Simotec FRP Rod & Silicone Elastomer Details
2FRP Rod
Inside:
Outside:
ECR-glass Epoxy Resin ~ 30%ECR-glass Epoxy Resin ~ 30%
Special glass fibresfor high tension load
Special glass fibresfor high tension load
Additional protection due toungrinded rod surface
Additional protection due toungrinded rod surface
Every rod is labeled with month/yearand suppliers brandmark
Every rod is labeled with month/yearand suppliers brandmark
3Tests on Core
10 pcs. in dye solution of Fuchsin(1 g Fuchsin in 100 g Ethanol)
6 samples boiled in deionised water for 100 h
Dye penetration test Water diffusion test
After 20 min. no dye penetrated into the test specimen
12 kV / 1 min. no puncture or flashover occurred No current registration (max. value 1mA)
4Shortly performed test to prove acid resistance of ourECR glass fibre rod.
Result:Tests was passed succesfully
Remark:A parallel test using E-glassfailed after a few hours
Acid Resistance Test
5Acid Resistance Test
Density 1,07
Viskosity 120 000 mPa
Reactivity, T60-time 9,01 (at 90C)
Tracking resistance ~ 4,5 kV
Loss of mass 0,10%
Localized corrosion no
Arc resistance HL2
Tear resistance 23 N/mm
Elongation of break 430%
Shore A hardness 39
6Silicone Testing
3 flashover in vertical position No tracking Erosion occurred No sheds were punctured
Silicone A SIMOTEC -
Silicone
No flashover No tracking No erosion occurred No sheds were punctured