PRODUCTION AND QUALITY CONTROL
POLYCRYSTALLINE SILICONSOLAR CELLS
FEATURES
Color uniformityHigher peel strength
Tighter product performance distribution and 0.1% efficiency step reduce the mismatch power loss during module assemblyGood module reliabilityExcellent PID-free performanceLow reverse leakage current
Standard cells calibrated by Fraunhofer ISE LID monitoringPeel strength controlReverse current screening
IREX ENERGY JOINT STOCK COMPANYHead Office: 11 TTN 17 Street, Tan Thoi Nhat Ward, District 12, HCMC, VietnamTel: (+84) 8 6255 8092 | Fax: (+84) 8 6255 8093 | Email: [email protected]: 1A Street, Phu My 1 Industrial Zone, Tan Thanh District,Ba Ria - Vung Tau Province, Vietnam www. irex.vn
IRP156-3BB-96
08 17.80-17.9507 17.70-17.8006 17.60-17.7005 17.50-17.6004 17.40-17.5003 17.30-17.4002 17.20-17.3001 17.10-17.20
No.4.334.304.284.264.234.214.194.16
Pmpp(W)79.3179.1879.0578.8778.6778.4278.3978.32
FF(%)0.5310.5290.5260.5240.5220.5200.5180.518
Umpp(V)8.1598.1468.1378.1218.1058.0958.0778.037
Impp(A)0.6290.6280.6270.6260.6250.6240.6230.621
Uoc(V)8.6818.6618.6408.6258.6118.6018.5718.555
Isc(A)
Light intensitySpectrumTemperature
1000W/m²AM1.5G25℃
POLYCRYSTALLINE SILICONSOLAR CELLS
MECHANICAL DATA AND DESIGN
STANDARD TEST CONDITIONS (STC)
Efficiency (%)
FormatThicknessFront (-)Back (+)
156mm×156mm±0.5mm200±20um1.4mm bus bars (silver), blue anti-reflecting coating ( silicon nitride)1.8mm wide soldering pads (silver) back surface field (aluminum)
α (Isc)β (Voc)γ (Pmpp)
+0.05%/K-0.31%/K-0.41%/K
TEMPERATURE COEFFICENTS
IV CURVE