Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
139
Improvement of the mechanical properties of concretes and mortars by addition
of polypropylene
Abdelhamid Noufid and Sougrati Belattar
University of Cadi Ayyad, Faculty of Science Semlalia, Mly Abdelah’s Street, BP 2390/40000, Marrakech,
Morocco.
Abstract: The objective of this work is the valuation of polypropylene fibers in the manufacture of
concretes and mortars. The aim is to investigate the impact of adding polypropylene fibers to the
concrete and mortar in order to improve the mechanical properties. In order to measure the
compressive and tensile strengths of concrete at ages of 3 days, 7 days and 28 days and the
characteristics of adhesion of the mortar. The results obtained are compared with an ordinary
concrete and mortar. According to this study an optimal addition of the polypropylene fibers
allows an increase in the mechanical characteristics of the concretes and the mortars. This
increase can reach 12% of the compressive strength at the age of 28 days. In order to enhance this
work, we will try to compare the results with thorough research that has been carried out.
Keywords: concrete, mortar, fibers, compressive strength, tensile strength.
1. Introduction
Polypropylene fiber reinforced concrete (PFRC) belongs to the category of multiphase heterogeneous
composite materials composed of fine aggregates, coarse aggregates, cement and polypropylene fibers.
Because polypropylene fibers possess a good strengthening and toughening feature, which are able to improve
plain concrete’s mechanical performance, PFRC has been widely used and in engineering construction (e.g.,
applied in aqueduct structures to prevent cracks causing water leakage) [1-2]. Concrete is frequently used in
buildings, water structures, bridges and highways [3]. Relatively low tensile strength and poor resistance to
crack opening and propagation are the main disadvantages of conventional concrete [4-7]. To deal with this
kind of problem, additions are used, as is the case with steel or polypropylene fibers. There are several types
of fibers in both families, but this paper focuses on the addition of fibers in concrete and mortar
polypropylenes to assess the impact of these fibers on the characteristics. In parallel, for the mortar, many
researchers have treated the use of fibers in mortar to improve its thermal and / or mechanical properties,
including polypropylene fibers [8-9]. Moreover, studies have revealed that the main role of these fibers in
composites is the ‘‘sewing effect’’ [10-11], which consists of a bridging action by fibers across the formed
cracks, thus controlling propagation of cracks and leading to more post-cracking resistance. On the one hand
the addition of fibers to concrete has been shown to enhance the toughness of concrete [12]. On the other hand
a significant improvement of toughness and flexural post-cracking behavior have been observed in reinforced
mortars, regardless of the nature and amount of fibers [13]. As part of the upgrading of polypropylene fiber in
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
140
the field of ready-mix concrete production, an experimental program is launched to highlight the different
characteristics of the polypropylene fiber. For this purpose, two applications are possible:
- Incorporation in concrete
- Incorporation in mortar to be used as a masonry substrate for common elements.
The experimental study carried out in this direction has a dual objective:
- Identify the general characteristics of conventional concretes and mortars by comparing them to
polypropylene fiber concretes.
- Highlight the particular characteristics of polypropylene fiber-based concrete and mortars.
2 Tests on Basic Materials
2.1 Materials
The materials used in this study come from different quarries:
- Crushed gravel GII and crushed sand from BBENSLIMANE quarry/Morocco;
- GI gravels come from the SKHIRAT quarry/Morocco;
- The dune sand comes from the region of KENITRA/Morocco;
- The cement (binder) used is a Portland CPJ 45 cement brand HOLCIM/Morocco;
- The mixing water used is the drinking water of the network;
- Polypropylene fibers as shown in Fig1, whose geometry and properties are provided in Table 1.
Figure. 1. Picture taken of the fibers used in this study
Table 1. Properties of polypropylene
Shape of fiber Length l (mm) Diameter d
(mm)
Aspect ratio l/d Density (g/cm3) Tensile
strength (MPa)
Straight 12
0.022 545
9.1 350 6 273
2.2 Tests and Studies
The different basic materials were subjected to identification. The main results are summarized in Table 2:
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
141
Table 2. Test on aggregates
Aggregate Gravel GII Gravel GI Crushing sand Sand of dune
Sand Equivalent (%) [14] - - 56 89
Coefficient of flattening [15] 27 21 - -
Actual density [16] 2,65 2,66 - -
Absorption coefficient [16] 1,0 1,1 - -
Actual density [17] - - 2,60 2,64
Absorption coefficient [17] - - 1,2 1,0
Los Angeles [18] 17 18 - -
Superficial cleanliness [19] 1.2 0.8 - -
The results obtained show that the materials used meet the performance requirements for the manufacture
of concrete type B2 in the sense of Moroccan standard NM 10.1.008 [20].
3 Experimental Program on Concrete
3.1 Composition Study
Based on the results of Table 2, we will proceed to the formulation of the concrete using the method of
“DREUX-GORISS” [21]. Thus, on the basis of the "DREUX - GORISSE" method, the quantities of the
concrete mixture are shown in Table 3.
Table 3. Concrete formulation
Sample Granular class % of mixture Actual density Dosage
(Kg/m3)
GII 8.3/25 44 2.65 840
GI 6.3/16 18 2.66 345
Crushed sand 0/3.15 12.7 2.60 238
Sea sand 0/0.4 25.3 2.64 481
Cement CPJ 45 350
Mixing water - - - 185
3.2 Experimental Program
Three mixes were made with the same amounts of the mixture mentioned in the Table 3 by varying the level of
fibers in each mixture:
- Mixture B1 with 0% of fibers (witness concrete);
- Mixture B2 with a dosage of 900 g / m3, a percentage by volume of 0.10 %;
- Mixture B3 with a dosage of 1200 g / m 3, a percentage by volume of 0.15 %.
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
142
The fiber introduced is a polypropylene fiber 12 mm long. The three blends were subjected to the
characterization tests in the fresh and cured state.
Figure. 2. A mix of concrete with fibers at the time of mixing
4 Experimental Program on Mortar
The mortar object of the study is composed of sand (dune sand), cement and drinking water in the proportions
defined in Table 4.
Table 4. Composition of mortars
Materials Quantity (g)
Sand 1350
Cement 4450
Water 300
Three mixes were made with the same amounts of the mixture mentioned in the Table 9 by varying the
level of fibers in each mixture:
- A mixture M1 with 0% of fibers (witness mortar) ;
- A mixture M2 with a dosage of 600 g / m3, a percentage by volume of 0.07 % ;
- A mixture M3 with a dosage of 900 g / m3, a percentage by volume of 0.10 %.
The fiber used is a 6 mm long polypropylene fiber.
5 Results and Discussion
5.1 Results of Tests on Concrete
Fresh Tests. After the pouring of the mixes, fresh concrete tests were carried out, namely the test for
slumping, LCPC (Central laboratory for bridges and highways) maneuverability and density [22]. All the
results obtained, in the fresh state, are shown in Figs 3 and 4:
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
143
Figure. 3. Maneuverability tests for the three mixes studied
Figure. 4. Air occlus and density mass for the three mixes
The presence of the fibers in the concrete has the effect of reducing its maneuverability. Thus, for a
concrete test with 30 mm of collapse, the fiber concrete at 900 g / m3 has a lower slump (25 mm). This
collapse is reduced to 23 mm for the concrete dosed at 1200 g / m3. This remark remains valid for the LCPC
maneuverability test whose time t (s) increases with a larger fiber dosage.
Hardened Tests. The hardened concrete undergoes a crushing program, namely a compression test at the age
of 3, 7 and 28 days and a tensile test at the age of 28 days. We represent the results in Tables 5, 6 and 7.
Figure. 5. Hardened concrete without fiber
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
144
Table 5. Tests on hardened concrete without fiber
Ref specimen Age (days) Weight (kg) Density
(Kg/m3)
Compressive
strength (MPa)
Tensile
strength (MPa)
B1/1
/2
/3
3
15.361
15.370
15.368
2.39
2.39
2.39
15.0
15.5
15.0
-
-
-
/4
/5
/6
7
15.586
15.572
15.566
2.42
2.42
2.42
19.0
18.5
19.0
-
-
-
/7
/8
/9
28
15.627
15.641
15.636
2.43
2.43
2.43
28.0
28.0
28.0
-
-
-
/10
/11
/12
28
15.638
15.647
15.656
2.43
2.43
2.43
-
-
-
2.5
2.5
2.6
Figure. 6. Hardened concrete containing fibers 900 g/m
3
Table 6. Tests on hardened concrete: Fiber concrete (900g/m3)
Ref specimen Age (days) Weight (kg) Density
(Kg/m3)
Compressive
strength (MPa)
Tensile
strength (MPa)
B2/1
/2
/3
3
15.362
15.377
15.356
2.40
2.40
2.40
15.0
16.5
17.0
-
-
-
/4
/5
/6
7
15.483
15.471
15.496
2.41
2.40
2.41
20.0
19.5
19.0
-
-
-
/7
/8
/9
28
15.651
15.661
15.648
2.43
2.43
2.43
30.0
30.5
29.5
-
-
-
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
145
/10
/11
/12
28
15.672
15.663
15.656
2.43
2.43
2.43
-
-
-
2.8
2.6
2.6
Figure. 7. Hardened concrete containing fibers 1200 g/m
3
Table 7. Tests on hardened concrete: Fiber concrete (1200 g/m3)
Ref specimen Age (days) Weight (kg) Density
(Kg/m3)
Compressive
strength (MPa)
Tensile
strength (MPa)
B3/1
/2
/3
3
15.452
15.463
15.448
2.40
2.40
2.40
19.0
19.5
18.5
-
-
-
/4
/5
/6
7
15.520
15.531
15.538
2.41
2.41
2.41
22.5
22.5
22.0
-
-
-
/7
/8
/9
28
15.441
15.456
15.463
2.40
2.40
2.40
31.0
31.5
32.0
-
-
-
/10
/11
/12
28
15.445
15.459
14.470
2.41
2.41
2.41
-
-
-
2.7
2.8
2.7
We represent in Figs 8 and 9 the average of the results at the age of 3, 7 and 28 days:
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
146
Figure. 8. Compressive strength at the age of 3, 7 and 28 days
Figure. 9. Tensile strength at the age of 28 days
Thus, there is an improvement in the compressive strength between the ordinary concrete and the fiber
concrete, this improvement being 2 MPa for the concretes measured at 900 g / m 3 (approximately 7%) and 3.5
MPa for the concrete measured at 1200 g / m3 (about 12%). On the similar trend, there is an improvement in
flexural strength (respectively 6 % and 8 %). Similar studies have been conducted to confirm these results.
Indeed, Afroughsabet V & Ozbakkaloglu T [23] recorded an increase in compressive and tensile strengths by
addition of PP fibers: this increase reached 8% for compressive strength and 13% for resistance to bending at
the age of 28 days.
Correlation between flexural and compressive strength. In this paragraph, the correlation between the compressive
strength and the tensile strength is studied; The BAEL code [24] speaks of this correlation and gives a correlation law
between the compressive strength and the tensile strength in accordance with equation (1). According to Fig 10, there is a
good linear correlation between the compressive and tensile strength (correlation coefficient : R2 = 0.979). The slope of
this correlation is almost the same with respect to the BAEL 91 code, but a difference of 0.3 MPA between the additional
parameters, i.e. 0.9 MPa instead of 0.6 MPa.
28 280.06* 0.6c tf f ; For 2840 60cMPa f MPa (1)
With:
- 28cf : Compressive strength at the age of 28 days;
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
147
- 28tf : Tensile strength at the age of 28 days;
Figure. 10. Correlation between compressive and tensile strengths
5.2 Results of Tests on Mortar
Study of Behavior in the Fresh State. Measurement of the start and end of setting time was carried out
according to the European standard (EN 196-1) [25]. The main results obtained are given in Table 8.
Table 8. Start and end of cement setting
Mortar Start of setting End of setting
M1 (witness) 4 hours 5 hours 30 min
M2 (600 g/m3) 3 hours 35 min 5 hours 10 min
M3 (900 g/m3) 3 hours 35 min 5 hours 15 min
There is thus a decrease in the start and end time of setting for the fiber mortar in comparison with the
ordinary mortar. This reduction is approximately 20 minutes for mortars at 600 g/m3 and 15 min for mortars at
900 g / m3.
Study of Behavior in the Hardened State. The different mixtures were introduced into 4 × 4 × 16 cm3
prismatic molds. The made-up prisms were subjected to bending and compression tests at 3, 7 and 28 days .
The main results obtained are given in Figs 10 and 11. The measurements were carried out in accordance with
the European standard EN 196-1 test standard.
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
148
Figure. 11. Flexural strength at the age of 3,7 and 28 days
Figure. 12. Compressive strength at the age of 3, 7 and 28 days
According to these results, it can be said that the best results are obtained in the case of M2 (fiber dosage of
600 g / m3). Thus, the optimum dosage of use of the polypropylene fibers is 600 g / m 3. Silva E R et al [26]
studied several types of fibers, found an increase or decrease in flexural and compression strengths which
reached between -8.6% to 40.4% for the compressive strength and between 1.7% and 40.7% for the flexural
strength. This depends on the morphology, geometry and percentages of the fibers, but in our case, it is
interesting to study the percentage of fiber presence.
Study of Behavior in the Hardened State. Principle: The adhesion strength is measured as the maximum
tensile stress per direct charge perpendicular to the surface of the coating mortar applied to a support. The
tensile force is applied to a defined traction pad bonded to the test surface of the mortar. The force of adhesion
is the ratio between the breaking load and the corresponding surface [27].The test consists of bonding the
tensile pellets to the center of the surface of the specimens by means of a resin-based adhesive, for example an
epoxy resin or a methyl methacrylate resin. By means of the pulling apparatus, the tensile load is applied
perpendicularly to the test surfaces by means of the pellets. The load is applied without impact and at a uniform
speed. Using a velocity such as that stress increases in a range of 0.003 N / mm2.s to 0.100 N / mm2.s
depending on the expected bond strength so that failure occurs between 20 s and 60 s. The breaking load is
recorded. Adhesion strengths are calculated from the equation (2) at 0.05 N / mm2 [27]:
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
149
uu
Ff
A (2)
With:
- fu is the adhesion force (N / mm2);
- Fu is the breaking load (N);
- A is the test surface of the cylindrical specimen (mm2).
Forms of rupture giving reliable results are shown in Figs. 12 to 14. When rupturing forms such as those
illustrated in Figs. 13 and 14 are obtained, that is to say without breaking at the mortar interface / Support, the
results should be considered as values at the lower limit. These values must be taken into account when
calculating the average value of the adhesion force.
Figure. 13. Break at the interface between the mortar and the support: The test value is equal to the adhesion
force
Figure. 14. Break in the mortar: The adhesion strength is higher than the test value
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
150
Figure. 15. Breaking of the support: The adhesion strength is greater than the test value
Figure. 16. Test area for non-fiber mortar
Figure. 17. Test area for a mortar of 600 g/m
3 fiber
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
151
Figure. 18. Test area for a mortar of 900 g/m
3 fiber
The results obtained are summarized in the Table 9.
Table 9. Adhesion tests on mortar and mortar with fiber
Samples Charge (daN) Adhesion (MPa) Average Type of rupture
Mortar
N=°1 30.64 0.35
0.33
Adhesive failure
N=°2 34.46 0.40 Adhesive failure
N=°3 26.13 0.30 Adhesive failure
N=°4 29.24 0.30 Adhesive failure
N=°5 24.78 0.30 Adhesive failure
Mortar with
fiber (600 g/m3)
N=°1 12.21 0.15
0.17
Cohesive rupture
N=°2 17.88 0.20 Adhesive failure
N=°3 14.18 0.15 Adhesive failure
N=°4 15.99 0.15 Adhesive failure
N=°5 16.28 0.20 Adhesive failure
Mortar with
fiber (1200
g/m3)
N=°1 62.39 0.70
0.32
Adhesive failure
N=°2 31.69 0.35 Cohesive rupture
N=°3 24.27 0.30 Cohesive rupture
N=°4 8.25 0.10 Cohesive rupture
N=°5 13.88 0.15 Cohesive rupture
It is then noted that:
- For witness mortar (0g/m3), they have an adhesive strength of 0.33 MPa (arithmetic average) with
adhesive failure.
- For mortars with a dosage of 600 g/m3 of fiber, bond strength of 0.17 MPa (arithmetic average) is
observed with adhesive failure mode in the majority of cases.
- For mortars with a dosage of 900 g/m3 of fiber cement, an adhesion strength of 0.32 MPa (arithmetic
average) with a cohesive rupture mode is noted.
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
152
The comparison of the different values obtained shows that with the addition of the polypropylene fiber,
there is an improvement in the adhesion of the mortar to the support since the mode of rupture is in most cases
cohesive.
6 Conclusions
We conclude with the following points:
At the concrete level, the incorporation of the polypropylene fibers in the concrete has improved
the mechanical performance of the concretes studied, in particular the compressive strength, this
improvement is approximately 7% for a dosage of 900 g / m 3 and of 12% for a dosage of 1200
g/m3. Conversely this improvement reaches 6% for the tensile strength in the case of a dosage of
900 g / m3 and 8% for a dosage of 1200 g / m3. These results are confirmed in comparison with
similar studies that have been carried out in this direction.
At the mortar level, the incorporation of the polypropylene fibers has reduced the initial setting time
for mortars. This reduction is approximately 20 minutes for mortars at 600 g and 15 min for mortars
at 900 g / m 3. As to regard of the resistances, the optimum dosage for better results in terms of
compressive and flexural strengths is 600 g / m 3, being a percentage of 0.07 % of volume.
The study of the adhesion of the mortars to the support shows that the incorporation of the fibers
improves the adhesion of the mortars to the support since one passes from an adhesive rupture for a
mortar without fibers to a cohesive rupture for a fibered mortar.
References
[1]. Zhang. H, Liu. Y, Sun. H, Wu. S, “Transient dynamic behavior of polypropylene fiber reinforced mortar
under compressive impact loading”, Constr Build Mater 2016; 111:30–42.
[2]. Zhang. H, Liu. L, Dong. M, Sun. H, “Analysis of wind-induced vibration of fluid– structure interaction
system for isolated aqueduct bridge”, Eng Struct 2013; 46:28–37.
[3]. Erdem. RT, Gucuyen. E, Kantar. E, Bag. M, “Impact effect on different sized reinforced concrete
specimens”, Indian J Eng & Mater Sci 2015; 22:597-603.
[4]. Rashiddadash. P, Ramezanianpour. AA, Mahdikhani. M, “Experimental investigation on flexural
toughness of hybrid fiber reinforced concrete (HFRC) containing metakaolin and pumice”, Constr Build
Mater 2014; 51:313–320.
[5]. Yan. H, Sun. W, Chen. H, “The effect of silica fume and steel fiber on the dynamic mechanical
performance of high-strength concrete”, Cem Concr Res 1999. 29 (3):423–426.
[6]. Kayali. O, Haque. M.N, Zho. B, “Some characteristics of high strength fiber reinforced lightweight
aggregate concrete”, Cem Concr Compos 2003; 25 (2):207–213.
[7]. Brandt. AM, “Fiber reinforced cement-based (FRC) composites after over 40 years of development in
building and civil engineering”, Compos Struct 2008; 86 (1–3):3–9.
Journal of Engineering Technology Volume 6, Special Issue on Technology Innovations and Applications Oct. 2017, PP. 139-154
153
[8]. Boumhaout. M, Boukhattem. L, Hamdi. H, Benhamou. B, Nouh. A F, “Thermomechanical
characterization of a bio-composite building material: Mortar reinforced with date palm fibers mesh”,
Constr Build Mater 2017; 135:241–250.
[9]. Shaikh. F U A, Shafaei. Y, Sarker. PK, “Effect of nano and micro-silica on bond behaviour of steel and
polypropylene fibres in high volume fly ash mortar”, Constr Build Mater 2016; 115:690–698.
[10]. Foti. D, “Preliminary analysis of concrete reinforced with waste bottles PET fibers”, Constr Build Mater
2011; 25:1906–1915.
[11]. Felekoglu. B, Tosun. K, Baradan. B, “Effects of fibre type and matrix structure on the mechanical
performance of self-compacting micro-concrete composites”, Cem Concr Res 2009; 39:1023–1032.
[12]. Srikar. G, Anand. G, Prakash. S, “A Study on Residual Compression Behavior of Structural Fiber
Reinforced Concrete Exposed to Moderate Temperature Using Digital Image Correlation”, Int J Con Str
Mater 2016; 10:75–85.
[13]. Liguori. B, Caputo. D, Iucolano. F, “Fiber-reinforced lime-based mortars: Effect of zeolite addition”,
Constr Build Mater 2015; 77:455–460.
[14]. EN 933-8, “Tests for Geometrical Properties of Aggregates - Part 8: Assessment of Fines — Sand
Equivalent Test”, European Standard, 1999.
[15]. EN 933-3, “Tests for Geometrical Properties of Aggregates – Part 3: Determination of Particle Shape —
Flakiness Index”, European Standard, 2012.
[16]. EN 1097-6, “Tests for Mechanical and Physical Properties of Aggregates - Part 6: Determination of
Particle Shape — Flakiness Index”, European Standard, 2014.
[17]. NM 10.1.149, “Granulats-Mesure des Masses Spécifiques Coefficient d'Absorption et Teneur en Eau des
Sables”, Moroccan Standard, 1995.
[18]. EN 1097-2, “Tests for Mechanical and Physical Properties of Aggregate - Part 2: Methods for the
Determination of Resistance to Fragmentation”, European Standard, 2010.
[19]. NM 10.1.169, “Granulats-Détermination de la Propreté Superficielle”, Moroccan Standard, 1995.
[20]. NM 10.1.008, « Béton de Ciments Usuels », Moroccan Standard, 2007.
[21]. Gorisse. F and Dreux. G, “Formulation des Bétons”, ANNALES, France, 1993.
[22]. NF P 18-452, “Mesure du Temps d'Ecoulement des Bétons et des Mortiers aux Maniabilimètres”,
Moroccan Standard, 1988.
[23]. Afroughsabet. V, Ozbakkaloglu. T, “Mechanical and durability properties of high-strength concrete
containing steel and polypropylene fibers”, Constr Build Mater 2015; 94:73–82.
[24]. CSTB, “BAEL 91 Révisées 99”, France, 2000.
[25]. EN 196-1, “Methods of Testing Cement – Part 1 : Determination of Strength”, European Standard, 2006.
[26]. Silva. ER, Coelho. JFJ, Bordado. JC, “Strength improvement of mortar composites reinforced with
newly hybrid-blended fibres: influence of fibres geometry and morphology”, Constr Build Mater 2013;
40:473–480.
[27]. EN 1015-12, “Methods of test for mortar for masonry - Part 12: Determination of Adhesive Strength of
Hardened Rendering and Plastering Mortars on substrates”, European Standard, 2001.