PART 8 BITUMINOUS

MATERIALS

• 8.1 Introduction • Definitions

• Safety

• Production

• 8.2 Binders

• 8.3 Bituminous mixtures

• 8.4 Applications

Definitions: • Binder: A material used to hold solid particles together,

i.e. bitumen or tar.

• Bitumen: A heavy fraction from oil distillation (also occurs as part of natural asphalt).

• Tar: A viscous liquid obtained from distillation of coal or wood. Rarely used in construction currently in the UK.

• Asphalt: A mixture of bitumen and mineral filler. Note that Hot Rolled Asphalt is a road surfacing material.

• Mastic: An adhering asphalt which is placed with trowelling.

• Macadam: A road construction material with binder and coarse aggregate. Tarmacadam was the first road surfacing material.

SAFETY

• The flash point is the temperature at which vapour given off from the surface will burn.

• The fire point is the temperature at which the binder will burn.

• Water will spread a bitumen fire.

• The materials are generally used at temperatures high enough to cause severe burns.

• Both the materials and the vapours are potentially carcinogenic.

Melted

Bitumen

Bitumen Preparation

Petroleum Kerosene

(parafin) Diesel oil Lubricating

oil

Base

Bitumen

Light oil

Fractional Distillation

Crude

oil

Fluxing

Cut-back

bitumen

Emulsification

in water

Bitumen

Emulsion

Blending

Penetration Grade

Bitumen

Oxidation

Blown Bitumen

Tar Preparation

PART 8 BITUMINOUS

MATERIALS

• 8.1 Introduction

• 8.2 Binders • Properties

• Testing

• Binder Mixtures

• 8.3 Bituminous mixtures

• 8.4 Applications

Binder Properties

• Adhesion Bituminous materials adhere to clean dry surfaces.

• Viscosity All bituminous materials are viscous, i.e. when subject to a long term load they deform continuously.

• Softening point This is the temperature at which the binder softens to a pre-determined point.

Durability ….Bitumens are:

• Intrinsically durable, they oxidise, polymerise and lose light oil components when exposed to air and heat but all of these processes just make then harder

• Virtually impermeable if well compacted

• Intrinsically resistant to plant growth

• Softened by high temperature and solvents (often by fuel spills)

Cracking

of thin

surface

TESTING Binders • Sliding plate viscometer In this apparatus a thin film of

binder is sheared between two glass plates and the shearing force is measured.

• Standard tar viscometer In this test the time taken for a set volume of tar to flow through an opening at a given temperature is measured.

• Penetration test For straight bitumens viscosity is normally measured with a penetration test. A 1mm diameter needle is loaded with a weight of 100g and the distance it drops into a bitumen sample in 5 seconds is measured (at 25oC). A bitumen is referred to as 70 pen if the penetration is 7mm.

• Softening point test To measure the softening point a small sample is melted, cast in brass ring and cooled and then progressively re-heated until it deforms (i.e. "flows") by a given amount.

BINDER MIXTURES

• Cutbacks This term is used to describe a mixture of a binder and a light volatile oil. They are liquid at low temperatures until the volatile oil evaporates.. Due to the release of solvents into the atmosphere they are now rarely used.

• Emulsions When mixed with water binders will generally settle out. An emulsifier must be added to give a stable solution. Bitumen paints are made this way. The water evaporates and the bitumen remains on the surface. The current types of cold rolled materials are based on emulsions.

Rubberised bitumens

• The viscosity and softening point are increased and penetration is decreased.

• The elasticity is increased.

• The sensitivity to temperature changes is decreased.

• The beneficial properties are lost with prolonged heating.

The increased elasticity and penetration resistance makes this material ideal for expansion joints and repairs in roads.

PART 8 BITUMINOUS

MATERIALS

• 8.1 Introduction

• 8.2 Binders

• 8.3 Bituminous mixtures • Components

• Properties

• Testing

• 8.4 Applications

The four components of a typical

mix are:

• Coarse aggregate (retained on 2.36mm

sieve)

• Fine aggregate (passing 2.36mm sieve but

retained on 75µ)

• Filler (passing 75µ), may be cement.

• Binder: Bitumen etc.

Asphalt Mixing Plant

Adding aggregate to a binder has

the following general effects

• The cost is reduced.

• The strength is generally increased.

• If the mix has to be laid hot the aggregate

must also be heated (at considerable cost)

• May fail due to loss of adhesion between

aggregate and binder

TESTING Bituminous Mixtures

• Penetration test This test is similar in principle to the penetration test for binders but on a larger scale. The steel pin is 6.35mm (0.25") diameter and the load is 10 N/mm2

• Marshall test In this test asphalt mixes are made at several different binder contents. Cylindrical specimens are loaded in compression on their curved surfaces. The maximum load (stability) and the deformation (flow) is recorded.

• Dissolution of binder There are a number of BS tests which involve dissolution of the binder in solvents. The mix proportions and the nature of the binder may be determined.

• Percentage refusal density This test is used to measure compaction in road construction. The density of a core from the road is compared with the maximum density achievable using heat and heavy compaction (the refusal density).

Marshall Test

TESTING Bituminous Mixtures

• Penetration test This test is similar in principle to the penetration test for binders but on a larger scale. The steel pin is 6.35mm (0.25") diameter and the load is 10 N/mm2

• Marshall test In this test asphalt mixes are made at several different binder contents. Cylindrical specimens are loaded in compression on their curved surfaces. The maximum load (stability) and the deformation (flow) is recorded.

• Dissolution of binder There are a number of BS tests which involve dissolution of the binder in solvents. The mix proportions and the nature of the binder may be determined.

• Percentage refusal density This test is used to measure compaction in road construction. The density of a core from the road is compared with the maximum density achievable using heat and heavy compaction (the refusal density).

PART 8 BITUMINOUS

MATERIALS

• 8.1 Introduction

• 8.2 Binders

• 8.3 Bituminous mixtures

• 8.4 Applications

Applications

• Roads

• Tanking

• Roofing

Road construction types

Wearing course

Base course

Roadbase

Sub-base

Subgrade (limestone)

Wearing course

Roadbase

Lower base (crack

resistant)

Sub-base

Subgrade (limestone)

Paving

machine

Surfacing materials

• Hot rolled asphalt: Coarse aggregate dispersed in a mortar composed of sand, filler and bitumen. This is gap graded.

• Asphaltic concrete: Asphalt in which the aggregate particles are continuously graded to form an interlocking structure.

• Surface dressing: Sprayed bitumen binder with stone chippings rolled on. This is used for repair work.

• Slurry surfacings and micro asphalts: Bitumen emulsions with selected aggregate combinations. Also used for repair.

• Stone mastic asphalt: gap graded asphalt composed of a coarse crushed aggregate skeleton with mastic mortar.

Hot Rolled Asphalt Surface

Surfacing materials

• Hot rolled asphalt: Coarse aggregate dispersed in a mortar composed of sand, filler and bitumen. This is gap graded.

• Asphaltic concrete: Asphalt in which the aggregate particles are continuously graded to form an interlocking structure.

• Surface dressing: Sprayed bitumen binder with stone chippings rolled on. This is used for repair work.

• Slurry surfacings and micro asphalts: Bitumen emulsions with selected aggregate combinations. Also used for repair.

• Stone mastic asphalt: gap graded asphalt composed of a coarse crushed aggregate skeleton with mastic mortar.

Failure mechanisms.

• Wearing course:

– Rutting (shear failure)

– Potholes (bond failure)

– loss of skid resistance (viscous flow)

• Lower courses

– Cracking (Fatigue failure)

– Breakdown due to failure of lower courses (e.g. reflected cracking from dry-lean concrete)

Applications

• Roads

• Tanking

• Roofing

Tanking a basement

(modern systems use sheet materials)

Base slab cast on layer of

mastic asphalt

Asphalt trowelled onto

walls after casting

Applications

• Roads

• Tanking

• Roofing