Oligonucleotide delivery by chitosan-functionalized porous silicon nanoparticles
Morteza Hasanzadeh Kafshgari1,§, Bahman Delalat1,§, Wing Yin Tong1, Frances J. Harding1, Martti Kaasalainen2,
Jarno Salonen2, and Nicolas H. Voelcker1 ()
1 ARC Centre of Excellence in Convergent Bio-Nano Science and Technology, Mawson Institute, University of South Australia, GPO
Box 2471, Adelaide SA 5001, Australia 2 Department of Physics and Astronomy, University of Turku, FI-20014 Turku, Finland §These authors contributed equally to this work.
Supporting information to DOI 10.1007/s12274-015-0715-0
Calculation of degree of deacetylation of chitosan
Broussignac’s method
Linear potentiometric titration based on Broussignac’s method [S1, S2] determines the degree of deacetylation
(DD% = 71) of chitosan based on Eq. (S1) through identification of inflexion points in the titration curve (see
Fig. S1). Chitosan dissolved in an excess of hydrochloric acid becomes deprotonated during titration with
NaOH. The first and second inflexion points are equivalence points for titration of excess HCl and the titration
of protonated chitosan, respectively.
The degree of deacetylation (DD%) can thus be calculated using the equation
DD% = ∆V × CNaOH × 10–3 × 161/(Mchitosan × 0.0994) (S1)
where ∆V, CNaOH (0.1 M), and Mchitosan (0.15 g) are the volume of the added NaOH titrant (mL) between two
inflexion points, concentration of NaOH solution (g/mL), and the weight of chitosan (g), respectively. In addition,
161 and 0.0994 are constant.
Infrared spectroscopy
Diffuse reflectance infrared Fourier transform (DRIFT) spectroscopic methods were also used to calculate DD%
for the low molecular weight chitosan used. Spectra were obtained using a Thermo Nicolet Avatar 370MCT
(Thermo Electron Corporation, Waltham, MA, USA) instrument. A smart diffuse reflectance accessory was
used for the dried chitosan sample embedded within KBr pellets. The spectrum obtained was analyzed using
OMNIC version 7.3 software (Thermo Electron Corp., Waltham, MA, USA). For the spectrum analysis, 128 scans
were averaged in the range of 4,000 to 700 cm–1 with a resolution of 4 cm–1. The mixture of chitosan and KBr
was run in dry air to remove noise from CO2 and water vapor.
Address correspondence to [email protected]
| www.editorialmanager.com/nare/default.asp
Nano Res.
Figure S1 Titration curve of chitosan solution (1% w/v) based on Broussignac’s method.
DD% of the low molecular weight chitosan was calculated based on different baselines (see Fig. S2). These
baselines are based on the determination of the intensity of a probe band corresponding to N-acetyl or amine
content and the intensity of a reference constant band [S3].
Figure S2 DRIFT spectrum of chitosan presenting the baseline--a and baseline--b for calculating degree of deacetylation (DD%).
(1) Baseline--a
Baseline--a, which was proposed by Domszy and Robertsis [S3, S4] is a simple theoretical method to determine
DD% by following equation
DD% = 100 – [(A1655 / A3450) × 100 / 1.33] (S2)
where A1655 and A3450 are the absorbance at 1,655 cm–1 corresponding to the primary amide band, which is the
N-acetyl group content representative, and the absorbance at 3,450 cm–1 is the hydroxyl band as an internal
www.theNanoResearch.com∣www.Springer.com/journal/12274 | Nano Research
Nano Res.
standard reference band. The factor 1.33 describes the ratio of A1655 /A3450 for the fully N-acetylated chitosan
[S3, S4].
(2) Baseline--b
This is a modified form of the baseline reported by Domszy and Roberts. The baseline--b proposed by Baxter
et al. [S3, S4] can be estimated by Eq. (S3)
DD% = 100 – [(A1655 / A3450) × 115] (S3)
where A1655 and A3450 are the absorbance at 1,655 and 3,450 cm–1. The factor 115 is the reciprocal value of the
slopes of the linear curves (the absorption ratio versus degree of N-acetylation) [S3, S4].
The absorbances of amide and hydroxyl bands can be calculated by the following mathematical expressions
proposed by Sabnis and Block [S4]
A1655 = log10 (DG/DE) (S4)
A1655 = log10 (DF/DE) (S5)
A3450 = log10 (AC/AB) (S6)
where DG (corresponds to the baseline--a) and DF (corresponds to the baseline--b), DE, AC, and AB are
depicting the absolute heights of the absorption bands of the functional groups at their respective wavelengths.
All three methods of calculation of DD% produced a similar result for the low-molecular weight chitosan
used to coat THCpSiNP (Table S1).
Table S1 Calculated degree of deacetylation (DD%) of the low molecular weight chitosan using the different methods
Method DD%
Broussignac’s method 71
Infrared spectroscopy-Baseline--a 72
Infrared spectroscopy-Baseline--b 75
Molecular weight and gyration radius of chitosan
Poly-(β-1→4)-2-amino-2-deoxy-d-glucopyranose, chitosan, is a linear polysaccharide, so molecular weight (MW)
and gyration radius (Rg) are estimated by means of Eq. (S7) and Eq. (S8) [S5].
Figure S3 Viscosity at different shear stresses of 1% w/v aqueous solution of chitosan at 25 °C.
| www.editorialmanager.com/nare/default.asp
Nano Res.
Viscosity of chitosan (Pa·s, see Fig. S3) was measured using rheometer/viscometer (RA 1000, TA Instruments
Rheometers, Rydalmere, NSW). The gyration radius (Rg = 46 nm) of chitosan estimated is based on the intrinsic
viscosity ([η] = 3,933 mL/g) and average molecular weight (MW = 119 kDa).
[η] = 8.43 × 10−2 MW0.92 (S7)
Rg = 7.5 × 10−2 MW0.55 (S8)
Characterization of THCpSiNPs before and after chitosan capping
Figure S4 Representative average size of (a) THCpSiNPs and (b) CS/THCpSiNPs studied by means of SEM, and respective size distribution of (c) THCpSiNPs, (d) CS/THCpSiNPs, (e) Oligo/THCpSiNPs, and (f) CS/oligo/THCpSiNPs measured by means of DLS. Pores of THCpSiNPs before coating by using chitosan are indicated by red arrows (representative pores).
www.theNanoResearch.com∣www.Springer.com/journal/12274 | Nano Research
Nano Res.
Figure S5 Morphology and surface roughness of (a) THCpSiNPs and (b) CS/THCpSiNPs by means of representative SEM images. Pores of THCpSiNPs are indicated by blue arrows (representative pores).
Figure S6 Representative TEM images of (a) THCpSiNPs, (b) oligo/THCpSiNPs, and (c) and (d) CS/oligo/THCpSiNPs.
Figure S7 Measurement of IEP by pH titration for THCpSiNPs (□) and CS/THCpSiNPs (∆). Concentration of chitosan coating solution 0.1% w/v (n = 3; mean ± standard deviation shown).
| www.editorialmanager.com/nare/default.asp
Nano Res.
THCpSiNP degradation
Degradation of pSiNPs produces silicic acid measured by means of an ammonium molybdate colorimetric
assay. Unmodified pSiNPs and THCpSiNPs (0.1 mg) were placed into separate 1 mL solutions of 0.25 m
Tris–HCl (pH = 7.2). Each of these individual containers (1 mL) was allocated to a predetermined measurement
time over seven days. Supernatant to be assayed for silicic acid content was acidified with 0.3 M HCl at a ratio
of 5 :2 (100 μL:40 μL). Subsequently, 20 μL of a 42 mM ammonium molybdate solution was added to the acidified
supernatant, and incubated for 10 min. Finally, 20 μL of 27 mM EDTA and 1.35 M sodium sulphite was added
to each sample solution and the sample held for 1 h incubation at room temperature. Spectrophotometric
analysis at 650 nm was performed to measure the amount of the silicic acid released into solution. A silicic acid
concentration standard curve was prepared with sodium metasilicate pentahydrate.
Biocompatibility, cell uptake, and oligonucleotide release from chitosan capped THCpSiNPs
Figure S8 Measurement of degradation for unmodified (a) pSiNPs and (b) THCpSiNPs by means of a colorimetric ammonium
molybdate assay. THCpSiNPs were placed into 1 mL of Tris buffer (pH = 7.2). Concentration of THCpSiNPs 0.1 mg/mL (n = 2; mean ±
standard deviation shown).
Figure S9 Cell viability of BSR cells incubated with CS/oligo/THCpSiNPs (+CS) and oligo/THCpSiNPs (–CS) compared to BSR cell
sample incubated without the NP (control) as determined by LDH assay after 48 h exposure to pSiNPs (n = 3; mean ± standard deviation
shown).
www.theNanoResearch.com∣www.Springer.com/journal/12274 | Nano Research
Nano Res.
Figure S10 Viability of BSR cells incubated with (a) CS/oligo/THCpSiNPs, (b) oligo/THCpSiNPs, and (c) no treatment after 24 h towards BSR cells as measured by Live/Dead assay after 48 h (NP concentration: 0.1 mg/mL).
Figure S11 Progressive Z-stack laser scanning confocal microscopy image series for BSR cells incubated with CS/FAM-oligo/ THCpSiNPs (0.1 mg/mL). Cell nuclei were stained with Hoechst 33342 (blue), the CS/cell membranes were stained with phalloidin- TRITC (red) and FAM-oligo/THCpSiNPs emit green fluorescence. The roman numbers correspond to images at different planes (height interval: 250 nm; down to up). I and V are representative of the bottom and center plane of the central BSR cell, respectively.
| www.editorialmanager.com/nare/default.asp
Nano Res.
Figure S12 Time-lapse fluorescence microscopy images of BSR cells after incubation with CS/FAM-oligo/THCpSiNPs (0.1 mg/mL) for (A) 0, (B) 1, (C) 3, (D) 5, (E) 7, (F) 16, and (G) 24 h. The cell nuclei were stained with Hoechst 33342 (blue), the CS/FAM-oligo/THCpSiNPs emit green fluorescence and cell membranes were stained with phalloidin-TRITC (red). The roman numbers represent (I) merged images of nuclear and FAM labeling, and (II) merged images of nuclear, FAM, and cell membrane labeling.
www.theNanoResearch.com∣www.Springer.com/journal/12274 | Nano Research
Nano Res.
Oligonucleotide release in HS
To simulate an environment closer to in vivo release conditions, CS/FAM-labeled oligo (FAM-oligo)/THCpSiNPs
coated with chitosan solution of concentration of 0.1% w/v were suspended at a concentration of 0.1 mg/mL
in HS at 37 ± 0.5 °C. Retention of FAM-labelled oligonucleotide within the NP was monitored through the
extinguishing of green fluorescence during release an inverted fluorescence microscope Eclipse Ti-S (Nikon Inc.,
Rhodes, NSW, Australia) for 48 h. Prior to imaging, CS/FAM-oligo/THCpSiNPs were centrifuged and washed
briefly with MilliQ water.
Figure S13 Release study of FAM-oligo from CS/FAM-oligo/THCpSiNPs (0.1 mg/mL) by time-lapse fluorescence microscopy imaging of CS/FAM-oligo/THCpSiNPs after incubation with HS derived from male AB plasma, T = 37 ± 0.2 °C for (a) 0, (b) 6, (c) 12, (d) 24, and (e) 48 h. The CS/FAM-oligo/THCpSiNPs emit green fluorescence because of FAM labeled oligonucleotide. The excitation 490 nm and emission 520 nm were used.
| www.editorialmanager.com/nare/default.asp
Nano Res.
Figure S14 TEM images of BSR cells after exposure to CS/FAM-oligo/THCpSiNPs (0.1 mg/mL) for 24 h.
www.theNanoResearch.com∣www.Springer.com/journal/12274 | Nano Research
Nano Res.
In vivo compatibility of oligonucleotide loaded chitosan capped THCpSiNPs
Figure S15 Fluorescence microscopy images of the skin tissue site after the subcutaneous injection of CS/FAM-oligo/THCpSiNPs (700 µg/kg, over the right flank) and saline (control, over the left flank). The skin tissues were stained with Hoechst 33342 (blue emission), and CS/FAM-oligo/THCpSiNPs emit green fluorescence. Accumulation of the NPs is indicated by white arrows.
References
[S1] Jiang, X.; Chen, L.; Zhong, W. A new linear potentiometric titration method for the determination of deacetylation degree of
chitosan. Carbohydr. Polym. 2003, 54, 457–463.
[S2] Wang, Q. Z.; Chen, X. G.; Liu, N.; Wang, S. X.; Liu, C. S.; Meng, X. H.; Liu, C. G. Protonation constants of chitosan with
different molecular weight and degree of deacetylation. Carbohydr. Polym. 2006, 65, 194–201.
[S3] Kasaai, M. R. A review of several reported procedures to determine the degree of n-acetylation for chitin and chitosan using
infrared spectroscopy. Carbohydr. Polym. 2008, 71, 497–508.
[S4] Khan, T. A.; Peh, K. K.; Ch'ng, H. S. Reporting degree of deacetylation values of chitosan: The influence of analytical methods. J.
Pharm. Pharmaceut. Sci. 2002, 5, 205–212.
[S5] Bertha, G.; Dautzenbergb, H. The degree of acetylation of chitosans and its effect on the chain conformation in aqueous solution.
Carbohydr. Polym. 2002, 47, 39–51.