Innovative Products For The Infrastructure Repair Industry
Stephen's Technologies Newlife Liner Epoxy Lamination System
DESCRIPTION: A medium-viscosity, highly chemical-resistant, 2-part epoxy system formulated for the lamination of special fiberglass reinforcements designed by Stephen's Technologies, Inc. for the infrastructure repair
CHARACTERISTICS: Formulated with special additives and modifiers to enhance the water resistance, chemical resistance, bond strength to a variety of substrates, and internal strength. It is also has characteristics which provide for rapid wet-out of most types of reinforcing materials. It is designed to cure at temperatures as low as 40-deg. F.
APPLICATION: Designed for the lamination system patented by Stephen’s Technologies or for general hand lamination of felts, fiberglass, and other reinforcing materials.
ADVANTAGES: *Rapid Wet-Out Of Conventional Substrates* *Fast Cure To Allow Rapid Removal Of Carriers/Bladders* *Excellent Cure At Low Temperature And High Humidity* *Zero Induction Time* *0% VOC’s* *100% Solids* *Highly Water/Chemical Resistant * Long Working Time Relative To Cure Time* *Rapid Cure In Cold Temperatures* *DOT Non-Corrosive*
Skin Contact: Wash thoroughly with soap and water. Remove contaminated clothing and wash before re-wearing. Eye Contact: Flush immediately for 15 minutes with large volumes of water and seek immediate medical attention.
LIQUID PROPERTIES (System):
Viscosity 2500 cps
Thix Index 1.0-1.5
Specific Gravity 0.99
Flash Point (Closed Cup) >235-Deg. F.
Color Varies
Geltime (200g @77-Deg F.
10-25 Minutes
Thin Film Set @ 77-Deg. F.
2.5 Hours
Thin Film Set @ 40-Deg. F.
8.0 Hours
Mix Ratio (By Volume)
3:1
SAFETY AND HANDLING: This epoxy is typical of most epoxies in that the activator can cause skin and eye damage in the uncured state. Even the resin can cause some irritation upon prolonged or repeated exposure. Rubber gloves, protective eyewear, and protective clothing are strongly recommended when handling these materials. In the event of accidental contact, treat as follows:
TYPICAL PROPERTIES:
STEPHEN’S TECHNOLOGIES, INC. 3921 Prospect Avenue Naples, Florida 34104
TEL 1-888-S.T.E.P.H.E.N. FAX 239-643-3984
Tensile Strength (ASTM D638-86) 9500 PSI 12,900 PSI
Flexural Strength (ASTM D790-86) 15,700 PSI 18,100 PSI
Flexural Modulus @ .100” (ASTM D790-86) 475,000 PSI 685,000 PSI
Compressive Strength (ASTM D695-85) 11,700 PSI 15,780 PSI
Bond Strengtrh To Damp Concrete >3,200 PSI >3,500 PSI
Glass Transition Temperature (ASTM D3418-82) 131-Deg. F 148-Deg. F.
Tensile Elongation @ Break 4.8% 5.2%
Thin Film Set Time @ 77-Deg. F 2.0 Hours 2.0 Hours
Shore D Hardness 81-82 82-84
TYPICAL PROPERTIES: W/O Liner W/ 3mm Liner
Chemical Resistance (28 Day Immersion)
Weight Gain
Toluene 2.23%
Ethanol 6.68%
10% Acetic Acid 4.81%
70% Sulfuric Acid 0.18%
50% Sodium Hydroxide 0.11%
Distilled Water 1.39%
TYPICAL PROPERTIES (CONTINUED):
Chemical Resistance (28 Day Immersion)
Weight Gain
Methanol 11.94%
Xylene 0.87%
Butyl Cellosolve 1.48%
Methyl Ethyl Ketone 13.99%
10% Lactic Acid 4.05%
Bleach 1.16%
1,1,1 Trichloroethane 0.54%
10% Nitric Acid 2.56%
30% Nitric Acid 5.22%