ICF-8, KIEV, 8 — 14. 06. 1993
fracture mechanic!
successes ano
PMDBLEMi
Collection of Abstracts
Part I
, JOSv
V
Editors: V.V.PanasyukF.Rama Rao
A.Ye.AndreykivN.V.KuznyakM.P.Savruk
ICF-8 Organizing Committee
Academy of Sciences of Ukraine
Karpenko Physiko-Mechanical Institute
UB/TIB Hannover111 982 154
89
Lviv-1993
ICF8 PARTI I
CONTENTS
INTRODUCTION
PLENARY LECTURES
DEFORMATION CRITERIA IN FRACTURE
MECHANICS OF MATERIALS
VKPanasyuk 3
THE SCIENCE AND ENGINEERING OF FRACTURE
J.F.Knott 4
WELDING AND STRENGTH OF STRUCTURESB.Ye.Paton 5
MECHANICS AND CRITERIA OF FRACTURE 7
FRACTURE OF MATERIALS IN COMPRESSION
ALONG CRACKS BASED ON THE CONCEPT OF A
LOCAL INSTABILITY NEAR DEFECTS
AMGuz', V.M.Nazarenko 9
CLEAVAGE FRACTURE OF HY80 STEEL IN
AS-QUENCHED CONDITION
W.Zhou, J.F.Knott 9
ASYMPTOTIC ANALYSIS OF THE GRIFFITH
PROBLEM WITH ACCOUNT OF THE ACTION OF
THE' INTERATOMIC. COHESION FORCES
VMAleksandrov, B.I.Smetanin 11
TWILIGHT ZONE OF FRACTURE FROM SINGULAR
CRACK TIP TO NON REGULAR PROCESS REGION
KB.Broberg 12
HOW TO DEFINE THE SHAPE OF A PROPAGATING
CRACK DUE,TO GRIFFITH AND IRWIN
APPROACHES
SA.Nazarov, O.R.Polyakova 12
BEARING CAPACITY OF A RADIALLY CRACKED
FLOATING PLATE INCLUDING CRACK-CLOSURE
EFFECTS
J.P.Dempsey, LLSkpyan 13
MECHANICS OF MACRO- AND MICRO-FRACTURE:
SIZE/TIME/TEMPERATURE INTERACTION EFFECTS
• G.C.Sih 14
tl PARTI ICF8
FRACTURE TOUGHNESS EVALUATION FROM
TENSION AND CHARPY-TYPE SPECIMENS BASED
ON MICROMECHANICAL MATERIAL MODELS
D.-Z.Sun, W.Brocks, W.Schmitt 16
A NON-LOCAL CRITERION OF STRENGTH TAKING
INTO ACCOUNT THE SURFACE LAYER
Vratislav Kafka, Miroslav Hlavacek,Vaclav Kvet, Martin Ehrenberger 17
MICROMECHANISMS AND MECHANICS OF
FRACTURE — TRANSFERABILITY OF
LABORATORY TEST RESULTS TO COMPONENTS
A.Pineau 18
STATE-OF-THE ART ON DETERMINISTIC FRACTALS
IN FRACTURE
B.KRaghuprasad, G.S.Bhattacharya 19
PROBABILISTIC FATIGUE FRACTURE MODELS OF
COMPLEX SYSTEMS
KAArutunian 20
ANISOTROPY OF MECHANICAL FAILURE OF
POROUS MATERIALS
G.A.Babushkin 20
LIMITING STATE OF CONSTRUCTION ELEMENTS
WITH DIFFERENT KINDS OF DAMAGES
N.M.Borodachev, Yu.I.Kazarinov,OA.Shevchenko 21
A CRACK PROPAGATION IN RESIDUAL
MICROSTRESS FIELD SIMULATION
T.V.Busheva 22
ENERGETIC MODEL OF MICROCRACKING AND
FRACTURE OF CONTINUOUSLY REINFORCED
COMPOSITE MATERIALS BY LONG-TERM LOAD
M.VDelavsky 23
DEFORMATION AND FRACTURE IN POROUS
BODIES
Eva Dudrova, Karol Pelikdn,Ludovit Parildk 23
INVARIANT FRACTURE CRITERIA FOR A MODE I
CRACK AND THEIR APPLICATIONS
G. V.Galatenko 24
ICF8 PARTI III
GENERALIZATIONS OF THE WEIBULL
DISTRIBUTION IN THE STATISTICAL MODEL OFSTRENGTH OF FRACTURED MEDIUM
G.T.Kimichansky, G.XRubets,B.M.Usachenko 25
STRUCTURAL OPTIMIZATION ACCOUNTING FORREALIABILITY CRITERIA
V.P.Malkov, A.KLjubimov 2.6
STRUCTURAL AND MECHANICAL CRITERION OF
BRITTLE FRACTURE
B.Z.Margolin, VA.Shvetsova 26
GRADIENT CRITERIA OF STRENGTH AND THEIR
RELATION WITH LINEAR FRACTURE MECHANICS
M.D.Novopashin, MA.Legan 27
COHESIVE-ADHESIVE FRACTURE OF REINFOFCEDCOMPOSITES
B.LPelekh, I.M.Korovajchuk 28
FRACTAL APPROACHES IN FRACTURE MECHANICS
OF HETEROGENEOUS SOLIDS
V.V.Silberschmidt 29
A TWO-CRITERIA. APPROACH TO PREDICTING
FRACTURE IN CYLINDERS WITH AXIAL CRACKS
V.M.Torop, I.VOrynyak 30
CONTINUOUS THEORY OF DEFORMATION AND
FRACTURE OF DAMAGED MATERIALS
V.LYanko, V.I.Fedenko 31
MIXED MODE CRACK GROWTH IN HIGH
STRENGTH ALUMINIUM
FMlsson, N.Hallbdck 32
ANALYSIS OF A MULTIPLE CRACK BRANCHING IN
NON-ISOTROPIC MATERIALS
D.Leguillon 33
TWO-PARAMETER CHARACTERIZATION IN
ELASTIC-PERFECTLY PLASTIC
PRESSURE-SENSITIVE DILATANT MATERIALS
Guoyu Lin, Huang Yuan, Alfred Cornee,Karl-Heinz Schwalbe 34
THE FRACTURE OF SILICON PARTICLES IN AN
ALUMINIUM CASTING ALLOY DURING TENSILE
DEFORMATION
CH.Caceres, CJ.Davidson, J.RGriffiths 35
IV PARTI ICF8
PHYSICAL NATURE OF MATERIALS STRENGTH
AND FRACTURE CHARACTERISTICS EMPIRICAL
DEPENDENCES UPON TIME
A.Ya.Krasowsky, Toth Lasio 36
INFLUENCE OF PRELIMINARY PLASTIC
DEFORMATION ON CRACK RESISTANCE
V.T.Troshchenko, P.V.Yasniy 37
FAILURE MODES OF COMPOSITES:
A COMPREHENSIVE COMPARISON OF TENSOR
POLYNOMIAL CRITERIA
Pericles S. Theocaris 38
THE INFLUENCE OF THE TYPE OF STRESS STATE
ON THE FRACTURE TOUGHNESS OF PRESSURE
VESSEL STEELS IN DIFFERENT STATES
AA.Lebedev, N.G.Chausov, Yu.G.Dragunov,A. V.Getmanchuck 39
A FRACTURE CRITERION FOR NOTCHED SAMPLES
OF HIGH-STRENGTH PEARLITIC STEEL
J.Toribio 40
CRACK GROWTH AND FRACTURE AS INSTABILITY
PHENOMENA
V.V.Bolotin 40
A SHEAR STRESS BASED CRITICAL PLANE
CRITERION OF FAILURE FOR DESIGN AND LIFE
PREDICTION UNDER MULTIAXIAL FATIGUE STRESS
D.L.McDiarmid 41
MODELLING OF CREEP CRACK GROWTH UNDER
CONSTANT AND CYCLIC LOADING
VJAstafiev, VA.Pastukhov 42
DEVELOPMENT OF TABLES FOR DETERMINING
THE PARAMETERS OF THE BEREMIN MODEL FOR
CLEAVAGE FRACTURE
M.Di Fant, C.Rerolle, P.Testard, P.Rabbe 43
UNIFORM CRITERIA FOR ESTIMATION OF THE
MATERIAL LOCAL STRESS STATE AT'
THE CRACK TIP
G. V.Klevtsov, LRBotvina 44
QUASIMICROPLASTIC PROPERTIES OF SOLIDS AT
PRE-FRACTURE STAGE
G.G.Kochegarov, E.I.Mashinsky,V.ZKoksharov 45
ICF8 PARTI V
TO THE NON-LINEAR THEORY OF FRACTURE
MECHANICS
G.G.Kuliyev 46
ON THE APPLICABILITY OF DAMAGE MODELSFOR THE DESCRIPTION OF THE FAILURE
BEHAVIOR OF DUCTILE STEELS
K-Kussmaul, M.Seidenfiiss, U.Eisele 47
FRACTURE OF HETEROGENEOUS
TWO-D1MENS10NAI LATTICES UNDER THE
DIFFERENT REGIMES OF LOADING
N.I.Lebovka, V.V.Mank, l.I.Marczin,N.S.Pivovarova 47
THERMOFLUCTUATIONAL MODELS OF BRITTLE
AND QUASI-BRnTLE CRACK GROWTH
A.I.Malkin 49
PHYSICAL AND MECHANICAL MODEL OF
INTERCRYSTALLINE FRACTURE BY STATIC AND
CYCLIC LOADING
B.ZMargolin, V.A.Shvetsova, A.G.Gulenko 50
NON-LOCAL STRENGTH CONDITIONS AND
FRACTURE CRITERIA: FUNCTIONAL APPROACH
S.E.Mikhailov 51
SELF-ORGANIZATION, KINETIC TRANSITIONS IN
ENSEMBLES OF DEFECTS AND PROBLEMS OF
CONTINUUM DAMAGE MECHANICS
O.B.Naimark 52
A UNIFIED MODEL OF BRITTLE MODE 1
FRACTURE IN TENSION AND IN COMPRESSION
V.P.Naumenko 52
THE PHENOLOGICAL DESCRIPTION OF
LONG-RANGE FRACTURE WITH A MODEL OF THE
HEREDITARY TYPE
LJ.Ogorodov, RA.Pavlov 53
TO THE QUESTION ON DETERMINATION OF
CRACK GROWTH RESISTANCE CHARACTERISTICS
OF THE ELASTIC-PLASTIC MATERIALS WITHIN
THE SCOPE OF S^-MODELI.M.Pan'ko, B.M.Zaidel 55
FRACTURE AS A DISCRETE PROCESS
YuJ.Ragozin 56
NEW MIXED MODE FRACTURE CRITERIA
S.KRoy 57
VI PARTI ICF8
ENERGY ACCUMULATION CAPACITY AND
FRACTURE TOUGHNESS OF MATERIALS
LA.Skotnikov, G.D.Lebedev 51
FRACTURE AND EQUILIBRIUM DAMAGE
ACCUMULATION ON POSTCRITICAL
DEFORMATION STAGE
AA.Tashkinov, V.EWldeman, AMAnoshkin 58
A PROBABILISTIC CRITERIA OF HETEROGENEOUS
AND DEFECT MATERIALS FRACTURE
P.M.Vytvytsky, RI.Kvit 59
INTERNAL PLASTIC INCOMPATIBILITIES
ACCUMULATION AS FACTOR OF HARDENING AND
DAMAGING OF DEFORMED HETEROGENEOUS
MATERIALS
AA.Zisman, V.V.Rybin 60
CRACK PROPAGATION CRITERIA IN PLATES AND
SHELLS UNDER FINITE DEFORMATIONS
LMZubov 61
AUTOOSCILATIONS OF THE FATIGUE CRACK
G.I.Barenblatt, LRBotvina 62
DAMAGE LOCALIZATION: MICRO AND MACRO
FRACTURE CRITERIA
Ju.I.Kadashevich, JaA.Chernjakov 62
MODELLING OF THE CONSTITUTIVE BEHAVIOUR
OF MATERIALS WITH INTERNAL DAMAGE
Holm Altenbacht, Peer Schiefie 63
THE FRACTURE MECHANICS. THE DEVELOPMENT
OF THE OF KOLOSOV, NOVOZHILOV, KACHANOV
IDEAS AT THE ST.-PETERSBURG UNIVERSITY
N.Morozov 64
STOCHASTIC APPROACH OF THE RELIABILITY OF
FIBERGLASS REINFORCED LAMINATED WOOD
CONNECTING PIECES FOR GLULAM
CONSTRUCTION
CA. Szttcs, PhJodin, G.Pluvinage 64
MICROPOLAR WAVES IN FATIGUE AS A
GENERATOR OF DAMAGE MICROMECHANISMS
AND OF DISPERSION ON HARDENING
Anatoliusz Jakovluk 65
VARIANT OF STATISTIC THEORY OF BRITTLE
STRENGTH OF GLASS STRUCTURES AND THEIR
OPERATIVE RELIABILITY
A.M.Margolin, VA.Osadchuk 66
ICF8 PARTI VII
STRESS-STRAIN ANALYSIS IN
SOLIDS WITH CRACKS 69
SOME RECENT RESULTS ON CRACK-TIP ANALYSIS
MADE IN CHINA
. Hwang Keh-Chih 71
BEHAVIOUR OF THE STRESSES NEAR PLANE
WEDGESHAPED DEFFECTS
GA.Morari, G.Ya.Popov 71
EFFECT OF DAMAGE ON THE CRACK-TIP HELD
IN POWER-LAW MATERIALS
D.Gross, CkZhang 71
ON MAXIMAL STRESSES IN ELASTIC ISOTROPIC
PLANE WITH A CRACK OF NONLINEAR
DEFORMATIONS
LAPrusov 72
THE ORDER OF SINGULARITY AT CORNER POINTS
OF THE WEDGE-SHAPED CRACKS AND CONTACT
AREAS
VA.Babeshko, EV.Glushkov, N.VGlushkova 74
HIGH-ORDER ASYMPTOTIC FIELDS AT THE APEX
OF A NOTCH FOR A POWER-LAW HARDENING
BIMATERIAL
Shou-Wen Yu, Ming Yang 15
DEFORMATION AND FRACTURE OF CRACKED
MEDIA WITH FRICTION OF CRACK SURFACES AT
COMPLEX LOADING
RV.Goldstein, Yu.V.Zitnikov 76
NON-LINEAR LINE SPRING MODEL AND
COMPLEMENTARY ENERGY METHOD OF SURFACE
CRACK
Q.Gao, Z.Z.Huang 76
ON THE SOLUTION METHOD OF THREE
DIMENSIONAL PROBLEMS FOR CRACKED LAYER
VA.Shaldyrvan 77
BOUNDARY INTEGRAL EQUATION METHOD IN
FRACTURE MECHANICS
M.P.Savruk 77
INVESTIGATION OF A KINKED CRACK SYSTEM
WITH GENERALIZED STRESS SINGULARITIES BY
MEANS OF THE INTEGRAL EQUATION METHOD
W.Meiners, KRHerrmann 78
VIII PARTI ICF8
ON A GENERAL THREE-DIMENSIONAL WEIGHT
FUNCTION METHOD
A.N.Borodachev 79
THE INTENSITY OF THE STRESSES NEAR THE
PEAKS OF THE ELASTIC ANGULAR DEFECTS
I.T.Denisyuk 80
INVESTIGATION OF THE STRESSED NONLINEAR
ELASTIC PLANE WITH CRACK
L.G.Doborjginidze 81
A COMPATIBLE AND COMPLETE 6-NODED
ELEMENT TO MODEL SINGULARITIES
Bijan KDutta 82
ELASTO-PLASTIC FRACTURE ANALYSIS OF AN
ELBOW WITH A LONGITUDINAL SURFACE CRACK
UNDER IN-PLANE BENDING
Ph.Gilles, C.Franco, C.Migne 82
REINFORCEMENT OF CRACKED PLATE BY
SYSTEM OF PARALLEL STRINGERS
G.S.Ivanyts'ka, V.S.Kravets', O.I.Semenets' 83
INVESTIGATION ON THE SINGULARITIES OF
ASYMPTOTIC SOLUTIONS IN STATIONARY CRACK
AND STEADY CRACK GROWTH WITH NONLINEAR
MATERIALS
T.M.Guo 84
ANALYSIS OF STRESS FIELDS WELDED JOINTS
WITH SURFACE CRACKS
VAKarkhin 85
SLIP-LINES IN THE CORNER POINT OF THE
MEDIA-SEPARATING BOUNDARY
LA.Kipnis 86
PLASTICITY BAND BUNDLES AT THE ANTI-PLANE
DEFORMATION OF THE BODY WITH A CRACK
VA.Kryven 87
STATE OF THE ART IN BEM APPLICATIONS TO
FRACTURE MECHANICS OF ANISOTROPIC MEDIA
S. V.Kuznetsov, A.N.Kulikovski,M.N.Perelmuter 88
STRESS STATE OF THE BONDED HALFPLANES
WITH INCLUSIONS AND CRACKS OF ARBITRARY
SHAPE
N.V.Kuznyak 89
ICF8 PARTI IX
METHODS FOR PROMOTING COMPUTATIONAL
EFFICIENCY AND ACCURACY OF BEM IN 3-D
LEFM PROBLEMS
Chunyu Lee 90
MODELS OF ELASTIC-PLASTIC STATE AND CRACK
GROWTH FOR MIXED MODES UNDER BIAXIAL
LOAD
NA.Makhutov, V.N.Shlyannikov,VA.Dolgorukov 90
MODEL OF THE CRITICAL CRACK OPENING FOR
THE TRANSVERSAL ISOTROPIC MATERIALS WITH
WORK-HARDENING
LP.Mazurak 91
NONLINEAR ANALYSIS OF RC SLABS AND
PANELS BY THE BOUNDARY ELEMENT METHOD
M.Minch, D.Stys 92
ASYMPTOTIC ANALYSIS OF ELASTICITY
PROBLEMS IN NON-COMPACT DOMAINS
CONTAINING CRACKS AND ELASTIC INCLUSIONS
A.B.Movchan 93
MODIFIED CRACK CLOSURE INTEGRAL (MCCI)USING QUARTER-POINT THREE-DIMENSIONAL
(3-D) ELEMENTS
KBadari Narayana 94
A STATE OF STRESS AND STRAIN IN THE
BOUNDED PLATES WITH CRACK AND PLASTIC
STRIPS
RM.Osiv 95
PLASTIC STRIP MODEL SOLUTIONS FOR PLANE
PROBLEMS OF FRACTURE MECHANICS
V.V.Panasyuk, M.RSavruk, A.M.Danilovich 96
ON STRESS STATE OF FIBER COMPOSITE WITH
CRACK IN MATRIX
A.V.Pavlenko, T.S.Kagadiy 97
ASYMPTOTIC EQUATIONS FOR NONLINEAR
STRAINS IN MATERIAL INTERFACE CORNERS AND
CRACKS
Matthias Scherzer 98
THE STRESSED STATE OF AN ELASTIC PLANE
WEAKENED BY COUNTABLE SET OF CRACKS
V.VSilvestrov 99
X PARTI ICF8
JUMP FUCTION METHOD IN FRACTURE
MECHANICS
G.T.Sulym 100
STRESS INTENSITY FACTORS EVALUATION FOR
THREE-DIMENSIONAL MLXED PROBLEMS BY
LOCAL WEIGHT FUNCTIONS
S.V.Torgov 101
STRESS DISTRIBUTION OF AN INCLINED
SEMI-INFINITE CRACK TERMINATING AT
INTERFACE BETWEEN DISSIMILAR MATERIALS
Jia Wang 102
ON A NUMERICAL INVESTIGATION OF BOUNDARY
COLLOCATION PROCEDURE AND WILLIAMS
SERIES CONVERGENCY
Xiangzhen Yan and Xioujuan Yang 102
DUAL INTEGRAL EQUATIONS OCCURRING IN
SPATIAL PROBLEMS OF ELASTICITY FOR
CRACKED BODIES
Andrei F.Ulitko 103
STRESS-STRAIN STATE OF A TRANSVERSELY
ISOTROPIC BODIES WITH AN ELLIPTIC CRACK
Yu.N.Podil'chuk 104
STRESS-STRAIN STATE OF ELASTIC SEMIPLANE
RELAXED BY REGULAR ROW OF CRACKS
Michael L. Buryshkin'
105
CRACK IN DAMAGED BODY AT SHEAR STRESS
STATE
V.Tamuzs, VPetrova 106
STRESS ANALYSIS OF AN INFINITE PLATE WITH
TWO UNEQUAL ARBITRARILY ORIENTED CRACKS
V.G.Ukadgaonker, Venkata K.P.Koppaku 107
EFFECT OF STRONG MAGNETIC FIELDS ON
MECHANICAL STRESS IN PIECE-WISE
HOMOGENEOUS, CONDUCTING SOLIDS.
LA.Filshtinsky 108
NUMERICAL METHODS OF FRACTURE
MECHANICS PARAMETERS CALCULATION
E.M.Morozov, TA.Chemysh 109
FEM ANALYSIS OF THE STEERING KNUKLE IN
ELASTIC-PLASTIC FRACTURE MECHANICS
ERusinski 110
1CF8 PARTI XI
INTERACTION OF COPLANAR SURFACE FLAWS
UNDER TENSION
Andrea Carpinteri 110
A FEM BASED SOLUTION FOR SINGULAR
INTEGRAL EQUATIONS IN 3D FRACTURE
MECHANISM
KMayrhofer, F.D.Fisher 111
STRESS INTENSITY FACTOR VARIATIONS ALONG
CRACK FRONTS UNDER THREE MODES IN
A ROUND BAR
J.Royer, A. Le van 112
STUDY OF STRESS-STRAIN CONDITION TO
LOCALIZED NECKING IN THIN TENSILE BAR BY
NONLINEAR PHOTOELASTIC METHOD
M.HAchmetzyanov, G.NAlbaut,V.N.Barishnikov 114
ASYMPTOTIC SOLUTIONS OF THE CRACK
PROBLEM FOR A NONHOMOGENEOUS ELASTIC
MATERIAL
SMAizikovich, LS.Trubchic 114
INVESTIGATION OF PLASTIC STRESS
DISTRIBUTION NEAR THE THIN NOTCH TIPS BY
PHOTOELASTIC COATING
G.NAlbaut, V.P.Tyrin 115
A NUMERICAL ANALYSIS OF STRESS-STRAIN
STATE OF CONTACTING ELASTIC BODIES WITH
CRACKS
AA.Bobylev 116
DEVELOPMENT OF A DATABASE FOR STRESS
INTENSITY FACTOR OF CRACKED ELBOW FOR
VARIOUS GEOMETRIES AND LOADING
J.Chattopadhyay, B.KDutta,H.S.Kushwaha 117
EVALUATION OF THE RELIABILITY
OF A FLAWED PIPE
N. Constantin, D.M. Constantinescu,StPastrama 118
STRAIN ENERGY RELEASE RATE AT A CRACK TIP:
EVALUATIONS BY A MIXED HYBRID ELEMENT
R-M.Courtade, P.Hamelin 119
THE EVALUATION OF THROUGH-CRACK SIFs
USING THE STRAIN-GAGING DATA
AD.Dementyev 120
XII PARTI ICF8
DEVELOPING IRWIN FORMULA TO IMPROVE THEACCURACY OF EVALUATION OF STRESSES AND
CRACK TIP PLASTIC ZONE SIZE
AM.Dotsenko 121
ON FRACTURE OF ONE-DIMENSIONAL FIBROUS
COMPOSITE UNDER COMPRESSION
V.RGeorgievskyi 121
EVALUATION OF STRESS-STRAIN STATE IN THE
ZONES OF CONCENTRATION AT LOW-CYCLE
LOADING AND ANISOTROPY
A.G.Kazantsev 122
ADVANCES IN OPTICAL METHODS FOR
INVESTIGATION STRESS STATE OF STRUCTURES
WITH CRACK-TYPE DEFECTS
Tibery Yu.Kepich 123
NEW METHOD OF TESTING STRENGTH OF
BRITTLE BODY AT SINGULAR AND REGULAR
POINTS
V.D.Kharlab 124
TO THE PROBLEM OF DETERMINATION OF
STRESS INTENSITY FACTOR IN INSTRUMENTED
IMPACT TEST
I.VKhodan, S.Ye.Kovchyk, VA.Zazulyak 124
ANALYSIS OF STRESSED STATE OF CLOSED
CYLINDRICAL SHELLS WEAKENED BY SURFACE
CRACKS
I.S.Kostenko, Je.M.Fedjuk 125
SEVERAL PLANE PROBLEMS OF BRITTLE
FRACTURE MECHANICS FOR CRACKS WITH
INTERACTING EDGES
I.LKudish 126
STRESSED STATE OF THIN
PIECEWISE-HOMOGENEOUS SHELLS WITH CRACKS
RM.Kushnir, S.Ya.Olijnyk 127
THE SEMI-WEIGHT FUNCTION METHOD IN THE
DETERMINATION OF STRESS INTENSITY FACTORS
FOR A CRACKED REISSNER'S PLATE
C.T.Liu, M.X.Zhou 128
CALCULATION OF ENERGY INTEGRAL FOR
BODIES WITH NOTCHES AND CRACKS
Yu.G.Matvienko, E.M.Morozov 129
ICF8 PARTI XIII
DAMAGE MECHANICS IN TERMS
OF FINITE STRESS
VE.Mirenkov, VA.Shutov 130
LIMIT EQUILIBRIUM OF ELASTO-PLASTIC
TRANSVERSALLY ISOTROPIC SHELLS WITH FLAWSOF A NONTHROUGH CRACK TYPE
M.M.Nykolyshyn 131
USE OF THE FINITE ELEMENT ALTERNATING
METHOD FOR EFFICIENT SOLUTION OF
3-DIMENSIONAL FLAWS IN AIRCRAFT
COMPONENTS
P.EO'Donoghue, S.NAtluri, EF.Punch 132
ELASTIC AND LIMIT EQUILIBRIUM OF
CONTTNUOSLY REINFORCED RECTANGULAR
PLATES WITH CRACKS
LJ.Onyshko, L.T.Berezhnitsky 133
INFLUENCE OF STRESS STATE AND STRESS
HISTORY ON CRACK OCCURRENCE
M.Plancak, D.Vilotic, V.Vujovii 134
STRESSED STATE OF ANISOTROPIC CYLINDRICAL
SHELLS WITH CUTS
I.B.Prokopovich, LM.Senkiv 134
AUTOMATED PHOTOELASTIC EVALUATION OF
STRESS INTENSITY FACTORS IN MULTICRACKED
PRESSURISED THICK CYLINDER
KRamesh, D.P.S.Chauhan 135
THE CUTS WITH THE CONTACTING EDGES IN
THE BENDING SHALLOW SHELLS
LP.Shatsky 136
IDENTIHCATION OF STRESS STATE IN THE
CRITICAL ZONE IN UPSETTING OF PRISMATIC
SPECIMEN BY CYLINDRICAL DIES
Dragisa Vilotic, Vlado Vujovvb,Miroslav Planbak 137
NUMERICAL ANALYSIS FOR J INTEGRAL OF
SUBINTERFACE CRACK
Yu Yonghe, Lai Man On 137
LOCAL EFFECTS AND LIMIT DIMENSIONS OF
DELAMINATIONS IN THE THINWALLED
COMPOSITE STRUCTURES
N.VZvolinsky, D.D.Zakharov, LV.Simonov 138
XIV PARTI ICF8
ON DETERMINATION OF FRACTURE PARAMETERS
IN LAYERED STRUCTURES
NJonsson, LDolhage, A.E.Giannakopoulos,B.Stordkers 139
ANALYSIS OF THE J INTEGRAL DURING THE
DUCTILE FRACTURE OF STEEL AND ALUMINUM
COMPACT TENSION SPECIMENS
Ram B.Bhagat, Michael B.House 139
THE POROUS PLASTIC STRESSES-DEFORMATION
FIELDS NEAR BLUNTED CRACK TIP IN STANDARD
SPECIMENS
- Zhen-Bang Kuang, Fashang Ma 140
FRACTURE IN ANISOTROPIC MATERIALS -
CLEAVAGE
D.Leguillon, ESanchez-Palencia 141
A NUMERICAL ELASTIC-PLASTIC APPROACH OF
THE CRACK INITIATION PROBLEM
N.PAndrianopoulos, VC.Boulougouris 142
ANALISIS OF STRESS SINGULARITIES BY DIGITAL
IMAGE PROCESSING ENHANCED MOIRE
INTERFEROMETRY
Arkady S. Voloshin 143
COMPUTER-GRAPHICS ASSISTED EVALUATION OF
EXPERIMENTALLY RECORDED CAUSTICS
ASSOCIATED WITH GENERAL INTERFACE CRACK
PROBLEMS
H.RRossmanith, RE.Knasmillner 144
FATIGUE: PHYSICS AND MECHANICS OF
FRACTURE 147
SOME RECENT ADVANCES IN METAL FATIGUE:
UNDERSTANDING THE TWO THRESHOLDS OF
FATIGUE BEHAVIQURKJ.Miller 149
MODELING OF LOW AND HIGH CYCLE FATIGUE
IN NONELASTIC SOLIDS
M.RWnuk, M.P.Weiss 150
ELASTIC-PLASTIC FINITE ELEMENT SIMULATION
OF CRACK TIP DEFORMATION IN FATIGUE
M.M.I.Hammouda, H.E.M.Sallam 150
FATIGUE CRACK PROPAGATION IN TA6V AT
ELEVATED TEMPERATURE
J.Petit, C.Sarrazin, W.Berata, S. Lestertin 152
ICF8 PARTI XV
ANALYSIS OF THE GROWTH OF SHORT FATIGUE
CRACKS IN ALUMINIUM ALLOYS
AJ.McEvily, Z.Yang 152
AN ANALYSIS OF CRACK TTP SHIELDING IN
DUAL-PHASE STEELS: A COMPARISON AMONG
DIFFERENT LONG AND SHORT CRACKS
Y.S.Zheng, ZG.Wang, S.HAi 153
CYCLIC STRAIN CRITERIA OF FATIGUE CRACK
NUCLEATION AT HIGH-CYCLE LOADING
VT.Troshchenko 154
EFFECT OF FLAWS ON FATIGUE STRENGTH OF
CAST MATERIALS
KMorita, KKajimoto, RMurai 155
MODEL OF FATIGUE CRACK
INITIATION AND GROWTH
V.V.Panasyuk, O.P.Ostash, EM.Kostyk 156
FRACTAL KINETICS OF FATIGUE FRACTURE OF
METALS
V.S.Ivanova 157
FATIGUE BEHAVIOUR OF A 12mm THICK
TITANIUM GRADE 2 PLATE
LM.Plaza, A.M.Irissari 158
THE FATIGUE PROPERTIES OF A CORROSION
PROTECTIVE SURFACE COATING
J.H.Bulloch 158
EXTREME VALUE STATISTICS APPLICATION TO
FATIGUE CRACKS INITIATION MODELLING
V.M.Dupliakin, T.D.Kovalenko and
S.N.Perov 159
THE SHORT CRACKS GROWTH MECHANISM AND
DETAILS LONGEVITY
A.V.Fishgoit, V.M.Maistrov, MA.Rosanov 160
A HYPOTHESIS OF CUMULATIVE DAMAGE FOR
FATIGUE CRACK INITIATION AND PROPAGATION
KMGolos 161
RUPTURE KINETICS AND FATIGUE LIFETIME OF
CRACKED PLATES CONSIDERING TWO-STAGE
FRACTURE
V.P.Golub, EA.Panteleyev 162
FATIGUE FRACTURE OF STRAIN METALLIC
MATERIAL
G.P.Guslakova 163
2 566-3
XVI PARTI ICF8
AUTOMODELITY AND KINETICS OF CRITICAL
PHENOMENON IN FRACTURE MECHANICS
V.S.Ivanova, I.G.Grabar 164
ELECTRIC CURRENT EFFECT INVESTIGATIONS ON
METAL FATIGUE LIFE
V.VKarpenko, A.E.Podgorodetsky 165
CRACK RESISTANCE OF THE STRUCTURAL
ELEMENT WITH A SMALL CRACK
WKonovalov, I.S.Yablonsky 166
A MODEL OF FATIGUE CRACK PROPAGATION BY
STRIATION MECHANISM
LV.Kramarenko 166
RETARDATION OF FATIGUE CRACK GROWTH BY A
THERMO-MECHANICAL METHOD
Y.C.Lam, J.RGriffiths, B.D.Chen 167
THE PROPAGATING FATIGUE CRACK LENGTH
ESTIMATION BASED ON CRACK OPENING VALUE
AT THE SPECIMEN EDGE MEASUREMENT RESULTS
Cz.Goss, J.Lesniewski, S.Klysz 168
MICROSTRUCTURAL INFLUENCE ON FATIGUE
CRACK PROPAGATION BEHAVIOUR OF
Ti-25Al-10Nb-3V-lMo ALLOY
G.Onofrio, VLupine 169
EVOLUTION OF THE STRUCTURAL CHANGES IN
SUPERFICIAL LAYER DURING EARLY FATIGUE
PROCESS
LPalaghian, C.Gheorghies 170
THEORY OF RESIDUAL STRESSES INFLUENCE ON
FATIGUE RESISTANCE UNDER STRESS
CONCENTRATION CONDITIONS
V.F.Pavlov, S.I.Ivanov 171
FATIGUE FRACTURE MECHANISMS IN
POLYETHYLENE (HDPE) AND POLYCARBONATE (PC)A.C.Riemslag 171
INFLUENCE OF THE RESIDUAL STRESSES ON THE
FATIGUE CRACK VELOCITY
V.N.Selyukov H3
INFLUENCES OF CRYOGENIC TEMPERATURES AND
MEDIA ON THE FATIGUE FAILURE RESISTANCE OF
Al-Li ALLOYS
VA.Serdyuk, N.M.Grinberg, A.M.Gavrilyako,I.N.Fridlyander, A.M.Drits, I.P.Zhegina,T.V.Krymova 175
1CF8 PARTI
NUMERICAL SIMULATIONS OF FATIGUE GROWTH
BEHAVIOURS OF NON-COLLINEAR CRACKS
Shan-TUng Tu 176
LIFE ESTIMATION FOR FATIGUE CRACK
NUCLEATION AND GROWTH AT THE NOTCH ROOT
M.M.Stadnyk, RV.Riznychuk, LV.Didukh 111
FATIGUE CRACK GROWTH RATE AND FRACTURE
TOUGHNESS OF DIFFERENT GRADES OF RAIL
STEELS
U.P.Singh, Ramakant Singh 111
ACCUMULATED CYCLIC DEFORMATION AS A
MEASURE OF CYCLIC DAMAGE
Y.Ustinovshchikov, LDaskovsky 178
SHORT CRACKS FRACTURE MECHANICS
A.N. Vasyutin 179
FATIGUE LIFE ESTIMATION UNDER
NON-STATIONARY RANDOM LOADING
M.Bily, J.Prohacka 180
EFFECTS OF SELECTIVE VARIABLE AMPLITUDE
LOADING ON FATIGUE CRACK GROWTH
MA.S.Torres, HJ.C.Voorwald 181
DAMAGE AND FRACTURE OF STRUCTURAL
MATERIALS UNDER COMPLEX LOW-CYCLE
LOADING
N.S.Mozharovski, N.I.Bobyr, O.N.Mukoida 181
ELASTIC AND PLASTIC FATIGUE CRACK
PROPAGATION LAWS UNDER IRREGULAR LOADING
A.P.Gusenkov, S.G.Lebedinsky 182
FATIGUE BEHAVIOR AND LIFE PREDICTIONS FOR
AZ91E-T6 CAST MAGNESIUM ALLOY
Rl.Stephens, S.N.Perov,D.LGoodenberger, V.V.Ogarevic 183
PREDICTION OF CONSTANT-AMPLITUDE FATIGUE
LIFE TO FAILURE UNDER PULSATING-TENSION
(R2>0) BY USE OF THE LOCAL-STRAIN-APPROACH
AND THE PROBLEM OF PROPER CHOICE OF K
ABuch, V.Galperin 184
MULTIPLE SITE DAMAGE FATIGUE AND AGING OF
AIRPLANES
RM.Pelloux 185
XVIII PARTI ICF8
COVARIANCE EFFECT OF BIAXIAL STRESS STATE
ON FATIGUE LIFE CALCULATION
Cyprian T. Lachowicz, Tadeusz Lagoda,Ewald Macha 185
FRETTING FATIGUE RESISTANCE OF ALUMINIUM
JOINTS
Dimitris Kosteas, Roland Ondra 186
EFFECT OF CRACK CLOSURE ON KINETICS OF
FATIGUE CRACK PROPAGATION UNDER MIXED
MODE LOADING IN 2024 AL-ALLOY SHEETS
RKPandey, Abde'l Mageed 186
FATIGUE ANALYSIS METHOD FOR WING
LOWER-SURFACE ELEMENTS OF TRANSPORT
AIRPLANE AT RANDOM LOADING
VAbramov, V.Strizhius 187
PECULIARITY OF CRACK FATIGUE AND FAILURE
DEVELOPMENT UNDER COMPOUND STRESS
AF.Berman 188
FATIGUE CRACK GROWTH RATE PREDICTION
UNDER COMPLEX STRESS STATE
N.ZBraude, I.N.Shkanov 189
AN INVESTIGATION ON FATIGUE AND FRACTURE
BEHAVIOR OF 30 CRMNSIA STEEL
Chen Guo-Ping 190
CRACKS PROPAGATION UNDER ROLLING
CONTACT INTERACTION
AP.Datsyshyn, G.RMarchenko 190
THEORETICAL STUDIES IN KINETICS OF FATIGUE
SURFACE FAILURE-
I.G.Goryacheva, O.G.Checkina 191
PROBABILITY PREDICTION OF LIMITING STATES
OF MATERIALS SUBJECT TO INHOMOGENEITY
DISPERS DAMAGES DIMENSIONS
S.RIgnatovich, AN.Vetrov, GA.Trokoz,S.I.Yovenko, N.V.Grischenko 192
HCF AND LCF FRACTURE MECHANISMS OF A
COMMERCIAL PURE ZIRCONIUM
Xiao Lin, Gu Haicheng 193
AN EXPERIMENTAL STUDY ON RETARDATION
BEHAVIOR OF LC4-CS AL-ALLOY UNDER
SINGLE-CYCLIC OVERLOADING
Liu Xue-hui 194
ICF8 PARTI XIX
FAILURE OF DISCS MATERIAL AND STRUCTURALSTRENGTH OF DISC-BLADE JOINTS UNDERNEAR-OPERATING CONDITIONS
N.S.Mozharovski, AAZakhovayko,S.N.Shukayev, A.B.Ovseyenko,A.Yu.Medinets 194
FRETTING AND FRETTING-FATIGUE OF MATERIALS
AND COMPONENTS
A.N.Petukhov 195
WHAT WE KNOW ABOUT PITTING
S.Pytko, M.Szczerek 196
EFFECTS OF CRACK CLOSURE UNDER TENSILE
OVERLOADS AND COMPRESSIVE UNDERLOADS
APing, DJ.Wang, H.Xu 197
SIMULATION FATIGUE CRACKS GROWTH IN
ALUMINUM ALLOYS UNDER BIAXIAL LOADING
AND R-RATIO
A.A,Shanyavsky, K.Z.Karaev,M.Z.Koronov, EF.Orlov 198
PREDICTION METHODS OF CRACK RESISTANCE
AND FATIGUE OF STRUCTURAL COMPONENTS
UNDER BIAXIAL STRESS
I.N.Shkanov 199
ON SOME FEATURES OF FAILURE AT MULTIAXIAL
CYCLIC LOADING
V.N.Stebenev, YuA.Svirsky 200
ANALYSIS OF DIRECT AND BACK EFFECTS
UNDER WEAR-FATIGUE DAMAGES
LA.Sosnovskiy, VAShurinov 200
TWO-PARAMETER MODEL OF FRETTING FATIGUE
CRACK GROWTH IN STRUCTURAL ALLOYS
V.T.Troshchenko, G.Vlsybanev,A.O.Khotsynovsky 201
THE CALCULATIONS ON ITS FATIGUE DAMAGE
EVOLVING RATE AND TOTAL LIFE UNDER
MANY-STAGE LOADING FOR A CRANKSHAFT
Yu Yangui, Zhang Wenbin 202
THE CALCULATIONS TO ITS DAMAGE EVOLVING
RATE AND LIFE FOR A COMPONENT UNDER
UNSYMMETRIC CYCLIC LOAD
Yu Yangui 203
XX PARTI 1CF8
CALCULATIONS TO ITS DAMAGE EVOLVING RATE
AND LIFE FOR A COMPONENT UNDER
SYMMETRIC CYCLIC LOAD
Yu Yangui 204
FATIGUE CRACK GROWTH OF CCT SPECIMEN
UNDER SPECTRUM LOADING OF A STEAM LINE
Zhenren Huang, Jianhua Song,Jianguo Cheng 205
ON THE CHOICE OF PARAMETERS OF THE CURVE
OF FATIGUE
GA.Zhuravlev, V.V.Bormotov 206
FATIGUE-CRACK PROPAGATION BEHAVIOR IN
ADVANCED MONOLITHIC AND COMPOSITE
INTERMETALLICS AND CERAMICS AT AMBIENT
AND ELEVATED TEMPERATURES
RO.Ritchie, RH.Dauskardt,KT.Venkateswara Rao 207
FRACTURE AND LOW CYCLE FATIGUE
BEHAVIOUR OF A515 GRADE 70 STEEL
C.M.Branco, J.M.Ferreira 208
MICROSTRUCTURE EFFECTS ON FATIGUE OF
METAL MATRIX COMPOSITES
John J.Lewandowski 209
A FINITE ELEMENT ANALYSIS OF CRACK
CLOSURE STRESSES UNDER CYCLIC LOADING
B.RSeshadri, B.Dattaguru,T.S.Ramamurthy, RSunder 209
THE EFFECT OF MICROSTRUCTURE ON THE
NEAR-THRESHOLD AND THRESHOLD FATIGUE
CRACK GROWTH BEHAVIOR OF TWO ROTOR
ALLOYS
A.Tipton, Chief Metallurgist 210
FRACTURE AND FATIGUE OF SINTERED STEEL
B.Cotterell, Y.W.Mai 211
FATIGUE CRACK GROWTH CHARACTERISTICS OF
THE CRYOGENIC STRUCTURAL MATERIALS
Takayuki Suzuki, Kazumi Hirano 212
DYNAMIC FRACTURE 213
THE NUMERICAL SOLUTION OF SOME PROBLEMS
IN DYNAMIC FRACTURE MECHANICS
VG.Boriskovsky, V.ZParton 215
ICF8 PARTI XXI
A LAGRANGIAN DESCRIPTION OF THE MOVING
CRACK PROBLEM
Gilles Debruyne 215
MATHEMATICAL MODELLING OF DYNAMIC
PROCESSES OF DEFORMATION AND
MICROFRACTURE OF THERMOELASTOPLASTTC
MEDIA
AB.Kiselev, M.VYumashev, AS.Zelensky 216
MATHEMATICAL PROBLEMS OF
THERMOELASnCITY FOR BODIES WITH CUTS
T.V.Burchuladze, D.G.Natroshvili 217
DYNAMIC FRACTURE OF ELASTIC-PLASTIC BEAM
WITH AN EDGE CRACK
Yinchu Lu, Guogin Tang"
211
DYNAMIC ACTIONS ON ELEVATED TANKS IN
HIGH-RISK SEISMIC AREAS
C.Cocca, A.G.Pizza, S.Santorelli 218
ACOUSTIC EMISSION AND NEAR-TIP
ELASTODYNAMIC FIELDS OF A GROWING
PENNY-SHAPED CRACK
J.DAchenbach 218
ENERGY-WAVE APPROACH IN FAST BRITTLE
FRACTURE MECHANICS
AG.Kotousov, NA.Machutov 219
SOME DYNAMIC PROBLEMS OF FRACTURE
MECHANICS
A.S.Bykovtsev, D.B.Kramarovsky 220
DETERMINATION OF STRESS CONCENTRATION IN
SOLIDS WITH CRACKS AT DYNAMIC LOAD
G.S.Kit, M.V.Khaj, V.V.Mykhas'kiv 220
REGULARITIES OF DYNAMIC FAILURE PROCESS
IN FAST HEAT SHOCK MODE
A.I.Pavlovskii, E,K.Bonjushkin, Kl.Zavada,SA.Novikov, LAPlatonova, N.D.Rabion,A.Ya.Uchaev 221
STRUCTURE AND FRACTURE MECHANISMS IN
STEEL UNDER SHOCK LOADING
NA.Bondarevskaya, P.Yu. Volosevich,VV.Golubev, M.N.Mysienko, A.N.Smirnov 222
THE INFLUENCE OF THE DEFORMATION SPEED
ON THE STRENGTH OF VULNERABLE TO
DAMAGE MATERIALS
Aleksander S.Bychkoy 223
XXII PARTI ICF8
NUMERICAL SIMULATION OF DYNAMIC
FRACTURE OF CONCRETE TARGETS IMPACTED BY
STEEL RODS
E. P. Chen 224
EFFECT OF AGEING ON IMPACT FRACTURE
BEHAVIOR OF 2024 AL-ALjO;, PARTICLE
COMPOSITES
RGiridhar, M.KSurappa 225
THE CRITICAL CONDITION FOR DUCnLE/BRLTTLETRANSITION IN IMPACT NOTCH-BEND TEST
W.S.Lei, M.Yao, C.T.Tlan, D.M.Li 225
SHOCK-INDUCED TRANSLATIONAL AND
ROTATIONAL MECHANISMS OF STRAIN
LOCALIZATION IN SOLID
YuJ.Meshcheryakov, SAAtroshenko,
V.B.Vasilkov, AKDivakov 226
STOCHASTIZATION OF CRACK GROWTH
DIRECTION IN HETEROGENEOUS MEDIA
I.Micklashevich, A.Chigarev 227
DYNAMIC FRACTURE IN SOLIDS UNDER PULSE
DEFORMATION
RI.Nigmatulin, N. KhAkhmadeyev,RKhBolotnova 228
ANALYSIS OF MATERIALS FRACTURE PROCESSES
UNDER DYNAMIC LOADING
A.J.Rouzanov*
228
HIGHSPEED PIERCING OF HOLES
IN THE THIN BLANKS
Y.Shamarin 229
ON INFLUENCE OF THE ELECTRIC EXPLOSIONS
IN LIQUID ON COMPRESSED POROUS MEDIUM IN
THE COURSE OF FILTERING
O.N.Sizonenko, D.N.Liapis,V.N.Buriak, V.N.Banko 230
A NONSTATIONARY THREE-DIMENSIONAL
PROBLEMS OF CONCENTRATION STRESS IN
ELASTIC-PLASTIC BODIES
PA.Steblianko 231
THEORETICAL AND EXPERIMENTAL
INVESTIGATION OF DYNAMICAL DEFORMATION
AND FRACTURE OF FIBER-REINFORCED
COMPOSITES
S.V.Stepanenko, AVAseev, G.E.Makarov 232
ICF8 PARTI XXili
DYNAMIC TOUGHNESS AND ML-DUCTILITY
TRANSITION: SHEAR-LIP AND DYNAMIC PLASTICZONE SIZES
W.RTyson, RBouchard, LMalik 233
LOAD RATE EFFECT ON FRACTURE RESISTANCEOF SOME LOW-CARBON STEELS
S.B.Vodenicharov 233
QUANTIFICATION OF CONSTRAINT EFFECTS IN
AUSTENITE STEELS
Huang Yuan, Karl-Heinz Schwalbe 234
CONSTRAINT OF SIDE-GROOVE AND ITS
INFLUENCE ON FRACTURE TOUGHNESS
PARAMETER IN CHARPY-SIZE SPECIMENS
X.P.Zhang, Y.W.Shi 235
PROPAGATION OF THE BRITTLE CRACK ALONG
THE SLIGHTLY CURVED TRAJECTORY
Grigory M. Zrazhevsky 236
A WAVE-CRACK MODEL FOR DYNAMIC
FRACTURE INSTABILITIES
Huajian Gao 237
DISCUSSION OF THE TWO-DIMENSIONAL
FRACTURE SURFACE MARKS OBTAINED BY THE
MODEL OF A PRIMARY CRACK PROPAGATING
CIRCULARLY
ATakimoto, T.Fujli 237
THE DYNAMIC THERMOELASTICLTY PROBLEM
FOR A PLATE WITH A MOVING SEMI-INFINITE CUT
A.I.Zhornik, EM.Kartashov 238
REVIEW OF THE CRACK GROWTH THEORIES
ANeimitz 239
CRITERION OF DYNAMIC FRACTURE OF BRITTLE
SOLIDS
Yu.V.Petrov 240
A UNIFIED APPROACH TO THE CRACK PATH
INSTABILITY PHENOMENA
N.PAndrianopoulos, S.KKourkoulis 241
ON THE INFLUENCE OF HIGHER ORDER
TRANSIENT TERMS FOR DETERMINING DYNAMIC
STRESS INTENSITY FACTORS
J.F.Kalthoff 242
FRACTURE RESISTANCE OF ALUMINIUM ALLOY
WELDED JOINTS AT VARIOUS STRAIN RATES
T.M.Labur, AYaJshchenko 243
XXIV PARTI ICF8
DYNAMIC FRACTURE TOUGHNESS
DETERMINATION USING THE CCS TECHNIQUE:APPLICATION TO PMMA
D.Rittel, H.Maigre 243
FURTHER STUDIES ON MIXED CONCRETE
FRACTURE
Z.K.Guo, AS.Kobayashi, N.M.Hawkins 244
DYNAMIC FRACTURE TOUGHNESS OF THE STEEL
CONTROLLED ROLLING IN THE TEMPERATURE
RANGE FROM 77 TO 293 K
A. Ya.Krasowsky, V.N.Krasiko,AD.Romanyuk 245
THREE-DIMENSIONAL PROBLEMS ON CRACK
GROWTH ON MECHANICAL AND DIFFUSION
LOADING
A. V.Baluieva 246
SELF-ORGANIZATION EFFECTS IN MEDIA
INVOLVING MICROCRACKS AND DAMAGE
RELATIONSHIPS AT SPALL CONDITIONS
V.V.Belyaev 247
THE DESTRUCTION OF HIGH PRESSURE
COMPOSITE CASINGS UNDER SHOCK-WAVE
LOADING
AA.Cheprunov, N.I.Shentsev 247
STRESS-STRAIN STATE OF ELASTIC HALF-SPACE
WITH INCLUSION
VADobrushkin 248
NATURE OF REBINDER EFFECT BY NON-ORGANIC
DIELECTRICS AND ROCKS FAILURE
VD.Evseyev 249
ULTIMATE STRAIN OF ORIENTED GLASS PLASTIC
COMPOSITE SHELLS UNDER PULSE LOADING
AG.Fedorenko, MA.Syrunin, AG.Ivanor- 250
THE USE OF KINETICS OF CREEP DEFORMATIONS
TO ESTIMATE THE LEVEL OF STRESSES
L.N.Fomitsa 251
APPLICATION OF T*-INTEGRAL TO THE CRACK
PROPAGATION ANALYSIS UNDER THE
QUASI-STATIC AND DYNAMIC LOADING
Y.LKostylev, B.ZMargolin 252
ICF8 PARTI XXV
NUMERICAL MODELLING OF DYNAMICS OF
ROCKS DEFORMATION AND FRACTURING UNDER
DIFFERENT BLASTING CONDITIONS
S.V.Lukichov, SAKozyrev 253
DETERMINATION OF DYNAMIC FRACTURE
TOUGHNESS OF MATERIALS UNDER IMPACT
LOADING
AV.Naumov, V.V.Kalaida 254
CHARACTERIZATION OF THE INTriATION
BEHAVIOR OF MODE-H AND MIXED LOADED
CRACKS
RPodleschny, J.F.Kalthojf 255
THE FRACTURE OF EXPLOSIVELY LOADED STEEL
CYLINDERS AND THE FORMATION OF BIMODALE
FRAGMENT MASS DISTRIBUTION
VAOdintsov 255
COMPRESSION OF RUBY UNDER
DYNAMIC STRESS TO 200 GPa
A.I,Pavlovskiy V.V.Platonov,
O.M.Tatsenko, AAVolkov 256
INVESTIGATION OF FAILURE DYNAMICS UNDER
HIGH-SPEED LOADING
AARakitsky, V.V.Malyatin 257
BRITTLE PLATE FAILURE UNDER IMPACT EFFECT
A.I.Sadyrin 258
MODELING STRAIN RATE EFFECT ON BEHAVIOUR
OF THE PLASTIC ZONE NEAR A CRACK TIP IN
MODE II
I.V.Varfolomeyev, J.RKlepaczko 259
THE NEAR CRACK LINE SOLUTIONS FOR A
MODE-I PLANE STRAIN PROPAGATING CRACK IN
STEADY STATE CASE
Zhi-Jian Yt, Ting-Shi Zhao,
Guang-Qing Zhang 260
ON THE GENERAL FRAGMENTATION REGULARITY
IN A VARIETY OF PROPERTIES AND DIMENSIONS
OF THE OBJECTS
B.V.Zamyshlyayev, LS.Yevterev 260
STATIC AND DYNAMIC FRACTURE OF A
GLASS-CERAMIC MATRIX COMPOSITE
ENazarenko, D.Francois 261
XXVI' PARTI SCF8
DYNAMIC CONTACT INTERACTIONS AND
FRACTURE PROCESSES OF COMPOSITE MATERIALS
V.D.Koshur'
262
STRAIN RATE AND STRAIN-RATE HISTORY
EFFECTS ON THE MECHANICAL PROPERTIES OF
STRUCTURAL MATERIALS
Ugodchikov A.G., Bragov AM. 263
PRINCIPLE OF MAXIMUM ENERGY DISSIPATION
RATE IN CRACK DYNAMICS
LJ.Slepyan 264
DYNAMIC TENSILE FRACTURE PHENOMENA AND
NON-LINEAR WAVE EFFECTS IN CERAMICS
Jerzy Najar 265
THE NUMERICAL ANALYSIS OF COMPOSITE
MATERIALS DYNAMIC FRACTURE
E.G.Yevseev, SA.Sylantiev, G.P.Zaytsev 265
THE EFFECT OF p PHASE STABILITY ON THE
DYNAMIC FRACTURE TOUGHNESS
OF Ti - 6A1 - 4V ALLOY
T.Kobayashi, I.A.Akmoulin, M.Niinomi, 266
ENVIRONMENTAL EFFECTS 269
ENVIRONMENTAL EFFECTS ON FRACTURE
Markus O.Speidel 271
CONTROL OF THERMODYNAMIC ACTIVITY OF
CORROSIVE MEDIUM COMPONENTS TO INCREASE
CYCLIC DURABILITY
M.I.Chaevsky, J.M.Blednova 271
CORROSION CRACKING CRITERION
S.KFomichev 212
CONDITIONS OF A CORROSION CRACKING
INITIATION WITH PLASTIC DEFORMATION OF
HIGH-STRENGTH STEELS
V.N.Malyshev, V.V.Potapov 273
HYDROGEN EMBRJTTLEMENT OF METALS IN
THERMAL POWER STATION WATER-STEAM
CIRCUITS
A.B.Vainman 214
DETERMINING CORROSION CAUSES IN
INTER-SUPERHEATED PIPING
VSijacki-Zerav&t, A.Milosavljevi6,A.Markovi6, I.Blacii, BAndelit 275
ICF8 PARTI
CYCLIC RESPONSE-ELECTROCHEMICALINTERACTION IN FATIGUED STAINLESS STEEL
EXPOSED TO SULPHURIC ACID
Y.F.Li, A.LRadin, C.Laird 275
ELECTROCHEMICAL ASPECTS OF LOCAL
CORROSIVE MECHANICAL DAMAGES INITIATION
BA.KHadyrbekov, LM.Melnikov,V.N.Pechersky, IASugirberov 216
CRACK GROWTH RATE IN TITANIUM ALLOYS
SA.Shipilov 277
ENVIRONMENT-ASSISTED CRACKING IN ALLOY
COO COMPONENTS IN PWR PRIMARY WATER
P.M.Scott 278
FATIGUE PROPERTIES OF NITRIDED PURE
TITANIUM IN HYDROCHLORIC ACID
ENVIRONMENT
T.Morita, M.Shimizu, K.Kawasaki 219
A NUMERICAL MODEL FOR PITTING CORROSION
KINETICS IN PRESSURIZED PIPELINES
A.H.Baraov 279
LOCAL DAMAGES AND MATERIALS DURABILITY
PREDICTION FOR HIGH PARAMETERS MEDIUM
B.A.Khadyrbekov, PA. Pavlov,V.V.Borisevitch, V.N.Pechersky 280
MECHANISM OF THE EFFECT OF A MEDIUM ON
SUBSTRUCTURE, MECHANICAL PROPERTIES AND
FRACTURE OF SOLIDS
G.G.Kochegarov 281
RELATIONSHIP BETWEEN MICROSTRUCTURE
PARAMETERS AND STATIC FATIGUE STRUCTURAL
STEELS IN SOUR ENVIRONMENT
EMazancova, KMazanec 282
INVESTIGATION OF INFLUENCE OF THE SCALE
FACTOR ON CORROSION STABILITY OF TITANIUM
ALLOYS
V.F.Lukyanov, M.V.Soltovets, AV.Shumilin 283
EMBRrTTLEMENT OF HEAT-RESISTANT
STRUCTURAL STEELS IN LEAD MELT
J.M.Lyuty, O.I.Yeliseyeva, V.I.Kalandruk 284
REFERENCE DATA BANK "CORROSION OF
STRUCTURAL MATERIALS UNDER STRESS"
I.O.Nironovich, OJ.Lyzoon 284
XXVIII PARTI ICF8
DEVELOPMENT OF A MULTI - SPECIMEN STRESS
CORROSION CRACKING TESTING SYSTEM USING
A CONSTANT K SPECIMEN
Shigetomo Nunomura, Yakichi Higo,Masayuki Shimojou, Tomohiro Nishiyama 285
HIGH-STRENGTH CORROSION-RESISTANT STEELS
TOUGHNESS AFTER HEATING AT 623-773 K
A.F.Petrakov, G.S.Krivonogov, S.I.Birman,GA.Khakhaleva 286
DURABILITY'OF THE SEA RISER INTERACTTNG
WITH THE FLOODS OF AGGRESSIVE FLUIDS
V.V.Petrov, EN.Dereyfankina 287
CRITERIA AND MODELS OF CORROSION FATIGUE
AND STRESS CORROSION CRACKING
V.N.Polyakov 288
STRESSES INFLUENCE ON INTERACTION OF
ENVIRONMENT WITH THE DEFORMED MATERIALS
NEAR CRACKS AND INCLUSIONS
N.G.Stashchuk 289
FATIGUE FAILURE OF THIN METAL PLATES
UNDER CORROSION MEDIUM CONDITIONS
O.T.Tsyrulnyk, ZO.Terletska 290
DETERMINATION OF FRACTURE RESISTANCE IN
CORROSION FATIGUE OF AMMONIA STORAGE
SPHERES STEEL
AV.Voldemarov, Yu.V.Zima, KI.Kirilov 291
THE SUPPORTING POWER AND THE OPTIMAL
DESIGN OF THE THIN-WALLED CONSTRUCTIONS
WHICH ARE SUBJECTED TO THE INFLUENCE OF
THE AGGRESSIVE MEDIUMS
D.G.Zelentsov, YuMPochtman 291
STRUCTURAL ASPECTS OF CORROSION FATIGUE
OF METALS
O.M.Romaniv 292
THE EFFECT OF POWER PLANT ENVIRONMENT
ON FATIGUE CRACK GROWTH OF PIPE STEELS
E.AGrin' 293
STRUCTURAL DEFORMATION ASPECTS OF
DELAYED FAILURE OF MARAGING STEELS IN
ENVIRONMENTS
V. V.Berezovskaya, Y.G. Vexler,N.V.Zvigintsev 294
ICF8 PARTI XXIX
PHYSICAL METALLURGY OF CORROSION FATIGUEOF ULTRAHIGH STRENGTH STEELS
KMazanec 294
SOME APROACHES TO DETERMINATION
THRESHOLD STRESS INTENSITY FACTORS KISCcAND KIth UNDER STRESS CORROSION CRACKING
AND CORROSION FATIGUE OF STRUCTURAL
STEELS
I.M.Dmytrakh 295
CORROSION AND MECHANICAL STRENGTH OF
MATERIALS USED FOR REACTOR AND STEAM
GENERATOR PRODUCTION
VA.Fedorova, B.T.Timofeev 296
THE MAIN MECHANISMS OF WATER
ENVIRONMENT INFLUENCE ON CYCLIC
FRACTURE TOUGHNESS OF STEELS AT 300 °C
VLPokhmursky, I.P.Gnyp, E.I.Lychkovsky 297
ACCELERATED METHODS FOR THE STUDIES OF
CORROSIVE-MECHANICAL DAMAGES INITIATION
STAGES
V.N.Pechersky, V.V.Borisevich,
MAAlmukhanov, KG.Kayumov 298
INFLUENCE OF SURFACE-ACTIVE MELTS
DETERMINING THE PHENOMENON OF
LIQUID-METAL EMBRITTLEMENT
AA.Borghardt, MA.Krishtal 299
THE DEVELOPMENT AND USE OF
ENVIRONMENTALLY-ASSISTED CRACKING MODELS
FOR LIGHT WATER REACTORS
F.P.Ford 299
THE EFFECT OF SEAWATER EXPOSURE ON THE
FATIGUE DELAMINATION GROWTH OF A
POLYMERIC COMPOSITE
P.Chiou, W.LBradley 300
THE EFFECT OF HYDROGEN ON THE PROPERTIES
OF SUPERALLOYS
V.Duriagin, KKatsov,T.Madjanova, S.Moiseev 301
HYDROGEN-ELASTIC STRESSES AND FORM
CHANGING OF PALLADIUM PLATES
VAGoltsov, TA.Ryumshina, RV.Kotelva 302
XXX PARTI ICF8
NEW FACILITIES FOR INVESTIGATIONS OF
FRACTURE OF MATERIALS IN THE PRESENCE OF
HYDROGEN
KB.Katsov, V.I.Tkachov 303
THE INFLUENCE OF HYDROGEN TREATMENT ON
CRACK RESISTANCE OF STEELS
G.Kortenski 304
THE ACTUAL PROBLEMS OF THE STUDYING OF
HYDROGEN DIFFUSION IN METALS BY
ELECTROCHEMICAL METHODS
N.Krapivny 304
THE NEW APPROACH TO DESCRIPTION OF THE
INTERACTION BETWEEN HYDROGEN ATOMS AND
DEFECTS OF STRUCTURE IN METALS
N.Krapivny, V.Kleshnja,N.Minagureeva, V.Sobornitsky 305
THE INFLUENCE OF HYDROGEN ON FRACTURE
TOUGHNESS AND CRACK GROWTH IN TITANIUM
ALLOYS
A.V.Malkov, V.KAlexeyev, M.G.Mishanova 306
FATIGUE CRACK GROWTH RESISTANCE OF HK-40
STEEL IN GASEOUS HYDROGEN
G.M.Nykyforchyn, I.D.Skrypnyk,O.ZStudent 307
STATIC CRACK RESISTANCE OF HYDROGENATED
HIGH-STRENGTH STEELS
A.F.Petrakov, G.S.Krivonogov 307
ON METHODS OF ESTIMATING SERVICE LIFE IN
MAINS AND PREDICTING SERVICEABILITY OF
PIPE STEEL 09KhG2NABCh
VG.Starchak 308
EMBRITTLEMENT OF QUENCHED STEEL UNDER
THE EFFECT OF ULTRA LOW CONCENTRATIONS
OF DIFFUSION-MOBILE HYDROGEN
V.V.Velichko, V.V.Zabilsky 309
MODELLING OF MECHANISMS OF HYDROGEN
EFFECT ON MECHANICAL PROPERTIES AND MASS
TRANSFER IN METALS AND ALLOYS
A.M.Dobrotvorsky, Y.IArchakov 310
TOUGHNESS OF HYDROGEN CHARGED
MATERIALS, APPLICATION TO Cr-Mo STEELS FOR
HYDROTREATING REACTORS
L.Coudreuse, P.Bocquet, ACheviet 311
ICF8 PARTI XXXI
DESIGN OF STRESSED STATE AND LONGEVITY OF
CONSTRUCTION UNDER HYDROGEN CORROSION
I.G. Ovchinnikov 312
STRUCTURAL CHANGES AND HYDROGEN
INDUCED MATERIAL DESTRUCTION
VAGoltsov, AF.Volkov, AP.Kusint,YuAArtemenko, N.N.Vlasenko 313
GENERAL APPROACH TO THE DEVELOPMENT OF
TITANIUM CONSTRUCTIONS SAFE FROM
HYDROGEN FRACTURE
AV.Malkov, BAKolachev 314
SUBSTRUCTURAL DETERIORATIONS OF
ALUMINIUM ALLOYS AT NORMAL SERVICE
CONDITIONS
V.M.Polyanski, LA.Kurtasova 315
HYDROGEN ASSISTED STRESS CRACKING OF
TITANIUM ALLOYS
LAzkarate, ARecio, A.Del Barrio 316
3 566-3