Materials & Corrosion
Why worry about corrosion?
“One large chemical company spent more than $400,000 per year for corrosion maintenance in its sulfuric acid plants, even though the corrosion conditions were not considered to be particularly severe.”
Why worry about corrosion?
“A refinery employing a new process developed a serious problem after just 16 weeks of operation; some parts showed a corrosion loss of as much as 1/8 inch.”
Why worry about corrosion?
“The trend in the chemical process industries toward higher temperatures and pressures has made possible new processes or improvements in old processes. Higher temperatures and pressures usualy involve more severe corrosion conditions. Many of the present day operations would not have been possible or economical w/o the use of corrosion-resistant materials.”
Why Worry about Corrosion?
• Safety/Health• Environment• Operability• Profitability• Product Quality• Appearance of Facilities/Equipment
– Badly corroded and rusted equipment in a plant would leave a poor impression on the observer
Examples of Corrosion
• Erosion-corrosion of copper water pipe (tubing)
• Chloride Stress corrosion cracking of stainless steels
• Chloride pitting of stainless steel
• Nitric acid attack of titanium tubing
Corrosive Environments
• Atmospheric– Industrial– Urban– Rural– Marine
• Water– Seawater– Freshwater– Tapwater– Treated water
Corrosive Environments
• Soil• Industrial – commercial/institutional
Definition of corrosion
• Is the chemical or electro-chemical reaction between a material – usually a metal – ant it’s environment that produces a deterioration of the material and it’s properties.
Factors Influencing Corrosion
• Design, fabrication & materials– Design/configuration– Forming, welding, heat treating– Metallurgy, composition
• Environmental factors– Process chemistry including:
• pH• Dissolved materials
– Salt– Metal ions– Gases (O2, N2, CO2, ammonia, chlorine etc.)
• Suspended matter• Temperature• Flow velocity• Micro-organisms
Types of Corrosion
2 Main Types:1. General corrosion is the loss material over
the entire surface, at a relatively constant rate. The metal is thinned fairly uniformly, without appreciable localized attack.
2. Localized Attack is specific to certain areas of the material, and can take many forms.
Forms of Localized Attack
• Pitting is corrosion that produces sites of localized attack that are small relative to the overall exposed surface area. It is the most common form of corrosion in aqueous environments, and the major cause of corrosion service failures in
the chemical processing industry.
Forms of Localized Attack cont’d
• CREVICE CORROSION is attack at narrow spaces or gaps between two metal surfaces, or between a metal and non-metal. It can occur at cracks or seams in a metal, or under a washer, gasket, or deposit.Crevice corrosion results from a difference between the chemistry of the bulk environment and that in or at the crevice.
Forms of Localized Attack cont’d
• BIOLOGICAL ATTACK is that which caused or accelerated by organisms on the affected surface. Fouling organic deposits may cause crevice corrosion, or organisms may produce chemicals that cause corrosion.
• EROSION CORROSION is acceleration of material loss due to the combined effects of corrosion plus removal of material by the moving fluid.
Forms of Localized Attack cont’d
• CAVITATION & IMPINGEMENT is material loss due to collapse of voids or cavities in the fluid, due to pressure changes (cavitation), or due to impingement of liquid droplets. This may be strictly mechanical damage, or may
be worsened by the effects of corrosion.
S.E.M. What is it?
Forms of Localized Attack cont’d
• Fretting is a process combining wear and corrosion in removal of material from contacting solid surfaces. It typically involves very small relative movements of the components, oxidation of the surfaces, and abrasion by the oxidation products. It often occurs between a shaft and a component fitted on the shaft.
Forms of Localized Attack cont’d
• INTERGRANULAR ATTACK is corrosion at the boundaries of a metal grain, with little or no attack of the grain. It results in weakening of the metal, or separation at the grain boundary. (The composition and corrosion resistance of a metal grain varies from the surface to the interior.)
Forms of localized Attack cont’d
• DEALLOYING ATTACK is preferential removal of one constituent of an alloy in a corrosive environment. An example is the “dezincification” of brass, in which zinc is leached from the brass in some aqueous streams, leaving a weak structure of copper and copper oxide.
Forms of Localized Attack cont’d
• GALVANIC ATTACK is attack of a metal that is in electrical contact with a more noble metal, or a non-metallic conductor, in a corrosive environment. Examples are: corrosion of copper or brass couple to steel in an aqueous environment: or corrosion of a zinc coating on steel. The latter is done intentionally to protect the steel, as in roofing nails, fencing, corrugated galvanized sheets, etc.
Types of Corrosion
Environmentally-induced cracking:• Stress-corrosion cracking (SCC) is due to the
combined effects of a corrodent and sustained tensile stress. SCC of AUSTENTITIC (300-series) stainless steels by chorides is a major problem in the chemical industry. SCC can
be caused in copper alloys in
nitrates, and in steel by caustic.
Environmentally-induced Cracking
• CORROSION FATIGUE occurs in a cyclically loaded part in a corrosive environment. It occurs
at lower stress levels or after fewer cycles that would be the case in the absence of the corrosive environment.
Environmentally-induced Cracking
• Hydrogen-induced cracking or Embrittlement is reduction of the ductility or toughness of a metal due to the presence of atomic hydrogen. The hydrogen can be present due to introduction into the molten metal, or through absorption by the solid metal.
Environmentally-induced Cracking cont’d
• LIQUID METAL EMBRITTLEMENT is brittle failure of a normally ductile metal when coated with a thin film of liquid metal followed by stressing in tension. Examples of LME may occur when steel is brazed, soldered, welded, or plated, or dip-coated with zinc, cadmium, or tin.
Corrosion Control
• Materials selection• Design• Method of Operation• Barriers/coatings
– Paint systems– Linings – e.g. rubber or plastic– Cladding – metal on metal– Galvanizing– Plating– Glass/ceramic – e.g. porcelain on steel
• Inhibitors• Cathodic/Anodic Protection
MaterialsSelection
Corrosionresistance
StrengthAppearance
Cost
Fabricability Availability
Factors affecting choice of an engineering material
Corrosion-resistant Materials
All materials are resistant to corrosion in some specific environments. For example, carbon steel is resistant to many process and aqueous liquids. It may corrode slowly or not at all. Steel is the main material used in chemical plant equipment.
The term corrosion-resistant is used to refer to materials that resist attack in specific or unusually corrosive environments.
Corrosion-Resistant Materials
The following is a list of a few materials used in various corrosive services:
• Stainless steels• Nickel & nickel alloys• Reactive & refractory metals such as
tantalum, titanium, zirconium, & their alloys
• Copper/copper alloys (brasses, bronzes)
Corrosive-Resistant Materials
• Aluminum• Lead• Chromium• Plastics, such as teflon, PVC, nylon, polypropylene,
polyethylene, etc.• Rubbers/elastomers such as nitrile (NBR or BUNA-N)
EPDM (e.g. NORDEL), Viton, NEOPRENE, butyl, etc.• COMPOSITES, e.g. fiber-reinforced plastic (FRP,
fiberglass)• GLASS & CERAMICS, tile, porcelain, brick
STAINLESS STEELS
• Iron-based alloys, with at least 10.5% Chromium• Chromium-rich oxide surface film
– “passive”– Forms and heals in oxygen
• Additives of nickel, molybdenum, copper, titanium, aluminum, silicon, niobium, nitrogen, sulphur, selenium
• Processing applications, cutlery, decorative, health and sanitary, dairy, transportation, medical
STAINLESS STEELS
FERRITIC
• Iron plus 10-25% chromium (BCC)
• Magnetic
• High strength, limited toughness
• Good ductility & fabricability
• Examples : 405,409, 429, 430, 434, 442, monit
STAINLESS STEELS
AUSTENTITIC• Iron plus chromium plus nickel (FCC)• Also molybdenum, manganese, copper, nitrogen, others• Non-magnetic (Usually)• Relatively low strength• High ductility/toughness• Susceptible to chloride attack (SCC, pitting)• Good fabricability• Examples: 201, 202, 205, 301, 302, 303, 304, 304L, 305, 308, 309, 310,316, 316L, 317,
321, 330, 347, 348, 384, 904L, nitronic types, Alloy 20, 20Cb-3, sanicro 28
STAINLESS STEELS
DUPLEX
• Mixed structure of BCC ferrite & FCC austenite
• High corrosion resistance, SCC-resistant
• High strength, good toughness
• Examples: 329, 2205, 2507, 3RE60, 7-Mo PLUS, Ferralium 255
STAINLESS STEELS
MARTENSITIC• Martensitic structure (distorted BCC)• Lower chromium: 10-18 %• Higher carbon: 0.15% min• Magnetic, hardenable• High strength – limited toughness• Lower corrosion resistance• Examples: 403, 410, 414, 416, 420, 431, 440
STAINLESS STEELS
PRECIPITATION HARDENING• Chromium-nickel grades with copper, aluminum,
titanium additions• Hardened by ageing at moderately elevated
temperatures• Good formability (form then harden)• Susceptible to heat damage• Good corrosion resistance• Examples: 15-5 PH, 17-4 PH, 17-7 PH, PH 14-4 Mo,
Custom 450, custom 455
OTHER ALLOYS
COPPER & IT’S ALLOYS
Copper
• 99+% copper
• Water service, marine, heat exchangers, architectural
• Not heat treatable
• Resists biofouling
COPPER & IT’S ALLOYS
BRASSES
• 5-45% Zinc
• Dealloying above 15% zinc
• Tin added to stop dealloying (admiralty and naval brasses)
COPPER & IT’S ALLOYS
BRONZES
• Phosphour bronze – 10% tin
• Silicon bronze – 1-3% Si
• Aluminum bronze – 5-10% Al
COPPER & IT’S ALLOYS
CUPRO-NICKELS
• 90/10 Cu/Ni, 80/20, 70/30
• Resistant to seawater, erosion, pitting
ALUMINUM & IT’S ALLOYS
• Protected by barrier oxide film• Corrodes at low and high pH• Resistant to nitric acid (oxidizing)
1xxx – 99+% Al
2xxx • alloyed with copper• Strong, heat-treatable• Lower corrosion resistance
ALUMINUM & IT’S ALLOYS
4xxx – alloyed with Si
5xxx – Al-Mg-Mn, Al-Mg-Cr, Al-Mg-Mn-Cr
NICKEL & IT’S ALLOYS
NICKEL
• Alloy 200, commercially pure
• Plating/cladding
• Resistant to caustic
MONEL
• Alloy 400, approx. 30% copper
• Very good fabricability
NICKEL & IT’S ALLOYS
NICKEL-MOLY
• Hastelloy B, B-2
• Resistant to HCI
NICKEL-CHROMIUM
• Inconel or Alloy 600
(77% Ni-15%Cr-bal Fe)
NICKEL & IT’S ALLOYS
Ni-Fe-Cr• Incoloy or Alloy 800 (21Cr-32Ni-bal Fe)• Resistant to chlorides
Ni-Fe-Cr-Mo• Includes Alloys 20 & 20Cb3, Incoloy 825,
Hastelloy F & G• Increased resistance to sulphuric, phosphoric, and
organic acids and to SCC and chloride pitting
NICKEL & IT’S ALLOYS
Ni-Cr-Mo
• Hastelloy C, C276, C-22
• Inconel or Alloy 625
• Resistant to hot acid mixtures
NON-METALLICS
PLASTICSThermoplastics• Polyethylene, PP, ABS, PVC, CPVC,
PVDC• Fluorocarbons – PTFE or teflon, FEP, PFA,
CTFE etc.• Nylon• Acetals, acrylics, polycarbonates, styrenes
Plastics Cont’d
Thermosetting resins• Usually reinforced with glass• Epoxy, phenolics, polyester, furanesRubber & Elastomers• Synthetic & natural rubbersCarbon & graphiteGlassCeramics & RefractoriesConcreteWood
METALS
MATERIAL Advantages Disadvantage
Carbon Steel Low cost, readily available, resists abrasion, standard fabrication, resists alkali
Poor resistance to acids & strong alkali, often causes discolouration and contamination
Stainless steel Resists most acids, reduces discolouration, available with a variety of alloys, abrasion less than mild steel
Not resistant to chlorides, more expensive, fabrication more difficult, alloy materials may have catalytic effects
Monel-Nickel Little discoloration, contamination, resistant to chlorides
Not resistant to oxidizing environments, expensive
Hasteloy Improved over Monel-Nickel More expensive than Monel-Nickel
Other exotic metals
Improves specific properties Can be very high cost
From "Analysis, Synthesis, and Design of Chemical Processes" Turton, Bailie, Whiting, Shaeiwitz
Non-metals
Material Advantages Disadvantage
Glass Useful in laboratory and batch system, low diffusion at walls
Fragile, not resistant to high alkali, poor heat transfer, poor abrasion resistance
Plastics Good at low temperature, large variety to select from with various characteristics, easy to fabricate, seldom discolours, minor catalytic effects possible
Poor at high temperature, low strength, not resistant to high alkali conditions, low heat transfer, low cost
Ceramics Withstands high temperatures, variety of formulations available, modest cost
Poor abrasion properties, high diffusion at walls (in particular hydrogen), low heat transfer, may encourage catalytic reactions
Tensile Strength of Steel
0
200
400
600
800
1000
1200
1400
ambient 400 C 550C
carbon steelstainless steel3-D Column 3
Data in Text
In pages 168-174 of the text you can find a table recommending specific materials for specific chemicals, and descriptions of some common alloys
The Methanol Project
• Process streams in the methanol section are not corrosive
• Sulphur can cause problems in earlier stages, but that is not our problem
• Long term storage (days) of methanol in carbon steel can cause side reactions that generate impurities which interfere with proper operation of fuel cells
Workshop
• What material should we use for the majority of the equipment in the methanol reaction and purification section?
• What equipment requires other material?
• What would be some good choices for that material?