Paul Ashall, 2007
Operating considerations
Membrane fouling Concentration polarisation (the layer of solution
immediately adjacent to the membrane surface becomesdepleted in the permeating solute on the feed side of themembrane and enriched in this component on the permeateside, which reduces the permeating componentsconcentration difference across the membrane, therebylowering the flux and the membrane selectivity)
Flow mode (cross flow, co-flow, counter flow)
Thermodynamic driving force (P, T, c etc) for transportthrough membrane is activity gradient in membrane
Flux (kg m-2 h-1)
Selectivity
Membrane area
8/8/2019 Membrane Technology 10.8
2/37
Paul Ashall, 2007
Membrane fabrication
Isotropic
Solution casting
Melt extrusion
Track etch membranes
Expanded film membranes
Anisotropic
Phase separation Interfacial polymerisation
Solution coated composite membranes
8/8/2019 Membrane Technology 10.8
3/37
Paul Ashall, 2007
Membrane preparation methods TIPS
CIPS PIPS
SIPS
Track etching Stretching
8/8/2019 Membrane Technology 10.8
4/37
Paul Ashall, 2007
The TIPS method of membrane
formation A homogeneous solution of a polymer and a high boiling, low
molecular weight diluents or latent solvent (which does notcause appreciable dissolution or swelling of the polymer at roomtemperature) is formed by blending at an elevated temperature
the solution is cast or extruded through a slit die (to form a flatsheet) or a spinneret (to form a hollow fiber or tube)
the extruded melt-blend or nascent membrane passes through anair gap and is then cooled either in a quench bath or on a chillroll. This removal of thermal energy results in the formation of
polymer rich and diluent rich phase, and , eventually, the
solidification of the polymer- rich phase. after , the solidification of the polymer- rich matrix phase, the
diluent is extracted.
the extractant is removed (typically by evaporation) to yield amicro porous membrane
8/8/2019 Membrane Technology 10.8
5/37
Paul Ashall, 2007
Post processing treatments, such as stretching to modifythe pore structure or chemical modification to create or
alter functional groups, are optional. Depending on the nature and strength of the polymer-
diluent interactions, the initial polymer concentration, andthe rate at which the thermal energy is removed, the melt-blend may undergo one of three phase separation
sequences: liquid-liquid TIPS, in which the melt-blend separates into
polymer-rich and polymer-lean liquid phases, followed bysolidification of the polymer-rich phase.
solid-liquid TIPS, in which the polymer crystallizes fromthe melt-blend.
liquid-solid TIPS , in which the diluent crystallizes priorto the crystallization of the polymerization.
8/8/2019 Membrane Technology 10.8
6/37
Paul Ashall, 2007
The majority of the membrane formation
projects focus on liquid- liquid TIPS
because it has proven to be a valuable
method of making commercial membranes
8/8/2019 Membrane Technology 10.8
7/37
Paul Ashall, 2007
Advantages
TIPS can be used to form micro porous membranes from high- performance polymers that are difficult to process and do notdissolve at room temperature, including semi-crystalline polymers
that are chemically resistant and thermally stable. For any particular polymer , the structure development kinetics (and
therefore the pore size, pore size distribution , and overall porosityor void fraction) can be controlled by the choice of diluent, polymerconcentration, and quench temperature or cooling rate.
Phase separation is induced by heat transfer, which is easier to
control than the multi component mass transfer involved intraditional phase inversion methods. As such, the TIPS processresults in membranes with fewer defects such as the macro voidsthat often weaken membranes.
Since heat transfer is far more rapid than diffusion in polymersolutions, TIPS permits membrane structure to be formed viaspinodal decomposition. Consequently, TIPS membranes can be
made to have a narrower pore size distribution than membranesprepared by phase inversion techniques
Membrane can be prepared with porosities as high as 90%.
8/8/2019 Membrane Technology 10.8
8/37
Paul Ashall, 2007
TIPS can produce a variety of micro- structures including non-porous, open cell, closed cell, isotropic (uniform pore structurethroughout), anisotropic ( a variation in pore size from one
surface to the other surface), or asymmetric( a relatively denseskin on the surface of an isotropic or anisotropic structure).
pore sizes ranging from 0.01 to 20 micrometer have beenreported.
Only one diluent is needed for casting solution, as compared to
other membrane production techniques in which at least onesolvent and at least one non-solvent are needed. Therefore, fewerparameters need to be controlled during the process.
A simple, one- component quench bath can be used, ascompared to DIPS techniques in which multi- component bathsare used to induce phase separation. Since no componentexchange takes place in the quench bath, the bath can be reusedwithout the costly purification needed in some phase inversion
processes.
Micro-porous products can be readily prepared in the form ofsheet, fibres, hollow fibres, spheres, and blocks of various sizes
and shapes
8/8/2019 Membrane Technology 10.8
9/37
Paul Ashall, 2007
Applications
Membranes and membrane support materials: batteryseparators: closed- cell and open cell foams for thermaland sound insulators: breathable/disposable surgical
garments, diapers, tents, and packaging materials:medicated wound and burn dressings: controlled releasedevices of various geometries: and high surface areasfibres for improved dyeabiltiy and reduced density.
Most of the TIPS membranes produced on a commercialscale are used for micro filtration, plasmapheresis,controlled drug release, membrane distillation, and lithiumion battery separators.
8/8/2019 Membrane Technology 10.8
10/37
Paul Ashall, 2007
DialysisA process for selectively removing low mol. wt. solutes from
solution by allowing them to diffuse into a region of lowerconcentration through thin porous membranes. There is
little or no pressure difference across the membraneand the flux of each solute is proportional to theconcentration difference. Solutes of high mol. wt. aremostly retained in the feed solution, because theirdiffusivity is low and because diffusion in small pores is
greatly hindered when the molecules are almost as large asthe pores.
Uses thin porous membranes.
8/8/2019 Membrane Technology 10.8
11/37
Paul Ashall, 2007
PV Membranes
Composite membrane (dense layer + poroussupporting layer)
Hydrophilic membranes (PVA) e.g.ethanol/water
Hydrophobic membranes (organophilic)
Modules Plate & frame
8/8/2019 Membrane Technology 10.8
12/37
Paul Ashall, 2007
Mechanism Solution diffusion
Selectivity dependent on chemical structureof polymer and liquids
Activity driving force is provided bydifference in pressure between feed andpermeate side of membrane.
Component flux is proportional toconcentration and diffusivity in densemembrane layer.
Flux is inversely proportional to membranethickness.
8/8/2019 Membrane Technology 10.8
13/37
8/8/2019 Membrane Technology 10.8
14/37
Paul Ashall, 2007
Gas permeations Mechanisms Convective flow (large pore size 0.1 10
m)
Knudsen diffusion (pore size < 0.1m)
Molecular sieving (0.0005 0.002 m)
Solution-diffusion (dense membranes)
8/8/2019 Membrane Technology 10.8
15/37
Paul Ashall, 2007
Knudsen diffusionKnudsen diffusion occurs when the ratio of
the pore radius to the gas mean free path (
~ 0.1 micron) is less than 1. Diffusing gas
molecules then have more collisions with
the pore walls than with other gas
molecules. Gases with high D permeatepreferentially.
8/8/2019 Membrane Technology 10.8
16/37
Paul Ashall, 2007
Poiseuille flowIf the pores of a microporous membrane are
0.1 micron or larger, gas flow takes place
by normal convective flow.i.e. r/ > 1
8/8/2019 Membrane Technology 10.8
17/37
Paul Ashall, 2007
Transport of gases through dense
membranesJA = QA (pA1 pA2)
QAis permeability (L (stp) m-2 h-1 atm-1)
pA1 partial pressure A feed
pA2 partial pressure A permeate
8/8/2019 Membrane Technology 10.8
18/37
Paul Ashall, 2007
Membrane materials Metal (Pd Ag alloys/Johnson Matthey for
UP hydrogen)
Polymers (typical asymmetric membranes
are 50 to 200 microns thick with a 0.1 to 1
micron skin)
Ceramic/zeolite
8/8/2019 Membrane Technology 10.8
19/37
Paul Ashall, 2007
Modules Spiral wound
Hollow fibre
8/8/2019 Membrane Technology 10.8
20/37
Paul Ashall, 2007
Flow patterns Counter-current
Co-/counter
Radial flow
crossflow
8/8/2019 Membrane Technology 10.8
21/37
Paul Ashall, 2007
Applications
Oxygen/nitrogen separation from air (95
99% nitrogen)
Dehydration of air/air drying
8/8/2019 Membrane Technology 10.8
22/37
Paul Ashall, 2007
STRETCHED SEMI-CRYSTALLINE
POLYMER This method is used for only membrane which uses
crystalline materials for its construction. PROCESS
The crystalline membrane is made by rolling.
It is stretched perpendicular to the axis of crystallineorientation.
If stretched perpendicular to the axis of crystallineorientation may fracture in such a way as to make areproducible microchannels.
This microchannels act as pores for the membrane.
PROPERTIES
Stretched polymers have unusually large fractions of openspace, giving the fluxes. Hence they are used formicrofiltration
Most of the material are hydrophobic.
EXAMPLES
tefflon & polyolefin.
8/8/2019 Membrane Technology 10.8
23/37
Paul Ashall, 2007
NUCLEATION TRACK ETCHING
Process of forming well defined pores by exposing a dense film to ionbombardment followed by etching of the damaged region
PROCESS
These membranes are made by exposing a thin polymer film to acollimated beam of radiation strong enough to break chemical bonds in thepolymer chain.
This is achieved with a collimated beam of particle by separating auranium or californium source from the film evacuating the interveningspace, and exposing the assembly to thermal neutans.
Tracks can be developed in inorganic material when a massive chargedparticle (positive ion) passes through inorganic material,it propels electronout of the atom in crystal lattice,creating an ion-explosion spike.
In organic polymer, broken repulsion, thereby disrupting the regular lattice.
The larger the separation and the smaller the source area, the morecomplete the resulting hole alignment will be.
The film is then etched in a bath which selectively attacks the damagedpolymer.
Reacks can be enlarged by leaching with suitable reagents.
Nuclepore membranes are characterized by cylindrical pores with a narrowpore size distribution.
The technique produces photogenic pores.
8/8/2019 Membrane Technology 10.8
24/37
Paul Ashall, 2007
Tracks can be developed in non conducting substancesboth organic or inorganic films.
Flux obtained in this type of membranes is low.
High pore density cannot be achieved
The choice of the etchants varies with the chemical natureof the polymeric film, concentration, temperature, and theorientation of the attacked surface.
Length of the fission track varies with the nature of thesource.
Normal sodium hydroxide is widely used.
8/8/2019 Membrane Technology 10.8
25/37
Paul Ashall, 2007
SINTERING
Sintering is a method for making objects from powder, by heating the
material in a sintering furnace below its melting point (solid statesintering) until its particles adhere to each other. Sintering istraditionally used for manufacturing ceramic objects
ADVANTAGES OF SINTERING
The possibility of very high purity for the starting materials and theirgreat uniformity
Preservation of purity due to the restricted nature of subsequentfabrication steps
Stabilization of the details of repetitive operations by control of grainsize in the input stages
Absence of binding contact between segregated powder particles orinclusions (called stringering), as often occurs in melt processes
No requirement fordeformation to produce directional elongation ofgrains
The possibility of creating materials of uniform controlled porosity.
8/8/2019 Membrane Technology 10.8
26/37
Paul Ashall, 2007
PROCESS
Sintering is part of the firing process used in themanufacture of pottery and other ceramic objects. SomePOLYMER have a lower affinity for water and a lower
plasticity index than clay, requiring organic additives in thestages before sintering. The general procedure of creatingMEMBRANES via sintering of powders includes:
Mixing water, binder, deflocculant, and unfiredPOLYMER to form a slurry
Spray-drying the slurry Putting the spray dried powder into a mold and pressing it
to form a green body (an unsintered item)
Heating the green body at low temperature to burn off thebinder
Sintering at a high temperature to fuse the POLYMERtogether
There are two types of sintering: with pressure (alsoknown as hot pressing), and without pressure. Pressurelesssintering is possible with a nanoparticle sintering aid and
bulk molding technology. A variant used for 3D shapes iscalled hot isostatic pressing.
8/8/2019 Membrane Technology 10.8
27/37
Paul Ashall, 2007
PIPS-PHASE INVERSION
PHASE SEPERATION Phase inversion refers to the process b which a polymer solution (in which the solvent system iscontinuous phase) inverts into swollen threedimensional macromolecular networks or gel (where
the polymer is the continuous phase). In thin film formsuch a gel constitute a phase inversion membrane.
There are four types of phase inversion processes:
the dry process
the wet process thermal process
the polymer assisted phase inversion process (PAPI)
8/8/2019 Membrane Technology 10.8
28/37
Paul Ashall, 2007
Chemical Phase inversion:
This method can be used to produce very largequantities of symmetric membranes. The process
produces tortuous flow membranes. It involves
preparing a concentrated solution of a polymer in
a solvent.
The solution is then spread into a thin film and
then precipitated through the addition of a non
solvent usually water. This technique is capable of
producing fairly uniform membranes versatile.
8/8/2019 Membrane Technology 10.8
29/37
Paul Ashall, 2007
The dry Process:
The dry or complete evaporation process is the oldest of the phaseinversion processes. A dissolved polymer is precipitated by
evaporation of a sufficient amount of solvent to form a membranestructure.
Appropriate mixtures of additives are present in solutions with thepolymer to alter its precipitation tendency during solvent evaporation.
The solvent that occupies the void volume of the porous membrane iscompletely evaporated after the structure has stabilized. The originalsolvent may also be displaced by the solvent of the bathins solution.
Stages in the membrane formation:
Loss of solvents and the inversion of a clear one phase solution into aturbid two phase (Sol 2) solution.
Gelation. This is accompanied by a diminution in the reflectivity of thecast solutions.
concentrations of the gel with or with out synergetic
Capillary depletion. Here the non solvent liquid encompasses by thegel departs leaving behind empty capillaries
loss of residual solvents (final drying)
8/8/2019 Membrane Technology 10.8
30/37
Paul Ashall, 2007
Wet- Phase separation membranes formation:
Process in which a dissolved polymer isprecipitated by immersion in a non-solvent bath toform a membrane structure
The viscous polymer solution is allowed to
partially evaporate after which it is immersed intoa nonsolvent gelation bath wherever whatever leftof the solvent- pore former system is exchangedfor the nonsolvent. Or the viscous polymersolution may be immersed into the non- solventgelation bath for the exchange of the solventsystem for non solvent. The end products of thewet processes are water swollen membranes
8/8/2019 Membrane Technology 10.8
31/37
Paul Ashall, 2007
Polymer assisted phase inversion process (PAPI):
The 4 polymer assisted phase inversion process utilizes asolution consisting of a solvent and two physicallycompatible polymers to cast a dense film with amorphology known as interpenetrating polymer network(IPN).
after complete (dry PAPI) or partial (wet PAPI) solvent
evaporation, the IPN film is immersed in a liquid, usuallywater, which is a solvent for one of the polymers and anonsolvent for the other.
The insoluble network which remains after leaching is askinless micro porous PAPI process membrane. The
polymer which is leached is acting the role of a poleformer. A potential application for PAPI processmembrane is to serve as micro porous supports for thinfilm composites.
8/8/2019 Membrane Technology 10.8
32/37
Paul Ashall, 2007
Dense membranes:
Dense membranes may be formed by a variety of techniques:
solution methods melt processing
direct polymerization
Membranes can be prepared by dissolving a membrane forming polymer insome solvent. The solution is then spread on a support and the solvent isevaporated to leave the membrane. The detailed characteristics of the finalmembrane depend on the nature of the solution and the mode of preparation of
the final membrane. There are several techniques for producing dense membranes. The technique
of dissolving the molecules insolvent, spreading the solution on some supportand allowing the solvent to evaporate is quite commonly used. The nature ofthe final membrane is dictated by the polymer concentration in solution, thechoice of the solvent and aggregation of molecules while they are still insolution. A solvent in which solvent polymer interactions is small relative to
the polymer-polymer interactions produce a solution with a high percentage ofaggregate molecules. The properties of such a polymer are influenced by theaggregated molecules. If the same polymer is dissolved in a solvent withstrong solvent-molecules interactions. Thus a wide range of membranestructures may be produced from a single polymer.
8/8/2019 Membrane Technology 10.8
33/37
Paul Ashall, 2007
Dense membranes from polymer solutions (cast films) are prepared bydissolution of a polymer substrate in a solvent medium, followed by theapplications of a liquid film onto a suitable substrate and complete evaporation
of the solvent to form a dense film. The nature of both the polymer and thesolvent are important in determining the morphologies of amorphous and semicrystalline films.
The polymers to be used are dissolved, filtered, re-precipitated, filtered anddried prior to dissolution in the solution from which membrane are to be cast.The solvents to be used for membrane formation are pure solvents.
Dense membranes can be subjected to post-formation treatments which serve
to modify their structural and performance characteristics. Thermal annealing,particularly at temperatures in excess of the glass transition temperature can beutilized to increase both crystallite size and the extent of crystallinity.
Annealing of amorphous films has the effect of diminishing the average inter-chain displacement. Increasing the chain mobility by the inclusion ofplasticizers or by subjecting dense membranes to an atmosphere of solventvapors can also promote crystallization even at room temperature.
The crystallinity of polycarbonate films, for example, is increased by exposureto acetone vapor. The application of stress, particularly in the presence oflasticizers, has been utilized to increase crystallinity. Thus the crystallinity ofpolyethylene terephthalate, polycarbonate and cellulose membranes increasewhen subjected to stress under water amounting to 15% of ultimate strength.
8/8/2019 Membrane Technology 10.8
34/37
Paul Ashall, 2007
There are a number of factors that influence the finalstructure of the membrane.
Membranes can be formed from a specific solution, but
their final structure can still be influenced by theevaporating atmosphere, temperature and rate ofevaporation. The nature of the finished membrane can bealtered by applying stress, by spontaneous crystallization,and by thermal annealing.
The neat (pure material in a liquid or molten state) can beextruded to produce membranes in the absence of solvent.The structure of the membrane is dictated by the coolingconditions.
8/8/2019 Membrane Technology 10.8
35/37
Paul Ashall, 2007
Porous membranes
The porous membranes can be made from densemembranes by introducing solvent which inducesswelling. The solvent is then removed from swollenmembrane to produce the final porous membrane.
Porous membranes can also be generated directlyfrom a molecular solution. The phase inversions
membranes are formed from polymer- solventsystems in which the final structures of themembranes is produced while the solvent is stillpresent in the membrane.
8/8/2019 Membrane Technology 10.8
36/37
Paul Ashall, 2007
CIPS
As a new kind of preparation technique for porous polymermaterials, cryogenic induced phase separation (CIPS) process isperformed as follows:
(1) a homogeneous solution is formed at an elevated temperature byblending the polymer with a high boiling point, low molecular weightdiluents;
(2) the solution is cast into the desired shape and cooled at acontrolled rate to induce phase separation:
(3) the diluents is removed (usually by extraction) to produce thechitosen fluid. However, chitosen can easily dissolve in a dilute acidsolution. When the chitosen in the solution is crosslinked and cooled,the phase separation will occur because of the water (solvent)
crystallization (ice crystals). (4) Once the ice crystal is removed by the organic non solvent
extraction, chitosan porous membrane or another desired shape of thematerial (e.g. chitosan sponge) can be produced
8/8/2019 Membrane Technology 10.8
37/37
Paul Ashall, 2007
Cryogenic induced phase separation is process in which adissolved polymer is precipitated or coagulated by
controlled cooling to form a membrane structure. The solution of polymer in a poor solvent is prepared at an
elevated temperature. After being formed into its finalshape, a sudden drop in solution temperature causes the
polymer to precipitate.
The solvent is then washed out. Membrane may be spun athigh rates using this technique. This is latest technologywhere very low temperatures are used. The membranesdeveloped using this technique is used in:
Recovery of hydrogen from gases.
In oil refineries
Enrichment of oxygen
Removal of H2S from natural gas
Air separation.