a very thorough cleaning, pits may typically contain contaminationin the form of remnants of chemicals/water soluble salts. For this reason, repeateddetergent washing plus abrasive blasting may be necessary. After the first blasting, avery thorough vacuum cleaning is carried out in order to see if any "chemical bleeding"occurs as well as controls for water soluble salts (reference is made to separateinstructions) are made. Special care should be taken in evaluating pitted areas - ask forspecial guidelines.
For optimum performance, gritblast to very near white metal, Sa 2½-3, ISO8501-1:1988. In practice this requirement is to be understood as white metal Sa 3 atthe moment of abrasive blasting, but allows a slight reduction at the moment of paintapplication.
The resulting surface profile must be equivalent to Rugotest No. 3, min. BN 10,Keane-Tator Surface Comparator, G/S min. 3.0 or ISO/DIS 8503/1 rough MEDIUM (G).
Use steel grit, aluminium silicate, or similar sharp edged abrasives of a good quality freeof foreign matters, soft particles, and the like. Control for absence of contaminationaccording to separate guidelines.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPADUR 85671
In case steel grit is used this must furthermore be controlled so that a proper grain sizedistribution is maintained.
Steel grit with particle sizes of 0.2-1.2 mm or aluminium silicate of 0.4-1.8 mm willusually create the desired surface profile when the air pressure measured at the nozzleis 6-7 bar/85 -100 psi.
The compressed air must be dry and clean. The compressor must be fitted with suitableoil and water traps.
When the abrasive blasting is completed, remove residual grit and dust by vacuumcleaning. Abrasive particles not removed by vacuum cleaning are to be removed bybrushing with clean brushes followed by vacuum cleaning.
The importance of systematic working must be stressed when blasting. Poorly blastedareas covered with dust are very difficult to locate during the blast inspection made afterthe rough cleaning.
Shopprimed and previously painted surfaces: All shopprimer or existing coatingmaterials to be completely removed. Avoid the use of zinc shopprimer wheneverpossible.
However, if the steel is shopprimed with zinc, it is very important that all zinc is removedby abrasive blast cleaning. Separate check procedures will be necessary to demonstratethe effectiveness of removal. More blast cleaning may be deemed necessary! Use of ared zinc shopprimer will facilitate the visual check of the blast cleaning and is considerednecessary in order to obtain an acceptable surface preparation.
Note: Degree of steelwork finish and surface preparation are more detailed describedin HEMPEL’s Technical Standard for Tank Coating Work.
Application equipment: HEMPADUR 85671 is to be applied by airless spray equipment. Stripe coating and minorrepairs can be carried out by brushing.
Airless spray equipment: A large pump is preferred, with a pump capacity of 8-12Litres/minute.
Pump ratio: Min. 45:1Nozzle orifice: .018"-.021"Nozzle pressure: 200 bar (2900 psi)Hoses: To avoid excessive loss of pressure in long hoses, hoses with an
internal diameter of up to 0.5" can be used
(Spray data are indicative and subject to adjustment).
Thinning If required: max. 10% of THINNER 08450, possibly higher if tendency to dry-spray willrequire more thinning eg at higher temperatures. Thinning should only be at the requiredlevel to avoid possible risk of solvent entrapment.Only add thinner to the mixed paint.
Spraying properties are influenced by the induction time (premix time). Too much"thixotropy" will disappear after a certain reaction of the mixed components.
Cleaning of equipment: The whole equipment to be cleaned thoroughly with HEMPEL’S TOOL CLEANER 99610after use.
Mixing, pot life: a. Mix the entire content of corresponding base and curing agent packings. If it isnecessary to mix smaller portions, this must only be done by weighing base andcuring agent in the prescribed weight ratio: 158 parts by weight of base and 11.4parts by weight of curing agent or by volume 8.8 parts by volume base and 1.2parts by volume curing agent.
B. Stir the mixed paint thoroughly by means of a clean mechanical mixer until ahomogeneous mixture is obtained.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 2 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 85671
c. Allow the mixed paint to prereact before application, see table below.
d. Use all mixed paint before the pot life is exeeded. The pot life depends on thepaint’s temperature as shown in table below (valid for a 20 litres can):
(5 minutes)
(1 hours)
10 minutes
2 hours
15 minutes
3 hours
(25 minutes)
(4 hours)
Induction time
Spray application within
(30°C/86°F2))25°C/77°F20°C/68°F(15°C/59°F1))Temperature of mixed paint
1) Below 15°C/59°F the viscosity can be too high for airless spray application.2) Temperatures at 30°C/86°F and above should be avoided due to a risk of dry-spray.
Application procedure: The first full coat is usually applied immediately after vacuum cleaning. First stripe coatto follow afterwards.
Film-build/continuity: With this tank coating intended for aggressive service, it is ofspecial importance that a continuous, pinhole-free paint film is obtained at application ofeach coat. An application technique which will ensure good film formation and nodry-spray on all surfaces must be adopted.
It is very important to use nozzles of the correct size, ie not too big. Select small nozzlesfor spray application of complicated structures, while bigger nozzles may be used forregular surfaces.
A proper, uniform distance of the spray gun to the surface, 30-50 cm, should be aimedat. To obtain good and steady atomizing, the viscosity of the paint must be suitable andthe spray equipment must be sufficient in output pressure and capacity. At high workingtemperatures, use of extra thinner may be necessary to avoid dry-spray.
The paint layer must be applied homogenously and as close to the specification aspossible. The consumption of paint must be controlled and heavy layers must beavoided because of the risk of sags and cracks and solvent retention.
Furthermore, great care must be taken to cover edges, openings, rear sides of stiffenersetc. Thus, on these areas a stripecoat will usually be necessary.
The finished coating must appear as a homogeneous film with a smooth surface andirregularities such as dust, dry spray, abrasives, must be remedied.
Note: In case of old, pit corroded steel, application of a diluted, extra first coat is recommended to obtain better "penetration" in the fine pits. For this purpose, it isrelevant to dilute 5-10%. Application by brush is recommended and film thickness so lowthat the surface is "saturated" only.
Stripe coating: All places difficult to cover properly by spray application should be stripe coated twice bybrushing immediately before the spray application. First stripe coat is applied after thefirst full coat and second stripe coat after second full coat.
The second stripe coat with brush can be replaced with spray application with a smallnarrow nozzle, but still air slots and similar and possible undercuts (welds) and the likewill require brush application.
Film thicknesses: The final dry film thickness of the three coat system must be between 300-600 micron(max. 450 micron below 15°C)/12-24 mils (max. 18 mils below 59°F).
Corresponding to 100 micron/4 mils dry film thickness, the wet film thickness must be150-175 micron/6-7 mils and must be measured regularly.
Normally up to 200 micron/8 mils per coat may be accepted for 100 micron/4 milsspecifications, but at temperatures below 15°C/59°F, it is important not to exceed adry film thickness of 150 micron/6 mils in any area.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 3 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPADUR 85671
Microclimate: The actual climate conditions at the substrate during application:
The minimum surface temperature until full cure is 10°C/50°F.
To ensure an all-over steel temperature of minimum 10°C/50°F, special attention shouldbe paid to possible "cold bridges" eg stiffeners on deck.
In case of steel temperatures lower than 10°C/50°F there is a severe risk of incompletecuring, resulting in a too open film with reduced chemical resistance.
When the outside temperature is lower than 10°C/50°F, it is therefore recommended touse insulation mats on deck and in addition to aim at a general steel temperature of15°C/59°F to minimise the risk of too low steel temperatures.
Furthermore, the steel temperature should be kept reasonably constant - within therange of ± 3°C/5°F is recommended. Any changes of the outside temperature shouldtherefore be carefully monitored and heating equipment calibrated accordingly.
A sudden drop of the steel temperature shortly after application will result in solvententrapment and will cause a dry film containing vacuoles, ie resulting in reducedperformance.
The maximum surface temperature should preferably be below approximately30°C/86°F. In a warm climate it is recommended to carry out application duringnighttime. Application at higher temperatures is possible, but extra care must be takento avoid poor film formation and excessive spray-dust.
The steel temperature must be above the dew point. As a rule of thumb a steel temperature which is 3°C/5°F above the dew point can be considered safe.
The relative humidity should preferably be 40-60%, maximum 80%. In confined spaces,supply an adequate amount of fresh air during application and drying to assist theevaporation of solvent.
Drying and curing, In a dry film thickness of 100 micron/4 mils, a (steel) temperature of 20°C/68°F, aVentilation: relative air humidity of 40-80% and adequate ventilation, HEMPADUR 85671 will be dry
to touch after approximately 4-6 hours and accepts light traffic after approximately 16hours.
Correct film formation depends on an adequate ventilation during drying.
A good guideline for tank coating work is to ventilate to a calculated 10% of LEL duringapplication and until the coating is dry.
One litre undiluted HEMPADUR 85671 gives off in total 81 litres solvent vapour until it iscompletely dry.
The lower explosive limit, LEL, is 1.0%.
To reach a common safety requirement of 10% LEL, the theoretical ventilationrequirement is 81 m³ per litre paint.
Because solvent vapours are heavier than atmospheric air, effective ventilation requiresforced ventilation with exhaust from the lowest part of the tank.
During the following period until full curing a few air shifts per hour will suffice. Takeactions to avoid "pockets" of stagnant air.
Please contact HEMPEL for further advice. Actual safety precautions may require stronger ventilation.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 4 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPEL Product Data
ProductDataData
ProductHEMPADUR 85671
Curing time: Provided that adequate ventilation, recommended relative humidity, specified filmthickness, and recommended minimum recoating interval are kept, the following curingtimes are valid:
4 days6 days7 days8 days10 days14 days18 daysCuring time
40°C/104°F35°C/95°F30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteeltemperature
Recoating intervals: Provided observance of the above stated ventilation and relative humidity for thefollowing recoating intervals in relation to the (steel) temperature are valid:
14 hours
14 hours
30 hours
8 days
18 hours
12 hours
36 hours
11 days
24 hours
16 hours
2 days
14 days
36 hours
24 hours
3 days
21 days
60 hours
40 hours
5 days
36 days
90 hours
60 hours
7½ days
53 days
Minimum, non-potable water service
- between the first and the second coat
- between the second and the third coat
Potable water service,all coats; minimum:
Maximum
35°C/95°F30°C/86°F25°C/77°F20°C/68°F15°C/59°F10°C/50°FSteel temperature
* Absolute minimum temperature recommended.
The maximum relative humidity before and between the coats should not exeed 80% andthe steel temperature should always be above the dew point, in practice minimum3°C/5°F above the dew point.
Conditions for Dry spray is not acceptable as this will reduce the protective characteristics of the paintpaint application work: and make later tank cleaning difficult. Dry spray can be avoided by using adequate
stagings, spraying equipment and methods.
Hold spray gun at a right angle to and about 30 cm/1 foot from surface making evenparallel passes at a rate to produce the specified wet film thickness as per specification.
Avoid dry spray (overspray creating exessive paint mist), e.g. by using a smaller fan angle, and the lowest possible pressure. A small fan angle should also be used, if sprayapplication is used, for "stripe coating" of for instance reverse sides of stiffeners. Eachlayer must be applied homogeneously, must be free from pinholes and other defects andas near above the specification of 100 micron/4 mils dry film thickness, as possible.The consumption of paint must be controlled, and heavy layers must be avoidedbecause of the risk of saggings, cracks and solvent retention.
Surface irregularities such as dry spray, saggings, exaggerated thickness or embeddeddust or abrasives will have to be remedied.
If a sandpapering between layers, for instance on the bottom, is needed, great caremust be taken to avoid damaging of otherwise intact surfaces. When using mechanicalmeans only lightweight equipment should be used, orbital sander is recommended. Yet,avoid sandpapering on top of welds or irregularities or near to vertical surfaces.
The finished coating must appear as a homogeneous surface without pores, runners orpollution of any kind.
Control of For the standard specification following applies to the dry film thickness:dry film thicknesses:
The minimum dry film thickness is 300 micron/12 mils, maximum recommendedthickness is 600 micron/24 mils (below 15°C/59°F: 450 micron/18 mils). The minimumdry film thickness is evaluated according to the "80-20" rule, ie no more than 20% of the total number of individual measurements must be lower than the minimum dry filmthickness, and the lowest individual measurement must be at least 80% of minimum dryfilm thickness, ie 240 micron/9.6 mils. The maximum dry film thickness can also beevaluated according to the "80-20" rule.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 5 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
HEMPADUR 85671
Dry film thickness control must not be carried out within the first 24 hours afterapplication of final coat (20°C, sufficient ventilation). The measurement must be carriedout using an electromagnetic dry film thickness gauge calibrated with shims placed on asmooth steel substrate.
Taking into use: Do not use the tank or pipeline before the coating is properly cured. Reference is madeto curing time on page 5. When cured, but before taking the tank into use for potablewater, fill twice with water each time for a period of no less than 24 hours and finallyflush with fresh water.
Repairs: It is of great importance that all damage to the coating is repaired.
Repair shall be started as soon as possible. Repair of mountings for stagings, etc. Musttake place in connection with the dismantling of the stagings, the tempo of which shouldbe adjusted to the touch-up procedure.
It is important that the repaired areas, as well as the rest of the coated areas, are fullycured before the tank is taken into use or washed by the tank cleaning system.
The extent of damage to the coating can be evaluated by a seawater test: Wash thetanks with clean seawater by means of the tank cleaning machines until profiles and/orheating coils on tanktop is covered. Allow the water to stay for minimum 3 days, afterwhich period the tank is emptied and cleaned with clean fresh water to remove salts.
The repair process: General: Before mechanical treatment is started, surfaces to be repaired have to becleaned for any salts and other contamination.
Areas less than 5 x 5 cm:
The surface preparation can be executed by grinding to a clean rough metal surface,feathering edges of intact coating and slightly sanding the adjacent surface.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up to full film thickness with minimum 3 coats of HEMPADUR 85671.
Areas up to 1 sq.m:
The surface preparation must be executed by vacuum blasting or open nozzle blasting sothat the steel has a proper roughness and a cleanness to Sa 3 according to ISO8501:1988. The overlapping zone must be sanded or sweep blasted to ensure a goodadhesion of the new paint.
Clean and wash with HEMPEL’S THINNER 08450.
Touch-up to full film thickness with minimum 3 coats HEMPADUR 85671.
Areas above 1 sq.m. or areas where several damaged spots are concentrated:
Treatment: Repeat the original specification.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Issued: February 2002 - 8567111630CR002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 6 of 6HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 8567111630CR002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S NAVI WASH* 99330
Description: HEMPEL’S NAVI WASH 99330 is a concentrated detergent based on aromatichydrocarbons, glycol ether solvent, emulsifiers, and water.
Recommended use: For cleaning and degreasing, especially of surfaces heavily contaminated with oil and
grease. Residues must be removed completely before painting.
PHYSICAL CONSTANTS: Colours/Shade nos: Transparent/00000Active matter: 60%Flash point: 32°C/90°FSpecific gravity: 0.9 kg/litre
7.5 lbs/US gallonpH value: 9-10 undilutedV.O.C.: 420 g/litre - 3.5 lbs/US gallon
Application method: Apply by (low pressure) spray or by soft brushes.
Remarks: May be used as delivered or diluted maximum 50% with fresh water. The undiluted or slightly diluted product has a dissolving effect on most physically
drying coatings. In such cases, HEMPEL'S LIGHT CLEAN 99350 is recommended. In extreme cases with heavy oil and grease contamination, HEMPEL'S NAVI WASH99330 diluted 50% with fresh water, may, however, be suitable for cleaning ofphysically drying paints. It is recommended to try the effect on a small, representativearea before proceeding with the work proper.For cleaning of engines HEMPEL’S NAVI WASH 99330 can be diluted with HEMPEL'STHINNER 08080 or 08230. After approximately 15 minutes but within 2 hours hose down the surface with freshwater. Scrubbing increases the cleaning effect. The surface is free from oil and greasewhen the water does not form beads. A residual film of HEMPEL’S NAVI WASH 99330 will impair adhesion of any subsequentcoat of paint. Total removal of residues is therefore necessary when the treatedsurface is to be painted, e.g. by high pressure fresh water hosing, or by scrubbingcarefully with plenty of fresh water.
Note: HEMPEL'S NAVI WASH 99330 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Harmful or fatal if swallowed; immediately seek medicalassistance if swallowed. Avoid inhalation of possible solvent vapours or paint mist, aswell as paint contact with skin and eyes. Apply only in well ventilated areas and ensurethat adequate forced ventilation exists when applying paint in confined spaces or whenthe air is stagnant. Always take precautions against the risks of fire and explosions.
Issued: September 1996-9933000000CO005HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9933000000CO005
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S LIGHT CLEAN 99350
Description: HEMPEL’S LIGHT CLEAN 99350 is a solvent-free concentrated alkaline cleaner basedon emulsifiers, surface-active agents and water. The product is biodegradable.
Recommended use: For cleaning and degreasing of painted surfaces before recoating. Especially suited forremoval of dirt, soot and u.v. light degraded surface-layers. Suited for use in highpressure cleaning equipment.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent/00000Flash point: Non-flammableSpecific gravity: 1.1 kg/litre
9.2 lbs/US gallonpH value: App. 12 undiluted
App. 11 (10% solution)V.O.C.: 0 g/litre - 0 lbs/US gallon
Application method: Apply by stiff brush or by spraying using lowest possible pressure. To be diluted withfresh water: 1-20 parts of fresh water to 1 part of HEMPEL’S LIGHT CLEAN 99350. After5 minutes the surface must be high pressure hosed with fresh water or carefullyscrubbed with plenty of fresh water until all residues have been removed. If HEMPEL’SLIGHT CLEAN 99350 leaves a white film, it can be removed with warm water.
Remarks: Shake HEMPEL’S LIGHT CLEAN 99350 before use.Due to alkaline properties HEMPEL’S LIGHT CLEAN 99350 is not suited for cleaning ofself-polishing antifoulings and for cleaning of aluminium.Do not expose to frost.
Note: HEMPEL'S LIGHT CLEAN 99350 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limitedto, protection of lungs, eyes and of the skin, medical treatment in case of swallowingthe paint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: May 2000 - 9935000000CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9935000000CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL'S ABSENTA®99590
Description: HEMPEL'S ABSENTA 99590 is a gelatinous substance with a strong dissolving effect onmost kinds of old paint and varnish.
Recommended use: As a paint and varnish remover. Can also be used for restoring stiffened paint brushesand rollers. (See REMARKS)
Availability: Subject to confirmation
PHYSICAL CONSTANTS:Colour: TransparentShade No: 00000Volume Solids: 4%Flash Point: Not measurableSpecific Gravity: 1.2 kg/litre
10.0 lbs/US gallon
APPLICATION DETAILS:Application Method: Apply HEMPEL'S ABSENTA 99590 by brush in a thick layer and leave it on for 5-10
minutes after which the paint or varnish is removed with a scraper. Should not normallybe left on for more than 1 hour as difficulties may arise when scraping. Alternatively,cover the area in question with a polyethylene sheet to prevent evaporation.On very thick layers of old paint, or if the softened paint dries up, repeat the process.
The consumption depends on the nature and the thickness of the paint or varnish to beremoved. As a guideline a spreading rate of 3-6 m2 per litre/120-245 sq.ft per US gallonis indicated.
Remarks: Do not use at temperatures above 25C/77F, in direct sunlight, or in strong wind as theevaporation will then proceed too rapidly - alternatively cover with a polyethylene sheet.
Subsequent Treatment
Wood & Steel: Wash down thoroughly with a weak solution of ammonia water (oak,teak, and mahogany may be discoloured by ammonia), followed by hosing down withfresh water.
Brushes & Rollers: Rinse thoroughly in fresh water and hang up.
Cautions: Unscrew the lid with caution due to risk of over-pressure in the tin. Do notuse on cloth, linoleum, plexiglass, plastics, asphalt floors, and similar. Containschlorinated solvent. Do not apply on hot surfaces. Do not store or use in directsunshine or near to heat and open flame (eg: welding and burning) as poisonous gascan develop.
Note: HEMPEL'S ABSENTA 99590 is for professional use only.
Safety: Packings are provided with applicable safety labels which should be observed. Inaddition, national or local safety regulations should be followed.As a general rule, inhalation of solvent vapours or paint mist, and contact of liquid paintand paint remover with skin and eyes should be avoided. Forced ventilation should beprovided when working with paint remover in confined spaces or stagnant air. Evenwhen ventilation is provided, respiratory, skin, and eye protection are alwaysrecommended.
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9959000000
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMPEL’S TOOL CLEANER 99610Description: HEMPEL’S TOOL CLEANER 99610 is a blend of strong solvents for cleaning of tools that
have been used for mixing or application of two-component epoxy products. It has bettercleaning properties than epoxy thinners.
Does not contain chlorinated solvent.
Recommended use: For cleaning of brushes, paint rollers, spray equipment, and other tools which have beenused for mixing or application of HEMPADUR products.
Do not use as thinner for any paint.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade Nos: Transparent/00000Volume solids: 0%Flash point: 28°C/82°FSpecific gravity: 0.9 kg/litre
7.5 lbs/US gallonV.O.C.: 890 g/litre - 7.4 lbs/US gallon
Remarks: Cleaning should take place as soon as possible after use of the tools. Spray equipment does not require rinsing or flushing after use of HEMPEL’S TOOLCLEANER 99610.Do not use on cloth, linoleum, plexiglass, plastics, asphalt floors, and similar.Do not use it for cleaning of equipment after application of polyurethanes(HEMPATHANEs).
Note: HEMPEL'S TOOL CLEANER 99610 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: October 1999 - 9961000000CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9961000000CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®THINNER 99800Description: HEMUCRYL THINNER 99800 is a water-borne thinner containing a thickener to avoid
sagging.
Recommended use: For dilution of water-borne acrylic paints when low relative humidity are causing anunacceptable level of dry spraying. Can be added up to 50%* by volume to slow downthe drying time without reduction of the maximum possible dry filmthickness.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent/00000Volume solids, %: 0,9Flash point: Non-flammableSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonV.O.C.: 0 g/litre - 0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
Remarks: Recommended to be used together with HEMUCRYL PRIMER HI-BUILD 18030,HEMUCRYL ENAMEL HI-BUILD 58030 or HEMUCRYL TOPCOAT HI-BUILD 58230. Add HEMUCRYL THINNER 99800 to the paint and stir well with a mechanical stirrer.The paint will get a gel-like consistency when HEMUCRYL THINNER 99800 has beenadded.
The table below shows the wet film thickness is going to be increased to obtain thespecified dry filmthickness and the increase in drying time for different levels of addition. The increase in drying time is calculated on basis of a paint with a volumesolid on 44% (58030).
3 hours50503 hours4040
2½ hours30302½ hours20202¼ hours 1010
Minimum recoatinginterval (75 micron dry)
Increase wetfilmthickness %
Volume %99800 added
* It is recommended to add max. 20% to HEMUCRYL PRIMER HI BUILD 18030.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. Avoid inhalation, avoid contact with skin and eyes, and donot swallow. Take precautions against possible risks of fire or explosions as well asprotection of the environment. Apply only in well ventilated areas.
Note: HEMUCRYL THINNER 99800 is for professional use only.
Issued: June 2001 - 9980000000CO003HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9980000000CO003
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.
HEMPEL Product Data
ProductDataData
ProductHEMUCRYL®BRUSH AGENT 99810Description: HEMUCRYL BRUSH AGENT 99810 is a water-borne compound containing a
flow-improving thickener.
Recommended use: Addition of HEMUCRYL BRUSH AGENT to a water-borne acrylic paint will increase thehigh shear viscosity of the paint thereby making it more suitable for application by brushor roller. Eg relevant for touch-up work.
Availability: Part of Group Assortment. Local availability subject to confirmation.
PHYSICAL CONSTANTS:Colours/Shade nos: Transparent/00000Volume solids, %: 8 ± 1Flash point: Non-flammableSpecific gravity: 1.0 kg/litre - 8.3 lbs/US gallonV.O.C.: 0 g/litre - 0 lbs/US gallon
The physical constants stated are nominal data according to the HEMPEL Group's approved formulas. They are subjectto normal manufacturing tolerances and where stated, being standard deviation according to ISO 3534-1. Furtherreference is made to "Explanatory Notes" in the HEMPEL Book.
Remarks: Recommended as an additive to HEMUCRYL PRIMER HI-BUILD 18030, HEMUCRYLENAMEL HI-BUILD 58030 or HEMUCRYL TOPCOAT HI-BUILD 58230 when a brushapplicable paint is required.Add HEMUCRYL BRUSH AGENT 99810 in 3-8% by volume to the paint and stir well with amechanical stirrer. The viscosity of the paint will increase proportional to the amount ofthickener added.After addition of HEMUCRYL BRUSH AGENT 99810, the paint is less suitable for airlessapplication as this may cause microfoaming in the paint surface.
Note: HEMUCRYL BRUSH AGENT 99810 is for professional use only.
Safety: Handle with care. Before and during use, observe all safety labels on packaging andpaint containers, consult HEMPEL Material Safety Data Sheets and follow all local ornational safety regulations. This goes for personal protection such as, but not limited to,protection of lungs, eyes and of the skin, medical treatment in case of swallowing thepaint or in case of other direct contact with the paint. Take necessary precautionsagainst possible risks of fire or explosions as well as protection of the environment.Apply only in well ventilated areas and ensure that adequate forced ventilation existswhen applying paint in confined spaces or when the air is stagnant.
Issued: May 2000 - 9981000000CO002HEMPEL’S MARINE PAINTS A/S
Reissued by: HEMPEL PAINTS (QATAR) W.L.L. & Page 1 of 1HEMPEL PAINTS (EMIRATES) L.L.C. May 2002 - 9981000000CO002
This Product Data Sheet supersedes those previously issued. For definition and scope, see explanatory notes to applicable ProductData Sheets. Data, specifications, directions and recommendations given in this data sheet represent only test results or experienceobtained under controlled or specially defined circumstances. Their accuracy, completeness or appropriateness under the actualconditions of any intended use of the Products herein must be determined exclusively by the Buyer and/or User. The Products aresupplied and all technical assistance is given subject to HEMPEL's GENERAL CONDITIONS OF SALES, DELIVERY AND SERVICE, unlessotherwise expressly agreed in writing. The Manufacturer and Seller disclaim, and Buyer and/or User waive all claims involving, anyliability, including but not limited to negligence, except as expressed in said GENERAL CONDITIONS for all results, injury or direct orconsequential losses or damages arising from the use of the Products as recommended above, on the overleaf or otherwise. Productdata are subject to change without notice and become void five years from the date of issue.