- T.Vijaykumar
Application to key materials
MBE
Introduction
Technical data• Effusion cells• Growth mechanism• RHEED
Application• Quantum dots• HEMT• High Tc Superconductors• GMR
Summary
Outline
11
Invented in late 1960’s at Bell Laboratories by J. R. Arthur and A. Y. Cho.
22
33
Diagram of a typical MBE system growth chamber 44
55
Molecular beam epitaxy (MBE) is performed with different types of semiconducting materials like: i) Group IV elemental semiconductors like Si, Ge, and C ii) III-V-semiconductors: arsenides (GaAs, AlAs, InAs), antimonides like GaSb and phosphides like InP iii) II-VI- semiconductors: ZnSe, CdS, and HgTe
Electrons move through GaAs five times faster than through silicon.
66
Features of MBE 1. very low deposition rates typically 1um/hr or 1A/sec2. typically in ultra-high vacuum 3. Uses high purity elemental charge materials.4. very well controlled growth5. films with good crystalline structure 6. often use multiple sources to grow alloy films 7. deposition rate is so low that substrate temperature does not need to be as
high .
For good epitaxy:
deposition rate -
Epitaxy: Growth of film with a crystallographic relationship with the substrate Types: Homoepitaxy & Heteroepitaxy.
77
The Gas-Source MBE (GS-MBE) III-V semiconductors, group-V materials are hydrides such as arsine (AsH3) or phosphine (PH3)
Metalorganic MBE (MO-MBE) group-III materials are metalorganic compounds. e.g., TEGa and TMIn
Solid-Source MBE (SS-MBE) group-III and -V molecular beams.
Types of MBE
88
Cylindrical crucible offers good charge material capacity, but uniformity decreases as charge material is depleted. It offers excellent long-term flux stability, but permits large shutter flux transients.
Conical crucible offers reduced charge material capacity, excellent uniformity, and poor long-term flux stability, and permits large shutter flux transients.
SUMO crucible offers excellent charge material capacity, excellent uniformity, excellent long-term flux stability, and minimal shutter-related flux transients.
Effusion cells
99
- made of Ta, Mo, and pyrolytic boron nitride (PBN) - do not decompose or outgas impurities even when heated to 1400ºC.
1010
Valved cracker Effusion cell- combines the evaporation and cracking of elements like P,S, As, Se, Te etc.
Technical Data
Heating System Radiation heating, tantalum wires with PBN insulators
Temperature range 100 °C ...800 °C bulk zone100 °C ...1000 °C cracker
Temperature stability <= 0.1 K depending on the PID controller
Bake out temperature 250 °C
1111
Atoms arriving at the substrate surface may undergo• absorption to the surface, • surface migration, • incorporation into the crystal lattice, • thermal desorption. depends strongly on the temperature of the substrate..
MBE growth mechanism. 1212
Growth modes:At very high temperature of substrate, there are many different possible surface
diffusion mechanisms:
Ehrlich-Schwoebel barrier
• very low rates of impinging atoms, • migration on the surface and • subsequent surface reactions
epitaxial growth is ensured by-
1313
- high migration rate (IBAD is followed) Frank vander merwe growth mode.
- high rate of incoming atoms and high Ehrlich-Schwoebel barrier, island growth will occur. Volmer-Weber or Stranski-Krastanov growth modes.
- Stranski-Krastanov growth is possible in a heteroepitaxial system.
Depending on the migration rates, different growth modes can result:1414
1515
1616Reflection high-energy electron diffraction (RHEED).
sensitive to surface changes, either due to structural changes or due to adsorption. 1. to calibrate growth rates, 2. observe removal of oxides from the surface, 3. calibrate the substrate temperature, 4. monitor the arrangement of the surface atoms, 5. determine the proper arsenic overpressure, 6. give feedback on surface morphology, 7. provide information about growth kinetics
A high energy beam (3-100 keV) is directed at the sample surface at a grazing
angle.
- distance between the streaks - surface lattice unit cell size.
- atomically flat surface - sharp RHEED patterns.
- rougher surface - diffused RHEED pattern.
layer-by-layer growth mode - RHEED oscillations.
1717
RHEED is sensitive for surface structures and reconstructions.
a) GaAs(100) - 1x1 b) GaAs(100) - 2x1
electron beam is incident in the (110) with 8.6 keV
1818
Interpretation of some RHEED patterns1919
2020
Different stages of layer-by-layer growth by nucleation of 2D islands and the corresponding intensity of the diffracted RHEED beam.
(a) Transmission through high and wide crystal; (b) Transmission through high and narrow crystal; (c) Transmission through short and wide crystal; (d) Diffraction from nearly flat asperities.
2121
RHEED intensity oscillations: - direct measure of growth rates in MBE.- oscillation frequency corresponds to the monolayer growth rate.- incident angle dependence of the oscillations suggest that interference between electrons scattering from the underlying layer and the partially grown layer contribute to these oscillations.- magnitude of the RHEED oscillations damps because as the growth progresses, islands nucleate before the previous layer is finished.
2222
Beam Equivalent Pressure
- To measure the growth rate. - Proportional to the flux at the sample surface and hence the growth rate.
- The biggest difficulty is, the gauge gets coated.
2323
Epitaxial Growth of AlxGa1-xAs
Substrate temperatures - 580ºC-650ºC.Requires an As overpressure to prevent the surface from becoming Ga rich.
GaAs, there is a large window for which there is both unity sticking and sufficient mobility.
Ternary or quaternary compounds - the window becomes smaller - differences in the relative bond strengths of the different group III adatoms.
RHEED can be used to determine the minimum amount of As required to maintain the proper stoichiometry by measuring the incorporation ratio.
Values of the incorporation ratio for GaAs is 1.3 to 1.8.
2424
(100) is the predominant substrate orientation for MBE growth of compound semiconductors.
Growth of InGaAlAs on InP: Incorporating In into AlxGa1-xAs will decrease the bandgap.
In.52Al.48As - 1.49 eV 0.74 eV - In.53Ga.47As - small enough bandgap to detect light at the important wavelengths of 1.3 mm and 1.55 mm.
Lattice constants and mismatch for GaAs, AlAs and InP.
+3.7% on GaAs
5.869InP
-3.5% on InP
5.661AlAs
-3.7% on InP
5.653GaAs
Mismatch :
Lattice Constant
(Å)
Material
+3.7% on GaAs
5.869InP
-3.5% on InP
5.661AlAs
-3.7% on InP
5.653GaAs
Mismatch :
Lattice Constant
(Å)
Material
2525
Quantum dotsstructures based on highly lattice mismatched materials.
mean free path and the de Broglie wavelength of free carriers exceed the critical sizes of structures.
carriers experience a three-dimensional quantum confinement.InAs grows layer-by-layer till critical coverage - wetting layer (WL).
After θc=1.6 ML (w~0.5 nm), Stranski-Krastanow 3D growth occurs.
relaxation of the elastic energy which builds up as the thickness of mismatched epilayers increases.
2626
2727
AFM image of InAs/GaAsQuantumdots.
Mismatched heteroepitaxial systems for quantum dots:
III-V compounds arsenides (InGaAs/AlGaAs ,InAs/InGaAs, InAlGaAs /AlGaAs ) phosphides (InAs/InP, InP/InGaP ), antimonides and nitrides (GaN/AlN),
IV-IV compounds Ge/Si and SiGe/Si
II-VI compounds CdSe/ZnSe and
Mixed-group compounds InAs/Si.
2828
Bennett, Magno, and Shanabrook Appl. Phys. Lett. 68 (4), 22 (1996)
E = Eg + Ee + Eh
E - emission energy Eg - quantumdot bandgap energyEe - electron confinement energyEh - hole confinement energy Nt: Exciton binding energy is neglected.
2929
Tuning QD emission 3030
C. K. Chia et al., J. Crystal. Growth, 288, 57-60 (2006)
The two essential structural features in copper oxide superconductors –
1. CuO2 planes 2. charge reservoirs (CR)
High Tc Superconductivity:increases in the Tc in thin films of copper oxide superconductors hydrostatic pressures compressive epitaxial strain.Under compressive epitaxial strain a much larger increase in Tc is possible. Requires the choice of a suitable system and substrate combination
The possible control knobs are:1. the distance between the magnetic (black arrows) Cu atoms dab, 2. the corrugation of the CuO2 planes alpha 3. the thickness of CR dCR 4. the interlayer distance between two consecutive CuO2 planes dIL 5. the distance between the charge reservoir and the CuO2 plane dCT.
the lattice deformations associated with the strain fundamentally modify theenergy scales, leading to the formation and condensation of the superconducting pairs.
3131
"214" film on a SrTiO3 substrate, the Cu and O atoms of the CuO2 planes are expanded."214" thin film on a SrLaAlO4 substrate in-plane compression and an out-of-plane expansion.
- redox reaction at interface is a serious problem fabricating tunnel junctions using high-Tc Cuprates,
3232
J. P. Locquet et al., Nature 394, 453 (1998)
The graphite-like array of boron (shown in black)
MgB2 a novel material for high Tc superconductor.
-has great promise for superconducting electronics operated at T ~ 20 K.
Josephson tunnel junctions (MgB2/AlOx/MgB2) fabricated on sapphire -C substrates below 300° C.
3333
K. Ueda, S. Saito, K. Semba, T. Makimoto and M. Naito, APL 86 , 172502 (2005)
Gallium Nitride (GaN) HEMTDr. Takashi Mimura - inventor of HEMT ( - FET with a junction between two materials with different band gaps as the channel instead of an n-doped region.
Features of GaN HEMThigh frequency power transistors for RF transmission applications covering the 1-50 GHz band. inherently higher transconductance, good thermal management and higher cutoff frequencies.prime candidate for high power microwave applications.
3434
M. Aslf Khan, J. N. Kuznia, et al, Appl. Phys. Lett., 65(9):1121
extremely low noise device in terrestrial and space telecommunications systems, radio telescopes in the area of astronomy, DBS receivers and a car navigation receivers.In 1985, HEMT was announced as a unique microwave semiconductor device with the lowest noise characteristics in the world.
3535
- can receive TV programs from satellites 36,000Km above the ground.- The antenna is less than 30 centimeters in diameter,
3636
GMR heterostructures:
- magnetoresistance is much larger than that of the intrinsic magnetoresistance of the Fe layers themselves
Oscillatory coupling - a very general property of almost all transition-metal magnetic multilayered systems the nonferromagnetic layer comprises one of the 3d, 4d, or 5d transition metals or one of the noble metals
The oscillation period was found to be just a few atomic layers, typically about 10 Å, but varying up to ~20 Å.
- ferromagnetic cobalt layers separated by thin copper layers, was found to exhibit very large GMR effects even at room temperature
GMR sandwiches can achieve sensitivities to such fields of perhaps as much as five hundred times greater than conventional materials.
- prepared in 1986, using MBE
3737
For copper thickness (typically 1.9 nm) - anti-parallel magnetic coupling between successive cobalt layers in zero applied field.
"spin valve" effect:
the magnitude of the interlayer exchange coupling decreases much more rapidly with increasing Cu thickness.
3838
IBM J . RES. DEVELOP. VOL 42 NO. 1 JANUARY 1998
GMR read heads allows the reading of extremely small magnetic bits at an areal density of 2.69 gigabits per square inch.
One minute please…………..
Summary
- MBE is a versatile technique for device fabrication.
- A good lab for studying Molecular dynamics and surface mechanism.
- The primary application for MBE - grown layers is the fabrication of
electronic devices .
3939
www.research.ibm.com/research/demos/gmr/1.swf
www.research.ibm.com/research/demos/gmr/2.swf
Appropriate other meanings of MBE
• Mind Boggling Experiment
• Mostly Broken Equipment
• Mega-Buck Evaporator
• Medieval Brain Extractor
• Money Buys Everything
• Management Bullshits Everyone
4040