Pyrogel InsulationTECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�

Contents

Introduction 3

Thermal Conductivity ASTM C 177 - Thermal Conductivity 5 ASTM C 335 - Thermal Conductivity 5

Dimensional Stability ASTM C 356 - Linear Shrinkage Under Soaking Heat 6 ASTM C 411/C 447 - Hot Surface Performance 6 ASTM E 228 - Linear Coefficient of Thermal Expansion 6 Effects of Long Term Thermal Exposure 6

Mechanical Resilience ASTM C 165 - Compressive Strength (Room Temp) 7 ASTM C 59�, Section 11.11.6 - Procedure for Heat and Vibration 7 ASTM C 1101, Section 7.1 and 7.2 - Flexibility and Resilient Flexibility 7 Compression Recovery at High Stress Load 7

Water Resistance ASTM C 1559 - Wicking 8 ASTM C 1104 - Water Vapor Adsorption 8 ASTM C 1511 - Water Repellency 8

Chemical Resistance ASTM C 665, Section 13.8 - Corrosion Test 9 ASTM C 795 - Standard Specification for Thermal Insulation for Use in Contact With Austenitic Steel 9 Extractable pH Measurements of Pyrogel 6350 9 ASTM C 1338 - Fungal Resistance 9

Fire Testing ASTM E 84 - Flame and Smoke Spread 10 UL 1709 - Structural Steel Fire Protection 10 European Testing 10

Acoustical Properties ASTM E 1222 - Insertion Loss of Pipe Lagging Systems 11

Appendix A - C 177 THERMAL CONDUCTIVITY 1�

Appendix B - ASTM C 335 CONDUCTIVITY �1

Appendix C - ASTM C 356 - LINEAR SHRINKAGE UNDER SOAKING HEAT �6

Appendix D - ASTM C 411/C 447 - HOT SURFACE PERFORMANCE �8

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION 3�

Appendix F - EFFECTS OF LONG TERM THERMAL EXPOSURE 39

Appendix G - MECHANICAL RESILIENCE 44

Appendix H - PYROGEL 6350 COMPRESSION RECOVERY AFTER HIGH STRESS LOAD 51

Appendix I - ASTM C 795 STANDARD SPEC FOR THERMAL INSULATION FOR USE IN CONTACT WITH AUSTENITIC STEEL 57

Appendix J - EXTRACTABLE PH MEASUREMENTS OF PYROGEL 6350 60

Appendix K - ASTM C 1338 - FUNGAL RESISTANCE 64

Appendix L - ASTM E 84 - FLAME AND SMOKE SPREAD 69

Appendix M - UL 1709 - STRUCTURAL STEEL FIRE PROTECTION 71

Appendix N - EUROPEAN TESTING 88

Appendix O - ASTM E 1222 - INSERTION LOSS OF PIPE LAGGING SYSTEMS 93

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

3

Introduction

Pyrogel® is a high-temperature insulation blanket formed of silica aerogel and reinforced with a non-woven, carbon- and glass-fiber batting.

Silica aerogels possess the lowest thermal conductivity of any known solid. Pyrogel achieves this industry-leading thermal performance in a flexible, environmentally safe, and easy-to-use product.

Ideal for insulating the curved surfaces and complex shapes typical of today’s refining and petrochemical infrastructure, Pyrogel is an essential material for those seeking the ultimate in thermal protection.

Pyrogel Advantages:

Superior Thermal Performance — 2 to 8 times better than competing insulation products

Reduced Thickness and Profile — Equal thermal resistance at a fraction of the thickness

Less Time and Labor to Install — Easily cut and comformed to complex shapes, tight curvatures, and spaces with restricted access

Physically Robust — Soft and flexible but with excellent springback, Pyrogel recovers its thermal performance even after compression events as high as 50 psi

Shipping and Warehousing Savings — Reduced material volume, high packing density, and low scrap rates can reduce logistics costs by a factor of five or more compared to rigid, pre-formed insulations

Simplified Inventory — Unlike rigid pre-forms such as pipe cover or board, the same Pyrogel blanket can be kitted to fit any shape or design

Excellent Fire Protection — Equal to or better than other insulation materials, including mineral wool and calcium silicate

Hydrophobic Yet Breathable — Pyrogel repels liquid water but allows vapor to pass through

Environmentally Safe — Landfill disposable, shot-free, with no respirable fiber content

•

•

•

•

•

•

•

•

•

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

4

Pyrogel’s main properties are categorized and described on the following pages. Below is a a summary of key test results.

Specification Compliance and Performance

Introduction

Test Procedure Property Results

ASTM C165 Compressive Strength Stress at 10% strain = 11.6 psi (80 kPa)Stress at 25% strain = 24.7 psi (170 kPa)

ASTM C356 Linear Shrinkage Under Soaking Heat < 2.5%

ASTM C411 Hot Surface Performance Passed

ASTM C59� Modified Mineral Fiber - Weight Loss From Vibration Passed

ASTM C871 Leachable Chloride, Flouride, Silicate and Sodium Ions Passed chemical requirements of C795

ASTM C1101 Classifying the Flexibility of Mineral Fiber Blankets Class: Resilient Flexible

ASTM C1104 Water Vapor Sorption 4% (by weight)

ASTM C1338 Fungal Resistance of Insulation Materials Passed

ASTM C1511 Liquid Water Retention After Submersion 4% (by weight)

ASTM C1559 Modified Wicking of Water Into Glass Fiber Passed (no wicking)

ASTM E84 Surface Burning Characteristics Flame Spread Index = 0Smoke Developed Index = 5

UL 1709 Hydrocarbon Pool Fire- 4” (100 mm) steel pipe- 0.016” (0.4 mm) stainless steel cladding

6 mm = 15 min12 mm = 25 min18 mm = 34 min24 mm = 42 min30 mm = 51 min

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

5

ASTM C 177 - THERMAL CONDUCTIVITY

Aspen has completed third-party validation of its thermal conductivity results. Thermal conductivity of the Pyrogel 6350 material is as follows:

Pyrogel 6350 = 16.3 mW/m-K @ 50°C

Pyrogel 6350 = 34.8 mW/m-K @ 350°C

The final report in Appendix A shows the full thermal conductivity curve from 50°C to 300°C.

•

•

Thermal Conductivity

Thermal ConductivityASTM C 177 Results

Temperature (°C)0 100 �00 �50 350

�00 300 400 500 600Temperature (°F)

0

Thermal Conductivity, k (m

W/m

-K)

5

10

15

�0

�5

30

0

0.05

0.10

0.15

0.�0

Ther

mal

Con

duct

ivity

, k (

BTU

-in/h

r-ft

� -°F

)

50 150 300

35100

Mean Temp. °C 0 50 100 150 �00 �50 300 350

°F 3� 1�� �1� 30� 39� 48� 57� 66�

k mW/m-K 15.9 16.3 16.9 18.1 �0.� �3.5 �8.� 34.8

BTU-in/hr-ft�-°F 0.11 0.11 0.1� 0.13 0.14 0.16 0.�0 0.�4

ASTM C 335 - THERMAL CONDUCTIVITY

Aspen completed a third-party validation of its thermal conductivity using the guarded end pipe configuration. Results are in agreement with C-177 within the standard deviation of the two test results and are as follows:

Pyrogel 6350 = 21.6 mW/m-K @ 149°C

The final report is in Appendix B.

•

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

6

ASTM C 356 - LINEAR SHRINKAGE UNDER SOAKING HEAT

ASTM C 356 measures linear shrinkage when subjected to soaking heat for 24 hours. The third party result for Pyrogel 6350 at 309°C was <2.5%. The third party test result can be found in Appendix C.

ASTM C 411/C 447 - HOT SURFACE PERFORMANCE

Dimensional stability is also part of the criteria for determining maximum use temperature, ASTM C411/C447. This is a pipe test configuration. At a hot surface temperature of 385°C, shrinkage across the length of the pipe was <0.33%, and circumferential shrinkage measured at 10 cm intervals was <2.3%. Third party test results can be found in Appendix D.

ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

ASTM E ��8 can be found in Appendix E. A number of materials were tested in this report. However, only the table and plot for Pyrogel 6350 have been included in Appendix E. Testing was done from -170°C - 250°C.

EFFECTS OF LONG TERM THERMAL EXPOSURE

An internal analysis of simulated long term exposure (up to 20 years) was done to understand thermal and mechanical stability. The report is attached in Appendix F. The simulated 20-year exposure indicates that Pyrogel will exhibit minimal shrinkage and thermal performance degradation over the course of its lifetime at its recommended operating temperature. The shrinkage was less than 2% with no change in thermal performance.

Dimensional Stability

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

7

ASTM C 165 - COMPRESSIVE STRENGTH ( ROOM TEMP)

Compressive resistance measured at both 10% and 25% compression for standard conditions is shown in Appendix G, section 3.0, tables 2 and 3. It is part of a large report from Bodycote outlining a number of tests. The average compressive resistance was 80 kPa (@10%) and 170 kPa (@25%).

ASTM C 592, SECTION 11.11.6 - PROCEDURE FOR HEAT AND VIBRATION

In this test method, the sample is heated for 24 hours @ 210°C and then vibrated for 6 hours @ 12 Hz and 3 mm displacement. The results are attached in Appendix G, Table 1. Pyrogel 6350 shows a 6.4% weight loss upon heat treatment, which is mostly absorbed water. After vibration, the material recovers some of its weight due to re-absorption of water. The net result of heating and vibration is that there is essentially no loss due to vibration. Appendix G, Fig 1 shows the material after heating and vibration. As may be observed, the material is essentially pristine.

ASTM C 1101, SECTION 7.1 AND 7.2 - FLEXIBILITY AND RESILIENT FLEXIBILITY

The sample was tested for flexibility and resilient flexibility. The sample is classified as resilient flexible. The results of third party testing are in Appendix G, Page 6.

COMPRESSION RECOVERY AT HIGH STRESS LOAD

An internal analysis of compression recovery showed Pyrogel 6350 to recover 80% of its thickness after loads as high as 875 psi. The report is given in Appendix H. The stress strain curve is shown in Chart 1 at right.

Mechanical Resilience

Chart 1

Compressive Stress vs. Percent StrainCrosshead Speed = 5 ipm

Maximum Stress = 6.033 Mpa = 875 psi

0.0

1.0

2.0

3.0

4.0

5.0

6.0

7.0

0 10 20 30 40 50 60 70 80 90

% Strain

Com

pres

sive

Stre

ss, M

Pa

PG6350

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

8

ASTM C 1559 - WICKING

In this test, insulation is suspended in water, and the distance that water wicks is measured over 168 hours. Pyrogel 6350 is hydrophobic (repels water) and shows no water wicking. Results of third party testing are located in Appendix G, Tables 7 and 8.

ASTM C 1104 - WATER VAPOR ADSORPTION

This test measures the water absorbed by insulation exposed to a high humidity environment. Results are shown in Appendix G, Table 5. The average weight gain is 4%, and the average volume gain is 1%. Pyrogel 6350 meets the requirements for ASTM C 547 Standard Specifications for Mineral Fiber Pipe Insulation.

ASTM C 1511 - WATER REPELLENCY

Water repellency test results are given in Appendix G, Table 6. Average weight gain was 2.3 grams, which is 0.0023 kg. ASTM C 800 Specification for Fibrous Glass Blanket Insulation requires Repellency in kg 0.020 max. Pyrogel 6350 passes the requirement of ASTM C800.

Water Resistance

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

9

ASTM C 665, SECTION 13.8 - CORROSION TEST

Pyrogel 6350 was tested using the Standard Specification for Mineral-Fiber Blanket Thermal Insulation for Light Frame Construction and Manufactured Housing Section 13.8 only, aluminum and copper. The performance criteria for this test are outlined in ASTM C 547 Standard Specification for Mineral Fiber Pipe Insulation Section 7.4. The specification is corrosion no greater than comparative plates in contact with sterile cotton and is greater than or equal to 21 for aluminum and copper. Our test results in Appendix G, Table 4 give values of 39.5 and 40 for aluminum and copper respectively, a clear pass for these criteria.

ASTM C 795 - STANDARD SPECIFICATION FOR THERMAL INSULATION FOR USE IN CONTACT WITH AUSTENITIC STEEL

Difficulties were encountered with testing in accordance with ASTM C 795 “Standard Specification for Thermal Insulation for Use in Contact with Austenitic Steel.” This specification requires testing in accordance with C 871 and C 692. The chemical requirements of this specification, C 871, were easily met with our results being well within specification. The results were: pH 8.6, chloride 24 ppm, and fluoride 1 ppm. However, testing in accordance with C 692 proved to be an obstacle. Aspen’s insulation blanket is hydrophobic; the C 692 method requires contact between the insulation and the water. To circumvent the non-wicking behavior of our materials, tunnels were cut into the insulation coupons, and the water dripped directly into these cracks. The test result was a pass with 4 coupons showing no cracking. Appendix I has the results for C 795.

Extractable pH Measurements of Pyrogel 6350

Pyrogel 6350 is hydrophobic, therefore there was some question as to the validity of the pH measurement for C871. This test is also designed for materials that readily wick water. In order to replicate real-world conditions involving the use of Pyrogel 6350, a modified ASTM C871 test was done to determine surface extractable pH. The method was meant to replicate small amounts of water that may inadvertently compromise the insulation system. Details of the test are found in Appendix J. The results indicated that extractable pH values for Pyrogel 6350 using a modified ASTM C871 did not differ significantly from the values obtained by ASTM C871 — pH was 7.1 for the modified test and 7.3 for the official test.

ASTM C 1338 - FUNGAL RESISTANCE

Pyrogel 6350 was tested using the Standard Test Method for Determining Fungi Resistance of Insulation Materials and Facings. The criteria for a pass are that test specimens have growth no greater than on the comparative item. Pyrogel 6350 showed zero or no growth and is considered a pass. Appendix K has the third party test data.

Chemical Resistance

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

10

ASTM E 84 - FLAME AND SMOKE SPREAD

Testing in accordance with ASTM E 84 Standard Test Method for Surface Burning Characteristics of Building Materials was performed on Pyrogel 6350 and is given in Appendix L. Pyrogel 6350 satisfies the criteria for a Class A rating with flame spread index: 0, smoke developed index: 5, and fuel contribution: 0.

UL 1709 - STRUCTURAL STEEL FIRE PROTECTION

Pyrogel 6350 was tested for Rapid Rise Fire Tests of Protection Materials for Structural Steel. The sample is subjected to furnace heat of 2000°F and the approximate heat flux of 204 kW/m2. Thermocouples recorded the temperature of the steel pipe under the insulation and the time to reach 1000°F under the insulation is reported. Four layers of Pyrogel 6350 take 47:20 (MM:SS) to reach 1000°F. The third party test results can be found in Appendix M.

Fire Testing

0

100

200

300

400

500

600

700

800

900

1000

0 10 20 30 40 50 60

Hydrocarbon Pool FireUL 1709 Results

0 30 40 50

Pipe

Tem

pera

ture

(°F

)

Time (min)

0

100

300

400

500

600

700

1000

�00

800

900

10 �0 60

300

0

100

�00

400

500

Pipe Temperature (°C)

mm (in)

6 (0.24)

12 (0.48)

18 (0.72)

24 (0.96)

30 (1.20)

EUROPEAN TESTING

Pyrogel 6350 was tested according to EN ISO 13823 and EN ISO 11925-2. The results for the third party testing are located in Appendix N.

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

11

ASTM E 1222 - INSERTION LOSS OF PIPE LAGGING SYSTEMS

ASTM E1222 Standard Test Method for Laboratory Measurement of the Insertion Loss of Pipe Lagging Systems. The third party test results are presented in graph form and the complete test report is located in Appendix O.

Acoustical Properties

Pipe Lagging Insertion LossASTM E 1222-90 Results

-2

3

8

13

18

23

28

33

500 1000 1500 2000 2500 3000 3500 4000 4500 5000

0

5

10

15

�0

�5

30

35

1000 �000 3000 4000 5000

Inse

rtio

n Lo

ss (

dB)

Frequency (Hz)

f(kHz)

IL(dB)

f(kHz)

IL(dB)

0.6 13 �.0 18

0.8 8 �.5 �0

1.0 13 3.� �6

1.3 15 4.0 3�

1.6 15 5.0 35

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

1�

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

13

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

14

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

15

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

16

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

17

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

18

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

19

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�0

Appendix A - C 177 THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�1

Appendix B - ASTM C 335 - THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

��

Appendix B - ASTM C 335 - THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�3

Appendix B - ASTM C 335 - THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�4

Appendix B - ASTM C 335 - THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�5

Appendix B - ASTM C 335 - THERMAL CONDUCTIVITY

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�6

Appendix C - ASTM C 356 - LINEAR SHRINKAGE UNDER SOAKING HEAT

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�7

Appendix C - ASTM C 356 - LINEAR SHRINKAGE UNDER SOAKING HEAT

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�8

Appendix D - ASTM C 411/C 447 - HOT SURFACE PERFORMANCE

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

�9

Appendix D - ASTM C 411/C 447 - HOT SURFACE PERFORMANCE

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

30

Appendix D - ASTM C 411/C 447 - HOT SURFACE PERFORMANCE

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

31

Appendix D - ASTM C 411/C 447 - HOT SURFACE PERFORMANCE

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

3�

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

33

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

34

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

35

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

36

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

37

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

38

Appendix E - ASTM E 228 - LINEAR COEFFICIENT OF THERMAL EXPANSION

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

39

Appendix F - EFFECTS OF LONG TERM THERMAL EXPOSURE

TECHNICAL GUIDE

™

N A N O T E C H N O L O G Y A T W O R KTM Pyrogel Insulation

40

Appendix F - EFFECTS OF LONG TERM THERMAL EXPOSURE